CN100412182C - Bathing bead and method for preparing the same - Google Patents

Abstract

The present invention discloses a multicolor bathing bead and a preparing method thereof. The multicolor bathing bead of the present invention is made from the following raw materials: water-soluble crystalline ammonia salt, water-soluble high-molecular polymer, pearl powder, bactericide, skin protecting agents, edible pigment and essence. The preparing method of the present invention comprises dissolving the water-soluble high-molecular polymer to make adhesive, adding the crystalline ammonia salt, the high-polymer adhesive, the edible pigment, the bactericide and the skin protecting agents into a mixer to be uniformly mixed, adding the pearl powder into mixture to obtain a bead with the diameter of 2 to 3 millimeters, drying the bead in an oven, taking material out to be cooled to room temperature, adding the essence, etc. The present invention can be used as washing sanitary accessories for individuals or public places to have the effects of skin protection and skin moistening so that the skin of a human body is tender and moistened and simultaneously the cross infection of bacteria and the propagation of diseases can be prevented.

Description

Bath pearl and manufacture method thereof that a kind of bathing is used

Technical field

The present invention relates to a kind of bath pearl that is used for individual bathing, it belongs to the sanitary washing article field, the invention still further relates to the manufacture method of this bath pearl.

Background technology

Now the take a shower sanitary washing article of usefulness of the individual who sells on the market is of a great variety, as perfumed soap, body wash etc., these articless for washing are owing to have only the decontamination cleaning function, and there are not skin care and germ-resistant function, therefore more or less can produce human body skin behind the life-time service stimulates, and makes xerosis cutis, coarse; Simultaneously because repeatedly repeating and intersecting use of perfumed soap may cause transmission of disease in the above because of bacterial adhesion.

Summary of the invention

The purpose of this invention is to provide the bath pearl that a kind of bathing is used, it can be used as the personal cleansing sanitary product, plays the effect of skin care skin moisten, makes human body skin tender lubricated, can prevent the cross infection of bacterium simultaneously again, prevents the spread of disease.

Another object of the present invention provides the manufacture method of a kind of above-mentioned bath pearl.

The technical solution adopted for the present invention to solve the technical problems is:

The bath pearl that a kind of bathing is used, it mainly is to be made by following raw materials in percentage by weight: volatile salt or ammonium citrate or above-mentioned two kinds of materials are with arbitrarily than formed mixture 90～99%, high molecular weight water soluble polymer 0.01～5%, pearlescence 0.2～3.5%, sterilant 0.1～0.3%, skin-protecting agent 0.08～0.25%, food dye 0.01～0.08%, essence 0.03～1.2%, described bath pearl is particulate state, and diameter is 2～3 millimeters.

Preferred high molecular weight water soluble polymer is polyoxyethylene or emulsion or the polyvinylpyrrolidone is made up of the multipolymer of vinyl acetate between to for plastic, acrylate and N one n-methylolacrylamide, or chooses two kinds wantonly with arbitrarily than formed mixture in above-mentioned three kinds of materials.

Preferred sterilant is Tegosept M or Imidurea, or above-mentioned two kinds of materials are with arbitrarily than formed mixture.

Preferred skin-protecting agent is a wallantoin.

Pearlescence of the present invention can be a mica titanium nacreous material.

In order to obtain the bath pearl that above-mentioned bathing is used, manufacture method of the present invention comprises the steps:

(1). high molecular weight water soluble polymer is dissolved in alcohol or alcohol and water blended solvent, make glue paste;

(2). after superpolymer glue paste, food dye, sterilant and the skin-protecting agent of evengranular crystal type ammonium salt, step (1) gained got the raw materials ready in proportion, add the blender uniform mixing;

(3). pearlescence is added in proportion in the compound of step (2) gained, pearlescence is evenly covered on the glue paste of crystal type ammonium salt particle surface, obtain diameter and be 2～3 millimeters globule;

(4). globule is put into baking oven, under 45～55 ℃ temperature, dried by the fire 20～40 minutes;

(5). take out material and be cooled to room temperature, get final product behind the adding essence.

The invention has the beneficial effects as follows: 1. the present invention adopts above-mentioned prescription, can play the effect of skin care skin moisten, make human body skin tender lubricated,, can make people's spirit happy during use and after using simultaneously because product of the present invention has the gorgeous color of pearly-lustre and pleasant fragrance; 2. the bath pearl that bathing of the present invention is used is made particulate state, is suitable for disposable use, can prevent the cross infection of bacterium, prevents the spread of disease, and is applicable to the washing sanitary product as the individual; 3. manufacturing approach craft of the present invention is simple, easy and simple to handle, and facility investment is little, and cost is low.

The present invention is further described below in conjunction with embodiment.

Embodiment 1

(1). high molecular weight water soluble polymer polyoxyethylene 30 gram joined in the alcohol dissolve, make glue paste;

(2). superpolymer glue paste, food dye 0.8 gram, sterilant Imidurea 3 grams and skin-protecting agent wallantoin 2 grams with evengranular volatile salt crystal 950 grams, step (1) gained add the blender uniform mixing;

(3). pearlescence 10 gram is added in the compound of step (2) gained, and uniform mixing evenly covers on the glue paste of volatile salt particle surface pearlescence, obtains diameter and be 2～3 millimeters globule;

(4). globule is put into baking oven, and baking is 40 minutes under 45 ℃ temperature, removes alcohol;

(5). take out material and be cooled to room temperature, get final product behind the adding 4.2 gram essence.

