CN100343346C - 一种含纤维涂料组合物及其制备方法和应用 - Google Patents
一种含纤维涂料组合物及其制备方法和应用 Download PDFInfo
- Publication number
- CN100343346C CN100343346C CNB2003101039000A CN200310103900A CN100343346C CN 100343346 C CN100343346 C CN 100343346C CN B2003101039000 A CNB2003101039000 A CN B2003101039000A CN 200310103900 A CN200310103900 A CN 200310103900A CN 100343346 C CN100343346 C CN 100343346C
- Authority
- CN
- China
- Prior art keywords
- fiber
- fibre
- powder
- coating composition
- agents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种建筑壁面装饰使用的含纤维涂料组合物，该组合物包括天然纤维和/或人工纤维、软化剂、防霉剂、阳离子剂、粘合剂；适量涂料粉、灭菌剂、防水剂、阻燃剂、金丝、银丝、彩色粉、彩色荧光粉、彩色荧光丝材料。制备方法可为：将纤维用染色剂进行染色处理；将纤维进行软化处理；在纤维中加入防霉剂进行防霉处理；加入阳离子剂，干燥定型，在上述定型纤维中加入余料后，再加入粘合剂，干燥定型。本发明具有色彩变化丰富、易涂覆、可反复使用、易修复、保暖、环保的优点。
Description
技术领域
本发明涉及一种含纤维涂料组合物及其制备方法和应用，尤其涉及建筑壁面装饰使用的，可使壁面具有随意图案的含纤维涂料组合物及其制备方法和应用。
背景技术
目前，建筑壁面装饰，一种方法是采用涂料使墙面平整、防水、防霉、或加入颜料使之有色彩，另一种方法是采用贴墙纸或以有图案的纺织布料装饰壁面。但前者的装饰效果差，难以达到人们随意美化壁面的作用，而后者易污染、破裂后无法修复，无法达到象涂料那样可自由涂覆和修复的效果。
发明内容
本发明的目的是提供一种含纤维涂料组合物及其制备方法和应用，尤其提供建筑壁面装饰使用，可使壁面具有随意图案的含纤维涂料组合物及其制备方法和应用，克服了上述建筑壁面装饰的缺点，是一种新型的兼有涂料功能和美化作用的含纤维涂料组合物。
本发明的目的是通过以下技术方案来实现的：
一种含纤维涂料组合物，包括以下组分：天然纤维和/或人工纤维、软化剂、防霉剂、阳离子剂、粘合剂；
所述组合物可为以下重量份组分：天然纤维和/或人工纤维40-98、软化剂0.1-0.3、防霉剂0.05-0.15、阳离子剂0.05-0.15、粘合剂5-15；
优选为以下重量份组分：天然纤维和/或人工纤维68-90、软化剂0.05-0.25、防霉剂0.08-0.12、阳离子剂0.08-0.12、粘合剂8-12；
最好为以下重量份组分：天然纤维和/或人工纤维88、软化剂0.2、防霉剂0.1、阳离子剂0.1、粘合剂10；
