CN101024116A - Club-body of golf club and its surface coating method - Google Patents
Club-body of golf club and its surface coating method Download PDFInfo
- Publication number
- CN101024116A CN101024116A CNA2006100076947A CN200610007694A CN101024116A CN 101024116 A CN101024116 A CN 101024116A CN A2006100076947 A CNA2006100076947 A CN A2006100076947A CN 200610007694 A CN200610007694 A CN 200610007694A CN 101024116 A CN101024116 A CN 101024116A
- Authority
- CN
- China
- Prior art keywords
- cermet
- shaft
- rete
- golf clubs
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a golf ball rod body and its surface painting method. The ball rod body includes one nonmetallic plain rod body, one base paint film set, one metal ceramic film, and one protective film. The base paint film set has one primer film coated on the plain rod body. The metal ceramic film material is coated on the base paint film set by vacuum magnetron sputtering method. The protective film is transparent protective paint coated on the metal ceramic film. Sputter on the base paint film set can simplify making procedure, shorten time, and further save cost. In addition the proportion of the metal material and the carbon content can be adjusted to make the rod body appear different colors, increase purchasing wish.
Description
Technical field
The present invention relates to the method for a kind of club shaft and external coating thereof, particularly relate to a kind of shaft and method for coating surface thereof of golf clubs.
Background technology
Along with the raising of national life level, in the middle of the number of being engaged in golf just little by little increases.The consumer is before buying golf clubs, and except considering its function, still whether the color and luster of nationwide examination for graduation qualification gauge rod body is attractive in appearance.With regard to the shaft of present golf clubs, it is made that its material mostly is metal material greatly, mainly is considering of requirement of strength.Because metal material itself with regard to tool metallic luster, therefore, only applies layer protecting film usually on its outer surface, not worn and torn by scratch to protect the surface.In recent years, the shaft made with the carbon fiber material is welcomed by the general public gradually, mainly be because of the carbon fiber lighter weight, and intensity is also quite outstanding, so that can be accepted by popular gradually.
But, because with the made shaft of carbon fiber material, its appearance is to be black, feels that to the people dullness and texture are not good.Therefore, can add the colored paint of other color usually, to present different color and lusters.The practice haply is to apply one deck priming paint earlier on the carbon fiber shaft.Then, apply one deck colored paint again on the surface of this priming paint.Afterwards, stamp pictorial trademark on the surface of this colored paint.At last, on this colored paint, be coated with a transparent protective paint again.For colored paint can closely be attached on the priming paint as far as possible, before being coated with colored paint, must carrying out fine lapping by first outer surface, and make its surface slightly be coarse this priming paint.
Yet with the made shaft of said method, the adhesive force of this colored paint is not high; and may have the problem that applies inequality, add colored paint itself and do not have any intensity, therefore; after the protective paint wearing and tearing were peeled off, then colored paint also can be worn easily and lose color and luster.
As shown in Figure 1; the coating of existing golf clubs and coating process thereof are in body of rod surface primer coating, then; this priming paint is carried out fine lapping; go up the coating colored paint in its surface again, then, utilize the mode of ion evaporation (Ion Vapor Deposition); with one of them metal depositions such as titanium, chromium, aluminium or zirconiums on colored paint; stamp trade mark again, last, then be the last layer protective paint.Existing golf clubs coating is the aforesaid problem of improvement, and this metal level is set between this colored paint and protective paint, utilizes the intensity and the color and luster of metal, protection colored paint, increase metallic luster, and improve its abrasion resistance.Above-mentioned ion evaporation is to belong to physical vapour deposition (PVD) (Physical Vapor Deposition PVD), utilizes arc discharge to produce high heat, makes material (also can be described as target) the fusion evaporation of evaporation and plating in this body of rod surface.
Be not difficult to find from above-mentioned explanation, for existing coating process, exist following several shortcomings:
One, the processing procedure time causes expending of cost than length: because this metal level and light tight, when this metal level plating is on colored paint, the color and luster of colored paint can be covered by this metal level, the color of this colored paint can't display at all, lose the purpose of original use colored paint on the contrary, its processing procedure time also is elongated, and causes the raising of manufacturing cost.
Two, easily produce softening transform: because this ion evaporation mode is to utilize the high-temperature digestion target, plating is on the outer surface of colored paint again, thereby its integrated environment temperature is increased, make the priming paint that originally applied and colored paint because of temperature rise has the phenomenon of softening transform, cause the planarization and the uniformity of integral body to be affected.