Embodiment 2

(1). high molecular weight water soluble polymer polyvinylpyrrolidone 10 gram is joined in the mixed solution of alcohol and water and dissolve, make glue paste;

(2). superpolymer glue paste, food dye 0.4 gram, sterilant Tegosept M 1 gram and skin-protecting agent wallantoin 2.5 grams with evengranular ammonium citrate crystal 980 grams, step (1) gained add the blender uniform mixing;

(3). pearlescence 5 gram is added in the compound of step (2) gained, and uniform mixing evenly covers on the glue paste of ammonium citrate particle surface pearlescence, obtains diameter and be 2～3 millimeters globule;

(4). globule is put into baking oven, and baking is 35 minutes under 50 ℃ temperature, removes alcohol and moisture content;

(5). take out material and be cooled to room temperature, get final product behind the adding 1.1 gram essence.

Embodiment 3

(1). multipolymer 50 gram of high molecular weight water soluble polymer vinyl acetate between to for plastic, acrylate and N one n-methylolacrylamide is joined in the mixed solution of alcohol and water and dissolve, make glue paste;

(2). mixture 2 grams and skin-protecting agent wallantoin 1 gram with superpolymer glue paste, food dye 0.5 gram, sterilant Imidurea and the Tegosept M of evengranular volatile salt and ammonium citrate mixed crystal 900 grams, step (1) gained add the blender uniform mixing;

(3). mica titanium nacreous material 35 gram is added in the compound of step (2) gained, and uniform mixing evenly covers on the glue paste of volatile salt and ammonium citrate particle surface pearlescence, obtains diameter and be 2～3 millimeters globule;

(4). globule is put into baking oven, and baking is 30 minutes under 55 ℃ temperature, removes alcohol and water;

(5). take out material and be cooled to room temperature, get final product behind the adding 11.5 gram essence.

Embodiment 4

(1). mixture 40 grams of the multipolymer of high molecular weight water soluble polymer vinyl acetate between to for plastic, acrylate and N hydroxymethyl acrylamide and polyvinylpyrrolidone are joined in the mixed solution of alcohol and water and dissolve, make glue paste;

(2). mixture 2 grams and skin-protecting agent wallantoin 1 gram with superpolymer glue paste, food dye 0.1 gram, sterilant Imidurea and the Tegosept M of evengranular volatile salt and ammonium citrate mixed crystal 930 grams, step (1) gained add the blender uniform mixing;

(3). mica titanium nacreous material 20 gram is added in the compound of step (2) gained, and uniform mixing evenly covers on the glue paste of volatile salt and ammonium citrate particle surface pearlescence, obtains diameter and be 2～3 millimeters globule;

(4). globule is put into baking oven, and baking is 40 minutes under 50 ℃ temperature, removes alcohol and water;

(5). take out material and be cooled to room temperature, get final product behind the adding 6.9 gram essence.

The foregoing description fully discloses bath pearl and the manufacture method thereof that bathing of the present invention is used, but it is not construed as limiting the invention.

Claims (5)

1. bath pearl that bathing is used, it is characterized in that it mainly is to be made by following raw materials in percentage by weight: volatile salt or ammonium citrate or above-mentioned two kinds of materials are with arbitrarily than formed mixture 90～99%, high molecular weight water soluble polymer 0.01～5%, pearlescence 0.2～3.5%, sterilant 0.1～0.3%, skin-protecting agent 0.08～0.25%, food dye 0.01～0.08%, essence 0.03～1.2%, described bath pearl is particulate state, and diameter is 2～3 millimeters.

2. the bath pearl that a kind of bathing according to claim 1 is used, it is characterized in that described high molecular weight water soluble polymer is polyoxyethylene or emulsion or the polyvinylpyrrolidone be made up of vinyl acetate between to for plastic, acrylate and N hydroxymethyl acrylamide multipolymer, or in above-mentioned three kinds of materials optional two kinds with arbitrarily than formed mixture.

3. the bath pearl that a kind of bathing according to claim 1 is used is characterized in that described sterilant is Tegosept M or Imidurea, or above-mentioned two kinds of materials are with arbitrarily than formed mixture.

4. the bath pearl that a kind of bathing according to claim 1 is used is characterized in that described skin-protecting agent is a wallantoin.

5. a method of making the bath pearl that the described bathing of claim 1 uses is characterized in that it comprises the steps:

(1). high molecular weight water soluble polymer is dissolved in alcohol or alcohol and water blended solvent, make glue paste;

(2). after superpolymer glue paste, food dye, sterilant and the skin-protecting agent of evengranular crystal type ammonium salt, step (1) gained got the raw materials ready in proportion, add the blender uniform mixing;

(3). pearlescence is added in proportion in the compound of step (2) gained, pearlescence is evenly covered on the glue paste of crystal type ammonium salt particle surface, obtain diameter and be 2～3 millimeters globule;

(4). globule is put into baking oven, under 45～55 ℃ temperature, dried by the fire 20～40 minutes;

(5). take out material and be cooled to room temperature, get final product behind the adding essence.