CN110527338A - The solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind and construction method - Google Patents
The solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind and construction method Download PDFInfo
- Publication number
- CN110527338A CN110527338A CN201910803065.2A CN201910803065A CN110527338A CN 110527338 A CN110527338 A CN 110527338A CN 201910803065 A CN201910803065 A CN 201910803065A CN 110527338 A CN110527338 A CN 110527338A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- curing agent
- solvent
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention proposes a kind of solvent-free high levelling durability anti-corrosive paint of epoxy resin, including component A and B component;The component A is liquid-state epoxy resin, diluent, smooth functional additive, filler, toughener, initiator are obtained through mixing, and the B component is sheet composite curing agent;The smooth functional additive is the compound that silicone powder, aluminium powder and EDMA ethylene dimethacrylate are ground;The sheet composite curing agent is that curing agent is loaded into the composite curing agent that flaky molybdenum disulfide layer obtains.Coating workability of the present invention is good, waterproofness, anti-corrosive properties and the bonding fastness of big coating are improved, overcome that existing solventless epoxy resin coating matter is crisp, sticky, smoothness is poor, it is not easy the problem of constructing, can be widely applied to the waterproof and anticorrosion in the fields such as reservoir dam engineering, subway engineering, Tunnel Engineering, Urban Underground large-caliber drainage pipeline.
Description
Technical field
The present invention relates to building coating fields, apply more particularly to a kind of solvent-free high levelling durability epoxy resin anti-corrosion
Material and construction method.
Background technique
With the fast development of architectural engineering, concrete structure architectural engineering is more and more.As reservoir dam engineering,
The needs such as iron, tunnel, Urban Buried Pipeline Network, treatment tank engineering, sea port dock engineering, overhead road of city, underground parking garage are big
Measure waterproof, corrosion-inhibiting coating processing.For example esters of acrylic acid water-resistant coating is poor, durability is poor for common water paint;Application at present
More is epoxy coating, polyurethane coating.Since polyurethane coating and concrete substrate cementability are poor, epoxy
Resin becomes optimal selection.
Epoxy resin is a kind of high molecular material with linear structure, and per molecule on average contains 2 or 2 or more rings
Oxygroup is mainly synthesized by bisphenol-A and epoxychloropropane, and the hydroxyl and epoxy group contained in structure can be with acid anhydrides, phenolic aldehyde tree
Rouge, polyisocyanates, polyamide etc., which react, obtains the epoxy coating of different structure, different performance.In order to
Good application property, cementability and waterproof durability, usual epoxy resin are solvent based coating.Coating mostly contains volatilization at present
Organic matter (volatile organic compounds, VOC) causes sternly due to containing solvent and large-area construction to environment
The pollution of weight.Wherein, VOC refers under normal pressure, 50 DEG C -260 DEG C of boiling point of various organic compounds.It is most common have benzene, toluene,
Dimethylbenzene, styrene, trichloro ethylene, chloroform, trichloroethanes, diisocyanate (TDI), two isocyanide toluene esters etc..Work as residence
When VOC in room reaches a certain concentration, people can feel headache, Nausea and vomiting, out of strength etc. in the short time, will appear when serious
Twitch, stupor, and the brain, internal organ and nervous system of people can be hurt, cause the serious consequences such as failure of memory.
Nation-building resource-conserving and environment-friendly society at present, building coating is gradually to environmental-friendly and be conducive to
The development in healthy ecology building materials health direction.Solventless epoxy resin coating is not discharged into air during film-forming
Volatile organic matter, ingredient also have preferable working security finally all as film component, will not be because of solvent
It volatilizees and causes security risk, meet environmental requirement, while the drawbacks such as paint film contraction will not be caused because solvent volatilizees, by
The favor in market.As solventless epoxy resin coating was gradually developed in recent years, epoxy coating is to environment
Influence gradually decreases.At present there are mainly two types of the no-solvent type corrosion-resistant epoxy paints developed both at home and abroad: powdery paints and liquid without
Solvent epoxy coating.Powdery paints is made of a kind of with middle relative molecular mass or the solid epoxy of high relative molecular mass
Solid powder coating, liquid solvent-free epoxy coating is to use reactive reactive diluent as solvent, and solvent was solidifying
It will not volatilize in journey, but be cured and react with epoxy resin, eventually become a part in paint film.
