CA1036820A - Method and apparatus for producing fibers from heat-softenable materials - Google Patents

Abstract

ABSTRACT OF THE DISCLOSURE

A stream feeder for supply of streams of molten glass for attenuation into fibers. The feeder is formed of metal and is electric-resistance heated. The bottom wall and sidewalls of the feeder are of varied thickness and are formed from a single sheet of metal. The disclosure also includes method and apparatus for forming the bottom wall and varied thickness sidewalls from a single sheet of metal.

Description

~0368Z0 This invention relates to apparatus for melting heat-softenable materials and more particularly to stream feeders or bushings made of platinum, rhodium or other prec.ous metal alloys for producing continuous glass fibers and to a method of fabricating stream feeders from such metals.

Several methods have heretofore been employed in processing glass for forming continuous glass filaments or fibers.
One method involves the steps of melting glass in a comparatively large furnace, refining the glass in a refining chamber, and forming the glass into spherical bodies or marbles. The glass marbles are subsequently delivered into a stream feeder which is electrically heated to remelt the glass to a viscosity at which the streams of glass may be flowed through orifices in the feeder and attenuated into fibers.
The more common method used today is the direct melt process wherein glass batch is reduced to a molten state and reined in a furnace. The molten glass flows from the furnace along a forehearth channel to stream feeders disposed along the forehearth. The feeders are heated by electrical resistance heating to control glass viscosity. And the streams of the glass are delivered through orifices in the feeders or bushings for attenuation into fibers.
Both of the above fiber forming processes employ stream feeders or bushings made of high temperature resistant metal alloys such as platinum or rhodium. The stream feeder is a long metal box having orificed tips or projections attached to its bottom wall through which streams of glass flow for attenuation into fibers. Terminals to which electrical bus bars are attached for supply of current through the feeder are welded to either end of the box~shaped feeder. The feeder is then heated by its own A`~ 1 electrical resistance. To achieve the desired heating character-istics in the feeder, it has conventionally been the practice to vary the thickness of the feeder walls to control the amount of current passing therethrough.
Feeders have typically been manufactured from precut parts which are welded together by conventional fusion welding techniques. The plate for the bottom wall or tip section is u~ually of uniform thickness and the plates for the sides and flanges are of various lesser thicknesses to produce the desired heat pattern and/or to reduce the amount of precious metal required. Using thinner pieces for the side walls and flanges causes several difficulties in conventional feeder fabrication as well as feeder performance. For example, additional rolling of the thinner sections is required. The welding together of the pieces is time consuming and the uniformity of the welds may vary. Also, because of the cast nature of the fusion bead as-compared to the wrought sheet, resistivity is changed through the weld zone and the same heat pattern may be difficult to stabilize or reproduce from feeder to feeder. Severe warpage of the thinner sheet material may occur when fusion welded to the thicker material. In addition, if the welds are not made extremely carefully, they may leak glass. Also, if failures or fractures occur in the feeders, they usually occur in or adiacent to the welds.
If a technique could be developed for reducing the adverse effects of fusion welding during construction of the feeders or for improving current distribution through the feeder when it is in operation, a substantial contribution would be made to advance the art of forming high-temperature continuous fibers.

~4;

Accordingly, it is an object of the present invention to provide feeders for heat softenable fiber-forming materials that have predetermined and controlled current carrying and res-istance heating characteristics.
Another object is to provide glass stream feeders that are formed with a minimum of welding.
A still further object is to provide a method for fab-ricating feeders for high temperature heat softenable fiber form-ing materials that involves minimizing welds and yet retains the necessary varied wall thickness for controlling the resistance-heating of the feeders.
The present invention seeks to accomplish the above objectives by fabricating the feeder tip section, sidewalls and flanges from one piece of precious metal plate. A plate of the same thickness as the desired tip section, but somewhat wider, is centrally positioned over a rectangular opening or die formed by two spaced apart, ironing inserts held in a solid retainer block.
A tapered punch or ram presses the plate downwardly between the surface of the inserts and the ram surface under controlled con-ditions to compress and draw the thick plate to form thinner side-walls. Successive passes of various sizes of punches or inserts may be used to compressively iron the sidewalls to the desired taper and thickness. After the part is formed to the desired cross-sectional shape, the flanges and perhaps end plates can be formed and trimmed by hand or by conventional die-set methods.
Accordingly, one aspect of the invention involves a resistance heated feeder for supply of molten mineral material in the form of streams to be attenuated into fibers, said feeder comprising end walls, sidewalls and a stream flow region at a normally lower wall; said sidewalls and lower wall being formed C

