CH710846B1 - Micromechanical part comprising a microstructured tribological reservoir for a lubricating substance. - Google Patents
Micromechanical part comprising a microstructured tribological reservoir for a lubricating substance. Download PDFInfo
- Publication number
- CH710846B1 CH710846B1 CH00348/15A CH3482015A CH710846B1 CH 710846 B1 CH710846 B1 CH 710846B1 CH 00348/15 A CH00348/15 A CH 00348/15A CH 3482015 A CH3482015 A CH 3482015A CH 710846 B1 CH710846 B1 CH 710846B1
- Authority
- CH
- Switzerland
- Prior art keywords
- microcavities
- microstructured
- micromechanical part
- part according
- zone
- Prior art date
Abstract
L’invention se rapporte à une pièce de micromécanique, destinée notamment aux mécanismes d’horlogerie, comprenant localement au moins une zone microstructurée (1) au moyen d’un laser, la zone microstructurée présentant une surface tridimensionnelle formée de microcavités configurées pour servir de réservoir pour une substance lubrifiante.The invention relates to a micromechanical component, intended in particular for clockwork mechanisms, locally comprising at least one microstructured zone (1) by means of a laser, the microstructured zone having a three-dimensional surface formed of microcavities configured to serve as a tank for a lubricating substance.
Description
DescriptionDescription
Domaine de l’invention [0001] L’invention se rapporte aux pièces de micromécanique, notamment à celles d’une montre mécanique, dont certaines des pièces mobiles sont amenées à être lubrifiées.FIELD OF THE INVENTION [0001] The invention relates to micromechanical parts, in particular to those of a mechanical watch, some of whose moving parts are made to be lubricated.
Arrière-plan de l’invention [0002] Il est connu que dans les mécanismes d’horlogerie, nombreuses sont les pièces en mouvement et en contact avec frottement les unes avec les autres. Ces frottements doivent être réduits le plus possible car ils peuvent affecter la précision et/ou l’autonomie du mécanisme.BACKGROUND OF THE INVENTION [0002] It is known that in watchmaking mechanisms, many parts are in motion and in frictional contact with each other. This friction must be reduced as much as possible because it can affect the precision and / or the autonomy of the mechanism.
[0003] En effet, les frottements entraînent une usure des pièces, une augmentation de la consommation d’énergie pour déplacer les pièces et un ralentissement du mouvement.Indeed, friction leads to wear of the parts, an increase in energy consumption to move the parts and a slowing down of the movement.
[0004] Pour réduire ces frottements il est donc connu d’utiliser des lubrifiants liquides ou visqueux. Ces lubrifiants sont utilisés parcimonieusement sur des zones bien définies et en quantités adaptées. Ce type de lubrifiant doit être capable de se glisser entre deux pièces pour minimiser le frottement ou doit être déposé au cours du montage. A contrario des capacités à se glisser entre deux pièces, il peut également s’échapper de l’espace où il a été déposé. Il est en outre très sensible aux conditions environnementales de température et d’humidité relative car sa viscosité évolue en fonction de celles-ci.To reduce these friction it is known to use liquid or viscous lubricants. These lubricants are used sparingly on well-defined areas and in suitable quantities. This type of lubricant must be able to slip between two parts to minimize friction or must be removed during assembly. On the other hand, the ability to slip between two rooms can also escape from the space where it has been deposited. It is also very sensitive to the environmental conditions of temperature and relative humidity because its viscosity evolves according to these.
[0005] Un inconvénient d’une telle solution est que ces lubrifiants liquides ou visqueux se modifient dans le sens de la dégradation, par exemple en se chargeant de poussières ou en devenant plus visqueux ou en perdant de leurs capacités lubrifiantes par oxydation.A disadvantage of such a solution is that these liquid or viscous lubricants are modified in the direction of degradation, for example by loading with dust or becoming more viscous or losing their lubricating capacity by oxidation.
