CN100467564C - 抗穿刺防水片材及其制备方法 - Google Patents
抗穿刺防水片材及其制备方法 Download PDFInfo
- Publication number
- CN100467564C CN100467564C CNB2006100155826A CN200610015582A CN100467564C CN 100467564 C CN100467564 C CN 100467564C CN B2006100155826 A CNB2006100155826 A CN B2006100155826A CN 200610015582 A CN200610015582 A CN 200610015582A CN 100467564 C CN100467564 C CN 100467564C
- Authority
- CN
- China
- Prior art keywords
- parts
- sheet
- low density
- piercing resistant
- resistant flashing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种抗穿刺防水片材及其制备方法，它是由75～85份线性低密度聚乙烯树脂为基料，辅以5～10份热塑性弹性体SBS、2～8份色母料和2～5份助剂及5～10份填充剂组成，采用挤出压延成型的方法制成增强抗穿刺防水片材。本发明的抗穿刺防水片材具有优良的防水、防渗漏、耐候性、高拉伸强度、低线体膨胀、摩擦系数大、变形适应性强、温度适应范围宽、使用方便、寿命长、易施工及造价低等诸多优良综合经济、技术性能指标。可用于地铁、道路、港口码头、涵洞、坝池和地下大型工程等防水工程中使用。
Description
技术领域
本发明属于防水材料制备领域，涉及一种增强抗穿刺防水片材(简称LECB)及其制备方法.
背景技术
用于制造防水片材的主要原材料有改性橡胶和单一的合成树脂，如聚氯乙烯、聚乙烯等聚烯烃树脂，用以上材料制备的防水卷材，其弹性小、伸长率低、抗拉强度低、耐久性、耐低温性差，导致了卷材的防水渗漏性极差.而建筑渗漏是困扰建筑界的普遍性问题，近年来国家建设部、各省市建委等相关部门出台了各种法规、规定。各科研单位也研制开发了许多新型防水材料，但始终不能完全杜绝渗漏问题.现有的防水材料大多采用改性沥青和热塑性弹性体SBS共混制成防水卷材，由于防水材料的物性、结构变形、施工及保护不当等原因，仍不能防止建筑物的渗漏.
发明内容
本发明的目的在于克服现有技术的缺点与不足，提供一种抗穿刺防水片材及其制备方法.
本发明的技术方案如下:
本发明的增强抗穿刺防水片材由下述重量份数的原料组成:
线性低密度聚乙烯 75～85份
热塑性弹性体SBS 5～10份
色母料 2～8份
助剂 1～5份
填充剂 5～10份
其中所述的SBS是苯乙烯-丁二烯-苯乙烯三元共聚物，其组成比例为S/B为30/70～50/50(重量)。
本发明所述的助剂包括光稳定剂、抗氧剂或润滑剂等等.
所述的光稳定剂包括紫外线吸收剂UV531；
所述的抗氧剂包括抗氧剂1010；
所述的润滑剂包括硬脂酸、硬脂酸锌；
所述的填充剂是:轻质或重质活性碳酸钙。
所述的色料包括各种颜色如黑、红、黄或绿色等等.
本发明所述的色母料含线性低密度聚乙烯、白油和色料，其组成及配比如下:线性低密度聚乙烯35～65份、白油25～65份和色料15～25份.
本发明所述增强抗穿刺防水片材(简称LECB)的制备方法，是将上述所有原料按配方要求计量放进高速混合机进行混合均匀，将混合均匀的物料加到挤出机料斗中，进入加热的挤出机料筒、衣架式模唇中成熔融的片状，再进入三辊压延机压延成一定厚度的薄片，经截切成一定宽度的片，经牵引机牵引，切成一定长度的卷，制成增强抗穿刺防水片材。
本发明人仔细研究了目前的施工工艺，采用改性沥青和热塑性弹性体苯乙烯-丁二烯-苯乙烯三元共聚物(SBS)共混制成防水卷材，存在着如下的缺点:1、改性沥青和热塑性弹性体SBS共混制成防水卷材，拉伸强度低，伸长率小，性能差。2、铺设改性沥青和热塑性弹性体SBS共混制成防水卷材时容易破裂.3、该防水卷材的防水、防渗漏、耐候性等性能差.4、铺设防水卷材后容易窜水，窜水后不易发现窜水的水源.
为了解决这一长期不能解决的难题，本发明对目前使用的改性沥青和热塑性弹性体SBS共混制成防水卷材进行了分析，尤其是原材料的选用、配方的设计和增强抗穿刺防水片材的成型方法和成型工艺进行了试探与研究.选用线性低密度聚乙烯、热塑性弹性体SBS、助剂和色母料等为原料，经挤出和三辊压延机压延成一定厚度的薄片，经截切成一定宽度的片，经牵引机牵引切成一定长度的卷，便制成了LECB防水片材.
