CN100506551C - Liquid composition - Google Patents
Liquid composition Download PDFInfo
- Publication number
- CN100506551C CN100506551C CNB2004800102264A CN200480010226A CN100506551C CN 100506551 C CN100506551 C CN 100506551C CN B2004800102264 A CNB2004800102264 A CN B2004800102264A CN 200480010226 A CN200480010226 A CN 200480010226A CN 100506551 C CN100506551 C CN 100506551C
- Authority
- CN
- China
- Prior art keywords
- fluid composition
- substituted
- emulsion
- polyallylamine
- alkyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a liquid composition which helps carry out a successful cleaning operation without causing the residence of the composition in a cleaning cap while maintaining excellent color development properties and glossiness. This liquid composition contains a modified polyallylamine which is subjected to urea, urethane, acyl, Michael addition, alcoholic modifications and the like; a polymer particle; an organic solvent; and water, but does not contain a coloring agent, and is used by making it adhere to a recording medium together with an ink composition. Recording is achieved by sticking both liquid composition and ink composition to the recording medium. The polyallylamine is preferably a polymer comprising a recurring unit represented by the following formula (I).
Description
Technical field
The fluid composition that the present invention relates to use, do not contain colouring agent with the ink composite that contains colouring agent.
Background technology
Ink jet recording method be a kind of by making ink composite droplet ejection and attached to the printing process of writing down on the recording mediums such as paper.The method is characterized in that, both can use cheap device, again printed resolution height and harsh image at high speed.Up to now, the ink composite about using when writing down according to this ink jet recording method has various motions.In recent years, people increase just day by day for the requirement of high-quality document image, have particularly found out various methods for the colour rendering that further improves document image and glossiness.
In order to realize high-quality image, the someone proposed by make ink composite with second composition attached to the scheme that writes down on the recording medium.For example, open the reactant liquor that discloses a kind of ink composite that makes specific composition in flat 9-207424 communique and the flat 9-286940 communique of Te Kai and contained polyallylamine the spy and be attached to ink jet recording method on the recording medium together.In addition, open the spy and disclose the ink jet recording method that a kind of fluid composition that will contain cationic material prints with ink composite in the flat 8-81611 communique.
Summary of the invention
The inventor has found a kind of composition with superperformance, and said composition can be used as the fluid composition that is attached on the recording medium with ink composite and uses.Particularly found a kind of like this fluid composition, said composition can realize writing down the storage stability height of thing, keep good colour rendering and glossiness, can make the mixed liquor (hereinafter being sometimes referred to as " waste liquid ") of fluid composition or ink composite or fluid composition and ink composite not be trapped in the cleaning lid (Cleaning cap) again, can carry out good cleaning operation.
Therefore, the purpose of this invention is to provide a kind of fluid composition with superperformance, a kind of like this fluid composition particularly is provided, said composition can realize writing down the storage stability height of thing, keep good colour rendering and glossiness, can make fluid composition or ink composite or waste liquid not be trapped in the cleaning lid again, can carry out good clean operation.
Therefore, fluid composition of the present invention is a kind ofly to contain modification polyallylamine, water-miscible organic solvent and water and do not contain colouring agent, can be used for ink composite attached to the composition on the recording medium.The fluid composition that contains above-mentioned modification polyallylamine by use, can realize writing down the storage stability height of thing, keep good colour rendering and glossiness, can make fluid composition or ink composite or waste liquid not be trapped in the cleaning lid again, can realize good cleaning operation.
Description of drawings
Fig. 1 is the skeleton diagram that can realize the ink-jet recording apparatus of recording method of the present invention.
Fig. 2 is the skeleton diagram of the record head of ink-jet recording apparatus.
Fig. 3 is the simulation drawing of the printed patterns that formed by ink-jet recording apparatus.
Fig. 4 is the skeleton diagram of the nozzle arrangements of record head.
Fig. 5 is the skeleton diagram that can realize the ink-jet recording apparatus of recording method of the present invention.
Fig. 6 possesses the device that is used to add thermal recording media, the skeleton diagram that can realize the ink-jet recording apparatus of recording method of the present invention.
The specific embodiment
Definition
In this manual, as the alkyl of the part of group or group, can be the alkyl of straight or branched.
1.
The fluid composition of the present invention's first technical scheme
In the fluid composition of the present invention's first technical scheme, the modification polyallylamine is the macromolecule that contains at least a repetitive by following formula (I) expression:
(in following formula, R
1And R
2Represent independently of one another hydrogen atom, can substituted alkyl, can substituted aryl, can substituted pyridine radicals, can substituted alkyl amino, can substituted diazanyl, can substituted alkoxyl or can substituted hydroxyalkyl).
Use contains the fluid composition of the present invention of above-mentioned modification polyallylamine, can realize the record thing that storage stability is good when keeping good colour rendering and glossiness.More particularly, can realize being difficult to take place the image of variable color.
According to the preferred technical solution of the present invention, the substituent R in the formula (I)
1And R
2Preferably methyl, ethyl, propyl group etc. are more preferably methyl, especially preferably R
1, R
2Be all the dimethyl modification body of methyl.
Consider that from the viewpoint that improves colour rendering the modification polyallylamine preferably utilizes azo-initiator to synthesize.
The weight average molecular weight of modification polyallylamine is preferably below 10,000, more preferably below 5,000, particularly preferably in below 2,000.The degree of modification of above-mentioned modification polyallylamine is preferably more than 50mol%, more preferably more than 90mol%.
The content of modification polyallylamine can be considered to determine aptly from the viewpoint that improves colour rendering and raising glossiness, but according to the preferred technical solution of the present invention, the content of modification polyallylamine in fluid composition is preferably more than the 0.1 weight %, below the 30 weight %; More preferably be to be limited under it more than 0.1 weight %, more preferably more than the 0.5 weight %; More preferably be to be limited on it below 10 weight %, more preferably below the 5 weight %.Should illustrate that in the present invention, the content of modification polyallylamine is solid constituent conversion amount.
In the present invention, the modification polyallylamine can be mixed interpolation with the polyallylamine or derivatives thereof.Mix when adding, their total content is with respect to the total amount of fluid composition, preferably more than the 0.1 weight %, below the 30 weight %; Be more preferably and be limited under it more than 0.1 weight %, more preferably more than the 0.5 weight %; Be more preferably and be limited on it below 10 weight %, more preferably below the 5 weight %.
The modification polyallylamine is mixed the occasion of adding with the polyallylamine or derivatives thereof, can be to mix at modification polyallylamine below 2,000 and weight average molecular weight with weight average molecular weight greater than the modification polyallylamine below 2,000,10,000.By making fluid composition contain different alkyl-modified polyallylamine of such molecular weight and polyallylamine or derivatives thereof, can obtain when keeping good colour rendering and glossiness, being implemented in the cleaning lid does not have fluid composition to be detained, and has the advantage that can carry out good clean operation.
According to the preferred technical solution of the present invention, this fluid composition preferably also contains weight average molecular weight at the modification polyallylamine more than 5,000, and this modification polyallylamine preferably contains the macromolecule of at least a repetitive by above-mentioned formula (I) expression.Occasion in that the two or more mixing of polyallylamine or derivatives thereof are added preferably contains the polyallylamine or derivatives thereof of weight average molecular weight in polyallylamine or derivatives thereof more than 5,000 and weight average molecular weight less than 5,000.By making fluid composition contain the different polyallylamine of such molecular weight, can obtain when keeping good colour rendering and glossiness, being implemented in the cleaning lid does not have fluid composition to be detained, and has the advantage that can carry out good clean operation.
According to the preferred technical solution of the present invention, fluid composition is preferably according to the ratio of 1:0.25~1:4, more preferably according to the ratio of 1:0.5~1:2, contain weight average molecular weight 5, the low-molecular-weight polyallylamine or derivatives thereof of HMW polyallylamine or derivatives thereof more than 000 and weight average molecular weight less than 5,000.
2.
The fluid composition of the present invention's second technical scheme
The fluid composition of the present invention's second technical scheme preferably also contains the polymine or derivatives thereof except above-mentioned modification polyallylamine.The polymine or derivatives thereof is the macromolecule that contains at least a repetitive by following formula (II) expression:
—(NR
1CH
2CH
2)n— (II)
(in above-mentioned formula, R
1The expression hydrogen atom, can substituted alkyl, can substituted aryl, can substituted pyridine radicals, can substituted alkyl amino, can substituted diazanyl, can substituted alkoxyl or can substituted hydroxyalkyl).
According to the preferred technical solution of the present invention, the weight average molecular weight of polymine or derivatives thereof (Mw) is more preferably under it and is limited to 100 preferably below 10,000, is limited to 5,000 on it.
Polymine can easily obtain according to known manufacture method, for example can be by using carbon dioxide, hydrochloric acid, hydrobromic acid, p-methyl benzenesulfonic acid, aluminium chloride, boron trifluoride etc. as catalyst, make aziridine carry out ring-opening polymerisation and obtain, perhaps obtain by making vinyl chloride and ethylenediamines compound carry out polycondensation reaction with corresponding construction.
According to the preferred technical solution of the present invention, as the high molecular example that contains a kind of repetitive by above-mentioned formula (II) expression at least, can enumerate following compound,
(in following formula, m and n are that the weight average molecular weight (Mw) that can make polymine becomes the numerical value below 10,000).
In the present invention, polymine and derivative thereof can be that anion-modified or cation-modified polymer has taken place for its side chain or a terminal part.
In the present invention, the content of polymine and derivative thereof can consider to determine aptly from the viewpoint that improves colour rendering and glossiness, still, with respect to the total amount of fluid composition, preferably more than the 0.1 weight % to 30.0 weight %; More preferably be to be limited under it more than 0.2 weight %, more preferably more than the 0.5 weight %; More preferably be to be limited on it below 10.0 weight %, more preferably below the 5.0 weight %.In this manual, the content of polymine or derivatives thereof is solid constituent conversion amount.
In the present invention, can mix the two or more polymine or derivatives thereofs of interpolation.In the occasion of mix adding, their total content is with respect to the total amount of fluid composition, preferably more than the 0.1 weight % to 30.0 weight %; More preferably be to be limited under it more than 0.2 weight %, more preferably more than the 0.5 weight %; More preferably be to be limited on it below 10.0 weight %, more preferably below the 5.0 weight %.
3.
The fluid composition of the present invention's the 3rd technical scheme
The fluid composition of the present invention's the 3rd technical scheme is by containing a kind of composition that following repetitive forms as the modification polyallylamine that has, just by containing N, the copolymer of N-dialkyl group allylamine and allylamine is as the modification polyallylamine of basic structure and the composition that forms
(in the formula, R
1And R
2The alkyl of representing carbon number 1~4 independently of one another).
What is called can be used for modification polyallylamine among the present invention be meant as the allylamine repetitive-NH
2In one or two hydrogen atom by following (i)~(any group v) replaces the product that forms.
That is to say, can enumerate: (i)-CONH
2(hereinafter referred to as urea-modified polyallylamine); (ii)-COOR
3(hereinafter referred to as urethane-modified polyallylamine); (iii)-COR
4(polyallylamine of acyl group modification hereinafter referred to as); (iv)-CH
2CH (R
5)-A (polyallylamine of Michael's modification hereinafter referred to as); (v)-CH
2CH (OH)-B (hereinafter referred to as pure modification polyallylamine) etc.
Modification polyallylamine among the present invention one by one is described below.
(i) urea-modified polyallylamine
Urea-modified polyallylamine be by following repetitive (a) with (c1); Perhaps (a) and (b) and (c1) copolymer of formation,
(in the formula, R
1And R
2The alkyl of representing carbon number 1~4 independently of one another).
R
1And R
2Preferably with a kind of group, for example methyl, ethyl, propyl group, butyl, but methyl preferably.
In addition, with respect to the monomer sum that constitutes the modification polyallylamine, the ratio of repetitive (a) is preferably 5~95%, and more preferably 10~90%, be preferably 20~80% especially.At this moment, consider the carbamoylation degree from the dissolubility and stable two aspects of modification polyallylamine; repetitive (c1) shared ratio in repetitive (b) and sum (c1) just; be preferably 60~100%, more preferably 90~100%, be preferably 95~100% especially.
(ii) urethane-modified polyallylamine
Urethane-modified polyallylamine be by following repetitive (a) with (c2); Perhaps (a) and (b) and (c2) copolymer of formation,
(in the formula, R
1And R
2The alkyl of representing carbon number 1~4 independently of one another, R3 are represented the alkyl or aryl of carbon number 1~12).
R
1And R
2Preferably with a kind of group, for example methyl, ethyl, propyl group, butyl, but methyl preferably.
R
3The alkyl or aryl of expression carbon number 1~12.Work as R
3Be the occasion of the alkyl of carbon number 1~12, preferably the straight chained alkyl of carbon numbers 1~4 such as methyl, ethyl, propyl group, butyl for example.As the aryl of carbon number 1~12, can enumerate phenyl, o-tolyl, a tolyl, p-methylphenyl.
In addition, with respect to the monomer sum that constitutes the modification polyallylamine, the ratio of repetitive (a) is preferably 5~95%.More preferably 10~90%, be preferably 20~80% especially.At this moment; consider from the dissolubility and stable two aspects of modification polyallylamine; carboalkoxyization (or allyl oxygen phosphinylidyneization) degree; repetitive (c2) shared ratio in repetitive (b) and sum (c2) just; be preferably 60~100%; more preferably 90~100%, be preferably 95~100% especially.
(iii) acyl group modification polyallylamine
Acyl group modification polyallylamine be by following repetitive (a) with (c3); Perhaps (a) and (b) and (c3) copolymer of formation,
(in the formula, R
1And R
2The alkyl of representing carbon number 1~4 independently of one another, R
4The alkyl of expression carbon number 1~12).
R
1And R
2Preferably with a kind of group, for example methyl, ethyl, propyl group, butyl, but methyl preferably.
R
4The alkyl of expression carbon number 1~12, preferred example is methyl, ethyl, n-pro-pyl, isopropyl, normal-butyl, n-pentyl, n-hexyl, n-heptyl, n-nonyl.
In addition, with respect to the monomer sum that constitutes the modification polyallylamine, the ratio of repetitive (a) is preferably 5~95%, and more preferably 10~90%, be preferably 20~80% especially.At this moment, consider the acidylate degree from the dissolubility and stable two aspects of modification polyallylamine; repetitive (c3) shared ratio in repetitive (b) and sum (c3) just; be preferably 60~100%, more preferably 90~100%, be preferably 95~100% especially.
(iv) Michael's modification polyallylamine
Michael's modification polyallylamine is following repetitive (a), (c41) and/or copolymer (c42); Perhaps (a) and (b), (c41) and/or copolymer (c42),
(in the formula, R
1And R
2The alkyl of representing carbon number 1~4 independently of one another; R
5Expression hydrogen atom or methyl; A is for being selected from-CONR
6R
7,-CN and COOR
8In any group, wherein ,-CONR
6R
7In, R
6And R
7The alkyl (this alkyl can be selected from alkyl monosubstituted amino, two (alkyl of carbon number 1~4) amino of hydroxyl, ketone group, carbon number 1~4, any group in three (alkyl of carbon number 1~4) ammonium replaces) of representing hydrogen atom or carbon number 1~8 independently of one another, perhaps, NR
6R
7The cyclic amino of representing piperidino or morpholinyl together jointly); COOR
8In, R
8The alkyl of expression carbon number 1~8 (this alkyl can be selected from alkyl monosubstituted amino, two (alkyl of carbon number 1~4) amino of hydroxyl, ketone group, carbon number 1~4 and any group in three (alkyl of carbon number 1~4) ammonium replaces).
