CN100402751C - 一种路面快速修补填料 - Google Patents
一种路面快速修补填料 Download PDFInfo
- Publication number
- CN100402751C CN100402751C CNB2005100613849A CN200510061384A CN100402751C CN 100402751 C CN100402751 C CN 100402751C CN B2005100613849 A CNB2005100613849 A CN B2005100613849A CN 200510061384 A CN200510061384 A CN 200510061384A CN 100402751 C CN100402751 C CN 100402751C
- Authority
- CN
- China
- Prior art keywords
- road surface
- filling material
- parts
- quick speed
- repairing road
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种路面快速修补填料,所述的路面快速修补填料主要包括重量配比如下的组分:沥青70~80份,焦油60~80份,二氧化硅450~500份,沙石料350~450份。所述的沙石料中石子重量含量为40~60%,沙子重量含量为40~60%。本发明所述的路面快速修补填料的有益效果主要体现在:(1)操作简单快速,修补后2~3分钟即可通车,大大降低了工程对交通的影响;(2)修补后的路面抗冻性好,能耐重压,返修率低,大为节约成本。
Description
(一)技术领域
本发明涉及一种路面快速修补填料。
(二)背景技术
目前公路、桥梁的主体通常为混凝土结构,在使用中普遍存在着破损路面与桥梁的修补和养护问题。现有技术中,公路的修补办法是用柏油和石子经过高温修补而成,这样修补的路面在冬天抗冻性较差,导致维护频率高、总体成本高;也有用混凝土材料进行修补,但是存在维修、保养繁琐,周期长,成本也较高。而且此两种方法对道路进行修补后,均需要较长时间固化方可投入使用,不利于道路快速维修与快速投入使用。
(三)发明内容
本发明既是为了提供一种施工简单迅速、修补后道路可快速投入使用、且成本低的路面快速修补填料。
为达到发明目的本发明采用的技术方案是:
一种路面快速修补填料,所述的路面快速修补填料主要包括重量配比如下的组分:
沥青 70~80份
焦油 60~80份
二氧化硅 450~500份
沙石料 350~450份。
所述的沙石料中石子重量含量为40~60%,沙子重量含量为40~60%,所述的沙石料中石子直径为5~10mm。
优选的,所述的路面快速修补填料重量配比如下:
沥青 80份
焦油 80份
二氧化硅 500份
沙石料 400份。
通常的,所述的沙石料中石子重量含量为50%。
对路面进行修补时,只需将各种材料加入补胶机中,65~85℃下搅拌10分钟左右即可进行施工。
本发明所述的路面快速修补填料的有益效果主要体现在:(1)操作简单快速,修补后2~3分钟即可通车,大大降低了工程对交通的影响;(2)修补后的路面抗冻性好,能耐重压,返修率低,大为节约成本。
(四)具体实施方式
下面结合具体实施例对本发明进行进一步描述,但本发明的保护范围并不仅限于此:
实施例1:
填料配方:
沥青 80公斤
焦油 80公斤
二氧化硅 500公斤
沙子 200公斤
石子(直径5~10mm) 200公斤
浙江省慈溪市宗汉镇上梁山路,混凝土路面,缝约有6m长,宽约60cm,深度10~20cm,路面修补时为8月,将上述材料投入补胶机中,65~70℃下搅拌10分钟左右后,对路面进行修补,修补完成后2分钟即通车,经过一年多使用,以及几十吨重压至今安然无恙。
实施例2:
填料配方:
沥青 35公斤
焦油 30公斤
二氧化硅 250公斤
沙子 120公斤
石子(直径5~10mm) 80公斤
浙江省慈溪市高王到常河段桥头,石头路面,有直径80cm,深30cm大坑,路面修补时为冬季,将上述材料投入补胶机中,75~85℃下搅拌12分钟左右,对路面进行修补,修补完成后3分钟即通车,第二天下雪,路面丝毫无损,至今无返修。
实施例3:
填料配方:
沥青 8公斤
焦油 7公斤
二氧化硅 45公斤
沙子 16公斤
石子(直径5~10mm) 24公斤
浙江省慈溪市宗汉镇拆落市村,沥青公路,以前经常出现较多小洞,每1~2月需返修一次,用上述材料加入补胶机中,70~80℃下搅拌10分钟,对路面进行修补,使用半年多至今未返修。
Claims (4)
1.一种路面快速修补填料,其特征在于所述的路面快速修补填料主要包括重量配比如下的组分:
沥青 70~80份
焦油 60~80份
二氧化硅 450~500份
沙石料 350~450份;
所述的沙石料中石子重量含量为40~60%,沙子重量含量为40~60%。
2.如权利要求1所述的路面快速修补填料,其特征在于所述的沙石料中石子直径为5~10mm。
3.如权利要求2所述的路面快速修补填料,其特征在于所述的路面快速修补填料重量配比如下:
沥青 80份
焦油 80份
二氧化硅 500份
沙石料 400份。
4.权利要求3所述的路面快速修补填料,其特征在于所述的沙石料中石子重量含量为50%。