CN101041556A - Production method of colorful-substrate emulsifying glass capable of changing patterns along with visual angles - Google Patents
Production method of colorful-substrate emulsifying glass capable of changing patterns along with visual angles Download PDFInfo
- Publication number
- CN101041556A CN101041556A CN 200710048642 CN200710048642A CN101041556A CN 101041556 A CN101041556 A CN 101041556A CN 200710048642 CN200710048642 CN 200710048642 CN 200710048642 A CN200710048642 A CN 200710048642A CN 101041556 A CN101041556 A CN 101041556A
- Authority
- CN
- China
- Prior art keywords
- pattern
- glass
- ink
- dry
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparing method of coloured bottom emulsifying glass changing pattern with transformation of look angle, which comprises the following steps: 1) cleaning colorless transparent flat glass; air drying or drying; 2) printing coloured pattern on one side of flat glass with silk net of pre-designing pattern and coloured epoxide resin anti-septic ink; solidifying; 3) printing the same pattern with silk net on the other side of the flat glass; aligning; adopting antiseptic ink; air drying or drying; 4) washing, air drying or drying the flat glass with pattern on the two sides; putting into oil emulsion vessel; emulsifying; fetching out; putting into clean tank; soaking; 5) shifting out; putting into natrium hydroxydatum solution tank; soaking; fetching out; 6) cleaning the plate glass; removing anti septic ink; retaining coloured epoxide resin ink pattern; cleaning; air drying; drying; getting end product.
Description
Technical field:
The present invention is relevant with the production method of colorful-substrate emulsifying glass, and the production method of the colorful-substrate emulsifying glass of special and energy changing patterns along with visual angles is relevant.
Background technology:
Patent No. CN1544260 provides a kind of various visual angles frosting figured plate glass and production technique thereof, this method is the frosting face that is equipped with on the pros and cons of light surface glass, between each frosting face pattern is the light face, the frosting face mutual dislocation that on frosting face that is provided with on the front and reverse side, is provided with, use the silk screen printing corrosion-resistanting ink that is shaped on pattern in advance on the sheet glass two sides, pattern at two-face printing will misplace, put into then in the frosting treatment solution and soak, soak in the caustic lye of soda of putting into after again treatment solution on glass being disposed, rinse out the anticorrosion glossy black of glass surface, last further flushing is made finished product after drying.Its product look adopts single and owing to printed on both sides pattern mutual dislocation, so need two pattern complementary seal nets, technical difficulty is big, only be fit to produce simple long strip type pattern, once more, the corrosion-resistanting ink on two sides all need wash, so environmental pollution is bigger, the cost that disposes waste liquid is higher.
Summary of the invention:
The objective of the invention is provides a kind of rich color in order to overcome above deficiency, simple, only needs a seal net, and stereoscopic sensation is strong, the production method of the colorful-substrate emulsifying glass of energy changing patterns along with visual angles.
The present invention is achieved in that
The production method of the colorful-substrate emulsifying glass of the present invention's energy changing patterns along with visual angles comprises the steps:
1) dries after colourless transparent plate glass is cleaned or dry;
2) silk screen and the colored corrosion-resistanting ink of Resins, epoxy with pre-designed pattern is printed on multi color pattern on the one side of sheet glass, and solidifies;
3) on the another side of sheet glass with silk screen printing on identical patterns and make it to aim at, the printing-ink corrosion-resistanting ink dries or dries;
4) the figuratum sheet glass of perfecting is cleaned dry or dry after, put into after the container emulsification that fills emulsion taking-up and put into clean water basin and soak;
5) putting into the pond that fills sodium hydroxide solution after the sheet glass after soaking in the clean water basin is shifted out soaks the back and takes out;
6) clean and to remove the corrosion-resistanting ink on the sheet glass and to keep colour epoxy resin corrosion-resistanting ink pattern, clean again, dry or dry after be finished product,
Emulsion is by weight percentage by hydrogen fluoride amine 41-46% in the above-mentioned method, sulfuric acid 17-26%, and water 33-37% forms.
Plate metallic membrane on the face of the finished product Chromatic color pattern after will drying or dry in the above-mentioned method.
The inventive method adopts colour epoxy resin corrosion-resistanting ink and common corrosion-resistanting ink only printing mutual aligned identical patterns on the sheet glass with a seal net on the two sides of sheet glass, rich color, stereoscopic sensation are strong, and pattern can be with visual angle change, and method is simple.