[0006] Un autre inconvénient est que ce type de lubrifiant étant fluide ou visqueux, le mouvement des pièces tend à déplacer le lubrifiant de la zone des contacts vers une zone non soumise à frottement.Another disadvantage is that this type of lubricant is fluid or viscous, the movement of the parts tends to move the lubricant from the contact area to a non-frictional area.
[0007] Il est donc nécessaire de procéder régulièrement à un entretien qui consiste à nettoyer les pièces en frottement et remplacer le lubrifiant usagé par un lubrifiant neuf aux endroits appropriés.It is therefore necessary to conduct regular maintenance which consists in cleaning the parts in friction and replace the used lubricant with a new lubricant in the appropriate places.
[0008] La lubrification d’un mécanisme horloger a pour but de maîtriser les frottements des pièces en mouvement. Elle obéit à des règles complexes et précises afin de garantir une fiabilité maximale et durable. Son action, par un film d’huile ou de graisse, empêche le contact direct des matières en présence, ce qui se traduit par une diminution des pertes d’énergie et de l’usure, dues aux frottements, ainsi qu’une augmentation du rendement mécanique. Selon les pièces en contact, différentes huiles ou graisses sont appliquées avec des viscosités variables et dans des quantités bien déterminées.The lubrication of a watch mechanism aims to control the friction of moving parts. It obeys complex and precise rules in order to guarantee maximum and lasting reliability. Its action, by a film of oil or grease, prevents the direct contact of the materials in the presence, which results in a reduction of the energy losses and the wear, due to the friction, as well as an increase of the mechanical efficiency. Depending on the parts in contact, different oils or greases are applied with varying viscosities and in specific amounts.
[0009] En pratique, des pertes de lubrification sont observées dans le temps comme par exemple sur des pièces en rotation qui exercent un effet projection et favorisent la fuite. Par conséquent, des entretiens réguliers (nettoyage et/ou épilamage et huilage) doivent être effectués sur les mouvements. Pour diminuer la fréquence et les coûts de ces entretiens, différentes solutions ont été envisagées et appliquées dans l’industrie horlogère.In practice, losses of lubrication are observed over time, for example on rotating parts that exert a projection effect and promote leakage. Therefore, regular maintenance (cleaning and / or epilamming and oiling) must be performed on the movements. To reduce the frequency and costs of these interviews, various solutions have been considered and applied in the watch industry.
[0010] La première solution est axée sur des formulations spéciales de lubrifiant. Le lubrifar en est un exemple. Il correspond à un mélange d’huile Moebius 9010 et de particules solides de MoS2. En production, ce mélange est déposé par spray sur les flancs de roues d’échappement, donnant une coloration typique noire et pâteuse. Les micrograins permettent de piéger, telle une éponge, l’huile thixotrope 9415 appliquée dans un second temps sur la roue. Le lubrifar assure ainsi un fonctionnement plus stable et durable qu’une lubrification standard. Cependant, il pose de forts problèmes esthétiques, surtout pour les marques haut de gamme qui ont de hauts critères dans ce domaine.The first solution is focused on special lubricant formulations. Lubric is an example. It corresponds to a mixture of Moebius 9010 oil and MoS2 solid particles. In production, this mixture is deposited by spray on the sides of escape wheels, giving a typical black and pasty coloration. The micrograins make it possible to trap, like a sponge, the thixotropic oil 9415 applied in a second step on the wheel. The lubricant ensures a more stable and durable operation than standard lubrication. However, it poses strong aesthetic problems, especially for premium brands that have high standards in this area.
