CN100587013C - Damping and air-purifying surface coating and preparation method thereof - Google Patents
Damping and air-purifying surface coating and preparation method thereof Download PDFInfo
- Publication number
- CN100587013C CN100587013C CN200710173295A CN200710173295A CN100587013C CN 100587013 C CN100587013 C CN 100587013C CN 200710173295 A CN200710173295 A CN 200710173295A CN 200710173295 A CN200710173295 A CN 200710173295A CN 100587013 C CN100587013 C CN 100587013C
- Authority
- CN
- China
- Prior art keywords
- component
- air
- dispersion agent
- water
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to humidity controlling and air cleaning coating and the preparation method thereof, and belongs to the building material area technical field. The coating adopts meerschaum powder and nanometer titanium dioxide as the main material, and is combined with industrial chemicals of styrene-acrylate emulsion, calcium carbonate, white titanium pigment, ethylene glycol, dispersant 5040, dispersant H-34, 202 foam breaker, alcohol ester 12, methyl cellulose, and colorant, etc. according to a certain compounding ratio. The process of the invention is simple, the construction is convenient and clean, the invention can be used for wall surfaces, and also surfaces such as ceilings and ceiling slabs, etc. During the construction, the coating can be spray-coated by using a special spray gun, and can also be scraped. Because the coating is aqueous and environmental protecting, toxicity, harm, odor and new pollution do not exist during the manufacture, construction and long term application processes. The invention can not only be used for cleaning indoor air, but also be used for controlling indoor relative humidity, thereby being a surface material with indoor environment regulating function.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of damping and air-purifying surface coating and preparation method thereof.
Background technology
Along with the sustained, stable growth of economy and improving constantly of people's quality of the life, people's health, environmental consciousness are constantly strengthened.Pay close attention to health and at first will pay close attention to indoor environmental quality, the quality of IAQ (indoor air quality) is directly connected to the physiological well-being of human body, so people are to the material of construction demands for higher performance.Towards green functionalization, it is the development trend of domestic and international building materials that the environmental harmony direction develops.Under this background, aspect the inner wall surface material, a kind of surfacing of active demand with coordination indoor environment function.So the present invention a kind ofly both can purify the air of a room, and can regulate the surfacing of indoor relative humidity again.
Summary of the invention
The objective of the invention is to propose a kind of the have damping preferably of well attached ability, intensity and air-purifying surface coating and preparation method thereof.
Damping and air-purifying surface coating that the present invention proposes are main raw material with sepiolite powder, nano titanium oxide, add benzene emulsion and other batching compositions, and the weight percent of its component is:
Weight percentages of components
Water-ground limestone 8-14
Titanium dioxide 14-16
Sepiolite powder 12-18
Nano titanium oxide 1.5-2.5
Benzene emulsion 30-36
Dispersion agent 5040 1.0-1.3
Dispersion agent H-34 0.09-0.15
202 defoamer 1.0-3.0
Ethylene glycol 0.8-1.0
Alcohol ester 12 1.2-1.5
Methylcellulose gum 0.9-1.5
All the other are water,
Its gross weight satisfies 100%.
Among the present invention, can also add tinting material in material, the add-on of tinting material is the 0.07-0.1% of material gross weight, the color of tinting material should select for use can be as far as possible with the color of building wall be same system.
Among the present invention, the sepiolite powder particle diameter is the 60-80 order.
Among the present invention, the nano titanium oxide particle diameter is 30nm-50nm.
The damping that the present invention proposes and the preparation method of air-purifying surface coating, its concrete steps are as follows:
Part by weight by each component, measure each component, earlier sepiolite powder, lime carbonate, titanium dioxide, dispersion agent 5040, ethylene glycol and portion water are mixed, as component A, again benzene emulsion, 202 defoamers, alcohol ester 12, methylcellulose gum and tinting material are mixed, as B component, then nano titanium oxide, dispersion agent H-34 and remainder water are stirred, mix, as component C, again component A and B component are mixed, add component C at last, stir, promptly get desired product.
