CN100355117C - Lithium polymer battery and method for manufacturing same - Google Patents
Lithium polymer battery and method for manufacturing same Download PDFInfo
- Publication number
- CN100355117C CN100355117C CNB038222345A CN03822234A CN100355117C CN 100355117 C CN100355117 C CN 100355117C CN B038222345 A CNB038222345 A CN B038222345A CN 03822234 A CN03822234 A CN 03822234A CN 100355117 C CN100355117 C CN 100355117C
- Authority
- CN
- China
- Prior art keywords
- graphite
- carbon element
- powder
- crystalline
- composite graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Conventional lithium polymer batteries obtained by impregnating a graphite negative electrode with a precursor of polymer solid electrolyte and then conducting polymerization, have a problem that radicals generated during the polymerization are consumed by the graphite. Consequently, some monomers remain unreacted, thereby hindering the thus-obtained polymer battery from having an excellent long-term reliability. Conventional polymer batteries using physically crosslinked gel have a problem that a leakage occurs on abnormal occasions since the gel liquefies at high temperatures. A lithium polymer battery of the invention comprises a positive electrode, a negative electrode containing a negative electrode active material that is a carbon material powder, and a chemically crosslinked gel electrolyte. The carbon material powder is a mixture of at least two composite graphite material powders wherein a low-crystalline carbon material adheres to the surface of high-crystalline graphite particles. The composite graphite material powders are different from each other in values of physical properties. Accordingly, a battery having a high energy density and an excellent long-term reliability (excellent cycle characteristics) can be obtained.
Description
Technical field
The present invention relates to lithium polymerization cell and manufacture method thereof.More detailed theory, the present invention relates to use lithium polymerization cell and the manufacture method thereof of complex carbon material powder as the negative pole of active material, wherein, the complex carbon material powder is had the two or more complex carbon material powder that constitute of the graphite material powder of low-crystalline material with carbon element by the surface attachment at the high crystalline powdered graphite.
Background technology
In recent years, replace in negative pole, using lithium metal or its alloy, developed host materials such as the material with carbon element of the occlusion that utilizes lithium ion-emit process or electroconductive polymer.Thus, do not appear at the generation of the skeleton that produces when using lithium metal or its alloy on the principle, the result significantly reduces this problem of the short circuit of inside battery.Particularly known material with carbon element is compared with other material, the occlusion of lithium-emit more separating out-dissolution potential near lithium of current potential.Wherein, graphite material can enter in this lattice lithium to the ratio of six carbon atom with a lithium atom in theory.Therefore, the material of graphite is the material with carbon element that every unit weight and unit volume have high power capacity.And, as graphite material,, have chemical stability, so, can obtain the good battery of cyclical stability by using this material because the current potential of the insertion-disengaging of lithium is smooth.
For example, at J.Electrochm.Soc., Vol.137,2009 (1990), the spy opens flat 4-115457 communique, spy and open flat 4-115458 communique, spy and open that to record graphite in flat 4-237971 communique etc. be the battery that material with carbon element is used as negative electrode active material.Opening flat 4-368778 communique, spy the spy opens flat 5-28996 communique, spy to open the graphite that has recorded surface treatment in flat 5-114421 communique etc. is the battery that material with carbon element is used as negative electrode active material.
Graphite is that material with carbon element passes through to use with the organic electrolyte of ethylene carbonate (EC) as main body, can obtain almost the discharge capacity near theoretical capacity.In addition, its current potential that discharges and recharges and is very smooth only than the dissolving-deposition potential height of lithium a bit.Therefore,, high power capacity and the high secondary cell of cell voltage flatness can be realized, the high capacity of battery can be realized with graphite being material with carbon element when being used as negative electrode active material and making battery.
But graphite is material with carbon element because its crystallinity height, so residual have a problem points that causes the organic electrolyte decomposition.For example, owing to, be extensive use of so be used as the solvent of the electrolyte of secondary lithium batteries as organic electrolyte its current potential window width of propylene carbonate (PC), the solidifying point low (70 ℃) of solvent and the stability height of chemistry.But, J.Electrochm.Soc., Vol.142, following report is arranged: be that material with carbon element is when being used as negative electrode active material with graphite in 1746 (1995), the decomposition reaction of PC produces significantly, and only 10% PC is present in the electrolyte, is that the negative pole that material with carbon element constitutes can not discharge and recharge by graphite.
Proposed following method as its resolution policy, (1) adds the additive of vinylene carbonate etc. in electrolyte, be formation film positive on the material with carbon element at the graphite as negative electrode active material, utilizes the method for the electrolyte decomposition of this film after suppressing; Or (2) use low-crystalline material with carbon element covering high crystalline graphite is the method on the surface of material with carbon element.In one method of back, obtaining having concurrently high crystalline graphite and be the feature of the high power capacity that material with carbon element has and the electrolyte that the low-crystalline material has does not have the optionally composite graphite material of feature.
In recent years, be purpose, have the various researchs of the ionic conductivity polymer of high ion-conductivity with the leakproof that improves the battery that uses liquid electrolyte, high fail safe, long preservation.Proposed now as the ionic conductivity polymer: be the homopolymers of elementary cell or straight chain shape macromolecule, cross-linked network macromolecule or the comb type macromolecule etc. of copolymer with oxirane, constantly near practicability.
Use the battery of described ionic conductivity polymer extensively to be recorded in the patent documentation.For example can enumerate the 4th, 303, No. 748 communiques of United States Patent (USP) that are recorded in ァ one マ Application De (Armand) etc. and the United States Patent (USP) the 4th of ノ one ス (North), 589, the United States Patent (USP) of No. 197 and Off one パ one (Hooper) etc. waits the battery of patent documentation for the 4th, 547, No. 440.
The feature of these batteries for example can be enumerated, and uses the ionic conductivity polymer that contains the solution that is dissolved with electrolytic salt in having the macromolecular material of polyether structure.Because the ionic conduction degree of these ionic conductivity polymer below room temperature be low, so can not realize particularly towards desired small-sized, light weight of the battery of the driving power of mancarried electronic aid or shelf storage power supply and high-energy-densityization.
