BRPI0903351A2 - structural body, production method, steam release device, steam release method and steam release kit - Google Patents
structural body, production method, steam release device, steam release method and steam release kit Download PDFInfo
- Publication number
- BRPI0903351A2 BRPI0903351A2 BRPI0903351-3A BRPI0903351A BRPI0903351A2 BR PI0903351 A2 BRPI0903351 A2 BR PI0903351A2 BR PI0903351 A BRPI0903351 A BR PI0903351A BR PI0903351 A2 BRPI0903351 A2 BR PI0903351A2
- Authority
- BR
- Brazil
- Prior art keywords
- structural body
- liquid
- wick
- particles
- fibrous
- Prior art date
Abstract
A presente invenção refere-se a um corpo estrutural que é composto de um corpo estrutural fibroso e partículas das quais pelo menos parte está presente na forma de um agregado ligado ao corpo estrutural fibroso. O corpo estrutural pode absorver e então vaporizar liquido rapidamente e estavelmente. O corpo estrutural pode ser usado como um pavio de dispositivo de liberação de vapor, tal como um dispositivo inseticida de liberação de vapor quente do tipo absorção de líquido.The present invention relates to a structural body which is composed of a fibrous structural body and particles of which at least part is present in the form of an aggregate attached to the fibrous structural body. The structural body can absorb and then vaporize liquid rapidly and stably. The structural body can be used as a vapor release device wick, such as a liquid absorbing type hot vapor release insecticide device.
Description
Relatório Descritivo da Patente de Invenção para "CORPO ES-TRUTURAL, MÉTODO PARA A PRODUÇÃO DO MESMO, DISPOSITIVODE LIBERAÇÃO DE VAPOR, MÉTODO DE LIBERAÇÃO DE VAPOR EKIT PARA LIBERAÇÃO DE VAPOR".Report of the Invention Patent for "ESTRUCTURAL BODY, METHOD FOR PRODUCTION OF THE SAME, STEAM RELEASE DEVICE, EKIT STEAM RELEASE METHOD".
Campo da InvençãoField of the Invention
A presente invenção refere-se a um corpo estrutural compreen-dendo um material fibroso e partículas aderidas ao material fibroso, a ummétodo para produção do corpo estrutural, a um dispositivo de liberação devapor compreendendo o corpo estrutural, a um método de liberação de va-por e a um kit para liberação de vapor.The present invention relates to a structural body comprising a fibrous material and particles adhered to the fibrous material, a method for producing the structural body, a slow release device comprising the structural body, a method of releasing the vapor by and to a steam release kit.
Técnica AnteriorPrior Art
Dispositivos inseticidas de liberação de vapor quente do tipo ab-sorção de líquido têm sido convencionalmente usados a fim de vaporizarinseticidas e liberá-los eficientemente para o ar em um ambiente para o pro-pósito de controle de mosquito. Tais dispositivos inseticidas geralmente fun-cionam de maneira tal que um líquido químico que foi absorvido por um pa-vio inserido em um reservatório contendo o líquido químico é vaporizado a-través de aquecimento da extremidade superior do pavio. Em dispositivosinseticidas de liberação de vapor quente do tipo absorção de líquido, um pa-vio de absorção de líquido é usado, o qual é poroso e que tem espaços va-zios contíguos a fim de vaporizar um líquido químico estavelmente. Os dis-positivos são configurados de modo que um líquido químico possa ser ab-sorvido e vaporizado através de tal ação capilar que o líquido químico semove em espaços vazios pequenos no pavio.Insecticidal liquid vapor-absorbing hot vapor release devices have conventionally been used to vaporize insecticides and efficiently release them into the air in an environment for the purpose of mosquito control. Such insecticidal devices generally function in such a way that a chemical liquid that has been absorbed by a powder inserted into a reservoir containing the chemical liquid is vaporized by heating the upper end of the wick. In liquid-absorption type hot vapor-release insecticidal devices, a liquid-absorbing passage is used which is porous and has adjoining void spaces in order to vaporize a chemical liquid stably. The devices are configured so that a chemical liquid can be absorbed and vaporized through such capillary action that the chemical fluid moves in small void spaces in the wick.
A JP 55-58047 A divulga um pavio para dispositivos inseticidasde liberação de vapor quente do tipo absorção de líquido, o pavio sendo umproduto obtido através de fortificação de uma mistura de pó mineral, tal co-mo argila ativada, terra diatomácea e talco, com farinha de madeira ou pó decarvão, com um agente de cola, tal como dextrina ou amido. A JP 5-328884JP 55-58047 A discloses a wick for liquid-absorption type hot vapor release insecticidal devices, the wick being a product obtained by fortifying a mixture of mineral dust, such as activated clay, diatomaceous earth and talc, with wood flour or charcoal powder with a sizing agent such as dextrin or starch. JP 5-328884
A e a JP 8-205744 A revelam, cada uma, um pavio tendo em seu centro umacamada de absorção de líquido feita de fibras, camada que é coberta comum trançado de fibras, e também divulga um produto onde o trançado defibra acima mencionado é coberto ainda com verniz de silicone, deste modofixando a camada de absorção de líquido ao trançado.A and JP 8-205744 A each disclose a wick having at its center a fiber absorbing liquid layer, a layer which is covered with fiber braided joint, and also discloses a product where the aforementioned fiberglass braid is covered. still with silicone varnish, thus modifying the liquid absorption layer to the braided.
Descrição da InvençãoDescription of the Invention
Problemas a serem resolvidos pela invençãoProblems to be solved by the invention
No entanto, o pavio divulgado na JP 55-58047 A exibe uma taxade absorção de líquido baixa e precisa de várias horas para absorção de umlíquido químico. Deste modo, ele precisa de muito tempo até que ele absor-va uma quantidade necessária de líquido químico para se tornar pronto paravaporização do líquido.However, the wick disclosed in JP 55-58047 A exhibits low and precise liquid absorption rates of several hours for absorption of a chemical liquid. Thus, it needs a long time until it absorbs a necessary amount of chemical liquid to become ready for liquid vaporization.
Os pavios divulgados na JP 5-328884 A ou JP 8-205744 A tam-bém tinham um problema que a taxa de absorção de líquido é baixa e ospavios precisam de um longo tempo até que eles absorvam uma quantidadenecessária de líquido químico para se tornarem prontos para vaporização dolíquido.Wicks disclosed in JP 5-328884 A or JP 8-205744 Also had a problem that the liquid absorption rate is low and the waves need a long time before they absorb a necessary amount of chemical liquid to be ready. for doliquid vaporization.
A presente invenção foi feita em vista desses problemas, e oobjetivo então é prover um corpo estrutural que possa absorver um líquidorapidamente e estavelmente e que seja excelente em habilidade de libera-ção de vapor, sem usar um agente de colagem ou resina.The present invention has been made in view of these problems, and the purpose then is to provide a structural body that can absorb a liquid quickly and stably and which is excellent in vapor release ability without using a sizing agent or resin.
Meios para resolver os problemasMeans to solve problems
A fim de resolver os problemas acima, o corpo estrutural da pre-sente invenção é caracterizado pelo fato de que ele contém partículas e umcorpo estrutural fibroso e que pelo menos parte das partículas está presentena forma de um agregado ligado ao corpo estrutural fibroso.In order to solve the above problems, the structural body of the present invention is characterized by the fact that it contains particles and a fibrous structural body and that at least part of the particles is in the form of an aggregate attached to the fibrous structural body.
No corpo estrutural da presente invenção, é desejável que o di-âmetro de partícula médio das partículas seja 1 a 500 um.In the structural body of the present invention, it is desirable that the average particle diameter of the particles be 1 to 500 µm.
No corpo estrutural da presente invenção, é desejável que aspartículas sejam partículas inorgânicas.In the structural body of the present invention, it is desirable that the particles be inorganic particles.
No corpo estrutural da presente invenção, é desejável que aspartículas inorgânicas sejam sílica.In the structural body of the present invention, it is desirable for inorganic particles to be silica.
No corpo estrutural da presente invenção, é desejável que ocorpo estrutural fibroso seja feito de papel, tecido tecido ou tecido não-tecido.No corpo estrutural fibroso da presente invenção, é desejávelque a estrutura esteja em um formato colunar.In the structural body of the present invention, it is desirable that the fibrous structural body be made of paper, woven fabric or nonwoven fabric. In the fibrous structural body of the present invention, it is desirable that the structure be in a columnar shape.
Uma das aplicações preferidas do corpo estrutural da presenteinvenção é um pavio, e o uso do corpo estrutural da presente invenção comoum pavio é uma das modalidades preferidas da presente invenção.One preferred embodiment of the body of the present invention is a wick, and the use of the structural body of the present invention as a wick is one of the preferred embodiments of the present invention.
O dispositivo de liberação de vapor da presente invenção é ca-racterizado por ter:The vapor release device of the present invention is characterized by having:
um reservatório contendo um líquido vaporizável, ea reservoir containing a vaporizable liquid, and
um pavio feito do corpo estrutural da presente invenção, o pavioestando localizado de maneira tal que uma parte do pavio é imersa dentrodo líquido vaporizável e outra parte do pavio é exposta para o exterior doreservatório.It is a wick made of the structural body of the present invention, the wick being located in such a way that one part of the wick is immersed in vaporizable liquid and another part of the wick is exposed to the exterior of the reservoir.
É desejável que o dispositivo de liberação de vapor da presenteinvenção tenha ainda dispositivos de aquecimento para aquecimento de umaporção do pavio, a porção não sendo imersa no líquido vaporizável.It is desirable that the steam delivery device of the present invention further have heating devices for heating a portion of the wick, the portion not being immersed in the vaporizable liquid.
No dispositivo de liberação de vapor da presente invenção, édesejável que o líquido vaporizável compreenda um componente inseticida.In the vapor delivery device of the present invention, it is desirable for the vaporizable liquid to comprise an insecticide component.
No dispositivo de liberação de vapor da presente invenção, édesejável que o líquido vaporizável compreenda ainda um solvente orgânico.In the vapor delivery device of the present invention, it is desirable that the vaporizable liquid further comprise an organic solvent.
No dispositivo de liberação de vapor da presente invenção, édesejável que o líquido vaporizável compreenda água em adição ao solventeorgânico e o componente inseticida.In the vapor delivery device of the present invention, it is desirable that the vaporizable liquid comprises water in addition to the organic solvent and the insecticide component.
No dispositivo de liberação de vapor da presente invenção, édesejável que o componente inseticida seja um composto piretroide.In the vapor delivery device of the present invention, it is desirable for the insecticide component to be a pyrethroid compound.