from a single piece of ductile, high temperature resistant, electric current-conducting material, and wherein the thicknesses of said sidewalls are structured to provide non-uniformity in thickness along at least a portion thereof, said wall structuring facilitating a pattern of heat generation to provide uniformity of temperature in the molten material at the stream flow region.
Preferably, each of the sidewalls comprises an upper region and a lower region wherein the wall thickness of at least a portion of the lower region is greater than the wall thickness of at least a portion of the upper region. It is recommended that the wall thickness of a portion of the lower region is at least fifty percent greater than the wall thickness of a portion of the upper region.
Preferably the sidewalls are rectangular in shape having end regions and a center region wherein the wall thicknesses of the end regions are a different thickness than the wall thickness of the center region. It is recommended that the difference in wall thicknes5 between the end regions and the center region is at least twenty-five percent.
A further aspect of the invention includes a method for forming a channel-shaped member from a planar member of ductile, electric current-conducting material for use in fabricating a feeder which supplies molten mineral material in the form of streams to be attenuated into filaments, comprising the steps of:
disposing the planar member between a tapered projecting member and a block having an aperture formed therein and a raised land defining a linear pressing surface along the interior of the ap~rture; moving the projecting member and the block relative to each other such that the projecting member contacts a major surface of the iO36~20 planar member; forcing the tapered projecting member and planar member through the aperture in the block thereby urging the planar member to move in a direction transverse to the lands defining the pressing surface of the aperture; compressing the planar member between the tapered surface of the projecting member and the lands defining the pressing surface to form a channel-shaped member having sidewalls of predetermined varied thickness corresponding to the clearance between the surface of the tapered projecting member and the pressing s~urface~ and removing the channel-shaped member from the block.
It is possible to employ the following apparatus for forming a component of a resistance heated feeder for supply of molten streams of fiber forming mineral material, in which appara-tus the sidewalls and a normally lower wall are made from a plate of ductile, electric current-conducting and high temperature re-sistant material, comprising: a ram shaped to conform to the in-terior shape of the portion of the feeder component bounded by the side and lower walls, a structure defining an opening, oppos-ing linear pressing surfaces extending lengthwise of both sides of the opening, the opposing pressing surfaces each being a re-latively narrow land, the surface defining the shortest distance between a pair of spaced apart members in the structure; means for disposing a plate of said ductile, high temperature resistant current conducting material between the ram and the opening; means for moving the ram against the plate to force the ram and plate between the pressing surfaces thus urging the plate to move in a direction transverse to the linear pressing surfaces of the opening, the space between the ram and the pressing surfaces being such as to effect progressive compression of the sidewall portions of the plate between the surface of the ra~ and the pressing surface as ~ _5_ the ram moves past the pressing surfaces to form the plate into the feeder component; and means for moving the feeder component from the apparatus for further fabrication into a stream feeder.
The operational advantages of using this method to for~
feeders includes better or more stable control of feeder wall thick-ness, fewer weld lines, greater flexibility in feeder design, in-creased feeder strength and increased average feeder life. The fabrication advantages include reduced fabrication time, reduced inventory of precious metals, consistent dimensional characteristics, reduced rolling, stock cutting and layout and reduced skill needed to fabricate the feeders.
Other advantages and features of this invention will appear in the following description and appended claims reference being had to the accompanying drawings wherein like reference characters designate corresponding parts in the several views.

j~ -5a-~' FIGURE 1 is a generalized isometric view of apparatus for producing continuous glass fibers utilizing a resistance heated molten glass feeder made of metal.
FIGURE 2 is a front elevational view with parts in section of the punch and drawing apparatus of the present invention.
FIGURE 3 is a front elevational view similar to FIGURE

