CN100463793C - 一种尼龙挂胶轮片的生产方法 - Google Patents
一种尼龙挂胶轮片的生产方法 Download PDFInfo
- Publication number
- CN100463793C CN100463793C CNB2006100880897A CN200610088089A CN100463793C CN 100463793 C CN100463793 C CN 100463793C CN B2006100880897 A CNB2006100880897 A CN B2006100880897A CN 200610088089 A CN200610088089 A CN 200610088089A CN 100463793 C CN100463793 C CN 100463793C
- Authority
- CN
- China
- Prior art keywords
- nylon
- rubber
- wheel
- base wheel
- die cavity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种尼龙挂胶轮片的生产方法，属于尼龙制品加工技术领域。其特征是包括以下步骤：按设计要求生产尼龙基础轮和挂胶金属模，在尼龙基础轮的轮槽表面均匀涂刷橡胶粘接剂，同时在挂胶金属模模腔内表面均匀涂刷脱模剂，将尼龙基础轮正确定位在挂胶金属模模腔内。将橡胶均匀填充在模腔内后合模，同时对模腔进行加热硫化；加热硫化后将轮片脱模静置在空气中自然冷却。本发明科学合理，生产制造容易，尼龙和橡胶之间的亲和力好，不易脱胶。由于橡胶的硬度远低于导线外层铝绞线的硬度，可以很好的保护导线不受损伤。另外尼龙挂胶轮片的成品率高于铸造铝合金挂胶轮片，因此生产效率高、成本低，具有广阔的市场前景。
Description
技术领域
本发明涉及一种轮片的生产方法，特别是尼龙挂胶轮片的生产方法，属于尼龙制品加工技术领域。
背景技术
目前在导线放线和光缆架设施工中所采用的放线滑车轮片主要采用以下几种形式：1、铸造铝合金轮，由于该轮硬度高于导线铝丝，在张力放线中会对导线产生严重磨损，故此轮一般只适合用在人工放线中。2、铸造铝合金挂胶轮，由于铸造铝合金与橡胶的亲和力较差，在使用过程中易脱胶。故在橡胶磨损或脱胶的情况下会露出铸造铝合金基体，从而对导线产生损伤；3、MC尼龙轮，因强度高、耐磨性好、重量轻、抗老化、加工工艺性好等优点被普遍应用在放线施工中。但是因MC尼龙轮的硬度高于橡胶，该轮对导线的损伤已接近GB50233标准所规定的磨损极限下限，尤其是不断出现的扩径导线和光缆线，既要求轮片要有较高的强度和耐磨性，又要求有较低的硬度以减少对导线或光缆导线的损伤，从目前的施工情况来看，现有的放线滑车轮片已无法满足这些要求。所以研制生产出强度高和耐磨性好，又有较低硬度的放线滑车轮片，是摆在我们生产企业和科研部门面前的一个新课题。
发明内容
本发明所要解决的技术问题是提供一种尼龙挂胶轮片的生产方法，采用该方法生产的尼龙挂胶轮片既具有较高的强度和耐磨性，又有较低的硬度，在导线放线施工中能避免对导线或光缆的损伤。
本发明的技术方案是这样实现的：一种尼龙挂胶轮片的生产方法，其特征是包括以下步骤：
(1)、按设计要求采用热铸塑法生产尼龙基础轮；
(2)、以尼龙基础轮为基础，按设计要求设计并制造挂胶金属模，挂胶金属模的直径大于尼龙基础轮直径；
(3)、在尼龙基础轮的轮槽表面均匀涂刷橡胶粘接剂，同时在挂胶金属模模腔内表面均匀涂刷脱模剂，将尼龙基础轮正确定位在挂胶金属模模腔内。
(4)、将橡胶均匀填充在模腔内后合模，同时对模腔进行加热硫化；
(5)、加热硫化后将轮片脱模静置在空气中自然冷却。
所述的尼龙基础轮为MC尼龙基础轮。
所述的挂胶金属模材质为45号钢；硬度为HRC24-28；模腔内表面粗糙度低于0.8微米。
合模压力为155—165MPa。
加热硫化的硫化温度为140—160℃，硫化压力为155—165MPa，硫化时间为40—50min。
本发明科学合理，生产制造容易，采用尼龙如MC尼龙作为轮片的基体，使轮片具备了足够的机械强度，耐磨性高、绝缘性好，特别是尼龙和橡胶之间的亲和力好，不易脱胶。由于橡胶的硬度远低于导线外层铝绞线的硬度，可以很好的保护导线不受损伤。另外尼龙挂胶轮片的成品率高于铸造铝合金挂胶轮片，因此生产效率高、成本低。具有广阔的市场前景。
具体实施方式
以φ660mm MC尼龙挂胶轮片为例，阐述其生产方法：
1、将φ660mm滑轮产品图纸轮槽部分均缩小10mm，并在轮槽部分设计出half线，作为MC尼龙基体轮；
2、用热铸塑法生产MC尼龙基础轮；
3、以φ660mm滑轮产品图纸为原型，设计并制造挂胶金属模。金属模的材质为45号钢；硬度为HRC24-28；模腔内表面粗糙度低于0.8微米；
4、在MC尼龙基础轮要挂胶的表面均匀涂刷橡胶粘接剂，与此同时在挂胶金属模模腔内表面均匀涂刷脱模剂，尽快将MC尼龙基础轮正确定位在挂胶金属模模腔内。
5、将5.3kg丁腈橡胶均匀填充在模腔内后采用四柱敞开式压力机合模，合模压力为160MPa；
6、对模腔加热硫化。硫化温度为150℃，蒸汽硫化压力控制在160MPa，硫化时间控制在45min。
7、轮片脱模后，将MC尼龙挂胶轮片静置在空气中自然冷却。
Claims (4)
1.一种尼龙挂胶轮片的生产方法、其特征是包括以下步骤：
(1)、按设计要求采用热铸塑法生产尼龙基础轮；
(2)、以尼龙基础轮为基础，按设计要求设计并制造挂胶金属模，挂胶金属模的直径大于尼龙基础轮直径；
(3)、在尼龙基础轮的轮槽表面均匀涂刷橡胶粘接剂，同时在挂胶金属模模腔内表面均匀涂刷脱模剂，将尼龙基础轮正确定位在模腔内；
(4)、将橡胶均匀填充在模腔内后合模，同时对模腔进行加热硫化；
(5)、加热硫化后将轮片脱模静置在空气中自然冷却。
2.根据权利要求1所述的一种尼龙挂胶轮片的生产方法，其特征是所述的尼龙基础轮为MC尼龙基础轮。
3.根据权利要求1所述的一种尼龙挂胶轮片的生产方法，其特征是所述的挂胶金属模材质为45号钢；硬度为HRC24-28；模腔内表面粗糙度低于0.8微米。
4.根据权利要求1所述的一种尼龙挂胶轮片的生产方法，其特征是所述的加热硫化的硫化温度为140—160℃，硫化压力为155—165MPa，硫化时间为40—50min。