CH641845A5

CH641845A5 - ANTISTATIC THREADING.

Info

Publication number: CH641845A5
Application number: CH1014579A
Authority: CH
Inventors: Wolfgang Peschke; Diedrich Dr Dipl Ing Schilo; Chem Sipke Johannes Van D Meer
Original assignee: Akzo Nv
Priority date: 1978-11-23
Filing date: 1979-11-14
Publication date: 1984-03-15
Also published as: FR2442284B1; FR2442284A1; DE2850713C2; GB2036638B; SE435072B; GB2036638A; CA1150019A; DK149826B; ATA735979A; AT387596B; SE7909640L; DE2850713A1; DK493279A

Description

Die Erfindung betrifft ein antistatisches Fadengebilde aus Mehrkomponentenfäden aus wenigstens zwei synthetischen Polymerkomponenten, von denen eine Komponente aus einem elektrisch nichtleitenden, thermoplastischen, fadenbil5 The invention relates to an antistatic thread structure made of multi-component threads made of at least two synthetic polymer components, one component of which is made of an electrically non-conductive, thermoplastic thread thread

10 10th

15 15

20 20th

25 25th

30 30th

35 35

40 40

45 45

50 50

55 55

60 60

65 65

denden Polymerisat und eine andere Komponente aus einem thermoplastischen Polymerisat mit darin dispergiertem, elektrisch leitenden Pulver besteht, welches Fadengebilde bei einer Messpannung von 1 kV einen spezifischen Durchgangswiderstand nach DIN 54 345 von weniger als IO13 Ohm-cm aufweist. The polymer and another component consists of a thermoplastic polymer with an electrically conductive powder dispersed therein, the thread structure at a measuring voltage of 1 kV having a volume resistance according to DIN 54 345 of less than IO13 ohm-cm.

Unter einem Fadengebilde sollen im Rahmen der Erfindung Filamente, Stapelfasern, aus Filamenten und/oder Stapelfasern hergestellte Garne oder Fadenbündel verstanden werden. In the context of the invention, a thread structure is to be understood as meaning filaments, staple fibers, yarns or bundles of threads made from filaments and / or staple fibers.

Antistatische Fadengebilde dieser Gattung werden in der DE-OS 23 37 103 beschrieben, wobei das leitfähige Polymer den Kern in einem Kern-Mantelfaden bildet und der Mantel des Kern-Mantelfadens mindestens 50% der Fadenquerschnittsfläche einnehmen soll. Antistatic thread structures of this type are described in DE-OS 23 37 103, the conductive polymer forming the core in a core sheath thread and the sheath of the core sheath thread taking up at least 50% of the thread cross-sectional area.

Zwar wird trotz der isolierenden Abschirmung des Kernes noch eine ausreichende antistatische Wirksamkeit erreicht, dieses jedoch hauptsächlich auf Kosten eines hohen Materialeinsatzes an leitfähigem Russ. Mit steigendem Russgehalt nimmt die Spinnfähigkeit des Russ-Polymer-Gemisches sehr stark ab, was zu Schwierigkeiten bei der Herstellung der Bikomponentenfäden führt. Sufficient antistatic effectiveness is still achieved despite the insulating shielding of the core, but this is mainly at the expense of a high amount of material used in conductive carbon black. As the carbon black content increases, the spinnability of the carbon black polymer mixture decreases significantly, which leads to difficulties in the production of the bicomponent threads.

Die Verstreckung ist insbesondere bei Verwendung von fadenbildenden Polymeren für die russhaltige Kernkomponente ohne erhebliche Erhöhung des elektrischen Widerstandes nur bei erhöhten Strecktemperaturen und mit Polymeren mit niedrigem Schmelzpunkt möglich. Bei der Verarbeitung zu Stapelfasergarnen machen sich die an den Schnittstellen zutage tretenden schwarzen Russquerschnitte störend bemerkbar. In der genannten DE-OS wird eine von der DIN-Vorschrift 54 345 abweichende Methode zur Messung des Fadenwiderstandes beschrieben, deren Ergebnisse nur für den jeweiligen Fadenquerschnitt Gültigkeit haben. Drawing, in particular when using thread-forming polymers for the soot-containing core component, without significant increase in electrical resistance, is only possible at elevated drawing temperatures and with polymers with a low melting point. When processing into staple fiber yarns, the black soot cross-sections emerging at the interfaces are noticeable. In the DE-OS cited, a method for measuring the thread resistance deviating from the DIN regulation 54 345 is described, the results of which are only valid for the respective thread cross-section.

