CN100343199C - Fabrication method for hand painting pattern, filling ceramic glaze on bottom base of ceramic by using latex - Google Patents
Fabrication method for hand painting pattern, filling ceramic glaze on bottom base of ceramic by using latex Download PDFInfo
- Publication number
- CN100343199C CN100343199C CNB2006100318382A CN200610031838A CN100343199C CN 100343199 C CN100343199 C CN 100343199C CN B2006100318382 A CNB2006100318382 A CN B2006100318382A CN 200610031838 A CN200610031838 A CN 200610031838A CN 100343199 C CN100343199 C CN 100343199C
- Authority
- CN
- China
- Prior art keywords
- glaze
- ceramic
- sagging
- reaction
- latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a making method for manually drawing patterns and filling glazes on the blank bottom of a ceramic product by using latex. The present invention is characterized in that the method comprises the following steps: manually drawing latex patterns on the blank bottom; filling a sagging glaze or a reaction glaze; forming a pattern decoration effect naturally fused on the glaze layer during the firing process by using the property of strong fluidity of the reaction glaze and the sagging glaze. The method of the present invention is an expression method with boldness, peculiarity, innovation and easy manufacture, and can make the patterns and glaze layers on the surface of the ceramic product more concordantly reveal the visual effects of variety and particularity in nature. The present invention is the making method for reveal glaze layer pattern decoration effects naturally fused on the surface of the ceramic products and belongs to the method for increasing the texture and the aesthetic sense of the products by coloring and decorating the surfaces of ceramic ware for daily use.
Description
Technical field
The present invention relates to a kind of making method of utilizing latex hand painting pattern, filling glaze at the bottom of the ceramic base; It belongs to the decoration making method of ceramic ware for daily use.
Background technology
Present ceramic industry is in the ceramic surface colour.Carrying out pattern decorative is a kind of modal method that increases product texture and aesthetic feeling, most of impressing patterns are to adopt the oil that blocks water to transfer powdered frit to scrape pattern under glaze, the effect that scrapes pattern under glaze is generally comparatively inflexible, if it is excessive to scrape area, then be difficult to drawout, and easily produce defectives such as excess glaze, look dirty, dislocation, influence the artistic effect of product.The lip-deep decorative pattern of ceramic is generally on the glaze Freehandhand-drawing or printing forms, and can not merge pattern glaze layer naturally.
Summary of the invention
The objective of the invention is to overcome above-mentioned weak point, a kind of making method of utilizing latex hand painting pattern, filling glaze at the bottom of the ceramic base is provided.
Technical scheme of the present invention: be to be stained with one deck reaction glaze or sagging at the bottom of the ceramic base behind the Freehandhand-drawing latex pattern, tear off behind the latex glaze dust blown off and fill out glaze, if what ground-coat enamel was stained with is one deck reaction glaze, then fill out sagging, be sagging then fill out the reaction glaze (annotate: sagging is reacted between the glaze with one deck will certain aberration if ground-coat enamel is stained with, mutually intersect and use), send in 1130 ℃～1180 ℃ the raceway kiln and fire the glaze effect that forms a kind of natural harmony after 4～5 hours.Concrete steps are as follows:
A, on the ceramic dry body Freehandhand-drawing latex pattern, then be stained with one deck reaction glaze or the stream axle is ground-coat enamel, it is 0.3～0.6mm that the glaze layer adheres to thickness;
B, on the ceramic that is speckling with reaction glaze or stream axle, tear the latex pattern on the dry body off, fill out sagging or reaction axle after blowing off dust, its sagging is the strong glaze of a kind of translucent flowability, should notice that in filling out the glaze process glaze colours of filling out will ride on the ground-coat enamel, fill out that should to add ratio in the glaze be 100: 1 glycerine, the thickness that adheres to of sagging or reaction glaze is 0.3～0.6mm; In making method, the ground-coat enamel in the above A step is to be the reaction glaze, and filling out glaze is to be sagging, and ground-coat enamel is a sagging conversely, fills out glaze so and is the reaction glaze;
C, send in 1130 ℃～1180 ℃ the raceway kiln and fire the glaze pattern decorative effect that can form a kind of natural fusion in 4～5 hours at last.
Gordian technique of the present invention is a Freehandhand-drawing latex at the bottom of the ceramic base, utilize the mobile strong characteristic of reaction glaze and sagging, make its glaze pattern decorative effect that in sintering procedure, forms a kind of natural fusion, it be a kind of on the ceramic surface making method that represents glaze pattern decorative effect of natural fusion.Belong to the texture of the increase product that the ceramic ware for daily use surface colour decorates and the making method of aesthetic feeling.
Embodiment
A kind of making method of utilizing latex hand painting pattern, filling glaze at the bottom of the ceramic base, the making method that represents glaze pattern decorative effect of natural fusion is to adopt Freehandhand-drawing latex pattern at the bottom of the ceramic base, tears glue after being stained with one deck reaction glaze, fill out sagging and send into kiln and fire and form, concrete steps are as follows:
A, on the ceramic dry body Freehandhand-drawing latex pattern, then being stained with one deck reaction glaze is ground-coat enamel, it is 0.5mm that the glaze layer adheres to thickness;
B, on the ceramic that is speckling with the reaction glaze, tear latex pattern on the dry body off, fill out sagging (should notice that in filling out the glaze process glaze colours of filling out will ride on the reaction glaze) after blowing off dust, fill out that should to add ratio in the sagging be 100: 1 glycerine; It is 0.5mm that sagging is adhered to thickness;
C, send in 1160 ℃ the raceway kiln and fire the glaze pattern decorative effect that can form a kind of natural fusion in 4 hours at last.
Otherwise, if ground-coat enamel is the stream axle, fills out glaze so and be the reaction glaze, concrete steps such as above-mentioned step are identical, then form above-mentioned identical decorative effect.
Claims (1)
1, a kind of making method of utilizing latex hand painting pattern, filling glaze at the bottom of the ceramic base, its feature is a Freehandhand-drawing latex pattern on the ceramic base substrate, is stained with and tears glue after one deck reacts glaze or sagging, fill out sagging or reaction glaze and send into kiln and fire and form, concrete steps are as follows:
A is Freehandhand-drawing latex pattern on the ceramic dry body, then is stained with one deck reaction glaze or flows axle to be ground-coat enamel, and it is 0.3～0.6mm that the glaze layer adheres to thickness;
B, on the ceramic that is speckling with reaction glaze or stream axle, tear the latex pattern on the dry body off, fill out sagging or reaction glaze after blowing off dust, fill out that to add ratio in the glaze be 100: 1 glycerine, it is 0.3～0.6mm that sagging or reaction glaze adhere to thickness, described ground-coat enamel is the reaction glaze, filling out glaze is sagging, or ground-coat enamel is sagging, fills out glaze and is the reaction glaze;
C, in 1130 ℃～1180 ℃ raceway kiln, fire the glaze pattern decorative effect that formed a kind of natural fusion in 4～5 hours.