CA2009372C - A yankee cylinder and a method for coating a yankee cylinder - Google Patents
A yankee cylinder and a method for coating a yankee cylinder Download PDFInfo
- Publication number
- CA2009372C CA2009372C CA 2009372 CA2009372A CA2009372C CA 2009372 C CA2009372 C CA 2009372C CA 2009372 CA2009372 CA 2009372 CA 2009372 A CA2009372 A CA 2009372A CA 2009372 C CA2009372 C CA 2009372C
- Authority
- CA
- Canada
- Prior art keywords
- coating
- cylinder
- mantle
- surface layer
- spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a Yankee cylinder for a paper-making machine, in which a coating which is a mixture of a metal powder and a carbide or nitride and withstands well the wearing effect of the doctor blade and other corrosive and thermal stresses produced in paper making is formed on top of the cylinder mantle. The invention also relates to methods for coating a Yankee cylinder with such a coating by using a detonation, plasma or supersonic method.
Description
A Yankee cylinder and a method for coating a Yankee cylinder The invention relates to a Yankee cylinder for use in a paper-making machine and to coating methods used in its manufacture and repair.
The Yankee cylinders used in the paper-making process are in the main manufactured by casting from cast-iron. Cylin-der mantles have also been assembled from steel sheets by welding. The largest cylinders have diameters.of 6-7 m, and their length may be 5-6 m. The wall thickness of a new cyl-finder is 40-60 mm.
During paper-making, a so-called doctor blade, which de-taches the paper from the cylinder surface and crinkles it, scrapes against the cylinder surface.
The doctor blade wears away the cylinder surface and.espe-cially the edge parts of the cylinder. For this reason the cylinder must occasionally be ground to give the cylinder surface the correct shape and a suitable surface quality.
When a cylinder has been ground many times, its wall thick-ness will reach the limit set by the pressure vessel autho-rities. The thinner the wall thickness, the more the oper-ating pressure of the cylinder must be reduced. Reducing the operating pressure will mean a slowing down of the pro-duction rate. At this stage the Yankee cylinders are usual-ly repaired by coating.
Another reason for the coating is that the mantle surface may have pores which produce holes in the paper. If there are few holes, they can be plugged, but small cavities in (~~~"l~
The Yankee cylinders used in the paper-making process are in the main manufactured by casting from cast-iron. Cylin-der mantles have also been assembled from steel sheets by welding. The largest cylinders have diameters.of 6-7 m, and their length may be 5-6 m. The wall thickness of a new cyl-finder is 40-60 mm.
During paper-making, a so-called doctor blade, which de-taches the paper from the cylinder surface and crinkles it, scrapes against the cylinder surface.
The doctor blade wears away the cylinder surface and.espe-cially the edge parts of the cylinder. For this reason the cylinder must occasionally be ground to give the cylinder surface the correct shape and a suitable surface quality.
When a cylinder has been ground many times, its wall thick-ness will reach the limit set by the pressure vessel autho-rities. The thinner the wall thickness, the more the oper-ating pressure of the cylinder must be reduced. Reducing the operating pressure will mean a slowing down of the pro-duction rate. At this stage the Yankee cylinders are usual-ly repaired by coating.
Another reason for the coating is that the mantle surface may have pores which produce holes in the paper. If there are few holes, they can be plugged, but small cavities in (~~~"l~
large numbers will necessitate the coating of the mantle.
Yankee cylinders have been coated for nearly 20 years. The coating materials used have included:
- martensitic stainless steel (AISI 420), arc extruded - martensitic stainless steel (AISI 431), plasma extruded - CrNiMoAl alloy, plasma extruded - Mo-based alloys, plasma extruded Arc-extruded coatings have in certain cases been a success, but in the manufacture of new paper grades and as the speeds of paper-making machines increase, they do not meet the requirements.
Plasma-extruded coatings are considerably more resistant to corrosion, and also their resistance to wear is better than that of arc-extruded coatings. However, both CrNiMoAl al-loys and Mo-based alloys have the drawback that they wear away too rapidly when very thin papers are being made. The reason is the wearing effect of the doctor blade and the fact that flint particles from the paper stock adhere to the doctor blade during disturbances, and they "lathe" the coating.
The coatings currently known axe 0.8-2.0 mm thick, so that they can be ground often enough before re-coating. A thick coating decreases the thermal conductivity of the cylinder wall, slowing down production and increasing the energy costs.
Furthermore, the present-day coatings have to be ground at approximately one-year intervals, some even at 4-6 month intervals, as the quality of the surface deteriorates. An intermediate grinding will cause a stoppage of 5-8 days, resulting in extensive production losses. Repairing the cylinder.by re-coating will for its part cause a stoppage of 12-25 days.