R
1And R
2Preferably with a kind of group, methyl preferably wherein.
In addition, group-CH2CH
2(R
5)-A is the addition product of the michael reaction of acyclic compound normally, still, and when it is that (A is-CONR acrylamide addition product type6R
7Type) time, can be used as example and enumerate following groups :-CH2CH
2CONH
2、—CH
2CH
2CONHCH
3、—CH
2C
H
2CON(CH
3)
2、—CH
2CH
2CONHC
2H
5、—CH
2CH
2CON
(C
2H
5)
2、—CH
2CH
2CONH—nC
3H
7、—CH
2CH
2CON(nC
3H
7)
2、—CH
2CH
2CONH—iC
3H
7、—CH
2CH
2CONHCH
2O
—nC
4H
9、—CH
2CH
2CONHCH
2OH、—CH
2CH
2CONHCH
2C
H
2N(CH
3)
2、—CH
2CH
2CONHCH
2CH
2N(C
2H
5)
2、—CH
2
CH
2CONHCH
2CH
2CH
2N(CH
3)
2、—CH
2CH
2CONHCH
2C
H
2CH
2N(C
2H
5)
2、—CH
2CH·
2CONHCH
2CH
2N
+(CH
3)
3、
—CH
2CH
2CONHCH
2CH
2N
+(C
2H
5)
3、—CH
2CH
2CONHC
H
2CH
2CH
2N
+(CH
3)
3、—CH
2CH
2CONHCH
2CH
2CH
2N
+
(C
2H
5)
3、—CH
2CH
2CO-morpholinyl ,-CH2CH
2CO-piperidino ,-CH2CH(CH
3)CONH
2、—CH
2CH(CH
3)CONHC
H
3、—CH
2CH(CH
3)CON(CH
3)
2、—CH
2CH(CH
3)CON
HC
2H
5、—CH
2CH(CH
3)CON(C
2H
5)
2、—CH
2CH(CH
3)
CONH—nC
3H
7、—CH
2CH(CH
3)CON(nC
3H
7)
2、—CH
2C
H(CH
3)CONH—iC
3H
7、—CH
2CH(CH
3)CONHCH
2O—n
C
4H
9、—CH
2CH(CH
3)CONHCH
2OH、—CH
2CH(CH
3)C
ONHCH
2CH
2N(CH
3)
2、—CH
2CH(CH
3)CONHCH
2CH
(CH
3)N(C
2H
5)
2、—CH
2CH(CH
3)CONHCH
2CH
2CH
2N
(CH
3)
2、—CH
2CH(CH
3)CONHCH
2CH
2CH
2N(C
2H
5)
2、
—CH
2CH(CH
3)CONHCH
2CH
2N
+(CH
3)
3、—CH
2CH
(CH
3)CONHCH
2CH
2N
+(C
2H
5)
3、—CH
2CH(CH
3)CON
HCH
2CH
2CH
2N
+(CH
3)
3、—CH
2CH(CH
3)CONHCH
2CH
2CH
2N
+(C
2H
5)
3、—CH
2CH(CH
3) CO-morpholinyl ,-CH2
CH(CH
3) CO-piperidino.
In addition, as group-CH
2CH
2(R
5When)-A is acrylonitrile addition product type, can be used as example and enumerate :-CH
2CH
2CN and-CH
2CH (CH
3) CN.
In addition, as group-CH
2CH
2(R
5When)-A is acrylate addition product type, can be used as example and enumerate :-CH
2CH
2COOCH
3,-CH
2CH
2COOC
2H
5,-CH
2CH
2COOC
3H
7,-CH
2CH
2COOC
4H
9,-CH
2CH
2COOCH
2CH
2N (CH
3)
2,-CH
2CH
2COOCH
2CH
2CH
2N (CH
3)
2,-CH
2CH
2COOCH
2CH
2N (C
2H
5)
2,-CH
2CH
2COOCH
2CH
2CH
2N (C
2H
5)
2,-CH
2CH
2COOCH
2CH
2CH
2N
+(CH
3)
3,-CH
2CH
2COOCH
2CH
2N
+(C
2H
5)
3,-CH
2CH
2COOCH
2CH
2CH
2N
+(C
2H
5)
3
With respect to the monomer sum that constitutes the modification polyallylamine, the ratio of repetitive (a) is preferably 5~95%, and more preferably 10~90%, be preferably 20~80% especially.At this moment, consider from the dissolubility and stable two aspects of modification polyallylamine, the conversion ratio of Michael addition thing type, repetitive (c41) and/or (c42) be preferably 60~100% just in repetitive (b) and ratio shared (c41) and/or in the sum (c42), more preferably 90~100%, be preferably 95~100% especially.
In addition, consider that from the liquid waste processing aspect repetitive (c42) shared ratio in repetitive (c41) and sum (c42) is preferably 60~100%, more preferably 90~100%, be preferably 95~100% especially.
(v) pure modification polyallylamine
Alcohol modification polyallylamine is following repetitive (a), (c51) and/or copolymer (c52); Or (a) and (b), (c51) and/or copolymer (c52),
(in the formula, R
1And R
2The alkyl of representing carbon number 1~4 independently of one another, B are represented the alkyl (this alkyl can be selected from the alkoxyl of hydroxyl, carbon number 1~4 and any group in the alkene oxygen base replaces) of carbon number 1~8).
R
1And R
2Preferably with a kind of group, methyl preferably wherein.
B represents the alkoxyl of hydroxyl, carbon number 1~4 or can comprise the alkyl of the carbon number 1~8 of alkene oxygen base, for example can enumerate particularly: methyl, ethyl, propyl group, butyl, amyl group, hexyl, methoxyl methyl, ethoxymethyl, the third oxygen methyl, fourth oxygen methyl, penta oxygen methyl, methylol, (2-propenyloxy group) methyl.
As group-CH
2CH
2(R
5The example of)-B, can enumerate: 2-hydroxypropyl, 2-hydroxyl butyl, 2-hydroxyl amyl group, 2-hydroxyl hexyl, 2-hydroxyl heptyl, 2-hydroxyl octyl group, 3-methoxyl group-2-hydroxypropyl, 3-ethyoxyl-2-hydroxypropyl, 3-propoxyl group-2-hydroxypropyl, 3-(isopropoxy)-2-hydroxypropyl, 3-butoxy-2-hydroxypropyl, 3-amoxy-2-hydroxypropyl, 2,3-dihydroxypropyl, 3-(2-acrylic) 2-hydroxypropyl.
With respect to the whole number of monomers that constitute the modification polyallylamine, the ratio of repetitive (a) is preferably 5~95%, and more preferably 10~90%, be preferably 20~80% especially.At this moment, the dissolubility of said modification polyallylamine and stable two aspects are considered from the present invention, the hydroxyalkyl conversion ratio, repetitive (c51) and/or just (c52) in repetitive (b) and ratio shared (c51) and/or in the sum (c52), be preferably 60~100%, more preferably 90~100%, be preferably 95~100% especially.
In addition, consider that from the processing aspect of waste liquid with respect to repetitive (c51) and sum (c52), (c52) shared ratio is preferably 60~100%, more preferably 90~100%, be preferably 95~100% especially.
Structure to the modification polyallylamine is described above, and still, when the monomeric unit that allylamine is carried out modification when being a plurality of, whole monomeric units can be with a kind of monomeric unit, but also can be made of multiple different monomeric unit.
Above-mentioned N, the copolymer of N-dialkyl group allylamine and allylamine (hereinafter being sometimes referred to as " material copolymerization thing ") can synthesize by the method for for example putting down in writing in No. 00/21901 open brochure of WO.As the N that contains in the material copolymerization thing, N can be enumerated in N-dialkyl group knee supports and foot supports unit, N-dimethyl allylamine, N, N-diethyl allylamine, N, N-dipropyl allylamine, N, N-dibutyl allylamine.In addition, consider, preferably use N, the N-dimethyl allylamine from improving the deliquescent aspect of modifier.
The weight average molecular weight of material copolymerization thing is preferably below 5,000, and more preferably 200~3,000, be preferably 500~2,000 especially.When molecular weight is in above-mentioned scope, the modification polyallylamine that generates just can be dissolved in the solvent that constitutes printing ink well, and can suppress corrosivity to the parts that use in the ink-jet recording apparatus, and the parts that constitute ink pathway are not weathered, therefore comparatively desirable.
The ratio of monomer in the material copolymerization thing is preferably 5/95~95/5, and more preferably 10/90~90/10, be preferably 20/80~80/20 especially.
The modification polyallylamine that contains in fluid composition of the present invention can prepare by following method; promptly; make a material copolymerization thing and a class amino can be substituted by the substituent reagent of carbon number 1~12; for example N-methoxy acylating reagent, carboalkoxy reagent, allyl oxygen phosphinylidyne reagent, acylating reagent or can carry out the acrylic compounds of Michael addition reaction or can have substituent 1; 2-epoxyalkane compound reacts, make knee supports and foot supports in the material copolymerization thing-NH
2Part or all of hydrogen atom be modified as " NH-substituting group " and/or " N-is disubstituted ", thereby can obtain N, N-dialkyl group allylamine and N-replace the copolymer of allylamine.
In the present invention, the content of modification polyallylamine can be considered decision aptly from the colour rendering of raising record thing and the viewpoint of glossiness, but according to the preferred technical solution of the present invention, modification polyallylamine content in fluid composition is preferably 0.1~30 weight %, more preferably 0.1~10 weight % is preferably 0.5~5 weight % especially.
In addition, in the present invention, the modification polyallylamine can be mixed interpolation with the polyallylamine or derivatives thereof.When mixing interpolation, their total content is preferably 0.1~30 weight %, and more preferably 0.1~10 weight % is preferably 0.5~5 weight % especially.
4.
Polymer particles
As optimized technical scheme, fluid composition of the present invention also contains polymer particles.In the present invention,, preferably use anionic polymer particulate and/or nonionic particulate, be more preferably more than one anionic polymer particulate and more than one non-ionic polyalcohol particulate are used in combination as polymer particles.
According to the preferred technical solution of the present invention, with polymer particles as a kind of dispersion (mixing) in aqueous medium and the emulsion that obtains is added in the fluid composition.By it is added in the fluid composition as emulsion, the stability in the time of can improving fluid composition stability during fabrication and storage can further improve its reliability, thereby can obtain the high quality record image.
According to the preferred technical solution of the present invention, emulsion can be selected from oil-in-water type emulsion, colloidal sol type emulsion, anionic polyethylene emulsion or its modifier, anionic polypropylene emulsion or its modifier or their mixture.According to technical scheme of the present invention, anionic polyethylene emulsion or anionic polypropylene emulsion are carboxylic acid modifier or sulfonated modifier etc.
The averaged particles of polymer particles directly is preferably below 10~200nm, glass transition temperature (Tg; Measure according to JIS K6900) be preferably below 50 ℃, the minimum film temperature (MFT) of making is preferably below 20 ℃, and weight average molecular weight (Mw) is 5,000~1,000,000, is preferably 6,000~600,000.
In the present invention, with respect to the fluid composition total amount, the content of above-mentioned polymer particles is preferably 0.1~20.0 weight %, and more preferably 0.2~5.0 weight % is preferably 0.5~3.0 weight % especially.Should illustrate that in this manual, the content of polymer particles is solid constituent conversion amount.
In the present invention, fluid composition preferably also contains polymine or the polyallylamine of 0.1~30.0 weight %, can improve the glossiness of the non-printing of document image so significantly.
Below the various polymer particles in the preferred technical solution of the present invention are described.
(1) anionic polymer particulate
As by the anionic polymer particulate is mixed the preferred concrete example that is scattered in the emulsion that obtains in the aqueous medium, can enumerate the emulsion of from oil-in-water type emulsion, colloidal sol type emulsion, anionic polyethylene emulsion or its modifier, anionic polypropylene emulsion or its modifier and composition thereof, selecting.The following describes these emulsions.
(I) oil-in-water type emulsion
In the present invention, " oil-in-water type " emulsion is meant that a kind of surfactant that uses is scattered in the solvent monomer when the synthetic polymer particulate, and forms the particle diameter emulsion more than 70 μ m greatly of the polymer particles of emulsion.
Consider the glass transition temperature (Tg of oil-in-water type emulsion from the viewpoint that improves glossiness and document image stability; Measure according to JIS K 6900) preferably below 30 ℃, more preferably below 10 ℃.
Consider that from the viewpoint that improves glossiness and document image stability the weight average molecular weight (Mw) that constitutes the anionic polymer particulate of oil-in-water type emulsion is preferably 100,000~1,000,000, more preferably 400,000~600,000.When weight average molecular weight (Mw) was in this scope, its storage-stable improved, and can further improve the glossiness of the non-printing of document image.
The average grain diameter that constitutes the anionic polymer particulate of oil-in-water type emulsion is preferably more than the 70nm, and more preferably 100~200nm is preferably below 110~150nm especially.When the average grain diameter of anionic polymer particulate was in this scope, the anionic polymer particulate formed emulsion easily in water, storage-stable is improved, thereby can obtain the high quality record image.
Consider that from the viewpoint that improves glossiness and document image stability the minimum film temperature (MFT) of making of oil-in-water type emulsion is preferably below 20 ℃, more preferably below 0 ℃.When the minimum film temperature (MFT) of making in this scope the time, can further improve the glossiness of the non-printing of document image.
(II) colloidal sol type emulsion
In the present invention, " colloidal sol type " emulsion is meant that those do not need surfactant that monomer is dispersed in the solvent basically when the synthetic polymer particulate, and forms the particle diameter emulsion below 70 μ m greatly of the polymer particles of emulsion.
Consider the glass transition temperature (Tg of colloidal sol type emulsion from the viewpoint that improves glossiness and document image stability; Mensuration according to JIS K 6900) be preferably below 50 ℃, more preferably below 30 ℃, be preferably especially below 20 ℃.
Consider that from the viewpoint that improves glossiness and document image stability the weight average molecular weight (Mw) that constitutes the anionic polymer particulate of colloidal sol type emulsion is preferably 1,000~1,000,000, more preferably 3,000~500,000, be preferably 5,000~15,000 especially.When weight average molecular weight (Mw) was in this scope, its ejection stability was high, and can further improve the glossiness of the non-printing of document image.
The average grain diameter of the anionic polymer particulate of formation colloidal sol type emulsion is preferably below 70nm, more preferably below 50nm.When the average grain diameter of anionic polymer particulate was in this scope, the anionic polymer particulate formed emulsion easily in water, make colloidal sol type dispersity stabilisation, storage-stable is improved, thereby can obtain the high quality record image.
Consider that from the viewpoint that improves glossiness and document image stability the minimum film temperature (MFT) of making of colloidal sol type emulsion is preferably below 20 ℃, more preferably below 0 ℃.When the minimum film temperature (MFT) of making in this scope the time, can further improve the glossiness of the non-printing of document image.
As the preferred concrete example of colloidal sol type emulsion, can enumerate alkali-soluble emulsion, contain sulfonic emulsion.
Above-mentioned alkali-soluble emulsion is preferably used alkali, is more preferably to use inorganic base, preferably regulates the emulsion of pH value especially with alkali metal hydroxide or alkaline earth metal hydroxide.The acid number of this emulsion is preferably below 40.
Alkali-soluble emulsion preferably obtains as follows, promptly, in the presence of the water-soluble high-molecular compound of alcoholic hydroxy or copolymerization surfacant, make the ethylene type unsaturated carboxylic acid monomer and can carry out polymerization with the monomer of this monomer copolymerization, obtain polymer, with this polymer dispersed in aqueous medium, thereby obtain emulsion.
