CN100507089C - Method for repairing liner on side of electrolytic tank without stopping the tank - Google Patents
Method for repairing liner on side of electrolytic tank without stopping the tank Download PDFInfo
- Publication number
- CN100507089C CN100507089C CNB2004100102571A CN200410010257A CN100507089C CN 100507089 C CN100507089 C CN 100507089C CN B2004100102571 A CNB2004100102571 A CN B2004100102571A CN 200410010257 A CN200410010257 A CN 200410010257A CN 100507089 C CN100507089 C CN 100507089C
- Authority
- CN
- China
- Prior art keywords
- electrolyzer
- anode block
- repaired
- groove
- cofferdam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A method for reparing the lateral liner of electrolyzer without stopping working includes using a working carbon block, electrically insulating between conducting rod and bus, horizontally putting the anodic carbon block on the bottom of electrolyzer, filling the mixture of electrolyte blocks and alumina powder to form a dam for isolating electrolyte from molten aluminium, removing the molten aluminium and material blocks inside said dam, exposing the original surface of damaged carbon block, adhering the silicon carbide-silicon nitride brick, pressing, using normal carbon black, and electrically connecting the conducting rod with bus.
Description
Affiliated technical field
The invention belongs to the repairing technique of electrolytic aluminum prebake sun electrolyzer, what relate generally to is a kind of method that groove is repaired electrolytic bath side part inner lining of not stopping, and mainly is applicable to the electrolyzer of above large-sized prebaked, the silicon carbide of 300KA in conjunction with silicon nitride liner.
Background technology
Large-sized prebaked electrolyzer is the important component part of producing electrolytic aluminum, and the quality of its operation is directly connected to the production efficiency of electrolytic aluminum.Known electrolyzer is generally the rectangular slot pond, be illustrated in figure 1 as normal operating electrolyzer, bottom, groove pond is a cathode block, lateral lining is silicon carbide knot and silicon oxide fragment of brick (being called for short the carbon piece) 2, outer wall is a steel plate 1, and the combining site between electrolyzer sidepiece and the trench bottom is to prevent that the artificial of seepage from stretching one's legs 3.The bottom in groove pond is the aluminium liquid 4 of separating out, top is electrolyte solution 5, be provided with tens groups of two rows' anode block 6.1,6.2 on the top in groove pond, every group of anode block constitutes by two, be fixed in the electrolytic solution by the suspention of steel pawl, every group the shared big buses of two anode carbon (supply lead) 8, big bus to the energising of carbon piece, carries out electrolytic chemical reaction by guide rod 7.
Large-sized prebaked electrolyzer because powerful direct current 10 enters (as shown in Figure 2) behind the electrolyzer, causes high-intensity magnetic field 12 when electrolysis, aluminium liquid and electrolytic liquid in the groove are constantly flowed.Be in operation and occur the phenomenon that the sense of current 10 makes magnetic field 12 concentrate to current output terminal inevitably, make the stove nation at this position be difficult to form, secularly wash away local 11 breakages of the liner that easily makes the electrolyzer sidepiece, cause the electrolyzer bakie and be forced to stop the groove maintenance, otherwise, can cause electrolyzer to scrap, cause very big waste.The method for repairing and mending of taking at present is the blowing out reparation, needs electrolytic solution all extracted out repair, and about about 20-30 days of whole mending course has reduced the service efficiency of electrolyzer thus, causes production cost to strengthen.
Summary of the invention
The objective of the invention is to propose a kind of method that groove is repaired electrolytic bath side part inner lining of not stopping, it can make electrolyzer in operational process the lateral lining that damages be repaired, thereby reduces loss, guarantees the normal operation of electrolyzer.
Purpose of the present invention can adopt following technical scheme to realize: it extracts the corresponding anode block of liner that the electrolyzer sidepiece damages, change the anode block that is used to construct, to insulate between guide rod and the big bus, make the carbonium utmost point piece of construction be seated in bottom land and level-off, all pile the real cofferdam that separates ionogen and aluminium liquid that forms to its bight along the anode block outside with electrolyte block companion aluminum oxide powder, clean out the aluminium water in the cofferdam, and the material piece in the cofferdam all dug out, then the sidewall carbon brick that damages is dug to its original face, pack into on-the-spot cut out good silicon carbide in conjunction with nitrogenize silica brick piece (carbon piece) and bonding after, smash the paste tamping in the bottom with heat, form artificial stretching one's legs, bonding carbon piece is pressed with pressing plate, behind the cleaning bottom land, change the anode block of normal use, guide rod and big bus are connected, electrolyzer can normally move.
The liner distance that anode block when being used to construct is mended apart from need is 50-60cm.
Cofferdam thickness in repairing is 30-40cm.