The most extensive production losses, in addition to the above, occur when a paper-making machine cannot be used for making those paper grades for which the best prices.can be obtained.
The primary object of the present invention is to provide a Yankee cylinder with such a mantle surface layer that the doctor blades wear it away very little, with an improved thermal conductivity of the mantle, and with longer inter-vals between its mantle maintenance sequences.
It is also an object of the invention to provide coating methods to be used in the manufacture and repairs of a Yankee cylinder; by using the methods a cylinder mantle with the above-mentioned properties is obtained.
The present invention thus relates to a Yankee cylinder for use in a paper-making machine, the cylinder having ends and axle pins, as well as a cylinder mantle which is made of metal and primarily gives the cylinder its mechanical strength, the Yankee cylinder being characterized in that on top of the cylinder mant~.e there is formed a coating w which constitutes the surface layer and which is a mixture of metal powder and carbide or nitride and well withstands the wearing effect of the doctor blade as well as other corrosive and thermal stresses occurring in paper making.
The surface layer of a Yankee cylinder according to the invention is primarily made of a mixture of a carbide or nitride of tungsten, titanium, vanadium or boron and a powder of cobalt, nickel or iron. The surface layer prefer-ably contains the above-mentioned carbide or nitride 60-94 weight percent and the above-mentioned metal 6-40 weight percent. The thickness of the surface layer is in the main less than 0.5 mm and preferably within 0.2-0.3 mm.
According to the invention, a Yankee cylinder can be coated ,so that, on top of the cylinder mantle directly or on top of a metallic coating which has first been extruded on the cylinder mantle and constitutes an intermediate layer, there is extruded by a detonation, plasma or supersonic method a coating which forms the surface~layer and is a mixture of a metal powder and a carbide or nitride and well withstands the wearing effect of the doctor blade and other corrosive and thermal stresses occurring in paper making.
The particle size_of the coating material mixture forming the surface layer is preferably 5-70 uxn.
The mantle coating is made directly on the surface of a mantle made of._cast-iron or steel by extruding the coating by a detonation, plasma or supersonic method, the. surface having first been ground precisely to the correct dimension and shape.
According to another embodiment of the method according to the invention, the mantle surface of a Yankee cylinder is first coated with a martensitic stainless steel or a NiCrMoAl alloy or a Mo-based alloy by thermal extrusion, arc extrusion or plasma extrusion, and is then ground pre-cisely to the correct shape and dimension. ThEreafter the surface is pre-treated by grinding or grain blasting to roughen it, and then coated by extruding, by a detonation, plasma or supersonic method, a coating which contains a carbide or nitride and a metal powder.
Yankee cylinders have been coated for nearly 20 years. The coating materials used have included:
- martensitic stainless steel (AISI 420), arc extruded - martensitic stainless steel (AISI 431), plasma extruded - CrNiMoAl alloy, plasma extruded - Mo-based alloys, plasma extruded Arc-extruded coatings have in certain cases been a success, but in the manufacture of new paper grades and as the speeds of paper-making machines increase, they do not meet the requirements.
Plasma-extruded coatings are considerably more resistant to corrosion, and also their resistance to wear is better than that of arc-extruded coatings. However, both CrNiMoAl al-loys and Mo-based alloys have the drawback that they wear away too rapidly when very thin papers are being made. The reason is the wearing effect of the doctor blade and the fact that flint particles from the paper stock adhere to the doctor blade during disturbances, and they "lathe" the coating.
The coatings currently known axe 0.8-2.0 mm thick, so that they can be ground often enough before re-coating. A thick coating decreases the thermal conductivity of the cylinder wall, slowing down production and increasing the energy costs.
Furthermore, the present-day coatings have to be ground at approximately one-year intervals, some even at 4-6 month intervals, as the quality of the surface deteriorates. An intermediate grinding will cause a stoppage of 5-8 days, resulting in extensive production losses. Repairing the cylinder.by re-coating will for its part cause a stoppage of 12-25 days.
The most extensive production losses, in addition to the above, occur when a paper-making machine cannot be used for making those paper grades for which the best prices.can be obtained.
The primary object of the present invention is to provide a Yankee cylinder with such a mantle surface layer that the doctor blades wear it away very little, with an improved thermal conductivity of the mantle, and with longer inter-vals between its mantle maintenance sequences.
It is also an object of the invention to provide coating methods to be used in the manufacture and repairs of a Yankee cylinder; by using the methods a cylinder mantle with the above-mentioned properties is obtained.
The present invention thus relates to a Yankee cylinder for use in a paper-making machine, the cylinder having ends and axle pins, as well as a cylinder mantle which is made of metal and primarily gives the cylinder its mechanical strength, the Yankee cylinder being characterized in that on top of the cylinder mant~.e there is formed a coating w which constitutes the surface layer and which is a mixture of metal powder and carbide or nitride and well withstands the wearing effect of the doctor blade as well as other corrosive and thermal stresses occurring in paper making.
