CA2324628C - Water based adhesion promotor for polypropylene and method for coating to polypropylene materials using the promotor - Google Patents
Water based adhesion promotor for polypropylene and method for coating to polypropylene materials using the promotor Download PDFInfo
- Publication number
- CA2324628C CA2324628C CA002324628A CA2324628A CA2324628C CA 2324628 C CA2324628 C CA 2324628C CA 002324628 A CA002324628 A CA 002324628A CA 2324628 A CA2324628 A CA 2324628A CA 2324628 C CA2324628 C CA 2324628C
- Authority
- CA
- Canada
- Prior art keywords
- polypropylene
- weight
- water
- coating
- promotor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The water base adhesion promotor for polypropylene comprises: a grafted polypropylene chloride, which includes a polypropylene chloride moiety and a maleic anhydride moiety as bonded thereto, and which has a chlorine content of 15~25 weight % and a maleic anhydride moiety content of 1~5 weight %; an amine-neutralized water-soluble resin; a wettability-improving agent; and water; and is characterized by having: a combination ratio of 25~90 weight % as of the grafted polypropylene chloride to the total of the grafted polypropylene chloride and the amine-neutralized water-soluble resin; a combination ratio of 2.5~6.0 weight % as of the wettability-improving agent to the entirety of the promotor; and a solid content of 2~10 weight % of the entirety of the promotor. The method for coating to polypropylene materials comprises: a pretreatment step in which the polypropylene material is beforehand cleaned and then the above water base adhesion promotor is applied, and then dried; and a coating step in which a paint is coated to the material after the pretreatment step.
Description
DESCRIPTION
Water Based Adhesion Promoter for Polypropylene and Method for Coating to Polypropylene Materials Using the Promoter This application is divided out of Canadian Patent Application No. 2,320,276.
TECHNICAL FIELD
The present invention relates to: a water based adhesion promoter for improving the paint adhesion to polypropylene materials; and a method for coating to polypropylene materials using the promoter.
BACKGROUND ART
Polyolefins such as polypropylene are comparatively cheap and has excellent properties such as formability and chemical resistance, so they are widely used in the industrial fields including the automobile industry. The amount thereof as used tends to increase, because their recycling is possible and because their prices are low. Polypropylene materials are, for example, used for exterior decoration parts of automobiles, such as bumpers and molds, and their surfaces are usually coated to both improve their weather resistance and give the design property thereto.
The polypropylene material is inferior in wettability. Therefore, when being coated with a paint, the polypropylene material undergoes the following treatments: first, a degreasing treatment with a water base cleaning agent and a pretreatment to enhance the wettability using a surface-active agent, and then coating and baking treatments of a primer, and then a coating treatment of a paint. Incidentally, the coating treatment of the primer is carried out to enhance the adhesion of paints, but, in fact, as much as about 70 % of the amount of the primer as used is lost during application and therefore is not effectively used, thus resulting in high coating cost. Furthermore, there are problems in that:
the primer needs to be baked after being coated, so a large baking furnace is needed and the equipment cost is therefore high.
From the above circumstances, it is desired to develop a method for coating to polypropylene materials without primer coating.
DISCLOSURE OF THE INVENTION
An object of the present invention is to provide: a water base adhesion promotor to enhance the paint adhesion to polypropylene materials instead of the primer coating; and a method of coating to polypropylene materials using the promotor.
SUMMARY OF THE INVENTION
The present inventors made various examinations and experiments to solve the above problems. As a result, they attained the present invention by finding that: a composition, comprising a grafted polypropylene chloride of high adhesion to polypropylene materials, an amine-neutralized water-soluble resin of high water resistance, and a wettability-improving agent, could enhance the paint adhesion to polypropylene materials, so that the primer coating could be omitted.
That is to say, a water base adhesion promotor for polypropylene, according to the present invention, comprises:
a grafted polypropylene chloride, which includes a polypropylene chloride moiety and a malefic anhydride moiety as bonded thereto, and which has a chlorine content of 1525 weight % and a malefic anhydride
Water Based Adhesion Promoter for Polypropylene and Method for Coating to Polypropylene Materials Using the Promoter This application is divided out of Canadian Patent Application No. 2,320,276.
TECHNICAL FIELD
The present invention relates to: a water based adhesion promoter for improving the paint adhesion to polypropylene materials; and a method for coating to polypropylene materials using the promoter.
BACKGROUND ART
Polyolefins such as polypropylene are comparatively cheap and has excellent properties such as formability and chemical resistance, so they are widely used in the industrial fields including the automobile industry. The amount thereof as used tends to increase, because their recycling is possible and because their prices are low. Polypropylene materials are, for example, used for exterior decoration parts of automobiles, such as bumpers and molds, and their surfaces are usually coated to both improve their weather resistance and give the design property thereto.
The polypropylene material is inferior in wettability. Therefore, when being coated with a paint, the polypropylene material undergoes the following treatments: first, a degreasing treatment with a water base cleaning agent and a pretreatment to enhance the wettability using a surface-active agent, and then coating and baking treatments of a primer, and then a coating treatment of a paint. Incidentally, the coating treatment of the primer is carried out to enhance the adhesion of paints, but, in fact, as much as about 70 % of the amount of the primer as used is lost during application and therefore is not effectively used, thus resulting in high coating cost. Furthermore, there are problems in that:
the primer needs to be baked after being coated, so a large baking furnace is needed and the equipment cost is therefore high.
From the above circumstances, it is desired to develop a method for coating to polypropylene materials without primer coating.
DISCLOSURE OF THE INVENTION
An object of the present invention is to provide: a water base adhesion promotor to enhance the paint adhesion to polypropylene materials instead of the primer coating; and a method of coating to polypropylene materials using the promotor.