O método de liberação de vapor da presente invenção é caracte-rizado por incluir as ações que seguem de:The steam release method of the present invention is characterized by including the following actions:
Imersão de uma parte do corpo estrutural da presente invençãodentro de um líquido de vaporização, deste modo fazendo com que o corpoestrutural absorva o líquido, eImmersion of a structural body part of the present invention into a vaporizing liquid, thereby causing the structural body to absorb the liquid, and
liberação, a partir da superfície do corpo estrutural, de vapor ge-rado a partir do líquido vaporizável absorvido.releasing steam generated from the absorbed vaporizable liquid from the surface of the structural body.
O kit para liberação de vapor da presente invenção é caracteri-zado por compreender o corpo estrutural da presente invenção.The steam release kit of the present invention is characterized in that it comprises the structural body of the present invention.
O método da presente invenção para produção de um corpo es-trutural é caracterizado por incluir:The method of the present invention for producing a structural body is characterized by including:
uma etapa de absorção de trazer pelo menos parte de um corpoestrutural fibroso em contato com um líquido de dispersão onde partículassão dispersas em um meio líquido, deste modo fazendo com que o corpoestrutural fibroso absorva o líquido de dispersão, ean absorption step of bringing at least part of a fibrous body into contact with a dispersing liquid where particles are dispersed in a liquid medium, thereby causing the fibrous body to absorb the dispersing liquid, and
uma etapa de remoção de remoção do meio líquido do corpoestrutural fibroso que absorveu o líquido de dispersão.a removal step of removing the liquid medium from the fibrous structural body that has absorbed the dispersing liquid.
No método da presente invenção para produção de um corpoestrutural, é desejável que na etapa de absorção o ato de trazer pelo menosparte do corpo estrutural fibroso em contato com um líquido de dispersãoseja realizado através de imersão da pelo menos parte do corpo estruturalfibroso no líquido de dispersão.In the method of the present invention for producing a structural body, it is desirable that in the absorption step bringing at least part of the fibrous structural body into contact with a dispersing liquid is accomplished by immersing at least part of the fibrous structural body in the dispersing liquid. .
No método da presente invenção para produção de um corpoestrutural, é desejável que o corpo estrutural fibroso esteja em um formatocolunar e que na etapa de absorção o ato de trazer pelo menos parte de umcorpo estrutural fibroso em contato com um líquido de dispersão seja reali-zado através da imersão de uma parte da extremidade longitudinal do corpoestrutural fibroso no líquido de dispersão.In the method of the present invention for producing a structural body, it is desirable for the fibrous structural body to be in a columnar format and that in the absorption step the act of bringing at least part of a fibrous structural body in contact with a dispersing liquid is performed. by immersing a portion of the longitudinal end of the fibrous structural body in the dispersing liquid.
No método da presente invenção para produção de um corpoestrutural, é desejável que a remoção do meio líquido do corpo estruturalfibroso que absorveu o líquido de dispersão seja realizada através de seca-gem do corpo estrutural fibroso.In the method of the present invention for producing a structural body, it is desirable that removal of the liquid medium from the fibrous structural body that has absorbed the dispersing liquid is accomplished by drying the fibrous structural body.
No método da presente invenção para produção de um corpoestrutural, é desejável que a etapa de absorção e a etapa de remoção sejamrepetidas até que a proporção das partículas que estavam contidas no corpoestrutural fibroso fique 10 a 95% em peso, contanto que o peso do corpoestrutural seja deixado ser 100% em peso.In the method of the present invention for producing a structural body, it is desirable that the absorption step and the removal step be repeated until the proportion of the particles that were contained in the fibrous body is 10 to 95% by weight, provided that the weight of the body let be 100% by weight.
No método da presente invenção para produção de um corpoestrutural, é desejável que a concentração das partículas no líquido de dis-persão seja 1 a 50% em peso.No método da presente invenção para produção de um corpoestrutural, é desejável que o diâmetro de partícula médio das partículas seja 1 a 500 nm.In the method of the present invention for producing a structural body, it is desirable that the concentration of the particles in the dispersion liquid be 1 to 50% by weight. In the method of the present invention for producing a structural body, it is desirable that the particle diameter average particle size is 1 to 500 nm.
No método da presente invenção para produção de um corpoestrutural, é desejável que o corpo estrutural fibroso seja feito de papel, teci-do tecido ou tecido não-tecido.In the method of the present invention for producing a structural body, it is desirable for the fibrous structural body to be made of paper, woven fabric or nonwoven fabric.
No método da presente invenção para produção de um corpoestrutural, é desejável que as partículas sejam partículas inorgânicas.In the method of the present invention for producing a structural body, it is desirable that the particles be inorganic particles.
No método da presente invenção para produção de um corpoestrutural, é desejável que as partículas inorgânicas sejam sílica.In the method of the present invention for producing a structural body, it is desirable that the inorganic particles be silica.
O corpo estrutural da presente invenção é caracterizado por serproduzido através de qualquer um dos métodos acima.Vantagens da invençãoThe structural body of the present invention is characterized by being produced by any of the above methods.
A presente invenção torna possível prover um corpo estruturalque pode absorver e vaporizar líquido rapidamente e estavelmente.The present invention makes it possible to provide a structural body that can absorb and vaporize liquid rapidly and stably.
Breve descrição dos desenhosBrief Description of Drawings
A figura 1 é uma vista secional esquemática de um dispositivoinseticida de liberação de vapor quente do tipo absorção de líquido de acor-do com uma modalidade exemplar da presente invenção.Fig. 1 is a schematic sectional view of a liquid vapor absorption type insecticidal hot vapor release device according to an exemplary embodiment of the present invention.
A figura 2 é um diagrama mostrando os resultados de mapea-mento de Si02 por um EPMA (Electron Probe Micro Analyzer) de uma seçãotransversal de um pavio de acordo com uma modalidade exemplar da pre-sente invenção.Figure 2 is a diagram showing the results of mapping Si02 by an Electron Probe Micro Analyzer (EPMA) of a cross section of a wick according to an exemplary embodiment of the present invention.
A figura 3 é um diagrama mostrando uma imagem de microscó-pio eletrônico de um pavio de acordo com uma modalidade exemplar da pre-sente invenção.Figure 3 is a diagram showing an electron microscope image of a wick according to an exemplary embodiment of the present invention.
A figura 4 é um diagrama mostrando os resultados do mapea-mento de Si02 por um EPMA (Electron Probe Micro Analyzer) de uma seçãotransversal de um pavio de acordo com outra modalidade exemplar da pre-sente invenção.Figure 4 is a diagram showing the results of mapping of Si02 by an Electron Probe Micro Analyzer (EPMA) of a cross section of a wick according to another exemplary embodiment of the present invention.
A figura 5 é um diagrama mostrando os resultados de mapea-mento de Si02 por um EPMA (Electron Probe Micro Analyzer) de uma seçãotransversal de um pavio de acordo com outra modalidade exemplar da pre-sente invenção.Figure 5 is a diagram showing the results of mapping Si02 by an Electron Probe Micro Analyzer (EPMA) of a cross section of a wick according to another exemplary embodiment of the present invention.
A figura 6 é um diagrama mostrando uma imagem de microscó-pio eletrônico de um pavio de acordo com outra modalidade exemplar dapresente invenção.Figure 6 is a diagram showing an electron microscope image of a wick according to another exemplary embodiment of the present invention.
A figura 7 é um gráfico mostrando a habilidade de liberação devapor de um pavio.Figure 7 is a graph showing the slow release ability of a wick.
A figura 8 é um gráfico mostrando a habilidade de liberação devapor de um pavio.Figure 8 is a graph showing the slow release ability of a wick.
Descrição de modalidades preferidas da presente invenção[Corpo estrutural]Description of Preferred Embodiments of the Present Invention [Structural Body]
O corpo estrutural da presente invenção é caracterizado pelofato de que ele contém partículas e um corpo estrutural fibroso e que pelomenos parte das partículas está presente na forma de um agregado ligadoao corpo estrutural fibroso. O corpo estrutural pode ser usado adequada-mente, por exemplo, como um pavio que absorve e então vaporiza líquido. Opavio da presente invenção pode ser usado adequadamente como um pavio1 de um dispositivo inseticida de liberação de vapor quente do tipo absorçãode líquido 5 tal como aquele mostrado na figura 1. Além disso, ele pode serusado adequadamente também como um pavio de um dispositivo de aroma-tização, um dispositivo desodorizante, etc. O dispositivo inseticida de libera-ção de vapor quente do tipo absorção de líquido 5 mostrado na figura 1 édescrito em detalhes mais tarde.The structural body of the present invention is characterized by the fact that it contains particles and a fibrous structural body and that at least part of the particles is present in the form of an aggregate attached to the fibrous structural body. The structural body may be suitably used, for example, as a wick that absorbs and then vaporizes liquid. The opioid of the present invention may suitably be used as a wick of a liquid-absorption type hot vapor insecticidal device 5 such as that shown in Figure 1. In addition, it may suitably also be used as a wick of a flavoring device. a deodorizing device, etc. The insecticidal liquid-vapor type hot vapor release device 5 shown in Figure 1 is described in detail later.
(Corpo estrutural fibroso)(Fibrous structural body)
O pavio da presente invenção contém um corpo estrutural fibro-so como um material de base. No presente relatório, um corpo estrutural fi-broso pode ser referido também como um material de base. O corpo estrutu-ral fibroso é constituído de uma pluralidade de objetos lineares finos agrega-dos, que são geralmente chamados fibras, e o corpo estrutural fibroso temespaços vazios circundados pelas fibras agregadas. O corpo estrutural fibro-so contém de preferência fibras hidrofílicas e com mais preferência é papel,tecido tecido ou tecido não-tecido que são excelentes em habilidade de ab-sorção de líquido. Embora o corpo estrutural fibroso em si tenha excelentehabilidade de absorção de líquido, a presença de partículas na forma de umagregado no corpo estrutural fibroso torna o pavio excelente em estabilidadede formato e capaz de absorver líquido estavelmente e rapidamente. Se pa-pel for usado como o corpo estrutural fibroso, o pavio é estável e ele podemanter sua estrutura mesmo se ele for posto em um solvente aquoso. Comoo solvente aquoso, água ou um solvente hidrofílico é pretendido ser usado.The wick of the present invention contains a fibrous structural body as a base material. In the present report, a fine structural body may also be referred to as a base material. The fibrous structural body is comprised of a plurality of thin aggregate linear objects, which are generally called fibers, and the fibrous structural body has empty spaces surrounded by the aggregate fibers. The fibrous structural body preferably contains hydrophilic fibers and more preferably is paper, woven fabric or nonwoven fabric which is excellent in liquid absorbency. While the fibrous structural body itself has excellent liquid absorption ability, the presence of an ugly particle in the fibrous structural body makes the wick excellent in shape stability and capable of absorbing liquid stably and rapidly. If paper is used as the fibrous structural body, the wick is stable and it can maintain its structure even if it is placed in an aqueous solvent. As the aqueous solvent, water or a hydrophilic solvent is intended to be used.
