CA2224506A1 - Opaque security paper that can be authenticated by tearing, scratch-and-win tickets made out of the said paper and process for manufacturing the said paper - Google Patents
Opaque security paper that can be authenticated by tearing, scratch-and-win tickets made out of the said paper and process for manufacturing the said paper Download PDFInfo
- Publication number
- CA2224506A1 CA2224506A1 CA 2224506 CA2224506A CA2224506A1 CA 2224506 A1 CA2224506 A1 CA 2224506A1 CA 2224506 CA2224506 CA 2224506 CA 2224506 A CA2224506 A CA 2224506A CA 2224506 A1 CA2224506 A1 CA 2224506A1
- Authority
- CA
- Canada
- Prior art keywords
- paper
- fibrous
- colored
- color
- coloring agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
La présente invention concerne des supports fibreux d'écriture et/ou d'impressio n, de sécurité (e.g. papier). En particulier, l'invention vise un papier de sécurité opaque, authentifiable pa r déchirure, non délaminable, infalsifiable, économique et imprimable, caractérisé en ce qu'il est constitué notamment par un seul et même matelas fibreux, homogèn e notamment dans son épaisseur et obtenu à partir d'un seul jet fibreux, et en ce qu'il comprend, dans son épaisseur, au moins une tranche (2) sensiblement médiane de couleur (C2) et au moins une tranche (3,4) externe blanche ou de couleur (C1, C3 ) différente et/ou moins foncée que celle (C2) de la tranche médiane (2). De préférence, C1 et C3 = C2 décolorée et C2 = couleur foncée. L'invention a également pour objet le procédé d'obtention dudit papier et les ar ticles réalisés à partir dudit papier (e.g. ticket de jeu à gratter).The present invention relates to fibrous writing and / or printing, security media (e.g. paper). In particular, the invention relates to an opaque security paper which can be authenticated by tearing, cannot be delaminated, cannot be forged, is economical and printable, characterized in that it is constituted in particular by a single and same fibrous mattress, homogeneous in particular in its thickness. and obtained from a single fibrous jet, and in that it comprises, in its thickness, at least one slice (2) substantially median in color (C2) and at least one slice (3,4) external white or of color (C1, C3) different and / or less dark than that (C2) of the middle edge (2). Preferably C1 and C3 = discolored C2 and C2 = dark color. The invention also relates to the process for obtaining said paper and the articles made from said paper (e.g. scratch-off game ticket).
Description
CA 02224=,06 1998-01-21 PAP~ER DE SECURlTE OPAQUE, AUI~lENTrFL~BLE PA~R DEC~DRURE, IlCh~ETS DE JEU A GE~TTER REALISES A PA~RTIR DUDIT PAPIER ET SON
PROCEDE DE FABRICATION
Le domaine de la présente invention est celui des supports fibreux d'écriture et/ou d'impression, dits de sécurité, en particulier en papier Ces supports fibreux ou papier de sécurité sont utiles pour la réalisation de docum~nt~ de sécurité
tels que des tickets d'admission ou de voyages, des chèques, des documents légaux ou officiels, des docl-ment.~ de crédits, des certificats d'assurance, des tickets de spectacle, de train, d'avion ou analogues ou bien encore des tickets de jeu ou de 10 loterie à gratter, également dénommés billets de loterie in~t~nt~nés.
Plus précisément, I'invention concerne des supports fibreux tels que des papiers de sécurité inf~lsifi~hles car authentifiables par une déchirure révelant une structure en sand~,vich multicolore. Ce mode d'authentification et de lutte contre les contrefacons est utilisé en billeterie, où des valeurs importantes peuvent être en jeu.
La présente invention vise également des supports fibreux, en particulier des papiers de sécurité qui sont propres à l'écriture et à l'hlll)lession et qui peuvent etre employés pour réaliser des tickets de jeu à gratter dont les informations imprimées et masquées ne doivent pas être révélables par transvision et qui permettent aussi d'éviter un autre type de fraude par del~min~tion.
L'~l~thentification directe par déchirure d'une feuille de support fibreux par exemple en papier, permet de révéler une structure sandwich multicolore:
intérieur coloré et deux tranches extérieures blanches, claires ou de couleurs dif~érentes. Cette structure caractéristique permet d'attester avec certitude de la bonne origine de certains titres, de valeur parfois très élevée, tels que des tickets de 25 transport, des billets de spectacle ou autres. Dans la mesure où cette technique d'~lthentification par déchirure est rapide et sûre, elle est parfaitement compétitive par rapport à d'autre systèmes connus tels que le filigranage, qui existe depuis fort longtemps, ou bien encore l'introduction de fibres ou de fils de sécurité. Certains de ces systèmes connus, (dont les points ou les fibres fluorescentes ou 30 phosphorescenl-es), présentent l'inconvénient de nécessiter un appareillage de révélation pour l'authentification. Un exemple typique d'un tel appareillage est la larnpe W.
Il s'ensuit que les supports fibreux ou papiers de sécurité opaques et de structure sandwich multicolore leur conférant une authentifiabilité par déchirure ne 35 devraient pas avoir de difficulté à se tailler une place de choix, notamment dans les applications ticket de transport et de billeterie inf~l~ifi~hles, pour autant que puisse CA 02224~06 1998-01-21 être supprimé un défaut majeur consistant dans le caractère del~min~ble des supports fibreux ou papiers authentifiables par déchirure, existant à l'heure actuelle. Ce défaut rédhibitoire est lié à la structure et au mode de fabrication de ces supports fibreux ou papiers de sécurité connus.
On connaît ainsi un premier type de structure dans laquelle trois couches de papiers sont assemblées les unes aux autres par l~min~tion, la couche du centre étant colorée et les couches externes étant de couleur blanche.
Le deuxième type de structure connu est formé par une feuille de papier coloré, que l'on traite par couchage sur au moins l'une de ses faces à l'aide d'une 10 composition de couchage blanche ou opacifiante.
Le couchage de supports colorés dans le domaine des papiers de sécurité a été
divlllgué il y a déjà très longtemps, même si le but alors recherché et affiché n'était pas de fournir des papiers authentifiables par déchirure. C'est ainsi que le brevet américain N~ 1 417 820 décrit un procédé pour rendre inf~l~ifi~ble un papier en 15 procédant au couchage des deux faces d'un papier noir à l'aide d'un matériau de couchage opaque et sensible aux solvants contenus dans les ç~ce lrs d'encre utilisables à des fins de falsification. On est donc ici en présence d'une structure sandwich du type revêtemenf de couchage de couleur claire/papier noir ou de couleurfoncée~revêtement de couchage de couleur claire.
On connaît également dans le domaine des papiers de sécurité, celui divulgué par le brevet britannique N~ 1 435 686, qui est con~cu pour résister aux tentatives de fraude par abrasion de surface en vue d'éliminer l'encre d'impression et d'écriture. Ce papier de sécurité comprend une feuille de base en papier, couchée par un revêtement opaque sensible à l'abrasion et constitué par un pigment non métallique 25 (argile ou TiO2) dispersé dans un liant (polymère synthétique = copolymère vinylique /
acrylique-styrène/acrylique-styrène/butadiène ou polymère naturel-cellulose-amidon-caséine). La feuille de base en papier a une couleur qui contraste avec celle durevêtement de couchage de manière à pouvoir faire apparâître les traces d'abrasion de la couche supérieure par transvision. Ce brevet n'enseigne pas de structure sandwich:
30 couleur claire ou blanche/couleur différente ou plus foncée/couleur claire ou blanc*e.
Le couchage d'un papier coloré à l'aide d'une composition opacifiante ou blanche est également mis en oeuvre dans le domaine des papiers de sécurité voués à
une destination particulière, qui est la production de billets in~t~nt~nés de loterie ou de 35 tout autre analogue du type tickets de jeu à gratter. De tels articles contiennent des informations imprimées, masquées qui peuvent être, d'une part, un numéro, un CA 02224~06 1998-01-21 .
symbole7 un message donnant lieu éventuellement à un gain, et d'autre part, un numéro de sécurité permettant de prévenir les contrefa,cons. Le masquage de ces informations classiquement est obtenu au moyen d'une couche grattable, opaque con~ lallL, par exemple, un pigment métallique (~lllmini~m) dispersé dans un liant forl~né par un latex de caoutchouc ou d'autres polymères hydrocarbonés (voir couche 28 du ticket de loterie, décrit dans le brevet US N~ 4 726 608). Outre cette couche opaque, le ticket comprend comme revêtement d'un substrat papier 18, du haut vers le bas, une couche anti-adhérente 26, en polyamide, une couche protectrice 25 en copolymère vinylacétate maléisé, les caractères imprimés 24, une couche dle plilllaile en silice amorphe + polymère vinylacétate maléisé + solvant n-propyl acétate et enfm une feuille d'alllminil1m 20 accolée au substrat papier 18.
Pour tenter de supprimer les inconvénients liés à la présence de la feuille d'~ minillm dans ce type de ticket de jeu à gratter, le brevet européen N~ 0 428 489, propose l'utilisation de papier couché pour la fabrication de tels articles. Le papier de sécurité divulgué par ce brevet colllplelld un substrat de base en papier, d'un gramrnage de l'ordre de 225 g/m2, coloré par du noir de carbone, de manière à 8tre totalement opaque et couché à l'aide d'une composition conlprellall~ des pigments tels que l'argile ou le dioxvde de titane, du latex ou de l'amidon. Les faces du papier couché ainsi obtenues sont blanches, lisses et uniformes, donc imprimables. Ces papiers sont présentés comme étant non d~l~min~bles. Pour fabriquer un billet deloterie in.~nt~né, il est prévu de réaliser l'impression sur les faces du revêtement de couchage puis de procéder à une enduction finale à l'aide de latex coloré et grattable classique. Ce brevet divulgue donc une structure sandwich: revêtement de couchage blanc/substrat papier opaque noir/revêtement de couchage blanc.
