CN100476162C - Method for forming solidified filler by filling phosphorous gypsum in downhole goaf - Google Patents
Method for forming solidified filler by filling phosphorous gypsum in downhole goaf Download PDFInfo
- Publication number
- CN100476162C CN100476162C CNB2006100314288A CN200610031428A CN100476162C CN 100476162 C CN100476162 C CN 100476162C CN B2006100314288 A CNB2006100314288 A CN B2006100314288A CN 200610031428 A CN200610031428 A CN 200610031428A CN 100476162 C CN100476162 C CN 100476162C
- Authority
- CN
- China
- Prior art keywords
- ardealite
- filling
- cement
- flyash
- agitator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The method of forming solidified filler through filling ardealite in downhole goaf includes mixing cement, flyash and ardealite in the ratio of 1 to 1to 6-8; adding sodium sulfate as additive in the amount of 1.3-2.5 wt% of the foregoing three materials, mixing with water to form slurry of 57-63 wt% concentration, filling the slurry to the downhole goaf, and solidifying to form the high strength filler. The present invention can raise ore recovering rate, reduce ore loss, lower mining cost, avoid surface deposition, and utilize ardealite effectively.
Description
Technical field
The invention belongs to mining wastes comprehensive utilization field, be specifically related to a kind of filling phosphorous gypsum and form the method for solidifying obturation in underground goaf.
Background technology
Ardealite is chemical plant apatite and an effect of sulfuric acid, the byproduct that wet method produces when producing phosphoric acid.1 ton of phosphoric acid of every production will produce 5 tons of ardealites.Ardealite discharge value maximum in chemical gypsum, about 2,000 ten thousand tons of China's ardealite annual production occupies the third place in the world.Annual in the world at present discharge value reaches 1.1～1.3 hundred million tons, and only utilizes 460～4,700,000 tons, and utilization rate is very low.CaSO in the ardealite
42H
2O content still wherein also contains P usually generally up to more than 90%
2O
5: 0.3%～1.5%, F:0.1%～1.5% grade is detrimental to health and the objectionable impurities of biological growth, has constituted a kind of pollution sources.In addition, the discharging of ardealite not only takies a large amount of arable lands, contaminated environment, and caused very big burden to phosphatic fertilizer company.
Summary of the invention
The technical problem to be solved in the present invention is that ardealite is turned waste into wealth, and provides a kind of and improves ore recovery ratio and prevent that the filling phosphorous gypsum of using that ground settlement subsides from forming the method for solidifying obturation in underground goaf.
The present invention takes following technical scheme to solve the problems of the technologies described above: is cement with the material of following proportioning by mass ratio: flyash: ardealite=1: 1: (6～8) are mixed and are added additive sulfuric acid sodium by 1.3～2.5% of above-mentioned three kinds of material total amounts, water furnishing mass concentration is 57%～63% filling slurry again, filling slurry is imported underground goaf, through solidifying to form high-intensity obturation.Its processing step is: ardealite is transported to the ardealite pond,, to agitator, measures with impulse flowmeter through belt and conveying worm to disk feeder with motor grab; Flyash is transported to the fine coal ashpit, with motor grab to disk feeder, through belt and conveying worm to agitator; Additive sulfuric acid sodium adds agitator with water pump control; Cement in bulk is discharged in the bulk water hopper dredger through blowing pipe by bulk cement carrier, bulk water hopper dredger bottom is provided with spiral gate, cement in the cement bin is delivered to steady feed bin through conveying worm, through elasticity impeller dispenser and impulse flowmeter metering, cement enters agitator with ardealite, flyash, additive and water in described ratio and prepares filling slurry, and the filling slurry of preparation is delivered to the goaf through the filling borehole gravity flow.
Ardealite mixes with flyash and adds an amount of additive again among the present invention, can improve the ardealite consolidation strength, be applied to mining with stowing, can improve ore recovery ratio and reduce the mining depletion loss rate, reach the purpose that reduces mining cost, and can effectively prevent the ground settlement of digging up mine, and ardealite is turned waste into wealth, have higher economic value and social benefit.
Description of drawings
Fig. 1 is a process chart of the present invention.