As the ethylene type unsaturated carboxylic acid monomer, for example can enumerate: the ethylene type unsaturated monocarboxylic acid monomer of acrylic acid, methacrylic acid etc.; The unsaturated polybasic carboxylic acid monomer of ethylene type of itaconic acid, maleic acid, fumaric acid, butylene tricarboxylic acids etc.; The partial ester monomer of the unsaturated polybasic carboxylic acid of ethylene type of fumaric acid mono, butyl maleate, maleic acid list-2-hydroxypropyl acrylate etc.; The polybasic acid anhydrides of maleic anhydride, citraconic anhydride etc. etc. can use one or more mixture of these monomers.Wherein, particularly preferably be acrylic or methacrylic acid.
Monomer as carrying out copolymerization with the ethylene type unsaturated carboxylic acid monomer does not have particular determination, for example can enumerate: the aromatic vinyl monomer of styrene, AMS, vinyltoluene, chlorostyrene etc.; (methyl) acrylate monomer of (methyl) methyl acrylate, (methyl) ethyl acrylate, (methyl) propyl acrylate, (methyl) acrylic acid n-pentyl ester, (methyl) acrylic acid isopentyl ester, (methyl) Hexyl 2-propenoate, (methyl) EHA, (methyl) 2-ethyl hexyl acrylate, (methyl) hydroxy-ethyl acrylate, (methyl) hydroxypropyl acrylate, (methyl) glycidyl acrylate etc.; The ethylene type unsaturated monomer of cyano-containings such as (methyl) acrylonitrile; Unsaturated glycidyl ether monomers such as the ethylene type of allyl glycidyl ether etc.; The ethylene type unsaturated acyl amine monomers of (methyl) acrylamide, N-methylol (methyl) acrylamide, N-butoxymethyl (methyl) acrylamide etc.; 1,3-butadiene, isoprene, 2, the conjugate diene monomer of 3-dimethyl-1,3-butadiene, 1,3-pentadiene etc.; The vinyl esters of carboxylic acids monomers of vinylacetate etc. etc. can use one or more mixture of these monomers.Wherein, consider from the light resistance and good two aspects of glossiness of image, preferably ethylene type esters of unsaturated carboxylic acids monomer, especially preferably (methyl) acrylate monomer of (methyl) methyl acrylate, (methyl) ethyl acrylate etc.
In the water-soluble high-molecular compound of above-mentioned alcoholic hydroxy, preferably vinyl alcohol polymer specifically, contains the water-soluble high-molecular compound of 2~25 alcoholic extract hydroxyl groups in preferably per 1,000 molecular weight.For example can enumerate: the vinyl alcohol polymer of polyvinyl alcohol or its various modifiers etc.; The saponification resultant of the copolymer of vinylacetate and acrylic acid, methacrylic acid or maleic anhydride; The cellulose derivative of alkylcellulose, hydroxy alkyl cellulose, alkyl carboxyl alkyl cellulose etc.; The starch derivatives of alkyl starch, CMS etc.; Gum arabic, bassora gum; Poly-alkane glycol etc. can use one or more mixture of these macromolecular compounds.
The copolymerization surfacant is the surfactant that has more than vinyl that can polymerization in molecule, for example can enumerate: the anionic polymerization surfacant of acrylic-2-ethylhexyl sulfosuccinate sodium, (methyl) acrylic acid polyoxyethylene sulfuric ester, polyxyethylated propenyl ether sulfuric ester ammonium salt, (methyl) acrylic acid polyoxyethylene ester phosphate etc.; The anionic polymerization surfacant of polyxyethylated phenylate (methyl) acrylate, polyoxyethylene alkyl ether (methyl) acrylate etc. can use one or more mixture of these surfactants.Wherein, from the emulsion dispersion property of monomer and and the copolymerization of monomer between the good viewpoint of balance consider preferably polyxyethylated propenyl ether sulfuric ester ammonium salt.
Contain in the sulfonic emulsion above-mentioned, preferably contain the sulfonic emulsion of dienes or contain the sulfonic emulsion of non-dienes.
Contain sulfonic emulsion as above-mentioned, can enumerate: by to carrying out the polymer that homopolymerization obtains by following monomer or carrying out that copolymer that copolymerization obtains carries out that the emulsion (opening flat 11-217525 communique with reference to the spy) that obtains is handled in sulfonation or by will carry out the emulsion that polymer dispersed that homopolymerization or copolymerization obtain obtains in aqueous medium by monomer through oversulfonate; Can also enumerate: with the dienes monomer as neccessary composition contain the sulfonic emulsion of dienes, perhaps not with the dienes monomer as the sulfonic emulsion of non-dienes of containing of neccessary composition.
The monomer that uses as being used to obtain to contain the sulfonic emulsion of dienes, can enumerate the dienes monomer and can with other monomers of dienes monomer and usefulness.
As the concrete example of dienes monomer, be that carbon number is 4~10 dienes compound, for example can enumerate: 1, the 3-butadiene, 1, the 2-butadiene, 1,3-pentadiene, 1, the 2-pentadiene, 2, the 3-pentadiene, isoprene, 1, the 2-hexadiene, 1, the 3-hexadiene, 1, the 4-hexadiene, 1, the 5-hexadiene, 2, the 3-hexadiene, 2, the 4-hexadiene, 2,3-dimethyl-1,3-butadiene, 2-ethyl-1,3-butadiene, 1, the 2-heptadiene, 1, the 3-heptadiene, 1, the 4-heptadiene, 1, the 5-heptadiene, 1, the 6-heptadiene, 2, the 3-heptadiene, 2, the 5-heptadiene, 3, the 4-heptadiene, 3, the 5-heptadiene, cycloheptadiene etc. can use one or more mixture of these dienes compounds.
As can with the concrete example of other monomers of dienes monomer and usefulness, can enumerate: the aromatic monomer of styrene, AMS, o-methyl styrene, p-methylstyrene, a methyl styrene, vinyl naphthalene etc.; (methyl) alkyl acrylate of (methyl) methyl acrylate, (methyl) ethyl acrylate, (methyl) butyl acrylate etc.; List or the dicarboxylic acids or the dicarboxylic anhydride of (methyl) acrylic acid, crotonic acid, maleic acid, itaconic acid etc.; The acrylonitrile compound of (methyl) acrylonitrile etc.; The unsaturated compound of vinyl chloride, vinylidene chloride, vinyl methyl ethyl ketone, vinylacetate, (methyl) acrylamide, (methyl) glycidyl acrylate etc. can use one or more mixture of these monomers.
With the occasion of these other monomers and usefulness, the consumption of dienes monomer is preferably more than 0.5 weight %, more preferably more than 1 weight %, more than 5 weight %.
The common emulsion (co-emulsion) of dienes that is obtained with carrying out copolymerization with other monomers of dienes monomer and usefulness by above-mentioned dienes monomer can be to comprise random copolymer, block copolymer at any interior copolymer.
As preferred copolymer, for example can enumerate: isoprene homopolymer, dienite, isoprene-styrene random copolymer, isoprene-styrene block copolymer, styrene-isoprene-phenylethene ternary block polymer, butadiene-styrene random copolymer, butadiene-styrene block copolymer, SBS, s-B-S ternary block polymer, ethylene-propylene-diene ternary block polymer etc.As preferred copolymer, for example can enumerate: isoprene-styrene block copolymer, styrene-isoprene-phenylethene ternary block polymer, butadiene-styrene block copolymer, SBS, s-B-S ternary block polymer etc.
Can be used for containing the sulfonic polymer of dienes among the present invention, can use known method of sulfonating, for example compile in Japanization association, new experimental chemistry lecture (14 volume III, 1773 pages) or the special method of opening middle records such as flat 2-227403 communique, for by to carrying out the polymer that hydrogenation obtains, carry out sulfonation and obtain based on part or all of the residual double bonds of above-mentioned diolefinic polymer and/or its precursor monomer.
As sulfonating agent, can enumerate: sulfuric anhydride, sulfuric acid, chlorosulfonic acid, oleum, bisulfites (Li salt, Na salt, K salt, Rb salt, Cs salt etc.) etc.With respect to above-mentioned polymer 1mol, the consumption of sulfonating agent is preferably 0.005~1.5mol when being scaled sulfuric anhydride, more preferably 0.01~1.0mol.
Above-mentioned contain the sulfonic emulsion of dienes preferably resemble above-mentioned according to by the state that sulfonation product and water and/or alkali compounds effect obtain is used.As alkali compounds, can enumerate alkali-metal hydroxide, alkali alcoholate, alkali-metal carbonate, ammoniacal liquor, organo-metallic compound, amine etc.Alkali compounds can use a kind of or and with two or more.With respect to the sulfonating agent 1mol that uses, the consumption of alkali compounds is below 2mol, preferably below 1.3mol.
The monomer that uses as being used to obtain to contain the sulfonic emulsion of non-dienes; for example can enumerate: allyl sulphonic acid, vinyl sulfonic acid or by making the vinyl monomer of methacryl sulfonic acid that the reaction of isobutene and sulfur trioxide obtains etc.; the perhaps Spinomar of the styrene monomer (Li of sodium p styrene sulfonate etc. such as Cao's East (strain) system), perhaps resemble general formula CH
2=C (CH
3)-COO (AO)
nSO
3(A: low-grade alkenyl) Biao Shi methyl acrylic ester monomer (for example Sanyo changes into the Eleminor RS-30 of (strain) system) has the monomer of sulfonyl to Na like that, and the sodium salt of above-mentioned monomer, sylvite, lithium salts etc.
Containing the sulfonic emulsion of non-dienes can above-mentionedly contain sulfonic monomer and not contain sulfonic monomer and carry out copolymerization and obtain by making.
As other monomers that can copolymerization, can enumerate: the aromatic series mono-vinyl compound of styrene, vinyl xylene, ethyl vinyl benzene, AMS, fluorobenzene ethene, vinylpyridine quinoline etc.; Butyl acrylate, 2-EHA, phthalic acid hydrogen Beta-methyl acryloxy ethyl ester, acrylic acid-N, the acrylate monomer of N '-dimethylamino ethyl ester etc.; Methacrylic acid 2-Octyl Nitrite, methacrylic acid methoxy base diethylene glycol (DEG) ester, methacrylic acid methoxy base macrogol ester, methyl methacrylate, EMA, butyl methacrylate, methacrylic acid N, the methacrylate monomers of N '-dimethylamino ethyl ester, GMA etc.; The vinyl cyanide based compound of acrylonitrile, methacrylonitrile etc.; Silicone-modified monomer; Macromonomer etc.Can also enumerate in addition: the conjugated double bond compound of butadiene, isoprene etc.; Or the vinyl esters compound of vinylacetate etc.; 4-methyl-1-pentene and other alpha-olefin compound etc.In can other monomers of copolymerization, preferably styrene, methyl methacrylate, acrylonitrile.
The consumption of monomer that can copolymerization is generally 1~93 weight % of polymerisable monomer, is preferably 5~80 weight %.
The emulsion that contains non-dienes carboxylic acid group can be by following method preparation, promptly, contain sulfonic monomer with above-mentioned, perhaps can be with other monomers that contain sulfonic monomer copolymerization, use in the solvent in the polymerization of for example water or organic solvent etc., use radical polymerization initiator, chain-transferring agent etc. to carry out radical polymerization, can make above-mentioned emulsion.
By making above-mentioned non-dienes monomer carry out the sulfonic emulsion of non-dienes that contains that copolymerization obtains can be to comprise random copolymer, block copolymer at any interior copolymer.
(III) anionic polyethylene emulsion or its modifier, and anionic polypropylene emulsion or its modifier
Consider that from the viewpoint that improves glossiness and document image stability the fusing point of anionic polyethylene emulsion or its modifier and anionic polypropylene emulsion or its modifier is preferably more than 70 ℃.In addition, preferably below 200nm, its average grain diameter is preferably below 160nm for the particle diameter of these emulsion particles.
The anionic polyethylene emulsion can use commercially available product, for example can buy as trade names such as AQUACER 507 from BYK-ChemieJapan KK..AQUACER 507 is oxidized high-density polyethylene emulsions of a kind of anionic, and its fusing point is 130 ℃, and pH 10, and particle diameter is 100nm~200nm.Average grain diameter is 150nm.
(2) non-ionic polyalcohol particulate
。As by the non-ionic polyalcohol particulate is mixed the concrete example that is scattered in the emulsion that obtains in the aqueous medium, can enumerate the emulsion of from nonionic polyethylene emulsion or its modifier, nonionic polypropylene emulsion or its modifier and their mixture, selecting.
Consider that from the viewpoint that improves glossiness and document image stability the fusing point of nonionic polyethylene emulsion or its modifier or polypropylene emulsion or its modifier is preferably more than 70 ℃.In addition, preferably below 200nm, average grain diameter is preferably below 160nm for its particle diameter.
These emulsions can be used its commercially available product, for example can buy as trade names such as AQUACER 513, AQUACER 593, AQUACER 543 from BYK-Chemie Japan KK..
AQUACER 513 is oxidized high-density polyethylene emulsions of a kind of nonionic, and its fusing point is 130 ℃, and pH 9, and particle diameter is 100~200nm, and average grain diameter is 150nm.In addition, AQUACER 593 is oxidation high density poly propylene emulsions of a kind of nonionic, and its fusing point is 160 ℃, and pH 9, and particle diameter is 100~200nm, and average grain diameter is 150nm.In addition, AQUACER 543 is the products that cooperate nonyl phenol to make by in AQUACER 593.
5.
Water and organic solvent
Fluid composition among the present invention contains water and organic solvent.
As water, can use the pure water of ion exchange water, ultrafiltration water, reverse osmosis water, distilled water etc., perhaps ultra-pure water.In addition,, can when the long preservation ink composite, prevent the generation of mould or bacterium by using with the ultraviolet ray irradiation or adding the water that hydrogen peroxide is sterilized, therefore preferred.
As the organic solvent that in fluid composition of the present invention, contains, can enumerate glycol ether compounds, alkyl diol compounds or multicomponent alcoholics compound etc.By using these compounds as organic solvent, can obtain good anti-obstruction and ejection stability, simultaneously colour rendering and glossiness are significantly reduced, thereby can improve the picture quality of document image.
Consider that from the viewpoint that improves picture quality the content of these compounds (referring to its total amount in the occasion of mixing multiple compound) is preferably 1 of fluid composition.0 weight % is above to 70 weight %, more preferably 10~50 weight %.
As the glycol ether compounds, can enumerate: triethylene glycol monobutyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monomethyl ether etc.Triethylene glycol monobutyl ether especially preferably.
The content of glycol ether compounds in fluid composition is preferably 0.1~30.0 weight %, and more preferably 1.0~20.0 weight % are preferably 2.0~10.0 weight % especially.
As the alkyl diol compounds, can enumerate: 1,2-hexylene glycol, 1,2-pentanediol, 2-butene-1,4-glycol, 2-ethyl-1,3-hexylene glycol, 2-methyl-2,4-pentanediol etc.Particularly preferably be 1, the 2-hexylene glycol.
The content of alkyl diol compounds in fluid composition is preferably 0.1~30.0 weight %, and more preferably 1.0~20.0 weight % are preferably 2.0~10.0 weight % especially.
As multicomponent alcoholics compound, can enumerate: the water-miscible organic solvent of glycerine, ethylene glycol, triethylene glycol, propane diols, diethylene glycol (DEG), pentamethylene glycol, trimethylene, DPG, tetraethylene glycol etc.Particularly preferably be glycerine.