Embodiment:
Embodiment 1:
The production method of the light blue ground patterns glass of present embodiment 1 energy changing patterns along with visual angles comprises the steps:
1,6mm is thick colourless transparent plate glass is cleaned, is dried;
2, will design the silk screen of pattern and light blue bicomponent epoxy resin corrosion-resistanting ink is printed onto the one side (reverse side) and the room temperature of sheet glass with light blue colored corrosion-resistanting ink pattern or is heating and curing;
3, the another side (front) that is printed on the sheet glass of light blue pattern after will solidifying with in the common corrosion-resistanting ink silk screen printing with sheet glass one side (reverse side) identical pattern, and dry, pattern must be aimed at, and can not misplace;
4, the figuratum glass of perfecting is put into put into clean water basin after emulsification pond internal emulsification 3 minutes takes out and soaked 1 minute;
5, soaked glass is moved in the 3% sodium hydroxide solution pond and to soak 10 minutes;
6, soaked glass is taken out, cleans with clear water after washing common corrosion-resistanting ink and keep light blue Resins, epoxy corrosion-resistanting ink with clear water and dry or dry, finished product.
Above-mentioned emulsion is by weight percentage by hydrogen fluoride amine 44%, sulfuric acid 20%, and water 36% is formed.
Light blue bicomponent epoxy resin corrosion-resistanting ink is by weight: filling a prescription is: white epoxy corrosion-resistanting ink 99, and blue color circle epoxy resins corrosion-resistanting ink 1, epoxy hardener (as the T-403 model) 23,
Above-mentioned raw materials mixed be above-mentioned light blue bicomponent epoxy resin corrosion-resistanting ink.
Embodiment 2:
Originally execute example 2 can with the production method of the light blue inferior photolytic silver ground patterns glass of angle changing patterns basic with embodiment 1 with, difference be in dry or dry after the one side plated aluminum film of finished product Chromatic color pattern, light blue inferior photolytic silver ground patterns glass.
Embodiment 3:
The production method of the transparent orange ground patterns glass of present embodiment 3 energy changing patterns along with visual angles comprises the steps:
1,6mm is thick colourless transparent plate glass is cleaned, is dried;
2, will design the silk screen of pattern and one side (reverse side) and the curing that transparent clear look bicomponent epoxy resin corrosion-resistanting ink is printed onto the transparent orange colored pattern sheet glass;
3, be printed on the pattern identical with reverse side in another side (front) silk screen printing of the sheet glass of pattern after will solidifying, and dry, pattern must be aimed at, and can not misplace, and printing-ink adopts common corrosion-resistanting ink on the market;
4, the figuratum glass of perfecting being put into emulsification pond internal emulsification takes out after 5 minutes and puts into clean water basin and soaked 2 minutes;
5, soaked glass is moved in the 3% sodium hydroxide solution pond and to soak 15 minutes;
6, soaked glass is taken out, cleans with clear water after water washes common corrosion-resistanting ink and keeps transparent orange colour circle epoxy resins corrosion-resistanting ink pattern and dry or dry, finished product.
Above-mentioned emulsion is by weight percentage by hydrogen fluoride amine 41%, sulfuric acid 26%, and water 33% is formed.Transparent orange bicomponent epoxy resin corrosion-resistanting ink is filled a prescription by weight and is: transparent orange colour circle epoxy resins 100, epoxy hardener (T-403) 33; Above-mentioned raw materials mixed be above-mentioned transparent orange bicomponent epoxy resin corrosion-resistanting ink.
Embodiment 4:
The orange metal-like that present embodiment 4 can changing patterns along with visual angles and the production method of inferior photolytic silver figured plate glass are basic same with embodiment 3, do not exist together be on the one side that orange pattern is being arranged on the embodiment 3 described finished products, plate translucent stainless steel membrane orange metal-like and inferior photolytic silver figured plate glass.
The foregoing description is that foregoing of the present invention is further described, but this should be interpreted as that the scope of the above-mentioned theme of the present invention only limits to the foregoing description.All technology that realizes based on foregoing all belong to scope of the present invention.
Claims (2)
1, the production method of the colorful-substrate emulsifying glass of energy changing patterns along with visual angles comprises the steps:
1) dries after colourless transparent plate glass is cleaned or dry;
2) silk screen and the colour epoxy resin corrosion-resistanting ink with pre-designed pattern is printed on multi color pattern on the one side of sheet glass, and solidifies;
3) on the another side of sheet glass with silk screen printing on identical patterns and make it to aim at, printing-ink adopts corrosion-resistanting ink, dries or dries;
4) the figuratum sheet glass of perfecting is cleaned dry or dry after, put into after the container emulsification that fills emulsion taking-up and put into clean water basin and soak;
5) putting into the pond that fills sodium hydroxide solution after the sheet glass after soaking in the clean water basin is shifted out soaks the back and takes out;
6) clean and to remove the corrosion-resistanting ink on the sheet glass and to keep colour epoxy resin corrosion-resistanting ink pattern, clean again, dry or dry after be finished product,
Emulsion is by weight percentage by hydrogen fluoride amine 41-46% in the above-mentioned method, sulfuric acid 17-26%, and water 33-37% forms.
2, the production method of the colorful-substrate emulsifying glass of energy changing patterns along with visual angles as claimed in claim 1 is characterized in that plating metallic membrane with oven dry or on the face of the finished product Chromatic color pattern after drying.