CN100556613C - A kind of heat forming technology with automobile stabilizer bar of complex end - Google Patents
A kind of heat forming technology with automobile stabilizer bar of complex end Download PDFInfo
- Publication number
- CN100556613C CN100556613C CNB2006100286095A CN200610028609A CN100556613C CN 100556613 C CN100556613 C CN 100556613C CN B2006100286095 A CNB2006100286095 A CN B2006100286095A CN 200610028609 A CN200610028609 A CN 200610028609A CN 100556613 C CN100556613 C CN 100556613C
- Authority
- CN
- China
- Prior art keywords
- bar
- termination
- carry out
- forming
- automobile stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of forming technology, be characterized in, comprising: a, at first according to the selected raw material of designing requirement with automobile stabilizer bar of complex end; B, according to designing requirement to selected raw material blanking, form bar; C, prebended in the termination; D, to the termination fulling punching after prebending; E, in forming machine, carry out the stabiliser bar hot forming; F, stabiliser bar quenching to being shaped; G, in tempering furnace, carry out tempering; H, the product after the tempering is carried out cold sizing; I, carry out bead; J, carry out powder coating at last, form final products.Has the advantage that operation is few, production efficiency is high, method is simple, stabiliser bar termination intensity is improved.
Description
Technical field
The present invention relates to a kind of heat forming technology with automobile stabilizer bar of complex end.
Background technology
Automobile stabilizer bar is in manufacture process, because the shape of its termination is special, as shown in Figure 1, tip bend not only occurs in the plane, but produces the first angle [alpha] α and the second angle beta β at the space both direction, as Fig. 2, shown in Figure 3.Therefore the manufacturing process of automobile stabilizer bar is generally as shown in Figure 4: blanking → termination fulling punching → hot forming → quenching → tempering → termination partial plastic forming → cold sizing → shot-peening → coating, wherein the formation of termination needs twice hot forming.
Because in the hot forming operation, need whole heating, the stabiliser bar termination also obtains high temperature accordingly, in the case, if in first angle [alpha] as shown in Figure 2 crooked termination, then the hole is easy to deform, and causes product rejection.Therefore, usually the formation of tip angle is to adopt special equipment to realize, it is not crooked promptly to keep the termination in the hot forming operation, after tempering is finished, local heat is carried out in the stabiliser bar termination, and then with special equipment with tip bend be shaped (as Fig. 3).
There is following shortcoming in above-mentioned technology:
1,,, cause the hardness of end portion to reduce so need secondary forming after the stabiliser bar hot forming because the stabiliser bar tip angle can't once-forming;
2, need additionally acquire special equipment, make cost of investment strengthen;
3, secondary forming causes operation to increase, and production efficiency reduces;
Summary of the invention
The present invention is the heat forming technology of a kind of automobile stabilizer bar that provides in order to overcome the above-mentioned shortcoming that prior art exists, and this heat forming technology step is simple, production efficiency is high, and, stabiliser bar termination intensity height.
The technical scheme that the present invention takes is: a kind of forming technology with automobile stabilizer bar of complex end, it is characterized in that, and comprising:
A, at first according to the selected raw material of designing requirement;
B, according to designing requirement to selected raw material blanking, form bar;
C, prebended in the termination;
D, to the termination fulling punching after prebending;
E, in forming machine, carry out the stabiliser bar hot forming;
F, stabiliser bar quenching to being shaped;
G, in tempering furnace, carry out tempering;
H, the product after the tempering is carried out cold sizing;
I, carry out bead;
J, carry out powder coating at last, form final products.
Above-mentioned a kind of forming technology with automobile stabilizer bar of complex end, wherein, the described termination step that prebends refers to: before the fulling punching, earlier the bar two ends are bent to required first angle [alpha] in advance on request in hydraulic press.
Above-mentioned a kind of forming technology with automobile stabilizer bar of complex end, wherein, described hot forming operation is meant whole bar is heated to 900 ℃～1000 ℃, stabiliser bar shape once-forming in hot former then, simultaneously, the stabiliser bar termination also is bent to desired second angle beta thereupon together; In conjunction with the angle that step produced that prebends, form stabiliser bar termination by designing requirement.
Above-mentioned a kind of forming technology with automobile stabilizer bar of complex end, wherein, the temperature of described hardening media is 40 ℃～90 ℃.
Above-mentioned a kind of forming technology with automobile stabilizer bar of complex end, wherein, described hardening media is an oil.
Above-mentioned a kind of forming technology with automobile stabilizer bar of complex end, wherein, described temperature is 400 ℃～550 ℃.