Therefore, the method that more can improve ionic conductivity than described ionic conductivity polymer has proposed: monomer is mixed with the electrolyte that is made of organic solvent (the particularly organic solvent of high-k such as EC or PC) and electrolytic salt, make the method for monomer polymerization.Utilize this method electrolyte can be remained in the polymer network, the gelatinous polymer electrolyte of the solid state that is maintained (hereinafter referred to as the chemical crosslinking gel).
The chemical crosslinking gel is the confining force height of electrolyte, even the also material of not fusion under high temperature (for example about 100 ℃) in addition is effective from the viewpoint of the leakage that prevents to produce when unusual.But the problem that should solve is also a lot, and is bad as the performance under the low temperature, remains in the battery for make its crosslinked initator that adds in the precursor of ionic conductivity polymer, causes the deterioration of battery performance etc.
On the other hand, show to have proposed in the flat 8-507407 communique, carry out physical crosslinking, make the gel electrolyte that electrolyte keeps (below be called the physical crosslinking gel) by the copolymer that makes hexafluoropropylene-polyvinylidene fluoride the spy.
The gel of the type injects electrolyte after forming cell device, by heating it is temporarily dissolved, and forms gel by cooling.Therefore have following advantage, promptly can by and used the similar method manufacturing of the manufacture method of lithium ion battery of liquid electrolyte etc.
The physical crosslinking gel at room temperature forms gel, can expect to have the effect of leaking of preventing to a certain degree.But when forming high temperature, gelatinous material fusion can not keep the state of gel, so the viewpoint of the leakage when preventing that battery is unusual is not enough.Under the basis of this situation, the high performance lithium polymer battery can fully expect to have the chemical crosslinking gel that prevents the effect of leaking is used in strong request.
Summary of the invention
The objective of the invention is to, a kind of high-performance lithium polymer battery is provided, even the temperature of this battery battery when battery is unusual rises, the leakage of liquid that also can not produce electrolysis, and have than part throttle characteristics, temperature characterisitic, the energy density of last lithium ion battery.
The invention provides a kind of lithium ion polymer battery like this, the electrolyte that it has positive pole, contains the negative pole of the negative electrode active material that comprises the material with carbon element powder and used the chemical crosslinking gel, material with carbon element powder are included in the surface attachment low-crystalline material with carbon element of high crystalline powdered graphite and have the mixture of the two or more at least composite graphite material powders of different mutually physics values.
And, the invention provides a kind of manufacture method of lithium ion polymer battery, it comprises: the operation that makes the precursor of dipping chemical crosslinking gel in the negative pole, described negative pole contains the material with carbon element powder as negative electrode active material, and described material with carbon element powder is at the surface attachment low-crystalline material with carbon element of high crystalline powdered graphite and has the two or more at least composite graphite material powder of mutually different physics values; With make precursor gelization, obtain electrolytical operation.
Description of drawings
Fig. 1 is the profile of one of composite graphite material powder of the present invention example.
Embodiment
The composite graphite material powder is good as negative electrode active material, but because the low-crystalline material with carbon element on surface, hindered the lubrification that high crystalline powdered graphite (below be called powdered graphite) had originally.Therefore, it is bad to occur fillibility sometimes, can not obtain the situation of highdensity negative pole.About this fillibility, the result that inventor of the present invention etc. study in great detail is, fillibility is subjected to the influence of physics value of the composite graphite material powders such as kind of cladding ratio or core significantly.
In addition, from above-mentioned viewpoint consideration, inventor of the present invention etc. find when the precursor with the chemical crosslinking gel hardens, can carry out crosslinked by using the different mutually two or more composite graphite material powder of physics value as negative electrode active material effectively.Carry out crosslinked reason effectively following supposition is arranged.Powdered graphite will be consumed at its active site by the free radical of initator by device generations such as heat or UV, hinders polymerization reaction.By utilizing low-crystalline material with carbon element covering surfaces, the consumption of the free radical that the inhibition powdered graphite causes makes the free radical of generation be used for polymerization reaction effectively.
In the present invention, the so-called two or more at least composite graphite material powder that has different physics values mutually that contains is meant, contains as the composite graphite material powder of main active substances at least and is used to improve two kinds of the composite graphite material powders of its fillibility.By containing the negative pole of so two or more at least composite graphite material powder, can make high capacity density, and the good high performance secondary cell of part throttle characteristics.
The composite graphite material powder is the aggregate of powder, strictly speaking, owing to be difficult to obtain the aggregate of powder fully uniformly, so have the physics value of each particle and as the physics value (mean value) of particle assembly body.In the present invention, so-called two or more being meant, as the latter's aggregate, the composite graphite material powder of mutual different physics values exists two or more.Here, physics value for example can be enumerated crystallinity (interplanar distance, crystallite size etc.), specific area, particle size distribution, cladding ratio, raman scattering intensity ratio, real density, boron bulk density, purity, shape etc.
In the present invention, preferably use cladding ratio different two or more composite graphite material powder mutually.Specifically, the mutual difference of so-called cladding ratio is meant, the mean value of the amount of low-crystalline material with carbon element/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element) (below be called cladding ratio) difference.By making the cladding ratio difference, can make the higher and high performance secondary cell of capacity density.
In addition, so-called cladding ratio is meant, is not the value of each particle, but the value of the aggregate of composite graphite material powder, i.e. mean value.This value by the powdered graphite in the manufacturing process weight and the weight change of the composite graphite material powder that finally obtains calculate.
The scope of the cladding ratio preferred 0.03~0.3 of the composite graphite material powder that cladding ratio is big, more preferably 0.1~0.25.When cladding ratio surpassed 0.3, low crystalline portion was too much, and charge/discharge capacity reduces, so not preferred.In addition, when being lower than 0.03, the control effect of the decomposition of electrolyte is reduced, so not preferred.
