BR112013005163A2 - trilho de aço para ferrovias de alta velocidade e velocidade quase alta e método de fabricação do mesmo - Google Patents

trilho de aço para ferrovias de alta velocidade e velocidade quase alta e método de fabricação do mesmo

Info

Publication number
BR112013005163A2
BR112013005163A2 BR112013005163A BR112013005163A BR112013005163A2 BR 112013005163 A2 BR112013005163 A2 BR 112013005163A2 BR 112013005163 A BR112013005163 A BR 112013005163A BR 112013005163 A BR112013005163 A BR 112013005163A BR 112013005163 A2 BR112013005163 A2 BR 112013005163A2
Authority
BR
Brazil
Prior art keywords
steel rail
rail
speed
equal
weight
Prior art date
Application number
BR112013005163A
Other languages
English (en)
Other versions
BR112013005163B1 (pt
Inventor
Dadong Li
Dongsheng Mei
Hua Guo
Jianhua Liu
Li Tang
Ming Zou
Quan Xu
Yong Deng
Yun Zhao
Zhenyu Han
Original Assignee
Pangang Group Co Ltd
Pangang Group Panzhihua Steel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pangang Group Co Ltd, Pangang Group Panzhihua Steel filed Critical Pangang Group Co Ltd
Publication of BR112013005163A2 publication Critical patent/BR112013005163A2/pt
Publication of BR112013005163B1 publication Critical patent/BR112013005163B1/pt

Abstract

trilho de aço para ferrovias de alta velocidade e velocidade quase alta e método de fabricação do mesmo. a presente revela um trilho de arco para ferrovias em alta velocidade e velocidade quase elevada e a um método de fabricação do mesmo. o trilho de aço tendo uma propriedade superior de fadiga de contato de rolamento pode ser obtido por reduzir teor de carbono em combinação com resfriamento controlado após laminação. o trilho de aço inclui 0,40 - 0,64% em peso de c, 0,10 - 100% em peso de si, 0,30- 1,50% em peso de mn, menos do que ou igual a 0,025% em peso de p, menos do que ou igual a 0,25% em peso de s, menos do que ou igual a 0,005% em peso de a1, mais do que 0 e menos do que ou igual a 0,20% em peso de pelo menos um de v, cr e ti, e um restante de fe e impurezas inevitáveis. o trilho de aço fabricado de acordo com o método da presente invenção mantém a resistência e dureza do trilho de aço existente para as ferrovias de alta velocidade, enquanto aumenta à tenacidade, plasticidade e resistência a deformação, e um valor de energia exigido para iniciar e expandir micro-rachaduras formadas na superfície do trilho de aço devido à fadiga é aumentado, e desse modo sob as mesmas condições, a propriedade de fadiga de contato de rolamento do trilho de aço pode ser aperfeiçoada, desse modo finalmente melhorando o tempo de vida em serviço e a segurança de transporte do trilho de aço.
BR112013005163-9A 2010-09-02 2011-09-02 trilho de aço para ferrovias e método de fabricação do mesmo BR112013005163B1 (pt)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
CN201010270439.8 2010-09-02
CN2010102704398A CN101921950B (zh) 2010-09-02 2010-09-02 用于高速和准高速铁路的钢轨及其制造方法
PCT/CN2011/079278 WO2012028111A1 (zh) 2010-09-02 2011-09-02 用于高速和准高速铁路的钢轨及其制造方法

Publications (2)

Publication Number Publication Date
BR112013005163A2 true BR112013005163A2 (pt) 2016-04-26
BR112013005163B1 BR112013005163B1 (pt) 2018-10-23

Family

ID=43337161

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112013005163-9A BR112013005163B1 (pt) 2010-09-02 2011-09-02 trilho de aço para ferrovias e método de fabricação do mesmo

Country Status (5)

Country Link
US (1) US20130193223A1 (pt)
EP (1) EP2612943A4 (pt)
CN (1) CN101921950B (pt)
BR (1) BR112013005163B1 (pt)
WO (1) WO2012028111A1 (pt)