La clem~ncle de brevet européen N~ 668 092 divulgue une invention relative à des papiers pour ticket de loterie in~t~nt~né (à gratter), qui préconisent d'apporter l'opacité au papier non pas par l'intermédiaire du substrat en papier de base comme proposé dans le brevet européen N~ 428 489, mais par l'intermédiaire d'un revêtement de couchage opaque appliqué sur ledit substrat de base en papier et complenanl un pigment du type noir de carbone dispersé dans un liant du type latex de copolymère styrène/butadiène. Cette couche opaque est par ailleurs revêtue d'une couche supérieure d'impl-ession, obtenue à partir d'une composition colllpl~nall~ du latex styrène/butadiène, du CaCO3 et des microsphères de polymère styrène-acrylique.
Le FR-A-2 192 211 divulgue un procédé pour colorer ou teindre du papier absorbant à surface nl~le~ls~7 avec une épaisseur de couche de colorant aussi faible que possible mais permettant néanmoins d'obtenir une teinte uniforme au point de vue optique.
CA 02224~06 1998-01-21 Une fois coloré sur une face, le papier peut être revêtu d'une couche de résine synthétique thermodurcissable.
Pour obtenir cette un;fu"~ é de coloration malgré le relief accidenté de la surface du papier absorbant considéré, ce procédé prévoit de soumettre la face du papier à
colorer à une opération de teinture par calendrage m~gnétique ou à rouleaux magnétique, visant à déposer le colorant dans tous les creux et pores, et à une opération d'i.llpl ~;s~ion par impression hélio en creux ou impression typoflexographique visant à assurer la coloration des bosses et des reliefs.
Selon l'enseignement de cette d~m~n~ une seule face du papier est colorée.
10 Le papier obtenu par ce procédé n'est pas homogène dans son épaisseur puisqu'il présente une couche de colorant en surface qui, bien que étant aussi faible que possible existe bel et bien et confère une hétérogénéité au papier dans son épaisseur.
Par ailleurs, ce papier absorbant coloré n'est pas obtenu à partir d'un seul et même matelas fibreux de couleur initiale C2 puis décoloré ensuite ou coloré di~ ent au 15 moins partiellement sur au moins une de ses faces pour former au moins une tranche externe blanche ou de couleur Cl-C3 (di~élen~e et/ou moins foncée que la couleurinitiale C2) Le FR-A-537 357 a trait à des perfectionnements à la fabrication de cartons et papiers colorés. Plus préçi.cemçnt, ce brevet français divulgue des stratifiés colllplt;llallL une 20 couche de base en carton, sur l'une ou les deux faces de laquelle est encolée une couche de papier, dont la surface est colorée à l'aide de moyens forrnés par desréservoirs à couleur 10 et par un appareil 11 destiné à régler les couches de couleur.
Selon une variante, le carton peut être coloré directement sur l'une de ses faces par une ou plusieurs couches de couleur.
25 Là encore il n'est pas contestable que ce stratifié n'est pas homogène dans son épaisseur puisqu'il comprend une ou plusieurs couches de couleur bien individualisé et éventuellement une couche de papier en plus de la couche de base en carton.
Par ailleurs, il est clair que le stratifié coloré connu n'est pas obtenu par décoloration ou transcoloration d'un con~iml-lm fibreux de couleur initial donné.
30 Le brevet ~llem:ln-l DE 67 632 C concerne un procédé de coloration d'une face de papier conçue de manière à éviter la migration du colorant d'une face à l'autre du substrat papier considéré, et ce afin de pouvoir colorer les deux faces indép~n~fmm~nt l'une de l'autre. Selon ce procédé on fait passer la bande de papier entre un cylindre de séchage .~ " ~ référencé
X et un cylindre de coloration référencé B La chaleur apportée par le cylindre de séchage X
35 permet de sécher rapidement le colorant et ainsi de le fixer à la surface du papier.
CA 02224~06 1998-01-21 -Ce procédé ainsi que le papier coloré qu'il permet d'obtenir, ne présentent pas les deux caractéristiques suivantes: I'homogénéité dans l'épaisseur (couche de colorant en surface) et l'obtention par décoloration ou transcoloration sur au moins une des faces d'une couleur initiale donnée.
Il ressort de cette revue de l'art antérieur que les papiers de sécurité
cormus, ~llth~ntifi~hles par déchirure et/ou s--ffi~mment opaques pour pouvoir être utilisés comme supports de billets de loterie in~ és ou de tickets de jeu grattables (absence de transvision), sont le plus souvent des supports fibreux multicouchesobtenus par la technique du couchage.
Or, on sait que cette technique est relativement coûteuse notamment en raison du fait qu'il est néc~s.s~ire de la réaliser la plupart du temps hors du circuit classique de la machine à papier. Il est clair que cela nuit à la productivité et à la rentabilité du procédé de fabrication de papiers. Par ailleurs, le couchage est une opération qui peut être très aisément reproduite avec des moyens arti~n~--x Cela ne fait qu'aug~nenter les risques de contrefaçon.
En outre, force est de constater que le couchage n'apporte pas de solution réellement s~ti~f~ nt~, en ce qui concerne le problème de la dél~min~tion. La persistance, dans les structures couchées, de ce problème inhérent à l'origine aux structures multi-l~m~ ires, est soulignée dans la d~m~ntle de brevet européen N~ 0 668 092 page 2 lignes 29-30.
Dans cet état de faits, I'un des objectifs essentiels de la présente invention, est de fournir un support fibreux, en particulier, un papier de sécurité, ~lltll~ntifi~ble par déchirure et susceptible de constituer un substrat opaque approplié pour la réalisation de ticket de jeu grattable, qui remédie aux inconvénients des papiers de sécurité couchés selon l'art antérieur.
Un autre objectif essentiel de l'invention est que ce papier de sécurité
réponde aux spécifications suivantes:
- authentifiable par déchirure, - non d~l~min~ble, inf~ ifi~ble, - totalement opaque de façon à ne pas être sujet à la fraude par transvision dans les tickets de jeu à gratter, - economlque, - offrant de bonnes qualités d'imprimabilité et d'écriture, - non reprod,uctible ~ m~nt par voie artisanale.
CA 02224~06 1998-01-21 Un autre objectif essentiel de la présente invention est de fournir un procédé d'obtention d'un support fibreux en particulier d'un papier de sécurité,authentifiable par déchirure, non dél~min~ble et totalement opaque, ledit procédé se devant d'être aisé à mettre en oeuvre et économique, du fait de sa parfaite intégration dans les lignes de fabrication classique du papier.
Un autre objectif essentiel de la présente invention est de fournir un papier de sécurité ~llth~ntifi~hle par déchirure, constitué par le support fibreux évoqué ci-dessus dans les objectifs de l'invention.
Un autre objectif essentiel de la présente invention est de fournir un ticket 10 de jeu à gratter réalisé à partir du susdit support fibreux.
S'étant fixée ces objectifs, la D~m~n-1eresse a eu le mérite de mettre en évidence, après de nombreuses recherches et eXpériment~tions~ qu'il convient de prévoir un support fibreux opaque, en particulier en papier, formé par un seul et même réseau fibreux homogène, initialement coloré puis transformé ultérieurement au 15 niveau de ces deux faces externes sur une certaine épaisseur, par décoloration et/ou transcoloration, de manière à obtenir une structure sandwich du type:
tranche externe blanche ou d~e couleur Cl/~ranche médiane de couleur C2 = ou ~ de Cl~et éventuellement tranche externe blanche ou de couleur Cl ou C3, avec dans le cas où Cl = Cz = C3 un gradient de couleur clair ~ foncé
20 de l'extérieur vers l'intérieur.
Il s'ensuit que la présente invention a pour objet un support fibreux opaque 1, en particulier papier, caractérisé en ce qu'il est obtenu à partir d'un seul et même matelas fibreux:
~ homogène, notamment dans son épaisseur;
~ produit à partir d'un seul jet fibreux;
et initialement de couleur (C2), puis décoloré ou coloré
di~él~."",ent, au moins partiellement sur au moins une de ses faces, pour former au moins une tranche externe (3,4) blanche ou de couleur (C1, C3), di~é~ e et/ou moins foncée que la couleur initiale (Cz).
Un tel support fibreux, en particulier un papier de sécurité, a pour avantage d'être non dél~min~ble, d'être totalement opaque, peu onéreux et facilement obtenable dans une m~f~hine à papier, sans modifications substantielles de cettedernière.
Par ailleurs, son,caractère industriel limite quelque peu les risques de contrefaçon selon un mode artisanal.
CA 02224~06 1998-01-21 Selon une variante, le support fibreux est obtenu à partir d'un seul et même matelas fibreux:
homogène, notamment dans son épaisseur;
~ produit à partir d'un seul jet fibreux;
S ~ et initialement de couleur (C2), puis décoloré ou coloré diLrélelllnlent, au moins partiellement sur au moins une de ses faces, pour former, d'une part, au moins une tranche externe (3,4) blanche ou de couleur (Cl, C3), di~élen~e et/ou moins foncée que la couleur initiale (C2) et d'autre part, au moins une tranche (2) sensiblement médiane de couleur (C2).
Dans la mesure où l'on vise des supports fibreux, en particulier des papiers de sécurité authentifiables par déchirure, il en résulte que le mode préféré mais non lil"il~irde réalisation de l'invention correspond à un SUppOlt fibreux comportant une tranche sensiblement médiane colorée, attenante par chacune de ses faces à une 15 tranche externe blanche ou de couleur di~elellle et/ou moins foncée que la tranche médiane, les deux tranches externes étant de même couleur ou non.
On aura reconnu là une structure multicolore, par exemple bicolore, de type sandwich: couleur Cl/couleur C2/couleur C3 avec Cl identique ou di~~ L à C3 et C2 identique ou différent à Cl et 20 ~3~
avec la condition selon laquelle, si C2 = Cl ou C3 alors C~ ou C3 est plus clair que C2.
Cette structure opaque non dçl~min~ble répond parfaitement aux spécifications évoquées supra.
La structure en réseau fibreux homogène et cohérent du support selon l'invention, est liée à sa formation en un seul jet fibreux sur la machine à papier.
La figure unique annexée montre une vue en coupe transversale d'un tel support selon le mode préféré de l'invention, à titre purement exemplatif non limit~tif Cette figure montre un support 1 formé d'un seul et même réseau fibreux d'épaisseur e comprenant dans son épaisseur une tranche médiane 2 de couleur C2,ladite tranche 2 follllanL un contin~1llm structurel fibreux avec les deux tranches externes 3 et 4 de couleur C1 et C3 respectivement.
