CN100494288C - Preparation process of sulfur black dye and product thereof - Google Patents
Preparation process of sulfur black dye and product thereof Download PDFInfo
- Publication number
- CN100494288C CN100494288C CNB2004100993608A CN200410099360A CN100494288C CN 100494288 C CN100494288 C CN 100494288C CN B2004100993608 A CNB2004100993608 A CN B2004100993608A CN 200410099360 A CN200410099360 A CN 200410099360A CN 100494288 C CN100494288 C CN 100494288C
- Authority
- CN
- China
- Prior art keywords
- black
- sulfide dye
- temperature
- black sulfide
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a preparation process of sulfur dye and a product thereof, in particular to a preparation process of sulfur black dye by spray drying and a sulfur black product prepared by the preparation process; the sulfur black product prepared by the inventionComprising: 1. the diameter of the sulfur black dye particle is 150-200 mu m, the particle is fine, and the specific surface area is 300-360cm2(ii)/g, greater; the product has good wettability, fluidity and solubility, excellent application performance, difficult color spots, figured cloth and color difference after dyeing, and various fastness is higher than that of the common product. 2. The sulfur black dye has uniform particles and uniform intensity, and is not easy to cause canthus during dyeing. 3. The pollution degree to the environment is greatly reduced.
Description
Technical field
The present invention relates to preparation technology of a kind of thioxine dyes and products thereof, relate in particular to a kind of preparation technology of spraying drying black sulfide dye and made sulphur black product thereof of adopting.
Background technology
Black sulfide dye is some organic aromatic compound and sulphur or the interactional dyestuff of sodium polysulphide, because its raw material and production process are all fairly simple, with low cost, and washing and light fastness are better, therefore, being in great demand of thioxine dyes, wherein especially with black, blue two kinds of dyestuffs in consumption maximum aspect the cotton products dyeing, be the bigger kind of output in the dyestuffs industries, sulphur black is with 2,2, 4-dinitrophenol and sodium polysulphide boil in the aqueous solution and form, and its production process is:
(1) sodium sulphite and sulfur reaction generate sodium polysulphide.
(2) 2,4-dinitrochlorobenzenes generate 2 through sodium hydroxide hydrolysis, the 4-sodium dinitrophenol.
(3) 2,4-sodium dinitrophenols reduce through sodium polysulphide, generate black sulfide dye through reactions such as condensation, sulfurations again.
(4) size mixing postcure black wash material drying and get finished product.
The black sulfide dye drying of prior art is to use the roller dryer drying, its principle of work is to utilize a kind of internal heating conduction type to rotate continuous drying equipment, the cylinder of rotation is by the bottom hopper, adhering to certain thickness material film, heat by pipe-line transportation to inner wall of rotary drum, be transmitted to cylinder outer wall, conduct the feed film again, make that the moisture in the material film is evaporated, dehumidification makes the material that contains moisture obtain drying, dry good material by device at the scraper shovel of cylinder surface from cylinder to the spiral conveyer that places below the scraper, by handling machinery dry material is concentrated, packing can obtain product.
Prior art adopts the roller dryer drying mainly to have following shortcoming:
A. adopt roller dryer exsiccant material dye granule bigger, general diameter is about 1mm, and the particle inequality, dye granule is thicker, and specific surface area is less, causes colorant dissolubility relatively poor, easy causing material inequality during dyeing forms color spot easily, influences dyefastness and application performance.
B. because material by sticking wall drying, certainly will cause dried dyestuff water ratio inequality, cause the dye strength inequality, cause dye aberration easily.
C. use roller drying, some material can be taken away from cylinder top along with moisture evaporated, has reduced the yield of dyestuff, and certainly will be caused pollution to environment by the material that moisture is taken away.
Summary of the invention
The present invention is directed to prior art adopts roller dryer and makes dried dyestuff water content inequality, cause dye aberration easily, and some material can be taken away from the cylinder top along with moisture evaporated, reduced the yield of dyestuff, and the shortcoming that the material of taking away pollutes the environment, provide a kind of material that can make to have good homogeneity, reduce tail gas with material environment is produced the spray-dired method of polluting.
