CN100415976C - Super softening treating technology for floss - Google Patents
Super softening treating technology for floss Download PDFInfo
- Publication number
- CN100415976C CN100415976C CNB2005100799068A CN200510079906A CN100415976C CN 100415976 C CN100415976 C CN 100415976C CN B2005100799068 A CNB2005100799068 A CN B2005100799068A CN 200510079906 A CN200510079906 A CN 200510079906A CN 100415976 C CN100415976 C CN 100415976C
- Authority
- CN
- China
- Prior art keywords
- product utilization
- dyeing
- treatment
- floss
- bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to an over soft treatment process of knitting wool. Said process includes the following several steps: after the antistatic agent and over soft adjuvant are added into the sliver made of Australian merino high count wool, utilizing sliver mixing machine to make treatment, then utilizing gilling machine to make treatment, and utilizing roving machine to make treatment and utilizing spinning frame to make treatment, then utilizing cone winding machine to make treatment and dyeing treatment.
Description
Technical field
The present invention relates to a kind of super softening treating technology for floss.
Background technology
Existing knitting wool fabric is compared with pure cashmere being difficult to aspect flexibility, elasticity and the bulkiness, and its ABRASION RESISTANCE and anti-pilling are also relatively poor, can't make consumer satisfaction.
Summary of the invention
At above-mentioned the deficiencies in the prior art, it is good to the invention provides a kind of fabric softness that knitting wool is made, elasticity and bulkiness, the super softening treating technology for floss that ABRASION RESISTANCE and anti-pilling are good.
Super softening treating technology for floss of the present invention, it comprises the steps:
(1) wool top of Australian merino high count wool being made utilizes gilling machine to handle after adding B301 antistatic additive and super soft additive;
(2) the product utilization gill box that step (1) is obtained carries out scalp acupuncture, two pins, the processing of three pins, makes the bar bar even;
(3) the product utilization Speed frames that step (2) is obtained are handled under the situation of Wu Site prosecution, and are even with the bar bar of guaranteeing to enter next procedure;
(4) the product utilization fine spining machine that step (3) is obtained is handled;
(5) the product utilization bobbin winder that step (4) is obtained carries out single treatment at least, to remove the yarn defect;
(6) the product utilization two-for-one twister that step (5) is obtained is handled, and makes the single thread twist be shaped;
(7) product that step (6) the is obtained processing of dyeing after dyeing finishes, adds water dyeing liquor is reduced to room temperature, and the pH value of adjusting dyeing liquor with acetic acid or formaldehyde is 5-6 then, adds the softener of 4%-8% again according to the weight of dyeing liquor.
Super softening treating technology for floss of the present invention utilizes bobbin winder to carry out after-treatment in the wherein said step (4), removing the yarn defect, adds 6% softener in the described step (7) according to the weight of dyeing liquor.
Compare with existing super softening treating technology for floss, advantage and good effect of the present invention are: because it adopts the distinctive processing step of the present invention: after the wool top that Australian merino high count wool is made adds B301 antistatic additive and super soft additive, utilize gilling machine to handle, the product utilization gill box that obtains is carried out scalp acupuncture, two pins, the processing of three pins, make the bar bar even; The product utilization Speed frames that obtain are handled under the situation of Wu Site prosecution, even with the bar bar of guaranteeing to enter next procedure, the product utilization fine spining machine that obtains is handled, the product utilization bobbin winder that obtains is carried out single treatment at least, to remove the yarn defect, the product utilization two-for-one twister that obtains is handled, make the single thread twist be shaped, with the product that the obtains processing of dyeing, in the dyeing processing procedure, add soft additive, thereby fabric softness, elasticity and bulkiness that knitting wool is made are good, and ABRASION RESISTANCE and anti-pilling are good.
The specific embodiment to super softening treating technology for floss of the present invention is described in further detail below.
