CN100408247C - Hastelloy B-3-钢金属复合材料的制造方法 - Google Patents

Hastelloy B-3-钢金属复合材料的制造方法 Download PDF

Info

Publication number
CN100408247C
CN100408247C CNB2006100175177A CN200610017517A CN100408247C CN 100408247 C CN100408247 C CN 100408247C CN B2006100175177 A CNB2006100175177 A CN B2006100175177A CN 200610017517 A CN200610017517 A CN 200610017517A CN 100408247 C CN100408247 C CN 100408247C
Authority
CN
China
Prior art keywords
steel
composite material
hastelloy
transition zone
explosive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100175177A
Other languages
English (en)
Other versions
CN1817546A (zh
Inventor
辛宝
侯发臣
岳宗洪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Luoyang Shuangrui Metal Composite Material Co., Ltd.
Original Assignee
Luoyang Shuangrui Metal Composite Materials Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Luoyang Shuangrui Metal Composite Materials Co ltd filed Critical Luoyang Shuangrui Metal Composite Materials Co ltd
Priority to CNB2006100175177A priority Critical patent/CN100408247C/zh
Publication of CN1817546A publication Critical patent/CN1817546A/zh
Application granted granted Critical
Publication of CN100408247C publication Critical patent/CN100408247C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种金属复合材料的制造方法。提出的Hastelloy B-3-钢金属复合材料的制造方法是将基层钢板和过渡层不锈钢板通过爆炸焊接复合一体获得过渡层-钢复合材料，再将获得的过渡层-钢复合材料和Hastelloy B-3通过爆炸焊接复合一体获得Hastelloy B-3-钢金属复合材料。通过本发明方法制造的Hastelloy B-3-钢金属复合材料具有良好的复合质量。