O papel a ser usado como o corpo estrutural fibroso é um produ-to obtido através de dispersão em água de uma substância fibrosa (polpa)isolada de plantas tal como madeiras, espalhamento da dispersão resultanteem uma rede ou tela de modo que uma camada fina possa ser formada, en-trelaçamento das polpas, desidratação e secagem. Dentre os papéis, umpapel que é classificado como papel sanitário inclui papel de seda, papelhigiênico, papel toalha, etc, e esses são caracterizados por sua alta absorvi-dade de água. Especialmente papéis sanitários são preferidos como o papelpara a presente invenção.Paper to be used as the fibrous structural body is a product obtained by dispersing in water a fibrous substance (pulp) isolated from plants such as wood, spreading the resulting dispersion into a mesh or mesh so that a thin layer can formed, interlacing of the pulps, dehydration and drying. Among the papers, a paper that is classified as toilet paper includes tissue paper, hygienic paper, paper towels, etc., and these are characterized by their high water absorbability. Especially sanitary papers are preferred as paper for the present invention.
Tecidos tecidos ou tecidos não-tecidos a serem usados como umcorpo estrutural fibroso são feitos de fibras naturais, fibras químicas, fibrassintéticas, fibras inorgânicas, ou similar, e qualquer uma de tais fibras podeser escolhida apropriadamente dependendo da aplicação pretendida. As fi-bras naturais conforme aqui referido são fibras obteníveis a partir de materiaisexistentes na natureza. Fibras naturais derivadas de planta incluem algodão,linho, bambu e polpa. Fibras naturais derivadas de animal incluem lã e seda.Woven fabrics or nonwoven fabrics to be used as a fibrous structural body are made from natural fibers, chemical fibers, fiber fibers, inorganic fibers, or the like, and any such fibers may be chosen appropriately depending on the intended application. Natural fibers as referred to herein are fibers obtainable from naturally existing materials. Natural plant-derived fibers include cotton, linen, bamboo and pulp. Natural animal-derived fibers include wool and silk.
As fibras químicas são fibras obtidas através de tratamento quí-mico de materiais existentes na natureza e incluem raion e raion de cupra-mônio, que são obtidos dissolvendo celulose, tal como polpa, em um solven-te e então regeneração de celulose, e acetato de celulose (triacetato) resul-tante de tratamento químico de celulose. As fibras sintéticas são fibras qui-micamente sintetizadas de matérias-primas tal como petróleo, e há muitosexemplos delas, tal como náilon, um poliéster, fibra acrílica, polipropileno,poliuretano e vinilon. Fibras inorgânicas incluem fibras de vidro, fibras demetal e fibras de carbono.(Partículas)Chemical fibers are fibers obtained by chemically treating naturally occurring materials and include cuprammonium raion and raion, which are obtained by dissolving cellulose, such as pulp, in a solvent and then regenerating cellulose, and acetate. of cellulose (triacetate) resulting from chemical treatment of cellulose. Synthetic fibers are chemically synthesized fibers from raw materials such as petroleum, and there are many examples of them, such as nylon, a polyester, acrylic fiber, polypropylene, polyurethane and vinyl. Inorganic fibers include glass fibers, demetal fibers and carbon fibers.
No pavio da presente invenção, as partículas ligadas ao corpoestrutural fibroso não são particularmente restritas com relação à sua com-posição química. Embora vários materiais possam ser usados para as partí-culas, substâncias inorgânicas, substâncias orgânicas e suas misturas sãoadequadamente usadas. Exemplos de partículas que podem ser usadas a-dequadamente para a presente invenção são como segue.In the wick of the present invention, the particles bound to the fibrous body are not particularly restricted with respect to their chemical composition. Although various materials may be used for the particles, inorganic substances, organic substances and mixtures thereof are suitably used. Examples of particles which may be suitably used for the present invention are as follows.
A substância inorgânica inclui metais alcalinos, metais alcalino-terrosos, metais de transição e metais não-ferrosos e exemplos específicosdos mesmos incluem ouro, paládio, platina, prata, e alumínio, ou seus óxi-dos, hidróxidos, sulfetos ou sais, tal como carbonatos e sulfatos, e exemplosadicionais incluem óxidos, hidróxidos, sulfetos ou sais, tal como carbonatose sulfato, de silício, alumínio, zinco, magnésio, cálcio, bário, titânio, zircônio,manganês, ferro, cério, níquel, estanho e similar. Dentre essas partículas,partículas inorgânicas são preferidas, e sílica é particularmente preferida.The inorganic substance includes alkali metals, alkaline earth metals, transition metals and nonferrous metals and specific examples thereof include gold, palladium, platinum, silver, and aluminum, or their oxides, hydroxides, sulfides or salts, such as carbonates and sulfates, and additional examples include oxides, hydroxides, sulfides or salts, such as carbonate sulfate, from silicon, aluminum, zinc, magnesium, calcium, barium, titanium, zirconium, manganese, iron, cerium, nickel, tin and the like. Among these particles, inorganic particles are preferred, and silica is particularly preferred.
A substância orgânica inclui resinas, etc, e exemplos das resinasincluem resinas de poliolefina, tal como polietileno, polipropileno e poliestire-no; resinas acrílicas tal como metacrilato de polimetila; resinas de poliamidatal como policondensado de hexametilenodiamina-ácido adípico; resinas depoliéster tal como tereftalato de polietileno e ácido poliacético; resinas depoliéter, tal como polifenileno éter e polipropileno glicol; resinas de policar-bonato e resinas do tipo cristal líquido.The organic substance includes resins, etc., and examples of resins include polyolefin resins, such as polyethylene, polypropylene and polystyrene; acrylic resins such as polymethyl methacrylate; polyamidatal resins such as hexamethylenediamine adipic acid polycondensate; polyester resins such as polyethylene terephthalate and polyacetic acid; polyether ether resins, such as polyphenylene ether and polypropylene glycol; polycarbonate resins and liquid crystal resins.
Com relação a tamanho e à forma das partículas que constituemos agregados ligados ao corpo estrutural fibroso, quaisquer partículas po-dem ser usadas que tenham um tamanho tão pequeno que as partículaspossam ser aceitas dentro de espaços vazios no corpo estrutural fibroso.Partículas preferidas particulares são aquelas que são tão pequenas queelas podem ser fornecidas na forma de uma solução coloidal onde partículassão dispersas em um meio líquido. Quando as partículas são fornecidas apartir de uma solução coloidal, embora as partículas possam estar em qual-quer tamanho de modo que elas possam ser dispersas coloidalmente em ummeio líquido, é preferido usar partículas tendo um diâmetro de partícula mé-dio de 1 a 500 nm, com mais preferência 2 nm a 100 nm e com mais prefe-rência ainda 5 nm a 70 nm porque elas podem ser manuseadas facilmente.O diâmetro da partícula pode ser escolhido dependendo da aplicação pre-tendida. Quanto menores os espaços vazios no corpo estrutural fibroso equanto menor a porosidade, menor é a velocidade de absorção de líquidoquando sendo usado como um pavio.With respect to the size and shape of the aggregate particles attached to the fibrous structural body, any particles may be used that are so small that the particles may be accepted into voids in the fibrous structural body. Particular preferred particles are those. They are so small that they can be supplied as a colloidal solution where particles are dispersed in a liquid medium. When the particles are provided from a colloidal solution, although the particles may be of any size so that they can be colloidally dispersed in a liquid medium, it is preferred to use particles having an average particle diameter of 1 to 500 nm. more preferably 2 nm to 100 nm and even more preferably 5 nm to 70 nm because they can be handled easily. The particle diameter can be chosen depending on the intended application. The smaller the voids in the fibrous structural body, the smaller the porosity, the slower the rate of liquid absorption when used as a wick.
Soluções coloidais convencionais podem ser usadas como asolução coloidal acima mencionada para a presente invenção. Exemplos detais soluções coloidais incluem soluções coloidais de metal, soluções coloi-dais de oxido, soluções coloidais de hidróxido, soluções coloidais de carbo-nato e soluções coloidais de sulfato. Exemplos de elementos de metal conti-dos em soluções coloidais de metal incluem ouro, paládio, platina e prata.Exemplos dos elementos contidos em soluções coloidais de oxido, soluçõescoloidais de hidróxido, soluções coloidais de carbonato e soluções coloidaisde sulfato incluem silício, alumínio, zinco, magnésio, cálcio, bário, titânio,zircônio, manganês, ferro, cério, níquel e estanho. Em particular, é preferidousar uma solução coloidal de oxido ou uma solução coloidal de hidróxido, eespecialmente uma solução coloidal de oxido de silício é preferida. Quandouma solução coloidal de oxido de silício é usada, um pavio resultante contémsílica como partículas. Tal pavio é preferido porque ele é excelente em resis-tência a calor.Conventional colloidal solutions may be used as the aforementioned colloidal solution for the present invention. Examples of such colloidal solutions include metal colloidal solutions, colloidal oxide solutions, hydroxide colloidal solutions, carbonate colloidal solutions and colloidal sulfate solutions. Examples of metal elements contained in colloidal metal solutions include gold, palladium, platinum, and silver. Examples of elements contained in colloidal oxide solutions, hydroxide colloidal solutions, colloidal carbonate solutions, and colloidal sulfate solutions include silicon, aluminum, zinc. , magnesium, calcium, barium, titanium, zirconium, manganese, iron, cerium, nickel and tin. In particular, a colloidal oxide solution or a colloidal hydroxide solution is preferred, and especially a colloidal silicon oxide solution is preferred. When a colloidal silicon oxide solution is used, a resulting wick contains silica as particles. Such a wick is preferred because it is excellent in heat resistance.
