CN101077952B - Preparation technique of decoration perlite particle spraying material - Google Patents
Preparation technique of decoration perlite particle spraying material Download PDFInfo
- Publication number
- CN101077952B CN101077952B CN200710015835A CN200710015835A CN101077952B CN 101077952 B CN101077952 B CN 101077952B CN 200710015835 A CN200710015835 A CN 200710015835A CN 200710015835 A CN200710015835 A CN 200710015835A CN 101077952 B CN101077952 B CN 101077952B
- Authority
- CN
- China
- Prior art keywords
- parts
- clear water
- perlite particle
- perlite
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The ceiling decorating granular perlite paint consists of perlite grain, vinyl acetate copolymer emulsion, styrene-acrylic emulsion, sodium polyacrylate, anatase type titanium white powder, heavy calcium carbonate, calcium chloride and water. Its preparation process includes the following steps: 1. dissolving sodium polyacrylate in water; 2. adding vinyl acetate copolymer emulsion and styrene-acrylic emulsion into the solution to form mixture; 3. adding anatase type titanium white powder mixed with water, and heavy calcium carbonate into the mixture; 4. adding calcium chloride aqua into the mixture; and 5. adding perlite grain and water into the mixture through stirring, and packing the paint product.
Description
Technical field
The present invention relates to a kind of ceiling decoration perlite particle spraying material and preparation technology thereof.
Background technology
The spray material that uses requires height to base treatment at present, and operation is many, and constructional difficulties is seriously polluted, the cost height.
Summary of the invention
The invention provides a kind of ceiling decoration perlite particle spraying material easy to use.
To achieve these goals, technical scheme of the present invention is: a kind of ceiling decoration perlite particle spraying material is characterized in: ceiling decoration perlite particle spraying material proportioning by weight is as follows:
28～36 parts of 10～12.5 parts of Vinyl Acetate Copolymer copolymer emulsions of perlite particle
1～1.8 part of 12～15 parts of sodium polyacrylate of benzene emulsion
20～28 parts of 4～8 parts of water-ground limestones of anatase thpe white powder
43～55 parts in 10～17 parts of clear water of calcium chloride
A kind of preparation technology of ceiling decoration perlite particle spraying material is characterized in: this technical process is:
A, with clear water and sodium polyacrylate according to the mixed of parts by weight proportioning 18～22: 1～1.8, stir, dissolve and become to dissolve material
B, add 28～36 parts of Vinyl Acetate Copolymer copolymer emulsions according to above-mentioned parts by weight proportioning in dissolving material, 12～15 parts of benzene emulsions mix then, stir into and stir material
C, according to above-mentioned parts by weight proportioning, with the mixed of anatase thpe white powder and clear water 4～8: 4～6, add 20～28 parts of water-ground limestones, mix, stir and dissolve into compound
D, according to above-mentioned parts by weight proportioning, the ratio of calcium chloride and clear water 10～17: 18～22 stirred dissolves the adding compound, stir then
E, according to above-mentioned parts by weight proportioning, add 10～12.5 parts of perlite particles, 3～5 parts in clear water is packaged into finished product after the stirring.
Advantageous effect of the present invention is: it is ornamental and adaptability is more intense that this spray material is looked mask hairiness velour texture, and construction is simple, is convenient to mechanized operation, can save the full Puttying operation of ceiling, low to the base treatment requirement, covering effect is good, can also improve the sound effects in room, reduce labor intensity accelerating construction progress, products material wide material sources, production technique is simple, with low cost, pollution-free, chemical stability is good.
Embodiment
Embodiment 1:
A kind of ceiling decoration perlite particle spraying material, ceiling decoration perlite particle spraying material proportioning by weight is as follows:
28 parts of 10 parts of Vinyl Acetate Copolymer copolymer emulsions of perlite particle
1 part of 12 parts of sodium polyacrylate of benzene emulsion
20 parts of 4 parts of water-ground limestones of anatase thpe white powder
43 parts in 10 parts of clear water of calcium chloride
This technical process is:
A, with clear water and sodium polyacrylate according to 18 parts of parts by weight proportionings: 1 part mixed, stir, dissolve and become to dissolve material
B, add 28 parts of Vinyl Acetate Copolymer copolymer emulsions according to above-mentioned parts by weight proportioning in dissolving material, 12 parts of benzene emulsions mix then, stir into and stir material
C, according to above-mentioned parts by weight proportioning, with 4 parts in anatase thpe white powder and clear water: 4 parts mixed, add 20 parts of water-ground limestones, mix, stir and dissolve into compound
D, according to above-mentioned parts by weight proportioning, with 10 parts in calcium chloride and clear water: 18 parts ratio stirs dissolves the adding compound, stirs then
E, according to above-mentioned parts by weight proportioning, add 10 parts of perlite particles, 3 parts in clear water is packaged into finished product after the stirring.
