CN100369992C - 水性纳米铝塑漆 - Google Patents

水性纳米铝塑漆 Download PDF

Info

Publication number
CN100369992C
CN100369992C CNB2006100165851A CN200610016585A CN100369992C CN 100369992 C CN100369992 C CN 100369992C CN B2006100165851 A CNB2006100165851 A CN B2006100165851A CN 200610016585 A CN200610016585 A CN 200610016585A CN 100369992 C CN100369992 C CN 100369992C
Authority
CN
China
Prior art keywords
water
nanometer
agent
plastic
company
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100165851A
Other languages
English (en)
Other versions
CN1807532A (zh
Inventor
徐静涛
周华起
董立群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGCHUN SAINA NANO PAINT Co Ltd
Original Assignee
CHANGCHUN SAINA NANO PAINT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGCHUN SAINA NANO PAINT Co Ltd filed Critical CHANGCHUN SAINA NANO PAINT Co Ltd
Priority to CNB2006100165851A priority Critical patent/CN100369992C/zh
Publication of CN1807532A publication Critical patent/CN1807532A/zh
Application granted granted Critical
Publication of CN100369992C publication Critical patent/CN100369992C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种水性纳米铝塑漆，涉及建筑、装饰行业用的涂料，是由纳米丙烯酸聚酯乳液、纳米丙烯酸聚酯单体乳液、水性稳定型铝颜料、增稠剂、分散剂、润湿剂、消泡剂、去离子水经过分散机搅拌分散、砂磨、过滤等工艺制成致密的涂膜，有效的阻止水和氧的透入，涂膜平滑，绿色环保、无污染，具有超强的耐洗刷性，完全可替代铝塑板，造价低廉，施工简单。