2 showing another embodiment of the invention.
FIGURE 4 is a front elevational view with parts in section of one step in the use of the apparatus shown in FIGURE
2.
FIGURE 5 is a front elevational view similar to FIGURES
2 and 4 illustrating another step in the use of the invention.
FIGURE 6 is a cross sectional view taken substantially along line 6-6 of FIGURE 4.
FIGURE 7 is an enlarged sectional view of the pressing member shown in FIGURE 2.
FIGURE 8 is an enlarged sectional view similar to FIGURE 7 showing another embodiment of the pressing member.
20FIGURE 9 is a cross sectional view similar to FIGURE
2 illustrating release means for the invention.
FIGURE 10 is a sectional view of apparatus made by the invention.
FIGURE 11 is a sectional view similar to FIGURE 10 illustrating another form of the apparatus made by the invention.
Before explaining the present invention in detail it is to be understood that the invention is not limited in its application to the details of construction and arrangement of parts illustrated in the accompanying drawings, since the invention is capable of other embodiments and of being practiced or carried out in various ways to produce elements for other end uses. Also it is to be understood that the phraseology or te~minology employed herein is for the purpose of description and not of limitation.
As shown in FIGURE 1, continuous glass fibers are formed utilizing a stream feeder or bushing 40 provided with electrical terminals 42 to which electric lines ~not shown) are connected. Electric current is supplied from a source and is passed through the feeder to heat the same by its own electrical resistance. An insulating refractory (not shown~ is typically provided around the bushing to retain heat and improve eficiency.
Glass fiber forming material in the form of molten glass i9 fed by gravity int~ the feeder 40 from a forehearth connected to a glass melting furnace (not shown). In the feeder the molten material is further conditioned or heated and discharged downwardly as small molten streams 48 from orifices 46 formed in aligned array along the bottom of the feeder. This bottom orificed plate is generally referred to as the tip section 44 since the orifices are usually formed in projecting tips 45.
The streams are attenuated into fibers 50 by a tension device such as a winder, pull wheel or blower (not shown). Then the fibers may be lubricated by a liquid sizing or binder and pulled or conveyed to a conventional collection device.
The stream feeder or bushing 40 is basically a specially shaped box made of high temperature resistant alloys such as platinum, rhodium or the like. It has been a practice to fabricate the feeders using precut metal strips manually welded together. As previously stated, the welding process requires skilled labor and the welds even if accurately executed may cause feeder operating problems. The present invention minimizes the number of welds required in feeder fabrication and maintains the variable wall thickness needed for optimum operation of the feeder.
The apparatus used for fabricating glass stream feeders in accordance with the present invention is illustrated in FIGURES 2 - 6. It comprises modified forms of apparatus sometimes used by the drawing industry when deep drawing cans or pressure vessels. The apparatus includes a ram or male portion 20 and a die or female portion 10. The ram 20 is a tapered rectangular member designed to be passed through the larger rectangular opening formed by the die 10. The die 10 includes a heavy duty retainer block 12 with removable ironing or pressin~
inserts 14 set therein to form the femal portion o the system.
A tip nest or support plate 16 is connected by means of a rod 18 to a hydraulic or air cushion means (not shown). The tip plate nest or support 16 is designed to move freely up and down within the rectangular opening formed by the inserts 14 and the retainer block 12. The support 16 applies resistive pressure to the bottom of the plate 30 to be formed. Thus, the support 16 helps to hold the plate 30 and stabilize the process.
FIGURES 2, 4 and 5 illustrate the progressive steps of forming a glass stream feeder of the present invention. The metal plate 30 from which the feeder 40 is to be formed is properly rolled, cut to size and annealed. The prepared plate 30 is formed to the thickness of the desired tip section 44.