Another object of the present invention provides a kind of have excellent every fastness and dyeing behavior, has bigger specific surface area again, and solubility property is good, and application performance is superior, the particulate black sulfide dye that cost is low.
Above-mentioned technical problem of the present invention is mainly solved by following technical proposals; A kind of preparation method of black sulfide dye, it is characterized in that, comprise the black sulfide dye intermediate and alkali reaction (2) resultant of reaction of (1) initiation (I) formula and vulcanize the black sulfide dye that reaction generates between compound or the mixture, (3) size mixing, (4) size mixing postcure black wash material through press spray dry and finished product, the dry used pressure of described press spray is 2Mpa-8Mpa; Wherein the X in (I) formula is halogens or hydroxyl, and R is a kind of in nitro, nitroso-group and the amino, R
1A kind of in nitro, nitroso-group and the amino
Drying of the present invention is the press spray drying, sulphur black slurry after sizing mixing, under the pressure of high-pressure pump, enter at a high speed from the tangential passage of spraying gun and to produce high-speed motion in the rotating room, being sprayed into droplet is dispersed in the hot gas flow, air enters the airheater heating through gas blower, enters spray-dryer then, drips contact drying with spray.Product section falls at the bottom of the tower, and part sucks primary cyclone by the one-level induced draft fan, and tail gas purifies with sack cleaner and water film dedusting and reclaims.
As preferably, described press spray exsiccant mode is to carry out from the top down, and the aperture of described nozzle is 0.8-3.0mm, and described shower nozzle number is 1-10.
As preferably, described black sulfide dye intermediate is 2, the 4-dinitrochlorobenzene, and described sulfuration compound or mixture are sulphide salt and sulphur, described alkaline solution is a sodium hydroxide solution.
As preferably, the aperture of described nozzle is 1.5-2.4mm, and described shower nozzle number is 4-8, and the dry used pressure of described press spray is 4Mpa-6Mpa.
As preferably, described size mixing postcure black wash material drying and the finished product whole process be in full temperature control state, the temperature of wherein controlling inlet air is 120 ℃-200 ℃, the temperature of outlet air is 30 ℃-100 ℃, the temperature of slurry is 50 ℃-110 ℃, the solid solid content 25-50% of slurry before the control spraying.
Those of ordinary skill is thought because the viscosity ratio of dyestuff is bigger; adopt press spray exsiccant mode can make slurry stop up shower nozzle, not only influence the drying effect of slurry, and usually can cause the damage of shower nozzle; this is a technology barrier, so they can not walk this mistaken ideas all the time.
The inventor once also entered into such mistaken ideas, but by the discovery that studies for a long period of time: because traditional technology has adopted the method for drum drying, this method will certainly cause the particle of material bigger, the particle inequality, Color is poor, the inventor adopts rational mixing method, full temperature control state carries out spraying drying, greatly reduce the viscosity of slurry, and the chance that adopts suitable pressure and nozzle bore to make the slurry of technology of the present invention stop up shower nozzle has significantly reduced, the black sulfide dye particle that spraying drying produces is less, be evenly distributed, Color improves greatly.
As preferably, described size mixing postcure black wash material drying and the process of finished product adopts full temperature control state, the temperature of wherein controlling inlet air is 150 ℃-180 ℃, the temperature of outlet air is 60 ℃-90 ℃, the temperature of slurry is 75 ℃-100 ℃, and the solid solid content of slurry is 35%-45% before the control spraying.
A kind of black sulfide dye, warp (1) causes the black sulfide dye intermediate and alkali reaction (2) resultant of reaction of (I) formula and vulcanizes between compound or the mixture and react, (2) size mixing, (3) size mixing and make after press spray is dry, it is characterized in that, described black sulfide dye particulate diameter is 150-200 μ m, and specific surface area is 300-360cm
2/ g; Wherein the X in (I) formula is halogens or hydroxyl, and R is a kind of in nitro, nitroso-group and the amino, and R1 is a kind of in nitro, nitroso-group and the amino;
R1
The sulphur black slurry is after the press spray drying, and general diameter is 150-200um, and the specific surface area of product is 300-360cm
2/ g.Product has good flowability, wettability, performances such as solubleness height.By after the spraying drying, dyestuff has good homogeneity simultaneously.Thereby make black sulfide dye reach the top standard of like product at dyeing and printing and dyeing application performance.