[0011] Une autre solution consiste à structurer la matière de base constituant la pièce mouvement. Une telle solution est décrite dans le document DE 10 2009 046 647. La pièce de base en aluminium ou alliage d’aluminium comprend un revêtement à base d’oxydes formé par oxydation anodique. Ce revêtement bien que dur possède une structure alvéolaire avec des pores pouvant recevoir une huile, graisse ou un lubrifiant solide. Cependant, une telle solution ne permet pas d’être appliquée de façon sélective sur des zones précisément délimitées de la pièce. De plus, elle est limitée à un seul type de matière de base, à savoir les alliages à base d’aluminium. Résumé de l’invention [0012] L’invention a notamment pour objectif de pallier les différents inconvénients de ces techniques connues.Another solution is to structure the basic material constituting the movement piece. Such a solution is described in DE 10 2009 046 647. The base part made of aluminum or aluminum alloy comprises an oxide-based coating formed by anodic oxidation. This coating although hard has a honeycomb structure with pores that can receive an oil, grease or a solid lubricant. However, such a solution does not allow to be applied selectively to precisely defined areas of the room. In addition, it is limited to only one type of base material, namely aluminum-based alloys. SUMMARY OF THE INVENTION [0012] The purpose of the invention is in particular to overcome the various disadvantages of these known techniques.
[0013] Plus précisément, un objectif de l’invention est de fournir une lubrification localisée permettant d’optimiser le rôle du lubrifiant.More specifically, an object of the invention is to provide localized lubrication to optimize the role of the lubricant.
[0014] L’invention a également pour objectif, au moins dans un mode de réalisation particulier, de fournir une lubrification qui soit fiable et durable.The invention also aims, at least in a particular embodiment, to provide lubrication that is reliable and durable.
[0015] Ces objectifs, ainsi que d’autres qui apparaîtront plus clairement par la suite, sont atteints selon l’invention à l’aide d’une pièce de micromécanique, destinée notamment aux mécanismes d’horlogerie, comprenant localement au moins une zone microstructurée au moyen d’un laser, la zone microstructurée présentant une surface tridimensionnelle formée de microcavités configurées pour servir de réservoir pour une substance lubrifiante.These objectives, as well as others which will appear more clearly later, are achieved according to the invention with the aid of a micromechanical part, intended in particular for clockwork mechanisms, comprising locally at least one zone. microstructured by means of a laser, the microstructured area having a three-dimensional surface formed of microcavities configured to serve as a reservoir for a lubricating substance.
[0016] Ainsi, l’objet de la présente invention, par ses différents aspects fonctionnels et structurels décrits ci-dessus, permet d’obtenir une pièce dont les zones soumises aux frottements présentent une lubrification localisée permettant d’optimiser le rôle du lubrifiant et d’en augmenter l’efficacité en concentrant le lubrifiant dans les zones soumises aux frottements, la technique de gravure par laser présentant l’avantage d’offrir une très grande précision de réalisation.[0016] Thus, the object of the present invention, by its different functional and structural aspects described above, makes it possible to obtain a part whose zones subjected to friction have localized lubrication making it possible to optimize the role of the lubricant and to increase the efficiency by concentrating the lubricant in the areas subject to friction, the laser engraving technique has the advantage of providing a very high accuracy of realization.
[0017] Conformément à d’autres variantes avantageuses de l’invention: - la zone microstructurée présente un réseau de microcavités distribuées de manière régulière; - la profondeur P des microcavités est inférieure ou égale à 100 μιτι; - le diamètre L des microcavités est comprise entre 0,1 μιτι et 100 μιτι, et de préférence entre 1 μιτι et 10 μιτι; - la profondeur P et le diamètre L des microcavités peuvent varier au sein d’une même zone microstructurée; - la profondeur P des microcavités est supérieure au diamètre L des microcavités; - les microcavités se présentent sous la forme de trous ou de canyons; - la zone microstructurée est réalisée par un procédé d’usinage par impulsions laser, par exemple picoseconde ou femtoseconde; - la zone microstructurée est en métal, céramique, polymère ou composite. Comme métal ou alliage métallique, on peut citer en exemple l’acier, l’aluminium, le titane, le laiton, le nickel ou l’or; - la zone microstructurée peut aussi être en rubis, en silicium, en quartz ou encore en diamant.According to other advantageous variants of the invention: the microstructured zone has a network of microcavities distributed in a regular manner; the depth P of the microcavities is less than or equal to 100 μιτι; the diameter L of the microcavities is between 0.1 μm and 100 μm, and preferably between 1 μm and 10 μm; the depth P and the diameter L of the microcavities may vary within the same microstructured zone; the depth P of the microcavities is greater than the diameter L of the microcavities; the microcavities are in the form of holes or canyons; the microstructured zone is produced by a laser pulse machining method, for example a picosecond or a femtosecond method; the microstructured zone is made of metal, ceramic, polymer or composite. Examples of metal or metal alloys are steel, aluminum, titanium, brass, nickel or gold; - The microstructured area can also be ruby, silicon, quartz or diamond.