Aus der DE-OS 26 23 672 ist ein anderer antistatischer, synthetischer Bikomponentenfäden bekannt, der in einer Komponente elektrisch leitfähigen Russ enthält, wobei der eine Bestandteil den russhaltigen Bestandteil nur teilweise, mindestens jedoch zu 50%, umhüllt und eine gekrümmte Grenzfläche bildet. Das bedeutet, dass lediglich ausschliesslich Fäden mit asymmetrischer Querschnittsanordnung ersponnen werden können. Another antistatic, synthetic bicomponent thread is known from DE-OS 26 23 672, which contains electrically conductive carbon black in one component, one component only partially, at least 50%, enveloping the carbon black-containing component and forming a curved interface. This means that only threads with an asymmetrical cross-sectional arrangement can be spun.

Darüberhinaus ist noch die DE-OS 27 18 343 bekannt geworden, die ein integrales elektrisch leitfähiges Textilfila-ment beschreibt, welches aus 2 bis 1000 elektrisch leitfähigen longitudial gerichteten Schichten aus faserbildenden poly-meren Material mit feinverteilten Teilchen aus elektrisch leitfähigem Russ in einer Konzentration von etwa 30 Gew.-% und in gemeinsamer Verbindung mit jeder elektrisch leitenden Schicht längs der Länge von mindestens einer Hauptoberfläche eine nicht leitende Schicht aus dem faserbildenden polymeren Material besteht. Derartige Fäden unterscheiden sich hinsichtlich ihrer Färbung nur wenig von Fäden die nur aus einem Gemisch aus leitfähigem Russ und fadenbildendem Material hergestellt sind. Furthermore, DE-OS 27 18 343 has become known, which describes an integral electrically conductive textile filament, which consists of 2 to 1000 electrically conductive longitudinally oriented layers of fiber-forming polymer material with finely divided particles of electrically conductive carbon black in a concentration of about 30% by weight, and in association with each electrically conductive layer along the length of at least one major surface, there is a non-conductive layer of the fiber-forming polymeric material. Such threads differ only slightly in their coloring from threads which are made only from a mixture of conductive carbon black and thread-forming material.

Matrixsegmentmehrkomponentenfäden, deren Herstellung und deren Spaltung werden in den deutschen Patentanmeldungen P 28 03 136.9 und P 28 09 346.1 beschrieben. Dort werden auch noch andere bekannte Mehrkomponentenfäden mit Matrixsegmentstrukturen beschrieben, von denen jedoch keine leitfähig und damit antistatisch wirksam ist. Matrix segment multicomponent threads, their production and their splitting are described in German patent applications P 28 03 136.9 and P 28 09 346.1. Other known multi-component threads with matrix segment structures are also described there, none of which, however, is conductive and thus has an antistatic effect.

Aufgabe der vorliegenden Erfindung war es, antistatische Fadengebilde, entsprechend der für den Rahmen der Erfindung angegebenen Definition zur Verfügung zu stellen, die eine gute antistatische Wirksamkeit und eine minimale optische Auffälligkeit in textilen Flächengebilden, wie Geweben, Gewirken, Fadengelegen, Teppichen, Vliesen, und dergleichen aufweisen. The object of the present invention was to provide antistatic thread structures, according to the definition given for the scope of the invention, which have good antistatic activity and minimal visual conspicuity in textile surface structures, such as woven fabrics, knitted fabrics, thread beds, carpets, nonwovens, and the like.

Diese Aufgabe wird erfindungsgemäss entsprechend der This object is achieved according to the

641 845 641 845

Lehre von Anspruch 1 gelöst. Weitere vorteilhafte Ausführungsformen werden in den Ansprüchen 2 bis 29 beschrieben. Teaching of claim 1 solved. Further advantageous embodiments are described in claims 2 to 29.