Multicomponent alcoholics compound is preferably 0 at the content of fluid composition.1~50.0 weight %, more preferably 1.0~40.0 weight % are preferably 8.0~30.0 weight % especially.
Fluid composition of the present invention can also contain in acetylenic diols compound, alkynol compounds or the polysiloxanes compounds any as surfactant.So just can make not remarkable deterioration of colour rendering and glossiness, thereby can improve the ejection stability of fluid composition.
The content of surfactant in fluid composition is preferably 0.1~10.0 weight %, and more preferably 0.1~3.0 weight % is preferably 0.3~2.0 weight % especially.
In addition, consider that from improving infiltrative viewpoint as the result who adds surfactant, the surface tension of fluid composition is preferably 15~45dyn/cm, more preferably 20~40dyn/cm is preferably 25~35dyn/cm especially.
In the present invention, as the acetylenic diols compound of useful as surfactants, can use 0LFINE E1010, STG, Y (all being trade name, day letter chemical company system), サ-Off
イThe commercially available product of ノ-Le 82,104,440,465,485 (all being trade name, Air Products andChemicals Inc. system) etc.
Alkynol compounds as preferably using in the present invention can use 3,5-dimethyl-1-hexin-3-alcohol, 2,4-dimethyl-5-hexin-3-alcohol, Surfynol 61 (trade name, AirProducts and Chemicals Inc. system) etc.
As the preferred polysiloxanes compounds that uses in the present invention, can use the compound represented by following general formula etc.
(in the formula, R
1~R
9Represent C independently of one another
1~C
6Alkyl; J, k and x represent the integer more than 1 independently of one another; EO represents ethyleneoxy; PO represents propenyloxy group; M and n represent the integer more than 0; M+n represents the integer more than 1; Repetitive EO and PO are no matter how its order all can be used, and it can be random, also can be block).
Can use BYK 347, the BYK 348 etc. of BYK-Chemie Japan corporate system particularly.
6.
Other compositions
Fluid composition of the present invention can also contain normally used solvent as required in the aqueous ink composition that ink mist recording is used.As such solvent, can enumerate 2-Pyrrolidone, triethanolamine, carbohydrate etc.
Concrete example as carbohydrate, can enumerate monosaccharide, disaccharides, oligosaccharides (containing three carbohydrates and tetrose class), as preferred carbohydrate, can enumerate: glucose, mannose, fructose, ribose, wood sugar, arabinose, galactolipin, glycuronic acid, glucitol, D-sorbite, maltose, cellobiose, lactose, sucrose, trehalose, maltotriose etc.Herein, polysaccharide is meant the carbohydrate of broad sense, and its implication comprises the material that alginic acid, alpha-cyclodextrin, cellulose etc. exist widely at nature.In addition, as the derivative of these carbohydrates, can enumerate: the reduced sugar of above-mentioned carbohydrate (for example sugar alcohol) is used general formula HOCH
2(CHOH)
nCH
2OH (in the formula, n represents 2~5 integer) expression), oxosugar (for example glycuronic acid, uronic acid etc.), amino acid, thiosugar etc.Particularly preferably be sugar alcohol,, can enumerate maltitol and D-sorbite etc. as its concrete example.In addition, as commercially available product, can buy HS-300, HS-500 (registration mark of the former business of woods) etc.
In fluid composition of the present invention, also have to add spray nozzle clogging and prevent that agent, anticorrisive agent, antioxidant, electrical conductivity from adjusting agent, pH adjusts agent, viscosity modifier, surface tension adjustment agent, oxygen absorbent, ultra-violet absorber, chelating agent etc.
Concrete example as anticorrisive agent, can enumerate: Sodium Benzoate, sodium pentachlorophenol, (the 2-pyridinethiol-1-oxide sodium) of 2-pyridine mercaptan-1-sodium oxide molybdena, sodium sorbate, dehydro sodium acetate, 1,2-bisbenzothiazole quinoline-3-ketone (Proxel CRL, the ProxelBDN of Avecia company, Proxel GXL, Proxel XL-2, Proxel TN) etc.
And then, as the concrete example of pH conditioning agent, cosolvent and antioxidant, can enumerate: the amine of diethanol amine, triethanolamine, Propanolamine, morpholine etc. and their modifier; The inorganic salts of potassium hydroxide, NaOH, lithium hydroxide etc.; Ammonium hydroxide, quaternary ammonium hydroxide (tetramethyl-ammonium etc.); The carbonate of potash, sodium carbonate, lithium carbonate etc. and their phosphate etc.; The perhaps ureas of N-N-methyl-2-2-pyrrolidone N-, urea, thiocarbamide, tetramethylurea etc.; The allophanate class of allophanate, uramido methyl formate etc.; The biuret class of biuret, dimethyl biuret, tetramethyl biuret etc. etc.; L-ascorbic acid and salt thereof.In addition, as the concrete example of ultra-violet absorber, can enumerate the oxide of Tinuvin 328,900,1130,384,292,123,144,622,770,292, Irgacor 252,153, Irganox1010,1076,1035, MD 1024 and the lanthanide series of Ciba-Geigy manufacturing.As the concrete example of chelating agent, can enumerate ethylenediamine tetra-acetic acid (EDTA).
In addition,, also can contain the organic solvent of alcohols etc.,, can enumerate methyl alcohol, ethanol, normal propyl alcohol, isopropyl alcohol, n-butanol, sec-butyl alcohol, the tert-butyl alcohol, isobutanol, n-amyl alcohol etc. as object lesson in order to adjust viscosity and in the permeability of record on the thing.Particularly preferably be monohydric alcohol.
The content of high boiling organic solvent in fluid composition is preferably 0.1~30.0 weight %, and more preferably 1.0~10.0 weight % are preferably 2.0~5.0 weight % especially.
7.
Ink composite
Ink jet recording method in another technical scheme of the present invention is undertaken by aforesaid liquid composition and ink composite are printed onto on the recording medium together.This ink composite contains colouring agent, water and water-miscible organic solvent at least.Below each composition that constitutes ink composite is described.
(1) colouring agent
Ink composite contains pigment or dyestuff as colouring agent, preferably uses pigment.As pigment, can use inorganic pigment, organic pigment.As inorganic pigment, except titanium oxide and iron oxide, can also use the carbon black of making by known method such as contact method, heating oven process, cracking process.In addition, as organic pigment, can use AZOpigments (comprising azo lake, insoluble azo colour, condensed azo pigment, chelating AZOpigments etc.), polycycle pigment (for example phthalocyanine color, perylene dye, perinone pigment, anthraquinone pigment, quinacridone pigment, triazine dioxin pigment, thioindigo color, isoindolinone pigment, quinophthalone pigment etc.), pigment chelate (for example basic dye type chelate, acid pigment type chelate etc.), nitropigments, nitroso pigments, nigrosine etc.
As the carbon black that can be used for black ink, can enumerate No.2300, No.900, MCF 88, No.33, No.40, No.45, No.52, MA 7, MA 8, MA 100, the No.2200B etc. of Mitsubishi Chemical's system; The Raven 5750,5250,5000,3500,1255,700 of Columbia Co., Ltd's system etc.; Rega 1400R, the 330R of Cabot corporate system, 660R, MogulL, Monarch700,800,880,900,1000,1100,1300,1400 etc.; The Color Black FW1 of Degussa corporate system, FW2, FW2V, FW18, FW200, S150, S160, S170, Printex 35, U, V, 140U, Special Black 6,5,4A, 4 etc.
As the pigment that can be used for Yellow ink, can enumerate C.I. pigment yellow 1,2,3,12,13,14C, 16,17,24,34,35,37,53,55,65,73,74,75,81,83,93,94,95,97,98,108,109,110,113,114,116,117,120,128,129,133,138,139,147,150,151,153,154,155,156,167,172,173,180,185,195 etc.
As the pigment that can be used for magenta ink, can enumerate C.I. paratonere 1,2,3,5,7,9,10,11,12,14,17,18,23,30,31,38,42,48 (Ca), 48 (Mn), 57 (Ca), 57:1,67,88,112,114,122,123,144,147,149,150,151,166,168,170,171,175,176,177,178,179,184,185,187,202,209,219,224,245 etc., and C.I. pigment violet 19.
As the pigment that can be used for cyan ink, can enumerate C.I. pigment blue 1,2,3,15:1,15:2,15:3,15:4,15:5,15:34,16,18,22,25,60,65,66, C.I. vat blue 4,60 etc.
As the pigment that can be used for red ink, can enumerate C.I. paratonere 17,49:2,112,149,177,178,188,255,264 etc.
As the pigment that can be used for purple ink, can enumerate C.I. pigment violet 3,9,19,23,31,32,33,36,38,43,50 etc.
The particle diameter of these pigment is preferably below 200nm, more preferably below 100nm.
The content of pigment in ink composite is 0.01~10 weight %, is preferably 0.1~6.0 weight %, more preferably 0.5~4.0 weight %.
In addition, as the pigment of above-mentioned colouring agent, preferably use dispersant to make dispersing of pigments liquid in advance, and then add in the printing ink.As dispersant, can enumerate natural polymer.As its concrete example, can enumerate the protein-based of animal glue, gelatin, casein, albumin etc.; The natural gum class of gum arabic, bassora gum etc.; The portugal glycoside of saponarin etc.; The alginate derivatives of alginic acid, propylene glycol alginate, alginic acid triethanolamine, ammonium alginate etc.; The cellulose derivative of methylcellulose, carboxymethyl cellulose, hydroxyethylcellulose, ethyl hydroxylated cellulose etc. etc.
As above-mentioned dispersant, preferably also have synthetic high polymer, can enumerate particularly: polyvinyl alcohol; The polyvinylpyrrolidone class; The acrylic resin of polyacrylic acid, acrylic acid-acrylonitrile copolymer, potassium acrylate-acrylonitrile copolymer, vinyl acetate-acrylate copolymer, acrylic acid and acrylic ester copolymers etc.; The styrene-propene acid resin of styrene-propene acid copolymer, styrene-methacrylic acid copolymer, styrene-methacrylic acid-acrylate copolymer, styrene--acrylic copolymer, styrene--acrylic acid and acrylic ester copolymers etc.; The vinyl acetate lipin polymer of styrene-maleic acid copolymer, styrene-maleic anhydride copolymer, vinyl naphthalene-acrylic copolymer, vinyl naphthalene-maleic acid, vinylacetate-ethylene copolymer, vinylacetate-fatty acid vinyl ester ethylene copolymer, vinylacetate-maleate copolymer, vinylacetate-crotonic acid copolymer, vinylacetate-acrylic copolymer etc. and their salt.
Wherein, particularly preferably be the copolymer that the monomer by monomer with hydrophobic group and possess hydrophilic property group forms, and the polymer that forms by a kind of monomer that in its molecular structure, has hydrophobic group and hydrophilic radical simultaneously.This copolymer can be any in random copolymer, the block copolymer.In addition, as above-mentioned salt, can enumerate the salt that forms with diethylamine, ammonia, ethamine, triethylamine, propylamine, isopropylamine, di-n-propylamine, butylamine, isobutyl amine, triethanolamine, diethanol amine, aminomethyl propanol, morpholine etc.
The weight average molecular weight of these copolymers is about 1,000~1,000,000, is preferably about 3,000~500,000 more preferably 5,000~300,000.
As pigment,, can not add dispersant in the occasion of using following self-dispersion type pigment, but do not using from the occasion of disperseing shape pigment, the content of above-mentioned dispersant is generally 0.001~14.0 weight %, is preferably 0.01~9.0 weight %, is preferably 0.05~6.0 weight % especially.
In ink composite of the present invention, as colouring agent, preferably use those pigment that does not need dispersant just can disperse and/or be dissolved in the water, just be commonly referred to as self-dispersion type pigment.The surface treatment that at least a functional group in surface by making pigment and carbonyl, carboxyl, hydroxyl or the sulfonic group or its salt combine can be so that this pigment need dispersant just to disperse and/or be dissolved in the water.Specifically, by the physical treatment or the chemical treatment (oxidation processes of for example utilizing hypochlorous acid, sulfonic acid etc. to carry out) of vacuum plasma etc., the molecule grafting that makes functional group or contain functional group is attached on the surface of pigment and obtains.In the present invention, the functional group that it can be single kind that grafting is attached to a functional group on the pigment particles also can be multiple functional group.Be used for the kind of functional group of grafting and the degree of grafting, can determine by considering that dispersion stabilization, color depth and the drying property in the ink gun front in printing ink wait aptly.The pigment that uses as self-dispersion type pigment can be identical with above-mentioned pigment.
In the present invention, the STA representation that pigment is not needed dispersant also can stably exist in water is " disperseing and/or dissolving ".Also there are many occasions to be difficult to distinguish clearly the state that material is dissolving or dispersion actually.According to the present invention, so long as do not need dispersant also can stably be present in pigment in the water, just no matter its state is to disperse or dissolving, such pigment all can use.Therefore, in this manual, the pigment that also those is not needed dispersant also can be in water stably to exist sometimes is called colouring agent, but this and do not mean that and get rid of the pigment that becomes dispersity.
(2) water, organic solvent and other compositions
Ink composite among the present invention contains water and water-miscible organic solvent.Water, organic solvent and other compositions can be identical with above-mentioned fluid composition.
Above-mentioned ink composite can prepare according to a conventional method, for example can be by each above-mentioned composition being disperseed by suitable method and mixing and make.Preferably at first pass through with other compositions that use as required ion exchange water, pigment, dispersant, organic solvent, use suitable dispersing apparatus (for example ball mill, sand mill, attritor, rolling grinder, agitator mill, Henschel mixer, colloid mill, ultrasonic homogenizer, jet mill, angmill etc.) to mix, prepare uniform dispersible pigment dispersion.Then, by with ion exchange water, organic solvent with other compositions that use as required, fully stir at normal temperatures and prepare printing ink solvent.Use suitable mixer that above-mentioned printing ink solvent is stirred, under this stirring, drip above-mentioned dispersible pigment dispersion and fully stirring at leisure.After fully stirring, filter removing those oversize grain that becomes plugging reason and foreign matters, thereby obtain required ink composite.
In addition, in the occasion of using self-dispersion type pigment as colouring agent, except pigment is carried out surface treatment so that pigment itself become the dispersity, can also with the above-mentioned ink composite that similarly prepares.
8.
Print cartridge
According to another technical scheme of the present invention, provide a kind of print cartridge that is used to accommodate the aforesaid liquid composition.This print cartridge can form according to the structure of only accommodating fluid composition, also can form according to accommodating the two structure of fluid composition and ink composite.
9.
Recording method
According to another technical scheme of the present invention, provide a kind of by fluid composition and ink composite are attached to the method that writes down on the recording medium.According to the preferred technical solution of the present invention, preferably carry out record with the ink jet recording method that prints according to a kind of being ejected on the recording medium by droplet with fluid composition and ink composite.
According to ink jet recording method of the present invention, fluid composition and ink composite can be sprayed in the same processing time.Herein, what is called " same processing time " is meant in once writing down (once passing through), utilizes fluid composition and ink composite to handle, to form a specific image.Therefore, except the occasion that both are all sprayed at the same time, " same processing time " also is included in once and by interior elder generation ink composite sprayed, and then with the occasion of fluid composition ejection, and once fluid composition is being sprayed, and then with the occasion of ink composite ejection by interior elder generation.
In addition, according to ink jet recording method of the present invention, can be at first carry out record on the recording medium, and then the temperature more than the glass transition temperature of above-mentioned polymer particles is carried out heat treated to recording surface by aforesaid liquid composition and color ink compositions are attached to together.By heat treated, can improve the glossiness of non-printing further.