~' ~036820 Projections or tips 45 are fused to the plate and holes 46 are drilled through the plate and projections by a techni~ue similar to that disclosed in U.S. Patent No. 3,598,952. Other methods for forming or attaching the projections which can also be used are described in U.S. Patent Nos. 3,514,841 and 2,933,950. The main advantage of forming the tips 45 at this point in the fabrication process is the ease of attachment because the flat rectangular plate 30 is more easily indexed in an auto~ated process than an already formed box-shaped feeder. However if desired, it is also possible with this invention to form the feeder to its final shape before adding the tips 45 and providing the orifices 46.
FIGURE 3 shows such a plain flat plate being readied for forming.
Once the plate 30 is ready with the attached orificed rips 45, it is placed over the rectangular opening of the die 10.
Fixtures (not shown) may be used to help assure proper positioning of the plate. The tip nest and ~upport 16 is brought into contact with the bottom of the plate 30. As shown in FIG~RE 6, slot5 17 are provided in the support 16 to form a tip nest which accommodates the rows of tips 45 and yet provides support for the plate.
The ram 20 is lowered into contact with the top of the plate 30 and pressure is applied to both sides of the plate by the ram 20 on one side and the support 16 on the other side. The hydraulic or air cushion means of the support or tip nest 16 provides a pneumatic force which resists the force of the ram by a predetermined amount. The opposing forces of the ram and support act to hold the plate firmly between the ram and support plate and isolate the stress in one sidewall 47 from the other.
It has been found that a constant resistance or back-up pressure of four to five tons against the support 16 is sufficient to _ g _ :1036820 securely hold the plate 30 and keep it in a stable position for the pressing of the metal which follows in later process steps.
Once the plate is securely held, the pressure on the ram or punch 20 is increased to overcome the resistance force of the support 16 and move and compress the thick plate 30 by passing it through the confined opening 22 that is formed between the tapered surface of the ram and the pressing surface 13 of the inserts 14. The space or clearance 22 varies because the ram is tapered. As the ram moves relative to the die opening the thick plate is forced or urged between the tapered ram and the die inserts and is compressively ironed to a reduced thickness filling the clearance space 22.
Because the plate 30 is being compressively irone~
between the ram and the ironing or pressing inserts 14, substantial frictional resistance is built up between the inserts and the metal plate. However, most of this force is directed against the inserts. It has been found that a pressure of only fity tons on the ram is enough to compressively form and reduce the plate in thickness from forty to fifty percent.
Great compressive and frictional forces are exerted on the inserts. Therefore, the retainer block 12 and the inserts 14 must be sufficiently strong to resist deformation. Also, the insert material must be sufficiently hard and smooth so that the plate metal is not galled or otherwise damaged. An insert having a hardness of about forty-five to fifty on the Rockwell C scale has been used successfully in the operation of this invention.
The resistance between plate metal and insert is also reduced by using an extreme pressure type lubricant to avoid metal to metal contact.