The cladding ratio of the composite graphite material powder that cladding ratio is little is preferred below 0.1, and more preferably 0.01~0.10.Further preferred 0.01~0.05.When use is lower than 0.01 material, can not fully suppress the principal element of above-mentioned obstruction polymerization, in addition, when using the material that surpasses 0.1 cladding ratio, be difficult to obtain function admirable, and the high negative pole of packed density, so not preferred.
In addition, the amount of the composite graphite material powder that the amount of the composite graphite material powder that cladding ratio is little is big with respect to cladding ratio is preferred below 50% in weight ratio, and more preferably from about 10~about 30%.When the amount of adding was too much, the character of its material became to take as the leading factor, the effect of the principal element of the obstruction that can not fully be inhibited polymerization, or because material orientation itself, reasons such as the infiltration variation of electrolyte, variation such as part throttle characteristics.If the quantity not sufficient of Tian Jiaing then can not fully obtain the effect that fillibility improves in addition.
In addition, replace the difference of cladding ratio,, also can obtain high capacity density and high performance battery by changing the kind of powdered graphite.Even the different two or more powdered graphite of crystallinity evaluation using by definition such as X-ray diffraction, raman spectroscopy method, real densities when covering the low-crystalline material with carbon element with identical cladding ratio, also can make the fillibility difference by the kind of powdered graphite.This is inferred as because can not utilize the arrangement of the micro organization that evaluating apparatus such as X-ray diffraction judges, the shape of the composite graphite material powder that produces by the shape of core, the differences such as balance of particle diameter, fillibility is created a difference.
The asynchronous cladding ratio of powdered graphite is not particularly limited, but in order to improve fillibility, and the cladding ratio of the composite graphite material powder that cladding ratio is big is preferred 0.03~0.3, the cladding ratio preferred 0.01~0.10 of the composite graphite material powder that cladding ratio is little.More preferably the latter's cladding ratio is 0.01~0.05.
In addition, the amount of the composite graphite material powder that the amount of the composite graphite material powder that cladding ratio is little is big with respect to cladding ratio is preferred below 50% in weight ratio, more preferably from about 10~about 30%, when the amount of adding is too much, the character Be Controlled of its material, the effect of the principal element of the obstruction that can not fully be inhibited polymerization, or because material orientation itself, various reasons such as the infiltration variation of electrolyte, variation such as part throttle characteristics.In addition, when the amount of adding was insufficient, generation can not fully obtain the problem that fillibility improves effect.
In the present invention, use block Delanium, use the powdered graphite of native graphite powder, obtain good result this moment as the little composite graphite material powder of cladding ratio as the big composite graphite material powder of cladding ratio.
In the present invention, as the index of expression fillibility degree, definition is called the parameter of compression ratio, the rerum natura of regulation composite graphite material powder.Here, so-called compression ratio is meant, in as the composite graphite material powder of object, add the PVDF (polyvinylidene fluoride) of 7.5 weight portions (with respect to composite graphite material powder 100 weight portions) as binding agent, and and solvent, the slurry coating that obtains is become the Copper Foil shape, the varied in thickness when pushing with line pressure 300kg/cm.Specifically, use following formula
Compression ratio=the thickness of thickness after the pushing/thickness of thickness before pushing
Define.
In addition, the film density of making when filming that is coated with also is important.That is, before pushing to be coated with film density high more, and compression ratio is more little, can obtain highdensity negative pole more.Even compression ratio is fully little, being coated with under the too small situation of film density before pushing, in order to obtain highdensity negative pole and to push, powdered graphite is easy to generate orientation, also forms the negative pole of part throttle characteristics difference sometimes.In addition, even be coated with fully high material of film density before pushing, when compression ratio is big, because can not obtain the negative pole of high-energy-density, so also not preferred.
In the present invention, preferably mix two or more composite graphite material powders, making the film density that is coated with before pushing is 0.7g/cm
3More than, compression ratio is 0.4~0.7, making the film density that is coated with after pushing is 1.5g/cm
3More than.After pushing to be coated with film density high more, can obtain the negative pole of high power capacity more.But, before pushing, be coated with the highdensity negative pole that the low and compression ratio of film density hour obtains, because the orientation of material etc., so part throttle characteristics variation sometimes is not preferred.In addition, the film density that is coated with after pushing preferably is suppressed to 1.8 g/cm
3About.When being higher than this degree, the space in the negative pole is insufficient, so electrolytical amount is insufficient in the negative pole, can not fully obtain the battery behavior of part throttle characteristics etc. sometimes.
Composite graphite material powder among the present invention can utilize methods such as vapor phase method, liquid phase method, solid phase method, as shown in Figure 1, obtains by adhere to low-crystalline material with carbon element 2 on the surface of high crystalline powdered graphite 1.
Can use one or more of graphitization goods such as the Delanium of native graphite, particle shape (flakey or bulk, fibrous, must crystalline, spherical, broken shape) or carbonaceous mesophase spherules, mesophase pitch powder, isotropic pitch powder as the powdered graphite of core.
At this, as the powdered graphite that constitutes, preferably according to X ray wide-angle diffraction method, (002) the centre plane spacing (d002) of face is 0.335~0.340nm, (002) the crystallite thickness (Lc) of face direction is 10nm above (more preferably more than the 40nm), (110) the crystallite thickness (La) of face direction is 10nm above (more preferably more than the 50nm), in addition, and the 1360cm that utilizes argon laser raman to record
-1Near peak intensity ratio is with respect to 1580cm
-1Near peak intensity is (more preferably below 0.4) below 0.5 than (being designated as R afterwards).The centre plane spacing during greater than 0.340nm or Lc, La during less than 10nm or the R value greater than 0.5 o'clock, the crystallinity of powdered graphite is insufficient.Therefore, when making the composite graphite material powder, (with the current potential of Li is that the capacity of benchmark 0~300mV) is insufficient, so not preferred because the electronegative potential part of separating out near the dissolving of lithium.