Description

水性纳米铝塑漆
技术领域：
本发明涉及一种涂料，尤其是涉及一种用于建筑、装饰行业的绿色环保水性纳米铝塑漆。
背景技术：
近年来，铝塑板在建筑、装饰行业中使用量逐年加大，但其价格较高，施工不便，因此，人们正在努力寻求一种可在墙面上直接涂装的涂料来替代铝塑板。目前，市场上的仿铝塑漆都是溶剂型的，内含大量的挥发性溶剂，在生产及使用过程中会挥发出大量的VOC，这种涂料中散发的有机挥发物是建筑污染的主要污染源，对环境，对人员都会产生巨大的损害。
发明内容：
本发明所要解决的技术问题是提供一种具有铝塑板效果的绿色环保水性纳米铝塑漆。
本发明的组分和含量以重量百分比为：
纳米丙稀酸聚酯乳液                3.8-7.5％
纳米丙稀酸聚酯单体乳液            40-57％
水性稳定型铝颜料                  4-10％
增稠剂                            1.9-6.8％
分散剂                 0.15-0.75％
润湿剂                 0.15-0.48％
消泡剂                 0.3-0.37％
去离子水               31-35％
本发明还包含有防冻剂、PH调节剂、成膜助剂醇酯-12、防腐剂、表面功能剂BYK-535，其重量百分比为：
纳米丙稀酸聚酯乳液            3.8-7.5％
纳米丙稀酸聚酯单体乳液        41-56.5％
水性稳定型铝颜料              4-10％
增稠剂                        1.8-4.8％
分散剂                        0.35-0.65％
润湿剂                        0.47-0.65％
消泡剂                        0.3-0.38％
去离子水                      23-27％
防冻剂                        2-3％
PH调节剂                      0.15-0.16％
成膜助剂醇酯                  -122.25-2.7％
防腐剂                        0.15-0.16％
表面功能剂BYK-535             3.25-3.90％
所述的增稠剂为：香港毅捷化工的EW、德国德固萨公司的R972和德国南方化学公司H600或者香港毅捷化工的EW、德国德固萨公司的R972和德国南方化学公司的H400或者香港毅捷化工的EW、德国德固萨公司的R972和德国南方化学公司的H600和德国南方化学公司的H400。
所述的分散剂为：海川化上3275或海川化工的5040或荷兰EFKA公司3580中至少一种。
所述的润湿剂为：海川化工H875和/或美国陶氏化学公司NP-9。
本发明的制备方法具体步骤如下：
1.在容器中按配方量加入去离子水、纳米丙烯酸聚酯乳液、分散剂、消泡剂、润湿剂、增稠剂EW和R972，用分散机进行低速搅拌分散，分散转速200-400转/分钟，分散时间20-30分钟；
2.用研磨设备将上述步骤取得的半成品进行砂磨至细度小于25um；
3.向2中加入纳米丙烯酸聚酯单体乳液进行搅拌分散，分散转速200-400转/分钟，分散时间40-50分钟；
4.向3中加入水性稳定型铝颜料进行搅拌、分散，分散转速200-400转/分钟，分散时间40-50分钟；
5、向4中加入增稠剂H600和/或H400。
如果还包含防冻剂、PH调节剂、成膜助剂醇酯-12、防腐剂、表面功能剂BYK-535，其制备方法是：在上述制备方法步骤3中与纳米丙烯酸聚酯单体乳液同时加入，其余步骤相同。
本发明积极效果如下：
(1)绿色环保、无污染；
(2)造价低，施工简单；
(3)形成致密的涂膜，有效的阻止水和氧的透入，涂膜平滑；
(4)热力学体系稳定，冻融性好；
(5)机械稳定性好，高速研磨不破乳；
(6)可提高成膜的抗菌性，抗污性和自洁性；
(7)具有超强的耐洗刷性，耐洗刷次数可达100000次以上；
(8)色泽丰满、金属质感强。
经检测，本发明的主要技术指标如下：
细度：um≤40
粘度ku：90±5
PH值：8-9
固含量：37-46％
耐洗刷，次：≥100000
容器中状态：搅拌混合后无硬块，呈均匀状态
施工性：涂刷二遍无障碍
干燥时间h：表干≤2，实干≤24
漆膜颜色处理：符合标准
附着力：1级
耐水性(浸于符合GB/6682三级水中)，168h：不起泡、不开裂、不剥离，允许轻微发白。
耐盐溶性(中性盐雾)，h：500h合格
漆膜柔韧性：mm：1
低温稳定性：不变质
VOC含量小于40g/L(国标小于200g/L)
安全性：有害物质含量(国际要求)：符合要求。
具体实施方式：
  组分   实施例1   实施例2   实施例3   实施例4   实施例5   实施例6
  去离子水   33.17   32.025   32.15   31.40   32.29   33.45
  纳米丙烯酸聚酯乳液   3.85   4.5   5.25   6.00   6.75   7.5
  分散剂3275   0.08   0.15   0.15   0.15   0.15   0.15
  消泡剂A34   0.314   0.30   0.30   0.30   0.33   0.37
  增稠剂EW   0.308   0.3   1.125   1.95   2.1   4.5
  增稠剂R972   0.231   0.225   0.3   0.3   0.38   0.68
  纳米丙烯酸聚酯单体乳液   56.21   56.25   53.25   48.75   46.50   41.25
  润湿剂H875   0.077   0.075   0.075   0.075   0.22   0.075
  分散剂EFKA3580   0.077   0.075   0.30   0.225   0.38   0.15
  分散剂5040   0.20   0.20   0.20   0.20   0.20   0.20
  润湿剂NP-9   0.10   0.40   0.40   0.40   0.20   0.10
  水性稳定型铝颜料   4.00   4.00   5.00   8.00   9.00   10.00
  增稠剂H600   1.383   1.50   1.125   1.125
  增稠剂H400   0.375   1.125   1.50   1.575
  组分  实施例7  实施例8   实施例9   实施例10   实施例11   实施例12
  去离子水   24.871   23.65   24.625   23.60   23.87   26.30
  纳米丙烯酸聚酪乳液   3.85   4.50   5.25   6.00   6.75   7.50
  分散剂3275   0.077   0.15   0.15   0.15   0.15   0.15
  成膜助剂酯醇-12   2.31   2.25   2.25   2.625   2.62   2.70
  消泡剂A34   0.308   0.30   0.30   0.30   0.33   0.375
  PH调节剂AMP-95   0.154   0.15   0.15   0.15   0.155   0.15
  防腐剂M-8   0.154   0.15   0.15   0.15   0.15   0.15
  增稠剂EW   0.154   0.15   0.15   0.15   0.15   0.15
  增稠剂R972   0.231   0.225   0.30   0.30   0.375   0.375
  纳米丙烯酸聚酯单体乳液   56.21   56.25   52.5   48.75   45.00   41.25
  润湿剂H875   0.154   0.15   0.075   0.075   0.225   0.225
  分散剂EFKA3580   0.077   0.075   0.15   0.225   0.30   0.30
  表面功能剂BYK535   3.31   3.25   3.375   3.375   3.875   3.50
  防冻剂丙二醇   2.00   2.50   2.50   3.00   3.00   2.00
  分散剂5040   0.20   0.20   0.20   0.20   0.20   0.20
  润湿剂NP-9   0.40   0.40   0.40   0.40   0.40   0.40
  水性稳定型铝颜料   4.00   4.00   5.00   8.00   9.00   10.00
  增稠剂H600   1.386   1.50   1.125   1.125
  增稠剂H400   1.125   1.125   3.00   3.75
消泡剂A34来源海川化工，表面功能剂BYK-535来源英国BYK公司，水性稳定型铝颜料来源德国爱卡公司。

