CA2487486A1 - Fluoropolymer interlayer dielectric by chemical vapor deposition - Google Patents

Fluoropolymer interlayer dielectric by chemical vapor deposition Download PDF

Info

Publication number
CA2487486A1
CA2487486A1 CA002487486A CA2487486A CA2487486A1 CA 2487486 A1 CA2487486 A1 CA 2487486A1 CA 002487486 A CA002487486 A CA 002487486A CA 2487486 A CA2487486 A CA 2487486A CA 2487486 A1 CA2487486 A1 CA 2487486A1
Authority
CA
Canada
Prior art keywords
fluoromonomer
thin film
film device
gas phase
polymerization initiator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
CA002487486A
Other languages
French (fr)
Inventor
Michael Mocella
Andrew E. Feiring
Theodore A. Treat
Eugene Lopata
Peter Rose
Yakov Brichko
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EIDP Inc
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of CA2487486A1 publication Critical patent/CA2487486A1/en
Abandoned legal-status Critical Current

Abstract

A process is disclosed for forming a fluoropolymer layer on a thin film device, comprising contacting said thin film device with a gas phase fluoromonomer, and initiating polymerization of said fluoromonomer with a fr ee radical polymerization initiator whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.

Description

TITLE
FLUOROPOLYMER INTERLAYER DIELECTRIC
BY CHEMICAL VAPOR DEPOSITION
BACKGROUND OF THE INVENTION
Modern electronic thin-film devices use layers of conductors and insulators_as the current-carrying structures of such devices. The dielectric (insulator) layers are often composed of silicon-containing materials such as silicon dioxide and silicon nitride. As the requirements of such devices become more demanding, there is a need for improved dielectric materials, having lower dielectric constants compared to the silicon-containing materials.
Fluoropolymers can have excellent dielectric properties. However, the methods to deposit thin films of such polymers are limited. In certain cases, the polymers can be made soluble in selected solvents, and so thin films can be formed by processes commonly used for, e.g. photoresist materials. However, the attributes of the polymer to produce solubility may not be the most desirable ones for dielectric applications. In other cases, emulsions or slurries of fine polymer particles can be applied to the device, and films produced by removing the solvent carrier and then heat treating the particles to produce a film. However, forming a uniform film by such methods with the desired properties may not be straightforward.
Therefore, it would be desirable to have alternative methods to form the fluoropolymer layers. In particular, thin-film-processing industries frequently use chemical vapor deposition methods to deposit the present dielectric materials It would thus be particularly desirable to have chemical vapor deposition means for fluoropolymer dielectric deposition.