[0018] Selon l’invention, la zone microstructurée peut être une paroi intérieure d’un barillet, un axe de mobile en rotation, des palettes d’échappement, des dents de roue d’échappement ou encore des pierres de pivotement.According to the invention, the microstructured zone may be an inner wall of a barrel, a rotating axis of rotation, exhaust vanes, escape wheel teeth or pivoting stones.
Description sommaire des dessins [0019] D’ autres particularités et avantages ressortiront clairement de la description qui en est faite ci-après, à titre indicatif et nullement limitatif, en référence aux dessins annexés, dans lesquels: les fig. 1a et 2a sont des vues schématiques de dessus d’une zone microstructurée selon deux modes de réalisation distincts; les fig. 1 b et 2b sont respectivement des vues en coupe selon les plans II et III des fig. 1 a et 2a; les fig. 3a et 3b illustrent respectivement une vue en perspective d’une palette d’échappement présentant une zone microstructurée et une vue en coupe de la palette.BRIEF DESCRIPTION OF THE DRAWINGS [0019] Other particularities and advantages will become clear from the description which is given hereinafter, by way of indication and in no way limiting, with reference to the appended drawings, in which: FIGS. 1a and 2a are schematic views from above of a microstructured zone according to two distinct embodiments; figs. 1b and 2b are respectively sectional views along planes II and III of FIGS. 1a and 2a; figs. 3a and 3b respectively show a perspective view of an exhaust pallet having a microstructured area and a sectional view of the pallet.
Description détaillée des modes de réalisation préférés [0020] Une pièce de micromécanique selon un mode de réalisation particulier va maintenant être décrite dans ce qui suit faisant référence conjointement aux fig. 1a, 1b, 2a, 2b, 3a et 3b.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS [0020] A micromechanical part according to a particular embodiment will now be described in the following with reference to FIGS. 1a, 1b, 2a, 2b, 3a and 3b.
[0021] L’invention concerne une pièce de micromécanique, destinée notamment aux mécanismes d’horlogerie, comprenant localement au moins une zone microstructurée 1 au moyen d’un laser, la zone microstructurée 1 présentant une surface tridimensionnelle formée de microcavités 10 configurées pour servir de réservoir pour une substance lubrifiante.The invention relates to a micromechanical component, intended in particular for clockwork mechanisms, comprising locally at least one microstructured zone 1 by means of a laser, the microstructured zone 1 having a three-dimensional surface formed of microcavities 10 configured to serve tank for a lubricating substance.
[0022] Un premier mode de réalisation est illustré à la fig. 1a, et représente schématiquement une zone microstructurée 1 d’une pièce de micromécanique. On peut observer des microcavités 10 formées sur la surface de la pièce de manière régulière.A first embodiment is illustrated in FIG. 1a, and schematically represents a microstructured zone 1 of a micromechanical component. Microcavities can be observed formed on the surface of the workpiece on a regular basis.
[0023] La zone microstructurée 1 est formée par un réseau de microcavités 10 formées au moyen d’un laser dont la durée des impulsions est de l’ordre de la femtoseconde, c’est-à-dire 10~15 seconde (typiquement 100 fs). La durée des impulsions peut aller de la femtoseconde à la picoseconde (10~12 seconde). Le laser est utilisé afin de modifier la structure de la pièce de micromécanique et former localement une zone microstructurée 1 présentant une surface tridimensionnelle. A cet effet, le laser est mis en mouvement de manière à ce qu’il balaie la surface de la pièce à microstructurer afin de provoquer localement une modification de la structure du matériau de la pièce.The microstructured zone 1 is formed by a network of microcavities 10 formed by means of a laser whose duration of the pulses is of the order of the femtosecond, that is to say 10 ~ 15 seconds (typically 100 fs). Pulse duration can range from femtosecond to picosecond (10 ~ 12 seconds). The laser is used to modify the structure of the micromechanical part and locally form a microstructured area 1 having a three-dimensional surface. For this purpose, the laser is set in motion so that it sweeps the surface of the microstructure part to locally cause a change in the structure of the material of the part.
