CN107382272A - A kind of nano ceramics energy thing - Google Patents

A kind of nano ceramics energy thing Download PDF

Info

Publication number
CN107382272A
CN107382272A CN201710620054.1A CN201710620054A CN107382272A CN 107382272 A CN107382272 A CN 107382272A CN 201710620054 A CN201710620054 A CN 201710620054A CN 107382272 A CN107382272 A CN 107382272A
Authority
CN
China
Prior art keywords
cobalt
energy
rubidium
arsenic
selenium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710620054.1A
Other languages
Chinese (zh)
Inventor
罗敏嘉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710620054.1A priority Critical patent/CN107382272A/en
Publication of CN107382272A publication Critical patent/CN107382272A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of nano ceramics energy thing, it is characterised in that is made up of the component of following mass ratio：Additive 10~80%, kaolin 20~90%；And it is made by conventional ceramic sintering process：The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：SiO2 0.05~99.51%, Al2O3 0.02~99.51%, ZrO2 0.01~99.88%, SiC 0.01~99.86%, infrared ceramic powder 0.01~99.81%, surplus is one or more elements in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, cobalt.The nano ceramics energy thing can launch rf wave and infrared ray simultaneously, coordinate warming heater to carry out processing materials, can be to material Implantation Energy, and material is water, beverage and food, the cigarette etc. that people drink, and then provides energy for human body.

Description

A kind of nano ceramics energy thing
Technical field
The present invention relates to a kind of nano ceramics energy thing, especially a kind of one kind that can launch rf wave and infrared ray simultaneously Nano ceramics energy thing, belongs to technical field of functional ceramics.
Background technology
1st, human body cell energy abundance is the key of good health and a long life
The basic physiological structural units of human body is cell, and cell itself has specific division cycle and division number, cell It is fixed to divide number, but the length of CDC decides the length in people's life-span.Human body cell is as one " small capacitances " of energy can be stored, the length of CDC, are determined by the energy sufficient degree of cell itself, When cellular energy is sufficient, longer by the time-to-live of cell, CDC is just grown, and the life-span of people also accordingly extends；When During cellular energy deficiency, cell survival limited time, with regard to short, the life-span of people can also shorten CDC.In addition, cell sheet Body energy deficiency, can also cause cytogene to make a variation, and then produce a variety of diseases.Therefore, as long as constantly supplementing energy to cell, Cell is allowed on the premise of energy abundance, the cell to have made a variation is thoroughly repaired through several CDCs, makes to be damaged Cell be restored, allow cytometaplasia, it is impaired caused by disease cured.
And under the premise of our own cells energy abundances, the cell divided is all in the pink of condition and vibrant, Ke Yida To the natural division time to live of cell.In the state of self-energy especially abundance, our cell division time to live Can also be more longer than the natural division time to live of cell.As the principle of this charging with battery is, battery Service life determined by its capacitance and the velocity of discharge.When battery discharging finishes, then must just fill again Electricity can be reused.And human body cell is exactly a small capacitances, usually make the electrolyte with electric charge molten by body fluid circulatory Liquid enters cell in the presence of infiltration, turns into negative pole on the inside of the cell membrane of electronegative accumulation, and the electric charge of positively charged Near the nucleus of aggregation, positive pole is formed, it is in from outside to inside focused radiation shape that the intracellular electronics direction of motion, which is, is individual do not roll over not The small capacitances that can store energy of button.Temporary transient exhaustless energy is stored in the triphosphoric acid in mitochondria in the form of biochemical energy In adenosine.When the energy of whole cell is in one than relatively low threshold values.Cell is begun into line splitting, and this is with regard to suitable After battery discharging, to start to charge up.If the atriphos in cell mitochondrial is relatively more, into the cell Energy is just more sufficient, can allow cell itself prolonged survival period a bit, allow CDC to extend.
So the length of CDC, is determined by the energy sufficient degree of cell itself.Cellular energy is got over Abundance, its cell survival time is longer, and division cycle is just grown, and the life-span of people also can accordingly extend on the basis of natural life-span； Cellular energy deficiency, its cell survival time can shorten, and CDC will be reduced, and the life-span of people can also shorten.
Certainly, because cell itself energy deficiency causes because of caused by DNA replication dna deviation cytogene to make a variation, as long as not Break the method for handing in energy retroactively to cell, allow cell on the premise of energy abundance, by several CDCs, being can be with Thoroughly repair the gene that has made a variation.And therefore the disease of produced device can also be completely cured the cell that has been damaged can be with Recovered completely.