该天然纤维和/或人工纤维可为自然颜色或通过已知染色剂染上的颜色，以及通过已知荧光染色剂染色后在光线下可呈现多种色彩变化的颜色；染色剂的色彩可为多种，如乳白色、浅棕色、棕色、红色、黑色、蓝色、绿色等或同时呈现的多种色彩。
所述天然纤维可选自植物纤维、动物纤维或其组合物，植物纤维为其籽、茎、皮、叶、杆等获得的天然纤维，如棉籽、棉纤维、木纤维、草纤维、禾杆、竹、芦苇、榨糖后的蔗渣、木浆、草浆、纸浆、纸片、麻纤维、椰壳、棕、蕉麻等；动物纤维为动物的毛或分泌物构成的天然纤维，如蚕丝、羊毛、羽绒、兔毛、骆驼毛、牦牛毛、马海毛、开士米等。
所述人工纤维可选自目前已知的人工原料制成的纤维或其组合物，包括纺织用的人造纤维、合成纤维，如粘胶纤维，醋酸纤维，海藻纤维，涤纶、丙纶、晴纶、尼龙等以煤、石油、天然气或农副产品等为原料经化学方应制成的高分子化合物，这些原料还可以作为增韧剂。
所述纤维的染色可采用已知的纤维染色剂，如380-780纳米波长电磁波的具有视觉效果的彩色颜料；有机染料，包括偶氮染料、酞氰染料、杂环染料、还原染料、色淀染料以及常用的毛发染料，如耐晒黄G、酞氰蓝、喹丫啶、蒽醌、偶氮色淀等。
所述软化剂可为已知的化工涂料用软化剂，尤其为十六烷基三(三羟香戊四醇基氧化铵)三(三羟香戊四醇基)氧化铵，目的是软化纤维原料，本发明十六烷基三(三羟香戊四醇基氧化铵)三(三羟香戊四醇基)氧化铵还具有灭菌的作用。
所述防霉剂可为已知的防霉剂，如卤化胺，尤其如溴化胺、氯化胺等。
所述阳离子剂可为已知的带阳离子的盐或其衍生物，如阳离子硅油，目的是使墙面与空气中的阳离子隔离，具有防静电的作用，从而使空气中的尘埃不易吸附在墙上，到达耐脏的目的，同时还可以使表面憎水，还可作为柔软剂。
所述粘合剂可为已知的涂料用粘合剂，最好为透明的粘合剂，如聚乙烯醇，目的是使纤维素及其它组分混合干燥后定型。
所述组合物还可进一步包括：适量涂料粉、灭菌剂、防水剂、阻燃剂、金丝、银丝、彩色粉、彩色荧光粉、彩色荧光丝等随光线呈现不同色彩等视觉效果的材料或其组合，尤其为以下重量份组分：涂料粉10-80、灭菌剂0.05-0.15、防水剂0.05-0.15、阻燃剂0.05-0.15；优选为以下重量份组分：涂料粉45、灭菌剂0.10、防水剂0.10、阻燃剂0.10、适量金丝、银丝、彩色粉、彩色荧光粉、彩色荧光丝。
所述涂料粉可为已知的不同粒度大小的涂料粉，如双飞粉、矿物粉、岩石粉；所述双飞粉为矿石如方解石、白云石、大理石、石灰土、粘土、高铝质土等煅烧而成的含硅酸钙、铝酸钙的组合物，可从市场购得；所述矿物粉、岩石粉包括天然矿物粉，人工矿物粉，如金、银、铜、丹砂、朱砂、玉石、云母、水晶、石英、长石、花岗岩石、石英砂岩等，目的是使成型后的涂料呈现质感，加入不同的重量份的涂料粉可呈现不同的质感。
所述灭菌剂可为已知的灭菌剂，如氧化钛、苯甲酸及其钠盐，三溴水杨酸基苯胺，其中氧化钛与十六烷基三(三羟香戊四醇基氧化铵)配合使用具有协同加强灭菌的作用；
所述防水剂可为已知的涂料用防水剂，如棕榈蜡与丙烯酸酯共聚乳液的水乳型复合物，加入防水剂的涂料具有不可逆性，与不加入防水剂的涂料相比，在墙上涂层后较难重复使用。