[0024] On peut également imaginer que c’est la pièce qui est mise en mouvement, ou bien une combinaison des deux, de manière à modifier la structure de la pièce.One can also imagine that it is the part that is set in motion, or a combination of both, so as to change the structure of the room.
[0025] Selon l’invention, la zone microstructurée 1 présente un réseau de microcavités 10 distribuées de manière régulière en suivant un schéma précis comme illustré à la fig. 1 a. La distribution des microcavités peut bien évidemment être réalisée de manière aléatoire en programmant les déplacements du laser et/ou de la pièce.According to the invention, the microstructured zone 1 has a network of microcavities 10 distributed in a regular manner following a precise diagram as illustrated in FIG. 1 a. The distribution of microcavities can obviously be performed randomly by programming the movements of the laser and / or the part.
[0026] Les microcavités 10 formant la surface tridimensionnelle peuvent être définies selon les trois paramètres suivants: la forme, les dimensions, à savoir le diamètre L et la profondeur P, et la surface de recouvrement.The microcavities 10 forming the three-dimensional surface can be defined according to the following three parameters: the shape, the dimensions, namely the diameter L and the depth P, and the surface of recovery.
[0027] La profondeur P des microcavités 10 est avantageusement inférieure ou égale à 100 μιτι, et le diamètre L des microcavités 10 est compris entre 0,1 μιτι et 100 μιτι, et de préférence entre 1 μιτι et 10 μιτι.The depth P of the microcavities 10 is advantageously less than or equal to 100 μιτι, and the diameter L of the microcavities 10 is between 0.1 μιτι and 100 μιτι, and preferably between 1 μιτι and 10 μιτι.
[0028] Selon un mode de réalisation particulier de l’invention, la profondeur P et le diamètre L des microcavités 10 peuvent varier au sein d’une même zone microstructurée 1. On peut par exemple envisager qu’un premier tiers de la zone micro-structurée 1 présente des microcavités 10 ayant une profondeur de 1 pm et un diamètre de 10 pm, qu’un deuxième tiers de la zone microstructurée 1 présente des microcavités 10 ayant une profondeur de 10 pm et un diamètre de 100 pm, et qu’un troisième tiers présente des microcavités 10 ayant une profondeur de 1 pm et un diamètre de 10 pm.According to a particular embodiment of the invention, the depth P and the diameter L of the microcavities 10 may vary within the same microstructured zone 1. It may for example be envisaged that a first third of the micro zone Structurally 1 has microcavities 10 having a depth of 1 μm and a diameter of 10 μm, whereas a second third of the microstructured zone 1 has microcavities having a depth of 10 μm and a diameter of 100 μm, and a third third has microcavities having a depth of 1 μm and a diameter of 10 μm.
[0029] Ainsi les combinaisons peuvent varier en fonction des besoins de l’homme du métier, c’est-à-dire en fonction du type d’application et du type de pièce.Thus the combinations can vary according to the needs of the skilled person, that is to say, depending on the type of application and the type of room.
[0030] Selon une variante de l’invention, la profondeur P des microcavités 10 est supérieure au diamètre L des microcavités, de l’ordre de trois par exemple.According to a variant of the invention, the depth P of the microcavities 10 is greater than the diameter L of the microcavities, of the order of three for example.