Claims (5)

1.一种水性纳米铝塑漆，其特征在于：其组分和含量以重量百分比为：
纳米丙稀酸聚酯乳液        3.8-7.5％
纳米丙稀酸聚酯单体乳液    40-57％
水性稳定型铝颜料          4-10％
增稠剂                    1.9-6.8％
分散剂                    0.15-0.75％
润湿剂                    0.15-0.48％
消泡剂                    0.3-0.37％
去离子水                  31-35％。
2.根据权利要求1所述的水性纳米铝塑漆，其特征在于：组分中还包含防冻剂、PH调节剂、成膜助剂醇酯-12、防腐剂、表面功能剂BYK-535，其重量百分比为：
纳米丙稀酸聚酯乳液        3.8-7.5％
纳米丙稀酸聚酯单体乳液    41-56.5％
水性稳定型铝颜料          4-10％
增稠剂                    1.8-4.8％
分散剂                    0.35-0.65％
润湿剂                    0.47-0.65％
消泡剂                    0.3-0.38％
去离子水                  23-27％
防冻剂               2-3％
PH调节剂             0.15-0.16％
成膜助剂醇酯-12      2.25-2.7％
防腐剂               0.15-0.16％
表面功能剂BYK-535    3.25-3.90％。
3.根据权利要求1或2所述的水性纳米铝塑漆，其特征在于：所述的增稠剂为：香港毅捷化工的EW、德国德固萨公司的R972和德国南方化学公司H600或者香港毅捷化工的EW、德国德固萨公司的R972和德国南方化学公司的H400或者香港毅捷化工的EW、德国德固萨公司的R972和德国南方化学公司H600和德国南方化学公司的H400。
4.根据权利要求1或2所述的水性纳米铝塑漆，其特征在于：所述的分散剂为：海川化工3275或海川化工5040或荷兰EFKA公司3580中至少一种。
5.根据权利要求1或2所述的水性纳米铝塑漆，其特征在于：所述的润湿剂为：海川化工H875和/或美国陶氏化学公司NP-9。
CNB2006100165851A 2006-02-15 2006-02-15 水性纳米铝塑漆 Expired - Fee Related CN100369992C (zh)