Above-mentioned a kind of forming technology with automobile stabilizer bar of complex end, wherein, described tempering time is between 30 minutes～1 hour.
Above-mentioned a kind of forming technology with automobile stabilizer bar of complex end, wherein, described raw material are real core bar.
Because the present invention has adopted above technical scheme, the angle on first plane that is shaped has in advance solved the problem that a plurality of angles of termination in the hot forming operation can't once-forming, and it is compared with the technology of prior art, have following advantage:
1, in the hot forming operation, the stabiliser bar termination also is heated, finish shaping after, quenched with stabiliser bar, so stabiliser bar termination intensity height;
2, need not to acquire again special equipment;
Though 3 operations that need a step termination to prebend, compared with the above-mentioned technology that needs secondary partial plastic forming operation, the efficient of this technology is obviously than higher;
In the 4 hot forming operations, because the aperture to not being stressed, so Kong Buhui deforms, has guaranteed product quality.
Description of drawings
Concrete characteristic performance of the present invention is further described by embodiment and accompanying drawing thereof once.
Fig. 1 is the structural representation of stabiliser bar termination.
Fig. 2 is the crooked schematic diagram of first angle [alpha] in the stabiliser bar end machining process.
Fig. 3 is the crooked schematic diagram of second angle beta in the stabiliser bar end machining process.
Fig. 4 is prior art stabiliser bar processing process figure.
Fig. 5 is stabiliser bar processing process figure of the present invention.
Fig. 6 is the prebend process schematic diagram of step of termination in the stabiliser bar end machining process of the present invention, and wherein, a is the structural representation of bar; B is the structural representation that the head with this bar prebends and is shaped.
Fig. 7 is the structural representation after the fulling punching of stabiliser bar of the present invention termination.
Fig. 8 is the right view of Fig. 7.
The specific embodiment
See also Fig. 5.The forming technology of automobile stabilizer bar of the present invention comprises: a, at first according to the selected raw material of designing requirement;
B, according to designing requirement to selected raw material blanking, form bar;
C, prebended in the termination; The described termination step that prebends refers to: before the fulling punching, bend to required angle by the first plain bending angle requirement with the bar two ends are local in advance earlier, as shown in Figure 6.Fig. 6 is the prebend process schematic diagram of step of termination in the stabiliser bar end machining process of the present invention, and wherein, a is the structural representation of bar; B is the structural representation that the head with this bar prebends and is shaped.When guaranteeing the fulling punching, the material behind the fulling can be full of whole stabiliser bar termination mold cavity;
D, to the termination fulling punching after prebending, as Fig. 7, shown in Figure 8;
E, in forming machine, carry out the stabiliser bar hot forming; Described hot forming operation is meant whole bar is heated to 900 ℃～1000 ℃, then stabiliser bar shape once-forming in hot former.In this hot forming operation, the termination of bar also is bent to desired second angle beta thereupon together, cooperates referring to Fig. 3.In conjunction with prebending the angle that step produced, form stabiliser bar termination, as shown in Figure 1 again by designing requirement.Drop into subsequently and carry out Quenching Treatment in the hardening media;
F, stabiliser bar quenching to being shaped; Described hardening media is an oil, and the temperature of this hardening media is 40 ℃～90 ℃;
G, carry out tempering in tempering furnace, tempering is exactly at a certain temperature, and the quenching rear stabilizer bar is carried out a heat treatment again, to obtain stable tissue and intensity.This temperature is controlled to be 400 ℃～550 ℃, tempering time between 30 minutes～1 hour,
H, the product after the tempering is carried out cold sizing;
I, carry out bead
J, carry out powder coating at last, form final products.
Further specify feature of the present invention and performance below in conjunction with several specific embodiments.
Embodiment one:
Selecting diameter is the real core bar of 20mm, and by the designing requirement blanking, forms bar.
Crooked in hydraulic press in advance to the termination, two ends, form first angle [alpha], when guaranteeing the fulling punching, the material behind the fulling can be full of whole stabiliser bar termination mold cavity.Then to the termination fulling punching after prebending.
Again whole bar is heated to 900 ℃, once-forming in hot former.In this hot forming operation, bar is formed the stabiliser bar shape on request, its termination also is bent to desired second angle beta thereupon together; In conjunction with prebending the angle that step produced, form stabiliser bar termination again by designing requirement.
Drop into subsequently and carry out Quenching Treatment in the hardening media.Hardening media is selected oil, and the temperature of hardening media is chosen as 40 ℃.Carry out tempering then in tempering furnace, this temperature is controlled to be 450 ℃, and tempering time is about 1 hour.Again the product after the tempering is carried out cold sizing; Carry out bead; Carry out powder coating at last, form final products.
