CN100503871C - 一种铁合金 - Google Patents

一种铁合金 Download PDF

Info

Publication number
CN100503871C
CN100503871C CNB2007101467590A CN200710146759A CN100503871C CN 100503871 C CN100503871 C CN 100503871C CN B2007101467590 A CNB2007101467590 A CN B2007101467590A CN 200710146759 A CN200710146759 A CN 200710146759A CN 100503871 C CN100503871 C CN 100503871C
Authority
CN
China
Prior art keywords
iron
sulphur
manganese
chromium
silicon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2007101467590A
Other languages
English (en)
Other versions
CN101100729A (zh
Inventor
金雹峰
金融
金媛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2007101467590A priority Critical patent/CN100503871C/zh
Publication of CN101100729A publication Critical patent/CN101100729A/zh
Priority to PCT/CN2008/072001 priority patent/WO2009024069A1/zh
Priority to EP08783992.4A priority patent/EP2189550B1/en
Application granted granted Critical
Publication of CN100503871C publication Critical patent/CN100503871C/zh
Priority to HK10109288.0A priority patent/HK1143408A1/xx
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种铁合金，它的化学成分按重量百分比，其组成成分为：碳0.01-0.22，硅0.08-1.00，锰4.5-12.00，磷0.02-0.2，硫0.025-0.06，镍9.50-22.00，铬15.00-24.00，钼0.05-6.00，其余为铁。本发明的铁合金，具有防爆和无火花特性，特别适用于制作危化品容器，应急救援设备和相关工具，广泛适宜防爆无火花领域应用。

Description

一种铁合金
技术领域
本发明涉及一种铁合金，具体地说是涉及一种具有碰撞磨擦无火花和防爆性能的铁合金材料。
背景技术
现有无火花金属材料主要是铜合金材料，无火花铜合金材料制作的设备和工具，由于硬度的缺陷，使设备和工具的使用寿命大减，工作成本居高不下，长期以来困扰着行业的发展。
中国专利申请号85103868公开了一种铁合金，它的重量百分比成份为：碳2.00-3.25，锰0.40-1.2，硅0.40-0.90，铬0.70-1.50，硼0.60-1.2，磷≤0.05，硫≤0.05，铁平衡到100％，其中磷和硫的含量越少越好。
中国专利申请号86102537公开了一种硬质耐磨铁合金，它的重量百分比成份为：碳2.50-3.00，锰0.50-1.30，硅0.30—1.3，铬25.0-30.0，镍3.90-4.75，钼2.0-2.5，磷小于0.05，硫小于0.05，钒0.4—1.0，硼3.0-4.0，铁总量为100％的余量。
以上两项专利申请文献中所涉及的铁合金均具有高硬度而耐磨的性能，但在金属碰撞磨擦中易产生火花，不适宜于防爆无火花领域应用。
发明内容
本发明的目的旨在提供一种具有碰撞磨擦无火花和防爆性能的铁合金，满足金属容器内危化品泄漏后应急救援设备制作的要求和危化品金属容器制作的要求，适宜于防爆无火花领域的应用。
为实现上述目的，本发明的铁合金按重量百分比，其组成成份为：
硫0.025—0.06；镍9.5—22；   铬15.0—24.0；
碳0.01—0.26； 硅0.08—1.00；锰4.50—12.00；
磷0.02—0.2；其余为铁(铁总量为100％的余量)。
本发明的铁合金按重量百分比，其组成成份可扩展为：
碳0.01—0.26；硅0.08—1.00：锰4.50—12.00；
镍9.50—22.00； 铬15.0—24.0；钼0.05—6.00；
硫S0.025—0.06；磷0.02—0.2； 其余为铁。
本发明的铁合金按重量百分比，其组成成份还可扩展为：
碳0.01—0.26； 硅0.08—1.00；  锰4.50—12.00；
镍9.50—22.00；铬15.00—24.00；钼0.05—6.00；
硫0.025—0.06；磷0.02—0.20；  铜0.01—4.00；
氮0.01—0.22；其余为铁。
本发明的铁合金与现有技术相比具有金属碰撞磨擦无火花和防爆的特性，用于危化品金属容器的制作，能避免危化品金属容器在运输和搬动过程中不慎碰撞磨擦而爆裂导致危化品泄漏的恶性事故发生，用于金属容器内危化品泄漏后应急救援设备的制作，能在危化品泄漏后应急救援设备和金属容器接触性碰撞磨擦不产生火花，既避免了恶性事故扩大的危害，又保证了应急救援的安全性和有效性；本发明的铁合金还适用于防爆无火花领域。
具体实施方式
实施例1：将含有理想成份的碳、锰、硅、硫、磷的钢料与一定量的镍、铬混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比的化学成份：碳0.15，锰5.0，硅0.085，磷0.03，硫0.025，镍17.00，铬16.00，其余为铁。将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例2：将含有理想成份的碳、锰、硅、硫、磷的钢料与一定量的镍、铬混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比的化学成份：碳0.18，锰8.00，硅0.09，磷0.05，硫0.02，镍19.00，铬18.00，其余为铁。将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例3：将含有理想成份的碳、锰、硅、硫、磷的钢料与一定量的镍、铬、钼混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比的化学成份：碳0.08，锰10.00，硅0.09，磷0.08，硫0.035，镍21.00，铬18.00，钼0.10，其余为铁，将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例4：将含有理想成份的碳、锰、硅、硫、磷的钢料与一定量的镍、铬、钼混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比的化学成份：碳0.04，锰11.00，硅1.00，磷0.10，硫0.035，镍12.00，铬22.00，钼0.06，其余为铁，将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例5：将含有理想成份的碳、锰、硅、硫、磷的钢料与一定量的镍、铬、钼混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比的化学成份：碳0.02，锰9.00，硅0.095，磷0.15，硫0.045，镍9.50，铬19.00，钼0.09，其余为铁。将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例6：将含有理想成份的碳、锰、硅、硫、磷、铜、氮的钢料与一定量的镍、铬、钼混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比的化学成份：碳0.017，锰7.50，硅0.085，磷0.02，硫0.025，镍15.00，铬17.00，钼2.00，铜0.09，氮0.09，其余为铁。将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例7：将含有理想成份的碳、锰、硅、硫、磷、铜、氮的钢料与一定量的镍、铬、钼混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比的化学成份：碳0.012，锰12.00，硅0.08，磷0.02，硫0.025，镍20.00，铬22.00，钼0.05，铜0.12，氮0.12，其余为铁。将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例8：将含有理想成份的碳、锰、硅、硫、磷的钢料与一定量的镍、铬、钼混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比为：碳0.020，硅0.09，锰10.00，磷0.08，硫0.035，镍21.00，铬20.00，钼0.10，剩余为铁。将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。
实施例9：将含有理想成份的碳、锰、硅、硫、磷的钢料与一定量的镍、铬、钼混合，然后加热使其溶化，经取样分析，使其达到如下按重量百分比为：碳0.08，硅0.095，锰9.00，磷0.15，硫0.045，镍9.50，铬19.00，钼0.09，剩余为铁。将该铁合金浇铸成不同型材，用其分别加工制作危化品金属容器和应急救援设备及其它工具。

