CN100386418C - Waterfree car washing type fresh maintenance agent and its prepn. method

Info

Publication number: CN100386418C
Application number: CNB2006100652570A
Authority: CN
Inventors: 王士奎
Original assignee: Individual
Current assignee: Individual
Priority date: 2006-03-21
Filing date: 2006-03-21
Publication date: 2008-05-07
Anticipated expiration: 2026-03-21
Also published as: CN1834215A

Abstract

The present invention discloses a curing agent for retreading automobile tyres without using water and a preparation method thereof, which relates to the field of curing articles for automobiles. Aiming to solve the problems that when a curing agent for retreading automobile tyres in the prior art is used, water resources are wasted as tyres are cleaned with water first, and the performance of a curing agent for retreading automobile tyres in the prior art is unstable, the present invention provides an environmental protecting curing agent for retreading automobile tyres without using water, which has stable performance and convenient application; the curing agent for retreading automobile tyres without using water comprises 10 to 50% of RHODORSIL EIP emulsion, 0.2 to 2.5% of nonionic surfactant, 0.5 to 5.0% of triethanolmine, 1.0 to 6.0% of ethylene glycol, 0.3 to 1.6% of BS-12, 1.0 to 6.0% of solvent oil, 0.3 to 1.5% of ammonium hydroxide, 0 to 0.2% of preservative, 0 to 0.005% of dye and deionized water as the rest. The curing agent has the advantages of simple technology, stable performance and easy use and is beneficial for environmental protection.

Description

A kind of vehicle tyre renovation curing agent and preparation method thereof

Technical field

A kind of vehicle tyre renovation curing agent and preparation method thereof relates to automobile maintenance articles for use field.

Background technology

Maintenance for tire in the prior art all is to need first water that tire is cleaned up, and then nurse maintenance with the tyre rebuilding curing agent, present commercial tyre rebuilding agent stability is bad, the mulser that these products are used high-shear mostly carries out emulsification pretreatment, or grind with colloidal mill, make emulsion more stable, but, even if adopted such operation, the performance of these products is also unstable, and easily layering approximately will layering about a week after the can, it need be shaken up during use, so just cause the instability of product performance.

The importance of water resources has been that people all know, and water cleans up tire needs a large amount of water, cause the significant wastage of water resources, and the cleaning of tire can't be carried out in the insufficient place at the water source.

Summary of the invention

An object of the present invention is to use the tyre rebuilding curing agent to need first water that tire is cleaned in the above-mentioned prior art for solving, waste water resource, tyre rebuilding maintenance formulation energy problem of unstable provides a kind of stable performance, it is convenient to use, and is beneficial to the vehicle tyre renovation curing agent of environmental protection.

Another object of the present invention provides a kind of preparation method of vehicle tyre renovation curing agent.

For achieving the above object, a technical scheme of the present invention provides a kind of vehicle tyre renovation curing agent, the material that comprises following weight per-cent: RHODORSIL EIP emulsion 10-50%, nonionogenic tenside 0.2-2.5%, trolamine 0.5-5.0%, ethylene glycol 1.0-6.0%, BS-12 0.3-1.6%, solvent oil 1.0-6.0%, ammoniacal liquor 0.3-1.5%, all the other are deionized water.

Can also comprise sanitas 0-0.2%, dyestuff 0-0.005%.

Screening formulation of the present invention: RHODORSIL EIP emulsion 15-30%, nonionogenic tenside 0.5-1.5%, trolamine 1.5-3.0%, ethylene glycol 2.0-4.0%, BS-12 0.5-1.2%, solvent oil 1.5-4.2%, ammoniacal liquor 0.5-1.0%, sanitas 0.07-0.15%, dyestuff 0.001-0.003%, all the other are deionized water.

Screening formulation of the present invention: RHODORSIL EIP emulsion 27.08%, TX-101.0%, trolamine 2.05%, ethylene glycol 2.5%, BS-12 0.8%, solvent oil 2.29%, ammoniacal liquor 0.68%, sanitas 0.1%, dyestuff 0.002%, all the other are deionized water.

Nonionogenic tenside be selected from alkylphenol polyoxyethylene, the fatty alcohol-polyoxyethylene ether any one or multiple, also can use nonionogenic tenside of the prior art.

The preferred TX-10 of nonionogenic tenside, TX-10 are the trade name of alkylphenol polyoxyethylene.

Described solvent oil is a boiling range 100-350 ℃ petroleum fractions.Preferred petroleum fractions is a kerosene.

Described ammoniacal liquor is strong aqua of the prior art, mass percent concentration (NH ₃Content) more than or equal to 20%.

Described sanitas is a sanitas of the prior art, as: Tegosept M, ethyl p-hydroxybenzoate, triumphant honeybee-88 etc.

Used dyestuff is a dyestuff of the prior art, as: emerald green blue, bright red, tangerine, bright orchid, light green, carbon black etc.

For achieving the above object, a technical scheme of the present invention provides a kind of preparation method of vehicle tyre renovation curing agent.

1) .A liquid: deionized water is added in the stirred pot, under constantly stirring, add nonionogenic tenside successively, trolamine, ethylene glycol, BS-12 then;

2) .B liquid: under agitation the EIP emulsion is added in the solvent oil;

3). under agitation the B liquid that mixes is added in the above-mentioned A liquid that mixes, add ammoniacal liquor, mix the back discharging.

A kind of preparation method of vehicle tyre renovation curing agent.

