CN100429287C - Organosilicon alcohol acid ready mixed paint coating composition and method of making the same - Google Patents
Organosilicon alcohol acid ready mixed paint coating composition and method of making the same Download PDFInfo
- Publication number
- CN100429287C CN100429287C CNB2006100474357A CN200610047435A CN100429287C CN 100429287 C CN100429287 C CN 100429287C CN B2006100474357 A CNB2006100474357 A CN B2006100474357A CN 200610047435 A CN200610047435 A CN 200610047435A CN 100429287 C CN100429287 C CN 100429287C
- Authority
- CN
- China
- Prior art keywords
- coating composition
- zinc
- mixed paint
- paint coating
- ready mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an organic silanol acid blending paint composition and preparing method, which comprises the following parts: solvent oil, organic silicon resin, titanium dioxide, phthalidyl, barium sulfate, cobaltic naphthenate, zinc naphthenate, manganese isooctanoic acid and zinc isooctanoic acid. the preparing comprises the following steps: blending titanium dioxide, phthalidyl, barium sulfate and organic silicon resin in the grinding container to grind with fineness not more than 30 mum; adding solvent oil to stir evenly to form the first liquid; putting cobaltic naphthenate, zinc naphthenate, manganese isooctanoic acid and zinc isooctanoic acid in the first liquid; stirring to ripening for 1 h.
Description
Technical field:
The present invention relates to a kind of coating for metal surfaces coating composition and preparation method thereof, particularly a kind of coating for metal surfaces coating composition that contains silicone resin and preparation method thereof.
Background technology:
Common alkyd ready-mixed paint is formed by modulation such as Synolac, pigment, pigment extender, siccative and organic solvents, only decoration function is played in the metallic surface, is higher than under 105 ℃ the operating condition and be lower than-45 ℃, easily sticks up layer, peeling; These deficiencies have determined the limitation of common alkyd ready-mixed paint on using, and have influenced industrial protection and decoration to metal.Though in order to address the above problem, each scientific research institutions, each chemical enterprise, develop various composition coating coating one after another, wherein are no lack of various resin paints, but also just have one's own knack in a certain respect, and over-all properties all can't satisfy the needs of industry in individual events such as sticking power, acidproof, alkaline-resisting, salt tolerant, oil resistant, moisture resistances.
Summary of the invention:
In order to address the above problem, the invention provides a kind of metal surface protection and ornamental organosilicon alcohol acid ready mixed paint coating composition of being used for.The coating that forms with this organosilicon alcohol acid ready mixed paint coating composition of the present invention has over-all propertieies such as strong adhesion, acidproof, alkaline-resisting, salt tolerant, oil resistant, moisture resistance, has solved industrial to the protection of metallic substance and the problem of decoration effectively.
Another object of the present invention provides a kind of preparation method of aforementioned coating composition.
The technical solution used in the present invention is: a kind of organosilicon alcohol acid ready mixed paint coating composition, it is characterized in that it is made of by weight percentage following component,
Solvent oil 5%～10% silicone resin 45%～60%
Titanium dioxide 15%～25% phthalein viridescent 1%～4%
Barium sulfate 5%～20% cobalt naphthenate 1%～3%
Zinc naphthenate 1%～3% manganese iso-octoate 1%～3%
Isocaprylic acid zinc 1%～3%;
Described solvent oil is aromatic solvent naphtha or dimethylbenzene.
The preparation method of organosilicon alcohol acid ready mixed paint coating composition is as follows: (a) titanium dioxide, phthalein viridescent, barium sulfate and silicone resin mixture are put into mill and be ground to fineness and be not more than 30 μ m, add solvent oil and stir, become first liquid; (b) cobalt naphthenate, zinc naphthenate, manganese iso-octoate and isocaprylic acid zinc are joined in the first liquid; (c) stirring and slaking are 1 hour; Above steps is all carried out under normal temperature and normal pressure.
In above-mentioned organosilicon alcohol acid ready mixed paint coating composition, solvent oil plays the solvent action of component, and each component is mixed; Silicone resin formal name used at school polyorganosiloxane resin has high temperature resistant, weather-proof and chemical-resistant, can strengthen the sticking power of enamelled coating, strengthens acidproof, alkaline-resisting, salt tolerant, oil resistant, moisture resistance performance, the viscosity of enhancing composition; Titanium dioxide is inorganic salt, strengthens the photosensitive property of enamelled coating; The dark green color and luster that strengthens enamelled coating of phthalein, the ornamental performance of raising paint film; Barium sulfate is inorganic salt, strengthens wear-resisting, the withstand voltage properties of enamelled coating; The siccative of cobalt naphthenate, zinc naphthenate, manganese iso-octoate system: compositions strengthens the drying varniss time effectively; Speed of response between the composition component is quickened in isocaprylic acid zinc and manganese iso-octoate acting in conjunction, strengthens the integrated performance index of enamelled coating.
The invention has the beneficial effects as follows: coating composition of the present invention can adopt conventional the coating, for example by roller coat, spraying or brushing method, convenient and equably this coating is coated on the metallic surface, form coating through natural air drying, the coating mean thickness is about 20 μ m, this coating has easy to operation, and time of drying is short, excellent comprehensive performances such as strong adhesion, moisture resistance performance be strong, it is acidproof, alkaline-resisting to have, salt tolerant, oil resistant.Can guarantee the effect that coating for metal surfaces plays protection and decorates metallic substance under-70 ℃～150 ℃ industrial condition.