SUMMARY OF THE INVENTIION
A process for forming a fluoropolymer layer on a thin film device has been discovered comprising:
a.) contacting said thin film device with a gas phase fluoromonomer, and b.) initiating polymerization of said fluoromonomer with a free radical polymerization initiator, whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.
A process for forming a fluoropolymer layer on a thin film device has been discovered comprising:
a.) delivering a gas phase fluoromonomer to said thin film device b.) contacting said thin film device with said gas phase fluoromonomer, and c.) initiating polymerization of said fluoromonomer with a free radical polymerization initiator, whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.
A process for forming a fluoropolymer layer on a thin film device has been discovered comprising:
a.) delivering a gas phase fluoromonomer and a gas phase free radical polymerization initiator to said thin film device, b.) mixing said gas phase fluoromonomer and said gas phase free radical polymerization initiator to form a gas phase mixture of said fluoromonomer and said free radical polymerization initiator, c.) contacting said thin film device with said gas phase mixture of said fluoromonomer and said free radical polymerization initiator, and d.) initiating polymerization of said fluoromonomer with said free radical polymerization initiator, whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.
DETAILED DESCRIPTION
The present invention is a process for forming a fluoropolymer layer on a thin film device, comprising contacting said thin film device with a gas phase fluoromonomer and initiating polymerization of said fluoromonomer with a free radical polymerization initiator, whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.
Fluoropolymers comprising the fluoropolymer layers formed by the present process are comprised of repeating units from fluoromonomers defined herein and may have a number averaged molecular weight of over 10,000.
Fluoropolyrner layers produced by the process of the present invention have a uniform thickness and are typically from about 500 angstroms to about 50,000 angstroms thick.
Thin film devices on which fluoropolymer layers may be formed by the present process comprise devices known in the microelectronics industry as semiconductor wafers, integrated circuits, flat panel displays, micromechanical devices, microelectrical mechanical systems, and thin film optical and optoelectrical devices. The surface of such thin film devices on which a fluoropolymer layer may be formed by the present process include: silicon;
silicon dioxide; silicon nitride; silicon oxynitride; silicon carbide; "carbon doped"
oxides (e.g. spin-on materials such as HSQ and MSQ, as well as CVD materials such as CoralTM and Black DiamondTM); phosphosilicate, borosilicate and borophosphosilicate glass; polyimides; aluminum; copper; tungsten; molybdenum;
titanium; tantalum; silicides and nitrides of aluminum, copper, tungsten, molybdenum, titanium and tantalum; and conductive alloys of aluminum, copper, tungsten, molybdenum, titanium, and tantalum, including aluminum doped with copper and/or silicon.
Fluoromonomers useful in the present process for forming fluoropolymer layers contain caxbon-carbon unsaturation and may include the elements carbon, fluorine, hydrogen, oxygen, nitrogen, sulfur and phosphorous. The fluoromonomers preferably comprise the elements carbon, fluorine and oxygen and most preferably comprise the elements caxbon and fluorine. A mixture of fluoromonomers may be used in the present process to produce co-, ter- or tetra-fluoropolymers. The fluoromonomers are preferably homopolymerizable, but non-homopolymerizable fluoromonomers may be used together with homopolymerizable fluoromonomers to modify the properties of the fluoropolymer layer.
Homopolymerizable fluoromonomers of the present invention include:
fluoroethylenes represented by the formula CaHXF~4-X>, wherein x is from 0 to 3, fluorodioxoles represented by the formula cyclo-[-(C(Rl)(R2))XOCF=CFO-] wherein x is 1 or 2, and Rl and Ra are independently selected from fluorine (F) and lineax and branched, saturated perfluoroalkane radicals represented by the formula -CXF(aX+i>, wherein x is from 1 to 5, fluoro-1,3-dioxolanes represented by the formula cyclo-[-G(=CF2)OC(F)(Rl)CF20-], and wherein Rl is selected from fluorine (F) and linear and branched, saturated perfluoroalkane radicals represented by the formula -CXF~2X+i>, wherein x is from 1 to 5, fluorodienes represented by the formula CF2=CFO(C(F)(Rl))XCF=CF2 wherein x is from 1 to 5, and wherein Rl is selected from fluorine (F) and linear and branched, saturated perfluoroalkane radicals represented by the formula -CXF~2X+i>, wherein x is from 1 to 5, and fluorovinyl hydrofluoroalkyl ethers represented by the formula CF2=CFOCH2R1, wherein Rl is hydrogen (H) or linear and branched, saturated radicals represented by the formula -CXHyF~2X+1-y> wherein x is from 1 to 5 and y is from 0 to 2x+1.
Specific examples of homopolymerizable fluoromonomers of the present invention include: CFa=CF2, CFa=CFH, CFa=CHI, cis- or traps-CFH=CFH, CFH=CH2, cyclo-[-CFZOCF=CFO], cyclo-[-CF2CF20CF=CFO], cyclo-[-C(F)(CF3)OCF=CFO], cyclo-[-C(CF3)(CF3)OCF=CFO], cyclo-[-C(CF3)(CaFs)OCF=CFO], cyclo-[-C(CaFs)(C2F5)OCF=CFO], cyclo-[-C(=CFa)OCF2CF20], cyclo-[-C(=CFa)OC(F)(CF3)CFaO], cyclo-[-C(=CF2)OC(F)(CZFS)CF20], CFa=CFOCFaCF=CF2, CFa=CFOCF(CF3)CF=CFa, CF2=CFOCF2CFaCF=CF2, CF2=CFOCF(CF3)CF2CF=CF2, CF2=CFOCFaCF(CF3)CF=CFa, CF2=CFOCH2CF3, CF2=CFOCHaC2F5, and CF2=CFOCH2CF2CF2CF3.
The preferred fluoromonomer used in the present process is CFa=CFA, (tetrafluoroethylene). Tetrafluoroethylene is preferably used in the present process as a mixture of CF2=CF2 and COa, a composition which allows for safe transport and handling of CF2=CFa, and which is described by Van Bramer et al. in U.S.
5,345,013, incorporated herein by reference. A preferred mixture of CF2=CF2 and C02 used in the present process comprises equal weights of CF2=CFa and COa.
Non-homopolymerizable fluoromonomers of the present invention include:
perfluoroalkenes represented by the formula CF2=CFRI, wherein Rl is selected from linear and branched, saturated perfluoroalkane radicals represented by the formula -CXF~2X+i> wherein x is from 1 to 5, perfluoroalkyl perfluorovinyl ethers represented by the formula FCC=CFORI, wherein Rl is selected from linear and branched, saturated perfluoroalkane radicals represented by the formula -CXF~2X+i> wherein x is from 1 to 5, functionalized perfluorovinyl ethers represented by the formula F~,G=CFO(CF2)xRl or F2C=CFOGFaCF(CF3)O(CF~)XRI, wherein x is from 1 to 3 and Rl is -CH20P(=O)(OH)2, -CH20H, -CH20CN, -CN, -C(=O)OCH3 and -S02F, and perfluorodivinyl ethers represented by the formula CF2=CFO(G(F)(Rl))XOCF=GFa, wherein x is from 1 to 5 and Rl is selected from fluorine (F) and linear and branched, saturated perfluoroalkane radicals represented by the formula -CXF~aX+y wherein x is from 1 to 5.
Examples of non-homopolymerizable fluoromonomers of the present invention include: CF2=CFCF3, CFa=CFC2F5, GFa=CFOCF3, GF2=CFOGaFs, FaC=CFOCF2CF(CF3)OCFaCFaCH20P(=O)(OH)2, F2C=CFOCFaCF(CF3)OCF2CF2CHaOH, F2C=CFOCFaCF(CF3)OCFaCFaCH20CN, F2C=CFOCF2CF(CF3)OCF2CF2CN, F2C=CFOCF2CF(CF3)OCF~CF2C(=O)OCH3, FaC=CFOCFaCF(CF3)OGF2CF2SOaF, F2C=CFOCFaCF(CF3)OCFaGF2CF2SOaF, F2C=CFOCF2GF2SO2F, CF2=CFOGF2CF2CF3, GFZ=CFOCFaOCF=GF2, CF2=CFOCF(CF3)OGF=CF2, CFa=CFOCFaCF2OGF=CF2, and CFa=CFOCF(CF3)CF20CF=CF2.
Free radical polymerization initiators of the present process comprise initiators that can form free radicals which initiate polymerization of the fluoromonomer and result in formation of a fluoropolymer layer on the thin filin , device. Initiators are preferably delivered to the thin film device in the gas phase, however it is contemplated that initiators may be present on, or integral with, the surface of the thin film device.
Free radical polymerization initiators of the present process include peroxides, saturated alkyl halides, haloalkenes, halogens and inorganic halides.
Peroxide initiators of the present invention contain at least one peroxide functional group (-00-) and may be represented by R10OR2, wherein Rl and R2 are independently selected from saturated hydrocarbon radicals which may further comprise halogen, oxygen and nitrogen atoms. Hydrocarbon peroxides such as di-t-butylperoxide may be used as initiator in the present process.
Perfluorodiacyl peroxides wherein RI and R2 are RFC(=O)- and RF is a perfluorocarbon radical which may contain oxygen, may be used as initiator in the present process.
Preferred of the perfluorodiacyl peroxide initiators are those produced from hexafluoropropylene oxide, such as (CF3CFaCFaOCF(CF3)C02)a.
Saturated alkyl halide initiators of the present process may be represented by R-X wherein X is a halogen, preferably fluorine, and R is a hydrocarbon radical, and preferably branched (a secondary or tertiary radical). Preferably R is fluorinated and more preferably R is perfluorinated. Saturated alkyl halide initiators include, for example, perfluorotetramethyl butane CF3(C(CF3)a)aCF3 as well as perfluorocarbon iodides such as F(C2F4)XI, wherein x is from 1-4.
Haloalkene initiators of the present invention are represented by RIR2C=CR3R4, wherein Rl through R4 are independently selected from hydrogen;