O pavio da presente invenção tem estabilidade de formato sufi-ciente porque ele contém partículas e um corpo estrutural fibroso e pelo me-nos parte das partículas está presente na forma de um agregado ligado aocorpo estrutural fibroso. Deste modo, o pavio exibe habilidade de absorçãode líquido estável. Particularmente quando papel é usado como o corpo es-trutural fibroso, o pavio exibe excelente estabilidade de formato em líquidoaquoso. Deste modo, mesmo se o pavio for induzido a absorver e então va-porizar uma solução química aquosa, o formato do pavio é mantido e absor-ção e vaporização de líquido estáveis e rápidas podem ser realizadas.The wick of the present invention has sufficient shape stability because it contains particles and a fibrous structural body and at least part of the particles is present in the form of an aggregate attached to the fibrous structural body. In this way the wick exhibits stable liquid absorption ability. Particularly when paper is used as the fibrous structural body, the wick exhibits excellent aqueous liquid shape stability. Thus, even if the wick is induced to absorb and then vaporize an aqueous chemical solution, the shape of the wick is maintained and rapid and stable liquid absorption and vaporization can be accomplished.
Na presente invenção, o formato do pavio é determinado de a-cordo com o formato do corpo estrutural fibroso. Por exemplo, um pavio emum formato colunar tal como um formato cilíndrico pode ser obtido usandoum corpo estrutural fibroso que foi formado em um formato colunar. Um pa-vio em uma forma tipo placa ou uma forma tipo folha pode ser obtido usandoum corpo estrutural fibroso tendo sido formado em uma forma tipo placa ouuma forma tipo folha. Tal configuração que o corpo estrutural fibroso se es-tende em uma direção onde o corpo estrutural fibroso absorve o líquido épreferida porque o líquido pode fluir bem. Por exemplo, quando um corpoestrutural fibroso cilíndrico é formado, uma folha de papel pode ser moldadaem uma forma cilíndrica enrolando-a espiralmente a partir de um lado dela.Neste momento, a direção onde o papel se estende combina com a direçãolongitudinal do cilindro e então a sucção acontece rapidamente.In the present invention, the shape of the wick is determined according to the shape of the fibrous structural body. For example, a wick in a columnar shape such as a cylindrical shape can be obtained using a fibrous structural body that has been formed into a columnar shape. A paver in a plate-like or sheet-like shape can be obtained using a fibrous structural body having been formed into a plate-like or sheet-like shape. Such a configuration that the fibrous structural body extends in a direction where the fibrous structural body absorbs the liquid is preferred because the liquid can flow well. For example, when a cylindrical fibrous structural body is formed, a sheet of paper may be shaped into a cylindrical shape by spiraling it from one side of it. At this time, the direction in which the paper extends matches the longitudinal direction of the cylinder and then Suction happens quickly.
O pavio da presente invenção pode ser produzido sem usar ade-sivos, tal como verniz. Além disso, uma vez que o tipo, o diâmetro de partícu-la, etc das partículas a serem usadas podem ser mudados, a habilidade deliberação de vapor de um pavio pode ser mudada através da mudança dessesfatores e, como resultado, vaporização pode ser controlada facilmente.[Método para produção de um corpo estrutural]The wick of the present invention can be produced without using adhesives such as varnish. In addition, since the type, particle diameter, etc. of the particles to be used can be changed, the vapor deliberation ability of a wick can be changed by changing these factors and, as a result, vaporization can be controlled. easily. [Method for producing a structural body]
Através do uso do método da invenção para produção de um cor-po estrutural, um corpo estrutural a ser usado como um pavio pode ser produ-zido. Nesta modalidade exemplar, um método da presente invenção para pro-dução de um corpo estrutural é descrito tomando um método para produçãode um pavio como um exemplo. O método da presente invenção para produ-ção de um pavio é caracterizado por compreender: uma etapa de absorção detrazer pelo menos parte de um corpo estrutural fibroso em contato com umlíquido de dispersão onde partículas são dispersas em um meio líquido, destemodo fazendo com que o corpo estrutural fibroso absorva o líquido, e umaetapa de remoção de remoção do meio líquido do corpo estrutural fibroso queabsorveu o líquido de dispersão. Um pavio pode ser produzido, por exemplo,trazendo um corpo estrutural fibroso feito de fibras em contato com um líquidode dispersão onde partículas são dispersas em um meio líquido para fazer ocorpo estrutural absorver o líquido de dispersão, deste modo enchendo o lí-quido de dispersão em um corpo estrutural fibroso, e simultaneamente remo-vendo o meio líquido dó líquido de dispersão absorvido. Através de tais pro-cedimentos, pelo menos parte das partículas é capturada e ligada às fibras docorpo estrutural fibroso e, como resultado, as partículas podem ser cheias nocorpo estrutural fibroso em uma alta densidade.By using the method of the invention for producing a structural body, a structural body to be used as a wick can be produced. In this exemplary embodiment, a method of the present invention for producing a structural body is described by taking a method for producing a wick as an example. The method of the present invention for producing a wick is characterized by: an absorption step causing at least part of a fibrous structural body in contact with a dispersing liquid where particles are dispersed in a liquid medium, thus causing the fibrous structural body absorbs the liquid, and a liquid medium removal removal step from the fibrous structural body that has absorbed the dispersing liquid. A wick may be produced, for example, by bringing a fibrous structural body made of fibers into contact with a dispersing liquid where particles are dispersed in a liquid medium to make the structural body absorb the dispersing liquid, thereby filling the dispersing liquid. in a fibrous structural body, and simultaneously removing the liquid medium from the absorbed dispersing liquid. Through such procedures, at least part of the particles are captured and bound to the fibrous structural body fibers and as a result, the particles may be filled to the fibrous structural body at a high density.
Aqui, é suficiente para o líquido de dispersão onde estão disper-sas partículas em um meio líquido ser um líquido de dispersão onde partícu-las estão dispersas no meio líquido sem sedimentar. A fim de dispersar par-tículas para um grau maior, um tensoativo, um emulsificante ou similar podeser adicionado ao líquido de dispersão. Embora o meio líquido onde partícu-las são dispersas não seja particularmente restrito, água é preferida a partirdo ponto de vista da simplificação de instalação de produção, a carga doambiente, etc. Embora a concentração de partículas em um líquido de dis-persão não seja particularmente limitada, ela é geralmente 1 a 50% em pe-so. A fim de encher e agregar partículas rapidamente em uma alta densida-de, uma concentração maior é preferida e uma concentração de 20 a 50%em peso é preferida.Here, it is sufficient for the dispersing liquid where the particles are dispersed in a liquid medium to be a dispersing liquid where particles are dispersed in the unsettled liquid medium. In order to disperse particles to a greater degree, a surfactant, an emulsifier or the like may be added to the dispersing liquid. Although the liquid medium in which the particles are dispersed is not particularly restricted, water is preferred from the standpoint of production facility simplification, environmental loading, etc. Although the concentration of particles in a dispersion liquid is not particularly limited, it is generally 1 to 50% by weight. In order to quickly fill and aggregate particles at a high density, a higher concentration is preferred and a concentration of 20 to 50% by weight is preferred.
O método para trazer um corpo estrutural fibroso em contatocom um líquido de dispersão pode ser, por exemplo, um método onde pelomenos parte do corpo estrutural fibroso é posta no líquido de dispersão ouum método onde o líquido de dispersão é aplicado ao corpo estrutural fibro-so. Quando um corpo estrutural fibroso é posto em um líquido de dispersão,o corpo estrutural fibroso pode ser imerso totalmente no líquido de disper-são. Alternativamente, o corpo estrutural fibroso pode ser posto parcialmenteno líquido de dispersão, de modo que o líquido de dispersão seja espalhadosobre o corpo estrutural fibroso através de ação capilar.The method for bringing a fibrous structural body into contact with a dispersing liquid may be, for example, a method wherein at least part of the fibrous structural body is placed in the dispersing liquid or a method where the dispersing liquid is applied to the fibrous structural body. . When a fibrous structural body is placed in a dispersing liquid, the fibrous structural body may be totally immersed in the dispersing liquid. Alternatively, the fibrous structural body may be partially disposed in the dispersing liquid such that the dispersing liquid is spread over the fibrous structural body by capillary action.
Se um corpo estrutural fibroso for imerso apenas parcialmenteem um líquido de dispersão, então irá absorver o líquido de dispersão, isto évantajoso porque apenas uma quantidade necessária de líquido é absorvidae então o líquido de dispersão não é desperdiçado. Além disso, a concentra-ção de partículas no corpo estrutural fibroso pode ser aumentada continuan-do a imersão no líquido de dispersão enquanto removendo o solvente ourepetindo a remoção do meio líquido e o contato com o líquido de dispersão.Particularmente, é desejável repetir a etapa de absorção e a etapa de remo-ção até que uma quantidade desejada de partículas esteja contida e um a-gregado desejado seja formado. Neste momento, a etapa de absorção e aetapa de remoção podem ser repetidas até que a proporção das partículasque foram ligadas ao corpo estrutural fibroso fique em 10 a 95% em peso,contanto que o peso do pavio seja 100% em peso. Quando um corpo estru-tural fibroso colunar é usado, absorção de líquido pode ser realizada mergu-lhando uma extremidade longitudinal do corpo estrutural fibroso em um líqui-do de dispersão. Quando um líquido de dispersão é pulverizado com umpulverizador ou similar ou é aplicado com uma escova ou similar a um corpoestrutural fibroso, é desejável fazer com que o líquido de dispersão banhecompletamente o corpo estrutural fibroso.If a fibrous structural body is only partially immersed in a dispersing liquid, then it will absorb the dispersing liquid, this is advantageous because only a necessary amount of liquid is absorbed and so the dispersing liquid is not wasted. In addition, the concentration of particles in the fibrous structural body may be increased by continuing immersion in the dispersing liquid while removing the solvent or repeating the removal of the liquid medium and contact with the dispersing liquid. In particular, it is desirable to repeat the the absorption step and the removal step until a desired amount of particles is contained and a desired Î ± -glue is formed. At this time, the absorption step and the removal step can be repeated until the proportion of particles that have been bonded to the fibrous structural body is 10 to 95 wt%, provided the wick weight is 100 wt%. When a columnar fibrous structural body is used, fluid absorption may be accomplished by dipping a longitudinal end of the fibrous structural body into a dispersing liquid. When a dispersing liquid is sprayed with a spray or the like or applied with a brush or similar to a fibrous structural body, it is desirable to cause the dispersion liquid to completely bath the fibrous structural body.