Three, the club color and luster is with low uncertainty: owing to only use the color and luster of single kind of metal material as club, therefore, also can only show used metal primary colors, alternative color and luster is less, is difficult to satisfy different consumer demands.
Summary of the invention
The objective of the invention is shaft and method for coating surface thereof, can simplify fabrication steps, to shorten the processing procedure time and to save manufacturing cost for a kind of golf clubs is provided.
Another purpose of the present invention can provide more various metallic luster, increases the color and luster kind of golf clubs, and promotes texture, to satisfy different consumer demands.
In order to achieve the above object, the shaft of golf clubs of the present invention, be secure bond on a bulb, the shaft of this golf comprises the plain body of rod, a base paint film layer group, a cermet rete made from non-metallic material, and a protective film.This base paint film layer group has one and entirely is coated on the lip-deep priming paint rete of this element body of rod, this cermet rete be plating on this base paint film layer group, and for metal material with contain carbon element and aerify that to close the cermet material that forms made.This protective film is the surface that is transparence and is coated on this cermet rete.
The method for coating surface of the shaft of golf clubs of the present invention comprises that one prepares step, a base paint coating step, a cermet plated film step, and a diaphragm coating step.This prepares step is to prepare an elongated rod shape and be the made plain body of rod of non-metallic material, and this element body of rod is ground and polishes.This base paint coating step is a coating paint layer and make it dry sclerosis on this element body of rod, and this base paint coating step has a priming paint coating step, is to form a smooth priming paint rete at this element body of rod surface-coated one priming paint.This cermet plated film step is with the vacuum magnetic-control sputtering method, on the surface of this priming paint rete deposition one with metal material with contain carbon element and aerify and to close the cermet rete that forms.This diaphragm coating step is to apply transparent protective paint on the surface of this cermet rete, to form the protective film that can protect this cermet rete.
Effect of the present invention is to finish after the making of this priming paint rete, and directly this cermet rete of plating saves fabrication steps such as fine lapping, simplifies processing procedure to shorten manufacturing time, reaches the reduction manufacturing cost.See through the ratio of adjusting contained metal material that has of this cermet rete and carbon element amount, make this shaft have more diversified color and luster, when the ratio of metal material is higher, can make this shaft present argenteous metallic luster, when the ratio of carbon element amount is higher, then can make this shaft present steel gray, allow the consumer that more multifarious selection can be arranged, choose the color and luster of oneself liking.
Description of drawings
Fig. 1 is a flow chart, and the coating and the coating process thereof of existing golf clubs is described;
Fig. 2 is a stereogram, and the preferred embodiment of the shaft of golf clubs of the present invention is described, is to combine with a bulb to fix;
Fig. 3 is a profile, and the face coat structure of this preferred embodiment is described;
Fig. 4 is a flow chart, and the preferred embodiment of method for coating surface of the shaft of golf clubs of the present invention is described;
Fig. 5 is an illustrative view, illustrates that this preferred embodiment is to utilize a vacuum magnetic-control sputtering equipment, carries out the magnetron sputtering operation to most ball bar semi-finished product;
Fig. 6 is a schematic top plan view, in order to aid illustration Fig. 5.
The specific embodiment
Be elaborated below by a preferred embodiment and accompanying drawing shaft and method for coating surface thereof to golf clubs of the present invention.
Shown in Fig. 2,3, the preferred embodiment of the shaft 3 of golf clubs of the present invention, be secure bond on a bulb 2, the shaft 3 of this golf clubs comprises a plain body of rod 31, a base paint film layer group 32, a cermet rete 33, and a protective film 34.In this preferred embodiment, this shaft 3 is to be applied on the golf clubs type that belongs to rod, but also can be applied on iron and the push rod.
This element body of rod 31 is to be elongated rod shape or stock tubulose, and made with the non-metallic material of carbon fiber material, but also can be glass fibre, boron fibre, high-intensity engineering plastic, or non-metallic material such as macromolecular material is made.
This base paint film layer group 32 has a priming paint rete 321, and a jaqan rete 322.This priming paint rete 321 is to be transparence also entirely to be coated on the surface of this element body of rod 31.This jaqan rete 322 is the surfaces that are transparence and are coated on this priming paint rete 321, to improve its flatness and brightness, to be preferably the nearly minute surface degree that is promoted to.