Claims (10)

1.一种铁合金，其特征在于化学成份的组成按重量百分比为：
碳0.01—0.26，硅0.08-1.00，锰4.50—12.00，磷0.02-0.20，硫0.025-0.06，镍9.50-22.00，铬15.00-24.00，其余为铁。
2.根据权利要求1所述的铁合金，其特征在于优选的化学成份按重量百分比为碳0.15，硅0.085，锰5.00，磷0.03，硫0.025，镍17.00，铬16.00，剩余为铁。
3.根据权利要求1所述的铁合金，其特征在于优选的化学成份按重量百分比为：碳0.18，硅0.09，锰8.00，磷0.05，硫0.02，镍19.00，铬18.00，剩余为铁。
4.一种铁合金，其特征在于化学成份按重量百分比：碳0.01-0.26，硅0.08-1.00，锰4.50-12.00，磷0.02-0.20，硫0.025-0.06，镍9.5-22.00，铬15.00-24.00，钼0.05-6.00，剩余为铁。
5.根据权利要求4所述的铁合金，其特征在于优选的化学成份按重量百分比为：碳0.020，硅0.09，锰10.00，磷0.08，硫0.035，镍21.00，铬20.00，钼0.10，剩余为铁。
6.根据权利要求4所述的铁合金，其特征在于优选的化学成份按重量百分比为：碳0.04，硅1.00，锰11.00，磷0.10，硫0.035，镍12.00，铬22.00，钼0.06，剩余为铁。
7.根据权利要求4所述的铁合金，其特征在于优选的化学成份按重量百分比为：碳0.08，硅0.095，锰9.00，磷0.15，硫0.045，镍9.50，铬19.00，钼0.09，剩余为铁。
8.一种铁合金，其特征在于化学成份按重量百分比为：碳0.01—0.26，硅0.08-1.00，锰4.5-12.00，磷0.02-0.20，硫0.025-0.06，镍9.50-22.00，铬15.00-24.00，钼0.05-6.00，铜0.01—4.00，氮0.01-0.22，剩余为铁。
9.根据权利要求8所述的铁合金，其特征在于化学成份按重量百分比为：碳0.017，硅0.085，锰7.50，磷0.02，硫0.025，镍15.00，铬17.00，钼2.00，铜0.09，氮0.09，剩余为铁。
10.根据权利要求8所述的铁合金，其特征在于化学成份按重量百分比为：碳0.012，硅0.08，锰12.00，磷0.02，硫0.025，镍20.00，铬22.00，钼0.05，铜0.12，氮0.12，剩余为铁。
CNB2007101467590A 2007-08-15 2007-08-15 一种铁合金 Active CN100503871C (zh)