Embodiment:
Further specify the present invention below by embodiment and Comparative Examples, with time of drying, wear resistance, acidproof, alkaline-resisting, salt tolerant, oil resistant, and envrionment temperature test and verify the present invention.Temperature experiment: metallic substance is placed under the certain temperature, check foaming, dropping situations; Wear resistance: by universal method, apply 1kg pressure, behind 1000r, measure loss amount (weight before loss amount=mill-mill is weight afterwards), the low more explanation sticking power of this numerical value is strong more; Acidproof: the sulphuric acid soln that metallic substance is placed 25% (mass percent); Alkaline-resisting: the sodium hydroxide solution that metallic substance is placed 40% (mass percent); Salt tolerant: the sodium chloride solution that metallic substance is placed 3% (mass percent);
Embodiment 1
At normal temperatures and pressures, press specified each component consumption in the table 1, titanium dioxide, phthalein viridescent, barium sulfate and silicone resin mixture are put into mill be ground to fineness and be not more than 30 μ m, add No. 200 solvent oils of aromatic hydrocarbons and stir, become first liquid; Cobalt naphthenate, zinc naphthenate, manganese iso-octoate and isocaprylic acid zinc are joined in the first liquid; The slurry coating material composition is made in stirring and slaking 1 hour.Viscosimetric, adopt spraying method that coating composition is coated on metal sheet (metal sheet smooth finish is Δ 7), make coating, under the normal temperature and pressure natural condition, drying, the performance under the time of drying of testing coating, thermotolerance, wear resistance, acidproof, alkaline-resisting, salt tolerant, oil resistant, the envrionment temperature then.Test result sees Table 1.
Embodiment 2
Press the consumption of specified each component in the table 1, repeat the method for embodiment 1, solvent oil is with No. 200 aromatic solvent naphthas, and test result sees Table 1.
Embodiment 3
Press the consumption of specified each component in the table 1, repeat the method for embodiment 1, but solvent oil dimethylbenzene, test result sees Table 1.
Comparative Examples 1
By weight, with 10 parts of solvent oils, 50 parts of Synolac, 25 parts of titanium dioxides, dark green 3 parts of phthalein, 10 parts in barium sulfate, 1 part of cobalt naphthenate, zinc naphthenate place container for 1 part, stir, and make the slurry coating material composition.
With aforementioned coating composition, adopt spraying method that coating composition is coated on metal sheet (metal sheet smooth finish is Δ 7), under the normal temperature and pressure natural condition, dry, make coating, then the performance under the time of drying of testing coating, thermotolerance, wear resistance, acidproof, alkaline-resisting, salt tolerant, oil resistant, the envrionment temperature.Test result sees Table 1.
Comparative Examples 2
By weight, with 10 parts of solvent oils, 60 parts of Synolac, 20 parts of titanium dioxides, dark green 2 parts of phthalein, 6 parts in barium sulfate, 1 part of cobalt naphthenate, zinc naphthenate place container for 1 part, stir, and make the slurry coating material composition.
With aforementioned coating composition, adopt spraying method that coating composition is coated on metal sheet (metal sheet smooth finish is Δ 7), under the normal temperature and pressure natural condition, dry, make coating, then the performance under the time of drying of testing coating, thermotolerance, wear resistance, acidproof, alkaline-resisting, salt tolerant, oil resistant, the envrionment temperature.Test result sees Table 1.
The test data of each embodiment and Comparative Examples coating explanation from table 1, organosilicon alcohol acid ready mixed paint coating composition of the present invention has good comprehensive performances.
Table 1
Claims (4)
1, a kind of organosilicon alcohol acid ready mixed paint coating composition is characterized in that it is made up of following compositions in weight percentage,
Solvent oil 5%～10% silicone resin 45%～60%
Titanium dioxide 15%～25% phthalein viridescent 1%～4%
Barium sulfate 5%～20% cobalt naphthenate 1%～3%
Zinc naphthenate 1%～3% manganese iso-octoate 1%～3%
Isocaprylic acid zinc 1%～3%.
2, organosilicon alcohol acid ready mixed paint coating composition according to claim 1 is characterized in that described solvent oil is an aromatic solvent naphtha.
3, organosilicon alcohol acid ready mixed paint coating composition according to claim 2 is characterized in that described aromatic solvent naphtha is a dimethylbenzene.
4, the preparation method of the described organosilicon alcohol acid ready mixed paint coating composition of a kind of claim 1 is characterized in that its preparation process is as follows:
(a) by proportioning, titanium dioxide, phthalein viridescent, barium sulfate and silicone resin mixture are put into mill be ground to fineness and be not more than 30 μ m, add solvent oil and stir, become first liquid;
(b) by proportioning, cobalt naphthenate, zinc naphthenate, manganese iso-octoate and isocaprylic acid zinc are joined in the first liquid;
(c) stirring and slaking are 1 hour;
Above steps is all carried out under normal temperature and normal pressure.