Constitute the preferably about 0.1~about 150 μ m of particle size distribution of the powdered graphite of core.There is the particle diameter of the composite graphite material powder of low-crystalline material with carbon element in fact to depend on particle diameter in the powdered graphite surface attachment as the powdered graphite of core.Therefore, according to the particle diameter of core, the particle diameter of end product also roughly is determined.At the particle diameter of core during less than 0.1 μ m, the emptying aperture of the dividing plate by battery causes that the danger of internal short-circuit raises, so not preferred.Greater than 150 μ m the time, in the packed density of the uniformity of negative pole, active material, make the reductions such as operability on the operation of negative pole, so not preferred.
The particle diameter here is the mean value of powder, in utilizing the fixed particle size distribution of laser diffraction formula particle size distribution instrumentation, is particle diameter with the value defined of representing the peak.
Form in the method for low-crystalline material with carbon element on the surface of described powdered graphite, vapor phase method is that gas shape raw material or liquid raw material are transported in the reaction system by methods such as spraying or foamings, and forms the method for carbon from gas phase on the surface of powdered graphite by the thermal decomposition of raw material.Heat decomposition temperature is different different because of raw material, can carry out under about 450~about 1500 ℃ temperature range.
Raw material for example can be enumerated sturated aliphatic hydrocarbons such as methane, ethane, propane; Unsaturated aliphatic hydrocarbons such as propylene; Aromatic hydrocarbons such as benzene,toluene,xylene, naphthalene, perylene.In addition, also can suitably use inert gases such as argon gas, nitrogen as carrier gas.In addition, also can consider to add hydrogen, the method for the coal smoke generation in the inhibition gas phase etc.
Form in the method for low-crystalline material with carbon element on the surface of described powdered graphite, described liquid phase method is to make the raw material of carbon precursor carbonization via liquid phase be attached to the surface of graphite, by its sintering is formed the method for carbon on the surface.Raw material for example can be enumerated naphthalene, phenanthrene, acenaphthylene, anthracene, 9,10-benzophenanthrene, pyrene, 1, aromatic hydrocarbons such as 2-benzophenanthrene, perylene; With above these materials tar that polycondensation obtains under heating and pressurizing or pitch or with the mixture of these aromatic hydrocarbons tar, pitch, pitch, oils of main component etc.The source of these raw materials can be oil system and carbon system.
In addition, before carrying out sintering, also the powdered graphite that the carbon precursor coats can be supplied to matting.By increasing matting, can obtain following effect, can remove the low molecular composition of carbon elimination precursor, can improve carbonation rate from the carbon precursor, simultaneously, can suppress particle and when sintering, occur fusion or aggegation each other.At this, the organic solvent that is used to clean for example can be enumerated: toluene, quinoline, acetone, hexane, benzene, dimethylbenzene, methyl naphthalene, alcohols, carbon system oil, oil are wet goods.Wherein, preferred toluene, quinoline, acetone, benzene, dimethylbenzene, methyl alcohol, carbon are that oil, oil are wet goods in the light oil in the light oil.
Surface at described powdered graphite forms in the method for low-crystalline material with carbon element, and described solid phase method is to make the surface of the raw material of carbon precursor carbonization via solid phase attached to graphite, by with its sintering, forms the method for carbon on the surface.Usually for example can enumerate following method: resin is via the continuous carbonization of solid phase, but in order to make the surface of such resin attached to powdered graphite, form aqueous by the methods such as temperature that resin is heated to more than the fusing point that is dissolved in the solvent, utilization is recorded in the method for described liquid phase method explanation and mixes, and adheres to from the teeth outwards.In addition, also can be by with powdered graphite and mixed with resin, when sintering, remain near the fusing point and mix.
Concrete raw material for example can be enumerated: polyamide-imide resin; Polyamide; Polyacetylene, poly-(right-penylene), poly-(right-the phenylene ethylene support) equiconjugate resin; Phenolic resins; Furfuryl alcohol resin; Cellulose; Polyacrylonitrile; Poly-acrylic resins such as (alpha-halogen acrylonitrile); Halogenated vinyl resins such as polyvinyl chloride, polyvinylidene chloride, chliorinated polyvinyl chloride; Deng.In addition, sintering condition can use sintering method and the sintering atmosphere of putting down in writing in the described liquid phase method.
In addition, the low-crystalline material with carbon element that utilizes described method to obtain, more preferably the centre plane spacing (d002) of (002) face of measuring by X ray wide-angle diffraction method is greater than 340nm, (002) the crystallite thickness (Lc) of face direction is less than 40nm (being more preferably less than 10nm), (110) the crystallite thickness (La) of face direction is less than (more being more preferably less than 10nm) more than the 50nm, in addition, the R value is greater than 0.4 (more preferably greater than 0.5).
With respect to described active material 100 weight portions, mix 1~30 weight portion binding material, form negative pole.This binding material can use fluorine based polymers such as polytetrafluoroethylene, polyvinylidene fluoride, polyolefin polymer such as polyethylene, polypropylene, and synthetic rubber class etc., but be not limited thereto.When binding material during more than 30 weight portions, because increases such as the resistance of negative pole or polarization, discharge capacity reduces, so can not make practical lithium polymer battery.On the contrary, when binding material is less than 1 weight portion, there is not cementitiousness, impracticable.When making negative pole,, also can under the temperature about the fusing point of binding agent, heat-treat for improving caking property.
For obtaining having the negative pole of described compression ratio, preferably use synthetic rubber class in the described binding material as binding material.Have described compression ratio, and have be coated with after pushing film density be the negative pole of the above rerum natura of 1.5g/cc along with discharging and recharging, the expansion of negative pole is shunk and is carried out repeatedly, causes the circulation deterioration sometimes easily.The binding material of rubber system is considered to have strong adhesive property and caoutchouc elasticity, shrinks so can follow the expansion of active material, suppresses the circulation deterioration of negative pole.