The matrix material that the present invention proposes has good physicochemical property.Press GB through appropriate authority and detect performance such as following table:
| Title | Conditioned disjunction unit | Performance |
| Surface drying time | Min | 30-45 |
| Water tolerance | 48h | The no bubble in surface, slight crack, obscission |
| Abrasion resistance | 2000 times | Do not have and destroy |
| Adhesion strength | MPa | 0.5-0.58 |
| Wettability power (EMC) | Relative humidity 98%, 10h, room temperature | 42％ |
| Moisture releasing ability (moisture releasing per-cent) | Relative humidity 11%, 10h, room temperature | 30％ |
| The ability that purifies air (purification rate) | 10h | 91％ |
| Shear bonding strength | MPa | 0.5 |
| Tensile strength | MPa | 1.5 |
| Elongation at break | /％ | 25 |
Technology of the present invention is simple, easy construction, and cleaning can be used for metope, also can be used for surfaces such as top ceiling, ceiling board.
The present invention is because the available special spray gun spraying of construction also can be scraped and be smeared, and cost is low.Owing to be water-based environment-friendly,, do not have newly and pollute at making, construction, nontoxic, the odorlessness of prolonged application process.
The present invention both can purify the air of a room, and can regulate indoor relative humidity again, was a kind of surfacing of coordinating the indoor environment function that has.
Embodiment
Embodiment 1: its set of dispense is such as following:
Water-ground limestone 110g
Titanium dioxide 150g
Sepiolite powder 150g
Nano titanium oxide 20g
Benzene emulsion 330g
Dispersion agent 5040 12g
Dispersion agent H-34 1.2g
202 defoamer 20g
Ethylene glycol 9g
Alcohol ester 12 13g
Methylcellulose gum 12g
Water 170g
Tinting material 0.95g
In the above-mentioned raw materials ratio, according to the matrix material that foregoing processing step makes, its performance index are:
Time of drying: 40min
Adhesion strength: 0.54MPa
Other every indexs are ditto described.
Embodiment 2: its set of dispense is such as following:
Water-ground limestone 100g
Titanium dioxide 145g
Sepiolite powder 160g
Nano titanium oxide 25g
Benzene emulsion 350g
Dispersion agent 5040 14g
Dispersion agent H-34 1.5g
202 defoamer 25g
Ethylene glycol 10g
Alcohol ester 12 14g
Methylcellulose gum 10g
Water 145g
Tinting material 0.5g
In the above-mentioned raw materials ratio, according to the matrix material that foregoing processing step makes, its performance index are:
Time of drying: 35min
Adhesion strength: 0.55MPa
Other every indexs are ditto described.
Embodiment 3: its set of dispense is such as following:
Water-ground limestone 90g
Titanium dioxide 155g
Sepiolite powder 170g
Nano titanium oxide 15g
Benzene emulsion 360g
Dispersion agent 5040 13g
Dispersion agent H-34 0.9g
202 defoamer 30g
Ethylene glycol 10g
Alcohol ester 12 14g
Methylcellulose gum 11g
Water 130g
Tinting material 0.9g
In the above-mentioned raw materials ratio, according to the matrix material that foregoing processing step makes, its performance index are:
Time of drying: 30min
Adhesion strength: 0.57MPa
Other every indexs are ditto described.
Claims (3)
1, a kind of damping and air-purifying surface coating is characterized in that with sepiolite powder, nano titanium oxide be main raw material, add benzene emulsion and other batching compositions, and the weight percent of its component is:
Weight percentages of components
Water-ground limestone 8-14
Titanium dioxide 14-16
Sepiolite powder 12-18
Nano titanium oxide 1.5-2.5
Benzene emulsion 30-36
Dispersion agent 5040 1.0-1.3
Dispersion agent H-34 0.09-0.15
202 defoamer 1.0-3.0
Ethylene glycol 0.8-1.0
Alcohol ester 12 1.2-1.5
Methylcellulose gum 0.9-1.5
All the other are water, and its gross weight satisfies 100%;
Wherein: described sepiolite powder particle diameter is the 60-80 order, and described nano titanium oxide particle diameter is 30nm-50nm.
2, damping according to claim 1 and air-purifying surface coating is characterized in that also adding tinting material, and the add-on of tinting material is the 0.07-0.1% of material gross weight.
3, the preparation method of a kind of damping as claimed in claim 2 and air-purifying surface coating is characterized in that concrete steps are as follows:
Part by weight by each component measures each component, earlier sepiolite powder, lime carbonate, titanium dioxide, dispersion agent 5040, ethylene glycol and water is mixed, as component A, again benzene emulsion, 202 defoamers, alcohol ester 12, methylcellulose gum and tinting material are mixed,, then nano titanium oxide, dispersion agent H-34 and water are stirred as B component, mix, as component C, again component A and B component are mixed, add component C at last, stir, promptly get desired product.