[0031] Selon les besoins de l’homme du métier, les microcavités 10 peuvent prendre différentes formes, et être par exemple de forme hémisphérique, elliptique, parallélépipédique ou encore se présenter sous la forme de rainures. Des modes de réalisation présentant respectivement des microcavités 10 de forme hémisphérique et des microcavités 10 sous la forme de rainures sont illustrés aux fig. 1a et 2a.According to the needs of those skilled in the art, the microcavities 10 may take different forms, and be for example of hemispherical, elliptical, parallelepiped shape or be in the form of grooves. Embodiments respectively having microcavities 10 of hemispherical shape and microcavities 10 in the form of grooves are illustrated in FIGS. 1a and 2a.
[0032] Selon l’invention, les microcavités 10 formant la zone microstructurée 1 peuvent occuper une surface variable, par exemple les microcavités peuvent occuper 20% de la surface de la zone microstructurée de manière à ne pas saturer de substance lubrifiante la zone microstructurée 1.According to the invention, the microcavities 10 forming the microstructured zone 1 can occupy a variable surface, for example the microcavities can occupy 20% of the surface of the microstructured zone so as not to saturate the microstructured zone with lubricating substance 1 .
[0033] Comme on peut l’observer sur la vue en coupe à la fig. 1b, selon la ligne ll-ll de la fig. 1a, le diamètre L des microcavités 10 peut varier en fonction de la profondeur P. Il en est de même pour la largeur L des rainures sur la vue en coupe à la fig. 2b, selon la ligne lll-lll de la fig. 2b.As can be seen in the sectional view in FIG. 1b, according to the line ll-ll of FIG. 1a, the diameter L of the microcavities 10 may vary according to the depth P. It is the same for the width L of the grooves in the sectional view in FIG. 2b, according to the line III-III of FIG. 2b.
[0034] Selon la pièce de micromécanique recevant la modification, la zone à microstructurer peut être en métal, en alliage métallique, céramique, polymère ou composite. Les métaux ou alliages métalliques peuvent être par exemple en acier, aluminium, titane, laiton, nickel ou en or. La zone à microstructurer peut aussi être en rubis, en silicium, en quartz ou encore en diamant.According to the micromechanical part receiving the modification, the zone to be microstructured may be metal, metal alloy, ceramic, polymer or composite. The metals or metal alloys can be for example steel, aluminum, titanium, brass, nickel or gold. The zone to be microstructured can also be in ruby, silicon, quartz or diamond.
[0035] Les pièces de micromécanique présentant au moins une zone microstructurée 1 peuvent être, par exemple, une paroi intérieure d’un barillet, un axe de mobile en rotation, des palettes d’échappement, des dents de roue d’échappement, ou encore des pierres de pivotement.The micromechanical parts having at least one microstructured zone 1 may be, for example, an inner wall of a cylinder, an axis of mobile rotation, exhaust vanes, exhaust wheel teeth, or still some pivoting stones.
[0036] Un exemple de réalisation pour une palette 100 d’une ancre est illustré aux fig. 3a et 3b.An exemplary embodiment for a pallet 100 of an anchor is illustrated in FIGS. 3a and 3b.
[0037] En se référant aux fig. 3a et 3b, on observe une palette d’ancre 100. La palette est une pièce généralement en rubis dont toutes les faces sont polies et qui est chassée et collée dans un logement 104 ménagé dans le bras 101 d’une ancre 102. La palette 100 comprend un plan d’impulsion 100a, un plan de repos 100b et un plan de fuite 100c, le plan d’impulsion 100a et le plan de fuite 100c se coupant selon une arrête de sortie ou bec d’impulsion 100d. Le plan d’impulsion 100a et le plan de repos 100b coopèrent respectivement avec les dents 106 d’une roue d’échappement et plus particulièrement avec le plan de repos 106a et le bec de repos 106b des dents 106. La roue d’échappement tourne de manière classique pas à pas dans le sens de la flèche F. Les points de lubrification particulièrement importants sont donc le plan d’impulsion 100a et le plan de repos 100b de sorte qu’une présence de lubrifiant entre les dents de la roue d’échappement et ces plans est nécessaire au cours des différentes phases de fonctionnement de l’échappement.Referring to FIGS. 3a and 3b, there is an anchor pallet 100. The pallet is a generally ruby piece whose all faces are polished and which is driven and glued in a housing 104 formed in the arm 101 of an anchor 102. The pallet 100 comprises a pulse plane 100a, a rest plane 100b and a leakage plane 100c, the pulse plane 100a and the leakage plane 100c intersecting at an output edge or pulse tip 100d. The impulse plane 100a and the rest plane 100b cooperate respectively with the teeth 106 of an escape wheel and more particularly with the rest plane 106a and the stopper 106b of the teeth 106. The escape wheel rotates. in a conventional manner step by step in the direction of the arrow F. Particularly important lubrication points are therefore the pulse plane 100a and the rest plane 100b so that a presence of lubricant between the teeth of the wheel of exhaust and these plans is necessary during the different phases of operation of the exhaust.