The specific embodiment
Ardealite and flyash Main physical mechanical property such as table 1, grade is formed as table 2.
Table 1 ardealite and flyash mechanical property
| The casting resin title | Density (t/m 3) | Air space ratio | Transmission coefficient (cm/s) | Median particle diameter d50, mm | Effective grain size d10, mm | Nonuniformity coefficient | Coefficient of curvature | Angle of repose waterborne | Angle of repose under water |
| Ardealite | 2.87 | 1.064～3.415 | 2.94×10 -4 | 0.043 | 0.014 | 3.71 | 1.00 | 47.0° | 23.5° |
| The duff ash | 2.35 | 1.098～2.219 | 1.90×10 -4 | 0.040 | 0.025 | 1.68 | 1.17 | 41.5° | 25.5° |
| The rough coal ash | 2.32 | 1.017～1.936 | 6.48×10 -4 | 0.072 | 0.035 | 2.31 | 1.11 | 41.5° | 26° |
Table 2 ardealite and flyash material grade are formed (%)
| The casting resin title | ＞0.50 | 0.50～0.30 | 0.30～0.15 | 0.15～0.106 | 0.106～0.075 | 0.075～0.045 | 0.045～0.030 | ＜0.030 |
| Ardealite | 0.5 | 0.5 | 1.5 | 4.5 | 10.5 | 32.0 | 14.5 | 34.5 |
| The duff ash | 0.2 | 1.4 | 18.4 | 64.5 | 15 | |||
| The rough coal ash | 0.5 | 4.0 | 12.0 | 11.0 | 20.5 | 30.5 | 17.5 | 5.5 |
The ardealite grade is thinner, 0.1mm following particle accounts for 93%, median particle diameter 0.043mm, void ratio (1.064～3.415) and transmission coefficient (0.00294cm/s) are unsuitable for obturation dehydration and quick-hardening, must influence cemented fill intensity, flyash particle diameter thinner (duff ash median particle diameter only is 0.040mm, and rough coal ash median particle diameter only is 0.072mm), transmission coefficient is littler, and (duff ash transmission coefficient is 0.0019cm/s, rough coal ash transmission coefficient is 0.00648cm/s), but its SiO
2Content is up to 52.42%, Al
2O
3Reach 21.84%, have certain potential bonding capacity, can be used as the cement substitute and substitute part cement, improve the obturation later strength, simultaneously because flyash density is little, when mix a certain amount of after, to alleviate obturation proportion, help reducing cement consumption, save filling cost; CaO content only is 7.32% in the flyash, and activity function is not high, necessary outer doping; Fluorine content in the ardealite is not high, charges into the down-hole to the subsurface environment influence not quite; Ardealite is respectively 3.71 and 2.31,1.68 with thick, the grey nonuniformity coefficient of fine breeze, all belongs to uniform clay class, is easy to during slurrying mix, and is convenient to line transportation, charge into stope after, will help reducing the segregation of cement; CaSO in the ardealite
42H
2O content is generally up to more than 90%, and gypsum is unfavorable for the early strength of cemented fill as retarding agent usually, so CaSO
42H
2The hydration reaction of cementitious material such as O and portland cement and consolidation effect are improved by adding additive sulfuric acid sodium, have improved the ardealite solidification intensity greatly.
Through great deal of experimental, obtaining the optimum formula of filling phosphorous gypsum in the down-hole is cement: flyash: ardealite is 1: 1: (6～8), 90 days intensity of formed filling firming body can reach 1.38～2.05MPa.Add additive sulfuric acid sodium and can improve strength of filling mass 15%～20%, the optimised quantity of adding is 1.3%～2.5%.
Ardealite belongs to acidic materials, and particle is thinner, in order to prevent of the pollution of filling phosphorous gypsum goaf,, find with the effect of flyash relatively good by a large amount of experimental studies to subsurface environment, because flyash belongs to alkaline matter, can in and the acidity of ardealite, prevent down-hole acid water discharging, and flyash belongs to a kind of active medium, can adsorb material, prevent that the granule ardealite runs off than granule.In addition, flyash is a kind of porous medium, and proportion is lighter, helps reducing the resistance of ducting in the filling slurry conveying, realizes high power line gravity flow conveying filling slurry down.
