CN100351416C - 花岗石锯条用钢 - Google Patents
花岗石锯条用钢 Download PDFInfo
- Publication number
- CN100351416C CN100351416C CNB021516251A CN02151625A CN100351416C CN 100351416 C CN100351416 C CN 100351416C CN B021516251 A CNB021516251 A CN B021516251A CN 02151625 A CN02151625 A CN 02151625A CN 100351416 C CN100351416 C CN 100351416C
- Authority
- CN
- China
- Prior art keywords
- saw blade
- granite
- steel
- present
- tensile strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开的是一种花岗石锯条用钢，主要成份为铁(Fe)，其它原料组分和含量采用如下配方比例(重量份)：碳(C)：0.50-0.80%，硅(Si)：0.13-0.65%，锰(Mn)：0.75-1.50%，铬(Cr)：≤0.25%，钒(V)：≤0.20%，稀土(RE)：≤0.15%，硫(S)：≤0.035%，磷(P)：≤0.035%，采用本发明配方用各种冶炼方式获得的钢坯制成的花岗石锯条硬度为26-37HRC，抗拉强度бb为950-1150Mpa，延伸率δ5为6-8%，金相组织含有珠光体及少量铁素体，因此具有抗拉强度高，韧性好，由于碳和锰的含量适中易成型，锯条板型平整，切割消耗低。采用该配方制成的锯条，相对国外的进口的锯条，成本低。
Description
技术领域
本发明属于一种石材加工设备，特别涉及一种用于切割花岗石的锯条用钢。
背景技术
随着我国国民经济建设的快速发展，人们生活水平的大幅度提高，人们对小康生活追求的多样化，带来了对居室及办公等场所环境美化的强烈要求，花岗岩因其所具有天然石材的独特风格而取得人们的青睐，无论是家庭居室、办公、娱乐、休息等场所，还是商店超市对花岗岩的使用都是有增无减，由于花岗岩用于装修时均为片材，因此需要加工设备进行切割，锯条在此就起着重要的作用。
传统用于切割花岗岩的锯条主要为砂锯，它被张紧在锯机的框架上，使用时，将其置于花岗岩荒石上，并作强力往复运动，将用坚硬的钢砂调制成的砂浆引带入切割面，磨出锯缝以完成切割。砂锯在切割花岗石的同时，自己也被磨损消耗，所以锯条的性能，在生产过程中，起着举足轻重的作用。根据使用的要求，它必须具有高强度、高耐磨性和足够的韧性，为了获得要求的机械性能，它应有相应的化学成份，经热处理取得要求的金相组织。
切割花岗岩的锯条作为一种易耗品，需求量大，由于它是用专门冶炼的钢种铸成坯料来制作的，且大多为进口，致使成本较高，导致花岗岩的加工成本高，影响了它的普遍利用；而为了降低成本自行研制切割花岗岩的锯条，首先需要解决材料的冶炼和轧坯问题，但由于种种原因，国内没有专用材料，若刻意去研制，必将花费较多的时间、人力和财力，同样导致成本升高，使做出的产品缺少竟争力。
发明内容
本发明的目的旨在克服现有技术的不足，提供一种抗拉强度高、韧性好、锯条板型平整、切割消耗低、同时成本降低的花岗石锯条用钢。
本发明的目的是这样实现的：发明人在设计制作花岗石锯条中，经过四年多的研究、对比、筛选，对花岗石锯条用钢化学成份的材质配方进行反复实验和研究，确定出用各种冶炼方式，获得的钢坯制成的花岗石锯条，具有抗拉强度高、韧性好、锯条板型平整、切割消耗低的花岗石锯条用钢的材质配方。
本发明花岗石锯条用钢，主要成份为铁(Fe)，其它原料组分和含量采用如下配方比例：
碳(C)：0.50-0.80％， 硅(Si)：0.13-0.65％，
锰(Mn)：0.75-1.50％， 铬(Cr)：≤0.25％，
硫(S)：≤0.035％， 磷(P)：≤0.035％。
所述的其它原料组份还包括钒(V)，其含量小于或等于0.20％(重量份)。
所述的其它原料组份还包括稀土(RE)，其含量小于或等于0.15％(重量份)。
按以上配方用各种冶炼方式获得的钢坯制成的花岗石锯条，它的硬度为26-37HRC，抗拉强度бb为950-1150Mpa，延伸率δ5为6-8％，金相组织含有珠光体及少量铁素体。
将本发明与非花岗石锯条钢性能对比其结果如附表1。由此表可得知，采用本发明配方用各种冶炼方式获得的钢坯制成的花岗石锯条具有抗拉强度高，韧性好，由于碳和锰的含量适中易成型，锯条板型平整，切割消耗低。采用该配方制成的锯条，相对国外的进口锯条，成本低。
具体实施方式
本发明花岗石锯条用钢，主要成份为铁(Fe)，其它原料组分和含量采用如下配方比例(重量份)：
碳(C)：0.50-0.80％， 硅(Si)：0.13-0.65％，
锰(Mn)：0.75-1.50％， 铬(Cr)：≤0.25％，
钒(V)：≤0.20％， 稀土(RE)：≤0.15％，
硫(S)：≤0.035％， 磷(P)：≤0.035％。
采用上述配方用各种冶炼方式获得的钢坯制成的花岗石锯条，其硬度为26-37HRC，抗拉强度бb为950-1150Mpa，延伸率δ5为6-8％，金相组织含有珠光体及少量铁素体。
将花岗石锯条用钢与非花岗石锯条钢性能对比：
一、C＞0.80％，其它元素含量超标，其硬度为≥37HRC，抗拉强度бb≥1150Mpa，延伸率δ5≤6％，金相组织为珠光体+渗碳体，采用此配方制成的锯条具有硬度过高、脆性大、易断裂等特点。
二、C＜0.80％，其它元素含量过低，其硬度为≤25HRC，抗拉强度бb≤1000Mpa，延伸率δ5≥7.5％，金相组织为珠光体+大量铁素体，采用此配方制成的锯条具有硬度过低、易变形、不耐磨等特点
由此可见，采用本发明花岗石锯条用钢的材质配方制成的锯条，具有硬度适中，韧性好易成型，锯条板型平整、抗拉强度高、耐磨，切割消耗低等特点。
| 化学成份(％) | 硬度(HRC) | 抗拉强度бb(Mpa) | 延伸率δ5(％) | 金相组织 | 特点 |
| C 0.50-0.80其它元素如表 | 26-37 | 950～1150 | 6-8 | 珠光体+少量铁素体 | 硬度适中，韧性好，耐磨 |
| C＞0.80或其它元素含量超标 | ≥37 | ≥1150 | ≤6.0 | 珠光体+渗碳体 | 硬度过高，脆性大，易断裂 |
| C＜0.50或其它元素含量过低 | ≤25 | ≤1000 | ≥7.5 | 珠光体+大量铁素体 | 硬度过低，易变形，不耐磨 |
表1
Claims (1)
1、一种花岗石锯条用钢，主要成份为铁，其特征在于其它原料组分和含量如下(重量份)：
碳(C)：0.5-0.8％，硅(Si)：0.13-0.65％，
锰(Mn)：0.75-1.5％，铬(Cr)：＜0.25％，
硫(S)：＜0.035％，磷(P)：＜0.035％，
钒(V)：0＜V≤0.20％，稀土(RE)：0＜RE≤0.15％。