CN100338160C - Plasticizing modified anticorrosive powder coating, and preparing method - Google Patents
Plasticizing modified anticorrosive powder coating, and preparing method Download PDFInfo
- Publication number
- CN100338160C CN100338160C CNB2004100204132A CN200410020413A CN100338160C CN 100338160 C CN100338160 C CN 100338160C CN B2004100204132 A CNB2004100204132 A CN B2004100204132A CN 200410020413 A CN200410020413 A CN 200410020413A CN 100338160 C CN100338160 C CN 100338160C
- Authority
- CN
- China
- Prior art keywords
- agent
- paint
- sericite
- pigment
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to plasticized modified corrosion-proof powdery paint which belongs to paint. The paint is prepared from 35 to 40% of novolac epoxy resin, 7 to 9% of acrylic acid silicone resin, 8 to 11% of solidifying agent, 7 to 9% of slipping agent, 0.4 to 0.6% hole eliminating agent, 0.8 to 1.0% of plasticizing agent, 14 to 16% of hollow micro bead, 6 to 8% of titanium white powder, 5 to 7% of barium sulfate, 2 to 3% of sericite, 1 to 3% of talcum powder and 0.6 to 0.8% of pigment. All the components are put into a container to be uniformly mixed, and the mixture is treated by the steps of extrusion, tabletting, wind cooling, grinding and sieving for obtaining the paint. The present invention has the advantages of simple technology, low cost, high impact resistance, difficult scratch and good corrosion-proof effect.
Description
Technical field
The invention belongs to coating, particularly a kind of plasticizing modification anti-corrosive powder paint.
Background technology
At present, the external corrosion prevention paint of widespread usage has individual layer epoxy powder, anticorrosion, the two component dual-layer epoxy powder of three-decker PE.But they are existing following defective in varying degrees: complex process, cost height, coating shock resistance, resistance to marring are poor, are prone to slight crack.
Summary of the invention
The present invention is intended to solve the deficiencies in the prior art, invented a kind of plasticizing modification anti-corrosive powder paint, formed by novolac epoxy, acrylic silicon resin, solidifying agent, smooth agent, pore eliminator, softening agent, cenosphere, titanium dioxide, barium sulfate, sericite, talcum powder, pigment.
Its preparation method is to comprise the steps to realize according to above-mentioned prescription:
A, novolac epoxy 35-40%, acrylic silicon resin 7-9%, solidifying agent 8-11%, smooth agent 7-9%, pore eliminator 0.4-0.6%, softening agent 0.8-1.0%, cenosphere 14-16%, titanium dioxide 6-8%, barium sulfate 5-7%, sericite 2-3%, talcum powder 1-3%, pigment 0.6-0.8% put into container and mix;
B, get among a mixed solution, promptly make finished product through extruding-compressing tablet-air-cooled-abrasive dust-screening.
Plasticizing modification anti-corrosive powder paint technology of the present invention is simple, cost is low, shock resistance is strong, be difficult for scuffing, favorable anti-corrosion effect.
Embodiment
Embodiment 1
Plasticizing modification anti-corrosive powder paint comprises following component: novolac epoxy 35-40%, acrylic silicon resin 7-9%, solidifying agent 8-11%, smooth agent 7-9%, pore eliminator 0.4-0.6%, softening agent 0.8-1.0%, cenosphere 14-16%, titanium dioxide 6-8%, barium sulfate 5-7%, sericite 2-3%, talcum powder 1-3% and pigment 0.6-0.8%.
Embodiment 2
The preparation method of plasticizing modification anti-corrosive powder paint is to comprise the steps: according to above-mentioned prescription
A, novolac epoxy 35-40%, acrylic silicon resin 7-9%, solidifying agent 8-11%, smooth agent 7-9%, pore eliminator 0.4-0.6%, softening agent 0.8-1.0%, cenosphere 14-16%, titanium dioxide 6-8%, barium sulfate 5-7%, sericite 2-3%, talcum powder 1-3%, pigment 0.6-0.8% are put into container and mix;
B, get among a mixed solution, promptly make finished product through extruding-compressing tablet-air-cooled-abrasive dust-screening.
Embodiment 3
The best of plasticizing modification anti-corrosive powder paint is formed: novolac epoxy 39.5%, acrylic silicon resin 8.0%, solidifying agent 9.5%, smooth agent 7.95%, pore eliminator 0.5%, softening agent 0.95%, cenosphere 15.7%, titanium dioxide 6.0%, barium sulfate 6.6%, sericite 3.0%, talcum powder 1.6% and pigment 0.7%.
Claims (2)
1, plasticizing modification anti-corrosive powder paint is by novolac epoxy, acrylic silicon resin, solidifying agent, smooth agent, pore eliminator, softening agent, cenosphere, titanium dioxide, barium sulfate, sericite, talcum powder and pigment are formed, and it is characterized in that the weight ratio of each component is: novolac epoxy 35-40%, acrylic silicon resin 7-9%, solidifying agent 8-11%, smooth agent 7-9%, pore eliminator 0.4-0.6%, softening agent 0.8-1.0%, cenosphere 14-16%, titanium dioxide 6-8%, barium sulfate 5-7%, sericite 2-3%, talcum powder 1-3%, pigment 0.6-0.8%.
2, the preparation method of plasticizing modification anti-corrosive powder paint is characterized in that comprising the steps: according to the prescription of claim 1
A, novolac epoxy 35-40%, acrylic silicon resin 7-9%, solidifying agent 8-11%, smooth agent 7-9%, pore eliminator 0.4-0.6%, softening agent 0.8-1.0%, cenosphere 14-16%, titanium dioxide 6-8%, barium sulfate 5-7%, sericite 2-3%, talcum powder 1-3%, pigment 0.6-0.8% are put into container and mix;
B, get among a mixed solution, promptly make finished product through extruding-compressing tablet-air-cooled-abrasive dust-screening.