CN100457428C - New-type electric fireplace flame board and its making process - Google Patents
New-type electric fireplace flame board and its making process Download PDFInfo
- Publication number
- CN100457428C CN100457428C CNB2006101713694A CN200610171369A CN100457428C CN 100457428 C CN100457428 C CN 100457428C CN B2006101713694 A CNB2006101713694 A CN B2006101713694A CN 200610171369 A CN200610171369 A CN 200610171369A CN 100457428 C CN100457428 C CN 100457428C
- Authority
- CN
- China
- Prior art keywords
- flame board
- polyester resin
- unsaturated polyester
- flame
- weight portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses one new type electric fireplace flame board and its making process. The flame board is made through mixing transparent unsaturated polyester resin, curing agent and hardening agent; vacu micron deairing and dewatering of the mixture inside a vacu micron machine; molding; demolding; washing and surface smoothness treatment. The flame board is tough and transparent, and can form vivid flame.
Description
Technical field
The present invention relates to a kind of novel electric fireplace flame board and preparation method thereof.
Background technology
In recent years, in order to obtain of an antique style effect, increase indoor attractive in appearancely, the electric fireplace that has emulation flame generating means and a flame board is because of its welcome that not only has the heating function of traditional fire and decorative effect and can also reduce environmental pollution, keep ecological balance thereby be subjected to consumers in general.Emulation flame generating means normally makes light emitted go out light in the electricity fireplace, utilize the flame effect flickering unit that the light of light source is carried out dynamic strong and weak change process again, make strong and weak different light pass the flame shaping assembly that is distributed with glory hole, make dynamic, project on the flame board (glass screen) that is placed in emulation carbon piece back as the light beam of flame seedling shape, send the flame pattern of a kind of plane emulation thereby form the burning of carbon piece.Yet the flame board of Chang Yong emulation pad fireplace all is the one-board structure in the market, is made by glass, and this flame board see-through of being made by glass is little, only has the level of plane animation, and flame simulation effect and verisimilitude are poor.
Summary of the invention
Problem to be solved by this invention provides that a kind of novel to produce the flame image third dimension strong, the preparation method of the flame board of the electric fireplace that simulated effect and verisimilitude are good.
Technical scheme of the present invention is as follows:
A kind of preparation method of flame board of electric fireplace may further comprise the steps:
A. in the unsaturated polyester resin of 90-98 weight portion, add the cobalt naphthenate of the methyl ethyl ketone peroxide of 0.5-1 weight portion or cycloethanone peroxide or oxygen dibenzoyl, 0.3-1 weight portion, put into the vacuum machine after the back inverted die that stirs is interior and carry out vacuum, air and moisture content in the unsaturated polyester resin are got rid of, treated the moulding of unsaturated polyester resin setting and hardening;
B. the flame board behind the taking-up hardened forming cleans and carries out smooth surface and handle from mould, obtains described flame board.For the flame pattern that makes generation is attractive in appearance, various informative, described preparation method is further comprising the steps of:
C. spraying or colored drawing flame board after the drying;
D. spray one deck paint behind spraying or the colored drawing from the teeth outwards.
Another technical problem to be solved of the present invention provides the flame board of the good electric fireplace of a kind of simulated effect and verisimilitude.
The technical scheme that solves the problems of the technologies described above is:
A kind of flame board of electric fireplace is to be prepared by the following method by unsaturated polyester resin:
A. in the unsaturated polyester resin of 90-98 weight portion, add the cobalt naphthenate of the methyl ethyl ketone peroxide of 0.5-1 weight portion or cycloethanone peroxide or oxygen dibenzoyl, 0.3-1 weight portion, put into the vacuum machine after the back inverted die that stirs is interior and carry out vacuum, air and moisture content in the unsaturated polyester resin are got rid of, treated the moulding of unsaturated polyester resin setting and hardening;
B. the flame board behind the taking-up hardened forming cleans and carries out smooth surface and handle from mould, obtains described flame board.As a further improvement on the present invention, also has pattern on the flame board of described electric fireplace by spraying or colored drawing.
The flame board of electric fireplace of the present invention has and high temperature resistantly reaches 90 ℃-100 ℃, and good toughness is analysed transparently clearly, and light transmittance is strong, can form to beat as genuine flame, and simulated effect and verisimilitude are good, and can be painted with various pattern, create an aesthetic feeling thereon; The flame board of this electricity fireplace is made simple, and cost is low, is fit to a large amount of production.