Embodiment two;
Selecting diameter is the real core bar of 22mm, and by the designing requirement blanking, forms bar.
Crooked in hydraulic press in advance to the termination, two ends, when guaranteeing the fulling punching, the material behind the fulling can be full of whole stabiliser bar termination mold cavity.To the termination fulling punching after prebending.
Again whole bar is heated to 1000 ℃, then once-forming in special-purpose hot former.In this hot forming operation, its termination also is bent to desired second angle beta thereupon together; In conjunction with prebending the angle that step produced, form stabiliser bar termination again by designing requirement.
Drop into subsequently and carry out Quenching Treatment in the hardening media; Hardening media is selected oil, and the temperature of hardening media is chosen as 90 ℃.Carry out tempering then in tempering furnace, this temperature is controlled to be 500 ℃, and tempering time is about 45 minutes.Again the product after the tempering is carried out cold sizing; Carry out bead; Carry out powder coating at last, form final products.
Embodiment three:
Selecting diameter is the real core bar of 20mm, and by the designing requirement blanking, forms bar.
Crooked in hydraulic press in advance to the termination, two ends, when guaranteeing the fulling punching, the material behind the fulling can be full of whole stabiliser bar termination mold cavity.To the termination fulling punching after prebending.Whole bar is heated to 900 ℃, then once-forming in special-purpose hot former.In this hot forming operation, its termination also is bent to desired second angle beta thereupon together; In conjunction with prebending the angle that step produced, form stabiliser bar termination again by designing requirement.
Drop into subsequently and carry out Quenching Treatment in the hardening media; Hardening media is selected oil, and the temperature of hardening media is chosen as 85 ℃.Carry out tempering then in tempering furnace, this temperature is controlled to be 550 ℃, and tempering time is about 30 minutes.Again the product after the tempering is carried out cold sizing; Carry out bead; Carry out powder coating at last, form final products.
The present invention is owing to adopt: in the fulling punching prebended in the termination, and the two ends of bar is respectively crooked To the first required angle requirement, in hot former, be shaped again then, form second angle, make steady Desired all angles of product design have been satisfied in the fixed pole termination. Therefore, the technique effect of the present invention's generation is Significantly:
1, operation is few, the production efficiency height,
Although 2 operations that need a step termination to prebend need the secondary part compared with prior art The technology of forming process, method is simple;
3, in the hot forming operation, because the aperture to not being stressed, so Kong Buhui deforms, has guaranteed Product quality.
4, finished product stabilizer bar end intensity improves.
Claims (8)
1, a kind of forming technology with automobile stabilizer bar of complex end is characterized in that, comprising:
A, at first according to the selected raw material of designing requirement;
B, according to designing requirement to selected raw material blanking, form bar;
C, prebended in the termination;
D, to the termination fulling punching after prebending;
E, in forming machine, carry out the stabiliser bar hot forming;
F, stabiliser bar quenching to being shaped;
G, in tempering furnace, carry out tempering;
H, the product after the tempering is carried out cold sizing;
I, carry out bead
J, carry out powder coating at last, form final products.
2, a kind of forming technology with automobile stabilizer bar of complex end according to claim 1 is characterized in that, the described termination step that prebends refers to: before the fulling punching, earlier the bar two ends are bent to required first angle [alpha] in advance on request.
3, a kind of forming technology according to claim 1 with automobile stabilizer bar of complex end, it is characterized in that, described hot forming operation is meant whole bar is heated to 900 ℃～1000 ℃, once-forming stabiliser bar shape in hot former then, simultaneously, the stabiliser bar termination also is bent to desired second angle beta thereupon together; In conjunction with the angle that step produced that prebends, form stabiliser bar termination by designing requirement.
4, a kind of forming technology with automobile stabilizer bar of complex end according to claim 1 is characterized in that, the temperature of described hardening media is 40 ℃～90 ℃.
5, a kind of forming technology with automobile stabilizer bar of complex end according to claim 1 is characterized in that, described hardening media is an oil.
6, a kind of forming technology with automobile stabilizer bar of complex end according to claim 1 is characterized in that, described temperature is 400 ℃～550 ℃.
7, a kind of forming technology with automobile stabilizer bar of complex end according to claim 1 is characterized in that, described tempering time is between 30 minutes～1 hour.
8, a kind of forming technology with automobile stabilizer bar of complex end according to claim 1 is characterized in that, described raw material are real core bar.