1) .A liquid: deionized water is added in the stirred pot, under constantly stirring, add nonionogenic tenside successively, thanomin, ethylene glycol, BS-12 then;

2) .B liquid: the EIP emulsion of inciting somebody to action under agitation adds in the solvent oil;

3). under agitation the B liquid that mixes is added in the above-mentioned A liquid that mixes, add ammoniacal liquor again, sanitas adds the dyestuff toning at last, mixes the back discharging, packs on request.

Beneficial effect:

1. present commercial tyre rebuilding agent stability is bad; easily layering; the present invention is a kind of tyre rebuilding curing agent of steady state of homogenous emulsion type; except that having stable emulsion state; on using method, also have greatly improved; traditional product needed elder generation water cleans up tire; thereby and then be a kind of water-saving environmentfriendly products with the product that the present invention relates to of effect that the tyre rebuilding curing agent plays the protection tire; has cleaning; maintenance; the function that glazing is finished simultaneously; i.e. water and directly use product of the present invention not just can decontamination; maintenance is finished simultaneously, is a kind of special product of waterless carwash.

2. improve owing to prescription of the present invention, thereby adopt novel macromolecule resin EIP emulsion that the vehicle tyre renovation agent of production can be existed with the form of a stable emulsion, thereby solved existing related products poor stability, easy stratified shortcoming, and because novel high polymer is stated the employing of resin EIP production technique is simplified, has therefore reduced production cost.

3.BS-12 adding make product have the antistatic effect that other like products did not have.The existing product in market is not owing to consider the influence of static to the product effect, make after using very fast by a lot of dust of electrostatic adhesion on tire, influence the effect of product.

4. production technique of the present invention is simplified, thereby has saved production cost.

5. the present invention has reversed needs first water that tire is cleaned up in the prior art, and then with the mindset of tyre rebuilding curing agent, provides a kind of new product and method, has greatly saved resource, simplifies technology, is beneficial to the protection of industrial production and environment

Embodiment

Enumerate embodiment below, the present invention is further specified, but the present invention is not only limited to these embodiment.The various raw materials of mentioning herein are the commercially available prod.

Embodiment 1

RHODORSIL EIP emulsion 27.08kg, TX-10 1.0kg, trolamine 2.05kg, ethylene glycol 2.5kg, BS-12 0.8kg, solvent oil 2.29kg, concentration are 20% ammoniacal liquor 0.68kg, Tegosept M 0.1kg, emerald green blue 0.1kg, deionized water 63.5kg.

1) .A liquid: deionized water is added in the stirred pot, under constantly stirring, add nonionogenic tenside, trolamine, ethylene glycol, BS-12 successively in proportion then;

2) .B liquid: a certain proportion of EIP emulsion under agitation adds in the solvent oil;

3). under agitation the B liquid that mixes is added in the above-mentioned A liquid that mixes, add ammoniacal liquor, Tegosept M adds emerald green blue toning at last, mixes the back discharging, packs on request.

Claims

1. a vehicle tyre renovates curing agent, the material that comprises following weight per-cent: RHODORSILEIP emulsion 10-50%, nonionogenic tenside 0.2-2.5%, trolamine 0.5-5.0%, ethylene glycol 1.0-6.0%, BS-120.3-1.6%, solvent oil 1.0-6.0%, ammoniacal liquor 0.3-1.5%, all the other are deionized water; Described nonionogenic tenside is TX-10; Described solvent oil is a boiling range 100-350 ℃ petroleum fractions.

2. according to the described vehicle tyre renovation of claim 1 curing agent, it is characterized in that, also comprise sanitas 0-0.2%, dyestuff 0-0.005%.

3. according to the described vehicle tyre renovation of claim 1 curing agent, it is characterized in that, comprise the material of following weight per-cent: RHODORSIL EIP emulsion 15-30%, nonionogenic tenside 0.5-1.5%, trolamine 1.5-3.0%, ethylene glycol 2.0-4.0%, BS-12 0.5-1.2%, solvent oil 1.5-4.2%, ammoniacal liquor 0.5-1.0%, sanitas 0.07-0.15%, dyestuff 0.001-0.003%, all the other are deionized water.

4. according to the described vehicle tyre renovation of claim 1 curing agent, it is characterized in that, the material that comprises following weight per-cent: RHODORSIL EIP emulsion 27.08%, TX-101.0%, trolamine 2.05%, ethylene glycol 2.5%, BS-12 0.8%, solvent oil 2.29%, ammoniacal liquor 0.68%, sanitas 0.1%, dyestuff 0.002%, all the other are deionized water.

5. according to the described vehicle tyre renovation of claim 1 curing agent, it is characterized in that described solvent oil is a kerosene.

6. according to the preparation method of the described vehicle tyre renovation of claim 1 curing agent, it is characterized in that the step of this method is as follows:

1) .A liquid: deionized water is added in the stirred pot, under constantly stirring, add nonionogenic tenside, trolamine, ethylene glycol successively, BS-12 then;

2) .B liquid: under whipped state, the EIP emulsion is added solvent oil;

3). under agitation the B liquid that mixes is added in the above-mentioned A liquid that mixes, add ammoniacal liquor again, mix the back discharging.

7. according to the preparation method of the described vehicle tyre renovation of claim 5 curing agent, it is characterized in that the step of this method is as follows:

2) .B liquid: under agitation the EIP emulsion is added in the solvent oil;

3). under agitation the B liquid that mixes is added in the above-mentioned A liquid that mixes, add ammoniacal liquor, sanitas, the dyestuff that adds at last toning mixes the back discharging, packs on request.