So long as have compatibility with electrolytical solvent solution, the compound with polymerisable functional group is just passable, is not particularly limited as the polymerizable monomer of chemical combination cross-linked gel raw material of the present invention.For example, the polymerizable monomer, oligoester acrylate, polyester, poly-imines, polythiaether, polysulfanes etc. that can two or more alone or in combination uses have polyether structure and unsaturated double-bond group form the polymerizable monomer of polymer.In addition, from considering preferably have the material of polyether structure and unsaturated double-bond group with the compatibility aspect of solvent.As the polyether structure unit, oxirane, expoxy propane, epoxy butane, glycidol ether etc. are for example arranged, preferably these are used singly or in combination two or more uses.In addition, when the two or more use of combination, its form can suitably be selected, and can be block, random.Wherein, in the acrylate based material, have the intensity and the flexible gel of following the negative pole change in volume, so preferred owing to use the polymerizable monomer that contains polyfunctional monomer and simple function group monomer to form.
The monomer of acrylic acid series can be fit to use the material that the terminal hydroxyl esterification of PPG is obtained with acrylic acid.Polyfunctional monomer can be with polyalcohols such as ethylene glycol, glycerol, trimethylolpropanes as starting material, with acrylic acid will make thereon oxirane (EO) separately or EO and expoxy propane (PO) addition polymerization and the terminal hydroxyl of the PPG that obtains carry out esterification and obtain together.The simple function group monomer can be a starting material with monohydric alcohols such as methyl alcohol, ethanol, propyl alcohol, with acrylic acid make make thereon oxirane (EO) separately or EO and expoxy propane (PO) addition polymerization and the terminal hydroxyl of the PPG that obtains carry out esterification and obtain together.
At this, more preferably polyfunctional monomer shows important effect on guarantor's fluidity of the electrolyte of gel electrolyte, and mean molecule quantity is 5,000~10,000 scope.When adjusting precursor under the situation of the polyfunctional monomer in adopting described scope, can easily in electrolyte, dissolve, in addition, have good guarantor's fluidity when making gel electrolyte.
On the other hand, can improve the flexibility of gel electrolyte when the mean molecule quantity of simple function group monomer is little, be fit to use about 200~about 3,000 the simple function group monomer of mean molecule quantity.
In addition, being used for electrolyte solution for example can enumerate: the cyclic carbonates of PC, EC, butylene carbonate etc.; Linear carbonate classes such as dimethyl carbonate, diethyl carbonate, ethylene methyl esters, dipropyl carbonate; Lactone such as gamma-butyrolacton, gamma-valerolactone; Furans such as oxolane, 2-methyltetrahydrofuran; Anaesthetie Ether, 1,2-Ethyl Methyl Ether, 1, ethers such as 2-diethoxyethane, ethyoxyl methoxy base ethane, two alkane; Dimethyl sulfoxide (DMSO), sulfolane, methyl sulfolane, acetonitrile, methyl formate, methyl acetate etc. can use above-mentioned substance.
Electrolytic salt for example can be enumerated, lithium perchlorate (LiClO
4), boron lithium fluoride (LiBF
4), phosphorus lithium fluoride (LiPF
6), hexafluoroarsenate lithium (LiAsF
6), hexafluoro-antimonic acid lithium (LiSbF
6), trifluoromethanesulfonic acid lithium (LiCF
3SO
3), trifluoroacetic acid lithium (LiCF
3COO), trifluoromethanesulfonic acid imines lithium (Li (CF
3SO
2)
2) wait lithium salts, above-mentioned in these more than one can be mixed and use.
Electrolyte can dissolve in the solvent of aforementioned selection by making electrolytic salt, prepares electrolyte, and mixes with described polymerizable monomer, and its polymerization is obtained.
As mentioned above, the ratio of polymerizable monomer and electrolyte is considered electrolyte: preferred 70: 30~99: 1 of monomer, more preferably 80: 20~97: 3 from the viewpoint of the retentivity of the performance that obtains being equal to electrolyte and the electrolyte that do not cause leakage.
In addition, with simple function group monomer and polyfunctional monomer mixing use the time, the mixing ratio of monomer is preferably at polyfunctional monomer: the simple function group monomer is that 4: 6~9: 1 scope is mixed.
The cross-linking method of polymer solid electrolyte can use the method for light energies such as ultraviolet ray, electronics line, visible light; The method of heating.If needed, it also is important using polymerization initiator.Particularly carry out in the crosslinked method, preferably add the following polymerization initiator of number % in ultraviolet ray or heating.Polymerization initiator can add: Photoepolymerizationinitiater initiaters such as trimethyl silyl benzophenone, benzoin, 2-methylbenzene accidental cause, 4-methoxy benzophenone, benzoin methyl ether anthraquinone, dibenzoyl dimethyl ketal, and benzoyl peroxide, methyl ethyl ketone peroxide, α, α '-polymerization initiators such as azobis isobutyronitrile.
In addition, preferred ultraviolet wavelength is 250~360nm during polymerizable ultraviolet.Even when using initator,, also can use a small amount of initator to obtain good condensate according to the present invention.The secondary product that remaining polymerization initiator, polymerization initiator produce produces harmful effect to battery behavior sometimes, is preferably limited to necessary Min..The amount of initator preferably with respect to the precursor that contains polymerizable monomer and electrolyte, is controlled at below the 3000ppm usually because of the kind of initator is different.
Positive pole as the secondary cell of lighium polymer of the present invention for example can use the oxide that contains lithium as positive active material.The positive active material concrete example is if any LiCoO
2, LiNiO
2, LiFeO
2, LiMnO
2, LiMn
2O
4Or with the material after the displacement of these transition metal part etc.Hybrid conductive material, binding material and according to circumstances different hybrid solid electrolytes etc. therein form anodal.
This mixing ratio can be that to make electric conducting material with respect to active material 100 weight portions be 5~50 weight portions, and binding material is 1~30 weight portion.This electric conducting material can use carbon black carbon classes such as (acetylene black, thermal black, channel carbon blacks etc.); Or powdered graphite; Metal dust etc., but be not limited thereto.
This binding material can use fluorine based polymers such as polytetrafluoroethylene, polyvinylidene fluoride; Polyolefin such as polyethylene, polypropylene polymer; Synthetic rubber class etc., but be not limited thereto.