If Chinese Patent Application No. 201710442599.8 discloses a kind of solvent free corrosion prevention erosion coating and preparation method thereof,
Its main constituents and weight proportion are as follows: wet process thin,tough silk female powder 5%-8%, reactive diluent 10%-15%, bentonite 8%-
10%, fatty amine curing agent 1.5%-5%, acrylic modified epoxy resin 35%-50%, glass flake 3.5%-5.5%, silicon
The coating of alkane coupling agent 3%-3.5%, thixotropic agent 0.5%-1% and defoaming agent 0.8%-1.5%, the invention have certain anti-corrosion
Property, it can effectively solve the problem that solvent volatility smell and pollution problem, however technical staff is using solventless epoxy resin coating
When, it is not easy working to ask since that there is matter is crisp, sticky, cementability is poor, smoothness is poor for solvent-free epoxy resin material itself
Topic further results in coating and is unable to satisfy the requirement under the harsh media environment such as corrosive liquid.Therefore, it is necessary to develop one
Kind no-solvent type epoxy anticorrosion coating, on the one hand can overcome epoxy coating to be difficult to the shortcomings that constructing, on the other hand exist
Still have adhesive force strong under corrosive liquid media environment, the excellent quality of acid and alkali resistance anticorrosive property, while can satisfy environmental protection and wanting
It asks.
Summary of the invention
For existing solventless epoxy resin coating matter is crisp, sticky, smoothness is poor, it is not easy to construct, anticorrosive property can
The problem of meeting the requirements, the invention proposes a kind of solvent-free high levelling durability anti-corrosive paint of epoxy resin, the present invention is proposed
The solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind and its construction method, are substantially improved waterproofness, the anti-corrosion of coating
Property and bonding fastness, be suitable for the media environments such as corrosive liquid.
To solve the above problems, the invention adopts the following technical scheme:
A kind of solvent-free high levelling durability anti-corrosive paint of epoxy resin, including component A and B component;
The component A is liquid-state epoxy resin, diluent, smooth functional additive, filler, toughener, initiator warp
It is mixed and obtains;
The B component is sheet composite curing agent;
The addition parts by weight of each raw material in the solvent-free high levelling durability anti-corrosive paint of epoxy resin are as follows: the liquid
Epoxy resin is 80~100 parts by weight, and the diluent is 10~20 parts by weight, and the smooth functional additive is 5~10 weights
Part is measured, the filler is 25~55 parts by weight, and the toughener is 0.5~3 parts by weight, and the initiator is 1~5 parts by weight,
The sheet composite curing agent is 15~25 parts by weight;
Wherein, the smooth functional additive is what silicone powder, aluminium powder and EDMA ethylene dimethacrylate were ground
Compound;The sheet composite curing agent is that curing agent is loaded into the composite curing agent that flaky molybdenum disulfide layer obtains, described solid
Agent loading mass is 30-40%.
Preferably, the liquid-state epoxy resin is one of E 51, E 42, E 44.
Preferably, the diluent is glycidyl methacrylate, tetrahydrophthalic acid 2-glycidyl ester, neighbour
One of phthalic acid 2-glycidyl ester.
Preferably, the filler is at least one of talcum powder, mica powder, kaolin, silicon powder.
Preferably, the toughener is that molten processing glass microsphere is soaked by waterglass, and the glass microsphere partial size is less than 20
Micron.
Preferably, the initiator is azodiisobutyronitrile.
Preferably, silicone powder is 65~75 parts by weight in the smooth functional additive, aluminium powder is 30~45 parts by weight, sub-
Ethyl dimethylacrylate is 10~25 parts by weight.