所述阻燃剂，可为已知的涂料用阻燃剂，如含卤素化合物，如常与三氧化二锑并用的十溴联苯醚、磷酸酯、过磷酸胺等。
本发明所用原料均可从市场直接获得。
本发明还提供了所述含纤维涂料组合物的制备方法，包括以下步骤：
将纤维软化处理；
将纤维加入防霉剂进行防霉处理；
在上述处理的纤维中加入阳离子剂；
将上述加入阳离子剂的纤维低温干燥定型，所述低温可为50-100℃，尤其为70-90℃，目的是使纤维呈分散状或集聚状，如束状、颗粒状、丝束状、球状、絮状及不规则状；
在上述定型纤维中加入粘合剂，低温干燥定型，所述低温可为50-100℃，尤其为70-90℃。
所述制备方法还包括：
将纤维用染色剂进行染色处理；
或还包括加入涂料粉、灭菌剂、防水剂、阻燃剂、适量金丝、银丝、彩色粉、彩色荧光粉、彩色荧光丝、或其组合物后再加入粘合剂，低温干燥定型，所述低温可为50-100℃，尤其为70-90℃。
本发明还提供了所述含纤维涂料组合物在建筑壁面装饰方面的应用，使用时，所述含纤维涂料组合物加入3-7倍体积或重量的水，尤其5倍体积或重量的水，混合均匀，按常规涂料涂覆法涂覆于墙面上，等自然干燥后即自然帖服于墙面。由于不同的涂覆方法，纤维涂料在墙面上将表现出不同的质感，因此，本发明优选为刷涂或滚涂。
本发明具有以下优点：
1、本发明含纤维涂料组合物定型于墙面上后，可反复使用，用适量水浸后，即可从墙面揭下。
2、本发明组合物原料符合环保要求。
3、本发明组合物具有防裂和透气的作用。
4、由于加入防静电的原料，防止尘埃粘合墙面。
5、本发明组合物涂于墙面后，美观，具有立体感和浮雕感，可根据需要，采用不同的材料结合配制的涂料，涂覆与墙面，极富美感。
6、施工方便，涂料加水即可涂覆于墙面。
7、可直接在墙面上修复，由于纤维涂料组合物在涂覆墙面时，纤维涂料不规则地运动，由于其不规则性，以及可加水容易揭离墙面的特性，故可直接在墙面上修复。
8、采用纤维原料，还具有保暖的效果，由于表面形成的突起具有吸音、隔音的效果。加入阻燃剂具有阻燃、防高温的效果。
9、本发明纤维涂料组合物在涂覆墙面后，呈现具有不规则质感、色彩的纤维涂层，花案形状变化丰富。
具体实施方式
实施例1
一种含亚麻纤维的涂料组合物
称取以下组分(Kg)：亚麻纤维88、十六烷基三(三羟香戊四醇基氧化铵)0.2、溴化胺0.1、阳离子硅油0.1、聚乙烯醇10。
制备方法，将亚麻纤维用浓度为1％的耐晒黄G进行染色处理，用十六烷基三(三羟香戊四醇基氧化铵)软化处理，加入溴化胺进行防霉处理，再加入阳离子硅油干燥定型，温度为90℃，使纤维呈集束状、丝束状、球状、絮状及不规则状。在定型纤维中加入聚乙烯醇，70℃干燥定型，即得。
实施例2
含羊毛纤维的涂料组合物
称取以下组分(Kg)：羊毛纤维68、十六烷基三(三羟香戊四醇基氧化铵)0.05、氯化胺0.08、阳离子硅油0.08、聚乙烯醇8、双飞粉30、水晶粉15、氧化钛0.1、十溴联苯醚0.10。
制备方法，将羊毛纤维用十六烷基三(三羟香戊四醇基氧化铵)软化处理，加入氯化胺、氧化钛进行防霉、灭菌处理，再加入阳离子硅油、双飞粉、水晶粉干燥定型，温度为50℃，使纤维呈丝束状、絮状及不规则状。在定型纤维中加入聚乙烯醇、十溴联苯醚，90℃干燥定型，即得。