halogen; alkyl radicals substituted with hydrogen, halogen and heteroatoms such as oxygen and nitrogen; and ether radicals represented by -OR, wherein R is an alkyl radical substituted with hydrogen, halogen and heteroatoms such as oxygen and nitrogen. Preferably, at least one of Rl through R4 is fluorine. In one embodiment of the present process, fluoromonomer acts as the free radical polymerization initiator under the conditions that the fluoromonomer is contacting the thin film device. In such an embodiment, tetrafluoroethylene (CF2=CF2) may be used as the fluoromonomer, and perfluoroalkyl vinyl ethers such as perfluoropropyl perfluorovinyl ether (CF2=CFOCF2CF2CF3) may be used as a free radical polymerization initiator. Without wishing to be bound by theory, it is believed that in this embodiment a small portion of fluoromonomer thermally decomposes under the conditions that the fluoromonomer is contacting the thin film device and forms free radical species which initiate polymerization of the fluoromonomer.
Halogen initiators of the present invention include molecular fluorine, chlorine, bromine and iodine. Fluorine, especially fluorine highly diluted in an inert gas such as nitrogen, is preferred among the halogen initiators.
Inorganic halide initiators of the present invention include nitrogen trifluoride and sulfur hexafluoride.
The present invention is a process for forming a fluoropolymer layer on a thin film device, and in part involves contacting said thin film device with a gas phase fluoromonomer.
The total pressure during contacting of the gas phase fluoromonomer with the thin film device is not critical and may be from about 101 kPa (1 atmosphere) to about 10.1 kPa (0.1 atmosphere) and preferably from about 101 kPa to about kPa. The total pressure may partly comprise the partial pressures of carrier, purge, and other process gases such as nitrogen, carbon dioxide and noble gases. In a preferred embodiment of the present process, the free radical polymerization initiator is in the gas phase and is reacted with the gas phase fluoromonomer at or near the surface of the thin film device and thus contributes to the total pressure.
The mole ratio of free radical polymerization initiator to fluoromonomer necessary to initiate and maintain an acceptable rate of polymerization of fluoromonomer is not critical and depends on a number of parameters (e.g. the contacting conditions, the chemical constitution of the fluoromonomer and free radical polymerization initiator used, the desired properties of the fluoropolymer layer) but is generally from about 1:100 to 1:100,000.
The temperature during contacting of the gas phase fluoromonomer with the thin film device is not critical and is generally maintained from about 20°C to about 500°C and preferably maintained from about 300°C to about 500°C.
The present invention is a process for forming a fluoropolymer layer on a thin film device, and in part involves initiating polymerization of fluoromonomer with free radical polymerization initiator. Without wishing to be bound by theory, it is believed that fluoromonomer polymerizes on the surface of the thin film device by a free radical, chain propagation mechanism initiated by free radicals arising from bond homolysis in the free radical polymerization initiator under the described contacting conditions.
In an embodiment of the present process where the free radical polymerization initiator is in the gas phase, the process involves mixing the gas phase fluoromonomer and gas phase free radical polymerization initiator to form a gas phase mixture of fluoromonomer and free radical polymerization initiator.
Mixing of the gases may occur by any process, but preferably occurs by diffusion following the direction of gaseous streams of the fluoromonomer and initiator into the same volume. Mixing may be controlled to occur prior to or during contacting of the gases with the thin film device.
In a preferred embodiment of the present process, gas phase fluoromonomer and gas phase free radical polymerization initiator may be delivered to the surface of the thin film device by chemical vapor deposition means. The gases are distributed over the surface of the thin film device so that the fluoromonomer and radicals formed from the free radical polymerization initiator react and form a fluoropolymer layer on the surface of the device.
The function of the chemical vapor deposition means is to distribute the gases to the surface of the thin film device in a substantially controlled manner. The chemical vapor deposition means preferably provides a substantially controlled flow profile of gases at a controlled flow rate to a particular surface area of the thin film device. The chemical vapor deposition means may also contain features which allow for control of premixing and reaction of the gases prior to their contacting the thin film device. Controlled distribution of the gases promotes complete, efficient and homogeneous reaction of the gases at the surface of the thin film device. Such controlled distribution provides for greater control over the properties and quality of the resultant fluoropolymer layer. For example, such controlled distribution results in uniformity of important fluoropolymer layer properties such as thickness and dielectric constant over large diameter, thin film devices. When the fluoropolymer layer is not of uniform composition and thickness, the proper functioning or further functionalization of the thin film device may be impaired.
In a preferred embodiment of the invention, the present process may be carried out using chemical vapor deposition means having a linear injector as taught by DeDontney et al. in U.S. Patent No. 5,683,516, herein incorporated by reference. The linear injector comprises an elongated member with end surfaces and at least one gas delivery surface extending along the length of the member and which includes a number of elongated passages formed therein. Also formed within the member are a number of thin distribution channels which extend between the elongated passages and the gas delivery surface. In another configuration of linear injector, a number of metering tubes may be inserted into each elongated passage and are spaced from the walls of said passages and extend between the ends. The metering tubes may contain openings of varying form and dimension which may be directed away from the distribution channels. The metering tubes receive a gas which is, conveyed along the metering tubes, whereby the gas flows out of the openings, and is conveyed through the corresponding distribution channel and is directed in a substantially controlled manner along the length of the gas delivery surface. In the instance where a number of gases such as fluoromonomer and free radical polymerization initiator are employed, the distribution channels direct the distribution of such gases to a controlled region on the surface of a thin film device where mixing of the gases is desired. In addition the distribution channels prevent potential chemical fouling of the injector by preventing premature reaction of gases which are particularly reactive under the chosen contacting conditions. The gases axe directed to a desired region above or on the thin film device where they mix, react and form a uniform fluoropolymer layer on the thin film device positioned beneath the injector.
In another embodiment of the invention, the present process may be carried out using chemical vapor deposition means having an annular injector as taught by Young et al. in U.S. Patent No. 5,851,294, herein incorporated by reference. The annular injector comprises a plenum body having at least one plenum formed therein and a plurality of nozzles for injecting fluoromonomer and initiator gases into a processing chamber. The nozzles are spaced from the plenum and are positioned and configured to provide a uniform distribution of gases across the thin film device where they mix, react and form a uniform fluoropolymer layer on the thin film device.
In another embodiment of the present process, the process of the present invention may be caxried out in a contoured plate reactor as taught by Mahawill in U.S. Patent No. 4,834,022, herein incorporated by reference. The contoured plate reactor is approximately cylindrical in shape. The base of the 'reactor is inclined at an angle of approximately 3°-5° from the vertical and has a central platform with a recessed well. The thin film device is placed in the well so that the surface of the device on which the fluoropolymer is deposited does not protrude above the platform surface. The fluoromonomer and initiator gases are mixed in a region adjacent the cylindrical wall of the reactor and flow radially inward across the device surface where they mix, react and form a unifornl fluoropolymer layer on the thin film device.
In another embodiment of the invention, the present process is carried out in a sub-atmospheric pressure tool using a MultiblockTM injector as taught in Miller and Dobkin, U.S. Patent No. 6,022,414 (Figure 18), herein incorporated by reference. The advantage of this type of injector is that it has a plurality of injector members and vent members to increase throughput in a production CVD
tool.
EXAMPLES
In the following examples: slm refers to standard liters per minute; sccm refers to standard cubic centimeters per minute.