Preferably, the curing agent is acid anhydride type curing agent or amine curing agent.
Preferably, the acid anhydride type curing agent is methyl hexahydro phthalic anhydride, methyltetrahydrophthalic
One of acid anhydride, hexahydro phthalic anhydride, tetrahydrophthalic anhydride;The amine curing agent is polyamide cure
One of agent, fatty amines curing agent, polyethers amine hardener.
The present invention also provides a kind of construction methods of solvent-free high levelling durability anti-corrosive paint of epoxy resin, comprising: will
The component A is uniformly mixed to obtain the solventless epoxy resin coating with the B component;On formation level, using brush,
The mode of roller coating or airless spraying applies the solvent-free high levelling durability anti-corrosive paint of epoxy resin;After construction coating,
It is heat-treated using 50-60 DEG C.
For the problem that existing solventless epoxy resin coating matter is crisp, sticky, smoothness is poor, it is not easy to construct, in consideration of it, this
Invention proposes a kind of solvent-free high levelling durability anti-corrosive paint of epoxy resin, by by silicone powder, aluminium powder and ethylene
Methacrylate grinds to obtain smooth function and service object, assigns the good smooth application property of coating, and compound dispersion
It in coating, after construction coating, is heat-treated using 50-60 DEG C, wherein silicone powder improves the mobility and glossiness of product, drop
Low-friction coefficient.EDMA ethylene dimethacrylate further polymerize with diluent initiation, and silicone powder, aluminium powder strong bond are existed
In coating, the waterproofness, anti-corrosive properties and bonding fastness of coating is substantially improved;Further, molybdenum disulfide is the typical case of tablet
One of represent, molybdenum disulfide is a kind of common solid lubricant, and on the one hand because having layer structure, sulphur between layers is former
Sub- binding force is weaker, is easy to slide and show good sliding effect.By the way that curing agent is loaded in flaky molybdenum disulfide
Interlayer and surface are concentrated in layer direction curing agent, are solidified in microcosmic auxiliary guiding film along in-plane, are prevented the formation in gap,
To form continuous fine and close coating, anti-corrosive properties and waterproofness are improved;By soaking molten processing glass microsphere using waterglass, so that
Not only cementability is good in coating for glass microsphere, and the glass microsphere of ball shape is easy smooth construction, buffer coat impact.
The anti-corrosive paint of epoxy resin overcomes that existing solventless epoxy resin coating matter is crisp, sticky, smoothness is poor, not easy working to ask
Topic.
The present invention proposes a kind of solvent-free high levelling durability anti-corrosive paint of epoxy resin, compared with prior art, dashes forward
Out the characteristics of and excellent effect are:
1, the present invention provides a kind of solvent-free high levelling durability anti-corrosive paint of epoxy resin, including component A and B component,
The component A is liquid-state epoxy resin, diluent, smooth functional additive, filler, toughener, initiator through being mixed
And it obtains.The smooth functional stuffing is the compound that silicone powder, aluminium powder and EDMA ethylene dimethacrylate are ground, compound
Object is scattered in coating, assign the good application property of coating, and construction coating after, using 50-60 DEG C be heat-treated, it is therein
EDMA ethylene dimethacrylate further polymerize with diluent initiation, in the coating by silicone powder, aluminium powder strong bond, substantially
The waterproofness, anti-corrosive properties and bonding fastness for promoting coating, it is crisp, sticky, refreshing to overcome existing solventless epoxy resin coating matter
Slip is poor, is not easy to construct, the defect that anticorrosive property can be met the requirements.
2, B component of the present invention is the sheet composite curing agent for being loaded into flaky molybdenum disulfide layer and obtaining, by by curing agent
It is loaded in interlayer and the surface of flaky molybdenum disulfide, is concentrated in layer direction curing agent, is conducive to guiding film and solidifies along in-plane,
To form continuous fine and close coating, anti-corrosive properties and waterproofness are improved.
3, process of preparing of the present invention is simple and easy, and the coating property of preparation is stablized, and storage stability is good, at low cost
It is honest and clean, it is suitble to large-scale production.