Leitfähige Pulver, die im Rahmen der Erfindung in ein thermoplastisches Polymer dispergiert werden können und eine gute antistatische Wirksamkeit hervorrufen, sind feintei-lige Metallpulver, wie beispielsweise Chrompulver oder leitfähige Metalloxide oder Metalloxidmischphasen wie z.B. Zinn-Antimonoxid. Bevorzugt sind wegen der guten Wirksamkeit und der guten Beschaffungsmöglichkeiten elektrisch leitfähige Russorten, die als elektrisch leitfähige Pulver in ein thermoplastisches Polymer dispergiert werden. Conductive powders which can be dispersed in a thermoplastic polymer in the context of the invention and which have good antistatic activity are finely divided metal powders such as, for example, chrome powder or conductive metal oxides or metal oxide mixed phases, such as e.g. Tin antimony oxide. Because of the good effectiveness and the good procurement options, electrically conductive types of soot are preferred, which are dispersed as an electrically conductive powder in a thermoplastic polymer.

Unter Matrix-Segmentfäden sind solche Mehrkomponentenfäden zu verstehen, bei denen die einzelnen Segmente und die Matrix kontinuierlich durchgehend entlang der Fadenachse angeordnet sind, so dass der Fadenquerschnitt im wesentlichen über die Fadenlänge gleich ist. Beispiele für Fadenquerschnitte, die im Rahmen der Erfindung geeignet sind, werden in den Figuren 1 bis 11 dargestellt, wobei a jeweils die Matrix und b Segmente bedeuten. Matrix segment threads are to be understood to mean those multi-component threads in which the individual segments and the matrix are arranged continuously continuously along the thread axis, so that the thread cross section is essentially the same over the thread length. Examples of thread cross sections which are suitable in the context of the invention are shown in FIGS. 1 to 11, where a in each case denotes the matrix and b segments.

Die Fäden können aussen rund, oder wie beispielsweise in den Figuren 10 und 11, aussen profiliert geformt sein. Sie können auch aussen in beliebiger Form gestaltet sein. The threads can be round on the outside or, as for example in FIGS. 10 and 11, profiled on the outside. They can also be designed in any shape on the outside.

Sollen die erfindungsgemässen Fadengebilde in Form ungespaltener Matrix-Segmentfäden eingesetzt werden, ist es vorteilhaft, in der Matrixkomponente das elektrisch leitfähige Pulver zu dispergieren. Insbesondere wenn die erfindungsgemässen Fadengebilde in Form von Filamenten Anwendung finden sollen, ist dieses von besonderem Vorteil, wobei dann auch zweckmässigerweise im Kern des Fadens ein oder mehrere zentrale Segmente angeordnet sind, das bzw. die von den peripheren Segmenten durch das Matrixpolymer, welches das elektrisch leitfähige Pulver enthält, vollständig getrennt sind. Bei einer solchen Anordnung genügen bereits relativ geringe Mengen an leitfähigem Pulver zur Erzielung hoher elektrischer Leitfähigkeit. If the thread structures according to the invention are to be used in the form of uncleaved matrix segment threads, it is advantageous to disperse the electrically conductive powder in the matrix component. This is particularly advantageous if the thread structures according to the invention are to be used in the form of filaments, in which case one or more central segments are also expediently arranged in the core of the thread, that of the peripheral segments through the matrix polymer, which is the electrical component contains conductive powder, are completely separated. With such an arrangement, relatively small amounts of conductive powder are sufficient to achieve high electrical conductivity.

Die Matrix-Segmentmehrkomponenten aus ausgewählten Polymeren mit unterschiedlichem Schrumpfverhalten mit Hilfe von schrumpfauslösenden Mittel zu spalten, ist dann vorteilhaft, wenn die antistatischen Fadengebilde im Gemisch mit anderen, nicht leitfähigen Fasern zu einem Stapelfasergarn verarbeitet werden sollen. Durch die Spaltung werden sehr feintitrige Segmentspaltfäden (beispielsweise ca. 0,1 dtex) erhalten, die im Stapelfasergarn so weitgehend von den übrigen, das Garn bildenden Fasern mit Einzeltitern von beispielsweise 8 dtex bedeckt werden, dass sie für das Auge unauffällig bleiben und der Eindruck eines gleichmässig gefärbten oder weissen Garnes entsteht. Splitting the matrix segment multicomponent from selected polymers with different shrinking behavior with the aid of shrinking agents is advantageous if the antistatic thread structures are to be processed into a staple fiber yarn in a mixture with other, non-conductive fibers. The splitting gives very finely divided segment split threads (for example approx. 0.1 dtex) which are so largely covered in the staple fiber yarn by the other fibers forming the yarn with individual titers of 8 dtex, for example, that they remain inconspicuous to the eye and the impression of an evenly dyed or white yarn.