SUMMARY OF THE INVENTION
The present inventors made various examinations and experiments to solve the above problems. As a result, they attained the present invention by finding that: a composition, comprising a grafted polypropylene chloride of high adhesion to polypropylene materials, an amine-neutralized water-soluble resin of high water resistance, and a wettability-improving agent, could enhance the paint adhesion to polypropylene materials, so that the primer coating could be omitted.
That is to say, a water base adhesion promotor for polypropylene, according to the present invention, comprises:
a grafted polypropylene chloride, which includes a polypropylene chloride moiety and a malefic anhydride moiety as bonded thereto, and which has a chlorine content of 1525 weight % and a malefic anhydride
2 moiety content of 1 ~5 weight %;
an amine-neutralized water-soluble resin;
a wettability-improving agent; and water;
and is characterized by having:
a combination ratio of 2590 weight % as of the grafted polypropylene chloride to the total of the grafted polypropylene chloride and the amine-neutralized water-soluble resin;
a combination ratio of 2.56.0 weight % as of the wettability-improving agent to the entirety of the promotor; and a solid content of 210 weight % of the entirety of the promotor.
A method for coating to polypropylene materials, according to the present invention, comprises:
a pretreatment step in which a polypropylene material is beforehand cleaned, and then the above water base adhesion promotor is applied, then dried; and a coating step in which a paint is coated to the material after the pretreatment step.
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, each component, constituting the present invention water base adhesion promotor for polypropylene, is explained in detail, and then the water base adhesion promotor for polypropylene and the method for coating to polypropylene materials are explained.
(Grafted polypropylene chloride):
The grafted polypropylene chloride, as used in the present invention, is a component to enhance the adhesion to polypropylene materials. The grafted polypropylene chloride is a polypropylene derivative which includes a polypropylene chloride moiety and a malefic anhydride moiety as bonded thereto, and is usually used in the form of an emulsion having the high handling property.
The polypropylene chloride moiety is a moiety comprising a polypropylene having at least one chlorine atom as a substituent. In addition, the malefic anhydride moiety is a moiety as obtained by grafting malefic anhydride, and has a cyclic acid anhydride group (deriving from malefic anhydride) and/or two free carboxyl groups.
The grafted polypropylene chloride is a product by reacting a polypropylene upon malefic anhydride and chlorine to internally graft the polypropylene, and is, for example, produced by reacting chlorine and malefic anhydride upon a polypropylene. Incidentally, whichever of chlorine and malefic anhydride may be reacted earlier than the other. The reaction with chlorine is, for example, carried out by introducing a chlorine gas into a solution including a polypropylene. In addition, the reaction with malefic anhydride is, for example, carried out by reacting malefic anhydride upon a polypropylene (or its chloride) in the presence of a peroxide.
The chlorine content in the grafted polypropylene chloride is in the range of 15-25 weight %o, preferably 1822 weight %. In the case where the chlorine content is less than 15 weight %o, the melting point of the grafted polypropylene chloride is so high that the crystallization easily occurs and that the emulsification is difficult, thus resulting in depression of the storage stability of the resultant water base adhesion promotor. On the other hand, in the case where the chlorine content exceeds 25 weight %, the grafted polypropylene chloride is noncrystalline, thus resulting in depression of the adhesion and the water resistance.
The malefic anhydride moiety content in the grafted polypropylene chloride is in the range of 1 ~5 weight %, preferably 34.5 weight %. In the case where the malefic anhydride moiety content is less than 1 weight %, the emulsification is difficult, thus resulting in depression of the storage stability of the resultant water base adhesion promotor. On the other hand, in the case where the malefic anhydride moiety content exceeds 5 weight %, the acid anhydride group content is too much, thus resulting in depression of the adhesion and the water resistance.
The weight-average molecular weight of the grafted polypropylene chloride is not especially limited, but is preferably in the range of 20,000100,000, more preferably 30,00080,000. In the case where the weight-average molecular weight is less than 20,000, the promotor might swell with a solvent for a top paint, so that the adhesion might be deteriorated. On the other hand, the weight-average molecular weight exceeds 100,000, the viscosity of the resultant water base adhesion promotor might be so high that the emulsification might be difficult and that the storage stability might be low.
(Amine-neutralized water-soluble resin):
The amine-neutralized water-soluble resin, as used in the present invention, is a resin as water-solubilized by neutralization with an amine, and is a film-formable component having high water resistance.
Incidentally, for example, water-soluble resins, which are not obtained by the amine neutralization, such as polyethylene glycol and polyvinylpyrrolidone, merely have low water resistance, because, even after film formation by drying, such water-soluble resins remain and retain its water solubility. In comparison, the amine-neutralized water-soluble resin, as used in the present invention, displays high water resistance, because it volatilizes the amine in the drying step, and thus loses the water solubility.
The amine-neutralized water-soluble resin, as used in the present invention, is not especially limited if it is a resin as neutralized with an amine, and examples thereof include products by neutralization of resins such as urethane resins, alkyd resins, and acrylic resins. These may be used either alone respectively or in combinations with each other.
Examples of the amine, as used for the above neutralization, include ammonia, triethylamine, and monoethanolamine. These may be used either alone respectively or in combinations with each other.
(Wettability-improving agent):
The wettability-improving agent, as used in the present invention, is a component to enhance the wettability of the water base adhesion promotor upon polypropylene materials (having much water-repellency). The use of this wettability-improving agent enables a coating film, resultant from the grafted polypropylene chloride and the amine-neutralized water-soluble resin as above, to adhere well to polypropylene materials.