It is " big an electricity being made up of the countless cells for storing energy i.e. " small capacitances " in fact for human body Hold ".If it can get up by all means to human body cell Implantation Energy and by the energy storage of injection, so that it may promote health and cure diseases, prolong Year lengthens one's life.Therefore, energy is conveyed to human body by energy cigarette, is exactly a kind of energy supplement approach well.
2nd, the biochemical energy that human body absorbs from food is generally insufficient
Under usual condition, human body absorbs biochemical energy from food, and by the enzymolysis of digestive system, biochemical energy transformation is made a living Thing electric energy, biological power is transported to by each cell by passages through which vital energy circulates system and body fluid circulatory, using the source as its life energy. Unnecessary biological energy source, then be synthesized into atriphos, is stored in the form of biochemical energy in the mitochondria of cell, in cell energy When measuring insufficient, the bond energy on atriphos phosphate bond is opened, energy is provided for cell.
And the bad habits and customs of many people, such as diet not timing quantify, lack rational diet nutritional collocation, it is inevitable Cause the biochemical energy deficiency that human body is taken in；And the life style day and night overturned, sultriness tobacco and wine, huge psychological pressure, allow The energy of atriphos in many human bodies excessively discharges, plus the influence of environmental loads, the cell energy that allows in many human bodies Measure the state all in wretched insufficiency.When some internal organs of human body or the cellular energy of system are less than specific threshold, ratio can be triggered More serious disease, and this can aggravate the state of human body cell energy deficiency.Well imagine, it is tight for a long time in such cellular energy Cell division in the state of weight deficiency, and cytogene variation how is not produced, and how can reach the natural division of cell Cycle.
3rd, the energy supplement method that biochemical energy is absorbed from food is not unique and best energy supplement method
At present, the mode of human body reception energy mainly has following several：Solar energy is absorbed from sunshine；Absorbed from food biochemical Energy；Earth magnetic energy is absorbed from geographical environment；Passages through which vital energy circulates reception universe energy is got through by practicing Buddhism or Taoism to do exercises.
Because food is limited by its growth conditions, its energy matter is largely nutriment less than 20%, in addition people Body physiological structure feature, it is far from being enough to depend merely on first two supplement energy, and for most people, first two be eventually its The exclusive source of the energy supplement in all one's life, and the special knowledge and skills of the necessary GPRS of latter two, this is to vast majority of people It is expected untouchable.It can reach one of major reason of desired life far away because of energy supplement deficiency here it is the mankind.Therefore, The mankind are earnestly finding more effective energy supplement approach always.
4th, using the most intimate apparatus of water, food and human contact as medium, by energy injection into these media, Energy is supplemented from these media to human body again, and these energy must form the energy required for human body cell.
Human body cell is made up of 27 kinds of biological elements and tens kinds of trace elements, therefore, the energy that cell needs And the cell frequency spectrum being made up of the atomic spectrum of these basic elements, if the frequency spectrum that these cells need can be sufficiently mended Fill to cell, the vigor with regard to cell can be greatly enhanced.
The present invention is exactly to obtain the function with this cell frequency spectrum using nanopowder prescription technology and sintering technology to make pottery Porcelain, then these cell power spectrums of function ceramics are sent to the most intimate medium of human contact by combining special device and method Such as water, liquid beverage, food, solid beverage, cigarette, cooker, tableware and apparatus, then given people by the conveying of these media Body.
The frequency spectrum that cell needs is mainly 1 ~ 1000MHz scopes and a length of 1 ~ 30 μ m of infrared wave in rf wave.
Traditional Nano-functional Ceramics typically only lay particular stress on transmitting infrared ray or rf wave, can launch rf wave and red simultaneously Outside line, and the rf frequency launched is in 1 ~ 1000MHz scopes, IR wavelength is in 1 ~ 30 μ m, with human body " life member The Nano-functional Ceramics country that element " frequency spectrum belongs to a wave band does not appear in the newspapers also.
The content of the invention
It is an object of the invention to provide a kind of nano ceramics energy thing, specifically one kind can launch rf wave and red simultaneously Outside line, and the rf wave scope launched is in the nano ceramics energy thing of 1 ~ 1000MHz, IR wavelength at 1 ~ 30 μm.
The present invention is to provide such a nano ceramics energy thing, it is characterised in that by the component group of following mass ratio Into：Additive 10~80%, kaolin 20~90%；
And pass through following conventional ceramic sintering process：
1）After additive, kaolin are mixed, blank is routinely made；
2）By step 1）Blank through conventional nano ceramics sintering process, nano ceramics energy thing is made.