According to the preferred technical solution of the present invention, a kind of like this recording method is provided, that is, ink composite is printed on the recording medium, after this or in the same processing time, fluid composition is printed at least the zone of not printed by ink composite.According to this recording method, can be on the high gloss ink-jet dedicated paper (glossy paper hereinafter referred to as) PM photographic paper that for example resembles the Seiko Epson corporate system etc., make the glossiness of the part of being printed by ink composite and the glossiness of non-printing reach equal degree, thereby can suppress the phenomenon of lustre lacking uniformity.
In addition, according to another technical scheme of the present invention, provide a kind of printing process that fluid composition is printed on the printing zone of ink composite.According to this method, can be on glossy paper, make the glossiness of the part of being printed by ink composite and the glossiness of non-printing reach more equal degree, thereby can suppress lustre lacking uniformity.In addition, on common paper, can improve the colour rendering of ink composite, and can suppress painted inhomogeneous, particularly at recycled writing paper or resemble the official and make on the paper of high hydrophobicity the postcard, enhanced water resistance, this advantage is more remarkable.
According to the recording method of using fluid composition of the present invention, when recording medium is the occasion of glossy paper, can enjoy the advantage that improves glossiness and suppress lustre lacking uniformity, on the other hand, when recording medium is the occasion of common paper, can enjoy and improve colour rendering and suppress painted uneven advantage.Therefore,, the kind of recording medium is not had particular determination according to the recording method of using fluid composition of the present invention, all can suppress since recording medium that influence caused was inhomogeneous.
In addition, according to another optimized technical scheme of the present invention, provide a kind of on recording medium method of printing, promptly, according to ink jet recording method of the present invention, print on recording medium by the spray volume of adjustment fluid composition and the spray volume of ink composite, reach substantial even at the printing zone of recording medium and the glossiness of non-printing zone so that make.The method of detail record is same on No. 02/08788 open brochure of the open WO of this recording method and international patent application.According to this method, can realize the uneven high-quality image of lackluster degree so that the ratio of the glossiness relevant with the difference of height of load capacity (duty) on the printed article becomes minimum (maximum glossiness/minimum glossiness equal 1 or near 1).
As the optimal technical scheme of the method for the spray volume of spray volume that is used to adjust the aforesaid liquid composition and ink composite, preferably the numerical value according to the load capacity of ink composite carries out.Can enumerate following method particularly, that is,, just increase the spray volume of fluid composition when the low occasion of the load capacity of ink composite; And work as the high occasion of load capacity of ink composite, just reduce the spray volume of fluid composition.Preferably the load capacity at ink composite is 20~60%, and the occasion in 30~50% scope particularly wishes to adjust the spray volume of fluid composition.
In addition,, can enumerate,, be adjusted to the aggregate value of the spray volume of ink composite and fluid composition a certain amount of when the low occasion of the load capacity of ink composite as other method for optimizing; And,, all the spray volume of fluid composition is adjusted to certain a small amount of just no matter the load capacity of ink composite is much when the high occasion of load capacity of ink composite.For example can enumerate,, just the aggregate value of the spray volume of ink composite and fluid composition be calculated in 20~60% the scope adjusted to by the aggregate value of load capacity when the low occasion of the load capacity of ink composite; And, just the spray volume of fluid composition is become the certain value in 1~20% the scope by the load capacity adjustment when the high occasion of load capacity of ink composite.
10.
Ink-jet recording apparatus
Utilize accompanying drawing explanation can implement the ink-jet recording apparatus of ink jet recording method of the present invention below.
The ink-jet recording apparatus of Fig. 1 has a kind of like this structure, and it can be accommodated in ink composite and fluid composition in the ink tank, and by the printing ink conduit ink composite and fluid composition is supplied in the record head.That is to say that record head 1 and ink tank 2 are interconnected by printing ink conduit 3.Herein, the inside of ink tank 2 is separated into different parts, ink composite wherein is set, according to circumstances is the cell of the cell of a plurality of color ink compositions and fluid composition.
Record head 1 is driven by the synchronous belt 6 that is driven by motor 5 along support 4.On the other hand, be positioned position with record head 1 opposite as the paper 7 of recording medium by paper pressing shaft 8 and guide rod 9.Should illustrate, a lid 10 is set in this technical scheme.This lid 10 is connected with a suction pump 11, carries out so-called clean operation.Fluid composition that is sucked and ink composite enter and lodge in the waste ink tank 13 by conduit 12.According to the present invention, in lid 10, there is not fluid composition to be detained, can carry out good clean operation.
Waste liquid printing ink foaming when being suppressed at clean operation has the porous material by for example nonwoven and so in the inside of lid 10.According to because clean method or used ink composite and the different foaming situations that cause of liquid combination species can randomly be provided with this porous material, but consider from the viewpoint that prevents to stop up, should be so that this porous material to be set.
The expanded view of the nozzle face of record head 1 has been shown among Fig. 2.The part of representing with 1b is the nozzle face of fluid composition, and the nozzle 21 that is used to spray fluid composition longitudinally is provided with.On the other hand, the part of representing with 1c is the nozzle face of ink composite, sprays Yellow ink composition, magenta ink compositions, cyan ink composition and black ink composition respectively from nozzle 22,23,24,25.
And then, the ink jet recording method that utilizes Fig. 3 to illustrate to use the record head put down in writing among this Fig. 2 to carry out.Record head 1 moves along the direction of arrow A.In this moving process, from nozzle face 1b ejection fluid composition, the result forms banded fluid composition adhering zone 31 on recording medium 7.Along the arrow B of paper feeding direction recording medium 7 is measured handover in accordance with regulations then.In this time, record head 1 moves along the direction opposite with arrow A among the figure, turns back to the position of recording medium 7 left ends.Then, adhered to the fluid composition adhering zone printing ink composition of fluid composition, thereby formed printing zone 32.
In addition, in the record head 1 as Fig. 4 record, nozzle also can constitute according to complete transversely arranged mode.In the figure, 41a and 41b are the nozzles of fluid composition, and spray Yellow ink composition, magenta ink compositions, cyan ink composition and black ink composition respectively from nozzle 42,43,44,45.In the record head of this technical scheme, record head 1 all can print in arbitrary approach in outlet that makes the support back and forth movement and loop, considers from this point, compares with the occasion of using record head shown in Figure 2, and can expect can be by the faster speed printing.
And then, preferably resembling the surface tension of adjusting fluid composition as described above and ink composite, so just can make, no matter be above-mentioned any order of adhering to, all can more stably obtain high-quality printing.In this occasion, also the nozzle of fluid composition can be merged into a nozzle (for example can save the nozzle 41b among the figure), can reach the high speed of the miniaturization and the printing of record head so further.
And then in ink-jet recording apparatus, replenishing of ink composite can be undertaken by the print cartridge of changing as ink tank.In addition, this ink tank and record head are become one.
The preferred example of the ink-jet recording apparatus that uses such ink tank has been shown among Fig. 5.In the figure, for the device of Fig. 1 in identical parts, put on identical Ref. No..In the technical scheme of Fig. 5, record head 1a and 1b, ink tank 2a and 2b all become one.Record head 1a and 1b spray ink composite and fluid composition respectively.The printing process device with Fig. 1 basically is identical.And in this technical scheme, record head 1a and ink tank 2a and record head 1b and ink tank 2b move on support 4 simultaneously.
And then, one be can be provided with and heater that the recording medium that prints is heated, the preferred example of an ink-jet recording apparatus shown in Fig. 6 are used for.In Fig. 6, except heater 14 was set, all the other were identical with the device shown in Fig. 1.This heater 14 can be a kind of by contact the device that heats with recording medium, also can be the heater that does not contact with recording medium by irradiation infrared ray etc. or blowing hot-air etc.
Embodiment
Wait below by embodiment to be described more specifically the present invention, but the present invention is not subjected to the qualification of these embodiment etc.
1.
The preparation of polymer particles
Prepare various polymer particulates according to following method.The glass transition temperature Tg of polymer particles is measured according to JIS K6900; Turbidity uses nephelometer (Japanese electric look industry system WATER-ANALYZER 2000), is that the cell of 10mm is measured with thickness.
(1)
The oil-in-water type emulsion
In a reaction vessel that is equipped with mixer, reflux condenser, Dropping feeder and thermometer, add ion exchange water 900g and lauryl sodium sulfate 3g, Yi Bian under agitation use nitrogen replacement, Yi Bian be warming up to 70 ℃.Temperature in the container is remained 70 ℃, add potassium peroxydisulfate 4g as polymerization initiator, after treating its dissolving, in 4 hours, in this reactant liquor, drip a kind of continuously in advance by under agitation in ion exchange water 450g, adding the emulsion that lauryl sodium sulfate 3g, acrylamide 20g, styrene 300g, butyl acrylate 640g and methacrylic acid 30g make.After dripping end, carry out 3 hours slaking.The oil-in-water type emulsion that is obtained is cooled to normal temperature, then by it being adjusted into solid constituent 40%, pH 8 to wherein adding ion exchange water and sodium hydrate aqueous solution.
The glass transition temperature (Tg) of the polymer particles in this oil-in-water type emulsion is 15 ℃, and average grain diameter is 130nm, and weight average molecular weight (Mw) is 500,000, and the minimum film temperature (MFT) of making is 0 ℃, and turbidity is more than the 30mg/l.
(2)
Colloidal sol type emulsion (alkali-soluble emulsion)
In a reactor that is equipped with mixer, reflux condenser, Dropping feeder and thermometer, add 2 parts of 130 parts of ion exchange waters and potassium peroxydisulfates, be warming up to 80 ℃.A kind of to wherein adding continuously in 4 hours in advance by under agitation in 280 parts of ion exchange waters, adding 55 parts of ethyl acrylates, 37 parts of methyl acrylates, 6 parts of methacrylic acids, adjusting the dispersion thing of 3 parts of the TGA monooctyl esters of agent and 2.5 parts of monomer mixtures of making of polyvinyl alcohol so that it carries out polymerisation as molecular weight.After adding end continuously, 80 ℃ of reactions of carrying out 30 minutes.
Then, add 10% sodium hydrate aqueous solution in reactor, its addition is the mole that equates with the methacrylic acid that adds, and carries out 1 hour heat treated again under 80 ℃, add an amount of ion exchange water then, obtained solid component concentration and be 15% alkali-soluble emulsion.The acid number of this alkali-soluble emulsion is 40, and the pH value is 9.2.
The glass transition temperature Tg of the polymer particles in this alkali-soluble emulsion (according to the mensuration of JISK6900) is 25 ℃, and average grain diameter is below the 50nm, and weight average molecular weight (Mw) is 1.1 ten thousand, and the minimum film temperature (MFT) of making is 15 ℃, and turbidity is below the 30mg/l.
(3)
Colloidal sol type emulsion (containing sulfonic emulsion)
In the reaction vessel of a glass system, add diox 100g, temperature in the container is remained 25 ℃ on one side then,, stirred 2 hours, obtained sulfuric anhydride-diox complexs on one side to wherein adding sulfuric anhydride 11.8g.
Then, temperature in the container is remained 25 ℃ on one side, (weight ratio is 10/80/10 on one side the complex of above-mentioned acquisition all to be added to the ternary block polymer of styrene/isoprene/styrene, Mw=100000) in the THF solution of 100g (concentration=15%), continue again to stir 2 hours, make solution.
In a flask, add entry 1200g, NaOH 7.1g, neopelex 1g, temperature in the container is remained 40 ℃.On one side temperature in the container is remained 40 ℃, 1 hour in to flask in drip above-mentioned solution whole on one side.After the dropping, stirred 2 hours down, by decompression distillation solvent is removed then and made water continue left behind, obtained concentration and be 15% the sulfonic emulsion that contains at 40 ℃.Sulfonic acid content in the solid constituent is 1.2mmol/g.
In this glass transition temperature Tg that contains the polymer particles in the sulfonic emulsion is 25 ℃, and average grain diameter is below the 50nm, and weight average molecular weight (Mw) is 10,000, and the minimum film temperature (MFT) of making is 15 ℃, and turbidity is below the 30mg/l.
2.
The preparation of fluid composition
In each example, the amount of the content of modification polyallylamine, polymine or derivatives thereof and polymer particles (emulsion) all is solid constituent conversion amounts.
(1) about the inventive embodiment in first technical scheme
Fluid composition A1
Use the polymer particles of above-mentioned acquisition, preparation contains the fluid composition A1 of following each composition of composition.
Dimethyl polyallylamine 5.0 weight %
(molecular weight 10,000/ dimethyl degree of modification: 50mol%)
Contain sulfonic emulsion 2.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition A2
Except with dimethyl polyallylamine (molecular weight 10,000/ dimethyl degree of modification: 50mol%) change to dimethyl polyamines (dimethyl polyamine) (molecular weight 10,000/ dimethyl degree of modification: 100mol%) in addition, similarly obtain fluid composition A2 with fluid composition A1.
Fluid composition A3
Except with dimethyl polyallylamine (molecular weight 10,000/ dimethyl degree of modification: 50mol%) change to dimethyl polyamines (molecular weight 2,000/ dimethyl degree of modification: 50mol%) in addition, similarly obtain fluid composition A3 with fluid composition A1.
Fluid composition A4
Except with dimethyl polyallylamine (molecular weight 10,000/ dimethyl degree of modification: 50mol%) change to dimethyl polyamines (molecular weight 2,000/ dimethyl degree of modification: 100mol%) in addition, similarly obtain fluid composition A4 with fluid composition A1.
Fluid composition A5
Change to the oil-in-water type emulsion except containing sulfonic emulsion, similarly obtain fluid composition A5 with fluid composition A4.
Fluid composition A6
Change to the alkali-soluble emulsion except containing sulfonic emulsion, similarly obtain fluid composition A6 with fluid composition A4.
Fluid composition A7
Change to the AQACER593 that belongs to the modified polypropene emulsion except containing sulfonic emulsion, similarly obtain fluid composition A7 with fluid composition A4.
Fluid composition A8
Contain the sulfonic emulsion except not adding, similarly obtain fluid composition A8 with fluid composition A4.
Fluid composition A9
Fluid composition A9 is a kind of composition that contains following each composition of composition, but does not wherein contain emulsion, and uses the polymine of the resin that belongs to cationic to replace the dimethyl polyallylamine to come the obtaining liq composition.
Polymine (molecular weight 1,000) 5.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition A10
Fluid composition A10 is mixed with the fluid composition that a kind of each composition that contains following composition does not still contain dimethyl polyallylamine and emulsion.
Glycerine 30.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
The surface tension of fluid composition A1~A10 uses the CBVP-Z of consonance interface science corporate system to measure, and the result is 25~35dyn/cm.
The composition of aforesaid liquid composition A1~A10 is shown in Table 1.
Fluid composition B1
Use the polymer particles of above-mentioned acquisition, preparation contains the fluid composition B1 of following each composition of composition.
Polyallylamine (molecular weight 10,000) 0.5 weight %
Contain sulfonic emulsion 2.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition B2
Except polyallylamine (molecular weight 10,000) being changed to polyamines (molecular weight 2,000) and the addition of glycerine being changed to beyond the 20 weight % by 25 weight %, similarly obtain fluid composition B2 with fluid composition B1.
Fluid composition B3
Preparation contains the fluid composition B3 of following each composition of composition.
Polyallylamine (molecular weight 10,000) 4.0 weight %
Polyallylamine (molecular weight 2,000) 1.0 weight %
Contain sulfonic emulsion 2.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition B4
Preparation contains the fluid composition B4 of following each composition of composition.