Dans cet exemple C1, C2 et C3 correspondent à la même couleur de base sachant que ~C1 et C3 sont nett~m~nt plus clairs que C2, à tel point qu'ils sont proches du blanc.
CA 02224~06 1998-01-21 Une telle structure opaque bicolore, non ~lél~min~ble est e~ e d'une marque de reconn~i.ss~nce inf~lci~kle~ correspondant à la couleur C2 de la tranche médiane 2, ce qui la rend parfaitement authentifiable par déchirure.
Selon une variante du support fibreux de sécurité selon l'invention, celui-ci est caractérisé en ce qu'il est obtenu à partir d'un matelas fibreux initialement coloré, puis décoloré au moins partiellement sur au moins une de ses deux faces, de pler~lellce les deux, pour former, les deux tranches externes 3 et 4 situées de part et d'autre de la tranche 2 médiane colorée.
Cette variante correspond à la structure sandwich: blanc ou marron très clair~marronfoncé~blanc marron très clair, représentée sur la Figure unique annexée et décrite ci-dessus. Dans cette variante, le contraste de couleur extérieur/intérieur est obtenu par l'intermédiaire d'un agent de décoloration absorbé par les faces du support fibreux considéré, sur une épaisseur variable en fonction de la pénétrabilité dudit agent à l'intérieur du support.
Selon une autre variante, correspondant au cas où C2 est diLrélelll de Cl etlou de C3, le support fibreux est obtenu à partir d'un matelas fibreux initialement coloré puis coloré di~~ ent au moins partiellement sur au moins une de ces deux faces, de plerelellce les deux, pour former les deux tranches externes 3, 4 situées de part et d'autre de la tranche médiane 2 colorée.
Dans le premier cas, I'agent de coloration réagit avec l'agent dle décoloration tandis que dans le second cas, il réagit avec un agent de transcoloration trans~ormant C2 en C, et C3 dans les couches superficielles du support fibreux 1.
L'existence de ces deux variantes structurelles (parmi d'autres) pour le support selon l'invention, entrâîne des particularités constitutionnelles. C'est ainsi que le support fibreux est caractérisé en ce qu'il comprend au moins un agent de coloration et éventuellement au moins un agent de décoloration et/ou au moins unagent de transcoloration, n'ayant pas réagi mais aptes à réagir avec l'agent de coloration dans les tranches externes.
Avantageusement, le couple agent de coloration/agent de décoloration et/ou transcoloration est choisi dans le groupe suivant:
CA 02224~06 1998-01-21 Agent de coloration Agent de décoloration et/ou de transcoloration oxyde métallique réducteur sel métallique séquestrant indicateur coloré de pH milieu à pH choisi indicateur coloré d'oxydo-réductionmilieu à potentiel Redox choisi colorant agent de dégradation du colorant et leurs mélanges Les oxydes ou les sels colorés métalliques, tels que les sels de fer ou de m~n~nèse~ peuvent être décolorés par des agents réd~1cte--rs ou par des séquestrants, tel que par exemple l'EDTA ou le phosphate mono-potassique.
S Sans que cela ne soit limit~tif on peut citer encore d'autres exemples de couple agent de coloration / agent de décoloration, e.g.:
- oxyde met~llique/récl~lctel-r = oxyde de cuivre ou de cobalt /
bisulfite en milieu acide, - sel mét~llique/séquestrant = sel de fer ou de v~n~ m / acide ascorbique.
Les indicateurs colorés de pH utilisables comme agent de coloration sont aisément décolorables, en faisant pénétrer sur les faces du matelas fibreux un milieu liquide de pH tel qu'il ramène l'indicateur sous une forme incolore ou dans une couleur diLrelellle. Ainsi, par exemple, la phénolphtaléine introduite initialement dans la pate à papier, est portée à un pH basique qui entrame une coloration rose de cette dernière. Une enduction superficielle ultérieure du matelas fibreux par un acide, amène la phénolphtaléine sous une forme incolore, correspondant à un pH acide.
Comme autre exemple d'indicateur de pH susceptible d'être utilisé comme agent decoloration, on mentionnera le rouge de phénol, le pourpre de bromocresol ou le bleu de bromophénol.
Les indicateurs colorés d'oxydo-réduction fonctionnent selon le meme principe que les indicateurs de pH évoqués ci-dessus, à la différence près bien enten(~ que le paramètre clé n'est pas le pH, mais le potentiel redox. Comme exemple de couple agent de coloration/agent de décoloration ou de transcoloration, on peut citer le bleu de méthylène ou le rouge neutre en combinaison avec l'eau de javel.
Les colorants constituent une autre classe d'agents de coloration convenables conformément à l'invention. Il peut s'agir not~mment des colorants CA 02224~06 1998-01-21 susceptibles d'être décomposés par des réactifs oxydants, comme par exemple l'eau de javel ou bien encore des sulfites, des bisulfites, des acides, des bases...
A titre d'illustration, on peut mentionner comme exemple les colorants avec la structure chimique du triphenyl méthane tel que le BLEU DUASYN POUR ENCRES
5 BJT de la société HOESCHT. Cet agent de coloration peut être associé à des agents de décoloration formés par de l'eau de javel et/ou par une base faible, ou bien encore par du sulfite de sodium.
Comme autre exemple de colorant entrant dans la constitution du support fibreux selon l'invention et susceptible de réagir avec des agents de dégradation t;llLI~înanl un 10 changement de couleur, on peut citer le rouge de crésol associé à l'eau de javel dans le bain de décoloration/transcoloration.
Pour illustrer la variante de réalisation selon laquelle le support fibreux comprend au moins un agent de coloration et au moins un agent de transcoloration, on évoquera les exemples suivants:
* le JAUNE LEVACELL 3 GX de la société BAYER en combinaison avec une solution basique.
* la SAFRANrNE O avec une solution d'eau de javel.
Outre, les moyens chimiques de décoloration et de transcoloration, on peut avoir recours, en complément ou en substitution à ces derniers, à des moyens physiques ayant les mêmes effets. Il peut s'agir par exemple:
- de rayonnement actiniques tels que les W et/ou les infra-rouges - la chaleur, - le bombardement d'électrons, - I'exposition à un faisceau laser, - les traitements aux ultra-sons ou aux micro-ondes - etc.
Le support fibreux de sécurité selon l'invention peut également être défini au travers de ses caractéristiques physiques particulières. Ainsi, avantageusement, son gramrnage est supérieur ou égal à 80 g/m2, de pli;r~;rence compris entre 100 et 400 g/m2 et, plus pl~relenliellement encore entre 120 et 300 g/m2.
Le ~ ",l"age du papier est un paramètre important au regard de la pénétrabilité des agents de décoloration/transcoloration. Il importe, en effet, que ceux-ci pénètrent à
l'intérieur du support fibreux sur une épaisseur snffi.~nte pour que le changement de couleur soit apparent, mais il est évident que cette pénétration ne doit pas être trop importante de manière à cons,erver une tranche médiane colorée en foncé ou colorée CA 02224~06 1998-01-21 .
cli~,;;",ll,ent, qui soit d'épaisseur signifcative pour permettre l'authentification par déchirure.
Ce controle de la pénétration des agents de décoloration peut également être obtenu en jouant sur le taux de raf3~inage des fibres con.~tihl~nt le support et donc 5 sa porosité ainsi que sur le collage, c'est-à-dire son aptitude au remouillage ultérieur par la solution de décoloration/transcoloration.
De pri;fé,t;nce, le taux de raffinage du support fibreux sera compris entre 15 et 55~ SR
(SHOPPER RIEGLER), et plus pl~rel ell~iellement encore entre 30 et 45~ SR. Il va de soi que la valeur du raffinage dépendra également du grammage du papier. L'homme10 du métier est parfaitement à même de déterminer les valeurs idoines de ces deux paramètres liés l'un à l'autre.
S'~gi.~s~nt du collage, l'agent utilisé peut être une colle classique de colophane, un alkyl cétène dimère ou tout autre produit permettant d'atteindre une valeur classique pour ce paramètre, comprise entre 15 et 30 g/m2 en valeur COBB, et plus 15 particulièrement de 16 à 20 glm2.
On reviendra ci-après dans le cadre de la description du procédé, sur un autre facteur important quant à la pénétrabilité, à savoir la viscosité du liquide contenant les agents de décoloration/transcoloration.
En tout état de cause, ces paramètres peuvent varier énormement en 20 fonction du grammage du support fibreux considéré. En effet, le problème de la pénétration des agents de décoloration/transcoloration est di~i;l t;ll~ pour un grammage léger, de moins de 120 g/m2 et pour un grammage plus lourd, au dessus de 200 glm2. I1 est très rare dans ce dernier cas que, même sans précaution particulière au niveau du support, la solution de décoloration/transcoloration pénètre jusqu'au 25 coeur de la feuille et décolore ou change la couleur du papier sur son épaisseur totale.
Suivant une disposition préférée de l'invention7 on choisit de réaliser un papier ou un support fibreux à intérieur coloré et à opacité renforcée7 en utili.~nt un agent de coloration intense apte à former une couleur sombre (e.g. brun ou marron:
oxyde de m~ng~nèse) Conformément à l'invention, le support fibreux de sécurité considéré peut avoir une composition fibreuse quelconque: soit purement cellulosique7 soit en partie synthétique.
De manière classique7 les fibres cellulosiques appropriées peuvent être des fibres de feuillus, des fibres de résineux... ou des mélanges d7entre elles.
35 Concernant les fibres synthét,iques, il peut s7agir par exemple de fibres de polyester7 polyamide ou polyoléfines.
CA 02224~06 1998-01-21 ~n pratique, le taux de fibres synthétiques par rapport au poids sec total de fibres cellulosiques + synthétiques, est de l'ordre de 10 à 30 % en poids et de pr~ré~ellce 15 %.
Avantageusement, le support fibreux selon l'invention peut ~on~p~endre 5 des adjuvants classiques de papeterie, à savoir:
- des charges minérales ou organiques du type kaolin, carbonate de calcium, talc...