4, coating prepared by the present invention can be widely applied to reservoir dam engineering, subway engineering, Tunnel Engineering, Urban Underground
Large-caliber drainage pipeline and treatment tank engineering, sea port dock engineering and bridge spanning the sea, highway, railway and subway overpass,
The concrete water-proof anti-corrosion of urban skyscraper underground engineering.
Specific embodiment
In the following, the present invention will be further described in detail by way of specific embodiments, but this should not be interpreted as to the present invention
Range be only limitted to example below.Without departing from the idea of the above method of the present invention, according to ordinary skill
The various replacements or change that knowledge and customary means are made, should be included in the scope of the present invention.
Embodiment 1
According to the solvent-free high levelling durability anti-corrosive paint of epoxy resin of the proportions of substance: component A group becomes liquid
Epoxy resin is 51 85 parts by weight of E, and 13 parts by weight of diluent glycidyl methacrylate, smooth functional additive is 8
Parts by weight, 35 parts by weight of filler mica powder, soaking molten processing glass microsphere partial size by waterglass is the toughener 0.5 less than 20 microns
Parts by weight, azodiisobutyronitrile are 5 parts by weight;The smooth functional additive is 68 parts by weight silicone powders, 34 parts by weight aluminium powders
The compound ground with 15 parts by weight EDMA ethylene dimethacrylates.
B component is that the acid anhydride type curing agent methyl hexahydro phthalic anhydride that useful load is 38% is loaded into two sulphur of sheet
Change 23 parts by weight of composite curing agent that molybdenum obtains.
The construction method of solvent-free high levelling durability anti-corrosive paint of epoxy resin in the present invention are as follows: by component A and B component
It is uniformly mixed and obtains the solventless epoxy resin coating.On formation level, the solvent-free height is applied using roller applications
Levelling durability anti-corrosive paint of epoxy resin;After construction coating, spontaneous curing 30min, then using 50 DEG C of hot winds on surface
It is heat-treated 25min, by heat treatment, makes to disperse EDMA ethylene dimethacrylate therein and diluent causes and further gathers
It closes, in the coating by silicone powder, aluminium powder strong bond, the waterproofness, anti-corrosive properties and bonding fastness of coating is substantially improved;Together
When, since curing agent to be loaded in interlayer and the surface of flaky molybdenum disulfide, is concentrated in layer direction with respect to curing agent, be conducive to draw
The film for leading flattening solidifies along in-plane, prevents the formation in gap, so that the continuous fine and close coating of formation, improves anti-corrosive properties and prevent
It is aqueous.
Embodiment 2
According to the solvent-free high levelling durability anti-corrosive paint of epoxy resin of the proportions of each substance: component A group becomes liquid
State epoxy resin E 44 is 100 parts by weight, and diluent tetrahydrophthalic acid 2-glycidyl ester is 10 parts by weight, smooth function
Additive is 10 parts by weight, and filler mica powder is 45 parts by weight, soaks molten processing glass microsphere partial size less than 20 microns by waterglass
3 parts by weight of toughener, azodiisobutyronitrile be 2 parts by weight;The smooth functional additive is 75 parts by weight silicone powders, 32 weights
The compound that amount part aluminium powder and 18 parts by weight EDMA ethylene dimethacrylates are ground.
B component be the polyamide curing agent 650 that useful load is 30% be loaded into flaky molybdenum disulfide interlayer obtain it is compound
18 parts by weight of curing agent.
The construction method of solvent-free high levelling durability anti-corrosive paint of epoxy resin in the present invention are as follows: by component A and B component
It is uniformly mixed and obtains the solventless epoxy resin coating.On formation level, the solvent-free height is applied using roller applications
Levelling durability anti-corrosive paint of epoxy resin;After construction coating, spontaneous curing 30min, then using 55 DEG C of hot winds on surface
It is heat-treated 25min, by heat treatment, makes to disperse EDMA ethylene dimethacrylate therein and diluent causes and further gathers
It closes, in the coating by silicone powder, aluminium powder strong bond, the waterproofness, anti-corrosive properties and bonding fastness of coating is substantially improved;Together
When, since curing agent to be loaded in interlayer and the surface of flaky molybdenum disulfide, is concentrated in layer direction with respect to curing agent, be conducive to draw
The film for leading flattening solidifies along in-plane, prevents the formation in gap, so that the continuous fine and close coating of formation, improves anti-corrosive properties and prevent
It is aqueous.
