CN100540289C - Tubulose enamelled iron skill assembly and preparation method thereof - Google Patents
Tubulose enamelled iron skill assembly and preparation method thereof Download PDFInfo
- Publication number
- CN100540289C CN100540289C CNB2007100164853A CN200710016485A CN100540289C CN 100540289 C CN100540289 C CN 100540289C CN B2007100164853 A CNB2007100164853 A CN B2007100164853A CN 200710016485 A CN200710016485 A CN 200710016485A CN 100540289 C CN100540289 C CN 100540289C
- Authority
- CN
- China
- Prior art keywords
- iron skill
- tubulose
- weight
- weight portion
- enamel paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of tubulose enamelled iron skill assembly, on the inner chamber and its outer surface of body, dip-coating has the enamel paint layer respectively, and this dope layer densification is firm, non-oxidizability is strong, has strengthened the ageing-resistant and resistant tarnishing on the inside and outside surface of tubulose enamelled iron skill assembly.After tested: the present invention improves three times than the tubular iron skill assembly of the outer brushing paint of prior art service life; Its material usage only is 1/3 of a cast iron solid-iron skill assembly, has obviously saved metal material.The present invention also provides the preparation method of above-mentioned enamelled iron skill assembly.
Description
(1) technical field:
The present invention relates to the iron skill assembly that a kind of usefulness connects combination jube or door and window; The invention still further relates to the method for making this iron skill assembly.
(2) background technology:
In the prior art, the iron skill assembly that building industry is used, as jube and the outdoor antitheft jube window of resident that is connected with on office or the residential quarters shadow-mark wall, the structure of its iron skill assembly, normally solid shape of cast iron or hollow iron pipe shape, all be at iron skill assembly outer surface brushing corrosion-resistant oil enamelled coating, and the surface of internal cavity of described tubular iron skill assembly can't brushing antirust oil enamelled coating.Exist not enough: under abominable natural environment wind, Exposure to Sunlight and sleet corrode, the very fast corrosion in inner chamber metal surface of described tubular iron skill assembly, and brushing comes off also easily aging the peeling off of skin of paint of its outer surface, and the corrosion of having accelerated tubular iron skill assembly damages.And described cast iron solid-iron skill assembly material consumption is big, the production cost height.
(3) summary of the invention:
The object of the present invention is to provide a kind of tubulose enamelled iron skill assembly, be intended to strengthen its ageing-resistant and resistant tarnishing, improve service life and save the metal material consumption; For this reason, the present invention also will provide the method for making this tubulose enamelled iron skill assembly.
For achieving the above object, tubulose enamelled iron skill assembly of the present invention improves and is: on the inner chamber and its outer surface of body, dip-coating has the enamel paint layer respectively; The composition of described enamel paint comprises: 48.5~52.5 weight portions be porcelain, 6.18~6.83 parts by weight of clay of matrix, the antimony oxide of 1.14~1.26 weight portions, the barium molybdate of 0.76~0.84 weight portion, the zinc oxide of 0.48~0.50 weight portion, the natrium nitrosum and the borax of each 0.95~1.05 weight portion with silica, and the water of 37~41 weight portions; Described enamel paint layer is 0.15~0.30 millimeter at the thickness of tube cavity and its outer surface respectively.The shape of cross section of common described body is circle, ellipse, rectangle, square, triangle, hexagon or dolioform wherein a kind of.
The method that the present invention makes tubulose enamelled iron skill assembly comprises following step: (1) dip-coating on the inner chamber of body and its outer surface has enamel paint, through 280~300 ℃ of oven dry; (2) check the leakage spot of repairing the inside and outside surperficial dip-coating porcelain layer inequality of body; (3) 900 ℃ of sintering, cooling.
Wherein, the preparation method of enamel paint is: with 48.5~52.5 weight portions is porcelain, 6.18~6.83 parts by weight of clay of matrix, the antimony oxide of 1.14~1.26 weight portions, the barium molybdate of 0.76~0.84 weight portion, the zinc oxide of 0.48~0.50 weight portion, the natrium nitrosum and the borax of each 0.95~1.05 weight portion with silica, and the water of 37~41 weight portions is in harmonious proportion evenly, by ball mill break-in 8~9 hours, filter through 70~90 mesh sieves.
Because the present invention is on the inside and outside surface of body, evenly dip-coating has the enamel paint layer that densification is firm, non-oxidizability is strong respectively, strengthened the ageing-resistant and resistant tarnishing of tubulose enamelled iron skill assembly, after tested: the present invention improves three times than the tubular iron skill assembly of the outer brushing paint of prior art service life; Its material usage only is 1/3 of a cast iron solid-iron skill assembly, has obviously saved metal material.