The specific embodiment
Embodiment 1
Super softening treating technology for floss, it comprises the steps:
(1) wool top of Australian merino high count wool being made utilizes gilling machine to handle after adding B301 antistatic additive and the super soft additive of Henkel board;
(2) the product utilization gill box that step (1) is obtained carries out scalp acupuncture, two pins, the processing of three pins, makes the bar bar even;
(3) the product utilization Speed frames that step (2) is obtained are handled under the situation of Wu Site prosecution, and are even with the bar bar of guaranteeing to enter next procedure;
(4) the product utilization fine spining machine that step (3) is obtained is handled;
(5) the product utilization bobbin winder that step (4) is obtained carries out after-treatment, to remove the yarn defect;
(6) the product utilization two-for-one twister that step (5) is obtained is handled, and makes the single thread twist be shaped;
(7) product that step (6) the is obtained processing of dyeing after dyeing finishes, adds water dyeing liquor is reduced to room temperature, and the pH value of adjusting dyeing liquor with acetic acid or formaldehyde is 5-6 then, adds 6% or 5% or 7% softener again according to the weight of dyeing liquor.
The auxiliary reagent factory is sent out by the manufacturer of above-mentioned B301 antistatic additive in the Chinese Academy of Sciences, the address is that the Technology Park is inspired in the Lixian County, Hebei province.The manufacturer of the super soft additive of above-mentioned Henkel board is a peaceful grease chemical article Co., Ltd of Shanghai section, and the address is: No. 3131, triumphant return road, Shanghai City.The manufacturer of above-mentioned soft additive gets chemical company for the Langfang City ALLRED.Above-mentioned Wu Site prosecution is meant that the Wu Site bar bar analyzer produced with Switzerland carries out prosecution, analysis to the bar bar of yarn, and is even to guarantee the bar bar.
Can obtain having the knitting wool of super flexible energy through above-mentioned PROCESS FOR TREATMENT.
Embodiment 2
Super softening treating technology for floss, it comprises the steps:
(1) wool top of Australian merino high count wool being made utilizes gilling machine to handle after adding antistatic additive and super soft additive;
(2) the product utilization gill box that step (1) is obtained carries out scalp acupuncture, two pins, the processing of three pins, makes the bar bar even;
(3) the product utilization Speed frames that step (2) is obtained are handled under the situation of Wu Site prosecution, and are even with the bar bar of guaranteeing to enter next procedure;
(4) the product utilization fine spining machine that step (3) is obtained is handled;
(5) the product utilization bobbin winder that step (4) is obtained carries out single treatment, to remove the yarn defect;
(6) the product utilization two-for-one twister that step (5) is obtained is handled, and makes the single thread twist be shaped;
(7) product that step (6) the is obtained processing of dyeing after dyeing finishes, adds water dyeing liquor is reduced to room temperature, and the pH value of adjusting dyeing liquor with acetic acid or formaldehyde is 5-6 then, adds 4% or 8% softener again according to the weight of dyeing liquor.
Can obtain having the knitting wool of super flexible energy through above-mentioned PROCESS FOR TREATMENT.
Embodiment recited above is described preferred implementation of the present invention, is not that design of the present invention and scope are limited.The content that the present invention asks for protection all is documented in claims.
Claims (2)
1. super softening treating technology for floss is characterized in that it comprises the steps:
(1) wool top of Australian merino high count wool being made utilizes gilling machine to handle after adding B301 antistatic additive and super soft additive;
(2) the product utilization gill box that step (1) is obtained carries out scalp acupuncture, two pins, the processing of three pins, makes the bar bar even;
(3) the product utilization Speed frames that step (2) is obtained are handled under the situation of Wu Site prosecution, and are even with the bar bar of guaranteeing to enter next procedure;
(4) the product utilization fine spining machine that step (3) is obtained is handled;
(5) the product utilization bobbin winder that step (4) is obtained carries out single treatment at least, to remove the yarn defect;
(6) the product utilization two-for-one twister that step (5) is obtained is handled, and makes the single thread twist be shaped;
(7) product that step (6) the is obtained processing of dyeing after dyeing finishes, adds water dyeing liquor is reduced to room temperature, and the pH value of adjusting dyeing liquor with acetic acid or formaldehyde is 5-6 then, adds the softener of 4%-8% again according to the weight of dyeing liquor.
2. a kind of super softening treating technology for floss according to claim 1 is characterized in that utilizing bobbin winder to carry out after-treatment in the described step (4), removing the yarn defect, adds 6% softener in the described step (7) according to the weight of dyeing liquor.