- des résines ou des agents de résistance divers, pour amener notamment des propriétés de résistance à l'état humide, - des liants du type amidon ou carboxymethyl cellulose pour améliorer les caractéristiques mécaniques des papiers, - des colorants de nuançage, - des produits de collage neutre, acide ou basique (sulfate d'alumine pour collage acide ou réglage du pH
- etc.
n peut également être envisagé, co~ ément à l'invention, d'incorporer des agents d'authentification supplément~ires à l'intérieur du support fibreux. Il peut s'agir par exemple de fils de sécurité, de planchettes et de fibres colorées, ou non, fluorescentes, ou non, ainsi que des agents permettant l'infalsification, à savoir par exemple des colorants insolubles dans l'eau mais organosolubles, à l'état pip;mçntslire~de facon à préserver les écritures ou les mentions imprimées portées sur ces supports fibreux, vis-à-vis des tentatives de falsification, à l'aide d'effaceurs comprenant des solvants organiques.
En définitive, de nombreux additifs peuvent être compris dans le support fibreux selon l'invention, à la condition qu'ils ne soient pas dégradables par les moyens de décoloration / transcoloration, qui doivent pénétrer à l'intérieur dudit support fibreux.
Selon un autre de ces aspects, la présente invention vise également un procédé d'obtention d'un support fibreux, en particulier de papier, constitué
not~mmçnt par un seul et même matelas fibreux, homogène notamment dans son épaisseur, opaque et compr~llalll, dans son épaisseur, au moins une (de plt;r~rence une) tranche sensiblement médiane colorée et au moins une (de pl~r~lence deux) tranche externe blanche ou de couleur di~lell~e et/ou moins foncée que la tranche médiane, caractérisé en ce qu'il consiste essentiellement, -1 - à plc~parer une pate fibreuse - de plc;ré~ence une pâte à papier, en y incorporant au moins un agent de coloration, CA 02224~06 1998-01-21 CA 02224 =, 06 1998-01-21 PAP ~ OPAQUE SECURITY ER, AUI ~ lENTrFL ~ WHEAT PA ~ R DEC ~ DRURE, Ilch ~ ETS OF GAME TO GET ~ TTER REALIZED TO PA ~ REMOVE FROM SAID PAPER AND ITS
MANUFACTURING PROCESS
The field of the present invention is that of fibrous supports writing and / or printing, known as security, in particular of paper These supports fibrous or security paper are useful for the production of security documents such as admission or travel tickets, checks, legal documents or official, docl-ment. ~ credits, insurance certificates, tickets show, train, plane or the like or even game tickets or 10 scratch lottery, also called lottery tickets in ~ t ~ nt ~ born.
More specifically, the invention relates to fibrous supports such as security papers inf ~ lsifi ~ hles because authentifiable by a tear revealing a structure in sand ~, multicolored vich. This mode of authentication and fight against Counterfeits is used in ticketing, where important values may be at stake.
The present invention also relates to fibrous supports, in particular security papers which are suitable for writing and writing and which can be employed to make scratch tickets which information printed and masked must not be revealable by transvision and which allow also to avoid another type of fraud by del ~ min ~ tion.
Direct lentification by tearing of a fibrous support sheet for example in paper, reveals a multicolored sandwich structure:
colored inside and two white, clear or colored outside edges dif ~ erent. This characteristic structure makes it possible to certify with certainty the good origin of certain titles, sometimes of very high value, such as 25 transport, show tickets or other. To the extent that this technique tear identification is fast and safe, it is perfectly competitive compared to other known systems such as watermarking, which has existed for a long time for a long time, or even the introduction of fibers or safety threads. Some of these known systems, (including fluorescent dots or fibers or 30 phosphorescenl-es), have the disadvantage of requiring an apparatus of revelation for authentication. A typical example of such an apparatus is the larnpe W.
It follows that the fibrous supports or opaque security papers and multicolored sandwich structure giving them tear authenticity 35 should have no difficulty carving out a place for themselves, especially in inf ~ l ~ ifi ~ hles transport and ticketing applications, as far as possible CA 02224 ~ 06 1998-01-21 be removed a major defect consisting in the character del ~ min ~ ble supports fibrous or tear-proof papers, existing today. This defect prohibitive is linked to the structure and the method of manufacture of these fibrous supports or known security papers.
We thus know a first type of structure in which three layers of papers are joined together by min ~ tion, the middle layer being colored and the outer layers being white.
The second known type of structure is formed by a sheet of paper colored, which is treated by coating on at least one of its faces using a 10 white or opacifying coating composition.
The coating of colored substrates in the area of security papers has been disclosed a long time ago, even if the goal then sought and displayed was not not to provide authenticated papers by tear. This is how the patent American N ~ 1,417,820 describes a method for rendering paper 15 coating the two sides of black paper with a opaque coating and sensitive to solvents contained in ç ~ ce lrs ink usable for falsification purposes. So here we are in the presence of a structure sandwich of the light coating / black paper coating type or dark color ~ light color coating.
Also known in the field of security papers, that disclosed by British Patent N ~ 1,435,686, which is designed to withstand surface abrasion fraud attempts to remove printing ink and writing. This security paper includes a base sheet of paper, coated with an opaque coating sensitive to abrasion and consisting of a non-metallic pigment 25 (clay or TiO2) dispersed in a binder (synthetic polymer = vinyl copolymer /
acrylic-styrene / acrylic-styrene / butadiene or natural polymer-cellulose-starch-casein). The base sheet of paper has a color which contrasts with that of the coating so as to be able to reveal the traces of abrasion of the upper layer by transvision. This patent does not teach a sandwich structure:
30 light or white color / different or darker color / light or white color * e.
The coating of colored paper using an opacifying composition or white is also used in the area of security papers dedicated to a particular destination, which is the production of tickets in ~ t ~ nt ~ born of lottery or 35 any other analogous type of scratch-off game tickets. Such articles contain printed, hidden information which can be, on the one hand, a number, a CA 02224 ~ 06 1998-01-21 .
symbol7 a message possibly giving rise to a gain, and on the other hand, a security number to prevent counterfeiting, cons. Hiding these information conventionally is obtained by means of a scrapable, opaque layer con ~ lallL, for example, a metallic pigment (~ lllmini ~ m) dispersed in a binder forl ~ born by a rubber latex or other hydrocarbon polymers (see layer 28 of the lottery ticket, described in US Patent N ~ 4,726,608). Besides this opaque layer, the ticket comprises as a coating of a paper substrate 18, top to bottom, a non-stick layer 26, made of polyamide, a protective layer 25 in maleic vinyl acetate copolymer, printed characters 24, one layer plilllail in amorphous silica + maleated vinylacetate polymer + n-propyl acetate solvent and finally an alllminil1m sheet 20 attached to the paper substrate 18.
To try to eliminate the disadvantages linked to the presence of the leaf of ~ minillm in this type of scratch ticket, the European patent N ~ 0 428 489, proposes the use of coated paper for the manufacture of such articles. The paper of security disclosed by this patent colllplelld a basic paper substrate, a weight of the order of 225 g / m2, colored with carbon black, so as to be completely opaque and coated with a conlprellall composition ~ pigments such than titanium clay or dioxin, latex or starch. The faces of the paper coated thus obtained are white, smooth and uniform, therefore printable. These papers are presented as non-l ~ min ~ bles. To make a delotery ticket in. ~ Nt ~ born, it is planned to perform printing on the faces of the coating coating then proceed to a final coating using colored and scrapable latex classic. This patent therefore discloses a sandwich structure: coating coating white / black opaque paper substrate / white coating.
The European patent clem N ~ 668,092 discloses an invention relating to lottery ticket papers in ~ t ~ nt ~ born (scratch), which recommend to bring opacity to the paper not through the paper substrate of base as proposed in European patent N ~ 428,489, but through an opaque coating coating applied to said paper base substrate and complenanl a pigment of the carbon black type dispersed in a binder of the latex type of styrene / butadiene copolymer. This opaque layer is also coated with a upper layer of impl-ession, obtained from a colllpl ~ nall ~ composition of styrene / butadiene latex, CaCO3 and styrene-acrylic polymer microspheres.
FR-A-2 192 211 discloses a process for coloring or dyeing absorbent paper at surface nl ~ le ~ ls ~ 7 with as little dye layer thickness as possible but nevertheless making it possible to obtain a uniform shade from an optical point of view.
CA 02224 ~ 06 1998-01-21 Once colored on one side, the paper can be coated with a layer of resin thermosetting synthetic.
To obtain this un; fu "~ é coloring despite the rugged relief of the surface of the absorbent paper considered, this method provides for subjecting the face of the paper to color in a dyeing operation by magnetic calendar or with rollers magnetic, aiming to deposit the dye in all the hollows and pores, and at a i.llpl ~; s ~ ion operation by intaglio or intaglio printing typoflexographic aiming at ensuring the coloring of the bumps and the reliefs.
According to the teaching of this d ~ m ~ n ~ only one side of the paper is colored.
10 The paper obtained by this process is not homogeneous in its thickness since has a layer of dye on the surface which, although being as weak as possible does exist and gives a heterogeneity to the paper in its thickness.
Furthermore, this colored absorbent paper is not obtained from one and the same fibrous mattress of initial color C2 then discolored then or colored di ~ ent at 15 at least partially on at least one of its faces to form at least one edge external white or of color Cl-C3 (di ~ elen ~ e and / or less dark than the initial color C2) FR-A-537 357 relates to improvements in the production of cardboard and paper colored. More precisely, this French patent discloses colllplt laminates; llallL une 20 cardboard base layer, on one or both sides of which is glued a layer of paper, the surface of which is colored using means formed by color reservoirs 10 and by an apparatus 11 intended to adjust the layers of color.
According to a variant, the cardboard can be colored directly on one of its faces by one or more layers of color.
25 Again, it cannot be disputed that this laminate is not homogeneous in its thickness since it comprises one or more layers of well individualized color and possibly a layer of paper in addition to the base layer of cardboard.
Furthermore, it is clear that the known colored laminate is not obtained by discoloration or transcoloration of a con ~ iml-lm fibrous of initial color given.