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
SiO2 0.05~99.51%
Al2O30.02~99.51%
ZrO2 0.01~99.88%
SiC0.01~99.86%
Infrared ceramic powder 0.01~99.81%
Surplus is in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 0.05~99.39%
TiO20.01~99.87%
ZnO 0.01~99.88%
Al2O30.02~99.51%
BN 0.01~99.86%
Infrared ceramic powder 0.01~99.81%
Surplus is one kind in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt Or multiple element；
Or
Al2O30.02~99.51%
SiO2 0.05~99.39%
ZrO2 0.01~99.88%
SiC0.01~99.86%
ZnO 0.01~99.88%
BN 0.01~99.86%
TiO20.01~99.87%
Surplus is in magnesium, calcium, sodium, magnesium, iron, copper, sodium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 0.05~99.39%
Na2O 0.01~99.86%
Al2O30.02~99.51%
K2O 0.01~99.81%
TiO20.01~99.87%
CaO 0.01~99.71%
Fe2O30.01~99.63%
Surplus is the one or more in magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element.
Or
ZrO20.01~99.88%
Al2O30.02~99.51%
SiC0.01~99.86%
TiO20.01~99.87%
BN 0.01~99.86%
ZnO 0.01~99.88%
Pelelith 0.01~99.81%
Infrared ceramic powder 0.01~99.81%
Graphite powder 0.01~99.81%
Surplus is one or more elements in copper, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt.
The kaolin is conventional commercial products.
Further, the additive includes the component of following mass ratio：
SiO2 0.2~95%
Al2O30.2~95%
ZrO2 0.1~92%
SiC0.2~95%
Infrared ceramic powder 0.1~92%
Surplus is in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 0.2~95%
TiO20.1~92%
ZnO 0.1~92%
Al2O30.2~95%
BN 0.1~92%
Infrared ceramic powder 0.1~92%
Surplus is one kind in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt Or multiple element；
Or
Al2O30.2~95%
SiO2 0.2~95%
ZrO2 0.1~92%
SiC0.2~95%
ZnO 0.1~92%
BN 0.1~92%
TiO20.1~92%
Surplus is in magnesium, calcium, sodium, magnesium, iron, copper, sodium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 1.5~90%
Na2O0.1~84%
Al2O30.5~87%
K2O 0.2~84%
TiO20.2~84%
CaO 0.1~84%
Fe2O30.1~84%
Surplus is the one or more in magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element.
Or
ZrO20.5~90%
Al2O30.2~87%
SiC0.1~84%
TiO2 0.2~84%
BN 0.2~84%
ZnO 0.1~85%
Pelelith 0.1~90%
Infrared ceramic powder 0.1~86%
Graphite powder 0.1~84%
Surplus is one or more elements in copper, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt.
Further, the additive includes the component of following mass ratio：
SiO2 1~81%
Al2O31~81%
ZrO2 2~83%
SiC2~83%
Infrared ceramic powder 1~81%
Surplus is in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 2~88%
TiO21~83%
ZnO 1~83%
Al2O32~88%
BN 1~83%
Infrared ceramic powder 1 ~ 81%
Surplus is one kind in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt Or multiple element；
Or
Al2O35~78%
SiO2 15~86%
ZrO2 1~72%
SiC 2~75%
ZnO 2~75%
BN 3~78%
TiO2 1~72%
Surplus be calcium, sodium, magnesium, iron, copper, sodium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, zirconium, silver, boron, rubidium, arsenic, nickel, One or more elements in cobalt；
Or
SiO215~89%
Na2O1~80%
Al2O31~80%
K2O 1~80%
TiO22~82%
CaO 1~80%
Fe2O31~80%
Surplus is the one or more in magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element.
Or
ZrO215~89%
Al2O32~82%
SiC1~80%
TiO22~82%
BN 2~82%
ZnO 1~80%
Pelelith 1~80%
Infrared ceramic powder 1~80%
Graphite powder 1~80%
Surplus is the one or more member in copper, cobalt, manganese, iron, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element.
The nano ceramics energy thing is the particle that substance is 5~500g, or cylinder, ring or piece to open wide up and down, or Person is opened upper end, the container of bottom lock, or is closed upper part, the lid of bottom-open, be can be used alone, also can be a variety of groups Close and use.