(4) description of drawings:
Fig. 1 has partial cross sectional views for first kind of embodiment of the present invention;
Fig. 2 is the vertical view of Fig. 1;
Fig. 3 is that the present invention is with reference to second kind of embodiment vertical view of Fig. 1;
Fig. 4 is that the present invention is with reference to the third embodiment vertical view of Fig. 1;
Fig. 5 is that the present invention is with reference to the 4th kind of embodiment vertical view of Fig. 1;
Fig. 6 is that the present invention is with reference to the 5th kind of embodiment vertical view of Fig. 1;
Fig. 7 is that the present invention is with reference to the 6th kind of embodiment vertical view of Fig. 1;
Fig. 8 is the 7th kind of embodiment front view of the present invention;
Fig. 9 is the vertical view of Fig. 8;
Figure 10 connects the schematic diagram that constitutes shadow-mark body of wall jube for the present invention;
Figure 11 is enamelled iron skill establishment of component process chart of the present invention.
(5) specific embodiment:
Fig. 1-shown in Figure 10.What get 50 weight portions is porcelain, 6.5 parts by weight of clay of matrix, the antimony oxide of 1.2 weight portions, the barium molybdate of 0.8 weight portion, the zinc oxide of 0.5 weight portion, the natrium nitrosum and the borax of each 1 weight portion with silica, and the water mediation of 39 weight portions stirs, by ball mill break-in 9 hours, be placed in the container through the filtration of 80 mesh sieves.With cross section is the length dimension blanking of the metal tube of circle according to setting, processing method is routinely cleaned the rusty stain greasy dirt on the inside and outside surface of body, airing earlier, again body is placed in the container, its inner chamber and outer surface are carried out repeatedly dip-coating enamel paint layer equably.The thickness of described enamel paint layer 1 is 0.20 millimeter (shown in Figure 1), thereafter send into drying baker and carry out 300 ℃ of oven dry, reexamine the leakage spot of repairing tube cavity and its outer surface dip-coating enamel paint layer inequality, after enter enamel furnace and carry out 900 ℃ of sintering, be cooled to finished product (Fig. 1, Fig. 2, shown in Figure 11) at last.According to different designing requirements, the cross section of described body can also be oval (shown in Figure 3); Rectangle (shown in Figure 5); Square (shown in Figure 6); Triangle (shown in Figure 4); Hexagon (shown in Figure 7) or dolioform (Fig. 8's, shown in Figure 9) is wherein a kind of.According to different use occasions and installation requirement, enamelled iron of the present invention skill assembly can connect and constitutes shadow-mark body of wall jube (shown in Figure 10) or multiple iron art products such as residential building outdoor anti-theft jube window, balustrade jube, tables and chairs supporting leg, clothes hanger or flower stand in the construction.
The above only is a preferred implementation of the present invention.Should be understood that; For the person of ordinary skill of the art; under the prerequisite that does not break away from the principle of the invention; need not other technical characterictic that the process creative work just can be associated; can also make some modification or improvement; these variations obviously all should be considered as equivalent feature, all belong within the protection domain of patent of the present invention.
Claims (3)
1, a kind of tubulose enamelled iron skill assembly is characterized in that on the inner chamber and its outer surface of body, dip-coating has enamel paint layer (1) respectively; The composition of described enamel paint comprises: 48.5~52.5 weight portions be porcelain, 6.18~6.83 parts by weight of clay of matrix, the antimony oxide of 1.14~1.26 weight portions, the barium molybdate of 0.76~0.84 weight portion, the zinc oxide of 0.48~0.50 weight portion, the natrium nitrosum and the borax of each 0.95~1.05 weight portion with silica, and the water of 37~41 weight portions; Described enamel paint layer (1) is 0.15~0.30 millimeter at the thickness of tube cavity and its outer surface respectively.
2, tubulose enamelled iron skill assembly according to claim 1, it is characterized in that: the shape of cross section of described body is circle, ellipse, rectangle, square, triangle, hexagon or dolioform wherein a kind of.
3, a kind of method of making the described tubulose enamelled iron skill of claim 1 assembly comprises:
(1) on the inner chamber of body and its outer surface respectively dip-coating enamel paint layer (1) is arranged, through 280~300 ℃ of oven dry;
(2) check the leakage spot of repairing the inside and outside surperficial dip-coating porcelain layer inequality of body;
(3) 900 ℃ of sintering, cooling;
Wherein, the preparation method of enamel paint is: with 48.5~52.5 weight portions is porcelain, 6.18~6.83 parts by weight of clay of matrix, the antimony oxide of 1.14~1.26 weight portions, the barium molybdate of 0.76~0.84 weight portion, the zinc oxide of 0.48~0.50 weight portion, the natrium nitrosum and the borax of each 0.95~1.05 weight portion with silica, and the water of 37~41 weight portions is in harmonious proportion evenly, by ball mill break-in 8~9 hours, filter through 70~90 mesh sieves.