As preferably, described black sulfide dye intermediate is 2,4-dinitrochlorobenzene or 2, and 2, 4-dinitrophenol or 2,4-dinitrobenzene phenates, described sulfuration compound or mixture are sulphide salt and sulphur, described alkaline solution is a sodium hydroxide solution.
As preferably, described black sulfide dye particulate diameter is 160-180 μ m, and specific surface area is 320-340cm
2/ g.
Therefore, the present invention produces black sulfide dye that black sulfide dye and prior art produce and compares and have the following advantages:
1. the black sulfide dye particle diameter is 150-200um, and be to compare about 1mm with the sulphur black particle diameter of prior art, particle is thinner, specific surface area is big, product has preferably wettability, flowability and solvability preferably, application performance is superior, is difficult for causing color spot, figured cloth and aberration after the dyeing, and every fastness is than general height.
2. black sulfide dye uniform particles, uniform intensity is difficult for causing the look corner of the eyes when dyeing.
3. the degree of environmental pollution reduces greatly.
Description of drawings
Fig. 1 is a kind of process flow sheet of prior art
Embodiment
Further set forth the beneficial effect of black sulfide dye of the present invention by the following examples with reference examples.
Embodiment 1
A. the preparation of sodium polysulphide: in the 500ml there-necked flask, add 150 parts in water, be warmed up to 80 ℃, add 150 parts in 60% Sodium Sulphide, stir, add 105 parts in sulphur until whole dissolvings, after adding, standby 98 ℃ of insulation reaction 2 hours.
B. hydrolysis: add 100 parts in water in the 500ml there-necked flask, 150 parts of 2,4-nitro Benzene Chloride drip 210 parts of 30% caustic soda solns at 70 ℃, and are 100 ℃ of insulation reaction 1 hour, standby.
C, sulfuration: in the 1000ml autoclave, add hydrolyzation material and the sodium polysulfide solution of having got ready, 100 ℃ of reactions 1 hour, sealed pot cover then, be warming up to 140 ℃, 120 ℃ of reactions 7 hours, reaction pressure was controlled at 0.1Mpa, after reaction is finished, exhaust, the caustic soda of the stink damp body and function 30% of discharging is recycled into sodium sulphite.
D, oxidation, filtration: the material that will vulcanizate is put into the 2000ml beaker, adds the water of 500ml, is warmed up to 50 ℃ and with gas blower air is fed under the liquid level, and bubbling air two hours filters well-oxygenated material with vacuum pump, washing.
E. size mixing: the filter cake after will washing is put into the 1000ml beaker, adds the water of 300ml, is warming up to 60 ℃, adds 30 parts in 60% Sodium Sulphide, stirs 45 minutes.
F, drying: the sulphur black slurry that will mix up, under the pressure of 2Mpa high-pressure pump, enter the rotating room at a high speed from the tangential passage of spraying gun, make slurry in the rotating room, produce high-speed motion, be sprayed into droplet and be dispersed in the hot gas flow, air enters the airheater heating through gas blower, the control inlet air temperature is 120 ℃, and the temperature of slurry is 50 ℃, and the solid content of slurry is controlled at 45%, enter spray-dryer then, with the droplet contact drying.Product section falls at the bottom of the tower.Air themperature is 30 ℃ during outlet, and part sucks primary cyclone by one-level air inducing, and tail gas purifies with sack cleaner and water film dedusting and reclaims.The black sulfide dye particle diameter majority of gained is 200um, and specific surface area is 300cm
2/ g, wettability can, solvability 180g/l, flowability can, particle is (wherein particle diameter is that 200um accounts for 90%) relatively evenly, the sulphur black that tail gas is taken away ten thousand/following (promptly dry sulphur black that 1 ton of sulphur black tail gas takes away below 0.01kg).