The wettability-improving agent is not especially limited, but examples thereof include ethylene glycol hexyl ether, dimethylpolysiloxane-polyethylene glycol block polymer (Polyflow KL-245). These may be used either alone respectively or in combinations with each other. Particularly, ethylene glycol hexyl ether improves the wettability, and further does not lower the water resistance because it volatilizes in the drying step and therefore does not remain in the resultant coating film. In comparison, materials as conventionally used to enhance the wettability, such as alkylphenylpolyethylene glycol, do not volatilize in the drying step, but remain in the coating film, thus depressing the water resistance.
(Other components):
The water base adhesion promotor of the present invention may further comprise the following other components: resin emulsions such as acrylic emulsions, urethane emulsions, and polyvinyl chloride emulsions; inorganic pigments such as titanium white and carbon black, extenders such as talc and precipitated barium; and various organic color pigments.
(Water base adhesion promotor for polypropylene and method for coating):
The water base adhesion promotor for polypropylene, according to the present invention, needs to comprise the grafted polypropylene chloride, the amine-neutralized water-soluble resin, the wettability-improving agent, and water (these components are explained in detail above), and may further comprise the above other components if necessary. Conditions, such as order, for mixing these components are not especially limited.
The combination ratio of the grafted polypropylene chloride, as contained in the present invention water base adhesion promotor for polypropylene, is in the range of 2590 weight %, preferably 3050 weight %, of the total (the total solid content) of the grafted polypropylene chloride and the amine-neutralized water-soluble resin. In the case where the combination ratio of the grafted polypropylene chloride is less than 25 weight %, the adhesion and the water resistance are both low. On the other hand, in the case where the combination ratio of the grafted polypropylene chloride exceeds 90 weight %, the adhesion and the water resistance as well as the film formability are low.
The combination ratio of the wettability-improving agent is in the range of 2.56.0 weight %o, preferably 3.04.0 weight %, of the entirety of the water base adhesion promotor. In the case where the combination ratio of the wettability-improving agent is less than 2.5 weight %, the polypropylene material crawls with the water base adhesion promotor, so uniform coating is impossible. On the other hand, in the case where the combination ratio of the wettability-improving agent exceeds 6.0 weight %, the storage stability of the water base adhesion promotor is low, and the grafted polypropylene chloride aggregates to precipitate.
The solid content of the present invention water base adhesion promotor for polypropylene is the nonvolatile matter and is in the range of 210 weight %, preferably 4--6 weight %, of the entirety of the water base adhesion promotor. In the case where the solid content is less than 2 weight %, the film thickness of the coating film resultant from the water base adhesion promotor is too thin, so the adhesion and the water resistance are both low. On the other hand, in the case where the solid content exceeds 10 weight %, marks of sagging are left after coating the water base adhesion promotor, so the resultant coating film has unevenness, and the appearance is therefore unfavorable.
The method of coating to polypropylene materials, according to the present invention, comprises the pretreatment step and the top coating step.
The pretreatment step includes the steps of cleaning the polypropylene material and applying the above water base adhesion promotor and then drying the material.
The cleaned polypropylene material is, for example, prepared by the following steps (1)~(3) in the pretreatment step.
(1) A step of spray-washing a polypropylene material with warm water of 6080 °C.
(2) A step of degreasing the polypropylene material with an alkaline cleaning agent after the above step (1).
an amine-neutralized water-soluble resin;
a wettability-improving agent; and water;
and is characterized by having:
a combination ratio of 2590 weight % as of the grafted polypropylene chloride to the total of the grafted polypropylene chloride and the amine-neutralized water-soluble resin;
a combination ratio of 2.56.0 weight % as of the wettability-improving agent to the entirety of the promotor; and a solid content of 210 weight % of the entirety of the promotor.
A method for coating to polypropylene materials, according to the present invention, comprises:
a pretreatment step in which a polypropylene material is beforehand cleaned, and then the above water base adhesion promotor is applied, then dried; and a coating step in which a paint is coated to the material after the pretreatment step.
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, each component, constituting the present invention water base adhesion promotor for polypropylene, is explained in detail, and then the water base adhesion promotor for polypropylene and the method for coating to polypropylene materials are explained.
(Grafted polypropylene chloride):
The grafted polypropylene chloride, as used in the present invention, is a component to enhance the adhesion to polypropylene materials. The grafted polypropylene chloride is a polypropylene derivative which includes a polypropylene chloride moiety and a malefic anhydride moiety as bonded thereto, and is usually used in the form of an emulsion having the high handling property.
The polypropylene chloride moiety is a moiety comprising a polypropylene having at least one chlorine atom as a substituent. In addition, the malefic anhydride moiety is a moiety as obtained by grafting malefic anhydride, and has a cyclic acid anhydride group (deriving from malefic anhydride) and/or two free carboxyl groups.
The grafted polypropylene chloride is a product by reacting a polypropylene upon malefic anhydride and chlorine to internally graft the polypropylene, and is, for example, produced by reacting chlorine and malefic anhydride upon a polypropylene. Incidentally, whichever of chlorine and malefic anhydride may be reacted earlier than the other. The reaction with chlorine is, for example, carried out by introducing a chlorine gas into a solution including a polypropylene. In addition, the reaction with malefic anhydride is, for example, carried out by reacting malefic anhydride upon a polypropylene (or its chloride) in the presence of a peroxide.