Embodiment 3
According to the solvent-free high levelling durability anti-corrosive paint of epoxy resin of the proportions of each substance: component A group becomes liquid
State epoxy resin is that E 42 is 95 parts by weight, 14 parts by weight of diluent o-phthalic acid diglycidyl ester, smooth function addition
Agent is 7 parts by weight, and 25 parts by weight of filler mica powder soak molten processing toughener of the glass microsphere partial size less than 20 microns by waterglass
2.5 parts by weight, azodiisobutyronitrile are 1 parts by weight;The smooth functional additive is 72 parts by weight silicone powders, 45 parts by weight aluminium
The compound that powder and 25 parts by weight EDMA ethylene dimethacrylates are ground.
B component is that the amine curing agent polyamide curing agent 650 that useful load is 38% is loaded into flaky molybdenum disulfide interlayer
Obtained 25 parts by weight of composite curing agent.
The construction method of solvent-free high levelling durability anti-corrosive paint of epoxy resin in the present invention are as follows: by component A and B component
It is uniformly mixed and obtains the solventless epoxy resin coating.On formation level, the solvent-free height is applied using roller applications
Levelling durability anti-corrosive paint of epoxy resin;After construction coating, spontaneous curing 30min, then using 50 DEG C of hot winds on surface
It is heat-treated 30min, by heat treatment, makes to disperse EDMA ethylene dimethacrylate therein and diluent causes and further gathers
It closes, in the coating by silicone powder, aluminium powder strong bond, the waterproofness, anti-corrosive properties and bonding fastness of coating is substantially improved;Together
When, since curing agent to be loaded in interlayer and the surface of flaky molybdenum disulfide, is concentrated in layer direction with respect to curing agent, be conducive to draw
The film for leading flattening solidifies along in-plane, prevents the formation in gap, so that the continuous fine and close coating of formation, improves anti-corrosive properties and prevent
It is aqueous.
Embodiment 4
According to the solvent-free high levelling durability anti-corrosive paint of epoxy resin of the proportions of each substance: component A group becomes liquid
State epoxy resin is that E 42 is 95 parts by weight, 14 parts by weight of diluent o-phthalic acid diglycidyl ester, smooth function addition
Agent is 7 parts by weight, and 20 parts by weight of filler talcum powder soak molten processing toughener of the glass microsphere partial size less than 20 microns by waterglass
2.5 parts by weight, azodiisobutyronitrile are 1 parts by weight;The smooth functional additive is 72 parts by weight silicone powders, 45 parts by weight aluminium
The compound that powder and 25 parts by weight EDMA ethylene dimethacrylates are ground.
B component be the polyamide curing agent 650 that useful load is 40% be loaded into flaky molybdenum disulfide interlayer obtain it is compound
18 parts by weight of curing agent.
The construction method of solvent-free high levelling durability anti-corrosive paint of epoxy resin in the present invention are as follows: by component A and B component
It is uniformly mixed and obtains the solventless epoxy resin coating.On formation level, the solvent-free height is applied using roller applications
Levelling durability anti-corrosive paint of epoxy resin;After construction coating, spontaneous curing 30min, then using 60 DEG C of hot winds on surface
It is heat-treated 25min, by heat treatment, makes to disperse EDMA ethylene dimethacrylate therein and diluent causes and further gathers
It closes, in the coating by silicone powder, aluminium powder strong bond, the waterproofness, anti-corrosive properties and bonding fastness of coating is substantially improved;Together
When, since curing agent to be loaded in interlayer and the surface of flaky molybdenum disulfide, is concentrated in layer direction with respect to curing agent, be conducive to draw
The film for leading flattening solidifies along in-plane, prevents the formation in gap, so that the continuous fine and close coating of formation, improves anti-corrosive properties and prevent
It is aqueous.