Embodiment 2
A. the preparation of sodium polysulphide: in the 500ml there-necked flask, add 150 parts in water, be warmed up to 85 ℃, add 150 parts in 60% Sodium Sulphide, stir, add 105 parts in sulphur until whole dissolvings, after adding, standby 99 ℃ of insulation reaction 2 hours.
B. hydrolysis: add 100 parts in water in the 500ml there-necked flask, 150 parts of 2,4-nitro Benzene Chloride drip 210 parts of 30% caustic soda solns at 80 ℃, and are 102 ℃ of insulation reaction 1 hour, standby.
C, sulfuration: in the 1000ml autoclave, add hydrolyzation material and the sodium polysulfide solution of having got ready, 100 ℃ of reactions 1 hour, sealed pot cover then, be warming up to 140 ℃, 130 ℃ of reactions 7 hours, reaction pressure was controlled at 0.12Mp, after reaction is finished, exhaust, the caustic soda of the stink damp body and function 30% of discharging is recycled into sodium sulphite.
D, oxidation, filtration: the material that will vulcanizate is put into the 2000ml beaker, adds the water of 500ml, is warmed up to 60 ℃ and with gas blower air is fed under the liquid level, and bubbling air two hours filters well-oxygenated material with vacuum pump, washing.
E. size mixing: the filter cake after will washing is put into the 1000ml beaker, adds the water of 300ml, is warming up to 70 ℃, adds 30 parts in 60% Sodium Sulphide, stirs 35 minutes.
F, drying: the sulphur black slurry that will mix up, under the pressure of 6Mpa high-pressure pump, enter the rotating room at a high speed from the tangential passage of spraying gun, make slurry in the rotating room, produce high-speed motion, be sprayed into droplet and be dispersed in the hot gas flow, air enters the airheater heating through gas blower, the control inlet air temperature is 150 ℃, and the temperature of slurry is 75 ℃, and the solid content of slurry is controlled at 43%, enter spray-dryer then, with the droplet contact drying.Product section falls at the bottom of the tower.Air themperature is 60 ℃ during outlet, and part sucks primary cyclone by one-level air inducing, and tail gas purifies with sack cleaner and water film dedusting and reclaims.The black sulfide dye particle diameter majority of gained is 180um, and specific surface area is 320cm
2/ g, wettability is better, and solvability 190g/l is better mobile, particle very even (wherein particle diameter is that 180um accounts for more than 95%), the sulphur black that tail gas is taken away ten thousand/following (promptly dry sulphur black that 1 ton of sulphur black tail gas takes away below 0.01kg).
Embodiment 3
A. the preparation of sodium polysulphide: in the 500ml there-necked flask, add 150 parts in water, be warmed up to 90 ℃, add 150 parts in 60% Sodium Sulphide, stir, add 105 parts in sulphur until whole dissolvings, after adding, standby 100 ℃ of insulation reaction 2 hours.
B. hydrolysis: add 100 parts in water in the 500ml there-necked flask, 150 parts of 2,4-nitro Benzene Chloride drip 210 parts of 30% caustic soda solns at 90 ℃, and are 105 ℃ of insulation reaction 1 hour, standby.
C, sulfuration: in the 1000ml autoclave, add hydrolyzation material and the sodium polysulfide solution of having got ready, 100 ℃ of reactions 1 hour, sealed pot cover then, be warming up to 140 ℃, 140 ℃ of reactions 7 hours, reaction pressure was controlled at 0.13Mp, after reaction is finished, exhaust, the caustic soda of the stink damp body and function 30% of discharging is recycled into sodium sulphite.
D, oxidation, filtration: the material that will vulcanizate is put into the 2000ml beaker, adds the water of 500ml, is warmed up to 80 ℃ and with gas blower air is fed under the liquid level, and bubbling air two hours filters well-oxygenated material with vacuum pump, washing.
E. size mixing: the filter cake after will washing is put into the 1000ml beaker, adds the water of 300ml, is warming up to 80 ℃, adds 30 parts in 60% Sodium Sulphide, stirs 45 minutes.