The chlorine content in the grafted polypropylene chloride is in the range of 15-25 weight %o, preferably 1822 weight %. In the case where the chlorine content is less than 15 weight %o, the melting point of the grafted polypropylene chloride is so high that the crystallization easily occurs and that the emulsification is difficult, thus resulting in depression of the storage stability of the resultant water base adhesion promotor. On the other hand, in the case where the chlorine content exceeds 25 weight %, the grafted polypropylene chloride is noncrystalline, thus resulting in depression of the adhesion and the water resistance.
The malefic anhydride moiety content in the grafted polypropylene chloride is in the range of 1 ~5 weight %, preferably 34.5 weight %. In the case where the malefic anhydride moiety content is less than 1 weight %, the emulsification is difficult, thus resulting in depression of the storage stability of the resultant water base adhesion promotor. On the other hand, in the case where the malefic anhydride moiety content exceeds 5 weight %, the acid anhydride group content is too much, thus resulting in depression of the adhesion and the water resistance.
The weight-average molecular weight of the grafted polypropylene chloride is not especially limited, but is preferably in the range of 20,000100,000, more preferably 30,00080,000. In the case where the weight-average molecular weight is less than 20,000, the promotor might swell with a solvent for a top paint, so that the adhesion might be deteriorated. On the other hand, the weight-average molecular weight exceeds 100,000, the viscosity of the resultant water base adhesion promotor might be so high that the emulsification might be difficult and that the storage stability might be low.
(Amine-neutralized water-soluble resin):
The amine-neutralized water-soluble resin, as used in the present invention, is a resin as water-solubilized by neutralization with an amine, and is a film-formable component having high water resistance.
Incidentally, for example, water-soluble resins, which are not obtained by the amine neutralization, such as polyethylene glycol and polyvinylpyrrolidone, merely have low water resistance, because, even after film formation by drying, such water-soluble resins remain and retain its water solubility. In comparison, the amine-neutralized water-soluble resin, as used in the present invention, displays high water resistance, because it volatilizes the amine in the drying step, and thus loses the water solubility.
The amine-neutralized water-soluble resin, as used in the present invention, is not especially limited if it is a resin as neutralized with an amine, and examples thereof include products by neutralization of resins such as urethane resins, alkyd resins, and acrylic resins. These may be used either alone respectively or in combinations with each other.
Examples of the amine, as used for the above neutralization, include ammonia, triethylamine, and monoethanolamine. These may be used either alone respectively or in combinations with each other.
(Wettability-improving agent):
The wettability-improving agent, as used in the present invention, is a component to enhance the wettability of the water base adhesion promotor upon polypropylene materials (having much water-repellency). The use of this wettability-improving agent enables a coating film, resultant from the grafted polypropylene chloride and the amine-neutralized water-soluble resin as above, to adhere well to polypropylene materials.
The wettability-improving agent is not especially limited, but examples thereof include ethylene glycol hexyl ether, dimethylpolysiloxane-polyethylene glycol block polymer (Polyflow KL-245). These may be used either alone respectively or in combinations with each other. Particularly, ethylene glycol hexyl ether improves the wettability, and further does not lower the water resistance because it volatilizes in the drying step and therefore does not remain in the resultant coating film. In comparison, materials as conventionally used to enhance the wettability, such as alkylphenylpolyethylene glycol, do not volatilize in the drying step, but remain in the coating film, thus depressing the water resistance.
(Other components):
The water base adhesion promotor of the present invention may further comprise the following other components: resin emulsions such as acrylic emulsions, urethane emulsions, and polyvinyl chloride emulsions; inorganic pigments such as titanium white and carbon black, extenders such as talc and precipitated barium; and various organic color pigments.
(Water base adhesion promotor for polypropylene and method for coating):
The water base adhesion promotor for polypropylene, according to the present invention, needs to comprise the grafted polypropylene chloride, the amine-neutralized water-soluble resin, the wettability-improving agent, and water (these components are explained in detail above), and may further comprise the above other components if necessary. Conditions, such as order, for mixing these components are not especially limited.
The combination ratio of the grafted polypropylene chloride, as contained in the present invention water base adhesion promotor for polypropylene, is in the range of 2590 weight %, preferably 3050 weight %, of the total (the total solid content) of the grafted polypropylene chloride and the amine-neutralized water-soluble resin. In the case where the combination ratio of the grafted polypropylene chloride is less than 25 weight %, the adhesion and the water resistance are both low. On the other hand, in the case where the combination ratio of the grafted polypropylene chloride exceeds 90 weight %, the adhesion and the water resistance as well as the film formability are low.
The combination ratio of the wettability-improving agent is in the range of 2.56.0 weight %o, preferably 3.04.0 weight %, of the entirety of the water base adhesion promotor. In the case where the combination ratio of the wettability-improving agent is less than 2.5 weight %, the polypropylene material crawls with the water base adhesion promotor, so uniform coating is impossible. On the other hand, in the case where the combination ratio of the wettability-improving agent exceeds 6.0 weight %, the storage stability of the water base adhesion promotor is low, and the grafted polypropylene chloride aggregates to precipitate.
The solid content of the present invention water base adhesion promotor for polypropylene is the nonvolatile matter and is in the range of 210 weight %, preferably 4--6 weight %, of the entirety of the water base adhesion promotor. In the case where the solid content is less than 2 weight %, the film thickness of the coating film resultant from the water base adhesion promotor is too thin, so the adhesion and the water resistance are both low. On the other hand, in the case where the solid content exceeds 10 weight %, marks of sagging are left after coating the water base adhesion promotor, so the resultant coating film has unevenness, and the appearance is therefore unfavorable.
The method of coating to polypropylene materials, according to the present invention, comprises the pretreatment step and the top coating step.
The pretreatment step includes the steps of cleaning the polypropylene material and applying the above water base adhesion promotor and then drying the material.