Nano ceramics energy thing provided by the invention can also launch infrared ray simultaneously in addition to rf wave is launched, therefore available The nano ceramics energy thing coordinates warming heater to carry out processing materials.The infrared radiation wherein launched is former in each composition of material Son electronically, because frequency range and the hydrogen electronics of infrared waves belong to a wave band around the frequency that core rotates, becomes in temperature In the environment of change, with the rise of temperature, if the infrared frequency meeting that the dry granular nano ceramics energy thing with thermal sensitivity is launched Increase as temperature raises, enter trip temperature field sweep, when the frequency that the electronics of infrared frequency and each composed atom rotates around core When identical, covibration occurs, the Electron absorption infrared ray of each composed atom and the transition of electron energy level occurs, while produce suction Spectrum is received, now the infrared wave energy of nano ceramics energy thing is just injected into material, material is turned into energy material.
The material is people water, beverage, the food drunk, is either cigarette or is other lives or production material.
The nutrient that human body cell needs is mainly protein, carbohydrate, sugar, mineral matter, fat, starch, dimension life Element and water etc., mainly by carbon, hydrogen, oxygen, nitrogen phosphate and sulfur, chlorine, potassium, sodium, calcium and magnesium, these macroelements form these compositions, and Containing silicon, carbon, calcium, sodium, magnesium, titanium, copper, iron, zinc, aluminium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, Several Ten microelements such as nickel, cobalt, therefore, as long as selecting the additive containing these elements in nano ceramics energy thing, lead to Prescription and sintering process are crossed, with regard to the rf wave and infrared ray that can be launched just and human body cell frequency spectrum belongs to a wave band Nano ceramics energy thing, handle the drinking water of people, beverage, food, cigarette etc. with it, just can to human body supplement required for Above-mentioned energy element.
When by material be placed in magnetic field intensity be 0.1-25T cryogenic magnetic field and nano ceramics energy thing transmitting rf wave In environment and infrared thread environment, the hydrogen nuclei in material（1H）, carbon atom（13C）, nitrogen-atoms（15N）Isospin nuclear atom exists In the presence of high-intensity magnetic field, axial precession and rotation around magnetic field are produced, the rf wave of nano ceramics energy thing transmitting is radiated at On these spin nuclear atoms, with the field sweep of magnetic field field sweep device（Progressively uniformly reduce or increase from high to low or from low to high Add the mode of magnetic field intensity）, these spin nuclear atoms is changed around the speed of axle precession also with the change of magnetic field intensity, when Atom around axle precession frequency it is identical with the radio frequency wave frequency rate that nano ceramics energy thing is launched when, these atoms produce resonance inhale Storage rice ceramic energy thing launches the rf wave come and the transition of nuclear-energy level occurs, while produces absorption spectrum, now receives The rf wave frequency spectrum of rice ceramic energy thing is just injected into these spin nuclear atoms.
Under the infrared radiation of nano ceramics energy thing transmitting, the electrons in material in each atom are to its characteristic wavelength Infrared radiation produce absorbing phenomenon, by taking hydrogen electronics as an example, radiating the photon of its equivalent energy level difference can be absorbed by hydrogen atom, obtain To the concealed wire of its absorption spectrum.It is this to produce the phenomenon of energy injection by absorbing the frequency spectrum of light source, it is former with above-mentioned self-rotating nuclear Under magnetic field environment, the phenomenon difference for absorbing rf wave generation nuclear magnetic resonance Implantation Energy is son：The latter is for there is magnetic The spin nuclear atom that precession could be produced under field condition produces resonance, to the nuclear atom Implantation Energy that spins；The former is for surrounding The spin of the electronics of atomic nucleus rotation produces resonance to electron injection energy, it is not necessary to can also occur under magnetic field environment；Both Energy rank and frequency difference it is larger, the frequency of self-rotating nuclear atom nuclear magnetic resonance is in 1 ~ 1000MHz；Hydrogen electronics is composed according to its discovery Energy section where line can be divided into Lay graceful system, Balmer series, Paschen series, Brackett series, pfund series and Humphrey System ..., wavelength is in 1 ~ 30 μ m.
Advantages of the present invention and effect：
1st, using such scheme, obtain the radio frequency wave frequency rate that can launch rf wave and infrared ray simultaneously and launch 1 ~ 1000MHz, nano ceramics energy thing of the IR wavelength at 1 ~ 30 μm.
2nd, it is pair most intimate with human contact in conjunction with heater and method using the nano ceramics energy thing of the present invention Medium such as water, liquid beverage, food, solid beverage, cigarette etc. be directly injected into energy, or pass through can Implantation Energy Cooker, tableware and apparatus etc. come machining medium such as water, liquid beverage, food, solid beverage, cigarette etc. and inject energy indirectly After amount, then by these media it is conveyed to human body, and then energy effectively and in all directions is supplemented to human body cell.