O método para remoção de um meio líquido a partir de um corpoestrutural fibroso cheio com um líquido de dispersão pode ser, por exemplo,secagem do corpo estrutural fibroso tendo sido feito absorver o líquido dedispersão naturalmente em temperatura ambiente ou através de facilitaçãoda vaporização do meio líquido compulsoriamente através de aquecimentocom um secador. Ao remover o meio líquido, apenas partículas aderem-seàs fibras e as partículas se agregam para endurecerem, de modo que rigideze resistência a líquido que são adequadas como um pavio são dadas aocorpo estrutural fibroso. Neste momento, a proporção das partículas ligadasao corpo estrutural fibroso é de preferência 10 a 95% em peso, e com maispreferência 50 a 90% em peso, contanto que o peso do pavio seja 100%. Ocorpo estrutural fibroso e o líquido de dispersão onde partículas são disper-sas podem, de acordo com a necessidade, conter corantes, pigmentos, anti-oxidantes, absorvedores de UV, conservantes, etc.The method for removing a liquid medium from a fibrous structural body filled with a dispersing liquid may be, for example, drying the fibrous structural body having been made to absorb the naturally dispersing liquid at room temperature or by facilitating vaporization of the liquid medium. compulsorily through heating with a dryer. By removing the liquid medium, only particles adhere to the fibers and the particles aggregate to harden, so that rigid liquid resistance that is suitable as a wick is given to the fibrous structural body. At this time, the proportion of the particles bound to the fibrous structural body is preferably 10 to 95 wt%, and more preferably 50 to 90 wt%, provided that the wick weight is 100%. Fibrous structural body and dispersing liquid where particles are dispersed may, as required, contain dyes, pigments, antioxidants, UV absorbers, preservatives, etc.
No pavio produzido através do método da presente invençãopara produção de um pavio, pelo menos parte das partículas é ligada aocorpo estrutural fibroso e está presente na forma de um agregado e as partí-culas foram enchidas no corpo estrutural fibroso em uma densidade alta.Então, o pavio tem estabilidade de formato suficientemente alta. Deste mo-do, um líquido pode ser absorvido e vaporizado estavelmente e rapidamente.[Dispositivo de liberação de vapor e método de liberação de vapor]In the wick produced by the method of the present invention for the production of a wick, at least part of the particles is bound to the fibrous structural body and is present in the form of an aggregate and the particles were filled into the fibrous structural body at a high density. the wick has sufficiently high format stability. In this way a liquid can be absorbed and vaporized stably and rapidly. [Steam Release Device and Steam Release Method]
O dispositivo de liberação de vapor da presente invenção é ca-racterizado por ter um reservatório contendo um líquido vaporizável e umpavio feito do corpo estrutural da presente invenção, o pavio estando locali-zado de tal maneira que uma parte do pavio é imersa dentro do líquido vapo-rizável e outra parte do pavio é exposta para o exterior do reservatório. Odispositivo de liberação de vapor da presente invenção pode ser usado, porexemplo, como um dispositivo inseticida usando um líquido inseticida con-tendo um componente inseticida como o líquido vaporizável. Nesta modali-dade exemplar, uma explicação é feita provendo, como um exemplo, umcaso onde o corpo estrutural da presente invenção é usado como um pavio eo dispositivo de liberação de vapor da presente invenção é usado como umdispositivo inseticida. O dispositivo inseticida da presente invenção pode serum dispositivo inseticida de liberação de vapor quente do tipo absorção delíquido tendo ainda um aquecedor (dispositivo de aquecimento) para aque-cer uma porção do pavio, a porção estando fora do líquido inseticida.The vapor release device of the present invention is characterized by having a reservoir containing a vaporizable liquid and a wick made of the structural body of the present invention, the wick being located such that a part of the wick is immersed within the liquid. vapable and another part of the wick is exposed to the outside of the reservoir. The vapor release device of the present invention may be used, for example, as an insecticide device using an insecticide liquid containing an insecticide component such as vaporizable liquid. In this exemplary embodiment, an explanation is made by providing, as an example, a case where the structural body of the present invention is used as a wick and the vapor delivery device of the present invention is used as an insecticide device. The insecticidal device of the present invention may be deliquid absorption type hot vapor release insecticidal device further having a heater (heating device) for heating a portion of the wick, the portion being outside the insecticide liquid.
Uma modalidade exemplar de um dispositivo inseticida de libe-ração de vapor quente do tipo absorção de líquido compreendendo um pavioda presente invenção é descrita abaixo com referência à figura 1. A figura 1é uma vista em seção esquemática ilustrando um dispositivo inseticida deliberação de vapor quente do tipo absorção de líquido 5 da presente inven-ção. Conforme ilustrado na figura 1, o dispositivo inseticida de liberação devapor quente do tipo absorção de líquido 5 tem um pavio cilíndrico 1, umaquecedor 2 de formato em anel para aquecimento do pavio 1, um apoio deaquecedor 3 que apoia o aquecedor 2 e um reservatório 4 que é enchidocom um líquido inseticida.An exemplary embodiment of a liquid-absorption type hot vapor release insecticidal device comprising a wicket of the present invention is described below with reference to Figure 1. Figure 1 is a schematic sectional view illustrating a hot vapor deliberation insecticide device of the invention. liquid absorption type 5 of the present invention. As shown in FIG. 1, the liquid-absorbent hot-vapor-release insecticidal device 5 has a cylindrical wick 1, a ring-shaped heater 2 for heating wick 1, a heater holder 3 supporting heater 2 and a reservoir 4 which is filled with an insecticide liquid.
O pavio 1 foi inserido em um reservatório 4 com uma extremida-de longitudinal do mesmo projetada a partir do reservatório e com a outraextremidade imersa na solução inseticida. O aquecedor 2 aquece indireta-mente a ponta do pavio 1 se projetando do reservatório 4. O aquecedor 2não é particularmente restrito contanto que ele seja um corpo exotermicoque possa aquecer o corpo estrutural fibroso indiretamente em cerca de 60 a150°C, e ele é tipicamente um aquecedor elétrico de formato em anel normalque gera calor através da aplicação de corrente elétrica. Neste caso, ao a-quecedor 2 é conectada uma corda (não-mostrada) para aplicação de cor-rente elétrica para fazer com que o aquecedor gere calor.Wick 1 was inserted into a reservoir 4 with a longitudinal end thereof projected from the reservoir and with the other end immersed in the insecticide solution. Heater 2 indirectly heats the tip of wick 1 protruding from reservoir 4. Heater 2 is not particularly restricted as long as it is an exothermic body that can indirectly heat the fibrous structural body to about 60 to 150 ° C, and is typically a normal ring-shaped electric heater that generates heat by applying electric current. In this case, heater 2 is connected with a rope (not shown) for applying electric current to cause the heater to generate heat.
A distância entre o aquecedor 2 e o pavio está geralmente den-tro da faixa de 0,5 mm a 2 mm e é desejável que, em um aspecto de segu-rança, a temperatura de aquecimento do aquecedor 2 seja 150°C ou menos.The distance between heater 2 and the wick is generally within the range of 0.5 mm to 2 mm and it is desirable that, in a safety aspect, the heating temperature of heater 2 is 150 ° C or less. .
O pavio é geralmente ajustado de modo que sua parte inferior inserida noreservatório 4 possa estar localizada 0 mm a cerca de 2 mm do fundo inter-no do reservatório 4. A fim de absorver o líquido inseticida no reservatório 4sem nenhum desperdício e usá-lo até em cima, é desejável localizar a ex-tremidade inferior próximo ao fundo do reservatório o máximo possível.The wick is generally adjusted so that its bottom inserted into the reservoir 4 can be located 0 mm to about 2 mm from the inner bottom of the reservoir 4. In order to absorb the insecticidal liquid in the reservoir 4 without any waste and use it until above, it is desirable to locate the lower end near the bottom of the reservoir as much as possible.
Embora o material formando o reservatório 4 não seja particu-larmente restrito contanto que ele seja um material através do qual uma so-lução química não vaze ou escape mesmo após passado um longo períodode tempo, materiais transparentes através dos quais a quantidade residualde um líquido químico restante no reservatório pode ser checada a partir doexterior, tal como vidro e plásticos, são preferidos. Além disso, materiaistendo uma propriedade de proteção contra UV são preferidos para o propósi-to de prevenir agentes químicos de fotodecomposição. O dispositivo insetici-da de liberação de vapor quente do tipo absorção de líquido pode ser equi-pado com uma lâmpada-piloto que indica se uma corrente elétrica está sen-do aplicada ou não.Although the material forming the reservoir 4 is not particularly restricted as long as it is a material through which a chemical solution does not leak or escape even after a long period of time, transparent materials through which the residual amount of a chemical liquid The remainder in the reservoir can be checked from the outside, such as glass and plastics, are preferred. In addition, materials having a UV protection property are preferred for the purpose of preventing photodecomposition chemical agents. The insecticidal liquid-absorbing hot vapor release device may be fitted with a pilot lamp indicating whether or not an electric current is being applied.
Na presente invenção, vários inseticidas convencionalmente co-nhecidos podem ser usados como um componente inseticida a ser contidoem uma solução inseticida e exemplos dos mesmos incluem inseticidas pire-troides, inseticidas carbamato e inseticidas organofosforosos. Inseticidaspiretroides são usados adequadamente porque eles são geralmente de se-gurança alta, e exemplos dos mesmos incluem aletrina, bioaletrina, praletri-na, metoflutrina, proflutrina, transflutrina, ftaltrina, etofenprox, resmetrin, fu-rametrin, permetrin, fenotrin, fenvalerato, esfenvalerato, cipermetrina, cifeno-trina, fempropatrina, fenflutrina, empentrina, teraletrina, d-tetrametrina, cife-notrina, tralometrina e deltametrina.In the present invention, various conventionally known insecticides may be used as an insecticide component to be contained in an insecticide solution and examples thereof include pyrethroid insecticides, carbamate insecticides and organophosphorous insecticides. Insecticidespyrethroids are suitably used because they are generally of high safety, and examples thereof include allethrin, bioalethrin, pralethrin, metofluthrin, profluthrin, transfluthrin, phthaltrin, etmophenprox, fu-rametrin, permethrin, fenotrin, fenvalerate, esfenerate, , cypermethrin, cyphenetrine, fenpropathrin, fenfluthrin, empentrin, teralethrin, d-tetramethrin, cife-notrin, tralometrin and deltamethrin.
Exemplos de inseticidas carbamato incluem fenobucarb (BPMC),metoxadiazona, alanicarb, oxamila, carbosulfano, benfuracarb, metomila,carbarila (NAC), tiodicarb e etiofencarb. Exemplos de inseticidas organofos-forosos incluem fenitrotiona, acefato, diazinona e malationa.Examples of carbamate insecticides include fenobucarb (BPMC), methoxyadiazone, alanicarb, oxamyl, carbosulfan, benfuracarb, methomyl, carbaryl (NAC), thiodicarb and ethiofencarb. Examples of organophosphorous insecticides include fenitrothione, acefate, diazinone and malationa.