30 The ~ llem patent: ln-l DE 67 632 C relates to a process for coloring a face of paper designed to avoid migration of the dye from one side to the other of the paper substrate considered, in order to be able to color the two independent faces ~ n ~ fmm ~ nt from one another. According to this process passes the strip of paper between a drying cylinder. ~ "~ referenced X and a coloring cylinder referenced B The heat provided by the drying cylinder X
35 allows the dye to dry quickly and thus fix it to the surface of the paper.
CA 02224 ~ 06 1998-01-21 -This process as well as the colored paper which it makes it possible to obtain, do not have both following characteristics: the homogeneity in the thickness (layer of dye in surface) and obtaining by discoloration or transcoloration on at least one of the faces of a given initial color.
It emerges from this review of the prior art that security papers cormus, ~ llth ~ ntifi ~ hles by tearing and / or s - ffi ~ even opaque to be able to be used as supports for lottery tickets or scratch-off game tickets (absence of transvision), are most often multilayered fibrous supports obtained by the coating technique.
However, we know that this technique is relatively expensive, particularly in due to the fact that it is nec ~ ss ~ ire to realize it most of the time outside the circuit classic paper machine. Clearly, this hurts productivity and profitability of the paper manufacturing process. Furthermore, sleeping is a operation which can be very easily reproduced with arti ~ n ~ --x means This does not increases the risk of counterfeiting.
In addition, it is clear that the coating does not provide a solution actually s ~ ti ~ f ~ nt ~, regarding the problem of del ~ min ~ tion. The persistence, in recumbent structures, of this problem inherent originally in multi-l ~ m ~ ires structures, is underlined in the European patent d ~ m ~ ntle N ~ 0 668 092 page 2 lines 29-30.
In this state of the facts, one of the essential objectives of the present invention, is to provide a fibrous support, in particular, a security paper, ~ lltll ~ ntifi ~ ble by tearing and capable of constituting an opaque substrate suitable for the making a scratch-off game ticket, which overcomes the disadvantages of safety coated according to the prior art.
Another essential objective of the invention is that this security paper meets the following specifications:
- authenticated by tearing, - not minable, inf ~ ifi ~ ble, - completely opaque so as not to be subject to fraud by transfer to scratch-off game tickets, - economlque, - offering good printability and writing qualities, - not reproduced, usable ~ m ~ nt by artisanal way.
CA 02224 ~ 06 1998-01-21 Another essential objective of the present invention is to provide a process for obtaining a fibrous support, in particular security paper, which can be authenticated by tearing, not del ~ min ~ ble and completely opaque, said process having to be easy to implement and economical, due to its perfect integration in the classic paper manufacturing lines.
Another essential objective of the present invention is to provide paper security ~ llth ~ ntifi ~ hle by tearing, constituted by the fibrous support mentioned above above in the objectives of the invention.
Another essential objective of the present invention is to provide a ticket 10 scratching game made from the above fibrous support.
Having set these objectives, the D ~ m ~ n-1eresse had the merit of putting in evidence, after much research and experience ~ tions ~ that it should provide an opaque fibrous support, in particular made of paper, formed by a single and same homogeneous fibrous network, initially colored then transformed later on 15 level of these two external faces over a certain thickness, by discoloration and / or transcoloration, so as to obtain a sandwich structure of the type:
white or colored outer edge Cl / ~ middle ranch of color C2 = or ~ of Cl ~ and possibly white or colored outer edge Cl or C3, with in the case where Cl = Cz = C3 a clear ~ dark color gradient 20 from outside to inside.
It follows that the subject of the present invention is a fibrous support opaque 1, in particular paper, characterized in that it is obtained from a single and same fibrous mattress:
~ homogeneous, especially in its thickness;
~ produced from a single fibrous jet;
and initially colored (C2), then discolored or colored di ~ él ~. "", ent, at least partially on at least one of its faces, to form at least one white outer slice (3,4) or color (C1, C3), di ~ é ~ e and / or less dark than the initial color (Cz).
Such a fibrous support, in particular a security paper, has for advantage of not being del ~ min ~ ble, of being completely opaque, inexpensive and easily obtainable in a m ~ f ~ hine to paper, without substantial modifications of this last.
Furthermore, its industrial character somewhat limits the risks of counterfeiting in an artisanal fashion.
CA 02224 ~ 06 1998-01-21 According to a variant, the fibrous support is obtained from a single and same fibrous mattress:
homogeneous, especially in its thickness;
~ produced from a single fibrous jet;
S ~ and initially colored (C2), then discolored or colored diLrélelllnlent, at least partially on at least one of its faces, to form, on the one hand, at least one outer slice (3,4) white or colored (Cl, C3), di ~ élen ~ e and / or less dark than the initial color (C2) and on the other hand, at least one substantially median slice (2) of color (C2).
Insofar as one targets fibrous supports, in particular security papers that can be authenticated by tearing, it follows that the preferred mode but non lil "il ~ irde embodiment of the invention corresponds to a fibrous SUppOlt comprising a substantially median colored slice, adjoining by each of its faces to a 15 outer slice white or di ~ elellle color and / or less dark than the slice median, the two outer edges being the same color or not.
We will have recognized a multicolored structure, for example bicolour, of sandwich type: color Cl / color C2 / color C3 with Cl identical or di ~~ L to C3 and C2 identical or different to Cl and 20 ~ 3 ~
with the condition that, if C2 = Cl or C3 then C ~ or C3 is more clear that C2.
This opaque structure not dcl ~ min ~ ble responds perfectly to specifications mentioned above.
The homogeneous and coherent fibrous network structure of the support according to the invention is linked to its formation in a single fibrous jet on the paper machine.
The attached single figure shows a cross-sectional view of such support according to the preferred embodiment of the invention, purely by way of nonlimiting example ~ tif This figure shows a support 1 formed from a single fibrous network of thickness e comprising in its thickness a middle slice 2 of color C2, said slice 2 follllanL a fibrous structural ~ 1llm contin with the two slices external 3 and 4 of color C1 and C3 respectively.
In this example C1, C2 and C3 correspond to the same basic color knowing that ~ C1 and C3 are nett ~ m ~ nt lighter than C2, so much so that they are close to white.
CA 02224 ~ 06 1998-01-21 Such a two-color opaque structure, not ~ lel ~ min ~ ble is e ~ e of a mark of recognize ~ i.ss ~ nce inf ~ lci ~ kle ~ corresponding to the color C2 of the middle edge 2, this which makes it perfectly authenticated by tearing.
According to a variant of the fibrous security support according to the invention, it ci is characterized in that it is obtained from a fibrous mattress initially colored, then at least partially discolored on at least one of its two faces, of pler ~ lellce both, to form, the two outer slices 3 and 4 located on the side and on the other side of the colored middle section 2.
This variant corresponds to the sandwich structure: white or very brown clear ~ dark brown ~ white very light brown, shown in the attached single figure and described above. In this variant, the exterior / interior color contrast is obtained by means of a bleaching agent absorbed by the faces of the support fibrous considered, over a variable thickness depending on the penetrability of said agent inside the holder.
According to another variant, corresponding to the case where C2 is diLrélelll of Cl and or C3, the fibrous support is obtained from a fibrous mat initially colored then colored di ~~ ent at least partially on at least one of these two sides, of plerelellce the two, to form the two external sections 3, 4 located on either side of the colored middle section 2.
In the first case, the coloring agent reacts with the coloring agent.
discoloration while in the second case it reacts with a coloring agent trans ~ ormant C2 in C, and C3 in the surface layers of the fibrous support 1.
The existence of these two structural variants (among others) for the support according to the invention, entails constitutional particularities. Therefore the fibrous support is characterized in that it comprises at least one agent for coloring and optionally at least one discoloration agent and / or at least one transcoloration agent, which have not reacted but are capable of reacting with the coloring agent coloring in the outer edges.
Advantageously, the couple of coloring agent / bleaching agent and / or transcoloration is chosen from the following group:
CA 02224 ~ 06 1998-01-21 Coloring agent Discoloration and / or coloring agent transcoloration reducing metal oxide sequestering metal salt colored medium pH indicator at selected pH
colored redox indicator medium with selected Redox potential dye degrading agent dye and their mixtures Oxides or metallic colored salts, such as iron or m ~ n ~ nèse ~ can be discolored by red agents ~ 1cte - rs or by sequestrants, such as for example EDTA or mono-potassium phosphate.
Without limiting it, we can cite other examples of couple of coloring agent / bleaching agent, eg:
- metallic oxide / recl ~ lctel-r = copper or cobalt oxide /
bisulfite in acid medium, - metallic ~ sequestering salt = iron or v ~ n ~ m / acid salt ascorbic.
The colored pH indicators which can be used as a coloring agent are easily discolored, making a medium penetrate the faces of the fibrous mat pH liquid as it brings the indicator back in a colorless form or in a diLrelellle color. So, for example, the phenolphthalein initially introduced into the pulp, is brought to a basic pH which starts a pink coloration of this last. A subsequent surface coating of the fibrous mattress with an acid, brings the phenolphthalein in a colorless form, corresponding to an acidic pH.
As another example of a pH indicator capable of being used as a coloring agent, mention may be made of phenol red, bromocresol purple or blue bromophenol.
The colored redox indicators work according to the same principle that the pH indicators mentioned above, with the difference enten (~ that the key parameter is not the pH, but the redox potential. As example of a coloring agent / discoloration or transcoloration agent couple, we can cite methylene blue or neutral red in combination with water bleach.
Dyes are another class of coloring agents suitable according to the invention. It can be not ~ mment dyes CA 02224 ~ 06 1998-01-21 likely to be broken down by oxidizing reagents, such as water bleach or even sulfites, bisulfites, acids, bases ...
By way of illustration, the dyes with the chemical structure of triphenyl methane such as BLUE DUASYN FOR INKS
5 BJT from HOESCHT. This coloring agent can be combined with agents discoloration formed by bleach and / or a weak base, or alternatively with sodium sulfite.
As another example of dye used in the constitution of the fibrous support according to the invention and capable of reacting with degrading agents t; llLI ~ înanl un 10 color change, we can cite cresol red associated with bleach in the discoloration / transcoloration bath.
To illustrate the alternative embodiment according to which the fibrous support comprises at least one coloring agent and at least one transcoloration agent, the following examples will be mentioned:
* the YELLOW LEVACELL 3 GX from the company BAYER in combination with a basic solution.