These cermet rete 33 plating are on the surface of the jaqan rete 322 of this base paint film layer group 32, and this cermet rete 33 is metal materials and contain carbon element and aerify that to close the cermet material that forms made.In this preferred embodiment, employed metal material is titanium, chromium, iron, nickel or zirconium metal, but also can be the alloy of above-mentioned metal material.The employed carbon element gas that contains then is hydrocarbon.Wherein be comparatively suitable, particularly as methane (CH with the less compound of molecular weight
4) and acetylene (C
2H
2) waiting hydrocarbon, this is because little then its active meeting of molecular weight is bigger, and easily in being combined to the cermet material with metal material.
Aforesaid cermet is to have fused metal and two kinds of materials of hydrocarbon, makes it to have concurrently the advantage of metal and pottery.Its hardness and wear resistance all uses single metal material to come highly, and more can be because of quenching or shock heating and produce embrittlement.Under this shaft 3 long-term uses, still can keep original gloss and be difficult for being worn.Preferably, the thickness of this cermet rete 33 is between 0.1~1 micron (μ m).
In this cermet rete 33, the ratio that metal material and gas include the carbon element amount can be 10: 1, or 1: 10, but also can the between adjustment change.By changing metal material and the ratio that contains the carbon element amount, can derive quite multiple different color and luster, for example, when the ratio that metal material occupied was higher, the color of this cermet rete 33 can be partial to comparatively bright metallic luster, as is silvery white in color.Along with the increase of carbon content, then the color of this cermet rete 33 can transfer dimness gradually to, for example is to be steel gray.
This protective film 34 is to be transparence and to be coated on the surface of this cermet rete 33, can protect this cermet rete 33 to avoid being worn and torn by scratch.Because this protective film 34 is to be transparence; therefore can't block the color that this cermet rete 33 is presented; in other words; the color and luster of this cermet rete 33 is the color and luster of this shaft 3 just; ratio by adjusting metal material and carbon element amount just can make this shaft 3 change and many different color and lusters.
As shown in Figure 4, and cooperate Fig. 3, the preferred embodiment of the method for coating surface of the shaft of golf clubs of the present invention comprises that one prepares step 41, a base paint coating step 42, a cermet plated film step 43, and a diaphragm coating step 44.
This prepares step 41 is to prepare an elongated rod shape and be the made plain body of rod 31 of carbon fiber material, and this element body of rod 31 is ground, polishes, and reaches processing such as corrosion protection, to promote its tack, wherein, grinding, polishing and corrosion protection are had the knack of by being engaged in this skill personage, will not describe in detail at this.In this preferred embodiment, this element body of rod 31 is to make with the carbon fiber material, but also can be glass fibre, boron fibre, high-intensity engineering plastic, or non-metallic material such as macromolecular material is made.
This base paint coating step 4 has a priming paint coating step 421, and a jaqan coating step 422.This priming paint coating step 421 is to apply one deck priming paint and make it dry sclerosis on the surface of this element body of rod 31, and forms a smooth priming paint rete 321.This jaqan coating step 422 is that a protective paint is coated on the surface of this priming paint rete 321, to form a jaqan rete 322, improves the flatness and the brightness of this priming paint rete 321 whereby, preferably, is to present nearly minute surface form.In this preferred embodiment, the mode of dry sclerosis is to utilize the high-temperature baking mode, in regular turn this priming paint rete 321 is dried sclerosis with jaqan rete 322, also can use the mode of ultraviolet ray irradiation.
This cermet plated film step 43 is to utilize vacuum magnetic-control sputtering (Vacuum MagnetronSputtering) method; the plain body of rod 31 that is coated with priming paint and protective paint is carried out sputter coating, make on the surface of this jaqan rete 322 deposition one with metal material with contain carbon element and aerify and close the cermet rete 33 that forms.Available metal material with contain the carbon element gaseous species, ask for an interview preamble explanation, do not repeat them here.
Shown in Fig. 3,5,6, below how explanation utilizes a vacuum magnetic-control sputtering equipment 7 to carry out vacuum magnetic-control sputtering, and this cermet rete 33 is deposited on the surface of this jaqan rete 322.
This vacuum magnetic-control sputtering equipment 7 comprises that a vacuum cavity 71, is communicated with that the traffic cycle 73, the plural number that can be this vacuum cavity 71 in rotate around self axis the unit 72 of bleeding of this vacuum cavity 71, articulate this traffic cycle 73 and contiguous its outer peripheral edges and the mini-roundabout 74, that can rotate voluntarily is arranged on sputter unit 75 on this vacuum cavity 71, reaches one and can import the gas transmission unit 76 of this vacuum cavity 71 with containing carbon element gas.