[0038] Pour ce faire, la palette 100 comprend une zone microstructurée servant de réservoir pour ce lubrifiant. On notera que les dimensions de la zone microstructurée sont sensiblement équivalentes ou supérieures à celles de la dent 106 de roue d’échappement.To do this, the pallet 100 comprises a microstructured zone serving as a reservoir for this lubricant. It will be noted that the dimensions of the microstructured zone are substantially equivalent to or greater than those of the tooth 106 of the escape wheel.
[0039] Selon l’invention, la zone microstructurée relie le plan de fuite 100c au plan d’impulsion 100a et au plan de repos 100b de manière à établir une zone de lubrification sur la surface en contact avec les dents 106 de la roue d’échappement.According to the invention, the microstructured zone connects the leakage plane 100c to the pulse plane 100a and to the rest plane 100b so as to establish a lubrication zone on the surface in contact with the teeth 106 of the wheel. 'exhaust.
[0040] Comme on peut l’observer sur la fig. 3b, le lubrifiant 107 qui est déposé sur la zone microstructurée de la palette 100 sous la forme d’une goutte s’introduit par capillarité dans les microcavités et remplit ces dernières jusqu’à ce que se forme une goutte 107a qui fait légèrement saillie à partir du plan d’impulsion 100a. Une goutte 107b se forme également sur le plan de repos 100b lorsque la palette 100 est en contact avec la dent 106.As can be seen in FIG. 3b, the lubricant 107 which is deposited on the microstructured zone of the pallet 100 in the form of a drop is introduced by capillarity into the microcavities and fills the latter until a drop 107a is formed which projects slightly to from the pulse plane 100a. A drop 107b is also formed on the rest plane 100b when the pallet 100 is in contact with the tooth 106.
[0041] Grâce à ces différents aspects de l’invention, on dispose d’une palette d’échappement présentant une lubrification localisée permettant d’optimiser le rôle du lubrifiant et d’en augmenter l’efficacité en concentrant le lubrifiant dans les zones soumises aux frottements. Le lubrifiant étant piégé dans la zone microstructurée, les phénomènes de fuites et migrations sont diminués et la durée de la lubrification est considérablement augmentée. De même, la fréquence et les coûts d’entretien du mouvement de la montre sont diminués.With these various aspects of the invention, there is an exhaust pallet with localized lubrication to optimize the role of the lubricant and increase its effectiveness by concentrating the lubricant in the areas subject to friction. As the lubricant is trapped in the microstructured zone, the phenomena of leaks and migrations are reduced and the duration of the lubrication is considerably increased. Similarly, the frequency and maintenance costs of the movement of the watch are decreased.
[0042] Bien entendu, la présente invention ne se limite pas à l’exemple illustré mais est susceptible de diverses variantes et modifications qui apparaîtront à l’homme de l’art. En particulier, toute pièce formant le mouvement d’une montre et soumise à des frottements est susceptible de comprendre une zone microstructurée telle que décrite précédemment.Of course, the present invention is not limited to the example shown but is susceptible to various variations and modifications that will occur to those skilled in the art. In particular, any piece forming the movement of a watch and subjected to friction is likely to include a microstructured area as described above.
Claims (11)