Embodiment 2:
A kind of ceiling decoration perlite particle spraying material, ceiling decoration perlite particle spraying material proportioning by weight is as follows:
31 parts of 10 parts of Vinyl Acetate Copolymer copolymer emulsions of perlite particle
1.5 parts of 13.6 parts of sodium polyacrylates of benzene emulsion
25 parts of 8 parts of water-ground limestones of anatase thpe white powder
49 parts in 15 parts of clear water of calcium chloride
This technical process is:
A, with clear water and sodium polyacrylate according to 20 parts of parts by weight proportionings: 1.5 parts mixed, stir, dissolve and become to dissolve material
B, add 31 parts of Vinyl Acetate Copolymer copolymer emulsions according to above-mentioned parts by weight proportioning in dissolving material, 13.6 parts of benzene emulsions mix then, stir into and stir material
C, according to above-mentioned parts by weight proportioning, with 8 parts in anatase thpe white powder and clear water: 5 parts mixed, add 25 parts of water-ground limestones, mix, stir and dissolve into compound
D, according to above-mentioned parts by weight proportioning, with 15 parts in calcium chloride and clear water: 20 parts ratio stirs dissolves the adding compound, stirs then
E, according to above-mentioned parts by weight proportioning, add 10 parts of perlite particles, 4 parts in clear water is packaged into finished product after the stirring.
Embodiment 3:
A kind of ceiling decoration perlite particle spraying material, ceiling decoration perlite particle spraying material proportioning by weight is as follows:
36 parts of 12.5 parts of Vinyl Acetate Copolymer copolymer emulsions of perlite particle
1.8 parts of 15 parts of sodium polyacrylates of benzene emulsion
28 parts of 8 parts of water-ground limestones of anatase thpe white powder
55 parts in 17 parts of clear water of calcium chloride
This technical process is:
A, with clear water and sodium polyacrylate according to 22 parts of parts by weight proportionings: 1.8 parts mixed, stir, dissolve and become to dissolve material
B, add 36 parts of Vinyl Acetate Copolymer copolymer emulsions according to above-mentioned parts by weight proportioning in dissolving material, 18 parts of benzene emulsions mix then, stir into and stir material
C, according to above-mentioned parts by weight proportioning, with 8 parts in anatase thpe white powder and clear water: 6 parts mixed, add 28 parts of water-ground limestones, mix, stir and dissolve into compound
D, according to above-mentioned parts by weight proportioning, with 17 parts in calcium chloride and clear water: 22 parts ratio stirs dissolves the adding compound, stirs then
E, according to above-mentioned parts by weight proportioning, add 12.5 parts of perlite particles, 5 parts in clear water is packaged into finished product after the stirring.
Claims (6)
1. the preparation technology of a ceiling decoration perlite particle spraying material, ceiling decoration perlite particle spraying material proportioning by weight is as follows:
28～36 parts of 10～12.5 parts of Vinyl Acetate Copolymer copolymer emulsions of perlite particle
1～1.8 part of 12～15 parts of sodium polyacrylate of benzene emulsion
20～28 parts of 4～8 parts of water-ground limestones of anatase thpe white powder
43～55 parts in 10～17 parts of clear water of calcium chloride is characterized in that: this technology
Flow process is: a, with clear water and sodium polyacrylate according to 18～22 parts of parts by weight proportionings: 1～1.8 part mixed, stir, dissolve and become to dissolve material
B, add 28～36 parts of Vinyl Acetate Copolymer copolymer emulsions according to the parts by weight proportioning in dissolving material, 12～15 parts of benzene emulsions mix then, stir into and stir material
C, according to the parts by weight proportioning, with 4～8 parts in anatase thpe white powder and clear water: 4～6 parts mixed, add 20～28 parts of water-ground limestones, mix, stir and dissolve into compound
D, according to the parts by weight proportioning, with 10～17 parts in calcium chloride and clear water: 18～22 parts ratio stirs dissolves the adding compound, stirs into then and stirs material
E, according to the parts by weight proportioning, add 10～12.5 parts of perlite particles, 3～5 parts in clear water is packaged into finished product after the stirring.
2. the preparation technology of ceiling decoration perlite particle spraying material according to claim 1 is characterized in that: the clear water in a stage and sodium polyacrylate are 20 parts according to the proportioning of parts by weight in the described technical process: 1.5 parts.
3. the preparation technology of ceiling decoration perlite particle spraying material according to claim 2 is characterized in that: 31 parts of the Vinyl Acetate Copolymer copolymer emulsions in b stage in the described technical process, 13.6 parts of benzene emulsions.
4. the preparation technology of ceiling decoration perlite particle spraying material according to claim 3 is characterized in that: the anatase thpe white powder in c stage and clear water ratio are 8 parts in the described technical process: 5 parts, water-ground limestone is 25 parts.
5. the preparation technology of ceiling decoration perlite particle spraying material according to claim 4 is characterized in that: the ratio of the calcium chloride in d stage and clear water is 15 parts in the described technical process: 20 parts.
6. the preparation technology of ceiling decoration perlite particle spraying material according to claim 5 is characterized in that: 10 parts of the perlite particles in e stage in the described technical process, 4 parts in clear water.