Além disso, o líquido inseticida pode conter um sinergista queaumenta a ação desses inseticidas, por exemplo, butóxido de piperonila. N-octilbiciclo-heptenodicarboxamida, N-(2-etil-hexil)-1-isopropil-4-metilbiciclo[2,2,2]oct-5-eno-2,3-dicarboximida e éter octaclorodipropílico. Oteor do sinergista é de preferência 0,1 a 10 vezes com base no teor do com-ponente inseticida.In addition, insecticidal liquid may contain a synergist that increases the action of these insecticides, for example piperonyl butoxide. N-octylbicycloheptenedicarboxamide, N- (2-ethylhexyl) -1-isopropyl-4-methylbicyclo [2,2,2] oct-5-ene-2,3-dicarboximide and octachlorodipropyl ether. The synergist's content is preferably 0.1 to 10 times based on the content of the insecticide component.
A concentração de um componente inseticida em um líquido in-seticida é dé preferência a partir de 0,3% em peso a 20% em peso e é commais preferência uma concentração dentro da faixa a partir de 0,3% em pesoa 5% em peso. Esses componentes inseticidas podem ser usados sozinhosou alternativamente podem ser usados em combinação. Auxiliares, tal comoestabilizadores, desodorantes e corantes, podem, se necessário, ser adicio-nados ao líquido inseticida em uma quantidade pequena. Por outro lado, emuso para o propósito de aromatização, um líquido que contém um ou maisperfumes naturais ou artificiais pode ser usado como o líquido no qual o pa-vio deve ser imerso. Ainda, vários agentes, tal como desodorantes, germici-das e repelentes, podem ser usados também para cada propósito. Essescomponentes podem ser também usados na forma de solução após seremdissolvidos em um solvente orgânico ou um líquido misturado de um solven-te orgânico e água.The concentration of an insecticide component in an insecticide liquid is preferably from 0.3 wt% to 20 wt% and more preferably a concentration within the range from 0.3 wt% to 5 wt%. Weight. These insecticidal components may be used alone or alternatively may be used in combination. Auxiliaries, such as stabilizers, deodorants and dyes, may, if necessary, be added to the insecticide liquid in a small amount. On the other hand, for the purpose of flavoring, a liquid containing one or more natural or artificial perfumes may be used as the liquid into which the powder is to be immersed. In addition, various agents, such as deodorants, germicides and repellents, may also be used for each purpose. These components may also be used in solution form after being dissolved in an organic solvent or a mixed liquid of an organic solvent and water.
No dispositivo inseticida da presente invenção, o líquido insetici-da pode ser uma solução obtida através de dissolução de um componenteinseticida em um solvente orgânico ou um líquido aquoso misturado de umsolvente orgânico e água. Apesar do solvente no líquido inseticida não serparticularmente restrito, exemplos do mesmo incluem líquidos oleaginososcompostos apenas de solventes e líquidos aquosos compostos de solventese água. Solventes a serem usados para líquido oleaginoso geralmente inclu-em solventes orgânicos, e de preferência incluem solventes de hidrocarbonosaturado (isto é, solventes de hidrocarbono saturado alifático e solventes dehidrocarbono saturado alicíclico) e com mais preferência incluem um ou doisou mais membros selecionados de solventes de hidrocarbono saturado ten-do um ponto de ebulição de 180°C a 310°C. Exemplos específicos de taissolventes de hidrocarbono saturado incluem Solvente H No. 0 (produzidopela Nippon Oil Corporation), Solvente M No. 0 (produzido pela Nippon OilCorporation), Solvente L No. 0 (produzido pela Nippon Oil Corporation), Pa-rafina Normal (produzida pela Nippon Oil Corporation), Solvente IP 2028(produzido pela Idemitsu Kosan Co., Ltd.), Norpar 12 (produzido pela Ex-xonMobil Chemical), Norpar 13 (produzido pela ExxonMobil Chemical), Nor-par 15 (produzido pela ExxonMobil Chemical), Isopar M (produzido pela Ex-xonMobil Chemical), Isopar L (produzido pela ExxonMobil Chemical), IsoparV (produzido pela ExxonMobil Chemical), Exxol D80 (produzido pela Exxon-Mobil Chemical), Exxol D110 (produzido pela ExxonMobil Chemical) e ExxolD130 (produzido pela ExxonMobil Chemical).In the insecticidal device of the present invention, the insecticidal liquid may be a solution obtained by dissolving an insecticidal component in an organic solvent or an aqueous liquid mixed with an organic solvent and water. Although the solvent in the insecticide liquid is not particularly restricted, examples thereof include oleaginous liquids composed only of solvents and aqueous liquids composed of solvents and water. Solvents to be used for oleaginous liquid generally include organic solvents, and preferably include hydrocarbon-saturated solvents (i.e. aliphatic saturated hydrocarbon solvents and alicyclic saturated hydrocarbon solvents) and more preferably include one or two or more selected members of hydrocarbon solvents. saturated hydrocarbon having a boiling point of 180 ° C to 310 ° C. Specific examples of such saturated hydrocarbon solvents include Solvent H No. 0 (produced by Nippon Oil Corporation), Solvent M No. 0 (produced by Nippon Oil Corporation), Solvent L No. 0 (produced by Nippon Oil Corporation), Paraphrin Normal ( Nippon Oil Corporation), Solvent IP 2028 (produced by Idemitsu Kosan Co., Ltd.), Norpar 12 (produced by Ex-xonMobil Chemical), Norpar 13 (produced by ExxonMobil Chemical), Nor-par 15 (produced by ExxonMobil Chemical), Isopar M (Produced by Ex-xonMobil Chemical), Isopar L (Produced by ExxonMobil Chemical), IsoparV (Produced by ExxonMobil Chemical), Exxol D80 (Produced by Exxon-Mobil Chemical), Exxol D110 (Produced by ExxonMobil Chemical) and ExxolD130 (produced by ExxonMobil Chemical).
A fim de controlar a vaporização de um líquido inseticida, umsolvente de ebulição alta tendo um ponto de ebulição de 300°C ou maior,por exemplo, pode ser adicionado ao líquido inseticida. Exemplos específi-cos dos mesmos incluem ésteres ou derivados do ácido graxo, tal como lau-rato de isopropila, ftalato de dibutila, sebacato de dibutila, citrato de acetiltributila e triglicerídeo de ácido graxo de cadeia média, alcoóis superiores talcomo octildodecanol e óleos e gorduras, tal como óleo de milho.In order to control the vaporization of an insecticidal liquid, a high boiling solvent having a boiling point of 300 ° C or higher, for example, may be added to the insecticidal liquid. Specific examples thereof include fatty acid esters or derivatives, such as isopropyl laurate, dibutyl phthalate, dibutyl sebacate, acetyltributyl citrate and medium chain fatty acid triglyceride, higher alcohols such as octyldodecanol and oils and fats. , such as corn oil.
Exemplos dos solventes a serem usados para os líquidos aquo-sos incluem um solvente obtido através da adição, à água, de um tensoativoque vaporiza a 100°C a 180°C, que é uma faixa de temperatura de aqueci-mento com um aquecedor conforme divulgado na JP 3-7207 A, e um líquidoobtido através da adição, à água, de um solvente orgânico hidrofílico quetem um peso molecular relativamente baixo e um ponto de ebulição dentroda faixa de 100°C a 300°C e que vaporiza no momento do aquecimento con-forme divulgado na JP 7-316002 A. Ao líquido misturado de tal solvente or-gânico hidrofílico e água podem ser adicionados compostos dióis hidrofílicos,composto álcool hidrofílico, etc, como um regulador de vaporização.Examples of solvents to be used for aqueous liquids include a solvent obtained by the addition to water of a surfactant which vaporizes at 100 ° C to 180 ° C, which is a temperature range of heating with a heater according to JP 3-7207 A, and a liquid obtained by the addition to water of a hydrophilic organic solvent having a relatively low molecular weight and a boiling point within the range of 100 ° C to 300 ° C and vaporizing at the time of heating as disclosed in JP 7-316002 A. To the mixed liquid of such hydrophilic organic solvent and water may be added hydrophilic diol compounds, hydrophilic alcohol compound, etc., as a spray regulator.
O dispositivo inseticida da presente invenção tem um pavio dapresente invenção. Então, se o pavio tiver que absorver um líquido inseticida eo líquido absorvido for então aquecido para ser liberado na forma de vapor apartir da superfície do pavio, o formato do pavio é mantido e o dispositivo po-de realizar absorção e vaporização do líquido estavelmente e rapidamente.The insecticidal device of the present invention has a wick of the present invention. Then, if the wick has to absorb an insecticidal liquid and the absorbed liquid is then heated to be released as a vapor from the wick surface, the wick shape is maintained and the device can steadily absorb and vaporize the liquid. quickly.
O método de liberação de vapor da presente invenção pode serrealizado, por exemplo, como um método inseticida usando um líquido inse-ticida. Nesta modalidade exemplar, um método de liberação de vapor dapresente invenção é descrito tomando um método inseticida como um e-xemplo. No método inseticida da presente invenção, um pavio da presenteinvenção é imerso parcialmente dentro de um líquido inseticida contendo umcomponente inseticida, de modo que o pavio absorva o líquido, e então opavio libere o líquido absorvido na forma de vapor a partir da sua superfície.É desejável, a partir do ponto de vista de eficiência de vaporização, aquecero pavio que absorve o líquido inseticida. Em uma modalidade exemplar, umpavio é imerso parcialmente dentro de um líquido inseticida e uma porçãoimersa do pavio é aquecida parcialmente. O método inseticida da presenteinvenção pode ser realizado também usando o método inseticida acimamencionado da presente invenção. Uma vez que o método inseticida da pre-sente invenção usa um pavio da presente invenção, um efeito inseticida édesenvolvido rapidamente e o efeito inseticida pode durar estavelmente.The vapor release method of the present invention may be performed, for example, as an insecticide method using an insecticide liquid. In this exemplary embodiment, a steam release method of the present invention is described by taking an insecticide method as an example. In the insecticidal method of the present invention, a wick of the present invention is partially immersed in an insecticidal liquid containing an insecticide component, so that the wick absorbs the liquid, and then the vapor releases the vapor-absorbed liquid from its surface. From a vaporization efficiency point of view, it is desirable to heat the wick which absorbs the insecticidal liquid. In an exemplary embodiment, a wick is partially immersed in an insecticidal liquid and an immersed portion of the wick is partially heated. The insecticide method of the present invention may also be carried out using the above-mentioned insecticide method of the present invention. Since the insecticidal method of the present invention uses a wick of the present invention, an insecticidal effect is rapidly developed and the insecticidal effect may last stably.