The cleaned polypropylene material is, for example, prepared by the following steps (1)~(3) in the pretreatment step.
(1) A step of spray-washing a polypropylene material with warm water of 6080 °C.
(2) A step of degreasing the polypropylene material with an alkaline cleaning agent after the above step (1).
(3) A step of washing the alkaline cleaning agent off the polypropylene material by spray-washing the polypropylene material with deionized water after the above step (2).
The coating film of the water base adhesion promotor is formed on the surface of the polypropylene material by applying the water base adhesion promotor onto the cleaned polypropylene material and then drying the material. This applying step may be accomplished by, for example, pouring, atomized spraying, dipping and/or showering. The choice of a given applying step for any specific part may be based on economic, process, and quality considerations. For some parts it is preferable to hold the polypropylene material upright after applying step and to then dry the material. For other parts, notably those in which the coating material may pool and/or sag after application, it is preferable to hold the polypropylene material at a slight angle, preferably about 1020°
and most preferably about 15° from the vertical during drying.
During the holding step, it is preferred to maintain an atomosphere within the environment to promote even coating after drying, For example, the holding environment may be preferably maintained at a temperature of between about 1530 °C and about 4070% relative humidity and most preferably between 2025 °C and about 4070%
relative humidity. This holding step is commonly referred to as flash condition.
The method for drying after the flash condition is not especially limited, and the drying is usually carried out with ovens such as hot-air drying ovens, long-wave infrared ovens, and short- wave infrared ovens at about 60120 °C for about 515 minutes. The thickness of the dried film, as obtained from the water base adhesion promotor in the above way, is preferably in the range of 0.11 Vim.
The coating step includes the step of coating a top paint to the above material after the pretreatment step and is carried out by coating the top paint and then drying it.
The type of the top paint is not especially limited, but examples thereof include one-component melamine baking paints, two-component urethane paints, and one-component lacquer paints.
The method of coating the top paint is not especially limited, but the spray coating is preferable. The method for drying the coated top paint is not especially limited, and the drying is usually carried out with ovens such as hot-air drying ovens, long-wave infrared ovens, and short-wave infrared ovens at 70120 °C for 20-60 minutes. The thickness of the dried film, as obtained from the top paint in the above way, is not especially limited, but is preferably in the range of 1560 ~.m.
In the method for coating to polypropylene materials, the use of the above water base adhesion promotor in the pretreatment step enables the omission of the primer coating. Therefore, the productivity in the coating step is largely improved.
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, the present invention is more specifically illustrated by the following examples of some preferred embodiments in comparison with comparative examples not according to the invention. However, the invention is not limited to the below-mentioned examples.
Hereinafter, the unit "part(s)" is "weight part(s)."
(EXAMPLE 1 ) First, 6 parts (nonvolatile matter: 1.8 parts) of a grafted polypropylene chloride emulsion (chlorine content = 16 weight %, malefic anhydride moiety content = 1.5 weight %, nonvolatile matter = 30 weight %), 12 parts (nonvolatile matter: 4.2 parts) of a water-soluble urethane (made by Sanyo Kasei Co., Ltd., U-Coat UWS-145, nonvolatile matter = 35 weight %) (as the amine-neutralized water-soluble resin), 3 parts of ethylene glycol hexyl ether (as the wettability-improving agent), and 79 parts of water were mixed in this order under stirring, thus preparing water base adhesion promotor (1) of 100 parts in entirety. Incidentally, the ratio of (grafted polypropylene chloride)/(amine-neutralized water-soluble resin) (ratio in terms of solid content) was 30/70, and the combination ratio of ethylene glycol hexyl ether was 3 weight % of the entirety of water base adhesion promotor (1), and the solid content of water base adhesion promotor (1) was 6 weight % as determined from its nonvolatile matter.
A polypropylene material was spray-washed with warm water of 6080 °C, and then degreased by spray-washing with an alkaline cleaning agent (Surf Cleaner PL-1000, made by Nippon Paint Co., Ltd.), and then spray-washed with deionized water of room temperature to wash the alkaline cleaning agent off, thus preparing a washed polypropylene material. This polypropylene material was immersed into water base adhesion promotor (1), and then left standing upright at room temperature for 1 minute, and then dried at 80 °C for 10 minutes. Next, an isocyanate curing type polyester resin paint (R-763, made by Morton Nippon Coatings Co., Ltd.) (as the top paint) was spray-coated to the above polypropylene material, and the coated paint was then dried at 80 °C
for 40 minutes, thus obtaining coated product (1). Incidentally, the dried-film thickness was in the range of 1525 Vim.
The properties of water base adhesion promotor (1) were evaluated by the following methods. The results thereof are shown in Table 1.
(Evaluation method):
1. Adhesion:
A cross-cut test was carried out for the coated product in accordance with JIS K5400. First, 100 cross-cuts of 2 mm x 2 mm were prepared to carry out the cellophane tape peeling test, and the evaluation was made on the following evaluation standard:
O: no peeling-off was seen;
x: one or more cross-cuts peeled off.
2. Water resistance:
The coated product was immersed into warm water of 80 °C for 3 hours, and water on the surface was then wiped off. Thereafter, the coated product was left for 1 hour, and the above adhesion evaluation was then carried out. The evaluation standard was the same as that for the adhesion.
3. Appearance:
A polypropylene material of 7.5 cm x 10 cm was prepared, and then treated with the water base adhesion promotor, and then stood upright, and then dried at 80 °C for 30 minutes, thus evaluating whether a sagging mark was seen or not with the eye on the following evaluation standard:
O: no sagging mark;
x: a sagging mark was seen.