Polyallylamine (molecular weight 10,000) 1.0 weight %
Polyallylamine (molecular weight 2,000) 2.0 weight %
Contain sulfonic emulsion 2.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition B5
Change to the oil-in-water type emulsion except containing sulfonic emulsion, similarly obtain fluid composition B5 with fluid composition B4.
Fluid composition B6
Change to the alkali-soluble emulsion except containing sulfonic emulsion, similarly obtain fluid composition B6 with fluid composition B4.
Fluid composition B7
Change to the AQACER593 that belongs to the modified polypropene emulsion except containing sulfonic emulsion, similarly obtain fluid composition B7 with fluid composition B4.
Fluid composition B8
Contain the sulfonic emulsion except not adding, similarly obtain fluid composition B8 with fluid composition B4.
Fluid composition B9
Fluid composition B9 is mixed with the fluid composition that contains following each composition of composition, wherein contains polymine and replace polyallylamine.
Polymine (molecular weight 1,000) 5.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition B10
Fluid composition B10 is mixed with a kind of each composition of following composition that contains, but does not contain the fluid composition of polyallylamine.
Glycerine 30.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
The surface tension of fluid composition B1~B10 uses the CBVP-Z of consonance interface science corporate system to measure, and the result is 25~35dyn/cm.
The composition of aforesaid liquid composition B1~B10 shows in the table 2.
(2) about the inventive embodiment in second technical scheme
Fluid composition C1
Use the polymer particles of above-mentioned acquisition, preparation contains the fluid composition C1 of following each composition of composition.
Polymine (molecular weight 1,000) 0.25 weight %
Polyallylamine (molecular weight 5,000) 0.25 weight %
Contain sulfonic emulsion 2.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition C2
In fluid composition C1,, similarly obtain fluid composition C2 with fluid composition C1 except polyene propylene (molecular weight 5,000) is changed to polyallylamine (molecular weight 1,000) in addition.
Fluid composition C3
In fluid composition C2, except with polyallylamine (molecular weight 1,000) addition changes to 4.75 weight % by 0.25 weight %, and the interpolation of glycerine is changed to beyond the 20.0 weight % by 25.0 weight %, similarly obtains fluid composition C3 with fluid composition C2.
Fluid composition C4
In fluid composition C3, change to the oil-in-water type emulsion except containing sulfonic emulsion, similarly obtain liquid with fluid composition C3 and stop composition C4.
Fluid composition C5
In fluid composition C3, change to the alkali-soluble emulsion except containing sulfonic emulsion, similarly obtain fluid composition C5 with fluid composition C3.
Fluid composition C6
In fluid composition C3, change to the AQACER593 that belongs to the modified propylene emulsion except containing sulfonic emulsion, similarly obtain fluid composition C6 with fluid composition C3.
Fluid composition C7
Preparation contains the fluid composition C7 of following each composition of composition.
Polymine (molecular weight 5,000) 0.25 weight %
Polyallylamine (molecular weight 2,000) 4.75 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition C8
Fluid composition C8 is prepared into a kind of each composition of following composition that contains, but does not contain the fluid composition of polyallylamine.
Polymine (molecular weight 1,000) 5.0 weight %
Glycerine 25.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
Fluid composition C9
Fluid composition C9 is prepared into a kind of each composition of following composition that contains, but does not contain the fluid composition of polymine and polyallylamine.
Glycerine 30.0 weight %
Triethylene glycol monobutyl ether 3.0 weight %
オ Le Off イ Application E1010 0.3 weight %
Water surplus
The surface tension of fluid composition C1~C9 uses the CBVP-Z of consonance interface science corporate system to measure, and the result is 25~35dyn/cm.
The composition of aforesaid liquid composition C1~C9 is shown in Table 3.
The preparation of printing ink
Following ink composite with composition of table 4 prepares by following operation.At first, pigment is mixed with dispersion liquid (styrene-propene acid copolymer), be placed on that (diameter 1.7mm is 1 of mixture with bead in the sand mill (peace river prepare made).5 times of amounts (weight)) carry out 2 hours dispersion treatment together.Remove bead then, add other additive, stirred at normal temperatures 20 minutes.Using a kind of aperture is the membrane filter filtration of 5 μ m, has obtained pigment ink.
Table 4
Ink composite | Yellow | Magenta | Cyan | Black |
C.I. pigment yellow-74 | 3.0 | - | - | - |
C.I. pigment violet 19 | - | 1.5 | - | - |
C.I. alizarol saphirol-15:3 | - | - | 1.5 | - |
Carbon black | - | - | - | 2.0 |
The styrene-propene acid copolymer | 1.0 | 0.5 | 0.5 | 2.0 |
BYK-347 | 0.5 | 0.5 | 0.5 | 0.5 |
Gly | 15 | 15 | 15 | 20 |
|
5 | 5 | 5 | 10 |
1,2- |
10 | 10 | 10 | 5 |
TEA | 0.9 | 0.9 | 0.9 | 0.9 |
Water | Surplus | Surplus | Surplus | Surplus |
Add up to | 100 | 100 | 100 | 100 |
In the table,
TEGmBE: triethylene glycol monobutyl ether
1,2-HD: 1, the 2-hexylene glycol
BYK-347: the trade name of polysiloxanes compounds
Gly: ethylene glycol
TEA: triethanolamine
Evaluation test
Estimate 1:
The glossiness test
Any composition among fluid composition A1~A10, B1~B10 and the C1~C9 and printing ink group (ink set) are filled into ink-jet printer (セ イ コ-エ プ ソ Application Co., Ltd. system; MC-2000) in, at ink-jet dedicated paper (セ イ コ-エ プ ソ Application Co., Ltd. system; The PM photography paper) upward prints by the condition of 720 * 720dpi.
Use printed patterns, so that make the load (duty) to the monochrome of the various printing ink of colored and black and two or more secondary colour total become 0% (non-lettering part), 10%, 15%, 40%, 100% respectively through adjusting.
In addition, when the total load that is printed on ink composite when fluid composition is a part below 20%, be that 20% condition is printed according to total total load of the total load of ink composite and fluid composition without exception.
Should illustrate that " load " is meant the value of calculating by following formula.
Load (%)=actual print is counted/(vertical resolution ratio * horizontal resolution ratio) * 100
(in the formula, " actual print is counted " is meant that the actual print of per unit area counts; " vertical resolution ratio " and " horizontal resolution ratio " are meant the resolution ratio of per unit area respectively.So-called 100% load is meant the maximum ink by weight with respect to the monochrome of pixel).
Glossiness evaluation of measuring 1-1
Each glossiness that writes down thing that is obtained is tested according to following method.Using " GP-200 " of village colouring material research company system, is the peak that 42.5 condition is measured glossiness according to 12V 50W, incident beam diameter 1mm, folded light beam diameter 1.Smm, ND 10 optical filters, incidence angle 45 degree, flapping angle 0 degree, standard mirror board.To the value that records by following benchmark evaluation.The peak of glossiness is high more, and the performance that gloss is given in expression is good more.
Metewand is as follows:
S: high gloss is more than 50.
A: high gloss is more than 45.
A
A: high gloss is more than 40.
B: high gloss more than 30, less than 40.
C: high gloss more than 20, less than 30.
D: high gloss more than 10, less than 20.
E: high gloss is a less than 10.
Evaluation result is shown in the following table.
The glossiness visual method is estimated 1-2
According to above-mentioned same printing process, the character image of ISO400 regulation press in printing, with the state of the gloss of visual method evaluation recording medium.
Metewand is as follows:
AA: the reflecting feel that has obtained good uniformity.
A: can obtain basically reflecting feel uniformly, but have the part of a part of gloss difference, some inharmonious senses are arranged slightly.
B: lustre lacking uniformity has inharmonious sense.
Evaluation result following table 5 shown in.
As can be seen, the glossiness that the total of ink composite loads on the part below 20% is high, is peer-level or higher and the total of ink composite loads on the glossiness of the part more than 20%.
Estimate 2:
The colour rendering test
Any composition among fluid composition A1~A10, B1~B10 and the C1~C9 and printing ink group are filled into ink-jet printer (セ イ コ-エ プ ソ Application Co., Ltd. system; MC-2000) in, upward print by the condition of 720 * 720dpi in common paper (Xerox 4024).At this moment, with the condition printing of ink composite according to 70% load, and basically side by side with the condition printing of fluid composition by 10% load.
Measured the optical concentration of the record thing that obtains.Optical concentration is by using the Gretag Macbeth SPM 50 of Gretag corporate system, is being light source with D50, and free of light filter and angle of visibility are to measure under 2 ° the condition.
Metewand is as follows.
Metewand
AA: do not have painted part to be difficult to confirm, compare, being increased in more than 0.06 of its OD value with the occasion that does not have the printed liquid composition with visual method.
A: do not have painted part to be difficult to confirm, compare, being increased in more than 0.03 of its OD value with the occasion that does not have the printed liquid composition with visual method.
B: do not have painted part to confirm easily with visual method, compare with the occasion that does not have the printed liquid composition, its OD value does not reach more than 0.03.
The results are shown in the following table 6.
Estimate 3:
The liquid waste processing performance test
Any composition among fluid composition A1~A10, B1~B10 and the C1~C9 and ink composite are filled into ink-jet printer (セ イ コ-エ プ ソ Application Co., Ltd. system; MC-2000) in, carry out the cleaning (by the clean button of a printer) of record head and the printing of nozzle check pattern then repeatedly.This test operation is carried out 10 times, and normally whether evaluation the print nozzles check pattern, also observes the waste liquid state in the lid in addition.For those fluid compositions that in 10 test operations, reaches normal print nozzles check pattern all, carry out 90 times test operation again, estimate it and whether normally printed check pattern, and observe the state of waste liquid in lid.And then the fluid composition for those all normal print nozzles check pattern in 90 times test operation carries out 100 times above-mentioned test operation again, and carries out same evaluation under 40 ℃ environment.
S: under 40 ℃ environment, whole 100 test operations have all normally printed check pattern, and do not have waste liquid to be detained in lid.
AA: under 20 ℃ environment, whole 100 test operations have all normally printed check pattern, and do not have waste liquid to be detained in lid.
A: under 20 ℃ environment, whole 10 test operations have all normally printed check pattern, and are provided with the waste liquid delay in lid.
B: under 20 ℃ environment, whole 10 test operations have all normally printed check pattern, but have some waste liquids to be detained in lid.
C: under 20 ℃ environment, in whole 10 test operations, can not carry out the normal printing of check pattern sometimes, in lid, have waste liquid to be detained.
The results are shown in the table 6.
Estimate 4:
The liquid waste processing performance test
In above-mentioned evaluation 3, except use is equipped with the ink-jet printer of a lid that possesses nonwoven, and estimates 3 and similarly estimate.
The results are shown in the table 6.
Estimate 5:
The storage stability test
Any composition among fluid composition A1~A10 and the B1~B10 and ink composite are filled into ink-jet printer (セ イ コ-エ プ ソ Application Co., Ltd. system; MC-2000) in, at ink-jet dedicated paper (セ イ コ-エ プ ソ Application Co., Ltd. system; The PM photography paper) upward prints by the condition of 720 * 720dpi and load 40%.It is that 80 ℃ and humidity are that 50% constant temperature and humidity cabinet placed for 1 week that each the lettering sample that is obtained is placed a temperature.After the placement, using the Cretag Macbeth SPM 50 of Gretag Macbeth corporate system, is being light source with D50, and free of light filter and angle of visibility are under 2 ° the condition, measure the value of the CIE-Lab of each lettering sample.By the CIE-Lab value that obtains by pre-colour examining before this measured value and the placement, obtain aberration Δ E according to following formula.
Δ E=[(L* (before placing)-L* (placing the back))
2+ (a* (before placing)-a* (placing the back))
2+ (b* (before placing)-b* (placing the back))
2]
1/2
This result is estimated according to following commentary part benchmark.
Metewand
A: Δ E less than 2
B: Δ E is more than 2
The results are shown in the table 6.
Table 6
Fluid composition | Estimate 2 | Estimate 3 | Estimate 4 | |
|
Embodiment A 1 embodiment A 2 embodiment A 3 embodiment A 4 |
Fluid composition A1 fluid composition A2 fluid composition A3 fluid composition A4 fluid composition A5 fluid composition A6 fluid composition A7 fluid composition A8 fluid composition A9 fluid composition A10 | AA AA AA AA AA AA AA AA A B | A AA A AA AA AA AA AA B A | B B A A A A A A C A | A A A A A A A A B - |
Embodiment B 1 Embodiment B 2 Embodiment B 3 Embodiment B 4 |
Fluid composition B1 fluid composition B2 fluid composition B3 fluid composition B4 fluid composition B5 fluid composition B6 fluid composition B7 fluid composition B8 fluid composition 89 fluid composition B10 | A AA AA AA AA AA AA AA A B | A A A A A A A A B A | B B B B B B B A C A | A A A A A A A A B - |
Embodiment C 1 Embodiment C 2 Embodiment C 3 Embodiment C 4 |
Fluid composition C1 fluid composition C2 fluid composition C3 fluid composition C4 fluid composition C5 fluid composition C6 fluid composition C7 fluid composition C8 fluid composition C9 | A A AA AA AA AA AA A B | A A A A A A A A A | B A A A A A A C A | - - - - - - - - - |
(3) about the inventive embodiment in the 3rd technical scheme
The manufacturing of allylamine is doubted in modification
Be manufactured on modification polyallylamine among the Production Example 1-13 according to following method.Sometimes polyallylamine is called hereinafter " PAA ", allylamine is called " AA ".In addition, if be provided with special instruction, " % " all represents weight %.
Production Example 1
In the four neck split flasks of a 2000ml who is equipped with mixer, Dimroth return channel and thermometer, adding concentration is 63.45% N, and N-dimethyl allylamine hydrochloride aqueous solution 431.24g and concentration are 58.11% monoene propylamin hydrochloride aqueous solution 362.25g.This monomer solution is heated to 60 ℃, add 2, two (2-amidine propane) the dihydrochloride 146.45g of 2 '-azo carry out 120 hours polymerisation as radical initiator.
After polymerisation finishes, be that 50% sodium hydrate aqueous solution 332.78g is so that neutralize hydrochloric acid in the ice-cold concentration of dropping down.After neutralization finishes, under the condition of decompression (80mmHg) and 50 ℃, distill and remove unreacted monomer.
The solution that is obtained carried out electrodialysis process so that its desalination, obtained concentration and be the N of 14.35% free radical type (free-type), the aqueous solution 1914.97g of the copolymer of N-dimethyl allylamine and allylamine (copolymerization ratio is 5:5).
Change the part of this aqueous solutions of polymers into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the copolymer salt hydrochlorate as solvent.The result of elementary analysis is C=44.80, H=9.12, N=12.58.These assay values and calculated value C=44.66, H=9.37, N=13.02 are consistent.
Production Example 2
Modification PAA-2 (N, the copolymer (5/5) of N-dimethyl AA and carbamyl AA)
Manufacturing
In the four neck split flasks of a 1000ml who is equipped with mixer, Dimroth return channel and thermometer, be added in the Production Example 1 concentration that obtains and be the N of 14.35% free radical type, the aqueous copolymers solution 421.29g of N-dimethyl allylamine and allylamine is 35% hydrochloric acid 88.65g in the ice-cold concentration that drips down.Then, it being heated to 50 ℃, is 7.5% Zassol aqueous solution 368.37g to wherein dripping concentration, carries out 24 hours reaction.