在材料的选用、配方的设计中本发明进行了一系列实验包括:(1)、固定色母料、助剂和填充剂的用量，分别选用HDPE、LDPE、EVA和LLDPE原料进行挤出压延实验，测试性能数据.(2)、固定原料、色母料和填充剂，改变助剂的种类和用量进行挤出压延实验，测试性能数据.(3)、为了降低成本，本发明采用改变填充剂的种类和用量进行挤出压延实验，测试性能数据.得到性价比最佳的配方.
本发明增强抗穿刺防水片材(简称LECB)的特点:具有优良的抗穿刺性、防水、防渗漏、耐候性、高拉伸强度、低线体膨胀、摩擦系数大、变形适应性强、温度适应范围宽、使用方便、寿命长、易施工及造价低等诸多优良综合经济、技术性能指标.
说明书附图
图1、LECB防水片材挤出压延流程:
具体实施方式
实施例1
配方及制备方法:
线性低密度聚乙烯 85kg
热塑性弹性体SBS 10kg
抗氧剂1010 1kg
色母料 3kg
轻质碳酸钙 3kg
将所有原料按配方要求计量放进高速混合机进行混合均匀，投到挤出机料斗中，按说明书附图所描述的工艺流程进行挤出压延成型，制成LECB防水片材.挤出机料筒和衣架模唇各段加工温度如下:
料筒:一区 二区 三区 四区 五区 六区 七区 法兰
140℃ 150℃ 155℃ 160℃ 165℃ 175℃ 185℃ 175℃
衣架模唇:一区 二区 三区 四区 五区 六区 七区 八区 九区
195℃ 190℃ 185℃ 180℃ 180℃ 185℃ 185℃ 190℃ 195℃
本发明所制备的LECB防水片材的主要性能:
| 序号 | 项目 | 指标 |
| 1 | 拉伸强度Mpa | 14 |
| 2 | 断裂伸长率％≥ | 500 |
| 3 | 撕裂强度N/mm≥ | 60 |
| 4 | 剪切性能(片材与铝板)N/mm≥ | 5.0或粘合面外断裂 |
| 5 | 剥离性能(片材与粘结剂)N/mm≥ | 1.5或粘合面外断裂 |
| 6 | 剪切性能(片材与水泥砂浆粘结)N/mm≥ | 6.0或粘合面外断裂 |
| 7 | 剥离性能(片材与水泥砂浆粘结)N/mm≥ | 2.0或粘合面外断裂 |
| 8 | 不透水性压力≥0.3Mpa保持30min | 不透水 |
| 9 | 臭氧老化40℃×168h | 无裂纹 |
| 10 | 10％Ca(OH)<sub>2</sub>常温168h断裂强度保持率％≥断裂伸长率保持率％≥ | 8090 |
| 11 | 柔度(低温弯折) | -35℃无裂纹 |
实施例2
高密度聚乙烯 85kg
热塑性弹性体SBS 6kg
紫外线吸收剂UV531 4kg
色母料 3kg
轻质碳酸钙 2kg
制备方法与实施例1相同.
实施例3
线性低密度聚乙烯 85kg
热塑性弹性体SBS 10kg
抗氧剂1010 2kg
色母料 3kg
轻质碳酸钙 8kg
制备方法与实施例1完全一样.
实施例4
线性低密度聚乙烯 85kg
热塑性弹性体SBS 3kg
抗氧剂1010 2kg
色母料 3kg
白油 1kg
制备方法与实施例1完全一样.
性能比较表
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | |
| 拉伸强度MPa | 14 | 17.4 | 12.5 | 15.8 |
| 断裂伸长率％ | 510 | 603 | 501 | 578 |
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内.
Claims (4)
1、一种抗穿刺防水片材，其特征在于:由下述重量份数的原料组成:
线性低密度聚乙烯 75～85份
热塑性弹性体SBS 5～10份
色母料 2～8份
光稳定剂、抗氧剂或润滑剂 1～5份
填充剂 5～10份
其中所述的SBS是苯乙烯-丁二烯-苯乙烯三元共聚物，其组成比例为S/B为30/70～50/50(重量)；
所述的色母料由下述原料组成:线性低密度聚乙烯35～65份、白油25～65份和色料15～25份。
2、如权利要求1所述的防水片材，其中所述的填充剂是:轻质或重质活性碳酸钙。
3、如权利要求1所述的防水片材，其中所述的光稳定剂为紫外线吸收剂UV531；所述的抗氧剂为抗氧剂1010；所述的润滑剂为硬脂酸或硬脂酸锌。
4、一种制备权利要求1所述防水片材的方法，其特征在于，将权利要求1所定义的原料按重量份数要求计量放进高速混合机混合均匀，制成抗穿刺防水片材的混合料；将混合均匀的物料加到挤出机料斗中，进入加热的挤出机料筒、衣架式模唇中成熔融的片状，再进入三辊压延机压延成一定厚度的薄片，经截切成一定宽度的片，经牵引机牵引，切成一定长度的卷，制成增强抗穿刺防水片材。