When electric conducting material is less than 5 weight portions, or binding material is during more than 30 weight portions, increases such as anodal resistance or polarization, and discharge capacity reduces, so can not make the lithium polymer battery of practicality.When electric conducting material during more than 50 weight portions (according to the kind of the electric conducting material that mixes, weight portion changes), the active material that is contained in anodal reduces, and the discharge capacity of pretending to positive pole reduces.When binding material is less than 1 weight portion, there is not cementitiousness.When more than 30 weight portions, identical with the situation of electric conducting material, be contained in anodal interior active matter quality and reduce, and as mentioned above, because increases such as anodal resistance or polarization, discharge capacity reduces, so impracticable.When making positive pole,, preferably under the temperature about the fusing point of each binding agent, heat-treat for improving caking property.
Embodiment
In order to observe influence, under the state that is mixed with the graphite material powder, carry out the sclerosis test of precursor to the precursor sclerosis of polymer solid electrolyte.
The modulation of precursor
The LiBF of 1mol/L will be dissolved with
4EC and 1: 1 mixed solution of gamma-butyrolacton as electrolyte.To contain the monomer that the simple function group acrylate monomer of the four-functional group propenoic acid ester monomer of mean molecule quantity 7500~9000 of copolymer of oxirane and expoxy propane and mean molecule quantity 200~300 uses with weight ratio at 7: 3 and be blended in the electrolyte, the ratio that makes electrolyte and monomer is 95: 5.The thermal polymerization of full weight amount interpolation 200ppm forms precursor relatively in this solution.The thermal polymerization that uses is a new peroxide tert-butyl caprate.
Powdered graphite and precursor are mixed, and making the ratio of powdered graphite and precursor is 1: 10 with weight ratio, keeps 24 hours in 80 ℃ thermostat, has confirmed the hardening state of precursor.
As powdered graphite, with テ ィ system カ Le society system Delanium (KS25) is core, use is by the composite graphite material powder that is attached with the low-crystalline material with carbon element, material after the mean value of amount/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element) of low-crystalline material with carbon element changed, the test of hardening (embodiment 1).In addition, with the situation that do not coat the low-crystalline material with carbon element as a comparative example 1.Table 1 display result.In the table 1, ◎ represents abundant sclerosis, does not have the situation of aqueous part; Zero expression gel is soft a little, but does not have the residual situation of aqueous part, and * expression is fully sclerosis not, observes the situation of aqueous part.
Table 1
The graphite kind | Cladding ratio | | |
Embodiment | |||
1 | Composite graphite | 0.05 | ○ |
Composite graphite | 0.1 | ◎ | |
Composite graphite | 0.2 | ◎ | |
Composite graphite | 0.28 | ◎ | |
Comparative example 1 | KS25 | - | × |
As known from Table 1, cladding ratio is big more, and hardening state is good more.
Equally, change the amount of initator, test, in any case the result changes, the tendency of hardenability is also identical, and cladding ratio helps sclerosis when increasing.
In addition, when the full dose that makes the relative precursor of initator is increased to the 5000ppm left and right sides, even have only powdered graphite also can get to a certain degree sclerosis situation.Therefore as can be known, composite graphite material powder and initiator concentration have nothing to do and harden, the zone of initator below 5000ppm particularly, and the effect when only core being arranged is bigger.
Anodal manufacturing
Positive active material uses cobalt acid lithium (LiCoO
2).The binding material polyvinylidene fluoride is dissolved in mortar in the solvent N-N-methyl-2-2-pyrrolidone N-temporarily obtains binder solution, the mixture of above-mentioned positive active material and acetylene black is dispersed in the binder solution of formation, make paste.
The paste that obtains like this is coated on the aluminium foil collector body, 60 ℃ it is predrying, after under 150 ℃, heat-treating, push.The negative pole size is set at 3.5 * 3cm, and (coating part 3 * 3cm) is at non-coating part welding aluminium foil (50 μ m).Further in order to remove moisture at 1 80 ℃ of following drying under reduced pressure, the material that the obtains positive pole as test usefulness is used.Being coated with film density is 2.9g/cm
3
The manufacturing of negative pole
In negative electrode active material, use 80 weight portions with テ ィ system カ Le corporate system Delanium (KS25) as core, composite graphite material powder (the particle diameter 12 μ m that the low-crystalline material with carbon element is arranged in surface attachment, d (002)=0.337nm, R value=0.4, the amount of low-crystalline material with carbon element/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element)=0.18) and 20 weight portions with native graphite (マ ダ ガ ス カ Le product) as core, composite graphite material powder (the particle diameter 16 μ m that low-crystalline carbon is arranged in surface attachment, d (002)=0.336nm, R value=0.21, the amount of low-crystalline material with carbon element/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element)=0.05) mixture is as negative electrode active material.It is dispersed in utilizes mortar to be dissolved in the solution that forms in the solvent N-N-methyl-2-2-pyrrolidone N-binding material polyvinylidene fluoride, the material of making pasty state is coated on the Copper Foil of 20 μ m, 60 ℃ it is predrying, after under 240 ℃, heat-treating, push.The negative pole size is set at 3.5 * 3cm, and (coating part 3 * 3cm) is at the lead of non-coating part welding nickel foil (50 μ m).Further, the material that obtains is used as negative pole in order to remove moisture behind 180 ℃ of following drying under reduced pressure.Being coated with film density is 1.58g/cm
3
The precursor modulation
To be dissolved with 1: 1 mixed solvent of the EC of LiBF4 of 1.8mol/L and gamma-butyrolacton as electrolyte.To contain the monomer that the simple function group acrylate monomer of the four-functional group propenoic acid ester monomer of mean molecule quantity 7500~9000 of copolymer of oxirane and expoxy propane and mean molecule quantity 200~300 is used with weight ratio at 7: 3, be blended in the electrolyte, the ratio that makes electrolyte and monomer is 97: 3.The full weight amount is added thermal polymerization 200ppm relatively in this solution, makes precursor.
