CN100515993C - All case nanometer high energy composite ceramic and its preparation method - Google Patents
All case nanometer high energy composite ceramic and its preparation method Download PDFInfo
- Publication number
- CN100515993C CN100515993C CNB2006100216285A CN200610021628A CN100515993C CN 100515993 C CN100515993 C CN 100515993C CN B2006100216285 A CNB2006100216285 A CN B2006100216285A CN 200610021628 A CN200610021628 A CN 200610021628A CN 100515993 C CN100515993 C CN 100515993C
- Authority
- CN
- China
- Prior art keywords
- powder
- composite ceramic
- pulverized
- tourmaline powder
- volcanics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses one kind of nanometer high energy composite ceramic and its preparation process. The nanometer high energy composite ceramic is prepared with volcanic rock and tourmaline powder as main material, and features that the material composition comprising volcanic rock 10-20 wt%, tourmaline powder 30-50 wt%, ruby powder 2-8 wt%, kaolin 3-10 wt%, Datong clay 2-10 wt%, spodumene 2-10 wt% and albite 4-20 wt%. The present invention has far infrared function and can activate the activity of biomicromolecule, promote blood circulation, strength metabolism, diminish inflammation, etc. It has wide application range.
Description
Technical field
The present invention relates to ceramic field, particularly a kind of nano composite ceramic and preparation method thereof with far-infrared functional.
Background technology
Common pottery generally just is used for making daily living article, and its effect is more single and traditional, does not also possess other nourishing function.
And the pottery that much has nourishing function that occurs on the market at present, its nourishing function and imperfection, can not reach the purpose of real useful human body health, this series products of great majority all contains quartzy composition, and radioelement is launched in quartzy meeting, can influence the health of human body, can not reach health-care effect, also there is defective in the making processes of this class pottery simultaneously, and the making processes more complicated is not suitable for fast and effeciently producing.
Summary of the invention
The object of the present invention is to provide a kind of all case nanometer high energy composite ceramic and preparation method thereof, this composite ceramics has far-infrared functional, and "dead" element produces, useful HUMAN HEALTH.
Technical scheme of the present invention is as follows:
A kind of nano composite ceramic, with volcanics and tourmaline powder is main raw material, it is characterized in that comprising according to components in weight percentage: volcanics 10～20%, tourmaline powder 30～50%, ruby powder 2～8%, kaolin 3～10%, Datong District's soil 2～10%, triphane 2～10% and albite 4～20%.
Described tourmaline powder is the elbaite powder, perhaps iron tourmaline powder, perhaps dravite powder, perhaps this three's mixed powder.
A kind of preparation method of nano composite ceramic is characterized in that may further comprise the steps:
A, at first tourmalinite is pulverized, levigate, reaching granularity is 30～80nm;
B, volcanics and tourmalinite pulverized sieve, be mixed in proportion stirring, granulation, oven dry with the tackiness agent of weight percent 2～6%, the system of reburning 8～12 hours, temperature requirement reaches 800～1200 ℃, and it is standby that the back is pulverized in cooling at last;
C, ruby, kaolin, Datong District's soil, triphane and albite pulverized sieve, mature calcined material is standby respectively again;
D, cooperate the tackiness agent of weight percent 10～15% to mix the grog of gained among the porcelain powder that obtains among the B and the C to stir, the press filtration kneading becomes mud, goes into mould, extrusion, moulding, oven dry at last;
E, be under 800～1200 ℃, fire after 8～12 hours and become high energy composite ceramic at temperature requirement.
The present invention has following advantage:
The present invention is used for various traditional articles for daily use, not only can play traditional function, the far infrared rays of being launched, has far-infrared functional, can activate the activity of biomacromolecule, promote and improve the blood circulation of local and whole body, strengthen metabolism, reach anti-inflammatory bacteriostatic purpose, improve the blood supply oxygen supply state of focal zone, strengthen the regenerative power of cell, the development that controls inflammation also makes its localization, quicken the reparation of focus, all right resolution oedema; Can play lenitive effect, really reach the purpose of body health benefits, its range of application is wider, no matter is daily living article, or health-care product or the like all is suitable for; Its production technique is comparatively simple simultaneously, is fit to fast and effeciently produce.