This unit 72 of bleeding can be extracted the air in this vacuum cavity 71 out, and makes the pressure of this vacuum cavity 71 be lower than an atmospheric pressure.This traffic cycle 73 can utilize its rotation and allow each mini-roundabout 74 be adjacent to this sputter unit 75 in regular turn.Each mini-roundabout 74 can be for being coated with the plain body of rod 31 of this priming paint rete 321 with jaqan rete 322 (below be referred to as club semi-finished product 35) intercalation erectly and having rotated.This sputter unit 75 has a magnetic part 751, a metal targets 752 that attaches on these magnetic part 751 front end faces, and the gas transmission part 753 of an exportable gas.This metal targets 752 is titaniums, can certainly be chromium, iron, nickel, or the zirconium metal one of them is made, but also can be titanium alloy, evanohm, ferroalloy, nickel alloy, or zircaloy one of them is made.
Utilize this unit 72 of bleeding that the air in this vacuum cavity 71 is extracted out, this gas transmission unit 76 also contains the gas of carbon element with suitable flow rate input, can maintain less than 7 * 10 to make a vacuum
-1The low vacuum environment of handkerchief (Pa).When the gas transmission part 753 of this sputter unit 75 is imported gas in this vacuum cavity 71 with suitable flow, and cooperate high-tension use, can produce free charged ion, electronics, and neutral proton (being collectively referred to as the electricity slurry).For avoiding unnecessary chemical reaction, these gas transmission part 753 employed gases are comparatively desirable with inert gas.Because the quality of argon gas (Ar) is higher, and also contain 0.93% argon gas in the air, price is the most cheap, so argon gas is chosen as the gas of input.
This metal targets 752 connected negative poles and pass to negative high voltage (as-300V~-800V), and described club semi-finished product 35 are electrically connected with positive pole, can certainly ground connection.Make to exist potential difference to produce electric field between the two, this electric field is to be used for quickening argon ion to move, and makes it clash into this metal targets that is connected with negative pole 752 surfaces with high speed kinetic energy.During bump, argon ion can carry out the transfer of energy with the titanium atom of this metal targets 752, and makes lip-deep titanium atom be broken away from this metal targets 752 by knocking-on sputter, and flies to towards contiguous club semi-finished product 35.
Because this vacuum cavity 71 has been full of the gas that contains carbon element, titanium atom is understood in the process of sputter and is contained carbon element gas generation reaction chemical combination and become the metal ceramic compound, be attached on the surface of described club semi-finished product 35, so as to forming this cermet rete 33.In this preferred embodiment, the thickness of formed cermet rete 33 is at 0.1~1 μ m.What deserves to be mentioned is that with the cermet rete 33 that the cermet material is made, the simple plated film of single metal that uses of its hardness ratio comes highly, more can protect priming paint rete 321, the jaqan rete 322 of this shaft 3, and the plain body of rod 31 is difficult for being worn and torn by scratch.
In the process of sputter, be see through this traffic cycle 73 with each club semi-finished product 35 in order near this sputter unit 75, and cooperate the rotation of each mini-roundabout 74, can allow the cermet rete 33 that is formed on each club semi-finished product 35 be even distributions.
The main feature of vacuum magnetic-control sputtering technology is to utilize the magnetic part 751 formed magnetic fields of this sputter unit 75, control the motion of the secondary electron that is produced when argon ion clashes into this metal targets 752, electronics is advanced with corkscrew motion, increase the electronic motion route and enlarge its range of movement, reach and improve the collision argon gas to form the chance of argon ion.Because argon ion has increased the relative speed that also improves sputter.
What deserves to be mentioned is, also because the magnetic field effect of this magnetic part 751, can be near this metal targets 752 with electron confinement, and do not remove the described club semi-finished product 35 of percussion, can avoid too high and softening this priming paint rete 321 of club semi-finished product 35 temperature rises.In this preferred embodiment, the temperature of this priming paint rete 321 with jaqan rete 322 can be controlled at below 200 ℃, to prevent its softening transform.Preferably, be that temperature is controlled at below 150 ℃.
Because the progress of coating technique, develop the vacuum magnetic-control sputtering technology of multiple application magnetic control principle gradually, for example cylindrical magnetic control sputter, the dull and stereotyped magnetron sputtering of disc type, the dull and stereotyped magnetron sputtering of microscler formula, and conical magnetron sputtering etc., and above-mentioned magnetron sputtering technique all can be applied in the present invention, should not limit to claim scope of the present invention with this.