The manufacturing of battery
The adhesive-bonded fabric that uses polyester makes the electrode that obtains as mentioned above overlapping relatively as spacer, inserts in the bag of the aluminium lamination stampings of processing pouch.Put into above-mentioned precursor therein, under reduced pressure seal mouth.Then, kept 4 hours, carry out thermal polymerization, make polymer battery at 80 ℃.Make the battery repeated charge under the condition of current value 4mA, charging 4.1V-CCCV (current/voltage is constant), discharge 2.75V-CC (current constant) that obtains, measure cycle characteristics.The material that uses, blending ratio etc. are presented at table 2, will be coated with film density (before pushing), compression ratio, be coated with film density (pushing the back), the volume energy density of every negative electrode active material layer, the capability retention of circulation time be presented at table 3.
Comparative example 2
Negative electrode active material uses the composite graphite material powder (amount of particle diameter 12 μ m, d (002)=0.337nm, R value=0.4, low-crystalline material with carbon element/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element)=0.18) that the low-crystalline material with carbon element is arranged as core, in surface attachment with テ ィ system カ Le corporate system Delanium (KS25) separately, in addition, other makes negative pole in the same manner with embodiment 2.The film density that is coated with of the negative pole that obtains is 1.46g/cm
3Use the negative pole that as above obtains, in addition make battery similarly to Example 2, discharge and recharge test.The material that uses, blending ratio etc. are presented at table 2, will be coated with film density (before pushing), compression ratio, be coated with film density (pushing the back), the volume energy density of every negative electrode active material layer, the capability retention of circulation time be presented at table 3.
Comparative example 3
Negative electrode active material use 80 weight portions with テ ィ system カ Le corporate system Delanium (KS25) as core, the mixture of the composite graphite material powder (amount of particle diameter 12 μ m, d (002)=0.337nm, R value=0.4, low-crystalline material with carbon element/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element)=0.18) of low-crystalline material with carbon element and the native graphite of 20 weight portions (マ ダ ガ ス カ Le produces, particle diameter 14 μ m, d (002)=0.3358nm, R value=0.1) is arranged as negative electrode active material in surface attachment.In addition and embodiment 2 make negative pole in the same manner.The film density that is coated with of the negative pole that obtains is 1.65g/cm
3Use the negative pole that as above obtains, in addition similarly make battery, discharge and recharge test with embodiment 2.The material that uses, blending ratio etc. are presented at table 2, will be coated with film density (before pushing), compression ratio, be coated with film density (pushing the back), the volume energy density of every negative electrode active material layer, the capability retention of circulation time be presented at table 3.Embodiment 3~5, comparative example 4~5
As material with carbon element, use the graphite material powder shown in the table 2 as active material, in addition similarly make negative pole and battery with embodiment 2.Result's (be coated with film density (before pushing), compression ratio, be coated with film density (pushing the back), the volume energy density of every negative electrode active material layer, the capability retention of circulation time) is presented at table 3.MCMB described in the table 2 is the abbreviation as the carbonaceous mesophase spherules of the spherical carbon material of pitch system.
Table 2
|
|
|
|||
Core | Cladding ratio | Core | | ||
Embodiment | |||||
2 | KS25 | 0.18 | Native graphite (マ ダ ガ ス カ Le product) | 0.03 | 8∶2 |
Embodiment 3 | KS25 | 0.15 | KS25 | 0.05 | 7∶3 |
Embodiment 4 | KS25 | 0.22 | MCMB | 0.02 | 6∶4 |
Embodiment 5 | Native graphite (マ ダ ガ ス カ Le product) | 0.08 | Native graphite (マ ダ ガ ス カ Le product) | 0.03 | 5∶5 |
Comparative example 2 | KS25 | 0.18 | - | - | 10∶0 |
Comparative example 3 | KS25 | 0.22 | Native graphite (マ ダ ガ ス カ Le product) | Do not coat | 6∶4 |
Comparative example 4 | Native graphite (マ ダ ガ ス カ Le product) | Do not coat | 10∶0 | ||
Comparative example 5 | Native graphite (マ ダ ガ ス カ Le product) | 0.05 | 10∶0 |
Table 3
Be coated with film density (before pushing) (g/cm 3) | Compression ratio | Be coated with film density (pushing the back) (g/cm 3) | Volume energy density (mAh/cm 3) | Capability retention the 1st time/the 100th time (-) | |
|
0.82 | 0.47 | 1.63 | 502 | 0.92 |
Embodiment 3 | 0.80 | 0.51 | 1.55 | 496 | 0.95 |
Embodiment 4 | 0.92 | 0.57 | 1.60 | 480 | 0.96 |
Embodiment 5 | 0.76 | 0.47 | 1.62 | 531 | 0.88 |
Comparative example 2 | 0.78 | 0.55 | 1.41 | 437 | 0.79 |
Comparative example 3 | 0.72 | 0.44 | 1.65 | 495 | 0.59 |
Comparative example 4 | 0.65 | 0.40 | 1.85 | 536 | 0.48 |
Comparative example 5 | 0.67 | 0.38 | 1.72 | 510 | 0.44 |
Shown in above result, embodiment can obtain high capacity density, and the good lithium polymer battery of cycle characteristics.When using the composite graphite material powder separately (comparative example 2 and 5), the capacity density of electrode is low, in addition, when using native graphite as filling additive (comparative example 3), can not obtain enough cycle characteristicss.Infer that this is because when using composite graphite separately, pushing property is low, causes density not improve; In addition, when using native graphite as filling additive, by the result of embodiment 1 as can be known, native graphite hinders the polymerization of precursor, and unreacted monomer remaining in the battery produces harmful effect.
Embodiment 6
Except that using the composite graphite material powder shown in the table 4 and embodiment 2 similarly make positive pole and negative pole.
Anodal modulation with precursor
To be dissolved with 1: 2: 1 the mixed solvent of the EC of LiBF4 of 2.5mol/L and gamma-butyrolacton and PC as electrolyte.To contain the monomer that the simple function group acrylate monomer of the four-functional group propenoic acid ester monomer of mean molecule quantity 7500~9000 of copolymer of oxirane and expoxy propane and mean molecule quantity 200~300 is used with weight ratio at 9: 1, be blended in the electrolyte, the ratio that makes electrolyte and monomer is 97: 3.The full weight amount is added UV initator 2000ppm relatively in this solution, makes precursor.