Families Citing this family (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101921950B (zh) * 2010-09-02 2011-12-14 攀钢集团有限公司 用于高速和准高速铁路的钢轨及其制造方法
CN103014486A (zh) * 2012-12-08 2013-04-03 内蒙古包钢钢联股份有限公司 一种高强度热处理钢轨专用钢材
CN104046765B (zh) * 2014-02-20 2016-03-23 攀钢集团攀枝花钢铁研究院有限公司 一种过共析钢轨的热处理方法
CN104195433B (zh) * 2014-09-02 2016-08-31 攀钢集团攀枝花钢铁研究院有限公司 一种高强韧性珠光体钢轨及其生产方法
CN105018705B (zh) * 2015-08-11 2017-12-15 攀钢集团攀枝花钢铁研究院有限公司 一种过共析钢轨及其制备方法
CN105671268A (zh) * 2016-01-30 2016-06-15 聂玲 一种真空感应淬火炉
CN106868275A (zh) * 2016-12-28 2017-06-20 内蒙古包钢钢联股份有限公司 抑制过共析钢轨钢中晶界渗碳体析出的方法
CN107755982A (zh) * 2017-10-31 2018-03-06 攀钢集团攀枝花钢铁研究院有限公司 耐腐蚀高速铁路用钢轨生产方法
CN109402520B (zh) * 2018-11-02 2020-11-24 包头钢铁（集团）有限责任公司 一种含稀土耐低温耐磨热处理钢轨及其制备方法
CN111254902B (zh) * 2020-01-30 2020-12-01 华东交通大学 一种铁路路基形变检测与预警系统
DE102021105566A1 (de) 2020-03-24 2021-09-30 Honeywell International Inc. Drehgeber
CN112410663B (zh) * 2020-11-04 2022-02-01 武汉钢铁有限公司 一种低电阻率耐磨导向钢轨用钢材及其制备方法
CN113930667B (zh) * 2021-09-03 2022-11-01 武汉钢铁有限公司 磨耗和滚动接触疲劳良好耦合的钢轨及其生产方法
CN113789473B (zh) * 2021-09-14 2022-09-16 鞍钢股份有限公司 一种高速铁路小半径曲线用高强耐磨钢轨及其生产方法
CN113774283B (zh) * 2021-09-14 2022-09-16 鞍钢股份有限公司 一种高速铁路非小半径曲线用高韧塑性钢轨及其生产方法
CN113909294A (zh) * 2021-10-28 2022-01-11 攀钢集团攀枝花钢铁研究院有限公司 一种高致密度道岔钢轨及其生产方法
CN114000057A (zh) * 2021-10-28 2022-02-01 河南中原特钢装备制造有限公司 加稀土冶炼的mc6c轧辊用钢及其冶炼连铸工艺
CN114015940B (zh) * 2021-11-03 2022-06-03 攀钢集团攀枝花钢铁研究院有限公司 一种中等强度低氧化皮钢轨及其生产方法
CN114507806A (zh) * 2022-01-10 2022-05-17 包头钢铁（集团）有限责任公司 一种低成本耐低温钢轨生产工艺
CN114752858B (zh) * 2022-04-24 2023-03-24 广东韶钢松山股份有限公司 一种不含马氏体组织的合金手工具钢盘条及制备方法和手工具钢
CN115287441B (zh) * 2022-07-31 2024-04-30 包头钢铁（集团）有限责任公司 一种U71MnG高速钢轨焊接接头的焊后热处理方法

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2907960C3 (de) * 1979-03-01 1984-04-19 Elhaus, Friedrich Wilhelm, Dipl.-Ing., 5600 Wuppertal Verfahren und Vorrichtung zum kontinuierlichen Wärmebehandeln von vereinzeltem, langgestrecktem metallischen Gut
CN1019586B (zh) * 1990-01-11 1992-12-23 任春山 一种汽油代用燃油剂的配方及其配制方法
US5351229A (en) 1991-12-24 1994-09-27 International Business Machines Corporation Tribo-attractive contact slider for an optical read/write system
JP3267772B2 (ja) * 1993-11-26 2002-03-25 新日本製鐵株式会社 高強度、高延性、高靭性レールの製造法
CN1044826C (zh) * 1994-11-15 1999-08-25 新日本制铁株式会社 耐磨性优良的珠光体类钢轨及其制造方法
JP3513427B2 (ja) * 1999-05-31 2004-03-31 新日本製鐵株式会社 耐摩耗性、耐内部疲労損傷性に優れたパーライト系レールおよびその製造方法
CN100443617C (zh) * 2005-12-29 2008-12-17 攀枝花钢铁(集团)公司 珠光体类热处理钢轨及其生产方法
PL2400040T3 (pl) * 2009-02-18 2016-05-31 Nippon Steel & Sumitomo Metal Corp Szyna perlityczna o doskonałej odporności na ścieranie i wiązkości
CN101921950B (zh) * 2010-09-02 2011-12-14 攀钢集团有限公司 用于高速和准高速铁路的钢轨及其制造方法

