CN101066598A - Process of producing charcoal coating floorboard - Google Patents
Process of producing charcoal coating floorboard Download PDFInfo
- Publication number
- CN101066598A CN101066598A CN 200710011708 CN200710011708A CN101066598A CN 101066598 A CN101066598 A CN 101066598A CN 200710011708 CN200710011708 CN 200710011708 CN 200710011708 A CN200710011708 A CN 200710011708A CN 101066598 A CN101066598 A CN 101066598A
- Authority
- CN
- China
- Prior art keywords
- floorboard
- laminated
- paper
- glue
- powdered carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention belongs to the field of decoration technology, and is especially process of producing charcoal coating Jingang floorboard comprising a facing layer and a base layer. The production process includes the following steps: spraying the mixture of charcoal powder and alumina powder in the weight ratio of 1 to 20 to glue-soaking decorating decoration paper, stoving, cutting to proper size, combining the decorating decoration paper layer with the base layer by using two steel plates including one upper one heated to 180-200 deg.c and one lower one heated to 160-180 deg.c, conventional re-moistening, and cutting into floorboard strips. The Jingang floorboard of the present invention has high wear resistance, good antibiotic performance and high UV resistance.
Description
Technical field:
The invention belongs to and decorate the decoration field, relate to a kind of preparation method of floor, particularly a kind of preparation method of charcoal coating floorboard.
Background technology:
As everyone knows, the traditional floor in indoor laying mainly contains wood floors, plastic floor and stone floor etc. by the material branch.Stone floor (generally based on lithotome) as the natural marble floor, although service life is long, hardness is high, because this floor is every cool, not heat insulation, and has radioactive material confrontation health to produce adverse influence.And wood floors have every cool, heat insulation, the function of quality softness, but most wood floors all easily are out of shape with air humidity varies, and anti-wear performance is poor, and is easy to change.Composite floor board on the market uses the colloid wearing layer, has improved the anti-wear performance on floor, but has increased the consumption of glue simultaneously, and then increased the burst size of harmful substance.The patent No. is 03101255.8, the name be called " solid wooden compound floor and superficial layer combination process " patent disclosure a kind of composite floor board and superficial layer combination process that constitutes by double-layer wood at least, promptly between surface layer veneer and floor base material, folded up Tetefol, make up then, hot repressing and processing then become floorboard integral body.This patent has been improved the serviceability on floor by the superficial layer combination process, the no crack performance in surface.The patent No. is 200520015661.8, name be called " a kind of novel antibacterial floor " patent disclosure a kind of combinable antibacterial and novel antibacterial floor sterilizing function of having, it is to be formed by 6 compactings of shape material stack layer by layer, mainly comprise antibiotic layer, overlay paper, wearing layer, facing paper, base material and balance paper, wherein antibiotic layer includes AOB, wearing layer is wear-resisting ply of paper, wherein contain alundum (Al, this utility model floor has anti-microbial property, but its complex structure, complex process.And do not see at present the floor that had both had better anti-wear performance, had anti-oxidant, uvioresistant and antibacterial action yet.
Summary of the invention:
The invention provides and a kind ofly have that anti-wear performance is good, antibiotic, the charcoal coating floorboard of uvioresistant effect, the present invention finishes by following flow process:
Graining paper---→ impregnation---→ adhere to carbon dust, aluminium powder---→ oven dry---→ cutting---→ synthetic---→ return wet---→ bar---→ mortise---→ packing cut out
Before the medium facing paper of the production process of gum dipped paper has soaked glue and enters drying baker, spray aluminium powder (alundum (Al is commonly called as synthetic diamond) and powdered carbon, available roll-type attachment method and blower fan spraying.Powdered carbon: the aluminium powder weight ratio is 1: 20.
The roll-type attachment method is powdered carbon and al powder mixt to be packed into evenly roll trickling to two steel in the case, and steel rolls and at the uniform velocity rotates attached on the gum dipped paper that passes through between two rolling.
The blower fan spraying is with air blast aluminium powder, powdered carbon mixture to be blowed to orifice plate, evenly is sprinkled upon downwards on the gum dipped paper that passes through by orifice plate, finishes attaching process.The temperature of surface attachment powdered carbon and aluminium powder is between 20～25 ℃, and gum dipped paper is by speed per minute 7-12 rice, also can adjust voluntarily according to the attachment method that adopts to reach the product effect and get final product.
Entering the drying baker oven dry all becomes to require size stand-by.