The coating film of the water base adhesion promotor is formed on the surface of the polypropylene material by applying the water base adhesion promotor onto the cleaned polypropylene material and then drying the material. This applying step may be accomplished by, for example, pouring, atomized spraying, dipping and/or showering. The choice of a given applying step for any specific part may be based on economic, process, and quality considerations. For some parts it is preferable to hold the polypropylene material upright after applying step and to then dry the material. For other parts, notably those in which the coating material may pool and/or sag after application, it is preferable to hold the polypropylene material at a slight angle, preferably about 1020°
and most preferably about 15° from the vertical during drying.
During the holding step, it is preferred to maintain an atomosphere within the environment to promote even coating after drying, For example, the holding environment may be preferably maintained at a temperature of between about 1530 °C and about 4070% relative humidity and most preferably between 2025 °C and about 4070%
relative humidity. This holding step is commonly referred to as flash condition.
The method for drying after the flash condition is not especially limited, and the drying is usually carried out with ovens such as hot-air drying ovens, long-wave infrared ovens, and short- wave infrared ovens at about 60120 °C for about 515 minutes. The thickness of the dried film, as obtained from the water base adhesion promotor in the above way, is preferably in the range of 0.11 Vim.
The coating step includes the step of coating a top paint to the above material after the pretreatment step and is carried out by coating the top paint and then drying it.
The type of the top paint is not especially limited, but examples thereof include one-component melamine baking paints, two-component urethane paints, and one-component lacquer paints.
The method of coating the top paint is not especially limited, but the spray coating is preferable. The method for drying the coated top paint is not especially limited, and the drying is usually carried out with ovens such as hot-air drying ovens, long-wave infrared ovens, and short-wave infrared ovens at 70120 °C for 20-60 minutes. The thickness of the dried film, as obtained from the top paint in the above way, is not especially limited, but is preferably in the range of 1560 ~.m.
In the method for coating to polypropylene materials, the use of the above water base adhesion promotor in the pretreatment step enables the omission of the primer coating. Therefore, the productivity in the coating step is largely improved.
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, the present invention is more specifically illustrated by the following examples of some preferred embodiments in comparison with comparative examples not according to the invention. However, the invention is not limited to the below-mentioned examples.
Hereinafter, the unit "part(s)" is "weight part(s)."
(EXAMPLE 1 ) First, 6 parts (nonvolatile matter: 1.8 parts) of a grafted polypropylene chloride emulsion (chlorine content = 16 weight %, malefic anhydride moiety content = 1.5 weight %, nonvolatile matter = 30 weight %), 12 parts (nonvolatile matter: 4.2 parts) of a water-soluble urethane (made by Sanyo Kasei Co., Ltd., U-Coat UWS-145, nonvolatile matter = 35 weight %) (as the amine-neutralized water-soluble resin), 3 parts of ethylene glycol hexyl ether (as the wettability-improving agent), and 79 parts of water were mixed in this order under stirring, thus preparing water base adhesion promotor (1) of 100 parts in entirety. Incidentally, the ratio of (grafted polypropylene chloride)/(amine-neutralized water-soluble resin) (ratio in terms of solid content) was 30/70, and the combination ratio of ethylene glycol hexyl ether was 3 weight % of the entirety of water base adhesion promotor (1), and the solid content of water base adhesion promotor (1) was 6 weight % as determined from its nonvolatile matter.
A polypropylene material was spray-washed with warm water of 6080 °C, and then degreased by spray-washing with an alkaline cleaning agent (Surf Cleaner PL-1000, made by Nippon Paint Co., Ltd.), and then spray-washed with deionized water of room temperature to wash the alkaline cleaning agent off, thus preparing a washed polypropylene material. This polypropylene material was immersed into water base adhesion promotor (1), and then left standing upright at room temperature for 1 minute, and then dried at 80 °C for 10 minutes. Next, an isocyanate curing type polyester resin paint (R-763, made by Morton Nippon Coatings Co., Ltd.) (as the top paint) was spray-coated to the above polypropylene material, and the coated paint was then dried at 80 °C
for 40 minutes, thus obtaining coated product (1). Incidentally, the dried-film thickness was in the range of 1525 Vim.
The properties of water base adhesion promotor (1) were evaluated by the following methods. The results thereof are shown in Table 1.
(Evaluation method):
1. Adhesion:
A cross-cut test was carried out for the coated product in accordance with JIS K5400. First, 100 cross-cuts of 2 mm x 2 mm were prepared to carry out the cellophane tape peeling test, and the evaluation was made on the following evaluation standard:
O: no peeling-off was seen;
x: one or more cross-cuts peeled off.
2. Water resistance:
The coated product was immersed into warm water of 80 °C for 3 hours, and water on the surface was then wiped off. Thereafter, the coated product was left for 1 hour, and the above adhesion evaluation was then carried out. The evaluation standard was the same as that for the adhesion.
3. Appearance:
A polypropylene material of 7.5 cm x 10 cm was prepared, and then treated with the water base adhesion promotor, and then stood upright, and then dried at 80 °C for 30 minutes, thus evaluating whether a sagging mark was seen or not with the eye on the following evaluation standard:
O: no sagging mark;
x: a sagging mark was seen.
4. Storage stability:
A polypropylene material was immersed into the water base adhesion promotor as had been stored at room temperature for 1 month, thus evaluating whether an aggregate was seen or not with the eye on the following evaluation standard:
~: no aggregate;
x: an aggregate was seen.