F, drying: the sulphur black slurry that will mix up, under the pressure of 5Mpa high-pressure pump, enter the rotating room at a high speed from the tangential passage of spraying gun, make slurry in the rotating room, produce high-speed motion, be sprayed into droplet and be dispersed in the hot gas flow, air enters the airheater heating through gas blower, the control inlet air temperature is 180 ℃, and the temperature of slurry is 90 ℃, and the solid content of slurry is controlled at 40%, enter spray-dryer then, with the droplet contact drying.Product section falls at the bottom of the tower.Air themperature is 90 ℃ during outlet, and part sucks primary cyclone by one-level air inducing, and tail gas purifies with sack cleaner and water film dedusting and reclaims.The black sulfide dye particle diameter majority of gained is 160um, and specific surface area is 340cm
2/ g, wettability is better, solvability 220g/l, mobile better, uniform particles (wherein particle diameter is that 160um accounts for more than 95%), the sulphur black that tail gas is taken away ten thousand/following (promptly dry sulphur black that 1 ton of sulphur black tail gas takes away below 0.01kg).
Embodiment 4
A. the preparation of sodium polysulphide: in the 500ml there-necked flask, add 150 parts in water, be warmed up to 90 ℃, add 150 parts in 60% Sodium Sulphide, stir, add 105 parts in sulphur until whole dissolvings, after adding, standby 100 ℃ of insulation reaction 2 hours.
B. hydrolysis: add 100 parts in water in the 500ml there-necked flask, 150 parts of 2,4-nitro Benzene Chloride drip 210 parts of 30% caustic soda solns at 100 ℃, and are 103 ℃ of insulation reaction 1 hour, standby.
C, sulfuration: in the 1000ml autoclave, add hydrolyzation material and the sodium polysulfide solution of having got ready, 100 ℃ of reactions 1 hour, sealed pot cover then, be warming up to 140 ℃, 130 ℃ of reactions 7 hours, reaction pressure was controlled at 0.14Mp, after reaction is finished, exhaust, the caustic soda of the stink damp body and function 30% of discharging is recycled into sodium sulphite.
D, oxidation, filtration: the material that will vulcanizate is put into the 2000ml beaker, adds the water of 600ml, is warmed up to 70 ℃ and with gas blower air is fed under the liquid level, and bubbling air two hours filters well-oxygenated material with vacuum pump, washing.
E. size mixing: the filter cake after will washing is put into the 1000ml beaker, adds the water of 400ml, is warming up to 90 ℃, adds 30 parts in 60% Sodium Sulphide, stirs 45 minutes.
F, drying: the sulphur black slurry that will mix up, under the pressure of 7Mpa high-pressure pump, enter the rotating room at a high speed from the tangential passage of spraying gun, make slurry in the rotating room, produce high-speed motion, be sprayed into droplet and be dispersed in the hot gas flow, air enters the airheater heating through gas blower, the control inlet air temperature is 180 ℃, and the temperature of slurry is 100 ℃, and the solid content of slurry is controlled at 35%, enter spray-dryer then, with the droplet contact drying.Product section falls at the bottom of the tower.Air themperature is 100 ℃ during outlet, and part sucks primary cyclone by one-level air inducing, and tail gas purifies with sack cleaner and water film dedusting and reclaims.The black sulfide dye particle diameter majority of gained is 150um, and specific surface area is 360cm
2/ g, wettability can, solvability 240g/l, flowability can, particle is (wherein particle diameter is that 150um accounts for more than 90%) evenly, the sulphur black that tail gas is taken away ten thousand/following (promptly dry sulphur black that 1 ton of sulphur black tail gas takes away below 0.1kg).
Embodiment 5
A. the preparation of sodium polysulphide: in the 500ml there-necked flask, add 150 parts in water, be warmed up to 90 ℃, add 150 parts in 60% Sodium Sulphide, stir, add 105 parts in sulphur until whole dissolvings, after adding, standby 100 ℃ of insulation reaction 2 hours.
B. hydrolysis: add 100 parts in water in the 500ml there-necked flask, 150 parts of 2,4-nitro Benzene Chloride drip 210 parts of 30% caustic soda solns at 100 ℃, and are 105 ℃ of insulation reaction 1 hour, standby.