Use the steel plate of brightness more than 600 degree and the gum dipped paper floor base material is synthesized big plate at the press upper plate in the process that is pressed into, its temperature is upper plate 180-200 ℃, lower plate 160-180 ℃.
The prepared gum dipped paper of the present invention can make the floorboards of wood surface increase anti-wear performance; Can in the furniture production process, add and make furniture surface increase wear-resisting, anti-zoned trace, antioxygenic property; Also can in the production process of plastic cement ground material, add the wearability that increases floor coil.
The present invention has following advantage: 1, owing to add three oxygen, two aluminium powders, make floor surface have anti-wear performance preferably; 2, anti-oxidant, anti-ultraviolet effect has been played in the adding of powdered carbon, makes the floor not easy to change; 3, because the colloid wearing layer is used on the conventional composite floor, the large usage quantity of glue, the harmful substance burst size is big, and this method can effectively reduce the consumption of glue, thereby reduces the release of harmful substance; 4, with the steel plate compacting of the above brightness of 600 degree, increased the brightness and the flatness on floor, can play effect antibiotic and attractive in appearance.
The specific embodiment:
Embodiment 1:
Get the graining paper of selection ready, impregnation (selecting the little glue of existing toxicity), mix standby by weight 1: 20 ratio powdered carbon and alundum (Al, the facing paper that will soak glue is placed on two steel and rolls on the conveyer belt, in per minute 7-12 rice speed, select a proper speed, as select the speed of 9 meters of per minutes, facing paper is at the uniform velocity advanced, the mixture of the powdered carbon that mixes and alundum (Al trickled equably soaking on the facing paper of glue, dry, cut into the size of the floor matrix that is laminated with.Again facing paper is laminated with the floor matrix and is in the same place, be laminated with and use 2 above of steel plates of brightness 600 degree to be laminated with in the process, wherein upper plate temperature requirement 180-200 ℃, following plate temperature is 160-180 ℃, (the pressing weight of upper and lower base plate with do not make by the pressing matrix be deformed into should) carry out again routine return wet after, can cut out bar, mortise, pack at last and dispatch from the factory.
Embodiment 2:
Get the graining paper of selection ready, impregnation (selecting the little glue of existing toxicity), mix standby by weight 1: 20 ratio powdered carbon and alundum (Al, the facing paper that will soak glue is placed on two steel and rolls on the conveyer belt, in per minute 7-12 rice speed, select a proper speed, as select the speed of 9 meters of per minutes, facing paper is at the uniform velocity advanced, the powdered carbon that mixes and the mixture of alundum (Al are blowed to orifice plate by blower fan, evenly be sprinkled upon downwards on the gum dipped paper that passes through by orifice plate, finish attaching process.The temperature of surface attachment powdered carbon and aluminium powder is between 20～25 ℃, and by speed per minute 7-12 rice, other is with embodiment 1 with gum dipped paper for empty oxygen flow.Powdered carbon that mixes and alundum (Al are to be contained in the material storing box, and an agitator is arranged in the material storing box, and material storing box one side-lower has an opening, and opening the place ahead connects orifice plate, and blower fan is dried in material storing box.
Embodiment 3:
Floor base material can also be selected density board and plastic floor material except selecting floorboards of wood.Production technology is with embodiment 1, and final products can select to make the floor, also can select to make furniture panel.
Claims (3)
1, a kind of preparation method of charcoal coating floorboard, it is made up of surface layer and basic unit, it is characterized in that: soaking on the graining paper of glue, spray the mixture of powdered carbon and alundum (Al equably, its weight ratio is 1: 20, the facing paper that soaked glue is placed on the conveyer belt, at the uniform velocity advance with per minute 7-12 rice speed, in the traveling process, the mixture of powdered carbon and alundum (Al, is dried attached on the facing paper that soaked glue by equably, cuts into the size of the basic unit that is laminated with, again facing paper is laminated with basic unit and is in the same place, be laminated with and use 2 above of steel plates of brightness 600 degree to be laminated with in the process, wherein upper plate temperature requirement 180-200 ℃, following plate temperature is 160-180 ℃, carry out again routine return wet after, can cut out bar.
2, the preparation method of a kind of charcoal coating floorboard according to claim 1 is characterized in that: the temperature of surface attachment powdered carbon and aluminium powder is between 20～25 ℃.
3, the preparation method of a kind of charcoal coating floorboard according to claim 1 is characterized in that: basic unit is plank or density board or plastic coil.