CN100436557C - 一种仿石材的喷涂涂料 - Google Patents
一种仿石材的喷涂涂料 Download PDFInfo
- Publication number
- CN100436557C CN100436557C CNB2005100574187A CN200510057418A CN100436557C CN 100436557 C CN100436557 C CN 100436557C CN B2005100574187 A CNB2005100574187 A CN B2005100574187A CN 200510057418 A CN200510057418 A CN 200510057418A CN 100436557 C CN100436557 C CN 100436557C
- Authority
- CN
- China
- Prior art keywords
- coating
- portions
- coatings
- powder
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于建筑材料领域,特别涉及一种仿石材的喷涂涂料。涂料由基料、辅料、粘接剂、表面漆料组成,各组分的组成为(以下为重量份)基料:玉石粉+腻子粉;其中玉石粉80~120目,8~35份;腻子粉200目,45~60份;辅料:增白剂和增稠剂;增白剂0.1~0.5份;增稠剂0.2~0.6份;粘接剂:胶水+纤维素+水性丙烯酸;其中胶水7~25份;纤维素0.3~10份;水性丙烯酸1.0~7份。本发明硬度与大理石、花岗石相当,并有一定的韧性,用于外墙有装饰美观,不脱落、开裂,浸泡不变形,无毒的优点。本涂料还有成本低的特点。
Description
技术领域
本发明属于建筑材料领域,特别涉及一种硬度大、有一定韧性的、无毒副作用的仿石材的喷涂涂料。
背景技术
目前,国内市场使用的外墙砖通常采用瓷砖、马赛克、天然大理石、人造大理石、花岗石等材料。由于这些材料用水泥粘贴墙上,除增加墙体的负荷以外,往往由于所用的材料不同而其附着力不同,使所贴的建筑材料如瓷砖、马赛克、天然大理石、人造大理石、花岗石等材料时有脱落,常危及路人和居民的安全。据不完全统计,全国每年因瓷砖、马赛克、天然大理石、人造大理石、花岗石等材料的脱落而被砸死砸伤造成伤害的约200人左右,因此上述材料不适宜用做外墙装饰。作为装饰材料瓷砖、马赛克等虽有价格便宜的优点,但脆性大,易破碎,光洁度较差,外表不够美观,由于瓷砖或马赛克是一块块的粘贴拼接的,常有色差产生,而影响装饰效果;大理石、花岗石虽然美观,硬度大,光洁度好,但因本身具有放射性,对人体有害,不适宜室内使用,另外大理石、花岗石有易破碎、有色差、易剥落、易变色等缺点,使得使用范围受到限制,另外大理石、花岗石还有安装施工复杂,价格昂贵,成本高的缺点。
发明内容
本发明的目的,是提供一种仿石材的喷涂涂料。它硬度与大理石、花岗石相当,并有一定的韧性,用于外墙有装饰美观,不脱落、开裂,浸泡不变形,无毒的优点。本涂料还有成本低的特点。
本发明的技术方案是:
涂料由基料、辅料、粘接剂组成,各组分的组成为(以下为重量份)
基料:玉石粉+腻子粉
其中天然玉石粉 80~120目 8~35份
腻子粉 200目 45~60份
辅料:增白剂和增稠剂
增白剂 0.1~0.5份
增稠剂 0.2~0.6份
粘接剂胶水+纤维素+水性丙烯酸
其中胶水 7~25份
纤维素 0.3~10份
水性丙烯酸 1.0~7份。
其中:纤维素采用上海赛璐洛厂生产的,产品名称为羧甲基纤维素钠的纤维素;腻子粉采用上虞市富强建陶有限公司生产的,产品名称为多功能内外墙腻子粉的腻子粉;胶水采用重庆长寿川维化工厂生产的,产品名称为高粘性1799胶水的胶水;水性丙烯酸采用江苏省南通生达化工有限公司生产的,产品名称为纯丙乳液的水性丙烯酸;增白剂采用江西青山化工有限公司生产的,产品名称为荧光增白剂的增白剂;增稠剂采用姜堰市新兴建筑材料有限公司生产的,产品名称为轻分型增稠剂的增稠剂。
本发明涂料若需要在喷涂层增加颜色,则可以添加微量调色漆,调色漆的添加量根据需要喷涂的色彩设定。
在本涂料表面喷涂表面漆料,可以增加涂料的硬度、光洁度、耐侯性、耐紫外线和耐酸碱性。表面漆料由树脂和油性丙烯酸组成。