Embodiment 5
According to the solvent-free high levelling durability anti-corrosive paint of epoxy resin of the proportions of each substance: component A group becomes liquid
State epoxy resin is that E 42 is 94 parts by weight, and diluent tetrahydrophthalic acid 2-glycidyl ester is 20 parts by weight, smooth function
Energy additive is 6 parts by weight, and 52 parts by weight of filler mica powder soak molten processing glass microsphere partial size less than 20 microns by waterglass
3 parts by weight of toughener, azodiisobutyronitrile are 1 parts by weight;The smooth functional additive is 65 parts by weight silicone powders, 35 weight
The compound that part aluminium powder and 25 parts by weight EDMA ethylene dimethacrylates are ground.
B component be the polyamide curing agent 650 that useful load is 40% be loaded into flaky molybdenum disulfide interlayer obtain it is compound
15 parts by weight of curing agent.
The construction method of solvent-free high levelling durability anti-corrosive paint of epoxy resin in the present invention are as follows: by component A and B component
It is uniformly mixed and obtains the solventless epoxy resin coating.On formation level, the solvent-free height is applied using roller applications
Levelling durability anti-corrosive paint of epoxy resin;After construction coating, spontaneous curing 30min, then using 50 DEG C of hot winds on surface
It is heat-treated 35min, by heat treatment, makes to disperse EDMA ethylene dimethacrylate therein and diluent causes and further gathers
It closes, in the coating by silicone powder, aluminium powder strong bond, the waterproofness, anti-corrosive properties and bonding fastness of coating is substantially improved;Together
When, since curing agent to be loaded in interlayer and the surface of flaky molybdenum disulfide, is concentrated in layer direction with respect to curing agent, be conducive to draw
The film for leading flattening solidifies along in-plane, prevents the formation in gap, so that the continuous fine and close coating of formation, improves anti-corrosive properties and prevent
It is aqueous.
Comparative example 1
According to the solvent-free high levelling durability anti-corrosive paint of epoxy resin of the proportions of substance: component A group becomes liquid
Epoxy resin is 51 85 parts by weight of E, 13 parts by weight of diluent glycidyl methacrylate, 35 weight of filler mica powder
Part, soaking molten processing glass microsphere partial size by waterglass is 0.5 parts by weight of toughener less than 20 microns, azodiisobutyronitrile 5
Parts by weight.
B component is that the acid anhydride type curing agent methyl hexahydro phthalic anhydride that useful load is 38% is loaded into two sulphur of sheet
Change 23 parts by weight of composite curing agent that molybdenum obtains.
The construction of coating and embodiment 1 are consistent.Comparative example 1 is not added by silicone powder, aluminium powder and ethylene metering system
Therefore the smooth functional stuffing that acid esters is ground influences the smooth application property of coating, while in heat treatment, without Asia second
Base dimethylacrylate participates in polymerization reaction, and the bonding firmness of coating has an impact, and fails to form silicone powder, aluminium powder securely glues
The coating connect influences waterproofness, anti-corrosive properties.
Comparative example 2
According to the solvent-free high levelling durability anti-corrosive paint of epoxy resin of the proportions of substance: component A group becomes liquid
Epoxy resin is 51 85 parts by weight of E, and 13 parts by weight of diluent glycidyl methacrylate, smooth functional additive is 8
Parts by weight, 35 parts by weight of filler mica powder, soaking molten processing glass microsphere partial size by waterglass is the toughener 0.5 less than 20 microns
Parts by weight, azodiisobutyronitrile are 5 parts by weight;The smooth functional additive is 68 parts by weight silicone powders, 34 parts by weight aluminium powders.
