CN102382522B - Styreneacrylic emulsion insulating coating - Google Patents
Styreneacrylic emulsion insulating coating Download PDFInfo
- Publication number
- CN102382522B CN102382522B CN201010269978.XA CN201010269978A CN102382522B CN 102382522 B CN102382522 B CN 102382522B CN 201010269978 A CN201010269978 A CN 201010269978A CN 102382522 B CN102382522 B CN 102382522B
- Authority
- CN
- China
- Prior art keywords
- parts
- styreneacrylic
- emulsion
- insulating coating
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a styreneacrylic emulsion insulating coating, which is mainly prepared by agitating the following raw materials in parts by weight: 70 parts of styreneacrylic emulsion, 35 parts of closed cell perlite, 36 parts of ethanediamine, 10 parts of polypropylene fibre, 45 parts of acrylic resin, 12 parts of sodium potassium silicate, 5 parts of triethanolamine, 10 parts of phenol, 6 parts of binder, 10 parts of turpentine, 65 parts of water, 2 parts of preservative, 15 parts of kaolin, 3 parts of thickener and 1 part of film forming auxiliary. The product has good insulating effect and better water and alkali resistance.
Description
Technical field
The present invention relates to a kind of Styreneacrylic emulsion insulating coating.
Technical background
At present, the building heat insulation material of China and goods thereof are two kinds of single products that material is different, purposes is different from coating.If used on same construction wall or terrace, obviously there is poor adhesive force, the defects such as structure is not firm, work-ing life is short, because it is fluffy that existing lagging material and goods belong to lightweight more, materials are slightly thick, as plastic foamboard, microporous fibre goods, granular polystyrene, normal expanded perlite and so on.Be bonded on body of wall or terrace, must add and make grid cloth and screed, then could blade coating.Outdoorly be even difficult to avoid getting loose drop, peeling cracking, indoorly obviously too much takies house usage space or affect decorative effect and the disadvantage such as construction complexity.Especially above-mentioned lightweight material is thick, the goods such as lagging material that poor adhesive force, structure are not firm, work-ing life is short can not with facing putty or the perfect combination of decorative paint, do not reach the two-layer effect of insulation and decoration.So limited applying aspect building.
Summary of the invention
The present invention seeks in order to overcome the deficiencies in the prior art, a kind of have very high water tolerance and alkali-proof Styreneacrylic emulsion insulating coating are provided.
For addressing the above problem, technical scheme of the present invention is: a kind of Styreneacrylic emulsion insulating coating stirs and makes according to weight proportion by following raw materials according: 70 parts of benzene emulsions, 35 parts of closed perlite, 36 parts of quadrols, 10 parts of polypropylene fibres, 45 parts of acrylic resins, 12 parts of sodium-potassium silicates, 5 parts of trolamines, 10 parts of phenol, 6 parts of binding agents, 10 parts of turps, 65 parts of water, 2 portions of sanitass, 15 parts of kaolin, 3 parts of thickening materials, 1 part of film coalescence aid.
Beneficial effect of the present invention:
1, in this product, add closed perlite and made it have good heat insulation and preservation effect.
2, water-fast, alkali resistance is good.
Embodiment
Example of the present invention is can not limit the present invention to explanation of the present invention, in the implication suitable with the present invention and any change and the adjustment in scope, all should think within the scope of the invention.
Embodiment 1
Styreneacrylic emulsion insulating coating is stirred and is made by stirrer high speed dispersion according to weight proportion by following raw materials according: 70 parts of benzene emulsions, 35 parts of closed perlite, 36 parts of quadrols, 10 parts of polypropylene fibres, 45 parts of acrylic resins, 12 parts of sodium-potassium silicates, 5 parts of trolamines, 10 parts of phenol, 6 parts of binding agents, 10 parts of turps, 65 parts of water, 2 portions of sanitass, 15 parts of kaolin, 3 parts of thickening materials, 1 part of film coalescence aid.The basic mechanical design feature of product prepared by the present invention is as following table 1
Table 1, basic mechanical design feature of the present invention
Claims (1)
1. a Styreneacrylic emulsion insulating coating, is characterized in that it is stirred and make according to weight proportion by following raw materials according: 70 parts of benzene emulsions, 35 parts of closed perlite, 36 parts of quadrols, 10 parts of polypropylene fibres, 45 parts of acrylic resins, 12 parts of sodium-potassium silicates, 5 parts of trolamines, 10 parts of phenol, 6 parts of binding agents, 10 parts of turps, 65 parts of water, 2 portions of sanitass, 15 parts of kaolin, 3 parts of thickening materials, 1 part of film coalescence aid.