The surface layer of a Yankee cylinder according to the invention is primarily made of a mixture of a carbide or nitride of tungsten, titanium, vanadium or boron and a powder of cobalt, nickel or iron. The surface layer prefer-ably contains the above-mentioned carbide or nitride 60-94 weight percent and the above-mentioned metal 6-40 weight percent. The thickness of the surface layer is in the main less than 0.5 mm and preferably within 0.2-0.3 mm.
According to the invention, a Yankee cylinder can be coated ,so that, on top of the cylinder mantle directly or on top of a metallic coating which has first been extruded on the cylinder mantle and constitutes an intermediate layer, there is extruded by a detonation, plasma or supersonic method a coating which forms the surface~layer and is a mixture of a metal powder and a carbide or nitride and well withstands the wearing effect of the doctor blade and other corrosive and thermal stresses occurring in paper making.
The particle size_of the coating material mixture forming the surface layer is preferably 5-70 uxn.
The mantle coating is made directly on the surface of a mantle made of._cast-iron or steel by extruding the coating by a detonation, plasma or supersonic method, the. surface having first been ground precisely to the correct dimension and shape.
According to another embodiment of the method according to the invention, the mantle surface of a Yankee cylinder is first coated with a martensitic stainless steel or a NiCrMoAl alloy or a Mo-based alloy by thermal extrusion, arc extrusion or plasma extrusion, and is then ground pre-cisely to the correct shape and dimension. ThEreafter the surface is pre-treated by grinding or grain blasting to roughen it, and then coated by extruding, by a detonation, plasma or supersonic method, a coating which contains a carbide or nitride and a metal powder.
After coating according to either the first or the second embodiment of the invention, the mantle surface is ground.
Since the wear-resistant components of the coating are car-bides or. nitrides of tungsten, titanium, vanadium or boron, the surface has to be ground with a diamond. Diamond grind-ing can be commenced as stone grinding, but the final grinding must be carried out using a diamond band in order to eliminate vibration. Furthermore, the surface quality can be superfinished using a diamond-containing liquid.
The advantages of the Yankee cylinder and coating method according to the invention over the prior art. are the fol-lowing:
1.0 Better resistance to wear The carbides and nitrides present in the coating are very hard (2400-4500 HV), and they have been-chosen so that ad-hesion between the doctor blade made of annealed steel and the carbides and nitrides is very small.
Thus the wearing away of the surface of the Yankee cylinder mantle is slight even in harsh operating conditions.
Furthermore, during disturbances in operation the hard -flint particles brought to the doctor blade in the paper stock cannot wear the coating since the hardness of the flint particles (approx. 1500 HV) is considerably less than that of the coating.
The hardness of prior-art coatings is only 350-700 HV, so that flint particles will easily "lathe" grooves into the coating.
~~~~~'~~
Since the wear-resistant components of the coating are car-bides or. nitrides of tungsten, titanium, vanadium or boron, the surface has to be ground with a diamond. Diamond grind-ing can be commenced as stone grinding, but the final grinding must be carried out using a diamond band in order to eliminate vibration. Furthermore, the surface quality can be superfinished using a diamond-containing liquid.
The advantages of the Yankee cylinder and coating method according to the invention over the prior art. are the fol-lowing:
1.0 Better resistance to wear The carbides and nitrides present in the coating are very hard (2400-4500 HV), and they have been-chosen so that ad-hesion between the doctor blade made of annealed steel and the carbides and nitrides is very small.
Thus the wearing away of the surface of the Yankee cylinder mantle is slight even in harsh operating conditions.
Furthermore, during disturbances in operation the hard -flint particles brought to the doctor blade in the paper stock cannot wear the coating since the hardness of the flint particles (approx. 1500 HV) is considerably less than that of the coating.
The hardness of prior-art coatings is only 350-700 HV, so that flint particles will easily "lathe" grooves into the coating.
~~~~~'~~
2.0 Possibility of making new paper grades .
When new, very thin paper grades are being made, the doctor blade often comes into direct contact with the mantle sur-face, since usually the so-called coating layer between the mantle surface and the doctor blade may become removed. If the mantle surface cannot withstand such wear, it becomes 'scratched and causes problems in paper-making. With the new, wear-resistant coating, this problem does not appear.
The corrosion-resistance of the new Coating is also very good; this enables special-purpose papers to be made in acid solutions in which the pH may be 3-5.
3.0 Energy costs will decrease The thickness of the new coating is only 0.2-0.3 mm. The thickness of previously used coatings is 0.8-2.0 mm.