* SAFRANrNE O with a bleach solution.
Besides the chemical means of bleaching and transcoloration, we may have recourse, in addition to or in substitution for these, to means with the same effects. It can be for example:
- actinic radiation such as W and / or infrared - the heat, - electron bombardment, - exposure to a laser beam, - ultrasound or microwave treatments - etc.
The fibrous security support according to the invention can also be defined through its particular physical characteristics. So, advantageously, its grammage is greater than or equal to 80 g / m2, ply; r ~; rence between 100 and 400 g / m2 and, more still, between 120 and 300 g / m2.
The ~ ", the age of the paper is an important parameter with regard to the penetrability of bleaching / transcoloring agents. It is important, in fact, that these penetrate inside the fibrous support on a snffi thickness. ~ nte so that the change of color is apparent, but it is obvious that this penetration should not be too important in order to cons, erve a middle section colored dark or colored CA 02224 ~ 06 1998-01-21 .
cli ~, ;; ", ll, ent, which is of significant thickness to allow authentication by tear.
This control of the penetration of bleaching agents can also be obtained by playing on the rate of raf3 ~ inage fibers con. ~ tihl ~ nt the support and therefore 5 its porosity as well as the bonding, that is to say its aptitude for subsequent rewetting by the bleaching / transcoloration solution.
De pri; fé, t; nce, the rate of refinement of the fibrous support will be between 15 and 55 ~ SR
(SHOPPER RIEGLER), and more pl ~ rel ell ~ iellement still between 30 and 45 ~ SR. It goes from the value of the refining will also depend on the grammage of the paper. Those skilled in the art are perfectly capable of determining the suitable values of these two parameters related to each other.
S ~ gi. ~ S ~ nt of bonding, the agent used can be a conventional rosin glue, a alkyl ketene dimer or any other product allowing to reach a conventional value for this parameter, between 15 and 30 g / m2 in COBB value, and more 15 particularly from 16 to 20 glm2.
We will return below in the context of the description of the process, to a another important factor with regard to penetrability, namely the viscosity of the liquid containing bleaching / transcoloring agents.
In any case, these parameters can vary enormously in 20 as a function of the grammage of the fibrous support considered. Indeed, the problem of penetration of bleaching / transcoloring agents is di ~ i; lt; ll ~ for a light weight, less than 120 g / m2 and for heavier weight, above 200 glm2. It is very rare in the latter case that, even without special precautions at the support level, the discoloration / transcoloration solution penetrates until 25 core of the sheet and discolour or change the color of the paper to its total thickness.
According to a preferred arrangement of the invention7, we choose to make a paper or a fibrous support with colored interior and with enhanced opacity7 in use.
intense coloring agent capable of forming a dark color (eg brown or brown:
oxide of m ~ ng ~ nèse) In accordance with the invention, the fibrous security support considered can have any fibrous composition: either purely cellulosic7 or partly synthetic.
Conventionally7 the suitable cellulosic fibers can be fibers of hardwoods, coniferous fibers ... or mixtures of them.
35 With regard to synthetic fibers, these may for example be polyester fibers7 polyamide or polyolefins.
CA 02224 ~ 06 1998-01-21 ~ n practical, the rate of synthetic fibers relative to the total dry weight of fibers cellulosic + synthetic, is around 10 to 30% by weight and pr ~ re ~ ellce 15%.
Advantageously, the fibrous support according to the invention can ~ on ~ p ~ endre 5 of the conventional stationery aids, namely:
- mineral or organic fillers of the kaolin, carbonate type calcium, talc ...
- various resins or resistance agents, to bring in particular wet strength properties, - binders of the starch or carboxymethyl cellulose type for improve the mechanical properties of papers, - shading dyes, - neutral, acidic or basic bonding products (alumina sulfate for acid bonding or pH adjustment - etc.
n can also be considered, co ~ ément to the invention, to incorporate authentication agents supplement ~ ires inside the fibrous support. he can for example, safety threads, boards and colored fibers, or not, fluorescent, or not, as well as agents allowing tampering, namely by example of dyes insoluble in water but organosoluble, in the state pip; mçntslire ~ in order to preserve the writings or the printed mentions carried on these fibrous supports, vis-à-vis attempts at falsification, using erasers comprising organic solvents.
Ultimately, many additives can be included in the carrier fibrous according to the invention, provided that they are not degradable by discoloration / transcoloration means, which must penetrate inside said fibrous support.
According to another of these aspects, the present invention also relates to a process for obtaining a fibrous support, in particular paper, consisting not ~ mmçnt by a single fibrous mattress, homogeneous especially in its thickness, opaque and compr ~ llalll, in its thickness, at least one (plt; r ~ rence a) substantially median colored slice and at least one (pl ~ r ~ lence two) white or di ~ lell ~ e outer edge and / or less dark than the edge median, characterized in that it consists essentially, -1 - plc ~ adorn a fibrous pulp - plc; re ~ ence a paper pulp, incorporating therein at least one coloring agent, CA 02224 ~ 06 1998-01-21
- 2 - à mettre cette pâte sous forme d'un support constitué par une seule et même feuille fibreuse, réalisée par monojet, - 2 - to put this paste in the form of a support constituted by a single and same fibrous sheet, produced by monojet,
- 3 - à éliminer au moins en partie l'eau présente dans le support-feuiUe, - 3 - at least partially eliminating the water present in the support -leafy,
- 4 - à décolorer et/ou à transcolorer au moins une tranche externe du support-feuille avant, pendant ou après l'élimin~tion d'eau Un tel procédé est l'un de ceux permettant d'obtenir le support fibreux con.~tif~1~nt le premier objet de la présente invention décrit ci-dessus Selon un mode préféré de mise en oeuvre du procédé, le support fibreux 10 visé (e g le papier) présente une tranche sensiblement médiane colorée et, de part et d'autre de celle-ci, une tranche externe blanche ou de couleur dirrérc;"~e et/ou moins foncée que la tranche médiane. Ces deux tranches externes sont de couleurs identiques ou di~e~ es. Conformément au mode préféré, on effectue la décoloration et/ou la transcoloration à l'aide de moyens chimiques et/ou physiques.
Un tel support fibreux correspond au mode préféré de réalisation du produit selon l'invention tel que décrit ci-avant et représenté dans la figure unique annexée.
L'étape I de préparation de la pâte fibreuse correspond à une opération relativement classique dans le domaine de la papeterie. Dans une m~chine à papier, cette opération intervient au niveau de la caisse de tête ou lors de la préparation de la pâte au pulpeur. En l'occurrence, il s'agit simplement de rajouter à la pâte au moins un agent de coloration et de réaliser un mélange homogène.
L'étape 2 est effectuée par l'intermédiaire de la filière de la caisse de tête de la machine à papier qui permet de produire en monojet un matelas fibreux contenant l'agent de coloration, ce matelas étant ensuite acheminé vers les modules d'égouttage, de pressage, puis de séchage de la machine à papier.
Ces trois modules ont vocation à satisfaire l'étape 3 d'elimin~tion de l'eau présente dans le support-feuille.
Dans le cas où l'on a affaire à une décoloration et/ou à une transcoloration chimique, conformément à un mode préféré de mise en oeuvre du procédé selon l'invention, I'étape 4 est réalisée par application d'un bain d'agent de décoloration et/ou transcoloration, à l'aide d'un dispositif prévu de pl ~rérence dans la machine à papier. De manière plus préférée encore, ce dispositif d'enduction est une presse encolleuse ou ~ Size Press ~ traditionnelle, voire une ~ blade metering size press ~, ou un ~ gate-roll~. U,ne telle presse encolleuse est usuellement située après la présécherie.
CA 02224~06 1998-01-21 Dans l'hypothèse moins avantageuse où l'enduction du bain de décoloration ou de transcoloration est réalisée, au sortir de la machine à papier, il est possible d'envisager soit l'emploi de moyens de couchage en ligne, tels que e.g. des dispositifs à lame métallique ou à lame d'air, soit les techniques d'hl~pl~ssionS traditionnelles.
n est à signaler que tout moyen convenable pour faire pénétrer une solution de décoloration/transcoloration dans le support fibreux, peut être substitué aux moyens classiques évoqués ci-dessus.
Tl va de soi que les concentrations en agent de décoloration/trans-10 coloration mis en oeuvre dans les bains d'enduction, sont déterminées en fonction dela quantité d'agent de coloration contenus dans le support fibreux et en fonction de la stoechiométrie de la réaction correspondante. Ces modalités opératoires sont parfaitement à la portée de l'homme du métier.
S'~ s~nt de la nature des agents de coloration ainsi que des agents de 15 décoloration/transcoloration, on se reportera à la description et aux définitions données à ce propos supra, dans la partie du présent exposé relative aux supports fibreux pris en tant que tels.
Comme déjà signalé auparavant, la pénétrabilité de l'agent de décoloration ou de transcoloration à l'intérieur du support fibreux, est une disposition 20 fondamentale du procédé selon l'invention. Les paramètres permettant d'exercer un contr81e sur ce point sont, d'une part, le g,~"u"age, le taux de raffinage et le collage du support fibreux et, d'autre part, la viscosité du bain d'enduction.
Ainsi, la viscosité de la solution de décoloration/transcoloration est ajustée en jouant sur la matière sèche et/ou en utilisant des liants filmogènes (amidon, cellulose...). Cet ajustement de viscosité est e~ectué en fonction de la nature du réactif de décoloration/transcoloration, de meme qu'en fonction de sa réactivité.
Il va de soi que les paramètres ~ s~nt sur la pénétrabilité de l'agent de décoloration/transcoloration sont inter-dépendants. Ainsi, au plus le grammage du support fibreux sera faible, au plus la viscosité du bain d'enduction devra etre élevée.
En pratique on peut indiquer, à titre d'exemple:
- que pour un grammage de 120 glm2, la viscosité du bain est avantageusement supérieure ou égale à 100 mPa.s, - et que pour un grammage de 150 g/m2, la viscosité est avantageusement supérieure ou égale à 80 mPa.s, - et que pour un grammage de 200 glm2, la viscosité du bain est avantageusement supérieure à 30-50 mPa.s.