3rd, nano ceramics energy thing provided by the invention has energy due to atom in itself, can launch rf wave and infrared Line, and there is higher thermal sensitivity and wider frequency range, nano ceramics energy thing is equivalent to the nothing for having countless atomic nucleus to form Several rf waves and infrared wave launcher, can be to N number of atom in food material while Implantation Energy, and therefore, injection efficiency is ratio Higher.
Brief description of the drawings
Fig. 1 is the principle schematic that nano ceramics energy thing rf wave is injected to water；
Fig. 2 is rf wave spectrum measurement figure in water.
Embodiment
The present invention is described further with reference to embodiment.
Embodiment 1
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 50%, kaolin 50%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
SiO2 0.05%
Al2O3 92.51%
ZrO2 0.24%
SiC0.20%
Infrared ceramic powder 5.2%
Surplus be 1.8% calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, 21 kinds of elements such as cobalt, each average content of preceding 20 kinds of elements is 0.08%, latter 0.2%；
And pass through following conventional ceramic sintering process：
1）After additive, kaolin are mixed, blank is routinely made；
2）By step 1）Blank through conventional nano ceramics sintering process, nano ceramics energy grain is made.
Experimental example
Below by the cooperation of the nano ceramics energy grain and following devices provided embodiment 1, to handle water, water is set to obtain energy Amount, it is specific as follows：
As shown in figure 1, the nano ceramics energy grain described in embodiment 1 is put into heating container, it is provided with the heating container Electromagnet, the electromagnet are connected and are connected respectively with electromagnetic scanning device and electromagnetic controller, wherein：The magnetic direction of electromagnet is with receiving The infrared ray and rf wave direction that rice ceramic energy grain is sent are perpendicular；Heating container is set to be in magnetic environment, nano ceramics In infrared thread environment and the rf wave environment that amount thing is sent；
Light water is injected in above-mentioned heating container, boiling point is heated in the magnetic field that magnetic field intensity is 0.1-25T, makes big point The water decomposition of son group is unimolecule or the water of subset, makes water atomic nucleus under the influence of a magnetic field, produces the axle around magnetic field To rotation and rotation, if then by dry granular nano ceramics energy grain launch rf wave be radiated on the water atom of rotation, and with The field sweep of magnetic field field sweep device（The mode of magnetic field intensity is progressively uniformly decreased or increased from high to low or from low to high）, make The nuclear precessional evlocity of water changes also with the change of magnetic field intensity, when nuclear precession frequency and some nano ceramics When energy grain radio frequency wave frequency rate is identical, if water atom occurs nuclear magnetic resonance absorption dry granular nano ceramics energy grain rf wave and occurred The transition of nuclear-energy level, while absorption spectrum is produced, now the radio frequency wave energy of nano ceramics energy grain is just injected into water In molecule.
Verify example 1
The water of above-mentioned experimental example Implantation Energy is put into the test device shown in Fig. 2, carries out the detection of radio frequency power spectrum, it is provable The nano ceramics energy grain of embodiment 1 can launch rf wave, while prove that the water of experimental example has been injected into energy, and specific method is: In an electromagnetic field, the receiving coil of a radio frequency receiver and amplifier is wound on the tube wall of teat glass, the radio frequency reception Device and amplifier are connected with logger or oscillograph, then the teat glass periphery setting radio frequency of receiving coil is wound with tube wall The transmitting coil of generator, and transmitting coil is mutually perpendicular to receiving coil, radio-frequency signal generator is connected with radio frequency scanner, such as Shown in Fig. 2；The water of the Implantation Energy of the present embodiment 1 is added in teat glass, by adjusting field scan device intensity, in scope From low to high or from high to low continuous adjustment magnetic field intensity in 0.1-25T, when find to have on logger or oscillograph more by force compared with When big wave spectrum continuously occurs, illustrate to generate resonance in the range of this magnetic field intensity, this magnetic field intensity scope corresponds to rf wave Frequency range be exactly rf wave energy frequency scope that nano ceramics energy grain has；According to the above method, embodiment 1 is measured Nano ceramics energy grain transmitting rf wave energy frequency spectrum be 1-200 MHz, it was demonstrated that coordinated again with the nano ceramics energy grain After above-mentioned energy injection device processing common drinking water, you can to water Implantation Energy.