Erfindungsgemässe Fadengebilde lassen sich nach bekannten Verfahren, beispielsweise nach dem in der deutschen Patentanmeldung P 28 03 136.9 beschriebenen Verfahren und mit den dort beschriebenen Vorrichtungen, herstellen. In der deutschen Patentanmeldung P 28 09 346.1 wird ein Verfahren beschrieben, welches sich auch für erfindungsgemässe Fadengebilde eignet, wenn die Mehrkomponentenfäden gespalten werden sollen. Thread structures according to the invention can be produced by known methods, for example by the method described in German patent application P 28 03 136.9 and with the devices described there. German patent application P 28 09 346.1 describes a method which is also suitable for thread structures according to the invention if the multi-component threads are to be split.

Dort werden Lehren für die Auswahl der Polymeren und für die Durchführung der Spaltung gegeben, die auch im Rahmen der vorliegenden Erfindung Gültigkeit haben. There are teachings for the selection of the polymers and for carrying out the cleavage, which are also valid in the context of the present invention.

Für die hohe Wirksamkeit der erfindungsgemässen antistatischen Fadengebilde ist offensichtlich der Umstand verantwortlich zu machen, dass die leitfähigen Polymeranteile bis an die Fadenoberfläche reichen. Enthält beispielsweise die Matrixkomponente leitfähigen Russ, und ist diese beispielsweise als drei- oder vierzackiger Stern mit engen Strahlen im Innern der Mehrkomponentenfaser angeordnet, dann ist lediglich auf einem sehr geringen Teil des Fadenumfanges Kontakt der leitfähigen Matrixkomponente mit der Oberfläche vorhanden, der aber bereits ausreicht, dass die Wirk- The fact that the conductive polymer components extend to the thread surface is obviously responsible for the high effectiveness of the antistatic thread structures according to the invention. If, for example, the matrix component contains conductive carbon black, and if it is arranged, for example, as a three- or four-pointed star with narrow rays inside the multi-component fiber, then only a very small part of the thread circumference has contact of the conductive matrix component with the surface, which is already sufficient, that the active

3 3rd

s s

10 10th

15 15

20 20th

25 25th

30 30th

35 35

40 40

45 45

50 50

55 55

60 60

65 65

641845 641845

samkeit in unerwartet hohem Masse verstärkt ist, wobei andererseits der Russ optisch kaum in Erscheinung tritt. unexpectedly increased, while on the other hand the soot hardly appears.

Als Russ kommen die im Handel erhältlichen elektrisch leitfähigen Russorten in Betracht, sofern sie eine für die erfindungsgemässen Fadengebilde ausreichende Dispersität aufweisen, d.h. dass ihre maximale Teilchengrösse weniger als 0,035 jorn beträgt. The commercially available electrically conductive types of soot come into consideration as soot, provided they have sufficient dispersity for the thread structures according to the invention, i.e. that their maximum particle size is less than 0.035 jorn.

Geeignete Russorten sind solche mit einer DBP-Absorp-tion von mehr als 120 ml/100 g Russ, beispielsweise derartige Acetylenrusse. Die DBP-Zahl ist der Netzpunkt mit Dibu-tylphthalat, der in einem Spezialkneter nach ASTM D 2414-25 T bestimmt wird und eine Masszahl für die Russstruktur darstellt. Suitable types of soot are those with a DBP absorption of more than 120 ml / 100 g of soot, for example such acetylene blacks. The DBP number is the network point with dibutyl phthalate, which is determined in a special kneader according to ASTM D 2414-25 T and represents a measure of the soot structure.