(EXAMPLES 2~4 AND COMPARATIVE EXAMPLES 1 ~7) Water base adhesion promoters (2)~(4) and comparative water base adhesion promoters (1)~(7) were prepared to evaluate their properties in the same way as of Example 1 except that the type and the combination amount of the grafted polypropylene chloride emulsion and the combination amounts of the water-soluble urethane and the ethylene glycol hexyl ether were changed to those as shown in Tables 1 and 2.
Tables 1 and 2 further show the ratio of (grafted polypropylene chloride)/(amine-neutralized water-soluble resin) (ratio in terms of solid content) and the combination ratio and the solid content of the ethylene glycol hexyl ether.
Table 1 Example Grafted 1.8 1.5 4.0 4.0 I polypropylene Water chloride base (CPO) adhesion Water-soluble4 1 6 1 promotor urethane . . . .
(AU) (parts)*
Ethylene 3.0 5.0 3.0 4.0 glycol hexylether (EGHE) Chlorine 16 21 25 21 content of CPO
(weight %) Malefic 1.5 4.5 1.0 4.5 anhydride content of CPO (weight %) (ratio in terms of solid content) Combination 3 5 3 4 ratio of EGHE
(weight %) Solid 6 3 10 5 content (weight %) Adhesion 0 0 0 EvaluationWater resistance results Appearance ~ 0 Storage stability * 1 Amount of each component in 100 weight parts of water base adhesion promotor; the balance is water.
Table 2 Comparative Example Grafted 1.0 9.5 1.8 1.8 1.8 0.5 6.0 polypropylene Water chloride base (CPO) adhesion Water-soluble4.0 0.5 4.2 4.2 4 0 1 promotor urethane . . .
(AU) (parts)*
Ethylene 3.0 3.0 3.0 3.0 7.0 3.0 3.0 glycol hexyl ether (EGHE) Chlorine 21 16 27 21 21 21 21 content of CPO
(weight %) Malefic 4. 1. 1.5 7 .0 4. 4. 4.
anhydride 5 5 5 S 5 content of CPO (weight %) (ratio in terms of solid content) Combination 3 3 3 3 7 3 3 ratio of EGHE
(weight %) Solid 5 10 6 6 6 1 12 content (weight %) Adhesion x x x x 0 x EvaluationWater resistancex x x x 0 x results Appearance ~ ~ ~ ~ 0 ~ x Storage stability--- --- --- --- x --- ---* 1 Amount of each component in 100 weight parts of water base adhesion promotor; the balance is water.
<Evaluation results>:
Examples 1 ~4 all provide excellent results with regard to the adhesion, the water resistance, the appearance, and the storage stability, and enable the omission of the conventional primer coating step.
Comparative Examples 1 and 2 provide inferior results with regard to the adhesion and the water resistance, because the combination ratio of the grafted polypropylene chloride is out of the claimed range. Comparative Example 3 provides inferior results with regard to the adhesion and the water resistance, because the chlorine content of the grafted polypropylene chloride is too large. Comparative Example 4 provides inferior results with regard to the adhesion and the water resistance, because the malefic acid moiety content is too large. Comparative Example 5 provides inferior results with regard to the storage stability, because the combination ratio of the ethylene glycol hexyl ether is too large. Comparative Example 6 provides inferior results with regard to the adhesion and the water resistance, because the coating film resultant from the water base adhesion promotor is thin due to too small solid content. Comparative Example 7 provides inferior results with regard to the appearance, because the coating film resultant from the water base adhesion promotor is thick due to too large solid content.
INDUSTRIAL APPLICATION
The use of the present invention water base adhesion promotor for polypropylene in the pretreatment step prior to coating of polypropylene materials enables the omission of the primer coating, and further, provides excellent results with regard to the adhesion of the paint and the water resistance and appearance of the coating film.
The present invention method for coating to polypropylene materials involves the use of the above water base adhesion promotor in the pretreatment step and therefore enables the omission of the primer coating and the great improvement of the productivity of the coating step. In addition, in this method, the water base adhesion promotor that does not remain on the polypropylene material can be recovered and recycled through the process, providing economical advantages to the process.
A polypropylene material was immersed into the water base adhesion promotor as had been stored at room temperature for 1 month, thus evaluating whether an aggregate was seen or not with the eye on the following evaluation standard:
~: no aggregate;
x: an aggregate was seen.
(EXAMPLES 2~4 AND COMPARATIVE EXAMPLES 1 ~7) Water base adhesion promoters (2)~(4) and comparative water base adhesion promoters (1)~(7) were prepared to evaluate their properties in the same way as of Example 1 except that the type and the combination amount of the grafted polypropylene chloride emulsion and the combination amounts of the water-soluble urethane and the ethylene glycol hexyl ether were changed to those as shown in Tables 1 and 2.
Tables 1 and 2 further show the ratio of (grafted polypropylene chloride)/(amine-neutralized water-soluble resin) (ratio in terms of solid content) and the combination ratio and the solid content of the ethylene glycol hexyl ether.
Table 1 Example Grafted 1.8 1.5 4.0 4.0 I polypropylene Water chloride base (CPO) adhesion Water-soluble4 1 6 1 promotor urethane . . . .
(AU) (parts)*
Ethylene 3.0 5.0 3.0 4.0 glycol hexylether (EGHE) Chlorine 16 21 25 21 content of CPO
(weight %) Malefic 1.5 4.5 1.0 4.5 anhydride content of CPO (weight %) (ratio in terms of solid content) Combination 3 5 3 4 ratio of EGHE
(weight %) Solid 6 3 10 5 content (weight %) Adhesion 0 0 0 EvaluationWater resistance results Appearance ~ 0 Storage stability * 1 Amount of each component in 100 weight parts of water base adhesion promotor; the balance is water.