Polytetrafluorethylene (PTFE) film was deposited on an 8" diameter, 750 pm thick, P-doped silicon wafer from Wafer Net, Inc. (San Jose, CA, USA), using an atmospheric pressure CVD tool.
A Monoblok~ (Monoblok is a trade mark of ASML Thermal Division, Scoffs Valley, CA, USA) linear injector as described in U.S. patent no.
5,683,516 was used to apply laminar reactant and initiator gas flows at a precisely metered rate to the wafer surface as it moved on a conveyor belt under the injector body through a heated, horizontal tunnel (muffle).
In this example, an equal weight mixture of tetrafluoroethylene (TFE) and COZ at a flow rate of 8 slm was flowed through the separator ports of the Monoblok~ linear injector while di-tert-butylperoxide (tbpo) vapor was delivered to the center port of the injector using a liquid bubbler system. The tbpo vapor stream comprised about 5 sccm tbpo vapor achieved by flowing NZ gas at a controlled flow rate of 50 sccm through a bubbler containing tbpo at room temperature.
The injector-conveyor belt spacing was 11 mm, the muffle setpoint temperature was 400 °C, and the belt speed was 0.5 inch per minute (ipm).
A PTFE film of average thickness 3,645 t~ was deposited on the wafer. C-V
plots ~a 1 MHz gave a dielectric constant ('k') = 2.2, while thermal oxide "control"
wafers had k = 4Ø

