CN100577602C - Dry powder ceramic tile binding agent - Google Patents
Dry powder ceramic tile binding agent Download PDFInfo
- Publication number
- CN100577602C CN100577602C CN200710016839A CN200710016839A CN100577602C CN 100577602 C CN100577602 C CN 100577602C CN 200710016839 A CN200710016839 A CN 200710016839A CN 200710016839 A CN200710016839 A CN 200710016839A CN 100577602 C CN100577602 C CN 100577602C
- Authority
- CN
- China
- Prior art keywords
- water
- pieces
- ceramic tile
- intension
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a drying powder ceramic tile , which consists of the following component with the stated molar ratio: 500 pieces of 425# Porland cement, 500 pieces of drying sand to match a grade above 40 items, 2-3 pieces of intension, 1-3 pieces of water-keeping and 3-5 pieces of cement compound; the intension is calcium formate; the water-keeping is methyl cellulose; the cement compound is polyethylene or the subdivided latex powder. Because the cement compound and the water-keeping increase the felting intension during being used so as to make the anti-flow ability and the water-keeping ability for the cement compound enhanced greatly; the decorating effect for the facing brick is much fixed, perfect; the method solves the problem that the decoration is easy to be fallen off; besides, the thickness of the felting sand slurry decreases to 3-4mm from the original 2cm; the device can not only save the material greatly, but also decrease the weight by the over-heavy sand slurry to the building; besides, the device can decrease the labor intension for the worker and make the construction much faster and more high-efficient.
Description
Technical field
The application relates to material of construction, especially relates to the ceramic tile matrix material.
Background technology
Inside and outside of buildings needs matrix material when using the ceramic tile veneer, and the ceramic tile adhesives relevant with the application is the sand-cement slurry (being generally about 2cm) that adopts on-the-spot preparation.This method is that sand and cement field mix are made simple sand-cement slurry, this mortar is coated in preimpregnation or gives the wetting ceramic tile back side, the ceramic tile that scribbles mortar be pressed onto wetting in advance wall () on the face, rap ceramic tile then, have certain planeness to guarantee ceramic tile.Adopt this method bonding, must add fixed bit to the bottom, because this traditional mortar does not possess sag resistance, in construction process, material usage is big, and labour intensity height, efficient are low, and skilled worker's skill level and sense of responsibility is had higher requirement.In addition, also need the different immersions of carrying out certain hour to the porosity of substrate and ceramic tile, mortar also needs with correct ratio, and denseness is mixed, and is time-consuming and loaded down with trivial details.What is more important according to " exterior wall ceramic wall and floor bricks construction and paste standard " requirement (JC126-2000), also has a lot of restrictions to the use of this technology.When pasting large-scale low water absorption ceramic tile, come off easily, construction quality is difficult to guarantee.
Summary of the invention
The application's purpose provides a kind of dry powder ceramic tile binding agent, and traditional adhesive mortar sag resistance is poor to overcome, come off easily during sticking brick, the technical problem of thick coating.
For achieving the above object, dry powder ceramic tile binding agent of the present invention is made up of the raw material of following weight part:
500 parts of 425# silicate cements, 500 parts in grain composition sand (doing husky), hardening accelerator 2-3 part, water-holding agent 1-3 part, tackiness agent 3-5 part.
Described grain composition sand is to be formed by 40-70 order and the common dried sand of the 70-140 purpose mixed by 1: 1;
Above-mentioned hardening accelerator is calcium formiate;
Above-mentioned water-holding agent is methylcellulose gum (MC);
Above-mentioned tackiness agent is polyvinyl alcohol or redispersable latex powder.
Its concrete production method is: carry out various raw-material accurate weighings according to prescription, start mixing machine then, earlier cement is dropped into mixing machine, successively various additives are dropped into mixing machine mixing 2-3 minute again, again the husky mixing machine that drops into of grating was carried out thorough mixing 10 minutes, begin the packing, dry powder ceramic tile binding agent.
During construction, 1, earlier basic unit is handled, require to keep Base Smoothness, clean and moistening; 2, preparation binding agent mortar carries out proportioning by water cement ratio 1: 4 (weight), stirs into required denseness, and leaving standstill thoroughly stirs after 5 minutes again can use; 3, the binding agent that mixes up is put on the ceramic tile back side or the substrate surface that is stuck, firmly presses brick, up to plain, thickness is different because of the brick material, and it is thick to be put on the bottom 3-4mm, and ceramic tile is fixed 15 minutes inward turnings and turn 90 degrees and do not influence cohesiveness.
Application notice of the present invention:
1, the mortar after mixing up should be finished using in 4-6 hour, must not add water after the mortar retrogradation again and use;
2, construction temperature should be more than 5 ℃;
3, guard against damp, waterproof.
Positively effect of the present invention is: because the effect of tackiness agent and water-holding agent has strengthened the cohesive strength when using, the anti-sag performance and the water retention property of this binding agent are improved, make the decorative effect of facing tile more firm, perfect, solved caducous problem, and the thickness that makes adhesive mortar by original 2cm about, be reduced to 3-4mm, both saved lot of materials, alleviated the blocked up weight of bringing to buildings of mortar again, also alleviated working strength of workers, made construction quick more, efficient.
The present invention is through detecting, the main performance index JC/T547-2005 " ceramic wall and floor bricks tackiness agent " that is up to state standards fully, and concrete detected result sees Table 1.
Embodiment
Be that example further specifies enforcement of the present invention below with the specific embodiment.
Accurately take by weighing 425# silicate cement 500kg, grain composition dried husky 500kg, hardening accelerator calcium formiate 3kg, water-holding agent methylcellulose gum (MC) 2kg, adhesive polyethylene alcohol or redispersable latex powder 4kg.Start mixing machine then, earlier cement dropped into mixing machine, successively hardening accelerator, tackiness agent, tackiness agent were gone into the mixing machine mixing 2-3 minute again, the more husky mixing machine that drops into of grating was carried out thorough mixing 10 minutes, begin packing, ceramic tile bond.
Table 1 salient features of the present invention is taken stopgap measures
| Test item | Standard-required | The detected value result |
| Tensile bond strength (Mpa) | ≥0.5 | 0.8 |
| Tensile bond strength after the immersion (Mpa) | ≥0.5 | 0.7 |
| Tensile bond strength after the thermal ageing (Mpa) | ≥0.5 | 0.5 |
| Tensile bond strength behind the freeze-thaw cycle (Mpa) | ≥0.5 | 0.6 |
| Time of repose 20min tensile bond strength (Mpa) | ≥0.5 | 0.5 |
Claims (2)
1, a kind of dry powder ceramic tile binding agent is characterized in that, it is made up of the raw material of following weight part:
500 parts of 425# silicate cements, grain composition are done 500 parts in sand, hardening accelerator 2-3 part, water-holding agent 1-3 part, tackiness agent 3-5 part;
The dried sand of described grain composition is to be formed by 40-70 order and the common dried sand of the 70-140 purpose mixed by 1: 1;
Described hardening accelerator is calcium formiate;
Described water-holding agent is a methylcellulose gum;
Described tackiness agent is polyvinyl alcohol or redispersable latex powder.
2, dry powder ceramic tile binding agent as claimed in claim 1 is characterized in that, described raw material preferred weight part is:
500 parts of 425# silicate cements, grain composition are done 500 parts in sand, 3 parts of hardening accelerator, 2 parts of water-holding agents, 4 parts of tackiness agent.