实施例3
含椰壳纤维、马海毛纤维的涂料组合物
称取以下组分(Kg)：椰壳纤维44、马海毛纤维24、十六烷基三(三羟香戊四醇基氧化铵)0.05、氯化胺0.08、阳离子硅油0.08、聚乙烯醇8、双飞粉10、氧化钛0.15、十溴联苯醚0.15。
制备方法同实施例2。
实施例4
含棕纤维的涂料组合物
称取以下组分(Kg)：棕纤维66、十六烷基三(三羟香戊四醇基氧化铵)0.05、氯化胺0.08、阳离子硅油0.08、聚乙烯醇8、丹砂10、氧化钛0.05、十溴联苯醚0.05。
制备方法同实施例2。
实施例5
含聚丙烯纤维的涂料组合物
称取以下组分(Kg)：聚丙烯纤维90、十六烷基三(三羟香戊四醇基氧化铵)0.25、溴化胺0.12、阳离子硅油0.12、聚乙烯醇12、丹砂30、玉石粉10、氧化钛0.12。
制备方法，将聚丙烯纤维用浓度为0.2％三芳甲烷色淀青莲染色，再用十六烷基三(三羟香戊四醇基氧化铵)软化处理，加入溴化胺、氧化钛进行防霉处理，再加入阳离子硅油、丹砂、玉石粉干燥定型，温度为90℃，使纤维呈颗粒状及不规则状。在定型纤维中加入聚乙烯醇，50℃干燥定型，即得。
实施例6
含聚酰胺纤维、聚氯乙烯纤维、棉纤维的彩色涂料组合物
称取以下组分(Kg)：聚酰胺纤维、聚氯乙烯纤维、棉纤维98(比例为1∶1∶1)，十六烷基三(三羟香戊四醇基氧化铵)0.3、溴化胺0.15、阳离子硅油0.15、聚乙烯醇15。
制备方法，将聚酰胺纤维、聚氯乙烯纤维、棉纤维混合物用浓度为0.05％蒽醌红染色，再用十六烷基三(三羟香戊四醇基氧化铵)软化处理，加入溴化胺、氧化钛进行防霉处理，再加入阳离子硅油、丹砂、玉石粉干燥定型，温度为70℃，使纤维呈颗粒状及不规则状。在定型纤维中加入聚乙烯醇，60℃干燥定型，即得。
实施例7
含聚丙烯腈纤维、羽绒的彩色涂料组合物
称取以下组分(Kg)：聚丙烯腈纤维、羽绒40(比例为5∶1)，十六烷基三(三羟香戊四醇基氧化铵)0.3、溴化胺0.05、阳离子硅油0.05、金丝1、银丝1、彩色丝1、聚乙烯醇5、棕榈蜡与丙烯酸酯共聚乳液的水乳型复合物1。
制备方法，将聚丙烯腈纤维、羽绒混合物用浓度为浓度0.1％二噁嗪永固紫RL染色，再用十六烷基三(三羟香戊四醇基氧化铵)软化处理，加入溴化胺、氧化钛进行防霉处理，再加入阳离子硅油干燥定型，温度为70℃，使纤维呈颗粒状及不规则状。在定型纤维中加入金丝、银丝、彩色丝、聚乙烯醇、棕榈蜡与丙烯酸酯共聚乳液的水乳型复合物，60℃干燥定型，即得。
实施例8
实施例1-7含纤维涂料组合物在建筑壁面装饰方面的应用，所述含纤维涂料组合物分别加入5倍体积的水，混合均匀，按常规涂料涂覆法涂覆于墙面上，等自然干燥后即自然帖服于墙面。由于不同的涂覆方法，纤维涂料在墙面上将表现出不同的质感，因此，本发明为刷涂，表现为表层较平整。
实施例9
实施例1-7含纤维涂料组合物在建筑壁面装饰方面的应用，所述含纤维涂料组合物分别加入3倍体积的水，混合均匀，按常规涂料涂覆法涂覆于墙面上，等自然干燥后即自然帖服于墙面。由于不同的涂覆方法，纤维涂料在墙面上将表现出不同的质感，因此，本发明为滚涂，表现为表层具有突兀与凹陷交错的图案。