Russorten mit einer DBP-Absorption von 200 ml/100 g Russ und darüber hinaus sind besonders gut geeignet, weil es sich dabei um hochleitfähige Russe handelt. Im Rahmen der vorliegenden Erfindung führen die hochleitfähigen Russe zu guten elektrischen Leitfähigkeiten der Fäden. Soot varieties with a DBP absorption of 200 ml / 100 g soot and beyond are particularly suitable because they are highly conductive soot. In the context of the present invention, the highly conductive Russian leads to good electrical conductivities of the threads.

Der Gehalt an Russ kann zwischen 12 und 45 Gew.-%, bezogen auf das Gesamtgewicht des Russ-Polymergemisches liegen. Bevorzugt werden Russgehalte zwischen 20 und 35 Gew.-%. The carbon black content can be between 12 and 45% by weight, based on the total weight of the carbon black polymer mixture. Soot contents between 20 and 35% by weight are preferred.

Der Russ kann in die Polymerschmelze in der von der Pigmentierung von synthetischen Polymeren her bekannten Weise eingemischt werden. Es kann auch zweckmässig sein, den Russ bereits vor bzw. während der Polymerisation dem Polymerisationsansatz zuzusetzen. In beiden Fällen ist eine gute Dispersität erreichbar, die sich auch in einer guten Leitfähigkeit bei relativ geringer Russmenge auswirkt. The carbon black can be mixed into the polymer melt in the manner known from pigmentation of synthetic polymers. It may also be expedient to add the carbon black to the polymerization batch before or during the polymerization. In both cases, good dispersity can be achieved, which also results in good conductivity with a relatively small amount of soot.

Die erfindungsgemässen antistatischen Fadengebilde können ganz oder teilweise aus Mehrkomponentenfäden bestehen, deren eine Komponente ein Polymerisat ist, The antistatic thread structures according to the invention can consist wholly or partly of multi-component threads, one component of which is a polymer,

welches elektrisch leitfähigen Russ dispergiert enthält. Neben den Mehrkomponentenfäden können also auch andere Faden- bzw. Faserarten vorliegen, die nicht leitfähig sind, wie beispielsweise übliche Monokomponentenfäden bzw. -fasern aus Polyamid, Polyester und dergleichen. Für ein Teppichgarn reicht es beispielsweise aus, zum üblichen Teppichgarn weniger als 3% der russhaltigen Mehrkomponentenfäden beizumischen, damit der Teppich in hohem Masse gegen elektrostatische Aufladungen geschützt ist. In manchen Fällen genügen bereits wesentlich geringere Mengen. which contains dispersed electrically conductive carbon black. In addition to the multicomponent filaments, other types of filaments or fibers that are not conductive can also be present, such as conventional monocomponent filaments or fibers made of polyamide, polyester and the like. For a carpet yarn, for example, it is sufficient to add less than 3% of the multicomponent threads containing soot to the usual carpet yarn, so that the carpet is protected to a high degree against electrostatic charges. In some cases, much smaller amounts are sufficient.

Die Erfindung wird anhand der nachfolgenden Beispiele näher erläutert. The invention is illustrated by the following examples.

Beispiel 1 example 1

Es werden erfindungsgemässe antistatische Fasern, wie sie in den Figuren 8 und 9 dargestellt sind, mit einer Spinndüse entsprechend der deutschen Patentanmeldung P 28 03136.9 unter sonst üblichen Spinnbedingungen ersponnen, wobei die Matrixkomponente aus einem Polyamid 6 mit 31% Russ mit einer DBP-Absorptions von 125 ml/100 g Russ bestand und als Segment-Komponente ebenfalls Polyamid eingesetzt wurde, welches mit 7% TÌO2 pigmentiert war. Die Flächenverhältnisse Matrixkomponente zu Segmentkomponente betrugen je 1:10 und 1:5. Es wurde mit einer Spinngeschwindigkeit von 1200 m/min gesponnen und anschliessend einstufig mit einem Streckverhältnis von 1:2,6 verstreckt. Antistatic fibers according to the invention, as shown in FIGS. 8 and 9, are spun with a spinneret according to German patent application P 28 03136.9 under otherwise customary spinning conditions, the matrix component being composed of a polyamide 6 with 31% carbon black with a DBP absorption of There was 125 ml / 100 g of carbon black and polyamide, which was pigmented with 7% TÌO2, was also used as the segment component. The area ratios of matrix component to segment component were 1:10 and 1: 5, respectively. It was spun at a spinning speed of 1200 m / min and then drawn in one stage with an aspect ratio of 1: 2.6.