Table 2 Comparative Example Grafted 1.0 9.5 1.8 1.8 1.8 0.5 6.0 polypropylene Water chloride base (CPO) adhesion Water-soluble4.0 0.5 4.2 4.2 4 0 1 promotor urethane . . .
(AU) (parts)*
Ethylene 3.0 3.0 3.0 3.0 7.0 3.0 3.0 glycol hexyl ether (EGHE) Chlorine 21 16 27 21 21 21 21 content of CPO
(weight %) Malefic 4. 1. 1.5 7 .0 4. 4. 4.
anhydride 5 5 5 S 5 content of CPO (weight %) (ratio in terms of solid content) Combination 3 3 3 3 7 3 3 ratio of EGHE
(weight %) Solid 5 10 6 6 6 1 12 content (weight %) Adhesion x x x x 0 x EvaluationWater resistancex x x x 0 x results Appearance ~ ~ ~ ~ 0 ~ x Storage stability--- --- --- --- x --- ---* 1 Amount of each component in 100 weight parts of water base adhesion promotor; the balance is water.
<Evaluation results>:
Examples 1 ~4 all provide excellent results with regard to the adhesion, the water resistance, the appearance, and the storage stability, and enable the omission of the conventional primer coating step.
Comparative Examples 1 and 2 provide inferior results with regard to the adhesion and the water resistance, because the combination ratio of the grafted polypropylene chloride is out of the claimed range. Comparative Example 3 provides inferior results with regard to the adhesion and the water resistance, because the chlorine content of the grafted polypropylene chloride is too large. Comparative Example 4 provides inferior results with regard to the adhesion and the water resistance, because the malefic acid moiety content is too large. Comparative Example 5 provides inferior results with regard to the storage stability, because the combination ratio of the ethylene glycol hexyl ether is too large. Comparative Example 6 provides inferior results with regard to the adhesion and the water resistance, because the coating film resultant from the water base adhesion promotor is thin due to too small solid content. Comparative Example 7 provides inferior results with regard to the appearance, because the coating film resultant from the water base adhesion promotor is thick due to too large solid content.
INDUSTRIAL APPLICATION
The use of the present invention water base adhesion promotor for polypropylene in the pretreatment step prior to coating of polypropylene materials enables the omission of the primer coating, and further, provides excellent results with regard to the adhesion of the paint and the water resistance and appearance of the coating film.
The present invention method for coating to polypropylene materials involves the use of the above water base adhesion promotor in the pretreatment step and therefore enables the omission of the primer coating and the great improvement of the productivity of the coating step. In addition, in this method, the water base adhesion promotor that does not remain on the polypropylene material can be recovered and recycled through the process, providing economical advantages to the process.
Claims (11)
1. A method for coating a polypropylene material, the method comprising the steps of:
pretreating in which a polypropylene material is cleaned, and then applying to the polypropylene material a water based adhesion promoter comprising:
a grafted polypropylene chloride, which includes a polypropylene chloride moiety and a maleic anhydride moiety, and which has a chlorine content of 15 ~ 25 weight % and a maleic anhydride moiety content of 1 ~ 5 weight %;
an amine-neutralized water-soluble resin;
a wettability-improving agent; and water;
being characterized by having:
a combination ratio of 25 ~ 90 weight % as of the grafted polypropylene chloride to the total of the grafted polypropylene chloride and the amine-neutralized water-soluble resin;
a combination ratio of 2.5 ~ 6.0 weight % as of the wettability-improving agent to the entirety of the promoter;
a solid content of 2 ~ 10 weight % of the entirety of the promoter;
drying the pretreated material; and coating in which a paint is coated to the pretreated material after the pretreating.
pretreating in which a polypropylene material is cleaned, and then applying to the polypropylene material a water based adhesion promoter comprising:
a grafted polypropylene chloride, which includes a polypropylene chloride moiety and a maleic anhydride moiety, and which has a chlorine content of 15 ~ 25 weight % and a maleic anhydride moiety content of 1 ~ 5 weight %;
an amine-neutralized water-soluble resin;
a wettability-improving agent; and water;
being characterized by having:
a combination ratio of 25 ~ 90 weight % as of the grafted polypropylene chloride to the total of the grafted polypropylene chloride and the amine-neutralized water-soluble resin;
a combination ratio of 2.5 ~ 6.0 weight % as of the wettability-improving agent to the entirety of the promoter;
a solid content of 2 ~ 10 weight % of the entirety of the promoter;
drying the pretreated material; and coating in which a paint is coated to the pretreated material after the pretreating.
2. The method of claim 1 wherein said wettability-improving agent is ethylene glycol hexyl ether.
3. The method of claim 1 wherein said applying comprises pouring, atomized spraying, dipping and/or showering.
4. The method of claim 1 further comprising holding the pretreated material prior to said drying.
5. The method of claim 4 wherein said holding is accomplished in an environment having a temperature of between about 15 ~ 30 ° C and a relative humidity of between about 40 ~ 70 %.
6. The method of claim 4 wherein said holding is accomplished in an environment having a temperature of between about 20 ~ 25 ° C and a relative humidity of between about 40 ~ 70 %.
7. The method of claim 4 wherein said pretreated material is held in a vertical position.
8. The method of claim 4 wherein said pretreated material is held at an angle of between about 10 ~ 20° from the vertical.
9. The method of claim 1 wherein adhesion promoter that does not remain on said polypropylene material after said applying is recovered and recycled.
10. The method of claim 1 wherein said drying is accomplished at a temperature of between about 60 ~ 120 °C.
11. The method of claim 10 wherein said drying is accomplished in about 5 ~ 15 minutes.