CN101059022A - High strength light wall plate - Google Patents

High strength light wall plate Download PDF

Info

Publication number
CN101059022A
CN101059022A CNA2007100722417A CN200710072241A CN101059022A CN 101059022 A CN101059022 A CN 101059022A CN A2007100722417 A CNA2007100722417 A CN A2007100722417A CN 200710072241 A CN200710072241 A CN 200710072241A CN 101059022 A CN101059022 A CN 101059022A
Authority
CN
China
Prior art keywords
slag
parts
cement
mixed slurry
haydite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007100722417A
Other languages
Chinese (zh)
Other versions
CN100501100C (en
Inventor
贾镠平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HARBIN FUTAI GREEN BUILDING MATERIALS CO., LTD.
Original Assignee
贾镠平
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 贾镠平 filed Critical 贾镠平
Priority to CNB2007100722417A priority Critical patent/CN100501100C/en
Publication of CN101059022A publication Critical patent/CN101059022A/en
Application granted granted Critical
Publication of CN100501100C publication Critical patent/CN100501100C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

High-intensity light wallboard, the used materials are: according to the weight ratio: ceramicite 235 - 300, slag 235 - 300, cement 120 - 80, coal ash 10-20 and steel fiber; first dipping the ceramicite and the slag in water, mixing the cement and 45-55 water and preparing cement slurry, then mixing and stirring the water dipped ceramicite and slag, cement slurry and coal ash uniformly and preparing mixed slurry, then adding steel fiber into mixed slurry which volume is 0. 15%-2. 4% of mixed slurry volume, stirring uniformly and casting into die, preparing the plate after solidifying, and demoulding; maximum diameter of used ceramicite and slag is 10 mm, the length of steel fiber is 50 - 75mm and the diameter is 0. 6 -0. 7 mm. It has advantages of high strength, small drying shrinkage, no cracks generated between wallboards, no efflorescence when meets water and good sound insulation, its weight is light, the board is thin, it can be planed, sawed and drilled, it is easy to be punched and embedded hanger, it has non-inflammability, the fire prevention performance is good, it uses slag and coal ash as raw materials, it is benefit for environmental protection.

Description

High strength light wall plate
Technical field
The present invention relates to Light trabs for building, particularly high strength light wall plate.
Background technology
Light trabs is widely used in building constructions at present, but existing Light trabs exists or intensity is low, or drying shrinkage value is big, easily produces the crack between wallboard, or meets the easy efflorescence of water, or the bad shortcoming of soundproof effect.
Summary of the invention
The high strength light wall plate that the purpose of this invention is to provide that a kind of intensity height, drying shrinkage value are little, do not produce the crack between wallboard, meet not efflorescence of water, soundproof effect is good.
Technical solution of the present invention is:
The present invention is raw materials used to be: by weight ratio, and 235～300 parts of haydites, 235～300 parts in slag, 80～120 parts of cement, 10～20 parts in flyash and steel fibre; At first haydite and slag are soaked full water, cement and 45～55 parts of waters are mixed and made into cement paste, the haydite that will soak full water then and slag, cement paste and flyash mixing and stirring are mutually made mixed slurry, the steel fibre that in mixed slurry, adds mixed slurry volume 0.15%～2.4% again, inject mould after stirring, make behind the cure and demold; The maximum gauge of used haydite and slag is 10mm, and the specification of steel fibre is long 50～75mm, diameter 0.6～0.7mm.
Technique effect of the present invention is: the advantage that it has, and intensity height, drying shrinkage value are little, do not produce the crack between wallboard, meet not efflorescence of water, soundproof effect is good; its light weight; plate is thin, can dig, and can saw; can hole; the pre-buried suspender member that is easy to burrow, nonflammable, fireproof performance is good; utilize slag and pulverized fuel ash as raw materials, help environmental protection.
The specific embodiment
The present invention is raw materials used to be: by weight ratio, and 270 parts of haydites, 270 parts in slag, 100 parts of cement, 15 parts in flyash, steel fibre and glass fiber; At first haydite and slag are soaked full water, cement and 50 parts of waters are mixed and made into cement paste, the haydite that will soak full water then and slag, cement paste and flyash mixing and stirring are mutually made mixed slurry, in mixed slurry, add the steel fibre of mixed slurry volume 1.2% and the glass fiber of mixed slurry volume 2.4% again, inject mould after stirring, make behind the cure and demold; The maximum gauge of used haydite and slag is 10mm, and the specification of steel fibre is long 70mm, diameter 0.65mm, and the length of glass fiber is 30mm.
After tested, be 0.56mm/m in the wallboard drying shrinkage value two weeks of the present invention, be 0.58mm/m in half a year, can solve wallboard because of the wet crack problem that produces that changes of doing of environment.

Claims (2)

1, high strength light wall plate is characterized in that: raw materials usedly be: by weight ratio, and 235～300 parts of haydites, 235～300 parts in slag, 80～120 parts of cement, 10～20 parts in flyash and steel fibre; At first haydite and slag are soaked full water, cement and 45～55 parts of waters are mixed and made into cement paste, the haydite that will soak full water then and slag, cement paste and flyash mixing and stirring are mutually made mixed slurry, the steel fibre that in mixed slurry, adds mixed slurry volume 0.15%～2.4% again, inject mould after stirring, make behind the cure and demold; The maximum gauge of used haydite and slag is 10mm, and the specification of steel fibre is long 50～75mm, diameter 0.6～0.7mm.
2, high strength light wall plate as claimed in claim 1 is characterized in that: raw materials usedly be: by weight ratio, and 270 parts of haydites, 270 parts in slag, 100 parts of cement, 15 parts in flyash, steel fibre and glass fiber; At first haydite and slag are soaked full water, cement and 50 parts of waters are mixed and made into cement paste, the haydite that will soak full water then and slag, cement paste and flyash mixing and stirring are mutually made mixed slurry, in mixed slurry, add the steel fibre of mixed slurry volume 1.2% and the glass fiber of mixed slurry volume 2.4% again, inject mould after stirring, make behind the cure and demold; The maximum gauge of used haydite and slag is 10mm, and the specification of steel fibre is long 70mm, diameter 0.65mm, and the length of glass fiber is 30mm.
CNB2007100722417A 2007-05-19 2007-05-19 High strength light wall plate Expired - Fee Related CN100501100C (en)