[Kit para liberação de vapor][Steam Release Kit]
Um kit para liberação de vapor da presente invenção pode serusado, por exemplo, como um kit para aplicações inseticidas. Nesta modali-dade exemplar, um kit para liberação de vapor da presente invenção é descri-to tomando um kit para aplicações inseticidas como um exemplo. O kit paraaplicações inseticidas é caracterizado por compreender um corpo estruturalda presente invenção a ser usado como um pavio. O kit para aplicações inse-ticidas tem de preferência um líquido inseticida contendo um componente in-seticida. O componente inseticida pode ser um selecionado daqueles providosacima como exemplos do componente inseticida a ser contido no dispositivoinseticida acima mencionado. O kit para aplicações inseticidas da presenteinvenção tem pelo menos um pavio da presente invenção. Isto torna possívelmelhorar a estabilidade do formato de um pavio em líquido enquanto manten-do a habilidade de absorção de líquido do pavio. Como resultado, absorção evaporização estáveis e rápidas de líquido podem ser conseguidas.A steam release kit of the present invention may be used, for example, as a kit for insecticide applications. In this exemplary embodiment, a steam release kit of the present invention is described by taking a kit for insecticide applications as an example. The insecticide application kit is characterized in that it comprises a structural body of the present invention to be used as a wick. The insecticide application kit preferably has an insecticide liquid containing an insecticide component. The insecticidal component may be one selected from those provided above as examples of the insecticidal component to be contained in the above-mentioned insecticidal device. The insecticide application kit of the present invention has at least one wick of the present invention. This makes it possible to improve the stability of the shape of a liquid wick while maintaining the liquid's absorption ability of the wick. As a result, stable and rapid evaporation absorption of liquid can be achieved.
A presente invenção será descrita em mais detalhes abaixo comreferência aos Exemplos, mas a invenção não é limitada aos Exemplos.The present invention will be described in more detail below with reference to the Examples, but the invention is not limited to the Examples.
[Exemplos][Examples]
[1. Preparação de pavio][1. Wick Preparation]
Um pedaço de KIMWIPES (marca registrada" "WIPER S-200"(100% de polpa, 215 mm x 120 mm de tamanho, produzido pela NIPPONPAPER CRECIA Co., Ltd.) foi dobrado na metade em seus lados mais lon-gos e então foi enrolado firmemente a partir de uma borda dele para um for-mato colunar. Este foi cortado em um comprimento de 73 mm em conformi-dade com a altura do dispositivo de aquecimento. Então, material de base Afoi preparado. O material de base pesava 0,6 g. Ainda, uma película PET foienvolvida em torno do material de base A de modo que a película podia co-brir o material de base, e a extremidade enrolada foi fixada com uma fita a-desiva. Em um tubo de vidro de 50 cm3 foram postos 10 cm3 de líquido desílica coloidal ("SNOWTEX 20" produzido pela Nissan Chemical Industries,Ltd.) tendo um diâmetro de partícula médio de 20 nm e uma concentraçãode sólido de 20% em peso. O material de base A foi deixado com sua extre-midade inferior (1 cm de comprimento) imersa no líquido de sílica coloidal.Trinta minutos mais tarde, o material de base A foi tirado do líquido de sílicacoloidal e foi mantido horizontalmente da noite para o dia. Então, a películaPET foi removida e o material de base foi deixado descansar até que elesecasse completamente. O material então obtido é deixado ser o pavio A. Opavio A pesava 1,2 g após secagem e a quantidade de partículas de sílicaligadas era 50% em peso.A piece of KIMWIPES ("WIPER S-200" trademark (100% pulp, 215 mm x 120 mm in size, produced by NIPPONPAPER CRECIA Co., Ltd.) was folded in half at its longest sides and then it was wrapped tightly from one edge of it to a columnar form. It was cut to a length of 73 mm in accordance with the height of the heating device. Then base material was prepared. It also weighed 0.6 g. Also, a PET film was wrapped around the base material A so that the film could cover the base material, and the coiled end was fixed with an aiding tape. 50 cm3 glass was placed 10 cm3 colloidal desyllic liquid ("SNOWTEX 20" produced by Nissan Chemical Industries, Ltd.) having an average particle diameter of 20 nm and a solid concentration of 20 wt%. was left with its lower end (1 cm long) immersed in the silica liquid with Thirty minutes later, A-base material was taken from the silica-colloidal liquid and kept horizontally overnight. Then, the PET film was removed and the base material was allowed to rest until it completely dried. The material then obtained is left to be wick A. Opavio A weighed 1.2 g after drying and the amount of bonded silica particles was 50% by weight.
Subseqüentemente, o pavio B foi preparado da mesma maneiraque na preparação do pavio A exceto que um material de base foi imerso emum líquido de sílica coloidal ("SNOWTEX ZL" produzido pela Nissan Chemi-cal Industries, Ltd.) tendo um diâmetro de partícula médio de 70 nm e umaconcentração de sólido de 40% em peso. O pavio B pesava 2,3 g após se-cagem e a quantidade de partículas de sílica ligadas era 74% em peso.Subsequently, wick B was prepared in the same manner as in preparation of wick A except that a base material was immersed in a colloidal silica liquid ("SNOWTEX ZL" produced by Nissan Chemi-cal Industries, Ltd.) having an average particle diameter. 70 nm and a solid concentration of 40% by weight. Wick B weighed 2.3 g after drying and the amount of bound silica particles was 74% by weight.
Os resultados de análise do pavio B são mostrados nas figuras 2 e3. A figura 2 é um diagrama mostrando os resultados de mapeamento de SÍO2através de um EPMA (Electron Probe Micro Analyzer) de uma seção transver-sal da porção superior (isto é, a extremidade que não foi imersa no líquido desílica coloidal) do pavio B. Na figura 2, uma imagem de elétron de difusão re-trógrada (BSE) é mostrada à esquerda e uma imagem de mapeamento Si damesma parte é mostrada à direita. Conforme mostrado na figura 2, muitas par-tículas de sílica agregam-se nas fibras do material de base do pavio B.Wick B analysis results are shown in figures 2 and 3. Figure 2 is a diagram showing the results of SiO 2 mapping through an Electron Probe Micro Analyzer (EPMA) of a cross-section of the upper portion (i.e., the end that was not immersed in fuse B). In Figure 2, a retrograde diffusion electron (BSE) image is shown on the left, and a Si mapping image is shown on the right. As shown in Figure 2, many silica particles aggregate into the fibers of wick B base material.
A figura 3 é um diagrama mostrando uma imagem de microscó-pio eletrônico do pavio B. Na figura 3, uma imagem obtida em uma tensãode aceleração de 10,0 kV e uma ampliação de x10,0 k é mostrada à esquer-da superior, uma imagem obtida em uma tensão de aceleração de 10,0 kV euma ampliação de x50,0 k é mostrada à direita superior, e uma imagem ob-tida em uma tensão de aceleração de 10,0 kV e uma ampliação de x100,0 ké mostrada à esquerda inferior. Conforme mostrado na figura 3, muitas par-tículas de sílica agregam-se e se ligam às fibras no material de base de mo-do que as fibras do material de base não podem ser observadas.Figure 3 is a diagram showing an electron microscope image of wick B. In Figure 3, an image obtained at an acceleration voltage of 10.0 kV and a magnification of x10.0 k is shown on the upper left, an image obtained at an acceleration voltage of 10.0 kV and a magnification of x50.0 k is shown at the upper right, and an image obtained at an acceleration voltage of 10.0 kV and an magnification of x100.0 ké shown at bottom left. As shown in Figure 3, many silica particles aggregate and bind to the fibers in the base material so that the fibers of the base material cannot be observed.
Subseqüentemente, o pavio C foi preparado da mesma maneiraque na preparação do pavio A exceto que um material de base foi imerso emum líquido de sílica coloidal ("SNOWTEX XS" produzido pela Nissan Chemi-cal Industries, Ltd.) tendo um diâmetro de partícula médio de 5 nm e umaconcentração de sólido de 20% em peso. O pavio C pesava 1,4 g após se-cagem e a quantidade de partículas de sílica ligadas era 57% em peso.Subsequently, wick C was prepared in the same manner as preparation of wick A except that a base material was immersed in a colloidal silica liquid ("SNOWTEX XS" produced by Nissan Chemi-cal Industries, Ltd.) having an average particle diameter. 5 nm and a solid concentration of 20% by weight. Wick C weighed 1.4 g after drying and the amount of bound silica particles was 57% by weight.
Os resultados de análise do pavio C são mostrados nas figuras 4a 6. A figura 4 é um diagrama mostrando os resultados de mapeamento deSi02 por um EPMA de uma seção transversal da porção superior (isto é, aextremidade que não foi imersa no líquido de sílica coloidal) do pavio C. Afigura 5 é um diagrama mostrando os resultados de mapeamento de Si02por um EPMA de uma seção transversal da porção inferior (isto é, a extremi-dade que foi imersa no líquido de sílica coloidal) do pavio C. Nas figuras 4 e5, uma imagem eletrônica de difusão retrógrada (BSE) é mostrada à esquer-da e uma imagem de mapeamento de Si da mesma parte é mostrada à direi-ta. Conforme mostrado nas figuras 4 e 5, muitas partículas de sílica agre-gam-se em ambas a porção superior e a porção inferior nas fibras do mate-rial de base do pavio C.The results of analysis of wick C are shown in Figures 4 to 6. Figure 4 is a diagram showing the results of mapping Si02 by an EPMA of a cross section of the upper portion (i.e., the end that was not immersed in colloidal silica liquid. Figure 5 is a diagram showing the results of Si02 mapping by an EPMA of a cross section of the lower portion (i.e. the end that was immersed in the colloidal silica liquid) of the wick. In Figures 4 e5, a retrograde diffusion electronic image (BSE) is shown on the left and a Si mapping image of the same part is shown on the right. As shown in Figures 4 and 5, many silica particles aggregate into both the upper portion and the lower portion in the fibers of wick C base material.
A figura 6 é um diagrama mostrando uma imagem de microscó-pio eletrônico do pavio C. Na figura 6, uma imagem obtida em uma tensãode aceleração de 10,0 kV e uma ampliação de x10,0 k é mostrada à esquer-da superior, uma imagem obtida em uma tensão de aceleração de 10,0 kV euma ampliação de x50,0 k é mostrada à direita superior e uma imagem obti-da em uma tensão de aceleração de 10,0 kV e uma ampliação de x100,0 k émostrada à esquerda inferior. Conforme mostrado na figura 6, tantas partícu-las de sílica agregam-se e se ligam às fibras do material de base que as fi-bras do material de base não podem ser observadas.Figure 6 is a diagram showing an electron microscope image of wick C. In Figure 6, an image obtained at an acceleration voltage of 10.0 kV and a magnification of x10.0 k is shown at the upper left, an image taken at an acceleration voltage of 10.0 kV and a magnification of x50.0 k is shown on the upper right and an image taken at an acceleration voltage of 10.0 kV and an magnification of x100.0 k is shown. bottom left. As shown in Figure 6, so many silica particles aggregate and bind to the fibers of the base material that the fibers of the base material cannot be observed.