实施例10
实施例1-7含纤维涂料组合物在建筑壁面装饰方面的应用，所述含纤维涂料组合物分别加入7倍体积的水，混合均匀，按常规涂料涂覆法涂覆于墙面上，等自然干燥后即自然帖服于墙面。由于不同的涂覆方法，纤维涂料在墙面上将表现出不同的质感，因此，本发明为滚涂，表现为表层具有浮雕般图案。
Claims (7)
1、一种含纤维涂料组合物，包括以下重量份的各组分：天然纤维和/或人工纤维40-98、软化剂0.1-0.3、防霉剂0.05-0.15、阳离子剂0.05-0.15和粘合剂5-15；所述天然纤维选自植物纤维、动物纤维或其组合物；所述植物纤维为植物籽、茎、皮、叶、杆的纤维；所述动物纤维为动物的毛或分泌物构成的天然纤维；所述人工纤维选自人造纤维、合成纤维；所述天然纤维和/或人工纤维为自然颜色或通过已知染色剂染色的纤维；所述人工纤维为粘胶纤维、醋酸纤维、海藻纤维、涤纶、丙纶、晴纶或尼龙；所述软化剂为十六烷基三(三羟香戊四醇基氧化铵)三(三羟香戊四醇基)氧化铵；所述防霉剂为卤化胺；所述阳离子剂为阳离子硅油；所述粘合剂为聚乙烯醇。
2、一种含纤维涂料组合物，包括以下重量份的各组分：天然纤维和/或人工纤维68-90、软化剂0.05-0.25、防霉剂0.08-0.12、阳离子剂0.08-0.12、粘合剂8-12；所述天然纤维选自植物纤维、动物纤维或其组合物；所述植物纤维为植物籽、茎、皮、叶、杆的纤维；所述动物纤维为动物的毛或分泌物构成的天然纤维；所述人工纤维选自人造纤维、合成纤维；所述天然纤维和/或人工纤维为自然颜色或通过已知染色剂染色的纤维；所述人工纤维为粘胶纤维、醋酸纤维、海藻纤维、涤纶、丙纶、晴纶或尼龙；所述软化剂为十六烷基三(三羟香戊四醇基氧化铵)三(三羟香戊四醇基)氧化铵；所述防霉剂为卤化胺；所述阳离子剂为阳离子硅油；所述粘合剂为聚乙烯醇。
3、根据权利要求1的含纤维涂料组合物，各组分的重量份是：天然纤维和/或人工纤维88、软化剂0.2、防霉剂0.1、阳离子剂0.1、粘合剂10。
4、根据权利要求1或2的含纤维涂料组合物，所述组合物进一步包括以下组分：适量涂料粉、灭菌剂、防水剂、阻燃剂、金丝、银丝、彩色粉、彩色荧光粉、彩色荧光丝材料或其组合物。
5、根据权利要求4的含纤维涂料组合物，其特征是所述涂料粉为双飞粉、矿物粉或岩石粉；所述灭菌剂为氧化钛、苯甲酸及其钠盐；所述防水剂为棕榈蜡与丙烯酸酯共聚乳液的水乳型复合物；所述阻燃剂为含卤素化合物。
6、一种制备权利要求1-5的任意一项含纤维涂料组合物的方法，包括以下步骤：
将纤维软化处理；
将纤维加入防霉剂进行防霉处理；
在上述处理的纤维中加入阳离子剂；
将上述加入阳离子剂的纤维干燥定型；
在上述定型纤维中加入粘合剂，干燥定型；
或进一步包括将纤维用染色剂进行染色处理；
或还进一步包括加入涂料粉、灭菌剂、防水剂、阻燃剂、适量金丝、银丝、彩色粉、彩色荧光粉、或彩色荧光丝及其组合物后，再加入粘合剂，干燥定型。
7、权利要求1-5的任意一项含纤维涂料组合物在建筑壁面装饰方面的应用，包括：向所述含纤维涂料组合物中加入3-7倍体积或重量的水，混合均匀，刷涂或滚涂于墙面上。