Von den erhaltenen Fäden wurde der spezifische Durchgangswiderstand nach DIN 54345 bei einer Einspannlänge von 5 cm und einer Messpannung von 1 kV bei 21 °C und 25% relativer Luftfeuchtigkeit ermittelt. Die Ergebnisse sind in nachfolgender Tabelle zusammengestellt. The specific volume resistance of the threads obtained was determined in accordance with DIN 54345 with a clamping length of 5 cm and a measuring voltage of 1 kV at 21 ° C. and 25% relative atmospheric humidity. The results are summarized in the table below.

Probe sample

Querschnitt cross-section

Fadentiter Thread titer

Flächen Verhältnis Matrix- zu Segmentfläche Area ratio of matrix to segment area

Spezifischer Durchgangswiderstand Ohm • cm a Volume resistivity Ohm • cm a

Fig. 8 Fig. 8

57 dtexf2 57 dtexf2

1:10 1:10

3,6-10" 3.6-10 "

b b

Fig. 8 Fig. 8

34 dtexf2 34 dtexf2

1: 5 1: 5

1,3 • 108 1.3 • 108

c c

Fig. 9 Fig. 9

55 dtexf2 55 dtexf2

1:10 1:10

9,6-10" 9.6-10 "

d d

Fig. 9 Fig. 9

33 dtexfl 33 dtex

1: 5 1: 5

6,8 • 107 6.8 • 107

Ein nichtleitfähiger Faden aus Polyamid 6 wies im Vergleich dazu unter gleichen Bedingungen einen spezifischen elektrischen Durchgangswiderstand von 5 • IO13 Ohm • cm auf. In comparison, a non-conductive thread made of polyamide 6 had a specific electrical volume resistance of 5 • IO13 Ohm • cm under the same conditions.

Beispiel 2 Example 2

Die Fadenproben c und d aus Beispiel 1 wurden je mit 2 Garnen 1260 dtexf64 zu einem Teppichgarn verarbeitet. Aus den erhaltenen Teppichgarnen wurden Teppiche hergestellt, die einem Begehtest unterworfen wurden. Der Teppich wurde bei 20°C und 25% relativer Luftfeuchtigkeit von einer Prüfperson begangen und dabei die Aufladungsspannung registriert. Die Spannung stieg zunächst auf einen Maximalwert an, der konstant blieb und das Messergebnis bildete. The thread samples c and d from example 1 were each processed with 2 yarns 1260 dtexf64 to a carpet yarn. From the carpet yarns obtained, carpets were produced which were subjected to a walk test. The carpet was walked on by a test person at 20 ° C and 25% relative humidity and the charging voltage was recorded. The voltage initially rose to a maximum value that remained constant and formed the measurement result.

Für den Teppich mit der Fadenprobe c betrug die Aufladung 1,4 kV, während bei der Probe d die Aufladung 1,1 kV betrug. Die an einen antistatischen Teppich gestellten Anforderungen sind damit voll erfüllt worden. For the carpet with thread sample c, the charge was 1.4 kV, while for sample d the charge was 1.1 kV. The requirements placed on an antistatic carpet have thus been fully met.

4 4th

s s

10 10th

15 15

20 20th

25 25th

30 30th

35 35

40 40

45 45

B B

1 Blatt Zeichnungen 1 sheet of drawings

Claims

641 845

2nd

PATENT CLAIMS

1. Antistatic thread structure made of multi-component threads made of at least two synthetic polymer components, of which one component consists of an electrically non-conductive, thermoplastic, thread-forming polymer and another component consists of a thermoplastic polymer with electrically conductive powder dispersed therein, which thread structure at a measuring voltage of 1 kV has a specific volume resistance according to DIN 54 345 of less than IO13 Ohm • cm, characterized in that in the thread cross section through one of the components - the matrix component - at least two segments of the other component or components - the segment component or components - are separated from each other and at least two segments are arranged peripherally.