Technological process of the present invention as shown in Figure 1.Ardealite is transported to the ardealite pond with automobile,, to agitator, with the impulse flowmeter metering, adjusts motor speed by robot control system(RCS) and realizes that control gives amount through No. 1 belt and conveying worm to disk feeder with 10 tons of motor grabs; Flyash is transported to the fine coal ashpit with automobile, with 10 tons of motor grabs to disk feeder, through No. 2 belts and conveying worm to agitator; Additive sulfuric acid sodium adds agitator with water pump control; After cement in bulk is transported to the preparation station by bulk cement carrier, be discharged in 150 tons of bulk water hopper dredgers through blowing pipe, the top of bulk water hopper dredger is provided with dust arrester installation, the bottom is provided with spiral gate and the arch breaking apparatus of calming the anger, during filling, start conveying worm, cement is delivered to steady feed bin, through elasticity impeller dispenser and impulse flowmeter metering, cement enters agitator with ardealite, flyash, additive and water and prepares filling slurry.The filling slurry of preparation is delivered to the filling stope through the filling borehole gravity flow.
Embodiment 1: certain phosphorus ore is produced phosphoric acid and is produced a large amount of ardealite waste materials, builds up a cover filling system with technological process shown in Figure 1.With 10 tons of cement, 10 tons in flyash, 70 tons of ardealites, 2.1 tons of fillings of sodium sulphate additive in the down-hole No. 5 stopes, the mass concentration of filling slurry is 60%.After filling slurry charges into stope, solidify the formation obturation, the scene is got 10 samples and is tested strength of filling mass, and 28 days average intensity of obturation is 1.08MPa, and this intensity can satisfy the mining technique requirement.
Embodiment 2: the mineral deposit of certain phosphorus ore is positioned under the highway, in order to realize safe working ore under the highway, builds up a cover filling system with technological process shown in Figure 1.With 15 tons of cement, 15 tons in flyash, 90 tons of ardealites, No. 1 stope of 2.5 tons of fillings of sodium sulphate additive, filling slurry mass concentration 58%.5 samples are got at the scene, and 28 days average intensity of test stope ardealite firming body reaches 1.28MPa.Analyze after deliberation, adopt the ardealite induration bashing of this intensity can not cause that underground mining destroys highway.
Embodiment 3: certain phosphate rock resource is of high grade, former employing avalanche method exploitation, and ore dilution rate reaches 38%, and the mining loss late reaches 42%.In order to reduce depletion loss rate, build up a cover filling system with technological process shown in Figure 1.With 5 tons of cement, 5 tons of flyash, 40 tons of ardealites and 0.8 ton of sodium sulphate additive filling test stope, filling slurry mass concentration 58%.The filling stope is got 5 samples, and 28 days average intensity of test ardealite firming body reaches 0.81MPa.Adopt the fixed filling process exploitated ore of ardealite, impoverishment rate in mining is reduced to 8%, and ore loss ratio is reduced to 5%.
Claims (1)
1, a kind of method that forms the curing obturation with filling phosphorous gypsum in underground goaf, it is characterized in that the material with following proportioning is a cement by mass ratio: flyash: ardealite=1: 1: 6～8 are mixed and are added additive sulfuric acid sodium by 1.3～2.5% of above-mentioned three kinds of material total amounts, water furnishing mass concentration is 57%～63% filling slurry again, filling slurry is imported underground goaf, through solidifying to form high-intensity obturation, its processing step is: ardealite is transported to the ardealite pond, with motor grab to disk feeder,, measure to agitator through belt and conveying worm with impulse flowmeter; Flyash is transported to the fine coal ashpit, with motor grab to disk feeder, through belt and conveying worm to agitator; Additive sulfuric acid sodium adds agitator with water pump control; Cement in bulk is discharged in the bulk water hopper dredger through blowing pipe by bulk cement carrier, bulk water hopper dredger bottom is provided with spiral gate, cement in the cement bin is delivered to steady feed bin through conveying worm, through elasticity impeller dispenser and impulse flowmeter metering, cement enters agitator with ardealite, flyash, additive and water in described ratio and prepares filling slurry, and the filling slurry of preparation is delivered to the goaf through the filling borehole gravity flow.