After reaction finishes, be that 50% sodium hydrate aqueous solution 34.00g is so that neutralize unreacted hydrochloric acid in the ice-cold concentration that drips down.
The solution that is obtained carried out electrodialysis process so that its desalination, obtained concentration and be the N of 10.30% free radical type, the copolymer of N-dimethyl allylamine and carbamyl allylamine (copolymerization ratio is 5:5) aqueous solution 729.61g (yield 95%).The weight average molecular weight of this copolymer is 1200.
This copolymer is condensed into solid, and examining or check it is 10% dissolubility in all kinds of solvents.Its result, this polymer is insoluble in acetone, acrylonitrile, but dissolves among methyl alcohol, ethanol, isopropyl alcohol, DMSO, the DMF.This result shows, compares with allyl amine polymer, and copolymer of the present invention also can be dissolved in the organic solvent.
Change the part of this aqueous solutions of polymers into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the copolymer salt hydrochlorate as solvent.This result shows that modification polyallylamine of the present invention can become cation type polymer.
The result of elementary analysis is C=48.96, H=8.58, N=18.64.These assay values and calculated value C=48.75, H=9.09, N=18.95 are consistent.In addition, be 47.89% by the result who the copolymer salt hydrochlorate is carried out the carbamyl molar percentage that acid-base titration calculates, the basically identical as a result of this and elementary analysis.
Production Example 3a
Modification PAA-3a (N, the copolymer (5/5) of N-dimethyl AA and methoxycarbonyl group AA)
Manufacturing
In the four neck split flasks of a 1000ml who is equipped with mixer, Dimoth reflux condenser and thermometer, be added in the Production Example 1 concentration that obtains and be the N of 14.35% free radical type, the aqueous copolymers solution 421.29g of N-dimethyl allylamine and allylamine, it is heated to 50 ℃, to wherein dripping purity is 99% dimethyl carbonate 38.67g, carries out 24 hours reaction.
After reaction finishes, under the condition of decompression (80mmHg) and 50 ℃, distill the methyl alcohol of removing as accessory substance, having obtained concentration is the N of the free radical type of 21.98 weight %, the aqueous solution 383.85g (yield 99%) of the copolymer of N-dimethyl allylamine and methoxycarbonyl group allylamine (copolymerization ratio is 5:5).The weight average molecular weight of this copolymer is 1300.
Change the part of this aqueous solutions of polymers into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the copolymer salt hydrochlorate as solvent.The result of elementary analysis is C=50.31, H=8.93, N=11.37.These assay values and calculated value C=50.73, H=8.94, N=11.83 are consistent.In addition, be 49.46% by the result who the copolymer salt hydrochlorate is carried out the methoxycarbonyl group molar percentage that acid-base titration calculates, the basically identical as a result of this and elementary analysis.
Production Example 3b
Modification PAA-3b (N, the copolymer (3/7) of N-dimethyl AA and methoxycarbonyl group AA
Manufacturing
In Production Example 1, except with N, the use amount of the N-dimethyl allylamine hydrochloride aqueous solution (concentration is 63.45 weight %) changes to 258.75g and the use amount of single allylamine hydrochloride aqueous solution (concentration is 58.11 weight %) is changed to beyond the 507.15g, similarly operate with Production Example 1, having obtained concentration is the N of the free radical type of 14.27 weight %, the copolymer of N-dimethyl allylamine and allylamine (copolymerization ratio is 3:7) aqueous solution 1978.93g.
Then, in Production Example 3a, except the concentration of using above-mentioned acquisition is the N of the free radical type of 14.27 weight %, the copolymer of N-dimethyl allylamine and allylamine (copolymerization ratio is 3:7) aqueous solution 390.23g and dimethyl carbonate 54.14g replace the N of the free radical type of manufacturing in Production Example 1, beyond the aqueous copolymers solution of N-dimethyl allylamine and allylamine, 3a similarly operates with Production Example, having obtained concentration is the N of the free radical type of 22.12 weight %, the copolymer of N-dimethyl allylamine and methoxycarbonyl group allylamine (copolymerization ratio is 3:7) aqueous solution 406.02g (yield 100%).The weight average molecular weight of this copolymer is 1300.
Production Example 3C
Modification PAA-3C (N, the copolymer (7/3) of N-dimethyl AA and methoxycarbonyl group AA)
Manufacturing
In Production Example 1, except with N, the use amount of the N-dimethyl allylamine hydrochloride aqueous solution (concentration is 63.45 weight %) changes to 603.74g and the use amount of the monoene propylamin hydrochloride aqueous solution (concentration is 58.11 weight %) is changed to beyond the 217.35g, similarly operate with Production Example 1, having obtained concentration is the N of the free radical type of 14.20 weight %, the copolymer of N-dimethyl allylamine and allylamine (copolymerization ratio is 7:3) aqueous solution 2045.55g.
Then, except the concentration of using above-mentioned acquisition is the N by free radical type of 14.20 weight %, beyond the aqueous copolymers solution 459.32g and dimethyl carbonate 22.08g that N-dimethyl allylamine and allylamine form, 3a similarly operates with Production Example, having obtained concentration is the N of the free radical type of 15.08 weight %, the copolymer of N-dimethyl allylamine and methoxycarbonyl group allylamine (copolymerization ratio is 7:3) aqueous solution 359.63g (yield 99%).The weight average molecular weight of this copolymer is 1200.
Production Example 4
Modification PAA-4's (N, the copolymer (5/5) of N-dimethyl AA and acetylation AA)
Make
In the four neck split flasks of a 500ml who is equipped with mixer, Dimroth return channel and thermometer, be added in the concentration that obtains in the Production Example 1 and be the N of 14.35% free radical type, the aqueous copolymers solution 421.29g of N-dimethyl allylamine and allylamine.At the ice-cold only allylamine of 1/2mol amount that in the acetic anhydride 44.27g of purity 98%, drips down, only in the mole of the acetate of giving birth to pair and the NaOH 34.00g of concentration 50%, should operate repeatedly and carry out, and reaction was carried out 24 hours so that complete soln drips off.
The solution that is obtained carried out electrodialysis process so that its desalination, obtained concentration and be the N of 14.94% free radical type, copolymer (copolymerization ratio 5:5) aqueous solution 522.50g (100%) of N-dimethyl allylamine and acetylation allylamine.The weight average molecular weight of this copolymer is 1200.
Change the part of this aqueous solutions of polymers into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the copolymer salt hydrochlorate as solvent.The result of elementary analysis is C=54.12, H=9.26, N=12.47.These assay values and calculated value C=54.41, H=9.59, N=12.69 are consistent.In addition, be 50.12% by the result who the copolymer salt hydrochlorate is carried out the acetylation molar percentage that acid-base titration calculates, the basically identical as a result of this and elementary analysis.
Production Example 5
Modification PAA-5 (N, the copolymer of N-dimethyl AA and mono amino formoxyl ethylization AA
(5/5)) manufacturing
In the four neck split flasks of a 500ml who is equipped with mixer, Dimroth return channel and thermometer, be added in the Production Example 1 concentration that obtains and be the N of 14.35% free radical type, the aqueous copolymers solution 421.29g of N-dimethyl allylamine and allylamine, it is heated to 50 ℃, to wherein dripping concentration is 50% acrylamide 60.42g, carries out 24 hours reaction.
Obtained concentration and be 18.82% N, copolymer (copolymerization ratio 5:5) aqueous solution 465.52g (97%) that N-dimethyl allylamine and oxygen base formoxyl ethylization allylamine form by free radical type.The weight average molecular weight of this copolymer is 1200.
Change the part of this aqueous solutions of polymers into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the copolymer salt hydrochlorate as solvent.The result of elementary analysis is C=45.84, H=8.69, N=14.38.These assay values and calculated value C=46.16, H=8.80, N=14.68 are consistent.In addition, be 48.15% by the result who the copolymer salt hydrochlorate is carried out single propyl amides molar percentage that acid-base titration calculates, the basically identical as a result of this and elementary analysis.
Production Example 6
Modification PAA-6 (N, the copolymer of N-dimethyl AA and diaminourea formoxyl ethylization AA
(5/5)) manufacturing
In Production Example 5; except using acrylamide 120.83g; similarly operate with Production Example 5, obtained concentration and be the N of 22.30% free radical type, copolymer (copolymerization ratio 5:5) aqueous solution 521.09g (96%) of N-dimethyl allylamine and diaminourea formoxyl ethylization allylamine.The weight average molecular weight of this copolymer is 1200.
Change the part of this aqueous copolymers solution into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the hydrochloride of copolymer as solvent.The result of elementary analysis is C=46.68, H=8.23, N=15.41.These assay values and calculated value C=47.00, H=8.48, N=15.62 are consistent.In addition, be 48.06% by the result who the copolymer salt hydrochlorate is carried out the dipropyl amidatioon molar percentage that acid-base titration calculates, the basically identical as a result of this and elementary analysis.
Production Example 7
Modification PAA-7 (N, the copolymerization of N-dimethyl AA and monosubstituted ethoxy-2-hydroxypropylation AA
Thing (5/5)) manufacturing
In the four neck split flasks of a 500ml who is equipped with mixer, Dimroth return channel and thermometer, be added in the Production Example 1 concentration that obtains and be the N of 14.35% free radical type, the aqueous copolymers solution 421.29g of N-dimethyl allylamine and allylamine, it is heated to 50 ℃, to wherein dripping purity is 100% ethyl glycidyl ether 43.41g, carries out 24 hours reaction.
Obtained concentration and be the N of 22.35% free radical type, copolymer (copolymerization ratio 5: the 5) aqueous solution 463.95g (100%) of N-dimethyl allylamine and monosubstituted ethoxy-2-hydroxypropylation allylamine.The weight average molecular weight of this copolymer is 1200.
Change the part of this aqueous copolymers solution into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the copolymer salt hydrochlorate as solvent.The result of elementary analysis is C=49.44, H=9.41, N=8.59.These assay values and calculated value C=49.21, H=9.53, N=8.83 are consistent.In addition, be 50.23% by the result who the copolymer salt hydrochlorate is carried out monosubstituted ethoxy-2-hydroxypropylation molar percentage that acid-base titration calculates, the basically identical as a result of this and elementary analysis.
Production Example 8
Modification PAA-8 (N, the copolymerization of N-dimethyl AA and diethoxy-2-hydroxypropylation AA
Thing (5/5)) manufacturing
In Production Example 7, except using ethyl glycidyl ether 86.81g, similarly operate with Production Example 7, obtained concentration and be the N of 28.98% free radical type, copolymer (copolymerization ratio 5:5) aqueous solution 504.19g (99%) of N-dimethyl allylamine and diethoxy-2-hydroxypropylation allylamine.The weight average molecular weight of this copolymer is 1200.
Change the part of aqueous copolymers solution into hydrochloride, utilize acetone it to be carried out precipitation process again, obtained the copolymer salt hydrochlorate as solvent.The result of elementary analysis is C=61.78, H=11.11, N=7.89.These assay values and calculated value C=61.57, H=11.20, N=8.01 are consistent.In addition, be 49.62% by the result who the copolymer salt hydrochlorate is carried out monosubstituted ethoxy-2-hydroxypropylation molar percentage that acid-base titration calculates, the basically identical as a result of this and elementary analysis.
Production Example 9
Modification PAA-9 (N, the ternary polymerization of N-dimethyl AA and carbamyl AA and AA
Thing (5/3/2)) manufacturing
In Production Example 2; except using Zassol aqueous solution 221.02g and sodium hydrate aqueous solution 54.40g; similarly operate with Production Example 2; obtained concentration and be the N of 11.65% free radical type, the terpolymer aqueous solution 606.48g (yield 99%) of N-dimethyl allylamine and carbamyl allylamine and allylamine.The weight average molecular weight of this copolymer is 1200.
Production Example 10
(N, the ternary of N-dimethyl AA and methoxycarbonyl group AA and AA altogether for modification PAA-10
The manufacturing of polymers (5/3/2)
In Production Example 3a, except using dimethyl carbonate 23.20g, 3a similarly operates with Production Example, has obtained concentration and be the N of 19.25% free radical type, the terpolymer aqueous solution 390.46g (yield 100%) of N-dimethyl allylamine and methoxycarbonyl group allylamine and allylamine.The weight average molecular weight of this copolymer is 1200.
Production Example 11
Modification PAA-11 (N, the terpolymer of N-dimethyl AA and acetylation AA and AA
(5/3/2)) manufacturing
In Production Example 4; except using acetic anhydride 26.56g and sodium hydrate aqueous solution 20.40g; similarly operate with Production Example 4; obtained concentration and be the N of 13.58% free radical type, the terpolymer aqueous solution 523.48g (100%) of N-dimethyl allylamine and acetylation allylamine and allylamine.The weight average molecular weight of this copolymer is 1200.
Production Example 12
Modification PAA-12 (N, N-dimethyl AA and mono amino formoxyl ethylization AA and AA
Terpolymer (5/3/2)) manufacturing
In Production Example 5; except using acrylamide 36.25g; similarly operate with Production Example 5, obtained concentration and be the N of 17.17% free radical type, the terpolymer aqueous solution 455.93g (100%) of N-dimethyl allylamine and mono amino formoxyl ethylization allylamine and allylamine.The weight average molecular weight of this copolymer is 1200.
Production Example 13
Modification PAA-13 (N, N-dimethyl AA and monosubstituted ethoxy-2-hydroxypropylation AA and AA
Terpolymer (5/3/2)) manufacturing
In Production Example 7, except using ethyl glycidyl ether 26.04g, similarly operate with Production Example 7, obtained concentration and be the N of 19.34% free radical type, the terpolymer aqueous solution 447.07g (100%) of N-dimethyl allylamine and monosubstituted ethoxy-2-hydroxypropylation allylamine and allylamine.The weight average molecular weight of this copolymer is 1200.
The weight average molecular weight (Mw) of the modification polyallylamine that obtains in above-mentioned Production Example is by using the L-6000 of Hitachi type high performance liquid chromatography, measuring according to gel permeation chromatography (GPC method).As eluent stream pump, use the L-6000 of Hitachi; As detector, use ShodexRI SE-61 type differential formula refractive index detector; As pillar, use interconnects the twin columns that form by the GS-220HQ (exclusion limit molecular weight 3,000) of the aqueous gel osmosis type of Asahipak with GS-620HQ (exclusion limit molecular weight 2,000,000).With eluent the concentration adjustment of sample is become 0.5g/100ml, amount of samples is 20 μ l.The sodium-chloride water solution that uses 0.4mol/l is as eluent.Condition according to 30 ℃ of column temperature, flow velocity 1.0ml/ minute is implemented.Use molecular weight to be respectively 106,194,440,600,1470,4100,7100,10300,12600,23000 etc. polyethylene glycol and make calibration curve, obtain the Mw of polymer again according to this calibration curve as standard sample.
Fluid composition D1a
Use the polymer particles and the modification PAA of above-mentioned acquisition to prepare the fluid composition D1a that contains following each composition of composition.
Modification PAA-2 5.0% (solid constituent conversion)
Oil-in-water type emulsion 2.0% (solid constituent conversion)
Glycerine 25.0%
Triethylene glycol monobutyl ether 3.0%
OLFINE E1010 0.3%
Water surplus
Fluid composition D1b
In fluid composition D1a, except replace the oil-in-water type emulsion with colloidal sol type emulsion (alkali-soluble emulsion), similarly obtain the fluid composition of fluid composition D1b with fluid composition D1a.
Fluid composition D1c
In fluid composition D1a, except replace the oil-in-water type emulsion with colloidal sol type emulsion (containing sulfonic emulsion), similarly obtain the fluid composition of fluid composition D1c with fluid composition D1a.