C, sulfuration: in the 1000ml autoclave, add hydrolyzation material and the sodium polysulfide solution of having got ready, 100 ℃ of reactions 1 hour, sealed pot cover then, be warming up to 140 ℃, 140 ℃ of reactions 7 hours, reaction pressure was controlled at 0.14Mp, after reaction is finished, exhaust, the caustic soda of the stink damp body and function 30% of discharging is recycled into sodium sulphite.
D, oxidation, filtration: the material that will vulcanizate is put into the 2000ml beaker, adds the water of 600ml, is warmed up to 60 ℃ and with gas blower air is fed under the liquid level, and bubbling air two hours filters well-oxygenated material with vacuum pump, washing.
E. size mixing: the filter cake after will washing is put into the 1000ml beaker, adds the suitably water of (how many ml), is warming up to 80 ℃, adds 30 parts in 60% Sodium Sulphide, stirs 45 minutes.
F, drying: the sulphur black slurry that will mix up, under the pressure of 6Mpa high-pressure pump, enter the rotating room at a high speed from the tangential passage of spraying gun, make slurry in the rotating room, produce high-speed motion, be sprayed into droplet and be dispersed in the hot gas flow, air enters the airheater heating through gas blower, the control inlet air temperature is 150 ℃, and the temperature of slurry is 85 ℃, and the solid content of slurry is controlled at 40%, enter spray-dryer then, with the droplet contact drying.Product section falls at the bottom of the tower.Air themperature is 75 ℃ during outlet, and part sucks primary cyclone by one-level air inducing, and tail gas purifies with sack cleaner and water film dedusting and reclaims.The black sulfide dye particle diameter majority of gained is 170um, and specific surface area is 330cm
2/ g, wettability can, solvability 205g/l, flowability can, particle very even (wherein particle diameter is that 170um accounts for more than 95%), the sulphur black that tail gas is taken away ten thousand/following (promptly dry sulphur black that 1 ton of sulphur black tail gas takes away below 0.1kg).
The comparative example 1
A. the preparation of sodium polysulphide: in the 500ml there-necked flask, add 150 parts in water, be warmed up to 90 ℃, add 150 parts in 60% Sodium Sulphide, stir, add 105 parts in sulphur until whole dissolvings, after adding, standby 100 ℃ of insulation reaction 2 hours.
B. hydrolysis: add 100 parts in water in the 500ml there-necked flask, 150 parts of 2,4-nitro Benzene Chloride drip 210 parts of 30% caustic soda solns at 100 ℃, and are 105 ℃ of insulation reaction 1 hour, standby.
C, sulfuration: in the 1000ml autoclave, add hydrolyzation material and the sodium polysulfide solution of having got ready, 100 ℃ of reactions 1 hour, sealed pot cover then, be warming up to 140 ℃, 140 ℃ of reactions 7 hours, reaction pressure was controlled at 0.13Mpa, after reaction is finished, exhaust, the caustic soda of the stink damp body and function 30% of discharging is recycled into sodium sulphite.
D, oxidation, filtration: the material that will vulcanizate is put into the 2000ml beaker, adds the water of 500ml, is warmed up to 60 ℃ and with gas blower air is fed under the liquid level, and bubbling air two hours filters well-oxygenated material with vacuum pump, washing.
E. size mixing: the filter cake after will washing is put into the 1000ml beaker, adds the water of 450ml, is warming up to 80 ℃, adds 30 parts in 60% Sodium Sulphide, stirs 45 minutes.
F. dry: that the black sulfide dye that mixes up is added the roller dryer drying, the cylinder of rotation is by the bottom hopper, adhering to certain thickness material film, heat by pipe-line transportation to inner wall of rotary drum, be transmitted to cylinder outer wall, conduct the feed film again, make that the moisture in the material film is evaporated, dehumidification, make the material that contains moisture obtain drying, dry good material by device at the scraper shovel of cylinder surface from cylinder to the spiral conveyer that places below the scraper, by handling machinery that dry material is concentrated, packing can obtain product.
