CN101058199A - Method for manufacturing formaldehydeless plywood and formaldehydeless multi-layer wood substrates - Google Patents
Method for manufacturing formaldehydeless plywood and formaldehydeless multi-layer wood substrates Download PDFInfo
- Publication number
- CN101058199A CN101058199A CN 200710028074 CN200710028074A CN101058199A CN 101058199 A CN101058199 A CN 101058199A CN 200710028074 CN200710028074 CN 200710028074 CN 200710028074 A CN200710028074 A CN 200710028074A CN 101058199 A CN101058199 A CN 101058199A
- Authority
- CN
- China
- Prior art keywords
- guide rail
- veneer
- hot pressing
- plate group
- sheetpile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a formaldehyde free laminated wood board and multi layer real wood material manufacture. It is made by putting the veneer horizontally crossing, laying fuse glue film or thermal plastic film between veneers to form board sets, then hot forming, pressurizing, cooling to normal temperature to get the final product. Using fuse film or thermal plastic film, it replaces the formaldehyde free adhesive agent to prevent the stretch of the veneer due to the absorption of water to increase the stability of the laminated board size.
Description
Technical field
The present invention relates to the manufacture method of a kind of zero-formaldehyde plywood, zero formaldehyde multi-layer wood substrates.
Background technology
Prior art since oneth century, has been glued together glued board or the multi-layer wood substrates that forms, traditional glue applying method in manufacture process and employed synthetic adhesive by multilayer thin wood plate (abbreviation veneer) at present.Have following shortcoming: 1, the adhesive of common use is based on synthetic resin, as urine aldehyde glue, phenol glue, melamine glue etc.; These adhesive all contain the formaldehyde of harmful to human.2, traditional glue applying method is to use liquid adhesive, with the glue spreader of drum-type, with adhesive applicating on veneer.Because liquid adhesive applicating is behind the veneer of drying, veneer absorbs adhesive, and the flexible phenomenon of veneer can take place.When actual mechanical process, be difficult to grasp the extension degree of every veneer, often cause the defective that " sandwich " or " hollow " arranged between veneer and the veneer.And when veneer has applied after the liquid glue, can improve the moisture content of veneer, glued board, influence the glued board size stability, even the phenomenon that is distorted.
Summary of the invention
The objective of the invention is: the manufacture method that a kind of zero-formaldehyde plywood, zero formaldehyde multi-layer wood substrates are provided, it has not only overcome the defective that contains the formaldehyde of harmful to human in the prior art effectively, and prevented that veneer is because of suction, the veneer that causes is upheld, and has increased the glued board size stability.
The present invention is achieved in that the manufacture method of a kind of zero-formaldehyde plywood, zero formaldehyde multi-layer wood substrates may further comprise the steps:
(1) with veneer cross arrangement in length and breadth, lay does not contain the hot melt adhesive film or the thermoplastic film of formaldehyde between veneer and veneer, makes the plate group;
(2) the plate group is through hot-forming;
(3) under the pressurize condition, be cooled to room temperature, get product.
The plate group is at 8~28kg/cm described in the step (2)
2Under the condition of pressure, 80~280 ℃ of temperature, hot pressing moulding in 1~12 hour in hot-press arrangement.
Described step (2) comprise following 3 step by step:
1. between two bearing plates, according to bearing plate, plate group, heat-conducting plate ... plate group, overlapping the banking up of bearing plate order are made the hot pressing sheetpile, wherein have two laminate groups, one deck heat-conducting plate at least;
2. the hot pressing sheetpile is moved on on the end guide rail that sets in advance in the preformer, on the hot pressing sheetpile, place the top guide rail then, be forced into 8kg/cm
2~28kg/cm
2, with the top guide rail and end guide rail is removably fastening is linked together;
3. with hot pressing sheetpile and top guide rail, after guide rail integral body is taken off at the end, move into baker, under 80 ℃~280 ℃ temperature, heated 1 hour~12 hours; Described step (3) is: after being cooled to room temperature, remove top guide rail, end guide rail and heat-conducting plate, get product.
The manufacture method of a kind of zero-formaldehyde plywood of the present invention, zero formaldehyde multi-layer wood substrates, substitute the adhesive that contains the formaldehyde composition of the prior art with hot melt adhesive film or thermoplastic plastic membrane, prevented that veneer is because of absorbing the moisture in the liquid glue, and the extension phenomenon that causes has strengthened the glued board size stability.
Description of drawings
Fig. 1 is the three-dimensional cutaway view of plate group of the present invention.
Fig. 2 is the three-dimensional explosive view of precompressed of the present invention, oven-dried condition.