Shown in Fig. 3,4, this diaphragm coating step 44 is to apply transparent protective paint on the surface of this cermet rete 33, to form the protective film 34 that can protect this cermet rete 33.In this preferred embodiment, the protective paint that can utilize high-temperature baking to apply makes it dry sclerosis, but also can utilize the ultraviolet ray irradiation.Because this protective film 34 is transparent, so the color and luster of this cermet rete 33 can directly appear, and makes this shaft 3 present metallic luster.In addition, can be before carrying out this diaphragm coating step 44, in the enterprising attaching printing of case of marking on a map of doing business of this cermet rete 33, apply this protective film 34 more earlier, the pictorial trademark of being printed also can protected this protective film 34 be covered.It should be noted, if when this cermet rete 33 is thin, then can present translucent, therefore, also can being attached under this cermet rete 33 with pictorial trademark.
Shown in Fig. 3,6, from the above, the shaft of golf clubs of the present invention and method for coating surface thereof have following several advantages in practical operation:
One, can simplify processing procedure and shortening time, to reduce manufacturing cost:, simplify processing procedure and shortening time whereby, and can reduce manufacturing cost owing to do not need the priming paint rete 321 of this base paint film layer group 32 is carried out fine lapping.
Two, can avoid causing because of temperature rise in the sputter process problem of softening transform: because the present invention utilizes the vacuum magnetic-control sputtering method, see through the magnetic field effect of the magnetic part 751 of this sputter unit 75, make free electronics can be restrained to this metal targets 752 near, and can not remove to clash into this priming paint rete 321 and jaqan rete 322, therefore, its temperature rise amplitude is also little, be unlikely because of temperature rise makes this priming paint rete 321 and with jaqan rete 322 phenomenon of softening transforms takes place, can keep preferable flatness.
Three, the variation of club color and luster is more: can be by the speed and the flow that contains the input of carbon element gas of these metal targets 752 sputters of control, adjust metal material and the ratio that contains carbon element gas, to produce the club of more kinds of different color and lusters, allow the consumer that many selections are arranged, improve the wish of its purchase.
Four, can improve wearability: because this cermet rete 33 is that the cermet compound is made, the hardness of the more single metal material of its hardness is come highly, therefore, can make this shaft 3 have preferable wearability, and then prolongs the useful life of golf clubs.
Five, the external coating layer has preferable tack: because this cermet rete 33 is to deposit with the vacuum magnetic-control sputtering method, utilize argon ion to be quickened and have higher momentum by high voltage electric field, when the bump target, also high momentum can be changed to metallic atom, and be attached on this jaqan rete 322 with higher speed, so preferable tack is arranged, in comparison, the ion evaporation coating method is to clash into target by high thermal evaporation ion, its momentum is above-mentioned relatively, and to be little many, thus its tack more not above-mentioned come good.
Conclude above-mentioned, the shaft of golf clubs of the present invention and method for coating surface thereof, be after the making of finishing this priming paint rete 321 and jaqan rete 322, directly with the vacuum magnetic-control sputtering method, carry out the sputter of cermet compound, on this jaqan rete 322, form this cermet rete 33, and do not need again this priming paint rete 321 to be imposed the fine lapping fabrication steps, simplify fabrication steps whereby, shorten the time of making, and then save manufacturing cost.Simultaneously,, make this cermet rete 33 that preferable tack be arranged, nor can allow these jaqan rete 322 temperature rises too high, can keep its original flatness because be to impose vacuum magnetic-control sputtering.Moreover with the cermet rete 33 that the cermet material is made, its wearability is also used good that the rete of single metal comes.Importantly, the present invention can see through adjust contain the ratio of metal material and carbon element amount, make the cermet rete 33 of this shaft 3 that more kinds of different color and lusters be arranged, when the content of metal material was high than the carbon element amount, the metallic luster of this shaft 3 was to present silvery white; When carbon element amount content is high than metal material, then can make this shaft 3 present comparatively dim steel gray, offer the more various color and luster of consumer and select the color of oneself liking, so can reach purpose of the present invention really.
Claims (22)
1. the shaft of a golf clubs is and a bulb secure bond it is characterized in that:
The shaft of this golf clubs comprise the made plain body of rod of a non-metallic material, a base paint film layer group, a plating in the cermet rete on this base paint film layer group, and one be transparence and be coated on protective film on this cermet film surface; this base paint film layer group has one and entirely is coated on the lip-deep priming paint rete of this element body of rod, and this cermet rete is a metal material and contain carbon element and aerify that to close the cermet material that forms made.
