CN100567439C - 聚硫密封胶溶解剂 - Google Patents
聚硫密封胶溶解剂 Download PDFInfo
- Publication number
- CN100567439C CN100567439C CNB2007101581562A CN200710158156A CN100567439C CN 100567439 C CN100567439 C CN 100567439C CN B2007101581562 A CNB2007101581562 A CN B2007101581562A CN 200710158156 A CN200710158156 A CN 200710158156A CN 100567439 C CN100567439 C CN 100567439C
- Authority
- CN
- China
- Prior art keywords
- polysulfur
- dissolving agent
- sealing gum
- ethyl acetate
- dimethylbenzene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
聚硫密封胶溶解剂,是聚硫密封胶的溶解剂,解决聚硫密封胶在航空产品上涂刷后固化出现气泡和窝孔的质量缺陷;聚硫密封胶溶解剂,其成份按重量份为: 二甲苯20%、乙酸丁酯60%、乙酸乙酯20%、聚丙烯酸树脂为以上三种成份总量的0.5%;其配制方法:是在常温条件下,按上述成份称量后,先将二甲苯、甲苯和乙酸乙脂混合均匀再加入聚丙烯酸树脂,再使用1500~2000转/分的高速分散机分散30-50分钟;其优点是聚硫密封胶涂刷在航空产品上,固化后表面消除了气泡及窝孔等质量缺陷。
Description
技术领域:
本发明是用于聚硫密封胶的溶解剂。
背景技术:
聚硫密封胶是目前在航空产品中使用较广泛的密封胶品种,用于整体油箱、密封舱的制造,以及产品的口盖和螺、铆接接头等部位,技术规范要求在每平方分米中不能超过4个气泡合格,使用中常用乙酸乙酯单一溶解剂,在聚硫密封胶固化后因表面出现气泡及窝孔等不符合技术规范要求,长期以来一直让步使用。
发明内容:
本发明的目的是提供一种使聚硫密封胶涂刷使用后固化后消除表面气泡及窝孔等质量缺陷的聚硫密封胶溶解剂;本发明的目的是通过下述的技术方案实现的:聚硫密封胶溶解剂,其成份按重量份为:二甲苯20%、乙酸丁酯60%、乙酸乙酯20%、聚丙烯酸树脂为以上三种成份总量的0.5%;其配制方法:是在常温条件下,按上述成份称量后,先将二甲苯、乙酸丁酯和乙酸乙脂混合均匀再加入聚丙烯酸树脂,再使用1500~2000转/分的高速分散机分散30-50分钟。
聚硫密封胶溶解剂使用说明:按100重量份的聚硫密封胶加入80-100重量份的聚硫密封胶溶解剂,混合均匀即可使用。
本发明创造的优点:聚硫密封胶溶解剂,采用了对聚硫橡胶溶解性良好的苯系溶剂和挥发性好的酯类溶剂为主体,配合微量聚丙烯酸树脂,消除了聚硫密封胶涂刷固化后表面出现的气泡以及窝孔等质量缺陷,使长期存在的质量问题得到了解决。
具体实施方式:
聚硫密封胶溶解剂,其成份按重量份为:二甲苯20%、乙酸丁酯60%、乙酸乙酯20%、聚丙烯酸树脂为以上三种成份总量的0.5%;其配制方法:是在常温条件下,按上述成份称量后,先将二甲苯、乙酸丁酯和乙酸乙脂混合均匀再加入聚丙烯酸树脂,再使用1500~2000转/分的高速分散机分散30-50分钟。将聚硫密封胶溶解剂,80-100重量份加入到100重量份的聚硫密封胶中充分混合均匀,便可以进行密封涂刷。根据上述配方及配制方法实验数据如下:实验一:在每平方分米中有1个气泡;实验二:在每平方分米中有1个气泡;实验三:在每平方分米中无气泡;实验四:在每平方分米中无气泡;实验五:在每平方分米中有2个气泡;实验六:在每平方分米中无气泡;其结果符合技术规范要求,并已在航空产品上的整体油箱、密封舱的内表面涂刷使用,并在航空产品口盖边缘及需要密封的螺栓、螺帽处,铆钉铆接头处涂刷,固化后表面气泡个数均满足技术规范要求。
Claims (1)
1、聚硫密封胶溶解剂,其成份按重量份为:二甲苯20%、乙酸丁酯60%、乙酸乙酯20%、聚丙烯酸树脂为以上三种成份总量的0.5%;其配制方法:是在常温条件下,按上述成份称量后,先将二甲苯、乙酸丁酯和乙酸乙脂混合均匀再加入聚丙烯酸树脂,再使用1500~2000转/分的高速分散机分散30-50分钟。