CN101020799A - Heavy duty coating capable of curing on wet surface - Google Patents
Heavy duty coating capable of curing on wet surface Download PDFInfo
- Publication number
- CN101020799A CN101020799A CN 200710027190 CN200710027190A CN101020799A CN 101020799 A CN101020799 A CN 101020799A CN 200710027190 CN200710027190 CN 200710027190 CN 200710027190 A CN200710027190 A CN 200710027190A CN 101020799 A CN101020799 A CN 101020799A
- Authority
- CN
- China
- Prior art keywords
- curing
- heavy duty
- component
- wet surface
- coating capable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Component | Title material | Parts by weight |
I | Low molecular weight liquid Resins, epoxy | 100 parts |
Active filler | 15 parts | |
Thickening material | 3 parts | |
Anti-sedimentation agent | 0.8 part | |
The physique filler | 40 parts | |
Defoamer | 0.1 part | |
Dispersion agent | 0.1 part | |
II | The cashew nut modified amine | 24 parts |
The phenolic aldehyde imines | 7 parts | |
Silane coupling agent | 0.8 part | |
Weight proportion | I∶II | 5∶1 |
Apply and curing condition | Cohesive strength (MPa) | Draw back state |
Maintenance is 14 days in the dry-coated air | 7.0 | Disconnected coating |
Wet be coated with in the air maintenance 14 days | 6.3 | Disconnected coating |
Band water was coated with in the air maintenance 14 days | 6.1 | Disconnected coating |
Band water is coated with and promptly immerses 3% salt solution 24 hours and took out in the air maintenance 14 days | 3.2 | The disconnected coating of most measuring points, minority measuring point partial coating is the end of from |
Apply and curing condition | Cohesive strength (MPa) | The disconnection situation |
Maintenance is 14 days in the dry-coated air | 3.4 | Draw back the concrete surface mortar |
Wet be coated with in the air maintenance 14 days | 3.0 | Draw back the concrete surface mortar |
Band water was coated with in the air maintenance 14 days | 2.9 | Draw back the concrete surface mortar |
Band water is coated with and promptly immerses 3% salt solution 24 hours and took out in the air maintenance 14 days | 2.5 | Draw back the part concrete mortar, part is drawn back from coating and concrete interface |
Component | Title material | Parts by weight |
I | Low molecular weight liquid Resins, epoxy | 100 parts |
Active filler | 12 parts | |
Thickening material | 1.5 part | |
Anti-sedimentation agent | 0.4 part | |
The physique filler | 30 parts | |
Defoamer | 0.5 part | |
Dispersion agent | 0.5 part | |
II | The cashew nut modified amine | 10 parts |
The phenolic aldehyde imines | 5 parts | |
Silane coupling agent | 0 part | |
Weight proportion | I∶II | 6∶1 |
Component | Title material | Parts by weight |
I | Low molecular weight liquid Resins, epoxy | 100 parts |
Active filler | 10 parts | |
Thickening material | 1 part | |
Anti-sedimentation agent | 0 part | |
The physique filler | 50 parts | |
Defoamer | 0 part | |
Dispersion agent | 0 part | |
II | The cashew nut modified amine | 40 parts |
The phenolic aldehyde imines | 15 parts | |
Silane coupling agent | 3 parts | |
Weight proportion | I∶II | 4∶1 |
Claims (10)