Embodiment
Embodiment 1
A kind of nano composite ceramic, with volcanics and tourmaline powder is main raw material, it is characterized in that comprising according to components in weight percentage: volcanics 10～20%, tourmaline powder 30～50%, ruby powder 2～8%, kaolin 3～10%, Datong District's soil 2～10%, triphane 2～10% and albite 4～20%.
Described tourmaline powder is the elbaite powder, perhaps iron tourmaline powder, perhaps dravite powder, perhaps this three's mixed powder.
A kind of preparation method of nano composite ceramic is characterized in that may further comprise the steps:
A, at first tourmalinite is pulverized, levigate, reaching granularity is 30～80nm;
B, volcanics and tourmalinite pulverized sieve, be mixed in proportion stirring, granulation, oven dry with the tackiness agent of weight percent 2～6%, the system of reburning 8～12 hours, temperature requirement reaches 800～1200 ℃, and it is standby that the back is pulverized in cooling at last;
C, ruby, kaolin, Datong District's soil, triphane and albite pulverized sieve, mature calcined material is standby respectively again;
D, cooperate the tackiness agent of weight percent 10～15% to mix the grog of gained among the porcelain powder that obtains among the B and the C to stir, the press filtration kneading becomes mud, goes into mould, extrusion, moulding, oven dry at last;
E, be under 800～1200 ℃, fire after 8～12 hours and become high energy composite ceramic at temperature requirement.
Embodiment 2
A kind of nano composite ceramic, with volcanics and tourmaline powder is main raw material, it is characterized in that comprising according to components in weight percentage: volcanics 20%, tourmaline powder 40%, ruby powder 5%, kaolin 7%, Datong District's soil 5%, triphane 8% and albite 15%.
Described tourmaline powder is elbaite powder, iron tourmaline powder and dravite powder mixed powder.
A kind of preparation method of nano composite ceramic is characterized in that may further comprise the steps:
A, at first tourmalinite is pulverized, levigate, reaching granularity is 30～80nm;
B, volcanics and tourmalinite pulverized sieve, be mixed in proportion stirring, granulation, oven dry with the tackiness agent of weight percent 2～6%, the system of reburning 8～12 hours, temperature requirement reaches 820 ℃, and it is standby that the back is pulverized in cooling at last;
C, ruby, kaolin, Datong District's soil, triphane and albite pulverized sieve, mature calcined material is standby respectively again;
D, cooperate the tackiness agent of weight percent 10～15% to mix the grog of gained among the porcelain powder that obtains among the B and the C to stir, the press filtration kneading becomes mud, goes into mould, extrusion, moulding, oven dry at last;
E, be under 800～1200 ℃, fire after 8～12 hours and become high energy composite ceramic at temperature requirement.
Claims (3)
1, a kind of nano composite ceramic, with volcanics and tourmaline powder is main raw material, it is characterized in that comprising according to components in weight percentage: volcanics 10～20%, tourmaline powder 30～50%, ruby powder 2～8%, kaolin 3～10%, Datong District's soil 2～10%, triphane 2～10% and albite 4～20%; The granularity of described tourmalinite is 30～80nm.
2, a kind of nano composite ceramic according to claim 1 is characterized in that: described tourmaline powder is the elbaite powder, perhaps iron tourmaline powder, perhaps dravite powder, perhaps this three's mixed powder.
3,, it is characterized in that may further comprise the steps according to the preparation method of the described a kind of nano composite ceramic of claim 1:
A, at first tourmalinite is pulverized, levigate, reaching granularity is 30～80nm;
B, volcanics and tourmalinite pulverized sieve, be mixed in proportion stirring, granulation, oven dry with the tackiness agent of weight percent 2～6%, the system of reburning 8～12 hours, temperature requirement reaches 800～1200 ℃, and it is standby that the back is pulverized in cooling at last;
C, ruby, kaolin, Datong District's soil, triphane and albite pulverized sieve, mature calcined material is standby respectively again;
D, cooperate the tackiness agent of weight percent 10～15% to mix the grog of gained among the porcelain powder that obtains among the B and the C to stir, the press filtration kneading becomes mud, goes into mould, extrusion, moulding, oven dry at last;
E, be under 800～1200 ℃, fire after 8～12 hours and become composite ceramics at temperature requirement.