B component is that the acid anhydride type curing agent methyl hexahydro phthalic anhydride that useful load is 38% is loaded into two sulphur of sheet
Change 23 parts by weight of composite curing agent that molybdenum obtains.
The construction of coating and embodiment 1 are consistent.Comparative example 2 has used smooth functional additive, but smooth functional additive
In there is no compound EDMA ethylene dimethacrylate, the smooth application property of coating is preferable, and initial anticorrosion, water resistance are preferable, but
Durability is poor.
Coating in comparative example 1-2 is tested with embodiment 1-5 same procedure, 300 microns of coating layer thickness.
Anticorrosive paint test, coating after heat treatment, prevent 3 days in the coating of 300 μ m-thick of concrete surface brushing, carry out
Test.48h is impregnated in 20% concentrated sulfuric acid solution of normal concentration, is impregnated in the sodium hydroxide solution that normal concentration is 20wt%
72h impregnates 7d in 3wt% sodium chloride solution, tests anticorrosion with coat performance respectively, obtains test data such as table through verification test
Shown in 1.
Table 1:
Claims (10)
1. a kind of solvent-free high levelling durability anti-corrosive paint of epoxy resin, it is characterised in that: including component A and B component;
The component A is liquid-state epoxy resin, diluent, smooth functional additive, filler, toughener, initiator through mixing
It stirs and obtains;
The B component is sheet composite curing agent;
Each raw material adds parts by weight in the solvent-free high levelling durability anti-corrosive paint of epoxy resin are as follows: the liquid epoxy tree
Rouge is 80~100 parts by weight, and the diluent is 10~20 parts by weight, and the smooth functional additive is 5~10 parts by weight, institute
Stating filler is 25~55 parts by weight, and the toughener is 0.5~3 parts by weight, and the initiator is 1~5 parts by weight, the sheet
Composite curing agent is 15~25 parts by weight;
Wherein, the smooth functional additive is ground compound for silicone powder, aluminium powder and EDMA ethylene dimethacrylate
Object;The sheet composite curing agent is that curing agent is loaded into the composite curing agent that flaky molybdenum disulfide layer obtains, the curing agent
Loading mass is 30-40%.
2. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 1, which is characterized in that institute
Stating liquid-state epoxy resin is one of E 51, E 42, E 44.
3. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 1, which is characterized in that institute
Stating diluent, to be that glycidyl methacrylate, tetrahydrophthalic acid 2-glycidyl ester, phthalic acid two shrink sweet
One of grease.
4. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 1, which is characterized in that institute
Stating filler is at least one of talcum powder, mica powder, kaolin, silicon powder.
5. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 1, which is characterized in that institute
Stating toughener is that molten processing glass microsphere is soaked by waterglass, and the glass microsphere partial size is less than 20 microns.
6. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 1, which is characterized in that institute
Stating initiator is azodiisobutyronitrile.
7. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 1, which is characterized in that institute
State that silicone powder in smooth functional additive is 65~75 parts by weight, aluminium powder is 30~45 parts by weight, ethylene methacrylic acid
Ester is 10~25 parts by weight.
8. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 1, which is characterized in that institute
Stating curing agent is acid anhydride type curing agent or amine curing agent.
9. the solvent-free high levelling durability anti-corrosive paint of epoxy resin of one kind according to claim 8, which is characterized in that institute
Stating acid anhydride type curing agent is methyl hexahydro phthalic anhydride, methyl nadic anhydride, hexahydro O-phthalic
One of acid anhydrides, tetrahydrophthalic anhydride;The amine curing agent be polyamide curing agent, fatty amines curing agent,
One of polyethers amine hardener.
10. the construction of solvent-free high levelling durability anti-corrosive paint of epoxy resin described in a kind of any claim of claim 1-9
Method characterized by comprising
The component A is uniformly mixed to obtain the solventless epoxy resin coating with the B component;
On formation level, the solvent-free high levelling durability epoxy is applied by the way of brushing, roller coating or airless spraying
Resin anti-corrosive paint;
After construction coating, it is heat-treated using 50-60 DEG C.