2. the shaft of golf clubs according to claim 1 is characterized in that:
Employed metal material is to be selected from following one of them material in this cermet rete: titanium, chromium, iron, nickel, zirconium, and the alloy of above-mentioned metal material.
3. the shaft of golf clubs according to claim 1 is characterized in that:
This cermet rete is employed to contain the gas that carbon element gas is hydrocarbon.
4. as the shaft of golf clubs as described in the claim 3, it is characterized in that:
The gas of this hydrocarbon is to be selected from following one of them gas: methane, and acetylene.
5. the shaft of golf clubs according to claim 1 is characterized in that:
Employed metal material is to be selected from following one of them material in this cermet rete: titanium, chromium, iron, nickel, zirconium, and the alloy of above-mentioned metal material, the employed carbon element gas that contains of this cermet rete is to be selected from following one of them gas: methane, and acetylene.
6. the shaft of golf clubs according to claim 1 is characterized in that:
The metal material that is contained in this cermet rete and the ratio of carbon element amount are between 10: 1~1: 10.
7. the shaft of golf clubs according to claim 1 is characterized in that:
The thickness of this cermet rete is 0.1~1 micron.
8. the shaft of golf clubs according to claim 1 is characterized in that:
This element body of rod is to be selected from following one of them material: carbon fiber, glass fibre, boron fibre, engineering plastic, macromolecular material are made.
9. the shaft of golf clubs according to claim 1 is characterized in that:
This base paint film layer group also has one and is coated on this primer film laminar surface and is transparent jaqan rete, can improve the flatness and the brightness of this priming paint rete.
10. the method for coating surface of the shaft of a golf clubs is characterized in that:
The method for coating surface of the shaft of this golf clubs comprises that one prepares step; one base paint coating step; one cermet plated film step; an and diaphragm coating step; this prepares step is to prepare an elongated rod shape and be the plain body of rod of non-metallic material; and this element body of rod ground and polish; this base paint coating step is at the surface-coated enamelled coating of this element body of rod and makes it dry sclerosis; this base paint coating step has a priming paint coating step that forms a smooth priming paint rete at this element body of rod surface-coated one priming paint; this cermet plated film step is with the vacuum magnetic-control sputtering method; deposition one is closed the cermet rete that forms with metal material with containing the carbon element aerification on the surface of this priming paint rete, and this diaphragm coating step is to apply transparent protective paint on the surface of this cermet rete.
11. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
In this cermet plated film step, employed metal material is to be selected from following one of them material: titanium, chromium, iron, nickel, zirconium, and the alloy of above-mentioned metal material.
12. the method for coating surface as the shaft of golf clubs as described in the claim 11 is characterized in that:
In this cermet plated film step, employedly contain the gas that carbon element gas is hydrocarbon.
13. the method for coating surface as the shaft of golf clubs as described in the claim 12 is characterized in that:
The gas of described hydrocarbon be selected from following one of them: methane, and acetylene.
14. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
In this cermet plated film step, employed metal material is to be selected from following one of them material: titanium, chromium, iron, nickel, zirconium, and the alloy of above-mentioned metal material, and employed contain carbon element gas be selected from following one of them: methane, and acetylene.
15. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
In this cermet plated film step, the metal material that is contained in this cermet rete and the ratio of carbon element amount are between 10: 1~1: 10.
16. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
Prepare in the step in this, this element body of rod is to be selected from following one of them material: carbon fiber, glass fibre, boron fibre, engineering plastic, and macromolecular material is made.
17. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
In this cermet plated film step, when carrying out vacuum magnetic-control sputtering, be that the priming paint film temperature on this element body of rod is controlled at below 200 ℃, to prevent its softening transform.
18. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
In the priming paint coating step of this base paint coating step, be to utilize the high-temperature baking mode, make the dry sclerosis of this priming paint.
19. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
In the priming paint coating step of this base paint coating step, be to utilize ultraviolet radiation modality, make the dry sclerosis of this priming paint.
20. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
In this cermet plated film step, formed cermet thicknesses of layers is 0.1~1 micron.
21. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
Also having a jaqan coating step after being positioned at this priming paint coating step in this base paint coating step, is to be coated on protective paint on this priming paint rete and to make it dry sclerosis, to increase its flatness and brightness.
22. the method for coating surface as the shaft of golf clubs as described in the claim 10 is characterized in that:
Prepare in the step in this, also this element body of rod is carried out corrosion protection and handle.