The specific embodiment
Embodiment 1
A kind of manufacture method of zero-formaldehyde plywood may further comprise the steps:
(1) as shown in Figure 1, with six layers of veneer 11 cross arrangement in length and breadth, lay hot melt adhesive film 12 between veneer 11 and veneer 11 is made plate group 1;
(2) plate group 1 was placed in the hot-press arrangement hot pressing 1 hour, temperature is controlled at 80 ℃, pressure and is controlled at 8kg/cm in the hot pressing
2
(3) under the pressurize condition, be cooled to room temperature, get product.
Embodiment 2
A kind of manufacture method of zero-formaldehyde plywood may further comprise the steps:
(1) as shown in Figure 1, with 10 layers of veneer 11 cross arrangement in length and breadth, lay hot melt adhesive film 12 between veneer 11 and veneer 11 is made plate group 1;
(2) plate group 1 was placed in the hot-press arrangement hot pressing 12 hours, temperature is controlled at 280 ℃, pressure and is controlled at 28kg/cm in the hot pressing
2
(3) under the pressurize condition, be cooled to room temperature, get product.
Embodiment 3:
A kind of manufacture method of zero-formaldehyde plywood may further comprise the steps:
(1) with six layers of veneer 11 cross arrangement in length and breadth, lay hot melt adhesive film 12 between veneer 11 and veneer 11 is made plate group 1;
(2) as shown in Figure 2, be divided into following 3 step by step:
1. between two bearing plates 2,, make the hot pressing sheetpile according to bearing plate 2, plate group 1, heat-conducting plate 3, plate group 1, overlapping the banking up of bearing plate 2 orders; Only illustrate among Fig. 2, four laminate groups 1, three layers of heat-conducting plate 3 are arranged.
2. the hot pressing sheetpile is moved on on the end guide rail 5 that sets in advance in the preformer, on the hot pressing sheetpile, place top guide rail 4 then, be forced into 8kg/cm
2After, the screw hole 8 that passes on top guide rail 4, the end guide rail 5 with double threaded screw 6 cooperates with nut 7, and top guide rail 4 is linked together with end guide rail 5 is removably fastening.
3. after hot pressing sheetpile and top guide rail 4, end guide rail 5 integral body being taken off; Move into baker, under 80 ℃ temperature, heated 1 hour.
(3) be cooled to room temperature after, remove top guide rail 4, end guide rail 5 and heat-conducting plate 3, get product.
Embodiment 4
Lay thermoplastic film replaces hot melt adhesive film 12 between veneer 11 and the veneer 11 in step (1), makes plate group 1, and figure slightly;
Step by step 2. in: be forced into 28kg/cm
2After, again top guide rail 4 is linked together with end guide rail 5 is removably fastening.Step by step 3. in: after hot pressing sheetpile and top guide rail 4, end guide rail 5 integral body are taken off; Move into baker, under 280 ℃ temperature, heated 12 hours.All the other steps are as described in the embodiment 3.
A kind of manufacture method of zero formaldehyde multi-layer wood substrates: detailed step as embodiment 1~4 arbitrary as described in, so summary.
Claims (3)
1, the manufacture method of a kind of zero-formaldehyde plywood, multi-layer wood substrates may further comprise the steps:
(1) with veneer cross arrangement in length and breadth, lay does not contain the hot melt adhesive film or the thermoplastic film of formaldehyde composition between veneer and veneer, makes the plate group;
(2) the plate group is through hot-forming;
(3) under the pressurize condition, be cooled to room temperature, get product.
2, the manufacture method of a kind of zero-formaldehyde plywood according to claim 1, multi-layer wood substrates is characterized in that: the plate group is at 8~28kg/cm described in the step (2)
2Under the condition of pressure, 80~280 ℃ of temperature, hot pressing moulding in 1~12 hour in hot-press arrangement.
3, the manufacture method of a kind of zero-formaldehyde plywood according to claim 1, multi-layer wood substrates is characterized in that: described step (2) comprise following 3 step by step:
1. between two bearing plates, according to bearing plate, plate group, heat-conducting plate ... plate group, overlapping the banking up of bearing plate order are made the hot pressing sheetpile, wherein have two laminate groups, one deck heat-conducting plate at least;
2. the hot pressing sheetpile is moved on on the end guide rail that sets in advance in the preformer, on the hot pressing sheetpile, place the top guide rail then, be forced into 8kg/cm
2~28kg/cm
2, with the top guide rail and end guide rail is removably fastening is linked together;
3. with hot pressing sheetpile and top guide rail, after guide rail integral body is taken off at the end, move into baker, under 80 ℃~280 ℃ temperature, heated 1 hour~12 hours;
Described step (3) is: after being cooled to room temperature, remove top guide rail, end guide rail and heat-conducting plate, get product.