~ CA 02224~06 1998-01-21 A titre d'exemple de liant hydrosoluble, on peut mentionner par exemple:
la carboxyméthylcellulose, I'amidon, I'alcool polyvinylique qui sont des liants naturels, employés de façon plus privilégiée, sans que soient exclus les liants synthétiques tels que les latex acryliques ou styrène-butadiènes.
Avantageusement, pour l'étape 4, on met en oeuvre, dans le cas d'une décoloration/transcoloration par moyen chimique, un couple agent de coloration/agent de décoloration et/ou transcoloration choisi dans le groupe suivant:
Agent de coloration Agent de décoloration et/ou de transcoloration oxyde métallique réducteur sel métallique séquestrant indicateur coloré de pH milieu à pH choisi indicateur coloré d'oxvdo-réductionmilieu à potentiel Redox choisi colorant agent de dégradation du colorant et leurs mélanges Conformement à une modalité préférée du procédé selon l'invention:
- I'agent de décoloration/transcoloration est un moyen chimique, - le support fibreux est du papier fabriqué à l'aide d'une machine à
papier, - et pour la réalisation de l'étape 4, on applique l'agent dle décoloration/transcoloration dans et/ou hors de la machine à papier, sur au moins une des faces externes de la feuille, de pl~relellce à
l'aide d'au moins l'un des moyens suivants: presse encolleuse, système de remouillage ou système de couchage.
La présente invention a également pour objet l'utilisation du support fibreux tel que défini ci-dessus et tel qu'obtenu par le procédé, pour la réalisation de papier de sécurité authentifiable par déchirure ainsi que de tickets de jeu à gratter ou de tickets in.ct~nt~nés de loterie.
La présente invention concerne ainsi un papier de sécurité authentifiable par déchirure caractérisé en ce qu'il est not~mm.ont constitué par le support fibreux tel que défini supra et/ou obtenu par mise en oeuvre du procédé tel que défini supra.
Enfin, la présente invention vise un ticket de jeu à gratter caractérisé, en ce qu'il est not~mment constitué par le support fibreux tel que défini supra, et/ou obtenu par mise en oeuvre du~ procédé tel que défini supra.
CA 02224~06 1998-01-21 Le support fibreux selon l'invention apparâît comme pouvant être un papier de sécurité authentifiable par déchirure, opaque, non del~min~ble, à faible prix de revient, et parfaitement adapté pour les applications de documents inf~l.ci~hles, et authentifiables par déchirure, de même que pour l'application de tickets de jeu à - 4 - to discolor and / or transcolour at least one outer edge of the sheet support before, during or after the elimination of water Such a process is one of those making it possible to obtain the fibrous support.
con. ~ tif ~ 1 ~ nt the first object of the present invention described above According to a preferred embodiment of the method, the fibrous support 10 aimed (eg paper) has a substantially median colored slice and, on the one hand and on the other, a white or dirrérc outer slice; "~ e and / or less darker than the middle edge. These two outer edges are colored identical or different. According to the preferred mode, the discoloration is carried out and / or transcoloration using chemical and / or physical means.
Such a fibrous support corresponds to the preferred embodiment of the product according to the invention as described above and shown in the single figure attached.
Stage I of preparation of the fibrous pulp corresponds to an operation relatively classic in the stationery industry. In a paper machine, this operation takes place at the head box or during the preparation of the pulp pulp. In this case, it is simply a question of adding to the dough at least a coloring agent and achieve a homogeneous mixture.
Step 2 is carried out through the headbox sector of the paper machine which makes it possible to produce a fibrous mattress in a single jet containing the coloring agent, this mattress then being conveyed to the modules draining, pressing, then drying the paper machine.
These three modules are intended to satisfy stage 3 of water elimination present in the sheet holder.
In the case where we are dealing with discoloration and / or chemical transcoloration, in accordance with a preferred embodiment of the method according to the invention, step 4 is carried out by applying a bath of discoloration and / or transcoloration, using a device provided for pl ~ rerence in the paper machine. Even more preferably, this coating device is a traditional size press or ~ Size Press ~, or even a ~ blade metering size press ~, or a ~ gate-roll ~. U, ne such glue press is usually located after the pre-drying.
CA 02224 ~ 06 1998-01-21 In the less advantageous hypothesis where the coating of the discoloration or transcoloration is carried out, when leaving the paper machine, it is it is possible to consider either the use of online sleeping means, such as eg metal blade or air knife devices, or traditional hl ~ pl ~ ssionS techniques.
It should be noted that any suitable means for penetrating a solution of discoloration / transcoloration in the fibrous support, can be substituted for the means classics mentioned above.
It goes without saying that the concentrations of bleaching / trans-10 coloring used in coating baths, are determined according to the quantity of coloring agent contained in the fibrous support and according to the stoichiometry of the corresponding reaction. These operating methods are perfectly within the reach of the skilled person.
Depending on the nature of the coloring agents as well as the coloring agents 15 discoloration / transcoloration, see description and definitions given in this connection above, in the part of this presentation relating to the supports fibrous taken as such.
As previously reported, the penetrability of the bleaching agent or staining inside the fibrous support, is an arrangement 20 fundamental of the method according to the invention. The parameters allowing to exercise a Contr81e on this point are, on the one hand, the g, ~ "u" age, the rate of refining and bonding of the fibrous support and, on the other hand, the viscosity of the coating bath.
Thus, the viscosity of the bleaching / transcoloring solution is adjusted by playing on dry matter and / or using film-forming binders (starch, cellulose ...). This viscosity adjustment is performed according to the nature of the reagent discoloration / transcoloration, as well as according to its reactivity.
It goes without saying that the parameters ~ s ~ nt on the penetrability of the discoloration / transcoloration are interdependent. Thus, at most the grammage of the fibrous support will be low, at most the viscosity of the coating bath should be high.
In practice we can indicate, by way of example:
- that for a grammage of 120 glm2, the viscosity of the bath is advantageously greater than or equal to 100 mPa.s, - and that for a grammage of 150 g / m2, the viscosity is advantageously greater than or equal to 80 mPa.s, - and that for a grammage of 200 glm2, the viscosity of the bath is advantageously greater than 30-50 mPa.s.
~ CA 02224 ~ 06 1998-01-21 As an example of a water-soluble binder, there may be mentioned for example:
carboxymethylcellulose, starch, polyvinyl alcohol which are natural binders, used more favorably, without excluding synthetic binders such than acrylic or styrene-butadiene latexes.
Advantageously, for step 4, use is made, in the case of a discoloration / transcoloration by chemical means, a couple of coloring / bleaching and / or transcoloration chosen from the following group:
Coloring agent Discoloration and / or coloring agent transcoloration reducing metal oxide sequestering metal salt colored medium pH indicator at selected pH
colored indicator of oxvdo-reduction medium with selected Redox potential dye degrading agent dye and their mixtures In accordance with a preferred method of the method according to the invention:
- the bleaching / transcoloring agent is a chemical means, - the fibrous support is paper made using a paper, - and to carry out step 4, apply the agent dle discoloration / transcoloration in and / or out of the paper machine, on at least one of the outer faces of the sheet, pl ~ relellce to using at least one of the following means: size press, rewetting system or sleeping system.
The present invention also relates to the use of the support fibrous as defined above and as obtained by the process, for the realization of security paper authenticated by tearing as well as scratch-off game tickets or lottery tickets in.ct ~ nt ~.
The present invention thus relates to an authenticated security paper by tear characterized in that it is not ~ mm.ont constituted by the fibrous support such as defined above and / or obtained by implementing the method as defined above.
Finally, the present invention relates to a scratched game ticket characterized, in what it is not ~ mment consisting of the fibrous support as defined above, and / or obtained by implementing the process as defined above.
CA 02224 ~ 06 1998-01-21 The fibrous support according to the invention appears to be able to be a security paper authenticated by tearing, opaque, not del ~ min ~ ble, at low price cost, and perfectly suited for document applications inf ~ l.ci ~ hles, and authenticated by tearing, as well as for the application of game tickets to
5 gratter non falsifiable par transvision.
Les di~lenls exemples ci-après permettront d'éclairer un peu mieux l'invention mais ne sont en aucun cas li",;~l;rs.
EXEMPLES:
EXE~PLE 1 Un indicateur coloré: de la phénolphtaléine solubilisée en milieu hydro-alcoolique est introduite à raison de 2 % par rapport à la pâte sèche à la mélangeuse dans une pâte à
papier composée pour 50 % de feuillus et 50 % de re~inellx, raffinée à 30~SR et portée à un pH de 11, il se développe une couleur rose intense. Un papier support 15 coloré de 250 g/m2 est produit sur la machine à papier.
A la presse encolleuse est enduite une solution d'acide sulfurique dilué de manière à
faire chuter le pH de surface de papier et par la même détruire la couleur rose-rouge du support; le papier final obtenu est blanc sur l'extérieur et rose en son centre.
Le papier est authentifiable par déchirure.
20 La reprise de bain à l'encolleuse est de 30 % en poids par rapport au papier support coloré.
Un billet authentifiable est réalisé par introduction dans la pâte à papier de colorant 25 BLEU DUASYN POUR ENCRES BJ'r de la Société HOECHST à raison de 0,2 % en poids par rapport à la pâte sèche, le pH de la pâte est ajusté à 4 avec de l'acide.
Le papier bleu ainsi produit avec un grammage de 300g/m2 arrive à la presse encolleuse de la machine à papier où le bain suivant est appliqué à raison de 20 % de prise en poids par rapport au papier:
30 Amidon: 15 % en poids sec par rapport au bain d'enduction, Javel à 12~: 15 % en poids en l'état par rapport au bain d'enduction Après séchage le papier est blanc sur ses parties externes et bleu à l'intérieur: la déchirure permet une a~lthentification visuelle directe.
De plus le papier avec ce colorant spécifique peut être authentifié à un deuxième 35 niveau: un trait de feutre eff,aceur d'encre ou l'application d'une solution basique sur la partie interne colorée permet une décoloration de cette partie.
CA 02224=,06 1998-01-21 .
r F 3 Un billet inf~l~ifi~ble est obtenu en encl~lis~nt sur le support papier bleu de l'exemple 2, avec un bain contenant 10 % de sulfite de sodium par rapport au bain, en S remplacement de l'eau de javel. Le même produit final est fabriqué.