Verify example 2
Pass through the detection of infrared spectrum, it was demonstrated that the nano ceramics energy grain that embodiment 1 provides can also be same in addition to rf wave is launched When launch infrared ray, i.e.,：According to the measuring principle of Atomic Absorption Spectrometer, instrument has provided elemental characteristic to be measured from radiation of light source The light of spectral line, by being absorbed during sample steam by element ground state atom to be measured in steam, subtracted according to radiation feature spectral line light Weak degree, to determine the content of element to be measured in sample, the energy water obtained by above-mentioned experimental example qualitative can be measured with this principle Characteristic spectral line, specific method is as follows：
Detected with Atomic Absorption Spectrometer, the forward and backward water of experimental example Implantation Energy be separately added into a teat glass, Atomic Absorption Spectrometer detection is sent into, the energy level formula of hydrogen atomic spectrum is pressed on the hollow cathode lamp of Atomic Absorption Spectrometer, N values are set from small to large since ground state, it is real with the characteristic spectrum with n values energy level transition to the corresponding hydrogen of n+1 energy levels, radiation Vapor of the water tested before and after an Implantation Energy in teat glass, when the spectrum of radiation is by the water Atomic absorption in vapor When, the reflected light that spectrometer is measured can be dimmed, corresponding n values and residing energy level is thus obtained, before experimental example Implantation Energy The n values of water afterwards carry out contrast and learnt, n=1 of the water before Implantation Energy, n=2-3 of the water after Implantation Energy, and 10, illustrate experiment The small molecule energy water of example has been injected into energy.
Energy level formula：E(n)=E(1)/n^2
In hydrogen spectrum, n=2,3,4,5 ... Lyman series n=3,4,5,6 ... are formed to the transition luminescence of n=2 to the transition luminescence of n=1 Form Balmer series；N=4,5,6,7 ... form paschen series to the transition luminescence of n=3；Sent out to the transition of n=4 n=5,6,7,8 ... Light forms cloth loudspeaker and burst at the seams；Wherein there was only preceding 4 H spectral lines of Balmer series（N=1,2,3,4）Fall in visible region It is interior；H spectral lines of the n more than 4 then not in visible region, illustrate to be in higher energy level.
N=1-3 of the water of experimental example is measured simultaneously, it was demonstrated that has been the micromolecular water for being marked with infrared spectrum.
Embodiment 2
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 10%, kaolin 90%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
SiO2 90.40%
TiO2 3.9%
ZnO 0.61%
Al2O3 0.28%
BN 0.01%
Infrared ceramic powder 3.0%
Surplus be 1.8% calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt, Every kind of element is 0.09%；
By the technique of embodiment 1, nano ceramics energy grain is made.
And energy water is obtained by the experimental example apparatus and method of embodiment 1, then by apparatus and method, the checking for verifying example 1 The method of example 2 is detected, and the rf wave energy frequency spectrum that measuring nano ceramics energy thing has is 180-420 MHz, is surveyed simultaneously Obtaining nano ceramics energy thing has infrared spectrum；Also measure n=2-4 of energy water, it was demonstrated that the water has been injected into energy.
Embodiment 3
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 80%, kaolin 20%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
Al2O3 91.6%
SiO2 1.4%
ZrO2 0.8%
SiC1.3%
ZnO 2.8%
BN 1.09%
TiO2 0.01%
Surplus be 1% magnesium, calcium, sodium, magnesium, iron, copper, sodium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, Cobalt, preceding 20 kinds of element average contents are 0.04%, and rear 2 kinds of elements are respectively 0.1%；
By the technique of embodiment 1, nano ceramics energy grain is made.
And energy water is obtained by the experimental example apparatus and method of embodiment 1, then by apparatus and method, the checking for verifying example 1 The method of example 2 is detected, and the rf wave energy frequency spectrum that measuring nano ceramics energy thing has is 360-510 MHz, is surveyed simultaneously Obtaining nano ceramics energy thing has infrared spectrum；Also measure n=3-5 of energy water, it was demonstrated that the water has been injected into energy.
Embodiment 4
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 30%, kaolin 70%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
SiO2 9.3%
Na2O0.8%
Al2O3 23.5%
K2O 5.0%
TiO2 0.01%
CaO 22.3%
Fe2O3 37.4%
Surplus be 1.8% magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt, Mei Zhongyuan Plain average content is 0.1%.
By the technique of embodiment 1, nano ceramics energy grain is made.
And energy water is obtained by the experimental example apparatus and method of embodiment 1, then by apparatus and method, the checking for verifying example 1 The method of example 2 is detected, and the rf wave energy frequency spectrum that measuring nano ceramics energy thing has is 350-490 MHz, is surveyed simultaneously Obtaining nano ceramics energy thing has infrared spectrum；Also measure n=2-4 of energy water, it was demonstrated that the water has been injected into energy.