PTFE film was deposited at atmospheric pressure using a Monoblok~linear injector using F2 as the initiator. In this case, a commercially available 5% F2 in N2 mixture was used. In order to achieve appreciable flows through the injector, this low flow of F2 in N~ was diluted with an additional flow of Na (called Dl N2). Eight slm of a gas being an equal weight mixture of tetrafluoroethylene (TFE) and CO~ was metered into the center (inner) port, the outer ports had 50 sccm of 5% F2 in N2 + 7.95 slm of D1 N~ flow, and the separator ports of the MonoblokTM linear inj ector had 16 slm of Na flow. The muffle was heated to a 250 °C setpoint, sufficient to thermally crack molecular fluorine into atomic F. The belt speed was 0.5 ipm.
ESCA analysis was performed on the PTFE thin film deposited on the wafer. The elemental composition proved to be 31.4% C and 68.6%F.
The 2:1 ratio of F:C is indicative of polytetrafluorethylene. No other elements were detected by ESCA. Moreover; chemical shifts indicated that all the fluorine was bonded to C atoms, and carbon was bonded either to other carbon atoms or to fluorine atoms, as expected for PTFE.

In this example PTFE was deposited using NF3 as the initiator. Thermal cracking of NF3 requires temperatures over 700 °C to generate atomic F
radicals.
A heater was located upstream of the injector to heat the incoming NF3 to temperatures >700 °C. Although built in-house, this heater was similar in construction to the commercially available Watlow StarflowTM Heater. The atomic F generated by this heat reacted with the TFE gas coming out of the injector slot to cause polymerization at the wafer surface.
Details of this experiment follow: TFE flow rate = 5 slm through the inner port, 50 sccm of NF3 + 1.00 slm of D 1 N2 flowed through the outer ports, while 1.00 slm of separator Na came through the separator ports of the Monoblok~linear injector. The upstream heater was set @ 740 °C, while the muffle setpoint was 500 °C.
In this case, a static deposition was done with the wafer stalled under the injector for a total time of 20 minutes. This experiment resulted in an average thickness of 174 tgr and a maximum thickness of 1194 A.