Table 1: the contrast of the material performance of two kinds of dry gained of drying installation
| Group | Particle diameter (um) | Specific surface area (cm 2/g) | Solvability (g/l) | The ratio of the sulphur black that tail gas is taken away and the sulphur black of oven dry |
| The roller drying group | 1000 soil 400 | 50 soil 25 | 75 soil 15 | Less than 0.1% |
| The spraying drying group | 175 soil 25 | 330 soil 30 | 210 soil 30 | Less than 0.01% |
Annotate: spraying drying group and roller drying group compare, P＜0.01
Table 2: other property comparison of material of two kinds of dry gained of drying installation
| Group | Wettability | Mobile | The uniform particles degree |
| The roller drying group | Generally | Generally | The particle diameter distribution inequality, wherein the 900um-1100um diameter accounts for 30%～40% |
| The spraying drying group | Fine | Fine | Particle diameter distribution is even, and wherein the 150um-200um diameter accounts for more than 90% |
From top embodiment and comparative example as can be seen:
1. the dry gained black sulfide dye of press spray particle diameter is 150-200um, and is to compare about 1mm with the sulphur black particle diameter of prior art, and particle is thinner, specific surface area 300-360cm
2/ g is bigger; Product has preferably wettability, flowability and solvability preferably, and application performance is superior, is difficult for causing color spot, figured cloth and aberration after the dyeing, and every fastness is than general height.
2. black sulfide dye uniform particles, uniform intensity is difficult for causing the look corner of the eyes when dyeing.
3. the degree of environmental pollution reduces greatly.
Claims (7)
1. the preparation method of a black sulfide dye, it is characterized in that, comprise the black sulfide dye intermediate and alkali reaction (2) resultant of reaction of (1) initiation (I) formula and vulcanize the black sulfide dye that reaction generates between compound or the mixture, (3) size mixing, (4) size mixing postcure black wash material through press spray dry and finished product, the dry used pressure of described press spray is 2Mpa-8Mpa; Wherein the X in (I) formula is halogens or hydroxyl, and R is a kind of in nitro, nitroso-group and the amino, R
1A kind of in nitro, nitroso-group and the amino
Described size mixing postcure black wash material drying and the finished product whole process be in a temperature control state, the temperature of wherein controlling inlet air is 120 ℃-200 ℃, the temperature of outlet air is 30 ℃-100 ℃, the temperature of slurry is 50 ℃-110 ℃, the solid solid content 25-50% of slurry before the control spraying.
2. the preparation method of black sulfide dye according to claim 1 is characterized in that, described press spray exsiccant mode is to carry out from the top down, and the aperture of described nozzle is 0.8-3.0mm, and described shower nozzle number is 1-10.
3. the preparation method of black sulfide dye according to claim 1, it is characterized in that, described black sulfide dye intermediate is 2,4-dinitrochlorobenzene or 2,2, 4-dinitrophenol or 2,4-dinitrobenzene phenates, described sulfuration compound or mixture are sulphide salt and sulphur, described alkaline solution is a sodium hydroxide solution.
4. according to the preparation method of right 1 described black sulfide dye, it is characterized in that the aperture of described nozzle is 1.5-2.4mm, described shower nozzle number is 4-8, and the dry used pressure of described press spray is 4Mpa-6Mpa.
5. the preparation method of black sulfide dye according to claim 1, it is characterized in that, described size mixing postcure black wash material drying and the process of finished product adopts full temperature control state, the temperature of wherein controlling inlet air is 150 ℃-180 ℃, the temperature of outlet air is 60 ℃-90 ℃, the temperature of slurry is 75 ℃-100 ℃, and the solid solid content of slurry is 35%-45% before the control spraying.
6. the black sulfide dye as any described method preparation in the claim 1～5 is characterized in that described black sulfide dye particulate diameter is 150-200 μ m, and specific surface area is 300-360cm
2/ g.
7. black sulfide dye according to claim 6 is characterized in that, described black sulfide dye particulate diameter is 160-180 μ m, and specific surface area is 320-340cm
2/ g.