Fluid composition D1d
In fluid composition D1a, except replace the oil-in-water type emulsion with the AQUACER593 (Bik-Chemie Japan K.K. system) that belongs to the modified polypropene emulsion, similarly obtain the fluid composition of fluid composition D1d with fluid composition D1a.
Fluid composition D2a~D12
In fluid composition D1c, except replace modification PAA-2 with modification PAA-3a~13, similarly obtain the fluid composition of fluid composition D2a~12 with fluid composition D1c.
Fluid composition D13
Modification PAA-2 2.4% (solid constituent conversion)
AQUACER593 (Bik-Chemie Japan K.K. system) 1.5% (solid constituent conversion)
Glycerine 28.0%
Triethylene glycol monobutyl ether 3.0%
OLFINE E1010 0.3%
Water surplus
Fluid composition D14
Modification PAA-2 2.4% (solid constituent conversion)
AQUACER513 (Bik-Chemie Japan K.K. system) 1.5% (solid constituent conversion)
Glycerine 28.0%
Triethylene glycol monobutyl ether 3.0%
OLFINE E1010 0.3%
Water surplus
Fluid composition D15
According to containing following each fluid composition of forming with the preparation of the same method of fluid composition D1a.
Unmodified PAA (a day east weaving strain formula is closed the PAA-01 of society's system) 5.0% (solid constituent conversion)
Glycerine 25.0%
Triethylene glycol monobutyl ether 3.0%
OLFINE E1010 0.3%
Water surplus
Liquid combination D16
In fluid composition D15, except replace unmodified PAA with modification PAA-1, similarly obtain the fluid composition of fluid composition D16 with fluid composition D15.
Fluid composition D17
In fluid composition D15, except (number of monomers of the number of monomers of dimethyl AA: AA is 95:5~100:0 with dimethyl modification PAA, and do not contain modification AA monomer in addition) replace beyond the unmodified PAA, similarly obtain the fluid composition of fluid composition D17 with fluid composition D15.
Fluid composition D18
In fluid composition D15, except not adding unmodified PAA, similarly obtain the fluid composition of fluid composition D18 with fluid composition D15.
Fluid composition D19
According to containing following each fluid composition of forming with the preparation of the same method of fluid composition D1a.
Modification PAA-1 2.4% (solid constituent conversion)
Glycerine 28.0%
Triethylene glycol monobutyl ether 3.0%
OLFINE E1010 0.3%
Water surplus
Use the CBVP-Z of consonance interface science corporate system to measure the surface tension of aforesaid liquid composition, the result shows, in the fluid composition of D1a~D19 of embodiment, the surface tension of any composition is 25~35dyn/cm.
The composition of aforesaid liquid composition D1a~D19 is shown in Table 7.
In addition, use the modification PAA of above-mentioned acquisition, preparation contains the fluid composition E1 of following each composition of composition.
Fluid composition E1
Modification PAA-2 5.0% (solid constituent conversion)
Glycerine 25.0%
Triethylene glycol monobutyl ether 3.0%
OLFINE E1010 0.3%
Water surplus
Fluid composition E2a~E12
In fluid composition E1, except replace modification PAA-2 with modification PAA-3a~13, similarly obtain the fluid composition of fluid composition E2a~12 with fluid composition E1.
Use the CBVP-Z of consonance interface science corporate system to measure the surface tension of aforesaid liquid composition, the result shows, in the fluid composition of E1~E12 of embodiment, the surface tension of any composition is 25~35dyn/cm.
The composition of aforesaid liquid composition E1~E12 is shown in Table 8.
The preparation of ink composite
Prepare the various ink composites shown in the following table 9 according to following operation.At first, pigment is mixed with resin (styrene-propene acid copolymer), be placed in the sand mill (peace river make made), carry out 2 hours dispersion treatment together with bead (diameter 1.7mm is 1.5 times of amounts (weight) of mixture).Remove bead then, add other additive, stirred at normal temperatures 20 minutes.Using a kind of aperture is the membrane filter filtration of 10 μ m, has obtained pigment ink.
Table 9
Ink composite | Yellow | Magenta | Cyan | Black |
C.I. pigment yellow 74 | 3.0 | - | 0 | - |
C.I. paratonere 202 | - | 3.0 | - | - |
C.I. pigment blue 15: 3 | - | - | 3.0 | - |
Carbon black | - | - | - | 3.0 |
The styrene-propene acid copolymer | 1.0 | 1.0 | 1.0 | 1.0 |
OLFINE E1010 | 0.5 | 0.5 | 0.5 | 0.5 |
Glycerine | 15.0 | 15.0 | 15.0 | 15.0 |
TEGmBE | 5.0 | 5.0 | 5.0 | 5.0 |
Triethanolamine | 0.9 | 0.9 | 0.9 | 0.9 |
Water | Surplus | Surplus | Surplus | Surplus |
Add up to | 100.0 | 100.0 | 100.0 | 100.0 |
In the table,
TEGmBE: triethylene glycol monobutyl ether
OLFINE E1010: acetylenediol class surfactant (day letter chemical industry system)
4. evaluation test
(1) glossiness test
Each fluid composition D1a~D19 and E1~E12 and ink composite are filled into ink-jet printer (Seiko Epson Corp's system; MC-2000) in, in ink-jet dedicated paper (Seiko Epson Corp's system; The PM photography paper) on, prints according to the condition of 720 * 720dpi and load 40%.
Should illustrate that " load " is the value of calculating by following formula.
Load (%)=actual print counts/and (in the formula, " actual print is counted " is that the actual print of per unit area is counted in (vertical resolution ratio * horizontal resolution ratio) * 100; " vertical resolution ratio " and " horizontal resolution ratio " is the resolution ratio of per unit area evenly.100% load is meant the maximum ink by weight with respect to the monochrome of pixel).
For obtained each the record thing glossiness, according to carry out the evaluation of glossiness about the same method of the glossiness evaluation of measuring 1-1 in the inventive embodiment of first technical scheme.
Evaluation result is shown in Table 10.In an embodiment, by the printed liquid composition, make the glossiness of non-lettering part increase.
(2)
The colour rendering test
Various fluid composition D1a~D19 and E1~E12 and ink composite are filled into ink-jet printer (Seiko Epson Corp's system; MC-2000) in, on common paper (Xerox4024), by the condition printing of 720 * 720dpi.Similarly estimate with above-mentioned 2. (1) colour rendering test.The results are shown in the following table 10.
(3)
The liquid waste processing performance test that does not have the lid of nonwoven
Various fluid composition D1a~D19 and E1~E12 are filled into ink-jet printer (Seiko Epson Corp's system with ink composite respectively; MC-2000) in, similarly estimate with above-mentioned 1 evaluation 3.
Evaluation result is shown in Table 10.In an embodiment, as can be seen, the liquid waste processing function admirable can be implemented good cleaning.
(4)
Liquid waste processing performance evaluation with lid of nonwoven
Carry out the evaluation same with above-mentioned 1 evaluation 4.Evaluation result is shown in Table 10.In an embodiment, as can be seen, the liquid waste processing function admirable can realize good cleaning.
(5)
The lettering estimation of stability
Various fluid composition D1a~D19 and E1~E12 and ink composite are filled into ink-jet printer (Seiko Epson Corp's system; MC-2000) in, then under 40 ℃ environment, on the PM of A4 photography paper, carry out 200 pages lettering continuously according to the condition of 720 * 720dpi and 100% load.Then, do not clean the printing that just begins to carry out the nozzle check pattern.And then, according to following metewand, be the occasion of A in quality, continue 400 pages of letterings (adding up to 600 pages) continuously, under the condition that does not clean, carry out nozzle then and detect.The printing of pattern.According to following benchmark it is estimated then.
AA: after 200 pages of continuous letterings and the check pattern after 600 pages of continuous letterings, the two all can normally print.
A: the check pattern after 200 pages of continuous letterings can normally be printed, but the check pattern after 600 pages of continuous letterings can not normally be printed.
B: the check pattern after 200 pages of continuous letterings can not normally be printed.
Evaluation result is shown in Table 10.
Claims (25)
1. fluid composition, it is used for being attached to recording medium with ink composite, this fluid composition contains two kinds of modification polyallylamines, water-miscible organic solvent and water, and do not contain colouring agent, wherein said modification polyallylamine is for containing the macromolecule of repetitive shown at least a following formula (I):
Wherein, R
1And R
2Represent hydrogen atom independently of one another, be not substituted or substituted alkyl, be not substituted or substituted aryl, be not substituted or substituted pyridine radicals, be not substituted or substituted alkyl amino, be not substituted or substituted diazanyl, be not substituted or substituted alkoxyl or be not substituted or substituted hydroxyalkyl, wherein, a kind of modification polyallylamine has less than 5,000 weight average molecular weight, another kind of modification polyallylamine has and is not less than 5,000 weight average molecular weight.
2. fluid composition as claimed in claim 1, wherein, a kind of modification polyallylamine has and is not more than 2,000 weight average molecular weight.
3. fluid composition as claimed in claim 1, said composition contain above-mentioned weight average molecular weight in the ratio of 1:0.25~1:4 and are not less than 5,000 modification polyallylamine less than 5,000 modification polyallylamine and above-mentioned weight average molecular weight.
4. fluid composition as claimed in claim 1, the degree of modification of wherein said modification polyallylamine is more than 50mol%.
5. fluid composition, it is used for being attached to recording medium with ink composite, and this fluid composition contains modification polyallylamine, polymine or derivatives thereof, water-miscible organic solvent and water, and does not contain colouring agent.
6. fluid composition as claimed in claim 5, wherein said polymine or derivatives thereof is for containing the macromolecule of repetitive shown at least a following formula (II):
-(NR
1CH
2CH
2)n- (II)
In the following formula, R
1The expression hydrogen atom, be not substituted or substituted alkyl, be not substituted or substituted aryl, be not substituted or substituted pyridine radicals, be not substituted or substituted alkyl amino, be not substituted or substituted diazanyl, be not substituted or substituted alkoxyl or be not substituted or substituted hydroxyalkyl.
7. as claim 5 or 6 described fluid compositions, wherein, the weight average molecular weight of above-mentioned polymine or derivatives thereof is 100~5,000.
8. fluid composition, it is used for being attached to recording medium with ink composite, this fluid composition contains modification polyallylamine, water-miscible organic solvent and water, and do not contain colouring agent, wherein said modification polyallylamine contains by the repetitive (a) of following chemical formulation and (c) or (a) and (b) and (c):
In the following formula,
R
1And R
2The alkyl of representing carbon number 1~4 independently of one another;
X be following (i)~(any group v):
(i)-CONH
2、
(ii)-COOR
3, in the formula, R
3The alkyl or aryl of expression carbon number 1~12,
(iii)-COR
4, in the formula, R
4The alkyl of expression carbon number 1~12,
(iv)-CH
2CH (R
5)-A, in the formula, R
5Expression hydrogen atom or methyl; A is selected from-CONR
6R
7,-CN and COOR
8, R wherein
6And R
7The alkyl of representing hydrogen atom or carbon number 1~8 independently of one another, this alkyl is not substituted or is selected from alkyl monosubstituted amino, two (alkyl of carbon number 1~4) amino of hydroxyl, ketone group, carbon number 1~4 and any group in three (alkyl of carbon number 1~4) ammonium replaces, perhaps, NR
6R
7The cyclic amino of representing piperidino or morpholinyl together jointly, R
8The alkyl of expression carbon number 1~8, this alkyl are not substituted or are selected from alkyl monosubstituted amino, two (alkyl of carbon number 1~4) amino of hydroxyl, ketone group, carbon number 1~4 and any group in three (alkyl of carbon number 1~4) ammonium replaces; Perhaps
(v)-CH
2CH (OH)-B, in the formula, B represents the alkyl of carbon number 1~8, this alkyl is not substituted or is selected from the alkoxyl of hydroxyl, carbon number 1~4 and any group in the alkene oxygen base replaces;
Y represents the definition same with above-mentioned X, perhaps represents hydrogen atom; And
X and Y repetitive separately is identical or different.
9. fluid composition as claimed in claim 8, wherein, above-mentioned modification polyallylamine contains 5~95% above-mentioned repetitive (a), and, with respect to above-mentioned repetitive (b) and sum (c), contain 60~100% repetitive (c).
10. fluid composition as claimed in claim 8 or 9, wherein, the weight average molecular weight of above-mentioned modification polyallylamine is below 5,000.
11., wherein also contain polymer particles as each described fluid composition in the claim 1,5 or 8.
12. fluid composition as claimed in claim 11, wherein, the glass transition temperature of above-mentioned polymer particles is below 50 ℃.
13. fluid composition as claimed in claim 11, wherein, above-mentioned polymer particles is anionic polymer particulate and/or non-ionic polyalcohol particulate.
14. fluid composition as claimed in claim 13 wherein contains by making above-mentioned polymer particles be scattered in the emulsion that obtains in the aqueous medium.
15. fluid composition as claimed in claim 14; wherein; when described polymer particles is an anionic polymer particulate or during for anionic polymer particulate and non-ionic polyalcohol particulate, be the emulsion of from oil-in-water type emulsion, colloidal sol type emulsion, anionic polyethylene emulsion or its modifier, anionic polypropylene emulsion or its modifier and their mixture, selecting by the emulsion that the anionic polymer microparticulate is obtained in aqueous medium.
16. fluid composition as claimed in claim 15, wherein, above-mentioned colloidal sol type emulsion is alkali-soluble emulsion and/or contains sulfonic emulsion.
17. fluid composition as claimed in claim 16, wherein, above-mentioned alkali-soluble emulsion is to make the ethylenic unsaturated carboxylic acid monomer and can carry out polymerization in the presence of water-soluble high-molecular compound that contains alcoholic extract hydroxyl group or copolymerization surfacant with the monomer that this ethylenic unsaturated carboxylic acid monomer carries out copolymerization, with the polymer dispersed that obtains in aqueous medium and the emulsion that forms.
18. fluid composition as claimed in claim 16, wherein, above-mentioned to contain sulfonic emulsion be to contain the sulfonic emulsion of dienes and/or contain the sulfonic emulsion of non-dienes.
19. fluid composition as claimed in claim 14; wherein; when described polymer particles is a non-ionic polyalcohol particulate or during for anionic polymer particulate and non-ionic polyalcohol particulate, be the emulsion of from nonionic polyethylene emulsion or its modifier, nonionic polypropylene emulsion or its modifier and their mixture, selecting by the emulsion that the non-ionic polyalcohol microparticulate is obtained in aqueous medium.
20. as each described fluid composition in the claim 1,5 or 8, wherein, above-mentioned organic solvent is a kind of compound or the two or more combination of compounds of selecting from glycol ether compounds, alkyl diol compounds and multicomponent alcoholics compound.
21. as each described fluid composition in the claim 1,5 or 8, it is used for ink jet recording method.
22. be used to carry out the print cartridge of ink mist recording, wherein contain each described fluid composition in the claim 1,5 or 8.
23. ink set, comprising:
Each described fluid composition in the claim 1,5 or 8; With
At least the ink composite that contains colouring agent, water-miscible organic solvent and water.
24. ink jet recording method, this method are to write down by the ink composite described in each described fluid composition and the claim 23 in the claim 1,5 or 8 is attached on the recording medium.
25. ink jet recording method, this method comprises:
By being attached to, each described fluid composition and ink composite in the claim 11~19 carry out record on the recording medium;
Then, the temperature more than the glass transition temperature of above-mentioned polymer particles is carried out heat treated to recording surface.