~4 ~036820 Another feature of the apparatus is the shape and size of the inserts. The corners or shoulders 11 of the inserts 14 are rounded to allow the plate to be fed or urged more easily into the clearance 22 between the ram and inserts. The opening formed by the shoulder must necessarily be wider than the initial thickness of metal being driven therethrough. FIGURE 7 shows the beveled form of the shoulder portion 11 of the pressing surface.
In this embodiment the corner 11 has been cut off at a forty-five degree angle A. An angle in the range of thirty to sixty degrees 9hould be satisfactory depending upon the metal to b~ formed. If the angle A is less than thirty degrees the opening leading to the pressing surface 24 is longer and narrower and may cause detrimental frictional forces between the surfaces. If the angle A is greater than 60 degrees the shoulder surface may act to cut or peel back the metal rather than feed it between the surfaces to be pressed. Also, all exposed corners that may come in contact with the metal plate are rounded to likewise avoid damage to the plate. F}GURE 8 shOws a form using a rounded corner greater than the original thickness of the metal plate 30 to assure smoother feed of the metal between the surface of the pressing inserts 14a and the ram 20.
Each shoulder 11 of the insert 14 provides a gradually diminishing dimension in the region of the entrance to assist the compression of the metal plate 30 between the pressure applying surface of the ram 20 and the ironing surface 13 of the die inserts 14. By providing a converging region for application of pressure the rounded shoulder or inlet 11 helps to urge the thick metal plate 30 between the thinner space between the ram 20 and the lands 13 of the inserts 14.
The lands or pressing surfaces 13 are the raised portions on the inserts 14 which do the actual pressing of the plate metal to its desired thickness. Shims (not shown) may be positioned between the inserts and the retainer block to obtain the desired clearance. The lands 13 are maintained as small as possible to reduce the frictional forces. Lands as small as one-quarter inch wide have been used successfully. However, it may be possible to reduce the area of the lands even more.
As pressure exceeding the resistance force of the support 16 is applied to the ram, the plate is forced between the ram 20 and the lands 13 of the insert 14 and the plate is compressively ironed to the desired thickness. The change in shape of the plate 30 is not like conventional drawing In conventional drawing processes a constant wall thickness is desired. Ideally, the plate change5 shape but not thickness.
Therefore, there is always a reduction in diameter or length and width of the part in one direction as well as an increase in height or width in another direction. When a change in thickness does occur, it is uncontrolled and may result in fracture of the part. The increase in height is almost totally dependent on the 2Q amount of reduction in another direction. Conversely for the compressive ironing in this invention, a change in thickness or tapering of the wall is desired. The diameter or the width of the plate is not effectively changed. The increase in height of the feeder walls is totally dependent upon the amount of cross-sectional reduction in thickness.
The amount of taper of the plate is controlled mainly by the shape or taper of the ram. The ram shown in FIGURES 2, 3 and 5 is uniformly tapered. And, therefore, the feeder wall made therefrom is thicker at the bottom taperins uniformly to a thinner cross-sectional area near the top. This taper 1036~ZO
approximates the feeder wall shape conventionally used.
To remove the formed plate 30 from the die 10 it has been found that the formed plate should be pushed completely past the lands 13 as shown in FIGURE 5. Because the inside walls of the pressing inserts diverge from the narrower lands, the pressure on the sidewalls 47 of the formed plate 30 is released and the ram can be more easily removed. FIGURE 9 illustrates an embodiment of the invention which provides means for aiding in the release of the part. As shown, wiper blades 25 may be inserted from their retracted position in the retainer blocks 12 to restrain the formed plate 30 and aid withdrawal of the ram 20 therefrom.
Once the ram is withdrawn, the hydraulic system of the support or tip nest 16 may be activated and the formed part pushed upwardly and out of the die 10. Alternatively, if the formed plate is not easily ejected upwardly from the die, the support plate 16 may be retracted further than that shown in FIGURE 5 and the part removed from an open end of the die 10 or from beneath the die.
Prior to forming the plate 30 into a feeder 40 it may be necessary to anneal the plate. The type or degree of annealing depends upon the reduction in the cross-section of thickness per pass and the type of alloy composition used. It has been found that for an alloy comprised mainly of platinum and rhodium that an annealing of ten minutes at 1850F followed by a ten minute cooling period yields a plate having sufficient tensile strength to avoid tearing yet ductile enough to go through the forming operation without fracture. The forming process of the invention also promotes grain growth in a different direction than that normally encountered with prior rolling and feeder fabrication methods 1036~20 FIGURES 10 and 11 illustrate completed forms of the unitary bottom wall 44 and sidewalls 47 of the present invention.
The change in thickness illustrated was attained by passing the metal through the compressing and forming apparatus at least two times. However, for some feeder designs or alloy compositions one pass may be sufficient. Once the plate is compressed to its predetermined thicknesses, the sidewalls 47 and flanges 49 are bent and formed by conventional metal working techniques to the final 8hape such as shown in FIGURE 11. Thereafter the thicker end plates 43, electric terminals 42 and other necessary parts are attached by conventional fusion bonding techniques.
The present invention does not eliminate all the welds in a feeder but does eliminate a major portion of them. Of special significance is the elimination of the long-welds that heretofore were necessary for attachment of the tip plate or bottom wall 44 to the feeder sidewalls 47 and for connection of the upper and thinner sidewall portions to the lower and thicker 8idewall portions.
One of the most important features of the invention is that for a particular feeder design, the bottom wall 44 and sidewalls 47 can be made more nearly identical. There is less variation of the type previously caused by differences in welding machines or in the ability of the personnel fabricating the feeders.
Although the invention has been described with regard to platinum-rhodium alloys, it will be evident that feeders in accordance with the present invention can be made from other ductile high temperature resistant metals.
It is apparent that, within the scope of the invention, modifications and different arrangements may be made other than as herein disclosed, and the present disclosure is illustrative merely, the invention comprehending all variations thereof. For example, many variations in the thickness of the feeder sidewalls are possible by using different shapes and sizes of punches and die inserts. Also, the plate 30 initially used may be rolled or formed to shapes other than the uniform thickness shown in FIGURES
2 and 3.
In addition, the contour of the ram 20 or pressing inserts 14 can be varied in the longitudinal direction from end to end. Heretofore, the feeder wall thickness has been varied mainly in the vertical direction; thickness variations along the length were too difficult to fabricate. Using the present `
invention variations in feeder sidewall thickness along the length are practical and reproducible. Thus for a particular feeder that operates characteristically hotter near its center portion, the ram and die can be modified to change the wall thickness in that typically hotter area, thereby making a feeder that operates with more uniform temperatures from end to end.

