CN100569692C - Efficient thermal-insulating and anti-cracking daub of crystallized waterproofing - Google Patents
Efficient thermal-insulating and anti-cracking daub of crystallized waterproofing Download PDFInfo
- Publication number
- CN100569692C CN100569692C CNB2007101300200A CN200710130020A CN100569692C CN 100569692 C CN100569692 C CN 100569692C CN B2007101300200 A CNB2007101300200 A CN B2007101300200A CN 200710130020 A CN200710130020 A CN 200710130020A CN 100569692 C CN100569692 C CN 100569692C
- Authority
- CN
- China
- Prior art keywords
- parts
- insulating
- powders
- kilograms
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of efficient thermal-insulating and anti-cracking daub of crystallized waterproofing, it is characterized in that: be mixed into 480~600 liters of heat preserving and insulating materials by per 100 kilograms of rubber powders by rubber powder and heat insulating pellet, described rubber powder is made up of following materials based on weight: 550~625 parts of 425# cement, 175~250 parts of quartz sands, 150~160 parts of water-ground limestones, 85~100 parts of ash calcium powders, 4~7 parts of Mierocrystalline celluloses, 3~5 parts of polypropylene monofilament fibers, 21~29 parts of redispersable latex powders, 13~17 parts of the active masterbatch of cement-base infiltration crystallization.This clay ventilation property, heat-insulating property, fire resistance are good, phenomenon such as be not prone to the crack, chap, come off.
Description
Technical field
The present invention relates to a kind of material of construction, is the building wall material specifically.
Background technology
After at present construction wall is laid bricks and finished, batch scrape one concrete mortar to put down, directly paste the building wall brick then, or carry out the brushing building coating after batch scraping two road building putties.There are the following problems for this body of wall treatment process:
(1) ventilation property is poor, and the inside and outside water vapor of body of wall is assembled inhomogeneous, causes phenomenon of osmosis easily.
(2) the body of wall snappiness is poor, easily causes crack, be full of cracks.
(3) thermal conductivity is big, and summer is not heat insulation, and be not incubated winter.
(4) the thermal conductivity deviation of adjacent materials is excessive, causes the body of wall materials used easily to come off.
Summary of the invention
Purpose of the present invention just is a kind of efficient thermal-insulating and anti-cracking daub of crystallized waterproofing is provided, and has solved the problems referred to above of prior art.
The present invention adopts following technical scheme: a kind of efficient thermal-insulating and anti-cracking daub of crystallized waterproofing, be mixed into 480~600 liters of heat preserving and insulating materials by per 100 kilograms of rubber powders by rubber powder and heat insulating pellet, and described rubber powder is made up of following materials based on weight:
550~625 parts of 425# cement
175~250 parts of quartz sands
150~160 parts of water-ground limestones
85~100 parts of ash calcium powders
4~7 parts of Mierocrystalline celluloses
3~5 parts of polypropylene monofilament fibers
21~29 parts of redispersable latex powders
13~17 parts of the active masterbatch of cement-base infiltration crystallization.
The efficient clay of this crystal type of the present invention water-fast insulation moisture-resistant cracking resistance has following characteristics:
(1) has ventilation property preferably.
(2) thermal conductivity is little, and fire resistance reaches the B1 level, has good heat-proof quality, and heat insulation winter in summer is warming.
(3) can pliable and tough release stress, the wall body slit that having solved expands with heat and contract with cold causes, phenomenon such as chap, come off.
(4) the system synthesis bonding strength is greater than 0.1Mpa, the construction good integrity, and flexible construction, shock resistance is greater than 3 grades.
Embodiment
The invention will be further described below in conjunction with specific embodiment.
Embodiment 1
Adopt 600 kilograms of 425# silicate cements
200 kilograms of quartz sands
155 kilograms of water-ground limestones
90 kilograms of ash calcium powders
5 kilograms of Mierocrystalline celluloses
4 kilograms of polypropylene monofilament fibers
25 kilograms of redispersable latex powders
15 kilograms of the active masterbatch of cement-base infiltration crystallization
5900 liters of heat insulating pellets
The heat insulating pellet adopts polystyrene foam grain.
Embodiment 2
Adopt 560 kilograms of 425# silicate cements
245 kilograms of quartz sands
150 kilograms of water-ground limestones
100 kilograms of ash calcium powders
4 kilograms of Mierocrystalline celluloses
5 kilograms of polypropylene monofilament fibers
28.5 kilograms of redispersable latex powders
13.5 kilograms of the active masterbatch of cement-base infiltration crystallization
6600 liters of heat insulating pellets
The heat insulating pellet can adopt polystyrene foam grain.
Embodiment 3
Adopt 620 kilograms of 425# silicate cements
180 kilograms of quartz sands
160 kilograms of water-ground limestones
85 kilograms of ash calcium powders
7 kilograms of Mierocrystalline celluloses
3 kilograms of polypropylene monofilament fibers
21.5 kilograms of redispersable latex powders
16.5 kilograms of the active masterbatch of cement-base infiltration crystallization
5300 liters of heat insulating pellets
The heat insulating pellet can adopt polystyrene foam grain.
Experimental example
As sample, test its physicals by the JG158-2004 standard with the clay among the embodiment 1, it the results are shown in Table 1
Table 1 is pressed the main performance index of JG JG158-2004 test
Project | Unit | Index | Detected result | Individual event is judged |
Wet apparent density | Kg/m 3 | ≤420 | 345 | Meet |
Do apparent density | Kg/m 3 | 180-250 | 218 | Meet |
Thermal conductivity | W/(m·k) | ≤0.060 | 0.050 | Meet |
Heat storage coefficient | W/(m 2·k) | ≥0.95 | 1.1 | Meet |
Ultimate compression strength | kpa | ≥200 | 315 | Meet |
Pressure is cut cohesive strength | kpa | ≥50 | 81 | Meet |
Linear shrinkage | % | ≤0.30 | 0.23 | Meet |
Coefficient of softening | ≥0.5 | 0.8 | Meet | |
Flame retardancy | The B1 level | The B1 level | Meet |
Measure snappiness according to JG149-2003, to detect its ventilation property, the results are shown in Table 2 according to the wet flow density of GB/T17146-1997 standard test water vapor
Table 2 snappiness and ventilation property test
Project | Standard | Requirement | Detected result | The individual event conclusion |
Snappiness (ultimate compression strength/folding strength) | JG149-2003 | ≤3.0 | 2.6 | Qualified |
The water vapor flow density that wets | GB/T17146-1997 | >0.85g/(m 2·h) | 2.2 | Qualified |
Claims (1)
1, a kind of efficient thermal-insulating and anti-cracking daub of crystallized waterproofing, it is characterized in that: be mixed into 480~600 liters of heat preserving and insulating materials by per 100 kilograms of rubber powders by rubber powder and heat insulating pellet, described heat insulating pellet is a polystyrene foam grain, and described rubber powder is made up of following materials based on weight:
550~625 parts of 425# cement,
175~250 parts of quartz sands,
150~160 parts of water-ground limestones,
85~100 parts of ash calcium powders,
4~7 parts of Mierocrystalline celluloses,
3~5 parts of polypropylene monofilament fibers,
21~29 parts of redispersable latex powders,
13~17 parts of the active masterbatch of cement-base infiltration crystallization.