本发明由于甲基纤维素是非离子型水溶性聚合物,在产品体系中起增稠、稳定、粘结、分散、乳化作用,能保留水分,形成薄膜和提供保护胶体(protectivecolloid)效应,能溶于冷热水中,有很好的相溶性,耐酸碱度。当PH值为2-12时,具有极佳的成膜性和良好的配伍性。因此甲基纤维素与玉石粉、腻子粉混合时,有遇水澎涨,遇低温收缩和极强的粘接力的特性,使整个喷涂层可以适应外界环境温度变化而热胀冷缩,具有一定的韧性。
水性丙烯酸有粒径细、高光泽、优良的耐候性和抗回粘性的特点;胶水有增粘和交联作用,因此将玉石粉、腻子粉与水性丙稀酸,胶水混合后,使本发明涂料的基料与墙面结合为一体,成为一种组织结构严密,密度高的一种复合性石材。
本发明加入的1799胶水中的聚乙烯醇有增粘和交联作用,可以减少胶水的用量,使涂料中的醛的含量大大降低,经检测本涂料的含醛大大低于国家标准。
油性丙烯酸能与阳光发生碳化作用,抵抗紫外线及红外线侵蚀,用于本涂料可以使其涂层的耐候性好,不变色,光泽高,硬度高,附着力强,耐磨性优良。
本涂料可以根据用户的需要,对涂料进行调色,使涂料层为大理石花纹、花岗石花纹、以及各种各样的色彩和花纹,因此本发明还有色彩变化多样的特点。本涂料喷涂为大理石花纹、花岗石花纹时与其有同样的感观但性能比大理石、花岗石更好。
本涂料的可以用于喷涂外墙面、内墙面、地面等,其装饰美观,无缝隙,用于墙面装饰可以减轻墙体的负荷。本涂料的表面涂层光亮度、硬度与大理石、花岗石相当、光滑度好,有一定的韧性,有色泽持久,无色差、不开裂,耐蚀性高,耐擦洗的优点。本涂料的使用寿命长,室外使用时间可达20年以上。是国家禁止用瓷砖、石材装饰外墙后的替代产品。
本涂料的成本低,其造价是大理石、花岗石的三分之一至四分之一,用于旧墙翻新其成本是大理石、花岗石的五分之一至六分之一。
本涂料还可以用于各种花台、装饰性建筑、工艺品、景观等的装饰,有着广泛的应用前景。
下面通过实施例对本发明做进一步的说明。
具体实施方式
按表1取各组分原料,按照下列方法配制涂料:在容器中加入天然玉石粉、腻子粉搅拌均匀后,加入增白剂和增稠剂,再加入1799胶水、纤维素,搅拌均匀即得到本涂料。若涂料需要调制为有颜色的和/或有花纹的,还应该添加调色剂。调色剂由调色粉和色浆组成,调色剂的加入量根据所需要调制的色彩深浅而设置。
表1本发明所述涂料的各原料成分组成:(各原料为重量份)
取上表配方涂料,按下列方法喷涂(以喷涂带色彩和花纹的墙面为例):用通常的方法清洁墙面,用本涂料在墙面批底,使墙面保持平整,待墙体干后再润湿墙面,喷调色漆,(调色漆的添加量根据需要喷涂的色彩深浅设定)再喷花纹漆,待漆面干燥度为75%~80%,打磨漆面。用外墙腻子膏满批喷涂表面,待干燥后打磨,再喷涂表面漆料,打磨抛光,即得到光感柔和、细腻、无颗粒、立体感强、层次分明、美观的墙面。
若喷涂无色墙面,去掉喷调色漆步骤,其余步骤与上述的工艺相同。
本涂料物理性能检测结果如表2所示。
表2仿石材涂料的性能检测结果
序号 | 检测项目 | 技术指标 | 检测结果 | 结论 |
1 | 施工性 | 喷涂无困难 | 无困难 | 合格 |
2 | 初期干燥抗裂性 | 无裂纹 | 无裂纹 | 合格 |
3 | 干燥时间(表面干燥) | 干燥时间h≤4 | 3.0小时表面干燥 | 合格 |
4 | 耐水性 | 120小时涂层无起鼓、开裂、剥落与未浸泡部分相比较颜色轻微变化 | 无起鼓、开裂、剥落,颜色无变化 | 合格 |
5 | 耐碱性 | 120小时涂层无起鼓、开裂、剥落与未浸泡部分相比较颜色轻微变化 | 无起鼓、开裂、剥落,颜色无变化 | 合格 |
6 | 耐冲性 | 涂层无裂纹、剥落和明显变化 | 涂层无裂纹、剥落和明显变化 | 合格 |
7 | 涂层耐温变化 | 12小时涂层无粉化、开裂、剥落与标准相比颜色轻微变化 | 无粉化、开裂、剥落与标准相比颜色轻微变化 | 合格 |
8 | 耐玷污性 | 循环实验 | 容易清洗,无污染 | 合格 |
建筑物的表面层不起泡的现象,在建筑行业中称为无起鼓。
Claims (2)
1.一种仿石材的喷涂涂料,其特征在于:涂料由基料、辅料、粘接剂、表面漆组成,各成分的组成为(以下为重量份)
基料:玉石粉+腻子粉
其中 玉石粉 80-120目 8-35份
腻子粉 200目 45-60份;
辅料:增白剂和增稠剂
增白剂 0.1-0.5份
增稠剂 0.2-0.6份;
粘接剂:胶水+纤维素+水性丙烯酸
其中 胶水 7~25份
纤维素 0.3~10份
水性丙烯酸 1.0~7份;
表面漆喷涂在由基料、辅料、粘接剂组成的涂料的表面。
2.根据权利要求1所述的一种仿石材的喷涂涂料,其特征在于:玉石粉为天然玉石粉。