Subseqüentemente, o pavio D foi preparado da mesma maneiraque na preparação do pavio A exceto que um material de base foi imerso emum líquido de sílica coloidal preparado misturando um líquido de sílica coloi-dal ("SNOWTEX 20" produzido pela Nissan Chemical Industries, Ltd.) tendoum diâmetro de partícula médio de 20 nm e um líquido de sílica coloidal("SNOWTEX SX" produzido pela Nissan Chemical Insdustries, Ltd.) tendoum diâmetro de partícula médio de 5 nm em uma razão de 1:1 para ajustar aconcentração de sólido a 20% em peso. O pavio D pesava 1,4 g após seca-gem e a quantidade de partículas de sílica ligadas era 57% em peso no total.Subsequently, wick D was prepared in the same manner as for wick A except that a base material was immersed in a colloidal silica liquid prepared by mixing a colloidal silica liquid ("SNOWTEX 20" produced by Nissan Chemical Industries, Ltd. ) tended to have an average particle diameter of 20 nm and a colloidal silica liquid ("SNOWTEX SX" produced by Nissan Chemical Insdustries, Ltd.) tended to have an average particle diameter of 5 nm at a ratio of 1: 1 to adjust the solid concentration to 20% by weight. Wick D weighed 1.4 g after drying and the amount of bound silica particles was 57% by weight in total.
O pavio E foi preparado da mesma maneira que na preparaçãodo pavio A exceto pelo uso de um filtro para cigarro (24 mm de perímetro,cortado em um comprimento de 70 mm, 0,4 g de peso) no lugar do materialde base A. O pavio E pesava 1,2 g após secagem e a quantidade de partícu-las de sílica ligadas era 67% em peso. Como um exemplo comparativo, umpavio de talco comercialmente disponível (7 mm de diâmetro e 73 mm decomprimento) foi usado como pavio F.Wick E was prepared in the same manner as in Wick A except that a cigarette filter (24 mm perimeter cut to a length of 70 mm, 0.4 g weight) was used in place of the base material A. Wick E weighed 1.2 g after drying and the amount of bound silica particles was 67% by weight. As a comparative example, a commercially available talcum powder (7 mm diameter and 73 mm length) was used as wick F.
[2. Preparação de um solvente para líquido inseticida]Um solvente oleaginoso foi preparado usando um solvente mis-turado (Norpar 13/Norpar 15 = 7peso/3peso) composto de Norpar 13 (produ-zido pela ExxonMobil Chemical Co., Ltd.) e Norpar 15 (produzido pela Ex-xonMobil Chemical Co., Ltd.), ambos sendo solventes de hidrocarbono satu-rado comercialmente disponíveis. Um solvente aquoso foi preparado usandoum solvente misturado (2-(2-butoxietóxi)etanol/água = 7 peso/3 peso) com-posto de 2-(2-butoxietóxi)etanol comercialmente disponível e água.[2. Preparation of a solvent for insecticide liquid] An oleaginous solvent was prepared using a mixed solvent (Norpar 13 / Norpar 15 = 7 weight / 3 weight) composed of Norpar 13 (produced by ExxonMobil Chemical Co., Ltd.) and Norpar 15 (produced by Ex-xonMobil Chemical Co., Ltd.), both of which are commercially available saturated hydrocarbon solvents. An aqueous solvent was prepared using a mixed solvent (2- (2-butoxyethoxy) ethanol / water = 7 weight / 3 weight) commercially available 2- (2-butoxyethoxy) ethanol compound and water.
[3. Dispositivo de liberação de vapor quente][3. Hot Steam Release Device]
Medição da taxa de vaporização de cada um dos pavios foi rea-lizada usando um dispositivo de liberação de vapor quente tal como aquelemostrado na figura 1. Aqui, o reservatório 4 usado estava comercialmentedisponível em uma forma cilíndrica de 55 mm de altura feito de plásticotransparente, tendo um diâmetro interno de fundo de 40 mm, uma altura pa-ra a curvatura da garrafa de 35 mm e um diâmetro interno de 16 mm. Comoo apoio de pavio (não-mostrado) para apoio do pavio foi usado um que foifeito de um material plástico macio de formato de tampa provido com umfuro que era de 7 mm de diâmetro em conformidade com o diâmetro externodo pavio 1 e que pode vedar a garrafa de solução química 4 de modo que olíquido químico com o qual a garrafa está cheia não vazaria ou escaparia.Measurement of the vaporization rate of each of the wicks was performed using a hot steam release device as shown in Figure 1. Here, the reservoir 4 used was commercially available in a 55 mm high cylindrical shape made of transparent plastic, having a bottom internal diameter of 40 mm, a height for the curvature of the bottle of 35 mm and an internal diameter of 16 mm. As the wick support (not shown) for wick support was used one which was made of a soft plastic lid-shaped material provided with a hole that was 7 mm in diameter in accordance with the outside diameter of wick 1 and which could seal the chemical solution bottle 4 so that the chemical liquid with which the bottle is full would not leak or escape.
Como um aquecedor em formato de anel 2 para aquecer indire-tamente a superfície superior do pavio 1 se projetando a partir do reservató-rio 4, um pedaço de metal de 15 mm de largura que tinha sido arredondadopara formar um anel tendo um diâmetro interno de 10 mm foi usado. Um a-poio de aquecedor 3 para apoiar o aquecedor 2 foi localizado em uma alturade 60 a 75 mm a partir da parte inferior do fundo do líquido químico, a saber,uma posição que correspondia à porção superior do pavio 1. O aquecedor 2foi ajustado para ter uma temperatura de cerca de 130°C através da aplica-ção de corrente elétrica.As a ring-shaped heater 2 for indirectly heating the upper surface of wick 1 protruding from the reservoir 4, a 15 mm wide piece of metal that had been rounded to form a ring having an internal diameter of 10 mm was used. A heater support 3 for supporting heater 2 was located at an altitude of 60 to 75 mm from the bottom of the chemical liquid bottom, namely a position corresponding to the upper portion of wick 1. Heater 2 was adjusted to have a temperature of about 130 ° C by applying electric current.
[4. Medição de taxa de vaporização][4. Vaporization Rate Measurement]
O reservatório 4 foi carregado com 30 g do solvente oleaginosopreparado através do procedimento descrito acima. Os pavios A a F foram,cada um, ajustados de modo que a sua extremidade poderia ser imersa nosolvente oleaginoso e entraria em contato com o fundo do reservatório 4.Então, o peso total foi medido. O reservatório 4 foi aquecido a cerca de130°C. Uma taxa de vaporização foi calculada pesando o reservatório 4 emcada momento que passou até que todo o solvente oleaginoso fosse exauri-do. Os resultados são mostrados na Tabela 7. Conforme mostrado na figura7, os pavios A-F, cada um, vaporizaram o solvente oleaginoso em uma taxaconstante até que o solvente na garrafa 4 tivesse sido exaurido.Reservoir 4 was charged with 30 g of the oleaginous solvent prepared by the procedure described above. Wicks A to F were each adjusted so that their end could be immersed in oilseed solvent and would contact the bottom of the reservoir 4. Then the total weight was measured. Reservoir 4 was heated to about 130 ° C. A vaporization rate was calculated by weighing the reservoir 4 at a time that passed until all the oil solvent was exhausted. The results are shown in Table 7. As shown in Figure 7, Wicks A-F each sprayed the oleaginous solvent on a constant until the solvent in bottle 4 had been exhausted.
Em seguida, usando um solvente aquoso ao invés do solventeoleaginoso, a medição da taxa de vaporização foi realizada da mesma ma-neira que acima para os pavios A e F. Os resultados foram mostrados naTabela 1. Conforme mostrado na figura 8, o pavio A vaporizou o solventeaquoso em uma taxa constante até que o solvente na garrafa 4 tivesse sidoexaurido como no caso de uso de um solvente oleaginoso. A taxa de vapori-zação do pavio F não pôde ser medida porque o pavio dissolveu imediata-mente após ser imerso no solvente aquoso.Then, using an aqueous solvent instead of the oil solvent, the vaporization rate measurement was performed in the same way as above for Wicks A and F. The results were shown in Table 1. As shown in Figure 8, Wick A the solvent was sprayed at a constant rate until the solvent in bottle 4 had been exhaled as in the case of using an oilseed solvent. The vaporization rate of wick F could not be measured because the wick dissolved immediately after being immersed in the aqueous solvent.
As taxas de vaporização médias dos respectivos pavios são da-das na Tabela 1.The average vaporization rates of the respective wick are given in Table 1.
Tabela 1Table 1
<table>table see original document page 23</column></row><table><table>table see original document page 24</column></row><table><table> table see original document page 23 </column> </row> <table> <table> table see original document page 24 </column> </row> <table>
Conforme mostrado na Tabela 1, os pavios A-E, que estão deAs shown in Table 1, Wicks A-E, which are in
acordo com a presente invenção, exibiram habilidade de liberação de vaporequivalente ao pavio F convencional. Ainda, enquanto o pavio F convencio-nal foi dissolvido em um solvente aquoso e então não foi possível ser usado,o pavio A da presente invenção exibiu habilidade de liberação de vapor es-tável e excelente mesmo quando o solvente aquoso foi usado.In accordance with the present invention, they exhibited the ability to release vapor equivalent to conventional F-wick. Further, while conventional wick F was dissolved in an aqueous solvent and thus could not be used, wick A of the present invention exhibited stable and excellent steam release ability even when the aqueous solvent was used.
Aplicabilidade IndustrialIndustrial Applicability
De acordo com a presente invenção, um corpo estrutural quepode absorver e vaporizar líquido estavelmente por um longo período detempo. O corpo estrutural pode, então, ser usado adequadamente para va-porizadores que absorvem e vaporizam várias soluções inseticidas, soluçõesaromatizantes, soluções desodorizantes e similar.According to the present invention, a structural body which can absorb and vaporize liquid stably for a long time. The structural body can then be suitably used for vaporizers that absorb and vaporize various insecticidal solutions, flavoring solutions, deodorizing solutions and the like.
Claims (26)