2. Antistatic thread structure according to claim 1, characterized in that the peripheral segments are completely separated by the matrix component.

3. Antistatic thread structure according to claim 2, characterized in that at least 6 segments are arranged peripherally.

4. Antistatic thread structure according to claim 3, characterized in that at least 12 segments are arranged peripherally in the thread cross section.

5. Antistatic thread structure according to one of the claims

1 to 4, characterized in that at least 20% of the circumference of the peripheral segments are not surrounded by the matrix component.

6. Antistatic thread structure according to claim 5, characterized in that about 50% of the circumference of the peripheral segments are not surrounded by the matrix component.

7. Antistatic thread structure according to one of claims 1 to 6, characterized in that the part of the segment circumference of the peripheral segments surrounded by the matrix component has a convex, essentially round shape.

8. Antistatic thread structure according to one of claims 1 to 6, characterized in that the part of the segment circumference of the peripherally arranged segments surrounded by the matrix has an irregular, optionally jagged shape.

9. Antistatic thread structure according to one of claims 1 to 8, characterized in that the peripheral segments are arranged symmetrically in the thread cross section.

10. Antistatic thread structure according to claim 8, characterized in that the peripheral segments are not arranged symmetrically in the thread cross section.

11. Antistatic thread structure according to one of claims 1 to 10, characterized in that in the thread cross-section in addition to the peripheral segments there is also a centrally arranged segment made of the same or a third polymer which is completely separated from the peripheral segments by the matrix polymer.

12. Antistatic thread structure according to one of claims 1 to 11, characterized in that the thread cross section contains further segments completely surrounded by the matrix component in a regular or irregular arrangement.

13. Antistatic thread structure according to one of claims 1 to 12, characterized in that the matrix component consists of a thermoplastic, synthetic polymer with electrically conductive powder dispersed therein.

14. Antistatic thread structure according to one of claims 1 to 12, characterized in that the segment component or one of the segment components consists of a thermoplastic, synthetic polymer with electrically conductive powder dispersed therein.

15. Antistatic thread structure according to claim 13 or 14, characterized in that the electrically conductive powder is an electrically conductive carbon black.

16. Antistatic thread structure according to claim 15, characterized in that the carbon black is a highly conductive carbon black.

17. Antistatic thread structure according to claim 16, characterized in that the carbon black content is 12 to 45% by weight, based on the total weight of the carbon black polymer mixture.

18. Antistatic thread structure according to claim 17, characterized in that the content of carbon black is 20 to 35 wt .-%.

19. Antistatic thread structure according to claim 18, characterized in that the particle size of the carbon black is less than 0.035 µm.

20. Antistatic thread structure according to one of claims 1 to 19, characterized in that the matrix component and segment component are polyamides.

21. Antistatic thread structure according to claim 20, characterized in that the matrix component and segment component are polyamides with different shrinkage behavior.

22. Antistatic thread structure according to one of claims 20 to 21, characterized in that the matrix component and / or the segment component are copolyamides.

23. Antistatic thread structure according to one of claims 1 to 19, characterized in that one component is a polyamide and one component is a polyester or copolyester.

24. Antistatic thread structure according to one of claims 1 to 23, characterized in that the area of the conductive component in the thread cross section is at least 5% of the total area.

25. Antistatic thread structure according to one of claims 1 to 24, characterized in that the multi-component threads are split into segments and matrix.

26. Antistatic thread structure according to claim 25, characterized by matrix and segment fibers of finite length in a random arrangement with different curvature, the segment fibers being more strongly curved than the matrix fibers.

27. Antistatic thread structure according to claim 26, characterized by fixed areas with uncleaved multi-component fiber components.

28. Antistatic thread structure according to claim 27, characterized by compressed, regularly arranged fixed areas.

29. Antistatic thread structure according to one of claims 1 to 24, characterized by a complete and / or partial cleavage in matrix fibers and segment fibers, wherein the only partially split multicomponent fibers still have a mechanical cohesion of the matrix and segment portions and in part slots between the matrix and have segment fibers and in some cases only have longitudinal grooves at the edge of the multi-component thread in accordance with the phase boundaries.