Embodiment 5
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 70%, kaolin 30%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
SiO2 40.8%
Na2O19.5%
Al2O3 12.7%
K2O 10.5%
TiO2 0.05%
CaO 7.5%
Fe2O3 8.35%
Surplus be 0.6% magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt, first 16 kinds The average every kind of content of element is 0.03, and latter 2 kinds are respectively 0.06%；
By the technique of embodiment 1, nano ceramics energy grain is made.
And energy water is obtained by the experimental example apparatus and method of embodiment 1, then by apparatus and method, the checking for verifying example 1 The method of example 2 is detected, and the rf wave energy frequency spectrum that measuring nano ceramics energy thing has is 480-630 MHz, is surveyed simultaneously Obtaining nano ceramics energy thing has infrared spectrum；Also measure n=5-8 of energy water, it was demonstrated that the water has been injected into energy.
Embodiment 6
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 40%, kaolin 60%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
SiO2 25.9%
Na2O3.5%
Al2O3 31.7%
K2O 9.6%
TiO2 5.9%
CaO 21.1%
Fe2O3 2.0%
Surplus be 0.3% magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt, first 16 kinds Average content is 0.015%, and rear 2 kinds of elements are respectively 0.03%；
By the technique of embodiment 1, nano ceramics energy grain is made.
And energy water is obtained by the experimental example apparatus and method of embodiment 1, then by apparatus and method, the checking for verifying example 1 The method of example 2 is detected, and the rf wave energy frequency spectrum that measuring nano ceramics energy thing has is 530-770 MHz, is surveyed simultaneously Obtaining nano ceramics energy thing has infrared spectrum；Also measure n=8-11 of energy water, it was demonstrated that the water has been injected into energy.
Embodiment 7
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 60%, kaolin 40%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
ZrO2 2.3%
Al2O3 16.8%
SiC 1.7%
TiO2 0.06%
BN 3.6%
ZnO 8.2%
Pelelith 46.7%
Infrared ceramic powder 12.3%
Graphite powder 5.34%
Surplus is 3% copper, cobalt, manganese, iron, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt, and first 16 kinds average Content is 0.15%, and rear 2 kinds of elements are respectively 0.3%；
By the technique of embodiment 1, nano ceramics energy grain is made.
And energy water is obtained by the experimental example apparatus and method of embodiment 1, then by apparatus and method, the checking for verifying example 1 The method of example 2 is detected, and the rf wave energy frequency spectrum that measuring nano ceramics energy thing has is 620-810 MHz, is surveyed simultaneously Obtaining nano ceramics energy thing has infrared spectrum；Also measure n=11-12 of energy water, it was demonstrated that the water has been injected into energy.
Embodiment 8
A kind of nano ceramics energy thing, is made up of the component of following mass ratio：Additive 45%, kaolin 55%；
The granularity of the additive is 1 ~ 100nm, includes the component of following mass ratio：
ZrO2 3.9%
Al2O3 7.5%
SiC9.1%
TiO2 2.5%
BN 2.9%
ZnO 5.7%
Pelelith 51.6%
Infrared ceramic powder 15.2%
Graphite powder 0.6%
Surplus is 1% copper, cobalt, manganese, iron, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt, and first 16 kinds average Content is 0.05%, and rear 2 kinds of elements are respectively 0.1%；
By the technique of embodiment 1, nano ceramics energy grain is made.
And energy water is obtained by the experimental example apparatus and method of embodiment 1, then by apparatus and method, the checking for verifying example 1 The method of example 2 is detected, and the rf wave energy frequency spectrum that measuring nano ceramics energy thing has is 710-1000 MHz, is surveyed simultaneously Obtaining nano ceramics energy thing has infrared spectrum；Also measure n=11-12 of energy water, it was demonstrated that the water has been injected into energy.

Claims (6)

1. a kind of nano ceramics energy thing, it is characterised in that be made up of the component of following mass ratio：Additive 10~80%, kaolinite Soil 20~90%；
And pass through following conventional ceramic sintering process：
1）After additive, kaolin are mixed, blank is routinely made；
2）By step 1）Blank through conventional nano ceramics sintering process, nano ceramics energy thing is made.
