CN100569909C - Solid barbecue charcoal and method for making thereof - Google Patents
Solid barbecue charcoal and method for making thereof Download PDFInfo
- Publication number
- CN100569909C CN100569909C CNB200710158031XA CN200710158031A CN100569909C CN 100569909 C CN100569909 C CN 100569909C CN B200710158031X A CNB200710158031X A CN B200710158031XA CN 200710158031 A CN200710158031 A CN 200710158031A CN 100569909 C CN100569909 C CN 100569909C
- Authority
- CN
- China
- Prior art keywords
- charcoal
- sawdust
- charing
- wood
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to fuel for burning.Solid barbecue charcoal, its mixture by bamboo sawdust, wood sawdust or bamboo sawdust and wood sawdust is made.Raw material sources side of the present invention is general, the waste and old wood sawdust that reclaims for each factory, bamboo sawdust etc., be treated to solid barbecue charcoal through effective processes, shape is identical with pure bamboo wood or pure solid wood charcoal, because of composition pure, smokeless during burning, combustion time, length and pure bamboo wood or pure solid wood charcoal were suitable, compared with machine-made carbon, like product can prolong 1-1.5 hour combustion time, and volume is little, and cost is low, and composition is that natural fuel is formed, there are not other compositions, heat height, ash content are few, frangibility not when barbecue is dialled charcoal, practical efficient height.Technology of the present invention is simple, the most effective control product performance, and making product can compare favourably with pure natural raw material charcoal.
Description
Technical field:
The present invention relates to fuel, particularly fuel for burning.
Background technology:
Barbecue is a kind of delicious diet that the various countries people like, when making, its fuel charcoal for roasting difference in quality is big, best is pure solid wood or pure bamboo charcoal, but the forest reserves are routed weary at present, and not only material source is limited, and its course of processing also causes waste, the cost height.The present grown just gradually phase, short bamboo charcoal or machine-made carbon replaced, and fire was smelt porose machine-made carbon after machine-made carbon mostly was and adopts sawdust to be pressed into rod, and this kind charcoal cost is low, but volume is big, and combustion time is short.Chinese patent application 200610052446.4 discloses a kind of machine-made carbon, the solid machine-made carbon that adopts bamboo charcoal powder, W-Gum and hydraulic pressure system to form, but the solid machine-made carbon that its technology makes in natural air, be easy to make moist so burn in easily the fracture, it is big that mixture material is made ash content, and combustion time is shorter.
Summary of the invention:
The objective of the invention is to overcome above-mentioned not enough problem, a kind of solid barbecue charcoal is provided, raw material and manpower and materials cost are low, solid, and combustion time is long, exactly likes the solid wood charcoal during barbecue.Its method for making also is provided in addition, simple to operation, make good product performance.
The technical scheme that the present invention is adopted for achieving the above object is: solid barbecue charcoal, its mixture by bamboo sawdust, wood sawdust or bamboo sawdust and wood sawdust is made.
Described its presses 100 by bamboo sawdust and wood sawdust: the 50-100 weight part is formulated.
Described solid barbecue charcoal cross section is square, circle or sexangle.
Described solid barbecue charcoal method for making makes by following step:
The first step, raw material prepare: reclaim the waste and old bamboo sawdust of each factory, wood sawdust or bamboo sawdust and wood sawdust, pulverize the system desired particle size, raw material stoving to moisture content less than 5%;
Second step, system rod: the above-mentioned raw material for preparing is delivered to rod-pressing machine, is squeezed into rod, press length requirement firewood rod cut-out back and collect;
The 3rd step, charing: the firewood rod after the cut-out is transported to and carries out kiln discharge behind the high temperature carbonization in the charcoal kiln, and packing gets final product.
Described charing is the segmented high-temperature charing, is initially 500-600 ℃ of charing 2-4 time, kiln discharge after the extremely complete charing of the 1000-1200 ℃ of charing that heat up then.
Raw material sources side of the present invention is general, the waste and old wood sawdust that reclaims for each factory, bamboo sawdust etc., be treated to solid barbecue charcoal through effective processes, shape is identical with pure bamboo wood or pure solid wood charcoal, because of composition pure, smokeless during burning, combustion time, length and pure bamboo wood or pure solid wood charcoal were suitable, compared with machine-made carbon, like product can prolong 1-1.5 hour combustion time, and volume is little, and cost is low, and composition is that natural fuel is formed, there are not other compositions, heat height, ash content are few, frangibility not when barbecue is dialled charcoal, practical efficient height.Technology of the present invention is simple, the most effective control product performance, and making product can compare favourably with pure natural raw material charcoal.