This example of PTFE deposition using an atmospheric pressure chemical vapor deposition (APCVD) tool with a Monoblok~linear injector used 30% H2O2 in a bubbler for initiation of the proprietary TFE gas mixture. In this case, 4.4 slm of TFE is controllably flowed through the center port, 1.2 slm of bubbler Na is flowed through the outer ports (with entrained HZOa), 1.0 slm of separator N2 is used. The muffle setpoint was 500 °C, and a 60 minute static deposition was done. A PTFE film was deposited, with maximum thickness of 2575 A and a refractive index (n) = 1.376 as measured on a Rudolph spectroscopic ellipsometer.

In this example PTFE film was deposited at atmospheric pressure using Trigonox-CTM as the initiator. This is a product of Akzo Nobel Polymer Chemicals LLC. A Monoblok~ linear injector was used. A gas being an equal weight mixture of tetrafluoroethylene (TFE) and C02 was flowed at a rate of 8 slm through the separator ports of the linear injector while a liquid bubbler system using N2 gas as a carrier at 3 slm brought Trigonox-C~'through the center port of the injector.
The injector-conveyor belt spacing was 11 mm, the muffle setpoint temperature was 400 °C, the belt speed was 0.25 ipm, and the exhaust setpoint was 0.25 in. HZO. A single pass through the deposition zone resulted in a coating of 3005 t~ and a refractive index (n) =1.37.

In order to demonstrate the effect of line speed on the PTFE deposition, an experiment similar to Example #1 was performed, except that the line speed was increased to 1 inch per minute, the exhaust setpoint was 0.25, and a total of passes were done to compensate for the reduced residence time in the deposition zone. A film of 1844 ~ was deposited at this higher line speed; furthermore, the film quality (as measured by the Rudolph spectroscopic ellipsometer goodness-of fit) was improved over that produced at lower line speeds.

In this example, an APNextTM (APNext is a trademark of ASML Thermal Division, Scotts Valley, CA, USA) subatmospheric pressure CVD tool was used for depositing a PTFE film. This tool uses a heated vacuum chuck to hold an 8"
silicon wafer while the chuck translates under the fixed injector body to improve film uniformity. A 2x injector was used (2 injectors housed in a single body), and deposition was done at 600 Torr in the process chamber, using the following conditions:
~ "monomer" flow rate (1:1 wt ratio of TFE:C02) =12 slm ~ bubbler N2 flow rate (di-tert-butylperoxide is room temperature initiator) =

sccm ~ chuck temperature = 400 °C
~ chuck translate speed = 0.4 mm/second ~ chuck-injector gap spacing = 6 mm ~ # passes = 1 (deposition time = 27.S~minutes) ~ Na chamber purge = 4 slm ~ N2 ballast flow = 40 slm (into pump foreline) ~ Slot Na purge flow = 8 slm (inner)/4 slin (outer) wafers were coated using the process above, with the following results:
1. Average thickness as deposited = 2731 t~ (1 a = 206 ~) 2. Average refractive index = 1.33 (1 ~ = 0.04) 3. Average thickness after 10' anneal (380 °C, in vacuo) = 2638 ~ (1 a =256 A)