~L

Claims (10)

THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:

1. A resistance heated feeder for supply of molten mineral material in the form of streams to be attenuated into fibers; said feeder comprising end walls, sidewalls and a stream flow region at a normally lower wall; said sidewalls and lower wall being formed from a single piece of ductile, high temperature resistant, electric current-conducting material and wherein the thicknesses of said sidewalls are structured to provide non-uniform-ity in thickness along at least a portion thereof, said wall structuring facilitating a pattern of heat generation to provide uniformity of temperature in the molten material at the stream flow region.

2. A resistance heated feeder as claimed in Claim 1, wherein each of said end walls is formed from a separate piece of ductile, high temperature resistant, electric current-conducting material attached to the sidewalls.

3. A resistance heated feeder as claimed in Claim 1, wherein said stream flow region is at a bottom wall therein.

4. A resistance heated feeder as claimed in Claim 1, wherein each of the sidewalls comprises an upper region and a lower region wherein the wall thickness of at least a portion of the lower region is greater than the wall thickness of at least a portion of the upper region.

5. A resistance heated feeder as claimed in Claim 4, wherein the wall thickness of the sidewalls diminishes in cross section from the lower region of the sidewalls to the upper region of the sidewalls.

6. A resistance heated feeder as claimed in Claim 4, wherein the wall thickness of a portion of the lower region is at least fifty percent greater than the wall thickness of a portion of the upper region.

7. A resistance heated feeder as claimed in Claim 1, wherein the sidewalls are rectangular in shape having end regions and a center region wherein the wall thicknesses of the end regions are a different thickness than the wall thickness of the center region.

8. A resistance heated feeder as claimed in Claim 7, where-in the difference in wall thickness between the end regions and the center region is at least twenty-five percent.

9. A method for forming a channel-shaped member from a planar member of ductile, electric current-conducting material for use in fabricating a feeder which supplies molten mineral material in the form of streams to be attenuated into filaments, comprising the steps of:
disposing the planar member between a tapered projecting member and a block having an aperture formed therein and a raised land defining a linear pressing surface along the interior of the aperture;
moving the projecting member and the block relative to each other such that the projecting member contacts a major surface of the planar member;
forcing the tapered projecting member and planar member through the aperture in the block thereby urging the planar member to move in a direction transverse to the lands defining the press-ing surface of the aperture;

compressing the planar member between the tapered surface of the projecting member and the lands defining the pressing sur-face to form a channel-shaped member having sidewalls of predeter-mined varied thickness corresponding to the clearance between the surface of the tapered projecting member and the pressing surface;
and removing the channel-shaped member from the block.

10. A method as claimed in Claim 9, wherein said aperture is large enough to accommodate the passage of the projecting member therethrough.