2. nano ceramics energy thing as claimed in claim 1, it is characterised in that the granularity of the additive is 1 ~ 100nm, bag Include the component of following mass ratio：
SiO2 0.05~99.51%
Al2O30.02~99.51%
ZrO2 0.01~99.88%
SiC 0.01~99.86%
Infrared ceramic powder 0.01~99.81%
Surplus is in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 0.05~99.39%
TiO20.01~99.87%
ZnO 0.01~99.88%
Al2O30.02~99.51%
BN 0.01~99.86%
Infrared ceramic powder 0.01~99.81%
Surplus is one kind in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt Or multiple element；
Or
Al2O30.02~99.51%
SiO2 0.05~99.39%
ZrO2 0.01~99.88%
SiC 0.01~99.86%
ZnO 0.01~99.88%
BN 0.01~99.86%
TiO20.01~99.87%
Surplus is in magnesium, calcium, sodium, magnesium, iron, copper, sodium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 0.05~99.39%
Na2O 0.01~99.86%
Al2O30.02~99.51%
K2O 0.01~99.81%
TiO20.01~99.87%
CaO 0.01~99.71%
Fe2O30.01~99.63%
Surplus is the one or more in magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element；Or
ZrO20.01~99.88%
Al2O30.02~99.51%
SiC 0.01~99.86%
TiO20.01~99.87%
BN 0.01~99.86%
ZnO 0.01~99.88%
Pelelith 0.01~99.81%
Infrared ceramic powder 0.01~99.81%
Graphite powder 0.01~99.81%
Surplus is one or more elements in copper, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt.
3. nano ceramics energy thing as claimed in claim 1, it is characterised in that the kaolin is conventional commercial products.
4. nano ceramics energy thing as claimed in claim 2, it is characterised in that the additive includes the group of following mass ratio Point：
SiO2 0.2~95%
Al2O30.2~95%
ZrO2 0.1~92%
SiC 0.2~95%
Infrared ceramic powder 0.1~92%
Surplus is in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 0.2~95%
TiO20.1~92%
ZnO 0.1~92%
Al2O30.2~95%
BN 0.1~92%
Infrared ceramic powder 0.1~92%
Surplus is one kind in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt Or multiple element；
Or
Al2O30.2~95%
SiO2 0.2~95%
ZrO2 0.1~92%
SiC 0.2~95%
ZnO 0.1~92%
BN 0.1~92%
TiO20.1~92%
Surplus is in magnesium, calcium, sodium, magnesium, iron, copper, sodium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 1.5~90%
Na2O 0.1~84%
Al2O30.5~87%
K2O 0.2~84%
TiO20.2~84%
CaO 0.1~84%
Fe2O30.1~84%
Surplus is the one or more in magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element；Or
ZrO20.5~90%
Al2O30.2~87%
SiC 0.1~84%
TiO2 0.2~84%
BN 0.2~84%
ZnO 0.1~85%
Pelelith 0.1~90%
Infrared ceramic powder 0.1~86%
Graphite powder 0.1~84%
Surplus is one or more elements in copper, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt.
5. nano ceramics energy thing as claimed in claim 2, it is characterised in that the additive includes the group of following mass ratio Point：
SiO2 1~81%
Al2O31~81%
ZrO2 2~83%
SiC 2~83%
Infrared ceramic powder 1~81%
Surplus is in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, boron, rubidium, arsenic, nickel, cobalt One or more elements；
Or
SiO2 2~88%
TiO21~83%
ZnO 1~83%
Al2O32~88%
BN 1~83%
Infrared ceramic powder 1 ~ 81%
Surplus is one kind in calcium, sodium, magnesium, copper, iron, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, silver, rubidium, arsenic, nickel, cobalt Or multiple element；
Or
Al2O35~78%
SiO2 15~86%
ZrO2 1~72%
SiC 2~75%
ZnO 2~75%
BN 3~78%
TiO2 1~72%
Surplus be calcium, sodium, magnesium, iron, copper, sodium, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, zirconium, silver, boron, rubidium, arsenic, nickel, One or more elements in cobalt；
Or
SiO215~89%
Na2O 1~80%
Al2O31~80%
K2O 1~80%
TiO22~82%
CaO 1~80%
Fe2O31~80%
Surplus is the one or more in magnesium, copper, zinc, cobalt, manganese, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element；Or
ZrO215~89%
Al2O32~82%
SiC 1~80%
TiO22~82%
BN 2~82%
ZnO 1~80%
Pelelith 1~80%
Infrared ceramic powder 1~80%
Graphite powder 1~80%
Surplus is the one or more member in copper, cobalt, manganese, iron, chromium, selenium, iodine, fluorine, molybdenum, vanadium, tin, strontium, boron, rubidium, arsenic, nickel, cobalt Element.
6. nano ceramics energy thing as claimed in claim 1, it is characterised in that the nano ceramics energy thing be substance be 5~ 500g particle is either cylinder, ring or the piece opened wide up and down or is opened upper end, the container of bottom lock, or is top Closing, the lid of bottom-open.
CN201710620054.1A 2017-07-26 2017-07-26 A kind of nano ceramics energy thing Pending CN107382272A (en)