With electrolysis tech control electrolyzer an anode effect taking place, with electrolysis tech control electrolyzer anode effect can not take place in mending course before repairing beginning.
Method of the present invention is not because when repairing cell lining, electrolyzer stops groove, and it is little to whole electrolyzer running influence only with one group of anode block when repairing, and has avoided repairing the loss of troughed belt, thereby has improved production efficiency, has saved cost.Carry out repairing work with aforesaid method and repair and compare, can reduce over one hundred ten thousand yuan of losses that stop troughed belt with original groove that stops.
Description of drawings
Accompanying drawing 1 is a normal operational centre cell construction synoptic diagram.
Accompanying drawing 3 is the cell construction synoptic diagram in repairing.
Shown in the figure: 1, steel plate, 2, silicon carbide is in conjunction with nitrogenize silica brick (carbon piece), 3, artificial stretching one's legs, 4, aluminium liquid, 5, electrolytic liquid, 6.1,6.1.1,6.2 anode blocks, 7, guide rod, 8, big bus, 9, artificial cofferdam, 10, the sense of current, 11, damaged position, 12, magnetic field.
Embodiment
In conjunction with the accompanying drawings, it is as follows to provide embodiments of the invention:
It is to repair under the situation of not stopping groove, extract part ionogen and aluminium liquid earlier, the corresponding anode block 6.1 of the liner that will repair takes out then, change working anode block 6.1.1, making the distance of itself and lateral lining is 55cm, insulating material on pad between guide rod 7 and the big bus 8 (as kraft paper etc.), both disconnect to make it, 6.1.1 is seated in bottom land with anode block, also the guide rod and the big bus of another anode block in one group of anode block can be disconnected as required simultaneously, and it is seated in bottom land.Electrolyte block (sodium aluminum fluoride) companion aluminum oxide powder is all hit tight as forming a cofferdam 9 that separates ionogen and aluminium liquid to its place, bight along the anode block carbon piece 6.1.1 outside, thickness is 35cm, clean out the aluminium water in the cofferdam 9, and the material pieces in the cofferdam 9 are all dug out, then the sidewall carbon brick that damages is dug its original face, the on-the-spot silicon carbide well of cutting out pack in conjunction with nitrogenize silica brick piece, after using tackiness agent (general purpose material) bonding then, smashing paste (general purpose material) tamping in its bottom with heat forms and artificially stretches one's legs 3, with pressing plate bonding carbon piece is pressed, available in case of necessity angle bar, behind the cleaning bottom land, 6.1.1 mentions with anode block, upgrades the anode block 6.1 when changing operation, make guide rod 7 and big bus 8 conductings, can enter in service normally.At this moment, electrolyte block (sodium aluminum fluoride) is met thermal change and is become electrolyte solution, with the electrolyte solution in the supplemental tank (can extract certain electrolyte solution and aluminium liquid as required before construction, to reduce the height of liquid in the groove).In above-mentioned mending course, want equalizing effect at interval, before repairing beginning, an anode effect takes place, in mending course, anode effect can not take place with electrolysis tech control electrolyzer with electrolysis tech control electrolyzer.
Claims (4)
1, a kind ofly do not stop the method that groove is repaired electrolytic bath side part inner lining, it is characterized in that: will take out with the corresponding anode block of liner (6.1) that the electrolyzer sidepiece damages, change working anode block (6.1.1), make insulation between guide rod (7) and the big bus (8), anode block is seated in bottom land and level-off, mix aluminum oxide powder with electrolyte block and pile the real cofferdam (9) that separates ionogen and aluminium liquid that forms along anode block (6.1.1) outside to its bight entirely, clean out the aluminium water in the cofferdam (9), and the material piece that cofferdam (9) are interior all digs out, when no aluminium water infiltrates, then the sidewall carbon brick that damages is dug to original face, the on-the-spot silicon carbide well of cutting out pack in conjunction with nitrogenize silica brick piece, bonding, smash the paste tamping in the bottom with heat and form artificial stretching one's legs, the carbon piece is pressed, behind the cleaning bottom land with pressing plate, change the anode block (6.1) of normal use, guide rod and big bus conducting are got final product.
2, a kind of method that groove is repaired electrolytic bath side part inner lining of not stopping according to claim 1 is characterized in that: the liner distance that working anode block (6.1.1) need be repaired apart from sidepiece is 50-60cm.
3, a kind of method that groove is repaired electrolytic bath side part inner lining of not stopping according to claim 1, it is characterized in that: the cofferdam that is used to repair (9) thickness is 30-40cm.
4, a kind of method that groove is repaired electrolytic bath side part inner lining of not stopping according to claim 1, it is characterized in that: before repairing beginning, an anode effect takes place, in mending course, anode effect can not take place with electrolysis tech control electrolyzer with electrolysis tech control electrolyzer.