Description of drawings:
Fig. 1 is a process flow sheet of the present invention.
Fig. 2 is a charcoal for roasting cross-sectional view of the present invention.
Embodiment:
The present invention will be described in detail below in conjunction with specific embodiment, but be not limited to specific embodiment.
Embodiment 1
Produce 100% pure bamboo sawdust solid barbecue charcoal according to technical process shown in Figure 1, concrete grammar is:
The first step, raw material prepare: reclaim the waste and old bamboo sawdust of each factory, pulverize and sieve particle, feed particles is sent in drying roller or the process furnace dries then, enter again cyclonic separator carry out centrifugal dry to moisture content be 3%;
Second step, system rod: the above-mentioned feed particles for preparing is delivered to screw extrusion press, and extruding system rod is made square cross section firewood rod under pressure, presses length requirement firewood rod and cuts off automatically;
The 3rd step, charing: the firewood rod after the cut-out is transported to and carries out charing in the charcoal kiln, and charing is the segmented high-temperature charing, is initially 550 ℃ of charings 2.5 hours, kiln discharge after the extremely complete charing of the 1100 ℃ of charings that heat up then, and graduation packing, metering are put in storage.
Embodiment 2
Produce 100% pure wood sawdust solid barbecue charcoal according to technical process shown in Figure 1, concrete grammar is:
The first step, raw material prepare: reclaim the waste and old wood sawdust of each factory, pulverize and sieve particle, feed particles is sent in drying roller or the process furnace dries then, enter again cyclonic separator carry out centrifugal dry to moisture content be 5%;
Second step, system rod: the above-mentioned feed particles for preparing is delivered to screw extrusion press, and extruding system rod is made circular cross section firewood rod under pressure, presses length requirement firewood rod and cuts off automatically;
The 3rd step, charing: the firewood rod after the cut-out is transported to and carries out charing in the charcoal kiln, and charing is the segmented high-temperature charing, is initially 600 ℃ of 2 times of charing, kiln discharge after 1200 ℃ of charings extremely complete charing in 4 hours that heats up then, and graduation packing, metering are put in storage.
Embodiment 3
Produce bamboo and wood mixing solid barbecue charcoal according to flow process shown in Figure 1,
The first step: prepare bamboo sawdust and wood sawdust according to embodiment 1 and the 2 described raw material methods of preparing;
Second step, system rod: above-mentioned bamboo sawdust for preparing and wood sawdust were mixed by weight 2: 1, mixed feed particles is delivered to screw extrusion press, extruding system rod is made hexagonal transverse cross section firewood rod under 15 kilowatts of electric motor, presses length requirement firewood rod and cuts off automatically;
The 3rd step, charing: the firewood rod after the cut-out is transported to and carries out charing in the charcoal kiln, and charing is the segmented high-temperature charing, is initially 600 ℃ of charings 2 hours, kiln discharge after 1000 ℃ of charings extremely complete charing in 4.5 hours that heats up then, and graduation packing, metering are put in storage.
Embodiment 4
Produce square cross section bamboo and wood mixing solid barbecue charcoal according to embodiment 3 described methods, bamboo sawdust and wood sawdust weight ratio are 1: 1.
Claims (2)
1, the method for making of solid barbecue charcoal is characterized in that: it presses 100 by bamboo sawdust and wood sawdust: the preparation of 50-100 weight part, make as follows:
The first step, raw material prepare: reclaim waste and old bamboo sawdust of each factory and wood sawdust, pulverize the system desired particle size, raw material stoving to moisture content less than 5%;
Second step, system rod: the above-mentioned raw material for preparing is delivered to rod-pressing machine, is squeezed into rod, press length requirement firewood rod cut-out back and collect;
The 3rd step, charing: the firewood rod after the cut-out is transported to and carries out high temperature carbonization in the charcoal kiln, and charing is the segmented high-temperature charing, is initially 500-600 ℃ of charing 2-4 hour, is warming up to 1000-1200 ℃ of charing kiln discharge to the complete charing then, and packing gets final product.
2, the method for making of solid barbecue according to claim 1 is characterized in that: make the solid barbecue charcoal cross section and be square, circle or sexangle.