EXlE~LE 4 Un papier coloré de 200 g/m2 servant de support est fabriqué sur machine à papier en nt le colorant JAUNE LEVACELL 3 GX de la société BAYER, le papier jaune 10 ainsi fabriqué est enduit à la presse encolleuse avec une solution diluée de soude caustique de manière à développer une coloration rouge à la surface du papier; la coloration de l'intérieur de la feuille restant jaune, le papier est authentifiable par déchirure.
Le papier ainsi coloré présente toutefois l'inconvénient de n'être pas aisément 15 utilisable dans des applications variées par les imprimeurs.
EXEME'LE 5 Un papier support de 250 g/m2 contenant de l'oxyde de m~ng~nçse à raison de 3 %
par rapport à la pâte sèche est fortement coloré en brun.
20 Ce support est enduit à la presse encolleuse avec une solution faiblement acide d'acide forrnami~1inesll1finique (à raison de 5 % par rapport au bain d'enduction) et d'une carboxyméthylcellulose de haute viscosité (à raison de 0,7 % en poids sec par rapport au bain d'enduction) servant de liant au bain.
La reprise de bain à l'encolleuse est de 30 % en poids par rapport au papier support.
25 Le papier final est blanc sur ses surfaces et coloré en brun au centre.
Un tel papier présente une opacité fortement améliorée, il est notablement impossible, même sous un fort éclairage de lire des inscriptions marquées au verso du papier, alors qu'un papier de grammage équivalent ne présente pas cette aptitude.
Ce produit blanc est imprimable et peut donc être utilisé comme papier support pour 30 ticket de loterie instantanée sans qu'il soit nécessaire d'effectuer un contrecollage avec une feuille d'~lllminil~m pour éviter la transvision. 5 scratch non-falsifiable by transvision.
The di ~ lenls examples below will shed some light the invention but are in no way li ",; ~ l; rs.
EXAMPLES:
EXE ~ PLE 1 A colored indicator: phenolphthalein dissolved in a hydro-alcoholic medium is introduced at a rate of 2% relative to the dry dough with a mixer in a dough paper composed for 50% hardwood and 50% re ~ inellx, refined to 30 ~ SR and brought to a pH of 11, it develops an intense pink color. Support paper 15 colored of 250 g / m2 is produced on the paper machine.
A sizing press is coated with a solution of sulfuric acid diluted so as to lower the pH of the paper surface and at the same time destroy the pink-red color support; the final paper obtained is white on the outside and pink in the center.
The paper can be authenticated by tearing.
20 The take-up of the bath with the gluing machine is 30% by weight relative to the backing paper colored.
An authenticated ticket is made by introducing dye into the paper pulp 25 DUASYN BLUE FOR BJ'r INKS from HOECHST at 0.2%
weight compared to the dry paste, the pH of the paste is adjusted to 4 with acid.
The blue paper thus produced with a grammage of 300g / m2 arrives at the press paper machine gluing machine where the following bath is applied at a rate of 20%
weight gain compared to paper:
30 Starch: 15% by dry weight compared to the coating bath, Bleach at 12 ~: 15% by weight in the state compared to the coating bath After drying the paper is white on its external parts and blue inside: the tear allows direct visualization.
In addition the paper with this specific dye can be authenticated at a second 35 level: a line of eff felt, ink scent or the application of a basic solution on the colored internal part allows a discoloration of this part.
CA 02224 =, 06 1998-01-21 .
r F 3 An inf ~ l ~ ifi ~ ble ticket is obtained in encl ~ lis ~ nt on the blue paper support of the example 2, with a bath containing 10% sodium sulfite relative to the bath, in S replacement of bleach. The same end product is produced.
EXlE ~ LE 4 A colored paper of 200 g / m2 serving as support is produced on a paper machine in nt the JAUNE LEVACELL 3 GX dye from the company BAYER, the yellow paper 10 thus produced is coated with a sizing press with a dilute soda solution caustic so as to develop a red color on the surface of the paper; the coloring of the inside of the sheet remaining yellow, the paper can be authenticated by tear.
The paper thus colored, however, has the disadvantage of not being easily 15 usable in various applications by printers.
A 250 g / m2 backing paper containing 3% m ~ ng ~ nçse oxide compared to the dry dough is strongly colored brown.
20 This support is coated with a size press with a weak acid solution of acid forrnami ~ 1inesll1finique (at a rate of 5% compared to the coating bath) and a high viscosity carboxymethylcellulose (at a rate of 0.7% by dry weight relative to in the coating bath) serving as a binder for the bath.
The resumption of bath with the gluing machine is 30% by weight relative to the support paper.
25 The final paper is white on its surfaces and colored brown in the center.
Such paper has a greatly improved opacity, it is notably impossible, even under strong lighting to read inscriptions marked on the back of the paper, whereas paper of equivalent grammage does not have this ability.
This white product is printable and can therefore be used as backing paper for 30 instant lottery tickets without the need to laminate with a sheet of ~ lllminil ~ m to avoid transvision.
Claims (12)
homogène, notamment dans son épaisseur;
produit à partir d'un seul jet fibreux;
et initialement de couleur (C2), puis décoloré ou coloré différemment, au moins partiellement sur au moins une de ses faces, pour former au moins une tranche externe (3,4) blanche ou de couleur (C1, C3), différente et/ou moins foncée que la couleur initiale (C2). 1- Opaque fibrous support (1), in particular paper, characterized in that it is obtained from a single mattress fibrous:
homogeneous, especially in its thickness;
produced from a single fibrous jet;
and initially colored (C2), then discolored or colored differently, at least partially on at least one of its faces, to form at at least one white or colored outer section (3,4) (C1, C3), different and / or less dark than the initial color (C2).
homogène, notamment dans son épaisseur;
produit à partir d'un seul jet fibreux;
et initialement de couleur (C2), puis décoloré ou coloré différemment, au moins partiellement sur au moins une de ses faces, pour former, d'une part, au moins une tranche externe (3,4) blanche ou de couleur (C1, C3), différent et/ou moins foncée que la couleur initiale (C2) et d'autre part, au moins une tranche (2) sensiblement médiane de couleur (C2). 2 - fibrous support according to claim 1, characterized in that it is obtained from a single fibrous mattress:
homogeneous, especially in its thickness;
produced from a single fibrous jet;
and initially colored (C2), then discolored or colored differently, at least partially on at least one of its faces, to form, on the one hand, at least one outer slice (3,4) white or colored (C1, C3), different and / or less dark than the initial color (C2) and on the other hand, at least one substantially median slice (2) of color (C2).
4 - Support fibreux selon la revendication 1 ou 2, caractérisé en ce qu'il comprend au moins un agent de coloration et éventuellement au moins un agent de décoloration et/ou au moins un agent de transcoloration, n'ayant pas réagi mais apte à
réagir avec l'agent de coloration dans les tranches externes. 4) white or of a different and / or less dark color (C1, C3), the color (C2) of the middle section (2), the colors (C1) and (C3), respectively of the two external sections (3) and (4) located on either side of the middle section (2) being identical or different.
4 - fibrous support according to claim 1 or 2, characterized in that it comprises at least one coloring agent and optionally at least one coloring agent discoloration and / or at least one transcoloration agent, which has not reacted but is capable of react with the coloring agent in the outer slices.
Agent de coloration Agent de décoloration et/ou de transcoloration oxyde métallique réducteur sel métallique séquestrant indicateur coloré de pH milieu à pH choisi indicateur coloré d'oxydo-réduction milieu à potentiel Redox choisi colorant agent de dégradation du colorant et leurs mélanges 5 - fibrous support according to claim 4, characterized in that the couple of coloring agent / bleaching agent and / or transcoloration is chosen in the following group:
Coloring agent Discoloration and / or coloring agent transcoloration reducing metal oxide sequestering metal salt colored medium pH indicator at selected pH
colored indicator of redox medium selected Redox potential dye degrading agent dye and their mixtures
en ce que le support fibreux visé (e.g. le papier) présente une tranche (2) sensiblement médiane de couleur (2) et, de part et d'autre de celle-ci, une tranche externe (3, 4) blanche ou de couleur (C1, C3) différente et/ou moins foncée que la tranche médiane (2), les couleurs (C1, C3) de ces deux tranches externes (3,4) étant identiques ou différentes. 8 - Method according to claim 7, characterized in that the targeted fibrous support (eg paper) has a wafer (2) substantially median in color (2) and, on either side thereof, a slice external (3, 4) white or color (C1, C3) different and / or less dark than the middle section (2), the colors (C1, C3) of these two external sections (3,4) being identical or different.
Agent de coloration Agent de décoloration et/ou de transcoloration oxyde métallique réducteur sel métallique séquestrant indicateur coloré de pH milieu à pH choisi indicateur coloré d'oxydo-réduction milieu à potentiel Redox choisi colorant - agent de dégradation du colorant et leurs mélanges 9 - Method according to claim 8, characterized in that in the case of discoloration / transcoloration by chemical means, a couple of coloring agent / bleaching agent and / or transcoloration chosen in the next group:
Coloring agent Discoloration and / or coloring agent transcoloration reducing metal oxide sequestering metal salt colored medium pH indicator at selected pH
colored indicator of redox medium selected Redox potential dye - dye degrading agent and their mixtures
en ce que l'agent de décoloration/transcoloration est un moyen chimique, en ce que le support fibreux est du papier fabriqué à l'aide d'une machine à papier, et en ce que l'on applique l'agent de décoloration/transcoloration dans et/ou hors de la machine à
papier sur au moins une des faces externes de la feuille, de préférence à l'aide d'au moins l'un des moyens suivants: presse encolleuse, système de remouillage ou système de couchage. 10 - Method according to any one of claims 7 to 9, characterized in that the bleaching / coloring agent is a chemical medium, in that the fibrous support is paper made using a paper machine, and in that the bleaching / coloring agent is applied in and / or out of the machine paper on at least one of the outer sides of the sheet, preferably using at least at least one of the following: glue press, rewetting system or sleeping system.
10. 12 - Scratch game ticket, characterized in that it is in particular consisting of the fibrous support according to any one of claims 1 to 6, and / or obtained by implementing the method according to any one of claims 7 to 10.