A thinner coating conducts heat better and thus reduces the energy required in the drying of paper.
4.0 The costs of stoppages and maintenance will decrease The coatings currently in use have to be ground on average at one-year intervals. When thin paper grades are manu-factured, the interval between grindings may be 4-6 months.
With the new coating, an average grinding interval of two years Can be achieved. Since for a large paper-making machine one grinding will cause a stoppage of approx. 5-8 days, resulting in production losses of 5-8 million FIM, the savings due to the longer maintenance sequence will be significant.
2Q~93"~~
5.0 Time required for maintenance will shorten The coatings currently in use are maintained by grinding the old coating off either in part or totally down to the basic material of the mantle. Thereafter the coating is renewed from the basic material up, and is ground.
By the new technology developed, the coating can be made over the old coating, once the old coating has first been pre-ground clean. The de~reloped technology 'thus shortens by up to several days the time required for the maintenance.
When new, very thin paper grades are being made, the doctor blade often comes into direct contact with the mantle sur-face, since usually the so-called coating layer between the mantle surface and the doctor blade may become removed. If the mantle surface cannot withstand such wear, it becomes 'scratched and causes problems in paper-making. With the new, wear-resistant coating, this problem does not appear.
The corrosion-resistance of the new Coating is also very good; this enables special-purpose papers to be made in acid solutions in which the pH may be 3-5.
3.0 Energy costs will decrease The thickness of the new coating is only 0.2-0.3 mm. The thickness of previously used coatings is 0.8-2.0 mm.
A thinner coating conducts heat better and thus reduces the energy required in the drying of paper.
4.0 The costs of stoppages and maintenance will decrease The coatings currently in use have to be ground on average at one-year intervals. When thin paper grades are manu-factured, the interval between grindings may be 4-6 months.
With the new coating, an average grinding interval of two years Can be achieved. Since for a large paper-making machine one grinding will cause a stoppage of approx. 5-8 days, resulting in production losses of 5-8 million FIM, the savings due to the longer maintenance sequence will be significant.
2Q~93"~~
5.0 Time required for maintenance will shorten The coatings currently in use are maintained by grinding the old coating off either in part or totally down to the basic material of the mantle. Thereafter the coating is renewed from the basic material up, and is ground.
By the new technology developed, the coating can be made over the old coating, once the old coating has first been pre-ground clean. The de~reloped technology 'thus shortens by up to several days the time required for the maintenance.
Claims (9)
1. A Yankee cylinder for a paper-making machine, having ends and axle pins, as well as a cylinder mantle which is made of metal and primarily gives the cylinder its mechanical strength, characterized in that a coating is formed on top of the cylinder mantle and constitutes the surface layer thereof, the coating being obtained from a mixture containing 60 to 94 percent by weight of a carbide or nitride of tungsten, titanium, vanadium or boron and 6 to 40 percent by weight of a powder of cobalt, nickel or iron by spraying the mixture by a denotation, plasma or supersonic method.
2. A Yankee cylinder as claimed in claim 1 wherein the thickness of the coating constituting the surface layer is less than 0.5 mm, preferably in the range of from 0.2 to 0.3 mm.
3. A method for coating a Yankee cylinder, characterized in that on top of the cylinder mantle or on top of a metal coating first sprayed onto the cylinder mantle and forming an intermediate layer, a coating is applied by spraying a mixture containing 60 to 94 percent by weight of a carbide or nitride of tungsten, titanium, vanadium or boron and 6 to 40 percent by weight of a cobalt, nickel or iron powder by a detonation, plasma or supersonic method the coating constituting the surface layer of the cylinder mantle and being resistant to the wearing effect of the doctor blade and to other corrosive and thermal stresses produced in paper making.
4. A method as claimed in claim 3 wherein the particle size of the coating material mixture is in the range of from 5 to 70 µm.
5. A method as claimed in claim 3 or claim 4 wherein the cylinder mantle is ground to precisely the correct shape and dimension before the spraying of the coating layer.
6. A method as claimed in any one of claims 3 to 5, wherein the coating material used in the intermediate layer is a martensitic stainless steel, a NICrMoAl metal alloy or a Mo-based metal alloy.
7. A method as claimed in any one of claims 3 to 5 or claim 6, wherein the coating used in the intermediate layer is produced by thermal spraying.
8. A method as claimed in any one of claims 3 to 4, claim 6 or claim 7, wherein the coating used in the intermediate layer is first ground precisely to the correct shape and dimension and is then roughened either by grinding or grain blasting before the spraying of the surface layer thereon.
9. A method as claimed in any one of claims 3 to 8 wherein the surface layer is ground by using either a diamond stone or diamond bands and is further superfinished, when necessary, by using a diamond-containing liquid.