Description

Hastelloy B-3-钢金属复合材料的制造方法
技术领域
本发明涉及一种金属复合材料的制造方法，尤其是涉及Hastelloy B-3-钢金属复合材料的制造方法。
背景技术
爆炸焊接就是以炸药为能源，在炸药爆炸载荷作用下复层金属高速碰撞基层金属并强固的连接在一起的金属加工方法。传统的用爆炸焊接制造双金属复合材料的方法是：将复层金属和基层金属直接爆炸焊接获得双金属复合材料，用这种方法制造Hastelloy B-3-钢金属复合材料的不足之处是制得的HastelloyB-3-钢金属复合材料的复合质量较差。
发明内容
本发明的目的是提出Hastelloy B-3-钢金属复合材料的制造方法，使利用该方法制造的Hastelloy B-3-钢金属复合材料具有良好的复合质量。
本发明所提出的制造方法为：将基层钢板和过渡层不锈钢板通过爆炸焊接复合一体获得过渡层-钢复合材料，再将获得的过渡层-钢复合材料和Hastelloy B-3通过爆炸焊接复合体获得Hastelloy B-3-钢金属复合材料。
通过本发明方法制造的Hastelloy B-3-钢金属复合材料具有良好的复合质量。
附图说明
图1为过渡层不锈钢板和基层钢板爆炸焊接安装示意图。
图2为复层Hastelloy B-3和过渡层-钢复合材料爆炸焊接安装示意图。
图中，1、8号工业电雷管，2、炸药，3、过渡层不锈钢板，4、支撑物，5、基层钢板，6、砂基础，7、复层Hastelloy B-3，8、过渡层-钢复合材料。
具体实施方式
结合实施例对本发明制造方法加以说明：
如图1所示，将基层钢板5和过渡层不锈钢板3用砂轮或抛光叶轮打磨干净，除去金属表面的氧化物，露出金属光泽，将基层钢板5置于砂基础6之上，将过渡层不锈钢板3通过支撑物4支撑置于基层钢板上方，不锈钢厚度在2～5mm之间，两者间距在3～8mm之间，把炸药2铺放在过渡层不锈钢板3上表面，炸药可为：硝酸铵∶梯恩梯∶木粉∶食盐按质量比为(60～65)∶(6～8)∶(2～4)∶(25～31)，单位面积装药量在1.2～4.9g/cm2之间，用8号工业电雷管1起爆，获得过渡层-钢复合材料8；如图2所示，再将过渡层-钢复合材料8和复层Hastelloy B-37用抛光叶轮或砂轮打磨干净，将过渡层-钢复合材料8置于砂基础6之上，将复层Hastelloy B-37通过支撑物4支撑置于过渡层-钢复合材料上方，复层Hastelloy B-3的厚度在3～20mm之间，间距在4～16mm之间，把炸药2铺放在复层Hastelloy B-37表面，单位面积装药量在1.8～7.4g/cm2之间，用8号工业电雷管1起爆，爆炸焊接即可获得Hastelloy B-3-钢金属复合材料。
上述金属复合材料基层钢板的尺寸和材料牌号可以根据需要确定，复层Hastelloy B-3的尺寸可根据需要确定，过渡层不锈钢板以奥氏体不锈钢为宜。获得的金属复合材料经过热处理、校平后可以采用火焰切割等加工方法加工成各种形状和尺寸的Hastelloy B-3-钢金属复合材料产品。
实施例1：
制造一块Hastelloy B-3-钢金属复合材料，基层钢板牌号为16MnIV，尺寸为60×1200×2250mm，过渡层不锈钢板牌号为321，尺寸为3×1200×2250mm，复层为Hastelloy-B3，尺寸为8×1200×2250mm，过渡层不锈钢板与基层钢板爆炸焊接的间距为6mm，炸药为硝酸铵∶梯恩梯∶木粉∶食盐按质量比63∶7∶2∶28混合而成，直接铺放在过渡层不锈钢板表面，单位面积装药量为2.8g/cm2，用8号工业电雷管起爆，爆炸焊接获得过渡层-钢复合材料，再将复层HastelloyB-3与过渡层-钢复合材料爆炸焊接，间距为12mm，将上述炸药铺放在复层Hastelloy B-3表面，单位面积装药量为5.2g/cm2，，用8号工业电雷管起爆，爆炸焊接所得Hastelloy B-3-钢金属复合材料具有良好的复合质量。
实施例2：
制造一块Hastelloy B-3-钢金属复合材料，基层钢板牌号为20R，尺寸为40×1200×2250mm，过渡层不锈钢板牌号为316L，尺寸为2×1200×2250mm，复层为Hastelloy B-3，尺寸为20×1200×2250mm，过渡层不锈钢板与基层钢板
爆炸
焊接的间距为3mm，炸药为硝酸铵∶梯恩梯∶木粉∶食盐按质量比60∶6∶3∶31混合而成，直接铺放在过渡层不锈钢板表面，单位面积装药量为1.2g/cm2，用8号工业电雷管起爆，爆炸焊接获得过渡层-钢复合材料，再将复层HastelloyB-3与过渡层-钢复合材料爆炸焊接，间距为16mm，将上述炸药铺放在复层Hastelloy B-3表面，单位面积装药量为7.4g/cm2，，用8号工业电雷管起爆，爆炸焊接所得Hastelloy B-3-钢金属复合材料具有良好的复合质量。
实施例2：
制造一块Hastelloy B-3-钢金属复合材料，基层钢板牌号为16MnR，尺寸为40×1200×2250mm，过渡层不锈钢板牌号为304，尺寸为5×1200×2250mm，复层为Hastelloy B-3，尺寸为3×1200×2250mm，过渡层不锈钢板与基层钢板爆炸焊接的间距为8mm，炸药为硝酸铵∶梯恩梯∶木粉∶食盐按质量比65∶6∶4∶25混合而成，直接铺放在过渡层不锈钢板表面，单位面积装药量为4.9g/cm2，用8号工业电雷管起爆，爆炸焊接获得过渡层-钢复合材料，再将复层HastelloyB-3与过渡层-钢复合材料爆炸焊接，间距为4mm，将上述炸药铺放在复层Hastelloy B-3表面，单位面积装药量为1.8g/cm2，，用8号工业电雷管起爆，爆炸焊接所得Hastelloy B-3-钢金属复合材料具有良好的复合质量。

Claims (2)

1. 一种Hastelloy B-3-钢金属复合材料的制造方法，其特征是：将基层钢板和过渡层不锈钢板通过爆炸焊接复合一体获得过渡层-钢复合材料，再将获得的过渡层-钢复合材料和Hastelloy B-3通过爆炸焊接复合一体获得HastelloyB-3-钢金属复合材料。
2. 根据权利要求1所述的Hastelloy B-3-钢金属复合材料的制造方法，其特征是：所述基层钢板(5)和过渡层不锈钢板(3)爆炸焊接复合一体的方法为：将基层钢板(5)和过渡层不锈钢板(3)经表面处理后，将基层钢板(5)置于砂基础(6)之上，将过渡层不锈钢板(3)通过支撑物(4)支撑置于基层钢板(5)上方，两者间距在3～8mm，把炸药(2)铺放在过渡层不锈钢板(3)上表面，爆炸获得过渡层-钢复合材料(8)；所述过渡层-钢复合材料(8)和复层Hastelloy B-3(7)爆炸焊接复合一体的方法为：将过渡层-钢复合材料(8)和复层Hastelloy B-3(7)经表面处理后，将过渡层-钢复合材料(8)置于砂基础(6)之上，将复层Hastelloy B-3(7)通过支撑物(4)支撑位于过渡层-钢复合材料(8)上方，间距为4～16mm，把炸药(2)铺放在复层Hastelloy B-3(7)表面，爆炸获得Hastelloy B-3-钢金属复合材料。
CNB2006100175177A 2006-03-13 2006-03-13 Hastelloy B-3-钢金属复合材料的制造方法 Expired - Fee Related CN100408247C (zh)