CN101058659A - 自消型环保evoh塑料 - Google Patents
自消型环保evoh塑料 Download PDFInfo
- Publication number
- CN101058659A CN101058659A CN 200610043813 CN200610043813A CN101058659A CN 101058659 A CN101058659 A CN 101058659A CN 200610043813 CN200610043813 CN 200610043813 CN 200610043813 A CN200610043813 A CN 200610043813A CN 101058659 A CN101058659 A CN 101058659A
- Authority
- CN
- China
- Prior art keywords
- agent
- evoh
- self
- environmental protection
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及到一种自消型环保EVOH塑料材料。是以EVOH、聚己内酯、脂肪族聚酯等可以分解的树酯为包覆料,加入C6H10O5复合片材及偶联剂,相容剂多种添加剂和助剂经混炼、捏和、挤出、冷却、造粒制成。可广泛应用适合自消的塑料产品,如一次性的生活用品,食品包装物、农业用地膜等。既可注塑也可吹塑,产品阻隔性好,具有全自消降解性,和其它塑料的理化性能,有利于环境保护和人身健康,生产工艺简单、成本价低。
Description
技术领域
本发明涉及到塑料领域,特别是一种自消型环保EVOH塑料及其生产方法。
现有技术
为了保护环境,消灭“白色污染”,解决石油化工产品塑料使用后不能自消的问题,国内不少科研单位投入大量资金开发研制一种可自消的塑料材料。如在聚烯烃物资中加入光敏剂,使塑料制品使用废弃后见光自消,有一种是聚烯烃类物资加入天然高分子化合物,以促进废弃塑料制品自消,此产品由于存在聚烯烃物质,不可能全部自消。
后来研制出了比较先进的PLA全降解塑料,其主要原料为天然高分子化合物,具有一定的发展前景。但制造PLA全降解塑料工艺比较复杂,如必须将玉米淀粉水解成葡萄糖,再用乳酸杆菌厌氧发酵制成乳酸,再用电渗析工艺制造高固含量的L-乳酸混合物,最后制成聚乳酸酯。不但生产成本高,而设备要靠进口,一时难以规模化生产。
发明内容
本发明之目的是为了集上述降解材料的优点,攻克存在的缺陷,提供一种生产工艺简单,生产成本不高,自消型环保EVOH塑料及其生产方法。
本发明是这样实现的:
采用C6H10O5复合片材,加入偶联剂、相容剂、EVOH树酯和填充剂、添加剂和助剂,通过捏和、混炼,挤出制成的一种自消型环保EVOH塑料,改变了自消型塑料的性能,如EVOH和C6H10O5亲和性好,提高了材料的降解性、透湿性、耐热性、耐寒性,增加了材料的成膜强度,韧性和透明性。
其重量配比为:
C6H10O5复合片材 60-70%
偶联剂 2-4%
相容剂 2-8%
酯肪族聚酯 7-10%
EVOH树酯 20-30%
聚己内酯 4-9%
低分子量蜡 1-4%
抗氧剂 0.2-0.4%
增塑剂 0.2-0.6%
滑润剂 0.4-0.8%
增白剂 0.1-0.3%
紫外线吸收剂 0.1-0.4%
填充剂 2-6%
稳定剂 1-4%
其生产方法为:
(1)将C6H10O5复合片材送入高速恒温的混炼机内,控温100℃,转速500转/分,依次加入偶联剂、相容剂、脂肪族聚酯、EVOH树酯、聚己内酯,混炼20-30分钟,逐步降温、低于30℃时卸料,成为混炼料。
(2)将混炼料送入S型捏和机、速比1.5,捏和30-45分钟,直至物料充分混合均匀。停机30分钟后,加入低分子量蜡,并依次加入抗氧剂、增塑剂、增白剂、紫外线吸收剂、填充剂、开机捏和5分钟,加入滑润剂、稳定剂,再捏和3分钟即成捏和料。
(3)将捏和料送入降解塑料专用,具有十一个区段双螺杆的挤出机中,控温在145-155℃之间,通过挤出、冷却、造粒,即成为合格的自消型环保EVOH塑料。
本发明产生的有益效果是:为国内市场提供一种自消型环保EVOH塑料新材料,用这种新型材料可以生产各种塑料制品,物品适合于生产一次性的塑料产品,如农膜、食品包装袋,因此产品不含对人体有害物质,使用度弃后可自身全部降解,变为肥料,不但保护了生态环境,防止“白色污染”,同时缓解了石油化工塑料求大于供的矛盾;同时C6H10O5复合片材来源于农作物的天然高分子化合物,剩余物资仍然可作为饲料,使农产品升值,只此一项可使经济效益增长30%以上。
实施例:
C6H10O5复合片材6千克,偶联剂0.2千克,相容剂0.2千克,脂肪族聚酯0.7千克,EVOH树酯2千克,聚己内酯0.4千克,低分子量蜡0.1千克,抗氧剂0.02千克,增塑剂0.02千克,滑润剂0.04千克,增白剂0.01千克,紫外线吸收剂0.01千克,填充剂0.2千克,稳定剂0.1千克。
①将C6H10O5复合片材加入到高速恒温混炼机中,控温100℃,依次加入偶联剂、相容剂、脂肪族聚酯、EVOH树酯、聚已内酯、混炼20=30分钟,即为混炼料。②将混炼料送入捏和机中,捏和30-45分钟,停机30分钟后,依次加入低分子量蜡、抗氧剂、增塑剂、增白剂、紫外线吸收剂、填充剂、捏和5分钟后加入滑润剂、稳定剂,再捏和3分钟即成捏和料。③将捏和料送入专用挤出机中通过挤出造粒即成。
Claims (2)
1、一种自消型环保EVOH塑料,其特征在于配方中加入了C6H10O5复合片材、偶联剂、相容剂、脂肪族聚酯、EVOH树酯,低分子量蜡、抗氧剂、增塑剂、滑润剂、增白剂、紫外线吸收剂、填充剂、稳定剂,经混炼、捏和、挤出造粒制成。
其重量配比为:
C6H10O5复合片材 60-70%
偶联剂 2-4%
相容剂 2-8%
酯肪族聚酯 7-10%
EVOH树酯 20-30%
聚己内酯 4-9%
低分子量蜡 1-4%
抗氧剂 0.2-0.4%
增塑剂 0.2-0.6%
滑润剂 0.4-0.8%
增白剂 0.1-0.3%
紫外线吸收剂 0.1-0.4%
填充剂 2-6%
稳定剂 1-4%
2、一种自消型环保EVOH塑料,其特征在于采取如下工艺和步聚:
①将C6H10O5复合片材送入高速恒温混炼机内,控温100℃,转速500转/分,依次加入偶联剂、相容剂、脂肪族聚酯、EVOH树酯、聚己内酯、混炼20-30分钟,逐步降温,低于30℃时卸料,成为混炼材料。
②将混炼料送入S型捏和机中,速比1.5,捏和30-45分钟,直至物料充分混合均匀。停机30分钟后,加入低分子量蜡,并依次加入抗氧剂、增塑剂、增白剂、紫外线吸收、填充剂,再捏和5分钟,加入滑润剂、稳定剂,再捏和3分钟,即成为捏和材料。
③将捏和材料送入降解塑料专用,具有十一个区段的双螺杆挤出机内,控温在145-155℃之间,通过挤出、冷却,造粒,即成为合格的自消型环保EVOH塑料。