Claims (10)

WHAT IS CLAIMED IS:
1.) A process for forming a fluoropolymer layer on a thin film device, comprising:
a) contacting said thin film device with a gas phase fluoromonomer, and b) initiating polymerization of said fluoromonomer with a free radical polymerization initiator, whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.
2.) A process for forming a fluoropolymer layer on a thin film device, comprising:
a) delivering a gas phase fluoromonomer to said thin film device b) contacting said thin film device with said gas phase fluoromonomer, and c) initiating polymerization of said fluoromonomer with a free radical polymerization initiator, whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.
3.) A process for forming a fluoropolymer layer on a thin film device, comprising:
a.) delivering a gas phase fluoromonomer and a gas phase free radical polymerization initiator to said thin film device, b.) mixing said gas phase fluoromonomer and said gas phase free radical polymerization initiator to form a gas phase mixture of said fluoromonomer and said free radical polymerization initiator, c.) contacting said thin film device with said gas phase mixture of said fluoromonomer and said free radical polymerization initiator, and d.) initiating polymerization of said fluoromonomer with said free radical polymerization initiator, whereby said fluoromonomer polymerizes to form said fluoropolymer layer on said thin film device.
4.) The process of claim 3 wherein the delivering a gas phase fluoromonomer is by chemical vapor deposition means.
5.) The process of claims 1, 2, or 3 wherein the fluoropolymer layer is 500 angstroms to about 50,000 angstroms thick.
6.) The process of claims 1, 2, or 3 wherein the fluoromonomer is selected from the group consisting of fluoroethylenes represented by the formula C2H x F(4-x), wherein x is from 0 to 3, fluorodioxoles represented by the formula cyclo-[-(C(R1)(R2))x OCF=CFO-] wherein x is 1 or 2, and R1 and R2 are independently selected from fluorine (F) and linear and branched, saturated perfluoroalkane radicals represented by the formula -C x F(2x+1), wherein x is from 1 to 5, fluoro-1,3-dioxolanes represented by the formula cyclo-[-C(=CF2)OC(F)(R1)CF2O-], and wherein R1 is selected from fluorine (F) and linear and branched, saturated perfluoroalkane radicals represented by the formula -C x F(2x+1), wherein x is from 1 to 5, fluorodienes represented by the formula CF2=CFO(C(F)(R1))x CF=CF2 wherein x is from 1 to 5, and wherein R1 is selected from fluorine (F) and linear and branched, saturated perfluoroalkane radicals represented by the formula -C x F(2x+1), wherein x is from 1 to 5, and fluorovinyl hydrofluoroalkyl ethers represented by the formula CF2=CFOCH2R1, wherein R1 is hydrogen (H) or linear and branched, saturated radicals represented by the formula -C x F(2x+1) wherein x is from 1 to 5 and y is from 0 to 2x+1.
7.) The process of claims 1, 2, or 3 wherein the fluoromonomer is tetrafluoroethylene.
8.) The process of claims 1, 2, or 3 wherein the free redical polymerization initiator is selected from the group of peroxides, saturated alkyl halides, haloalkenes, halogens and inorganic halides.
9.) The process of claims 1, 2, or 3 wherein the initiating step is performed at a pressure of about 101 kPa to about 10.1 kPa, at a temperature of about 20°C to about 500°C, and a mole ratio of free radical polymerization initiator to fluoromonomer of about 1:100 to about 1:100,000.
10.) The process of claim 4 wherein the chemical vapor deposition means is selected from the group of linear injector, annular injector, a contoured plate reactor, and a sub-atmospheric pressure tool using a Multiblock.TM. injector.
CA002487486A 2002-06-21 2002-06-21 Fluoropolymer interlayer dielectric by chemical vapor deposition Abandoned CA2487486A1 (en)