Also Published As

Publication number Publication date
WO2012028111A8 (zh) 2012-07-12
BR112013005163B1 (pt) 2018-10-23
CN101921950B (zh) 2011-12-14
CN101921950A (zh) 2010-12-22
EP2612943A4 (en) 2017-07-05
US20130193223A1 (en) 2013-08-01
EP2612943A1 (en) 2013-07-10
WO2012028111A1 (zh) 2012-03-08

Similar Documents

Publication Publication Date Title
BR112013005163A2 (pt) trilho de aço para ferrovias de alta velocidade e velocidade quase alta e método de fabricação do mesmo
BR112015020329A2 (pt) aço com resistência a desgaste aumentada e métodos para a produção do mesmo
BR112013025040A2 (pt) placa de aço resistente à abrasão, ou chapa de aço excelente em resistência a craqueamento por corrosão de tensão, e método para produção da mesma
CN104120354B (zh) 一种接触疲劳性能优良的钢轨及其生产方法
BR112013031500B8 (pt) chapa de aço laminada a frio revestida, processo de fabricação uma chapa laminada a frio e revestida processo de fabricação de uma peça por soldagem de pelo menos uma chapa laminada a frio revestida e uso de uma chapa de aço laminada a frio revestida
BR112014008032A2 (pt) compressor espiral
BR112014000376A2 (pt) chapa de aço de resistência ultra-alta, resistente ao desgaste, e método de produção da mesma
BR112014009103A2 (pt) material de camada de superfície de rolo para laminação a quente com excelente resistência à fadiga produzido por fundição centrífuga e rolo compósito para laminação a quente produzido através de fundição centrífuga
BR112017024692A2 (pt) placa de aço e método de produção da mesma
TWI476286B (zh) Wheel steel
BRPI0700840A (pt) liga para mancais de rolamento
BR112013011236A2 (pt) aço resistente à abrasão, método para fabricação de um aço resistente à abrasão e artigos feitos a partir do mesmo
BR112012029698A2 (pt) método de produção de uma chapa de aço de alta resistência para uma estrutura soldada
BR0209091A (pt) Processo para a produção de aços inoxidáveis com melhor resistência à corrosão
BRPI1015485A2 (pt) aço de baixa gravidade específica para uso ótimo em forja em usinagem
CN102094112B (zh) 合金钢产品的热处理工艺
BR112015027447A2 (pt) aço de alta resistência que exibe boa ductilidade e método de produção por meio de tratamento de têmpera e partição através de banho de zinco
BR112013007154A2 (pt) folha de aço de alta resistência e método para fabricação da mesma
BR112018071237A2 (pt) material compósito de alumínio, método para produzir um material compósito de alumínio, uso e trocador de calor
WO2017027085A3 (en) Low alloy high performance steel
BRPI0907583A2 (pt) Aços para trilhos com exelente combinação de propriedades de desgaste e resistência à fadiga por contato de rolagem
CN101067185A (zh) 一种高温长寿自润滑耐磨合金材料
BR112017002127A2 (pt) aço com alta resistência a desgaste, dureza e resistência à corrosão altas assim como baixa condutividade térmica e uso de tal aço
BR112014030829A2 (pt) tubulação de alta resistência e resistente à corrosão; e processo de fabricação de tubulação com alta resistência e resistente à corrosão
Ren et al. Fatigue analysis of 75 kg/m-12 heavy-haul railway frog based on finite element simulation

Legal Events

Date Code Title Description
B07A Application suspended after technical examination (opinion) [chapter 7.1 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 02/09/2011, OBSERVADAS AS CONDICOES LEGAIS.