The specific embodiment
Embodiment 1
Unsaturated polyester resin is purchased in Feitian chemical industry Co., Ltd, and greenery board, its Main Ingredients and Appearance are phthalic anhydride, cis-butenedioic anhydride, ethylene glycol, diethylene glycol, propane diols, styrene, shake the change agent.In the 910g unsaturated polyester resin, add 5g curing agent---methyl ethyl ketone peroxide, 4g curing agent---cobalt naphthenate, stir, put into the vacuum machine after being inverted in the mould that is fit to according to the required specification size of reality and carry out vacuum drying, air in the unsaturated polyester resin and moisture content are got rid of, product solidified in about 10 minutes, about 60 minutes hardened formings, clean after about 4 hours, flush away surface grease, make the clear wash rice of product lines clean, then, with the water wave yarn remained on surface foreign material are removed again, surface treatment is smooth, obtain the flame board that unsaturated polyester resin prepares.Treat dry laggard pedestrian worker's spraying of flame board or colored drawing figure line, spray one deck paint at last from the teeth outwards, play a protective role, finally had the simulated effect flame board true to nature of pattern.
The flame board of this electricity fireplace is easy to use, and is easy to operate, Pasting or directly go up screw and be fixed in the electric fireplace.
Embodiment 2
Unsaturated polyester resin is purchased in Feitian chemical industry Co., Ltd, and greenery board, its Main Ingredients and Appearance are phthalic anhydride, cis-butenedioic anhydride, ethylene glycol, diethylene glycol, propane diols, styrene, shake the change agent.In the 950g unsaturated polyester resin, add 6g curing agent---oxygen dibenzoyl, 9g curing agent---cobalt naphthenate, stir, put into the vacuum machine after being inverted in the mould that is fit to according to the required specification size of reality and carry out vacuum drying, air in the unsaturated polyester resin and moisture content are got rid of, product solidified in big 20 minutes, about 60 minutes hardened formings, clean after about 4 hours, flush away surface grease, make the clear wash rice of product lines clean, then, with the water wave yarn remained on surface foreign material are removed again, surface treatment is smooth, obtain the flame board that unsaturated polyester resin prepares.Treat dry laggard pedestrian worker's spraying of flame board or colored drawing figure line, spray one deck protection paint at last from the teeth outwards, finally had the simulated effect flame board true to nature of pattern.
Embodiment 3
Unsaturated polyester resin is purchased in Feitian chemical industry Co., Ltd, and greenery board, its Main Ingredients and Appearance are phthalic anhydride, cis-butenedioic anhydride, ethylene glycol, diethylene glycol, propane diols, styrene, shake the change agent.In the 980g unsaturated polyester resin, add 9g curing agent---cycloethanone peroxide, 5.5g curing agent---cobalt naphthenate, stir, put into the vacuum machine after being inverted in the mould that is fit to according to the required specification size of reality and carry out vacuum drying, air in the unsaturated polyester resin and moisture content are got rid of, product solidified in about 20 minutes, about 60 minutes hardened formings, clean after about 4 hours, flush away surface grease, make the clear wash rice of product lines clean, then, with the water wave yarn remained on surface foreign material are removed again, surface treatment is smooth, obtain the flame board that unsaturated polyester resin prepares.Treat dry laggard pedestrian worker's spraying of flame board or colored drawing figure line, spray the paint of one deck protective effect from the teeth outwards at last, finally had the simulated effect flame board true to nature of pattern.
Claims (4)
1. the preparation method of the flame board of an electric fireplace is characterized in that may further comprise the steps:
A. in the unsaturated polyester resin of 90-98 weight portion, stir behind the cobalt naphthenate of the methyl ethyl ketone peroxide of interpolation 0.5-1 weight portion or cycloethanone peroxide or oxygen dibenzoyl, 0.3-1 weight portion, put into the vacuum machine after in the inverted die and carry out vacuum, air and moisture content in the unsaturated polyester resin are got rid of, treated the moulding of unsaturated polyester resin setting and hardening;
B. the flame board behind the taking-up hardened forming cleans and carries out smooth surface and handle from mould, obtains described flame board.
2. the preparation method of the flame board of electric fireplace according to claim 1 is characterized in that further comprising the steps of:
C. spraying or colored drawing flame board after the drying;
D. spray one deck paint behind spraying or the colored drawing from the teeth outwards.
The flame board of 3 one kinds of electric fireplaces is characterized in that it is prepared from by the following method by unsaturated polyester resin:
A. in the unsaturated polyester resin of 90-98 weight portion, stir behind the cobalt naphthenate of the methyl ethyl ketone peroxide of interpolation 0.5-1 weight portion or cycloethanone peroxide or oxygen dibenzoyl, 0.3-1 weight portion, put into the vacuum machine after in the inverted die and carry out vacuum, air and moisture content in the unsaturated polyester resin are got rid of, treated the moulding of unsaturated polyester resin setting and hardening;
B. the flame board behind the taking-up hardened forming cleans and carries out smooth surface and handle from mould, obtains described flame board.
4. the flame board of electric fireplace according to claim 3 is characterized in that: also have pattern by spraying or colored drawing.