The negative pole modulation of precursor
To be dissolved with 1: 2: 1 the mixed solvent of the ethylene carbonate (EC) of the LiBF4 of 1mol/L and gamma-butyrolacton and (propylene carbonate) PC as electrolyte.To contain the monomer that the simple function group acrylate monomer of the four-functional group propenoic acid ester monomer of mean molecule quantity 7500~9000 of copolymer of oxirane and expoxy propane and mean molecule quantity 200~300 is used with weight ratio at 8: 2, be blended in the electrolyte, the ratio that makes electrolyte and monomer is 95: 5.The full weight amount is added UV initator 2000ppm relatively in this solution, makes precursor.
The manufacturing of battery
Use the adhesive-bonded fabric of polyester overlapping on positive pole as spacer, flood after the precursor of anodal usefulness, lived by the quartzy plate holder of making, the UV light of irradiation 30mW/cm 30 seconds makes spacer and anodal and dielectric substrate formation one.
The precursor that negative pole dipping negative pole is used shines UV light equally, makes negative pole and dielectric substrate form one.With the attachment of electrodes that obtains, make active material layer relative, insert in the aluminium duplexer of processing pouch, carry out heat seal under the decompression, make lithium polymer battery.With the battery repeated charge under the condition of current value 4mA, charging 4.1V-CCCV, discharge 2.75V-CC that obtains, measure cycle characteristics.The material that uses, blending ratio etc. are presented at table 4, will be coated with film density (before pushing), compression ratio, be coated with film density (pushing the back), the volume energy density of every negative electrode active material layer, the capability retention of circulation time be presented at table 5.
Embodiment 7
The negative pole binding material uses SBR (styrene butadiene ribber): 2 parts and CMC-NH4:2 part, decentralized medium makes water, in addition and embodiment 6 similarly make lithium polymer battery, estimate.Blending ratio is presented in the table 4, will be coated with film density (push before), compression ratio, be coated with film density (pushing the back), the volume energy density of every negative electrode active material layer, the capability retention of circulation time be presented at table 5.
Comparative example 6
Use the composite graphite material powder shown in the table 4, in addition made polymer battery similarly to Example 6.The result is as shown in table 5.
Table 4
|
|
|
|||
Core | Cladding ratio | Core | Cladding ratio | ||
Embodiment 6,7 | KS25 | 0.20 | Native graphite (マ ダ ガ ス カ Le product) | 0.05 | 9∶1 |
Comparative example 6 | Native graphite (マ ダ ガ ス カ Le product) | 0.15 | KS25 | Do not coat | 7∶3 |
Table 5
Be coated with film density (before pressing) (g/cm 3) | Compression ratio | Be coated with film density (pressing the back) (g/cm 3) | Volume energy density (mAh/cm 3) | Capability retention the 1st time/the 100th time (-) | |
Embodiment 6 | 0.85 | 0.51 | 1.66 | 510 | 0.93 |
Embodiment 7 | 0.86 | 0.52 | 1.65 | 515 | 0.95 |
Comparative example 6 | 0.66 | 0.39 | 1.68 | 513 | 0.77 |
From above result as can be known, have only the composite graphite material powder not simultaneously cycle characteristics be very different.This is because in the composite graphite material powder of comparative example, because the free radical that initator produces is consumed by powdered graphite, unreacted monomer remains in a large number in negative pole.And, when the negative pole binding material uses SBR (styrene butadiene ribber), can obtain more excellent characteristic.
According to the present invention,, can obtain the good lithium polymer battery of high-energy-density and long-term reliability (cycle characteristics) by using with mixed negative electrode active material more than composite graphite material powder at least 2 kinds.
And lithium polymer battery provided by the invention is because use the chemical crosslinking gel, so even battery exposes at high temperature, gel can not dissolve yet and form aqueous.Therefore, can obtain the battery of the high reliability that battery is difficult to occur expanding etc.
Lithium polymer battery is characterised in that, can slimming, and the shape freedom by using in the gap that is built in electronic equipment, can be brought into play its characteristic more effectively.In the application that the user can not replace simply, the difficult dilatancy of its long-term reliability, battery is extremely important.The present invention has great importance industrial.
Claims (5)
1, lithium polymer battery, it has positive pole, contains the negative pole of the negative electrode active material that comprises the material with carbon element powder, with the electrolyte that has used the chemical crosslinking gel, the material with carbon element powder is included in the mixture that adheres to the low-crystalline material with carbon element on the surface of high crystalline powdered graphite and have the two or more at least composite graphite material powders of different mutually physics values; Wherein, in the above-mentioned two or more composite graphite material powder, different mutually as the cladding ratio of the represented physics value of the mean value of amount/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element) of low-crystalline material with carbon element.
2, lithium polymer battery as claimed in claim 1, wherein, above-mentioned two or more composite graphite material powder is because the kind difference of high crystalline powdered graphite, and has different physics value mutually.
3, lithium polymer battery as claimed in claim 1, wherein, above-mentioned two or more composite graphite material comprises that cladding ratio is that 0.1~0.25 composite graphite material powder and cladding ratio are two kinds of 0.01~0.05 composite graphite material powder.
4, lithium polymer battery as claimed in claim 1, wherein, the chemical crosslinking gel comprises polyfunctional monomer and simple function group polymer of monomers in the acrylic ester material.
5, the manufacture method of lithium ion polymer battery, it comprises: the operation that makes the precursor of dipping chemical crosslinking gel in the negative pole, described negative pole contains the material with carbon element powder as negative electrode active material, and described material with carbon element powder is at the surface attachment low-crystalline material with carbon element of high crystalline powdered graphite and has the two or more at least composite graphite material powder of mutually different physics values; With make precursor gelization, obtain electrolytical operation; Wherein, in the above-mentioned two or more composite graphite material powder, different mutually as the cladding ratio of the represented physics value of the mean value of amount/(amount of the amount of high crystalline powdered graphite+low-crystalline material with carbon element) of low-crystalline material with carbon element.