CN100551788C - 双向拉伸聚丙烯易退包收缩烟用薄膜 - Google Patents
双向拉伸聚丙烯易退包收缩烟用薄膜 Download PDFInfo
- Publication number
- CN100551788C CN100551788C CNB2008100200093A CN200810020009A CN100551788C CN 100551788 C CN100551788 C CN 100551788C CN B2008100200093 A CNB2008100200093 A CN B2008100200093A CN 200810020009 A CN200810020009 A CN 200810020009A CN 100551788 C CN100551788 C CN 100551788C
- Authority
- CN
- China
- Prior art keywords
- base material
- polypropylene
- total weight
- polypropylene copolymer
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种双向拉伸聚丙烯易退包收缩烟用薄膜,分为上中下三层结构,在上表层中加入占二元聚丙烯共聚物基层材料总重量1~3%Mw≥100000的高分子硅酮作为爽滑剂和0.1~0.5%的交联丙烯酸甲酯作为防粘剂;在中间层中加入占聚丙烯基层材料总重量10~30%的氢化石油树脂作为增挺剂和0.2~1.0%的烷基(C14-18)双(2-羟乙基)胺作为抗静电剂;在下表层中加入占三元聚丙烯共聚物基层材料总重量1~3%Mw≥100000的高分子硅酮作为爽滑剂和0.1~0.5%的交联丙烯酸甲酯作为防粘剂。本发明内摩擦小,挺度和抗静电性能好。能使烟包很容易地从薄膜中退出。
Description
技术领域
本发明涉及一种烟用薄膜,尤其是涉及一种双向拉伸聚丙烯易退包收缩烟用薄膜。属于包装材料技术领域。
背景技术
烟用薄膜一直是双向拉伸聚丙烯产品中的高端产品。由于烟机的包装速度很快,对烟用薄膜的要求很高。薄膜要有:外层良好的爽滑性能、较高的收缩率、好的光学性能、好的适应各种烟机的能力。随着人们生活水平的提高,人们更加重视产品的外包装,包装产业的新技术也在不断进步,现在的烟用卡纸上大多采用了环氧树脂上光、镭射卡纸、复膜卡纸等技术来增加美观,而之前用的烟用薄膜内摩擦都比较大,加之上述卡纸和收缩膜包装后有吸附效应,烟包很难从薄膜中退出,给人们使用带来不便。
发明内容
本发明的目的在于克服上述不足,提供一种内摩擦很小(≤0.13N/m)的双向拉伸聚丙烯易退包收缩烟用薄膜。
本发明的目的是这样实现的:一种双向拉伸聚丙烯易退包收缩烟用薄膜,分为上表层、中间层和下表层三层结构,上表层是以二元聚丙烯共聚物为基层材料,中间层是以聚丙烯为基层材料,下表层是以三元聚丙烯共聚物为基层材料,其特征在于:
在上表层二元聚丙烯共聚物基层材料中加入占二元聚丙烯共聚物基层材料总重量1~3%的高分子硅酮(Mw≥100000)作为爽滑剂,以及加入占二元聚丙烯共聚物基层材料总重量0.1~0.5%的交联丙烯酸甲酯作为防粘剂;
在中间层聚丙烯基层材料中加入占聚丙烯基层材料总重量10~30%的C5氢化石油树脂作为增挺剂,以及加入占聚丙烯基层材料总重量0.2~0.5%烷基(C14-18)双(2-羟乙基)胺作为抗静电剂;
在下表层三元聚丙烯共聚物基层材料中加入占三元聚丙烯共聚物基层材料总重量1~3%的高分子硅酮(Mw≥100000)作为爽滑剂,以及加入占三元聚丙烯共聚物基层材料总重量0.1~0.5%的交联丙烯酸甲酯作为防粘剂。
本发明通过在上表层和下表层基层材料中加入高分子硅酮和交联丙烯酸甲酯,以提高薄膜的爽滑性和防粘性。使薄膜的内摩擦做到0.13N/m以下,通过减小内摩擦来达到烟包和条包从薄膜中退出即“易退包”的目的;还通过在中间层基层材料中加入氢化石油树脂以提高薄膜的挺度,加入烷基(C14-18)双(2-羟乙基)胺以提高薄膜的抗静电性能。
综上,本发明内摩擦小,挺度和抗静电性能好。能使烟包很容易地从薄膜中退出。
具体实施方式
本发明涉及的双向拉伸聚丙烯易退包收缩烟用薄膜,分为上表层、中间层和下表层三层结构,各层中各组份占该层总重量的百分比分别为:
上表层(0.5μ-1.0μ):二元聚丙烯共聚物96.5~98.9%,其起始温度为108℃。高分子硅酮(Mw≥100000)1%~3%和交联丙烯酸甲酯0.1~0.5%。
中间层:聚丙烯69.8~89.9%、C5氢化石油树脂10~30%、烷基(C14-18)双(2-羟乙基)胺0.2~1.0%。
下表层(0.5μ~1.0μ):三元聚丙烯共聚物96.5~98.9%,其起始温度为100℃。高分子硅酮(Mw≥100000)1~3%和交联丙烯酸甲酯0.1~0.5%。
本发明产品收缩率:摩擦系数外≤0.16N/m,内≤0.13N/m,
纵向,横向≥8%;
弹性模量≥2900。
Claims (1)
1、一种双向拉伸聚丙烯易退包收缩烟用薄膜,分为上表层、中间层和下表层三层结构,上表层是以二元聚丙烯共聚物为基层材料,中间层是以聚丙烯为基层材料,下表层是以三元聚丙烯共聚物为基层材料,其特征在于:
在上表层二元聚丙烯共聚物基层材料中加入占二元聚丙烯共聚物基层材料总重量1~3%Mw≥100000的高分子硅酮作为爽滑剂,以及加入占二元聚丙烯共聚物基层材料总重量0.1~0.5%的交联丙烯酸甲酯作为防粘剂;
在中间层聚丙烯基层材料中加入占聚丙烯基层材料总重量10~30%的氢化石油树脂作为增挺剂,以及加入占聚丙烯基层材料总重量0.2~1.0%的烷基(C14-18)双(2-羟乙基)胺作为抗静电剂;
在下表层三元聚丙烯共聚物基层材料中加入占三元聚丙烯共聚物基层材料总重量1~3%Mw≥100000的高分子硅酮作为爽滑剂,以及加入占三元聚丙烯共聚物基层材料总重量0.1~0.5%的交联丙烯酸甲酯作为防粘剂。